Mitsubishi Hostaphan® RN, 250 micron Nominal Thickness Universal Polyethylene Terephthalate Film price 2005 per MT

Physical Properties
Density
1.40 g/cc @Temperature 23.0 °C
Water Absorption
0.50 % @Temperature 23.0 °C
Linear Mold Shrinkage
0.010 cm/cm @Temperature 150 °C, Time 900 sec
Linear Mold Shrinkage, Transverse
0.010 cm/cm @Temperature 150 °C, Time 900 sec

Mechanical Properties
Film Tensile Strength at Yield, MD
150 MPa
Film Tensile Strength at Yield, TD
200 MPa
Film Elongation at Break, MD
>= 200 %
Film Elongation at Break, TD
140 %
Modulus of Elasticity
3.60 GPa @Temperature 23.0 °C
Modulus of Elasticity
4.30 GPa @Temperature 23.0 °C
Coefficient of Friction, Static
0.40

Optical Properties
Haze
40 %

Electrical Properties
Dielectric Constant
2.9 @Frequency 2.40e+8 Hz, Temperature 23.0 °C
Dielectric Constant
2.9 @Frequency 9.30e+9 Hz, Temperature 23.0 °C
Dielectric Constant
3.2 @Frequency 1.00e+6 Hz, Temperature 23.0 °C
Dielectric Constant
3.3 @Frequency 50.0 Hz, Temperature 23.0 °C
Dielectric Constant
3.3 @Frequency 1000 Hz, Temperature 23.0 °C
Dielectric Constant
3.6 @Frequency 50.0 Hz, Temperature 150 °C

Descriptive Properties
Conductivity of Aqueous Extract (ÂµS/cm)
2
F5-value (MPa)
105
F5-value (MPa)
105

Alternative products

DuPont Elvaloy® 3108 AC Ethylene and 7% Butyl Acrylate Copolymer (discontinued **) accurate 49%

$ 2171/MT

Density: 0.924 g/cc
Thickness: 40.0 microns
Melt Flow: 1.1 g/10 min @Load 2.16 kg, Temperature 190 °C
Film Tensile Strength at Yield, MD: 8.00 MPa
Film Tensile Strength at Yield, TD: 7.00 MPa

ExxonMobil LDPE LD 368HD Low Density Polyethylene Resin accurate 49%

$ 1506/MT

Density: 0.924 g/cc
Melt Flow: 1.5 g/10 min @Load 2.16 kg, Temperature 190 °C
Antiblock Level: 1800 ppm
Slip Level: 650 ppm
Film Elongation at Break, MD: 200 %

ExxonMobil Escorene® LD-104 LDPE Packaging Film Resin, High Clarity (discontinued **) accurate 49%

$ 2191/MT

Density: 0.925 g/cc
Thickness: 31.8 microns
Melt Flow: 2.0 g/10 min
Film Tensile Strength at Yield, MD: 9.70 MPa
Film Tensile Strength at Yield, TD: 11.0 MPa

Iran Petrochemical (PCC) 2101TN47 Low Density Polyethylene accurate 49%

$ 1633/MT

Density: 0.921 g/cc
Melt Flow: 0.85 g/10 min
Film Tensile Strength at Yield, MD: 12.0 MPa
Film Tensile Strength at Yield, TD: 11.0 MPa
Film Elongation at Break, MD: >= 200 %

DuPont Teijin Films Melinex® 725 Polyester Film accurate 49%

$ 1805/MT

Film Tensile Strength at Yield, MD: 89.6 MPa
Film Tensile Strength at Yield, TD: 89.6 MPa
Film Elongation at Break, MD: 200 %
Film Elongation at Break, TD: 120 %
Coefficient of Friction, Dynamic: 0.40

Mitsubishi Hostaphan® RN, 190 micron Nominal Thickness Universal Polyethylene Terephthalate Film accurate 49%

$ 1558/MT

Density: 1.40 g/cc @Temperature 23.0 °C
Water Absorption: 0.50 % @Temperature 23.0 °C
Linear Mold Shrinkage: 0.010 cm/cm @Temperature 150 °C, Time 900 sec
Linear Mold Shrinkage, Transverse: 0.0030 cm/cm @Temperature 150 °C, Time 900 sec
Film Tensile Strength at Yield, MD: 150 MPa

ExxonMobil LD 146.NH Packaging Film Resin (discontinued **) accurate 49%

$ 1899/MT

Density: 0.920 g/cc
Thickness: 38.1 microns
Melt Flow: 3.75 g/10 min
Antiblock Level: 1200 ppm
Slip Level: 900 ppm

LyondellBasell Petrothene® NA960070 Low Density Polyethylene accurate 49%

$ 1827/MT

Density: 0.919 g/cc
Thickness: 31.8 microns
Melt Flow: 0.90 g/10 min
Tensile Strength at Break: 14.5 MPa
Film Elongation at Break, MD: 200 %

DuPont Teijin Films Melinex® 561 Polyester Film accurate 49%

$ 1482/MT

Film Tensile Strength at Yield, MD: 96.5 MPa
Film Tensile Strength at Yield, TD: 96.5 MPa
Film Elongation at Break, MD: 200 %
Film Elongation at Break, TD: 120 %
Coefficient of Friction, Dynamic: 0.50

Victrex® APTIV® 2000-050 Polyetheretherketone (PEEK) Polymer Film, Amorphous accurate 99%

$ 2085/MT

Specific Gravity: 1.26 g/cc @Temperature 23.0 °C
Moisture Absorption at Equilibrium: 0.21 % @Temperature 23.0 °C, Time 86400 sec
Film Elongation at Break, MD: >= 200 %
Film Elongation at Break, MD: >= 200 % @Thickness 0.0250 mm
Film Elongation at Break, MD: >= 200 % @Thickness 0.0250 mm

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale ru. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for Mitsubishi Hostaphan® RN, 250 micron Nominal Thickness Universal Polyethylene Terephthalate Film

Seller from Baghdad – 2021-08-18:

Seller from Baghdad work with company: 3M, PolyOne Corporation, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2005 per MT

Seller from Lahore – 2021-06-04:

Seller from Lahore work with company: Celanese Corporation, Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics)

Price: $2594 per MT

Seller from Phoenix – 2021-03-27:

Seller from Phoenix work with company: 3M, Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics)

Price: $2257 per MT