LG Chemical Lupox® GP2156FM PBT+GF15% price 1925 per MT

Physical Properties
Specific Gravity
1.52 g/cc
Maximum Moisture Content
0.020
Linear Mold Shrinkage, Flow
0.0040 - 0.010 cm/cm @Thickness 3.20 mm

Mechanical Properties
Tensile Strength at Break
95.1 MPa @Thickness 3.20 mm
Elongation at Break
4.0 % @Thickness 3.20 mm
Flexural Yield Strength
149 MPa @Thickness 3.20 mm
Flexural Modulus
5.69 GPa @Thickness 3.20 mm
Izod Impact, Notched
0.520 J/cm @Thickness 3.20 mm, Temperature 23.0 °C

Thermal Properties
Melting Point
225 °C
Deflection Temperature at 0.46 MPa (66 psi)
210 °C @Thickness 6.40 mm
Deflection Temperature at 1.8 MPa (264 psi)
200 °C @Thickness 6.40 mm
UL RTI, Electrical
130 °C @Thickness >=0.710 mm
UL RTI, Electrical
130 °C @Thickness >=1.50 mm
UL RTI, Electrical
130 °C @Thickness >=3.00 mm
UL RTI, Mechanical with Impact
130 °C @Thickness >=0.710 mm
UL RTI, Mechanical with Impact
130 °C @Thickness >=1.50 mm
UL RTI, Mechanical with Impact
130 °C @Thickness >=3.00 mm
UL RTI, Mechanical without Impact
130 °C @Thickness >=0.710 mm
UL RTI, Mechanical without Impact
130 °C @Thickness >=1.50 mm
UL RTI, Mechanical without Impact
130 °C @Thickness >=3.00 mm
Flammability, UL94
V-0 @Thickness >=0.710 mm
Flammability, UL94
V-0 @Thickness >=1.50 mm
Flammability, UL94
V-0 @Thickness >=3.00 mm

Electrical Properties
Volume Resistivity
1.00e+17 ohm-cm
Dielectric Strength
26.0 kV/mm @Thickness 1.00 mm
Arc Resistance
0.00 - 60 sec
Comparative Tracking Index
175 V
Hot Wire Ignition, HWI
15 - 30 sec @Thickness >=0.710 mm
Hot Wire Ignition, HWI
15 - 30 sec @Thickness >=1.50 mm
Hot Wire Ignition, HWI
30 - 60 sec @Thickness >=3.30 mm
High Amp Arc Ignition, HAI
>= 120 arcs @Thickness 0.710 mm
High Amp Arc Ignition, HAI
>= 120 arcs @Thickness 1.50 mm
High Amp Arc Ignition, HAI
>= 120 arcs @Thickness 3.30 mm
High Voltage Arc-Tracking Rate, HVTR
80.0 - 150 mm/min

Processing Properties
Rear Barrel Temperature
235 - 250 °C
Middle Barrel Temperature
240 - 250 °C
Front Barrel Temperature
245 - 255 °C
Nozzle Temperature
245 - 255 °C
Melt Temperature
245 - 255 °C
Mold Temperature
60.0 - 100 °C
Drying Temperature
120 °C
Dry Time
4.00 - 5.00 hour

Alternative products

LG Chemical Lupox® GP2156FL PBT+GF15% accurate 99%

$ 1715/MT

Specific Gravity: 1.52 g/cc
Maximum Moisture Content: 0.020
Linear Mold Shrinkage, Flow: 0.0040 - 0.010 cm/cm @Thickness 3.20 mm
Tensile Strength at Break: 93.2 MPa @Thickness 3.20 mm
Elongation at Break: 3.0 % @Thickness 3.20 mm

LG Chemical Lupox® GP2306FG PBT+GF30% accurate 89%

$ 2058/MT

Specific Gravity: 1.62 g/cc
Maximum Moisture Content: 0.020
Linear Mold Shrinkage, Flow: 0.0030 - 0.010 cm/cm @Thickness 3.20 mm
Tensile Strength at Break: 125 MPa @Thickness 3.20 mm
Elongation at Break: 3.0 % @Thickness 3.20 mm

ChevronTexaco Texatherm® accurate 89%

$ 1472/MT

Specific Gravity: 0.6215 g/cc
Specific Gravity: 0.668 g/cc
Specific Gravity: 0.7032 g/cc
Specific Gravity: 0.7416 g/cc
Specific Gravity: 0.7763 g/cc

LG Chemical Lupox® GP2306FB PBT+GF30% accurate 89%

$ 1983/MT

Specific Gravity: 1.62 g/cc
Maximum Moisture Content: 0.020
Linear Mold Shrinkage, Flow: 0.0030 - 0.010 cm/cm @Thickness 3.20 mm
Tensile Strength at Break: 123 MPa @Thickness 3.20 mm
Elongation at Break: 3.0 % @Thickness 3.20 mm

LG Chemical Lupox® GP2306FC PBT+GF30% accurate 89%

$ 1880/MT

Specific Gravity: 1.62 g/cc
Maximum Moisture Content: 0.020
Linear Mold Shrinkage, Flow: 0.0030 - 0.010 cm/cm @Thickness 3.20 mm
Tensile Strength at Break: 127 MPa @Thickness 3.20 mm
Elongation at Break: 3.0 % @Thickness 3.20 mm

LG Chemical Lupox® GP2306FI PBT+GF30% accurate 89%

$ 1695/MT

Specific Gravity: 1.62 g/cc
Maximum Moisture Content: 0.020
Linear Mold Shrinkage, Flow: 0.0030 - 0.010 cm/cm @Thickness 3.20 mm
Tensile Strength at Break: 118 MPa @Thickness 3.20 mm
Elongation at Break: 3.0 % @Thickness 3.20 mm

LG Chemical Lupox® GP2306FS PBT+GF30% accurate 89%

$ 1473/MT

Specific Gravity: 1.62 g/cc
Maximum Moisture Content: 0.020
Linear Mold Shrinkage, Flow: 0.0030 - 0.010 cm/cm @Thickness 3.20 mm
Tensile Strength at Break: 127 MPa @Thickness 3.20 mm
Elongation at Break: 3.0 % @Thickness 3.20 mm

LG Chemical Lupox® GP2400G PBT+GF40% accurate 89%

$ 1791/MT

Specific Gravity: 1.61 g/cc
Maximum Moisture Content: 0.020
Linear Mold Shrinkage, Flow: 0.0040 - 0.010 cm/cm @Thickness 3.20 mm
Tensile Strength at Break: 127 MPa @Thickness 3.20 mm
Elongation at Break: 3.0 % @Thickness 3.20 mm

LG Chemical Lupox® GP2156FT PBT+GF15% accurate 99%

$ 1661/MT

Specific Gravity: 1.52 g/cc
Maximum Moisture Content: 0.020
Linear Mold Shrinkage, Flow: 0.0040 - 0.010 cm/cm @Thickness 3.20 mm
Tensile Strength at Break: 98.1 MPa @Thickness 3.20 mm
Elongation at Break: 3.0 % @Thickness 3.20 mm

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, tanker ship for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for LG Chemical Lupox® GP2156FM PBT+GF15%

Seller from Tokyo – 2021-06-14:

Seller from Tokyo work with company: Techmer ES, Arlon, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1925 per MT

Seller from Kinshasa – 2021-03-25:

Seller from Kinshasa work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2246 per MT

Seller from Philadelphia – 2021-07-09:

Seller from Philadelphia work with company: RTP Company, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2472 per MT