LATI Later 4 G/30-V0 PBT, 30% Glass Fiber Reinforced, Flame Retardant

Seller in New York price: $1948 per MT
Seller in Sydney price: $2511 per MT

LATI Later 4 G/30-V0 PBT, 30% Glass Fiber Reinforced, Flame Retardant in Polymer, Thermoplastic, Flame Retardant, 30% Glass Fiber Filled, Polyester, TP, Polybutylene Terephthalate (PBT)

  • Physical Properties
  • Density
  • 1.58 g/cc
  • Linear Mold Shrinkage, Flow
  • 0.0030 - 0.0050 cm/cm
  • Linear Mold Shrinkage, Transverse
  • 0.0095 - 0.0125 cm/cm
  • Mechanical Properties
  • Tensile Strength at Break
  • 40.0 MPa @Temperature 150 °C
  • Tensile Strength at Break
  • 50.0 MPa @Temperature 120 °C
  • Tensile Strength at Break
  • 65.0 MPa @Temperature 90.0 °C
  • Tensile Strength at Break
  • 85.0 MPa @Temperature 60.0 °C
  • Tensile Strength at Break
  • 120 MPa @Temperature 23.0 °C
  • Elongation at Break
  • 2.8 % @Temperature 23.0 °C
  • Elongation at Break
  • 4.0 % @Temperature 60.0 °C
  • Elongation at Break
  • 6.0 % @Temperature 90.0 °C
  • Elongation at Break
  • 6.2 % @Temperature 120 °C
  • Elongation at Break
  • 6.3 % @Temperature 150 °C
  • Tensile Modulus
  • 2.80 GPa @Temperature 150 °C
  • Tensile Modulus
  • 3.80 GPa @Temperature 120 °C
  • Tensile Modulus
  • 4.90 GPa @Temperature 90.0 °C
  • Tensile Modulus
  • 7.20 GPa @Temperature 60.0 °C
  • Tensile Modulus
  • 9.50 GPa @Temperature 23.0 °C
  • Charpy Impact Unnotched
  • 5.00 J/cm² @Temperature 23.0 °C
  • Charpy Impact Unnotched
  • 5.00 J/cm² @Temperature -20.0 °C
  • Charpy Impact, Notched
  • 0.700 J/cm² @Temperature -20.0 °C
  • Charpy Impact, Notched
  • 0.800 J/cm² @Temperature 23.0 °C
  • Thermal Properties
  • Maximum Service Temperature, Air
  • 135 °C
  • Deflection Temperature at 0.46 MPa (66 psi)
  • 215 °C
  • Deflection Temperature at 1.8 MPa (264 psi)
  • 205 °C
  • Vicat Softening Point
  • 205 °C @Load 5.00 kg
  • Flammability, UL94
  • V-0 @Thickness 3.00 mm
  • Flammability, UL94
  • V-0 @Thickness 1.50 mm
  • Flammability, UL94
  • V-0 @Thickness 0.750 mm
  • Oxygen Index
  • 31 %
  • Glow Wire Test
  • 960 °C @Thickness 1.00 mm
  • Glow Wire Test
  • 960 °C @Thickness 2.00 mm
  • Electrical Properties
  • Comparative Tracking Index
  • 250 V
  • Processing Properties
  • Melt Temperature
  • 240 - 250 °C
  • Mold Temperature
  • 70.0 - 90.0 °C
  • Drying Temperature
  • 110 - 130 °C @Time 10800 sec
  • Descriptive Properties
  • ISO Shrinkage - Pressure
  • 60 MPa

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale europe. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for LATI Later 4 G/30-V0 PBT, 30% Glass Fiber Reinforced, Flame Retardant

Seller from New York – 2021-07-24:

Seller from New York work with company: 3M, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1948 per MT

Seller from Sydney – 2021-04-24:

Seller from Sydney work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2511 per MT

Share on Pinterest
Share on LinkedIn
Share on Reddit

Would you like to sell LATI Later 4 G/30-V0 PBT, 30% Glass Fiber Reinforced, Flame Retardant?

Plastic warehouse

Find a direct plastic supplier if you're interested in a supplier or Ballet theater in Singapore open-nearme.com