Overview of materials for Nylon 66, Glass Fiber/PTFE Filled price 1503 per MT

Physical Properties
Density
1.22 - 1.78 g/cc
Filler Content
5.00 - 40.0 %
Water Absorption
0.300 - 6.00 %
Water Absorption at Saturation
0.800 - 5.50 %
Additive Loading
15.0 - 50.0 %
Linear Mold Shrinkage
0.000300 - 0.0200 cm/cm
Linear Mold Shrinkage, Transverse
0.00750 - 0.0140 cm/cm

Mechanical Properties
Hardness, Rockwell R
108 - 120
Tensile Strength, Ultimate
68.0 - 250 MPa
Tensile Strength, Yield
118 - 179 MPa
Elongation at Break
1.00 - 7.00 %
Elongation at Yield
2.50 - 5.00 %
Modulus of Elasticity
3.45 - 15.5 GPa
Flexural Yield Strength
89.0 - 320 MPa
Flexural Modulus
3.03 - 14.8 GPa
Compressive Yield Strength
68.9 - 165 MPa
Shear Strength
76.0 - 79.0 MPa
Izod Impact, Notched
0.427 - 2.14 J/cm
Izod Impact, Unnotched
3.74 - 13.3 J/cm
Charpy Impact Unnotched
3.00 J/cm² - NB
Charpy Impact Unnotched
2.70 - 6.00 J/cm² @Temperature -40.0 - -30.0 °C
Charpy Impact, Notched
0.350 - 1.50 J/cm²
Charpy Impact, Notched
0.300 - 0.300 J/cm² @Temperature -40.0 - -40.0 °C
Coefficient of Friction
0.130 - 0.620
Coefficient of Friction, Static
0.110 - 0.520
K (wear) Factor
5.10 - 50.4 x 10 mm³/N-M

Thermal Properties
CTE, linear
19.8 - 55.8 µm/m-°C
Thermal Conductivity
0.220 - 0.519 W/m-K
Melting Point
249 - 275 °C
Maximum Service Temperature, Air
90.0 - 160 °C
Deflection Temperature at 0.46 MPa (66 psi)
216 - 270 °C
Deflection Temperature at 1.8 MPa (264 psi)
199 - 260 °C
Vicat Softening Point
200 - 250 °C
Flammability, UL94
HB - V-0

Electrical Properties
Electrical Resistivity
1.00e+13 - 1.00e+16 ohm-cm
Surface Resistance
1.00e+12 - 1.00e+15 ohm
Insulation Resistance
1.00e+12 ohm
Dielectric Constant
3.70 - 4.20
Dielectric Strength
18.1 - 19.7 kV/mm
Dissipation Factor
0.0130 - 0.0200
Arc Resistance
100 - 120 sec

Processing Properties
Processing Temperature
274 - 293 °C
Nozzle Temperature
280 - 300 °C
Melt Temperature
260 - 310 °C
Mold Temperature
60.0 - 121 °C
Drying Temperature
75.0 - 107 °C
Moisture Content
0.200 %
Dew Point
-17.8 °C
Injection Pressure
68.9 - 124 MPa

Alternative products

BASF Ultramid® KR 4355 G7 BK 00564 35% Glass Filled PA6/6T (Conditioned) accurate 99%

$ 1599/MT

Bulk Density: 0.500 - 0.800 g/cc
Density: 1.43 g/cc
Water Absorption: 4.3 - 5.3 %
Moisture Absorption at Equilibrium: 0.80 - 1.2 %
Viscosity Measurement: 130

RTP Company RTP 1475 L Polyethersulfone (PES), Glass Fiber - Lubricated accurate 66%

$ 1543/MT

Specific Gravity: 1.47 g/cc
Water Absorption: 0.41 %
Linear Mold Shrinkage: 0.0030 cm/cm @Thickness 3.17 mm
Hardness, Rockwell R: 122
Tensile Strength at Break: 110 MPa

Axion Polymers Axpoly® PS02 1000 General Purpose Polystyrene accurate 66%

$ 2169/MT

Density: 1.03 g/cc
Density: 1.02 - 1.06 g/cc
Particle Size: 2000 - 4000 µm
Particle Size: 3000 µm
Melt Index of Compound: 5.0 - 9.0 g/10 min @Load 5.00 kg, Temperature 200 °C

Overview of materials for Polycarbonate, Glass + PTFE Filled accurate 99%

$ 1551/MT

Density: 1.28 - 1.61 g/cc
Filler Content: 10.0 - 40.0 %
Water Absorption: 0.0170 - 0.250 %
Additive Loading: 15.0 - 30.0 %
Linear Mold Shrinkage: 0.000500 - 0.00800 cm/cm

BASF Ultramid® KR 4355 G5 BK 00564 25% Glass Filled PA6/6T (Conditioned) accurate 99%

$ 1502/MT

Bulk Density: 0.500 - 0.800 g/cc
Density: 1.35 g/cc
Water Absorption: 5.0 - 6.0 %
Moisture Absorption at Equilibrium: 1.1 - 1.5 %
Viscosity Measurement: 130

BASF Ultramid® KR 4355 G5 25% Glass Filled PA6/6T (Conditioned) accurate 99%

$ 1663/MT

Bulk Density: 0.500 - 0.800 g/cc
Density: 1.35 g/cc
Water Absorption: 5.0 - 6.0 %
Moisture Absorption at Equilibrium: >= 1.3 %
Moisture Absorption at Equilibrium: 1.1 - 1.5 %

BASF Ultramid® KR 4350 BK 00464 PA6/6T (Conditioned) accurate 99%

$ 1909/MT

Bulk Density: 0.450 - 0.800 g/cc
Density: 1.16 g/cc
Water Absorption: 6.5 - 7.5 %
Moisture Absorption at Equilibrium: 1.6 - 2.0 %
Viscosity Measurement: 130

Shandong Dongyue Shenzhou New Material Co Vinylidene Fluoride (VDF) accurate 99%

$ 1581/MT

Density: 0.617 g/cc @Temperature 23.6 °C
Molecular Weight: 64 g/mol
Vapor Pressure: 35.9433 bar @Temperature 20.0 °C
Melting Point: -144 °C
Boiling Point: -85.7 °C @Pressure 0.1013 MPa

RTP Company RTP 1401 N Polyethersulfone (PES), Glass Fiber - High Viscosity accurate 66%

$ 1454/MT

Specific Gravity: 1.44 g/cc
Filler Content: 10 %
Water Absorption: 0.40 %
Linear Mold Shrinkage: 0.0060 cm/cm @Thickness 3.17 mm
Hardness, Rockwell R: 121

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, freighter ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

4 prices for Overview of materials for Nylon 66, Glass Fiber/PTFE Filled

Seller from Pune – 2021-08-01:

Seller from Pune work with company: 3M, Solvay, Techmer ES, SABIC Innovative Plastics (GE Plastics)

Price: $1732 per MT

Seller from Alexandria – 2021-03-08:

Seller from Alexandria work with company: 3M, Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics)

Price: $2357 per MT

Seller from Santiago – 2021-04-20:

Seller from Santiago work with company: Solvay, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1503 per MT

Seller from Dallas – 2021-07-01:

Seller from Dallas work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1626 per MT