LATI Latene® AG3H2W G/30-V0E PP Homopolymer, 30% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant

Seller in Kolkata price: $1532 per MT
Seller in Toronto price: $2501 per MT

LATI Latene® AG3H2W G/30-V0E PP Homopolymer, 30% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant in Polymer, Thermoplastic, Flame Retardant, Polypropylene (PP), Polypropylene, Polypropylene with 30% Glass Fiber Filler

  • Physical Properties
  • Density
  • 1.46 g/cc
  • Linear Mold Shrinkage, Flow
  • 0.0030 - 0.0050 cm/cm
  • Linear Mold Shrinkage, Transverse
  • 0.0075 - 0.0095 cm/cm
  • Mechanical Properties
  • Tensile Strength at Break
  • 30.0 MPa @Temperature 90.0 °C
  • Tensile Strength at Break
  • 45.0 MPa @Temperature 60.0 °C
  • Tensile Strength at Break
  • 75.0 MPa @Temperature 23.0 °C
  • Elongation at Break
  • 2.5 % @Temperature 23.0 °C
  • Elongation at Break
  • 4.0 % @Temperature 60.0 °C
  • Elongation at Break
  • 7.0 % @Temperature 90.0 °C
  • Elongation at Yield
  • 2.5 % @Temperature 60.0 °C
  • Elongation at Yield
  • 4.0 % @Temperature 90.0 °C
  • Tensile Modulus
  • 4.30 GPa @Temperature 90.0 °C
  • Tensile Modulus
  • 5.70 GPa @Temperature 60.0 °C
  • Tensile Modulus
  • 7.80 GPa @Temperature 23.0 °C
  • Charpy Impact Unnotched
  • 2.00 J/cm² @Temperature -20.0 °C
  • Charpy Impact Unnotched
  • 4.00 J/cm² @Temperature 23.0 °C
  • Charpy Impact, Notched
  • 0.500 J/cm² @Temperature -20.0 °C
  • Charpy Impact, Notched
  • 1.00 J/cm² @Temperature 23.0 °C
  • Thermal Properties
  • Maximum Service Temperature, Air
  • 110 °C
  • Deflection Temperature at 0.46 MPa (66 psi)
  • 155 °C
  • Deflection Temperature at 1.8 MPa (264 psi)
  • 140 °C
  • Vicat Softening Point
  • 135 °C @Load 5.00 kg
  • Flammability, UL94
  • V-0 @Thickness 3.00 mm
  • Flammability, UL94
  • V-0 @Thickness 1.50 mm
  • Flammability, UL94
  • V-0 @Thickness 0.750 mm
  • Oxygen Index
  • 26 %
  • Electrical Properties
  • Comparative Tracking Index
  • 575 V
  • Processing Properties
  • Melt Temperature
  • 190 - 220 °C
  • Mold Temperature
  • 30.0 - 50.0 °C
  • Drying Temperature
  • 80.0 - 90.0 °C @Time 10800 sec
  • Descriptive Properties
  • ISO Shrinkage - Pressure
  • 60 MPa

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, cargo boats for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for LATI Latene® AG3H2W G/30-V0E PP Homopolymer, 30% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant

Seller from Kolkata – 2021-03-23:

Seller from Kolkata work with company: RTP Company, SABIC Innovative Plastics (GE Plastics), LG Chemical, ALIMEX GmbH

Price: $1532 per MT

Seller from Toronto – 2021-02-26:

Seller from Toronto work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2501 per MT

Share on Pinterest
Share on LinkedIn
Share on Reddit

Would you like to sell LATI Latene® AG3H2W G/30-V0E PP Homopolymer, 30% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant?

Plastic warehouse

Find a direct plastic supplier if you're interested in a supplier or Industrial consultant in Singapore open-nearme.com