LATI Latene® 7H2-V2HF PP Homopolymer, Heat Stabilized, Flame Retardant price 1670 per MT

Physical Properties
Density
1.02 g/cc
Linear Mold Shrinkage, Flow
0.013 - 0.016 cm/cm
Linear Mold Shrinkage, Transverse
0.0135 - 0.0165 cm/cm

Mechanical Properties
Tensile Strength at Break
20.0 MPa
Elongation at Break
60 % @Temperature 23.0 °C
Elongation at Break
>= 100 % @Temperature 60.0 °C
Elongation at Break
>= 100 % @Temperature 90.0 °C
Elongation at Yield
7.5 % @Temperature 23.0 °C
Elongation at Yield
8.5 % @Temperature 60.0 °C
Elongation at Yield
9.0 % @Temperature 90.0 °C
Tensile Modulus
0.550 GPa @Temperature 90.0 °C
Tensile Modulus
0.850 GPa @Temperature 60.0 °C
Tensile Modulus
1.90 GPa @Temperature 23.0 °C
Charpy Impact Unnotched
1.50 J/cm² @Temperature -20.0 °C
Charpy Impact Unnotched
4.00 J/cm² @Temperature 23.0 °C
Charpy Impact, Notched
0.0400 J/cm² @Temperature -20.0 °C
Charpy Impact, Notched
0.150 J/cm² @Temperature 23.0 °C

Thermal Properties
Maximum Service Temperature, Air
100 °C
Deflection Temperature at 0.46 MPa (66 psi)
100 °C
Deflection Temperature at 1.8 MPa (264 psi)
60.0 °C
Vicat Softening Point
100 °C @Load 5.00 kg
Flammability, UL94
V-2 @Thickness 3.00 mm
Flammability, UL94
V-2 @Thickness 1.50 mm
Flammability, UL94
V-2 @Thickness 0.750 mm
Oxygen Index
25 %
Glow Wire Test
850 °C @Thickness 1.00 mm
Glow Wire Test
850 °C @Thickness 2.00 mm
Glow Wire Test
960 °C @Thickness 1.00 mm
Glow Wire Test
960 °C @Thickness 2.00 mm

Electrical Properties
Comparative Tracking Index
600 V

Processing Properties
Melt Temperature
180 - 210 °C
Mold Temperature
30.0 - 50.0 °C
Drying Temperature
80.0 - 90.0 °C @Time 10800 sec

Descriptive Properties
ISO Shrinkage - Pressure
60 MPa

Alternative products

LATI Latene® 7 TR-V2 PP Homopolymer, Mineral Reinforced, Flame Retardant accurate 49%

$ 1618/MT

Density: 0.970 g/cc
Linear Mold Shrinkage, Flow: 0.0135 - 0.0165 cm/cm
Linear Mold Shrinkage, Transverse: 0.014 - 0.017 cm/cm
Tensile Strength at Break: 25.0 MPa
Elongation at Break: 25 % @Temperature 23.0 °C

BASF Ultraform H 4320 Q600 POM accurate 41%

$ 1730/MT

Density: 1.39 g/cc
Water Absorption: 0.80 %
Moisture Absorption at Equilibrium: 0.20 %
Melt Flow: 26 g/10 min @Load 2.16 kg, Temperature 190 °C
Ball Indentation Hardness: 125 MPa

LATI Latene® 7H2W T-V0 PP Homopolymer, Mineral Reinforced, Heat Stabilized, Flame Retardant accurate 49%

$ 1565/MT

Density: 1.32 g/cc
Linear Mold Shrinkage, Flow: 0.0075 - 0.010 cm/cm
Linear Mold Shrinkage, Transverse: 0.0070 - 0.010 cm/cm
Tensile Strength at Break: 7.00 MPa @Temperature 90.0 °C
Tensile Strength at Break: 10.0 MPa @Temperature 60.0 °C

Aardvark Polymers Aardalloy® 3326 POM Alloy Rotational Molding Resin accurate 41%

$ 2560/MT

Density: 1.34 g/cc
Density: 1.34 g/cc
Water Absorption: 0.44 %
Moisture Absorption at Equilibrium: 0.35 %
Moisture Absorption at Equilibrium: 0.35 %

Thermal Ceramics Cerafelt accurate 49%

$ 2091/MT

Specific Gravity: 0.385 g/cc
Density: 0.128 g/cc
Density: 0.160 g/cc
Density: 0.192 g/cc
Density: 0.288 g/cc

LATI Later 4-V0HF1 PBT, Flame Retardant accurate 49%

$ 2019/MT

Density: 1.33 g/cc
Linear Mold Shrinkage, Flow: 0.015 - 0.018 cm/cm
Linear Mold Shrinkage, Transverse: 0.015 - 0.018 cm/cm
Tensile Strength at Break: 12.0 MPa @Temperature 90.0 °C
Tensile Strength at Break: 25.0 MPa @Temperature 60.0 °C

LATI Latene® 7-V2 PP Homopolymer, Flame Retardant accurate 57%

$ 1871/MT

Density: 0.940 g/cc
Linear Mold Shrinkage, Flow: 0.014 - 0.017 cm/cm
Linear Mold Shrinkage, Transverse: 0.0145 - 0.0175 cm/cm
Elongation at Break: >= 100 % @Temperature 23.0 °C
Elongation at Break: >= 100 % @Temperature 60.0 °C

EMS-Grivory Grivory® TS FR PA666 FR accurate 49%

$ 1502/MT

Density: 1.15 g/cc
Water Absorption: 8.0 %
Moisture Absorption: 2.50 %
Linear Mold Shrinkage, Flow: 0.0070 cm/cm
Linear Mold Shrinkage, Transverse: 0.0080 cm/cm

BASF Ultraform® S2320 0035 POM accurate 41%

$ 1589/MT

Density: 1.40 g/cc
Water Absorption: 0.80 %
Moisture Absorption at Equilibrium: 0.20 %
Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 190 °C
Ball Indentation Hardness: 130 MPa @Load 36.5 kg, Time 30.0 sec

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, ro ro ship for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

4 prices for LATI Latene® 7H2-V2HF PP Homopolymer, Heat Stabilized, Flame Retardant

Seller from Mexico City – 2021-05-23:

Seller from Mexico City work with company: Solvay, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1963 per MT

Seller from Lahore – 2021-07-20:

Seller from Lahore work with company: 3M, Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics)

Price: $2293 per MT

Seller from London – 2021-03-24:

Seller from London work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1670 per MT

Seller from Lagos – 2021-06-25:

Seller from Lagos work with company: RTP Company, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2593 per MT