Outokumpu 4565 High Performance Austenitic Stainless Steel price 1549 per MT

Physical Properties
Density
8.00 g/cc

Mechanical Properties
Hardness, Brinell
>= 240
Tensile Strength, Ultimate
825 MPa
Tensile Strength, Ultimate
610 MPa @Temperature 400 °C
Tensile Strength, Ultimate
640 MPa @Temperature 200 °C
Tensile Strength, Ultimate
640 MPa @Temperature 300 °C
Tensile Strength, Ultimate
750 MPa @Temperature 100 °C
Tensile Strength, Yield
420 MPa @Strain 0.200 %
Tensile Strength, Yield
440 MPa @Strain 0.200 %
Tensile Strength, Yield
480 MPa @Strain 1.00 %
Tensile Strength, Yield
210 MPa @Strain 0.200 %, Temperature 400 °C
Tensile Strength, Yield
240 MPa @Strain 0.200 %, Temperature 300 °C
Tensile Strength, Yield
240 MPa @Strain 1.00 %, Temperature 400 °C
Tensile Strength, Yield
270 MPa @Strain 1.00 %, Temperature 300 °C
Tensile Strength, Yield
270 MPa @Strain 0.200 %, Temperature 200 °C
Tensile Strength, Yield
310 MPa @Strain 1.00 %, Temperature 200 °C
Tensile Strength, Yield
350 MPa @Strain 0.200 %, Temperature 100 °C
Tensile Strength, Yield
400 MPa @Strain 1.00 %, Temperature 100 °C
Elongation at Break
55 %
Modulus of Elasticity
190 GPa
Modulus of Elasticity
165 GPa @Temperature 400 °C
Impact Test
>= 90.0 J

Thermal Properties
CTE, linear
14.5 µm/m-°C @Temperature 100 °C
CTE, linear
16.8 µm/m-°C @Temperature 400 °C
Specific Heat Capacity
0.450 J/g-°C
Thermal Conductivity
12.0 W/m-K
Thermal Conductivity
18.0 W/m-K @Temperature 400 °C

Component Elements Properties
Carbon, C
0.020 %
Chromium, Cr
24 %
Iron, Fe
48.53 %
Manganese, Mn
5.5 %
Molybdenum, Mo
4.5 %
Nickel, Ni
17 %
Nitrogen, N
0.45 %

Electrical Properties
Electrical Resistivity
0.0000920 ohm-cm

Processing Properties
Annealing Temperature
1120 - 1170 °C

Alternative products

Haynes HR-120® alloy, solution heat-treated aged at 1600°F for 1000 hours accurate 88%

$ 1673/MT

Density: 8.07 g/cc
Tensile Strength, Ultimate: 715 MPa
Tensile Strength, Yield: 325 MPa @Strain 0.200 %
Elongation at Break: 21 %
Modulus of Elasticity: 197 GPa

Haynes HR-120® alloy, solution heat-treated aged at 1400°F for 1000 hours accurate 88%

$ 1568/MT

Density: 8.07 g/cc
Tensile Strength, Ultimate: 725 MPa
Tensile Strength, Yield: 340 MPa @Strain 0.200 %
Elongation at Break: 24 %
Modulus of Elasticity: 197 GPa

Haynes 556® alloy, 20% cold reduction, 1121°C anneal for 5 minutes accurate 88%

$ 1792/MT

Density: 8.23 g/cc
Tensile Strength, Ultimate: 830 MPa
Tensile Strength, Yield: 405 MPa @Strain 0.200 %
Elongation at Break: 45.4 %
Modulus of Elasticity: 205 GPa

Haynes 556® alloy, 40% cold reduction accurate 88%

$ 2465/MT

Density: 8.23 g/cc
Tensile Strength, Ultimate: 1305 MPa
Tensile Strength, Yield: 1075 MPa @Strain 0.200 %
Elongation at Break: 10.1 %
Modulus of Elasticity: 205 GPa

Haynes 556® alloy, bar, after 4000 hours at 870°C (1600°F) accurate 88%

$ 1635/MT

Density: 8.23 g/cc
Tensile Strength, Ultimate: 770 MPa
Tensile Strength, Yield: 295 MPa @Strain 0.200 %
Elongation at Break: 29 %
Modulus of Elasticity: 205 GPa

Outokumpu 4828 High Temperature Austenitic Stainless Steel accurate 99%

$ 2405/MT

Density: 7.80 g/cc
Tensile Strength, Ultimate: 610 MPa
Tensile Strength, Ultimate: 320 MPa @Temperature 600 °C
Tensile Strength, Ultimate: 370 MPa @Temperature 500 °C
Tensile Strength, Ultimate: 400 MPa @Temperature 400 °C

Outokumpu 4841 High Temperature Austenitic Stainless Steel accurate 99%

$ 1868/MT

Density: 7.80 g/cc
Tensile Strength, Ultimate: 595 MPa
Tensile Strength, Yield: 275 MPa @Strain 0.200 %
Tensile Strength, Yield: 315 MPa @Strain 1.00 %
Elongation at Break: 55 %

Haynes 556® alloy, 50% cold reduction, 1065°C anneal for 5 minutes accurate 88%

$ 1759/MT

Density: 8.23 g/cc
Tensile Strength, Ultimate: 905 MPa
Tensile Strength, Yield: 535 MPa @Strain 0.200 %
Elongation at Break: 33.4 %
Modulus of Elasticity: 205 GPa

Haynes 556® alloy, bar after 16000 hours at 760°C (1400°F) accurate 88%

$ 1636/MT

Density: 8.23 g/cc
Tensile Strength, Ultimate: 500 MPa
Tensile Strength, Yield: 240 MPa @Strain 0.200 %
Elongation at Break: 25.3 %
Modulus of Elasticity: 205 GPa

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale today. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

4 prices for Outokumpu 4565 High Performance Austenitic Stainless Steel

Seller from Hyderabad – 2021-04-03:

Seller from Hyderabad work with company: Solvay, SABIC Innovative Plastics (GE Plastics), LG Chemical, ALIMEX GmbH

Price: $1987 per MT

Seller from Cairo – 2021-04-24:

Seller from Cairo work with company: 3M, RTP Company, Exxon Chemical, SABIC Innovative Plastics (GE Plastics)

Price: $1549 per MT

Seller from Shenyang – 2021-03-19:

Seller from Shenyang work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2476 per MT

Seller from Sydney – 2021-03-29:

Seller from Sydney work with company: Solvay, SABIC Innovative Plastics (GE Plastics), BASF, ALIMEX GmbH

Price: $2492 per MT