PEAK Werkstoff DISPAL S270 Aluminum Alloy, AlSi25Fe4Ni3CuMgMnCrTi, Condition T6 price 2037 per MT

Physical Properties
Density
2.651 - 2.930 g/cc

Mechanical Properties
Hardness, Vickers
>= 200
Hardness, Vickers
>= 230
Tensile Strength at Break
>= 252 MPa @Temperature 250 °C
Tensile Strength at Break
>= 425 MPa @Temperature 20.0 °C
Tensile Strength at Break
>= 480 MPa @Temperature 20.0 °C
Tensile Strength, Yield
>= 373 MPa @Temperature 20.0 °C
Tensile Strength, Yield
>= 470 MPa @Temperature 20.0 °C
Elongation at Break
>= 0.15 % @Temperature 20.0 °C
Elongation at Break
>= 0.20 % @Temperature 20.0 °C
Modulus of Elasticity
>= 99.0 GPa @Temperature 20.0 °C
Modulus of Elasticity
>= 100 GPa @Temperature 20.0 °C
Poissons Ratio
0.284 @Temperature 20.0 °C
Poissons Ratio
0.286 @Temperature 100 °C
Poissons Ratio
0.288 @Temperature 150 °C
Poissons Ratio
0.289 @Temperature 200 °C
Poissons Ratio
0.291 @Temperature 250 °C
Poissons Ratio
0.292 @Temperature 300 °C

Thermal Properties
CTE, linear
15.2 - 16.2 µm/m-°C @Temperature 20.0 - 100 °C
CTE, linear
15.7 - 16.7 µm/m-°C @Temperature 20.0 - 200 °C
CTE, linear
16.3 - 17.3 µm/m-°C @Temperature 20.0 - 300 °C
Specific Heat Capacity
0.800 - 0.840 J/g-°C
Thermal Conductivity
89.60 W/m-K @Temperature 400 °C
Thermal Conductivity
93.70 W/m-K @Temperature 300 °C
Thermal Conductivity
94.90 W/m-K @Temperature 200 °C
Thermal Conductivity
96.30 W/m-K @Temperature 100 °C
Thermal Conductivity
98.40 W/m-K @Temperature 30.0 °C
Melting Point
536 - 777 °C
Solidus
536.3 - 542.3 °C
Liquidus
770.9 - 776.9 °C

Component Elements Properties
Aluminum, Al
63 %
Chromium, Cr
1.0 %
Copper, Cu
1.0 %
Iron, Fe
4.0 %
Magnesium, Mg
1.0 %
Manganese, Mn
1.0 %
Nickel, Ni
3.0 %
Silicon, Si
25 %
Titanium, Ti
1.0 %

Electrical Properties
Electrical Resistivity
0.00000940 - 0.0000104 ohm-cm

Alternative products

CLAL-MSX SICLANIC S® TD4 Quenched Copper Alloy, 4/4 Hard accurate 99%

$ 1814/MT

Density: 8.90 g/cc
Hardness, Vickers: 195 - 250
Hardness, Vickers: 200 @Time 18000 sec
Hardness, Vickers: 203 @Time 14400 sec
Hardness, Vickers: 210 @Time 10800 sec

CLAL-MSX SICLANIC S® TH3 Quenched Copper Alloy, 1/2 Hard, precipitation treated accurate 87%

$ 2464/MT

Density: 8.90 g/cc
Hardness, Vickers: 190 - 215
Hardness, Vickers: 180 @Time 3600 sec
Hardness, Vickers: 190 @Time 7200 sec
Hardness, Vickers: 200 @Time 10800 sec

CLAL-MSX SICLANIC S® TB Quenched Copper Alloy accurate 99%

$ 1791/MT

Density: 8.90 g/cc
Hardness, Vickers: 79 - 85
Hardness, Vickers: 173 @Time 3600 sec
Hardness, Vickers: 195 @Time 7200 sec
Hardness, Vickers: 195 @Time 18000 sec

CLAL-MSX SICLANIC S® TF Quenched Copper Alloy, precipitation treated accurate 99%

$ 1671/MT

Density: 8.90 g/cc
Hardness, Vickers: 170 - 190
Hardness, Vickers: 150 @Time 3600 sec
Hardness, Vickers: 170 @Time 7200 sec
Hardness, Vickers: 180 @Time 10800 sec

Indium Corp. Germanium Corporation® GeCl4 Germanium Tetrachloride accurate 74%

$ 1866/MT

Specific Gravity: 1.875 g/cc @Temperature 20.0 °C
Molecular Weight: 214.45 g/mol
Vapor Pressure: 0.101 bar @Temperature 20.0 °C
Boiling Point: 83.0 °C
Aluminum, Al: <= 1.0e-7 %

PEAK Werkstoff DISPAL S270 Aluminum Alloy, AlSi25Fe4Ni3CuMgMnCrTi, Condition T4 accurate 74%

$ 1931/MT

Density: 2.651 - 2.930 g/cc
Hardness, Vickers: >= 175
Hardness, Vickers: >= 180
Tensile Strength at Break: >= 385 MPa @Temperature 20.0 °C
Tensile Strength at Break: >= 439 MPa @Temperature 20.0 °C

PEAK Werkstoff DISPAL S270 Aluminum Alloy, AlSi25Fe4Ni3CuMgMnCrTi, Condition F accurate 74%

$ 1596/MT

Density: 2.651 - 2.930 g/cc
Hardness, Vickers: >= 160
Tensile Strength at Break: >= 138 MPa @Temperature 300 °C
Tensile Strength at Break: >= 252 MPa @Temperature 250 °C
Tensile Strength at Break: >= 296 MPa @Temperature 200 °C

H.C. Starck Pure Molybdenum OMPP Pellets (99.8%) accurate 74%

$ 2379/MT

Density: >= 7.00 g/cc
Aluminum, Al: 0.0020 %
Aluminum, Al: <= 0.010 %
Calcium, Ca: 0.0010 %
Calcium, Ca: <= 0.010 %

CLAL-MSX SICLANIC S® TH4 Quenched Copper Alloy, 4/4 Hard, precipitation treated accurate 99%

$ 1526/MT

Density: 8.90 g/cc
Hardness, Vickers: 195 - 250
Hardness, Vickers: 200 @Time 3600 sec
Hardness, Vickers: 212 @Time 7200 sec
Hardness, Vickers: 220 @Time 10800 sec

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, ships for sale turkey. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for PEAK Werkstoff DISPAL S270 Aluminum Alloy, AlSi25Fe4Ni3CuMgMnCrTi, Condition T6

Seller from Hāora – 2021-07-15:

Seller from Hāora work with company: Solvay, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2037 per MT

Seller from Jakarta – 2021-07-01:

Seller from Jakarta work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2483 per MT