Physical Properties
Specific Gravity
1.62 g/cc
Maximum Moisture Content
0.020
Linear Mold Shrinkage, Flow
0.0030 - 0.010 cm/cm @Thickness 3.20 mm

Mechanical Properties
Tensile Strength at Break
125 MPa @Thickness 3.20 mm
Elongation at Break
3.0 % @Thickness 3.20 mm
Flexural Yield Strength
188 MPa @Thickness 3.20 mm
Flexural Modulus
8.34 GPa @Thickness 3.20 mm
Izod Impact, Notched
0.637 J/cm @Thickness 3.20 mm, Temperature 23.0 °C

Thermal Properties
Melting Point
225 °C
Deflection Temperature at 0.46 MPa (66 psi)
215 °C @Thickness 6.40 mm
Deflection Temperature at 1.8 MPa (264 psi)
200 °C @Thickness 6.40 mm
UL RTI, Electrical
140 °C @Thickness >=0.710 mm
UL RTI, Electrical
140 °C @Thickness >=1.50 mm
UL RTI, Electrical
140 °C @Thickness >=3.00 mm
UL RTI, Mechanical with Impact
140 °C @Thickness >=0.710 mm
UL RTI, Mechanical with Impact
140 °C @Thickness >=1.50 mm
UL RTI, Mechanical with Impact
140 °C @Thickness >=3.00 mm
UL RTI, Mechanical without Impact
140 °C @Thickness >=0.710 mm
UL RTI, Mechanical without Impact
140 °C @Thickness >=1.50 mm
UL RTI, Mechanical without Impact
140 °C @Thickness >=3.00 mm
Flammability, UL94
V-0 @Thickness >=0.710 mm
Flammability, UL94
V-0 @Thickness >=1.50 mm
Flammability, UL94
V-0 @Thickness >=3.00 mm

Electrical Properties
Volume Resistivity
1.00e+17 ohm-cm
Dielectric Strength
28.0 kV/mm @Thickness 1.00 mm
Arc Resistance
60 - 120 sec
Comparative Tracking Index
250 - 400 V
Hot Wire Ignition, HWI
7.0 - 15 sec @Thickness >=0.710 mm
Hot Wire Ignition, HWI
30 - 60 sec @Thickness >=1.50 mm
High Amp Arc Ignition, HAI
60 - 120 arcs @Thickness 0.710 mm
High Amp Arc Ignition, HAI
60 - 120 arcs @Thickness 1.50 mm
High Voltage Arc-Tracking Rate, HVTR
80.0 - 150 mm/min

Processing Properties
Rear Barrel Temperature
235 - 250 °C
Middle Barrel Temperature
240 - 250 °C
Front Barrel Temperature
245 - 255 °C
Nozzle Temperature
245 - 255 °C
Melt Temperature
245 - 255 °C
Mold Temperature
60.0 - 100 °C
Drying Temperature
120 °C
Dry Time
4.00 - 5.00 hour

Alternative products

LG Chemical Lupox® GP2156FL PBT+GF15% accurate 99%

$ 1715/MT

Specific Gravity: 1.52 g/cc
Maximum Moisture Content: 0.020
Linear Mold Shrinkage, Flow: 0.0040 - 0.010 cm/cm @Thickness 3.20 mm
Tensile Strength at Break: 93.2 MPa @Thickness 3.20 mm
Elongation at Break: 3.0 % @Thickness 3.20 mm

ChevronTexaco Texatherm® accurate 99%

$ 1472/MT

Specific Gravity: 0.6215 g/cc
Specific Gravity: 0.668 g/cc
Specific Gravity: 0.7032 g/cc
Specific Gravity: 0.7416 g/cc
Specific Gravity: 0.7763 g/cc

LG Chemical Lupox® GP2306FB PBT+GF30% accurate 99%

$ 1983/MT

Specific Gravity: 1.62 g/cc
Maximum Moisture Content: 0.020
Linear Mold Shrinkage, Flow: 0.0030 - 0.010 cm/cm @Thickness 3.20 mm
Tensile Strength at Break: 123 MPa @Thickness 3.20 mm
Elongation at Break: 3.0 % @Thickness 3.20 mm

LG Chemical Lupox® GP2306FC PBT+GF30% accurate 99%

$ 1880/MT

Specific Gravity: 1.62 g/cc
Maximum Moisture Content: 0.020
Linear Mold Shrinkage, Flow: 0.0030 - 0.010 cm/cm @Thickness 3.20 mm
Tensile Strength at Break: 127 MPa @Thickness 3.20 mm
Elongation at Break: 3.0 % @Thickness 3.20 mm

LG Chemical Lupox® GP2306FI PBT+GF30% accurate 99%

$ 1695/MT

Specific Gravity: 1.62 g/cc
Maximum Moisture Content: 0.020
Linear Mold Shrinkage, Flow: 0.0030 - 0.010 cm/cm @Thickness 3.20 mm
Tensile Strength at Break: 118 MPa @Thickness 3.20 mm
Elongation at Break: 3.0 % @Thickness 3.20 mm

LG Chemical Lupox® GP2306FS PBT+GF30% accurate 99%

$ 1473/MT

Specific Gravity: 1.62 g/cc
Maximum Moisture Content: 0.020
Linear Mold Shrinkage, Flow: 0.0030 - 0.010 cm/cm @Thickness 3.20 mm
Tensile Strength at Break: 127 MPa @Thickness 3.20 mm
Elongation at Break: 3.0 % @Thickness 3.20 mm

LG Chemical Lupox® GP2400G PBT+GF40% accurate 99%

$ 1791/MT

Specific Gravity: 1.61 g/cc
Maximum Moisture Content: 0.020
Linear Mold Shrinkage, Flow: 0.0040 - 0.010 cm/cm @Thickness 3.20 mm
Tensile Strength at Break: 127 MPa @Thickness 3.20 mm
Elongation at Break: 3.0 % @Thickness 3.20 mm

LG Chemical Lupox® GP2156FM PBT+GF15% accurate 99%

$ 1925/MT

Specific Gravity: 1.52 g/cc
Maximum Moisture Content: 0.020
Linear Mold Shrinkage, Flow: 0.0040 - 0.010 cm/cm @Thickness 3.20 mm
Tensile Strength at Break: 95.1 MPa @Thickness 3.20 mm
Elongation at Break: 4.0 % @Thickness 3.20 mm

LG Chemical Lupox® GP2156FT PBT+GF15% accurate 99%

$ 1661/MT

Specific Gravity: 1.52 g/cc
Maximum Moisture Content: 0.020
Linear Mold Shrinkage, Flow: 0.0040 - 0.010 cm/cm @Thickness 3.20 mm
Tensile Strength at Break: 98.1 MPa @Thickness 3.20 mm
Elongation at Break: 3.0 % @Thickness 3.20 mm

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, new cruise ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for LG Chemical Lupox® GP2306FG PBT+GF30%

Seller from Dallas – 2021-03-16:

Seller from Dallas work with company: RTP Company, PolyOne Corporation, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2239 per MT

Seller from Santiago – 2021-08-13:

Seller from Santiago work with company: RTP Company, SABIC Innovative Plastics (GE Plastics), BASF, ALIMEX GmbH

Price: $2193 per MT

Seller from Seoul – 2021-03-05:

Seller from Seoul work with company: Solvay, SABIC Innovative Plastics (GE Plastics), LG Chemical, ALIMEX GmbH

Price: $2058 per MT