PEAK Werkstoff DISPAL S693 Aluminum Alloy, AlCu5Ti, Condition T6 price 1614 per MT

Physical Properties
Density
2.679 - 2.961 g/cc

Mechanical Properties
Hardness, Vickers
>= 144
Tensile Strength
>= 123 MPa @Temperature 300 °C
Tensile Strength
>= 338 MPa @Temperature 200 °C
Tensile Strength
>= 491 MPa @Temperature 20.0 °C
Tensile Strength, Yield
>= 122 MPa @Temperature 300 °C
Tensile Strength, Yield
>= 318 MPa @Temperature 200 °C
Tensile Strength, Yield
>= 429 MPa @Temperature 20.0 °C
Elongation at Break
>= 9.3 % @Temperature 20.0 °C
Elongation at Break
>= 14.4 % @Temperature 200 °C
Elongation at Break
>= 21.2 % @Temperature 300 °C
Modulus of Elasticity
>= 58.0 GPa @Temperature 300 °C
Modulus of Elasticity
>= 65.0 GPa @Temperature 200 °C
Modulus of Elasticity
>= 72.0 GPa @Temperature 20.0 °C
Poissons Ratio
0.341 @Temperature 20.0 °C
Poissons Ratio
0.347 @Temperature 100 °C
Poissons Ratio
0.354 @Temperature 150 °C
Poissons Ratio
0.361 @Temperature 200 °C
Poissons Ratio
0.364 @Temperature 250 °C
Poissons Ratio
0.369 @Temperature 300 °C
Shear Modulus
23.0 GPa @Temperature 300 °C
Shear Modulus
24.0 GPa @Temperature 200 °C
Shear Modulus
24.0 GPa @Temperature 250 °C
Shear Modulus
25.0 GPa @Temperature 150 °C
Shear Modulus
26.0 GPa @Temperature 100 °C
Shear Modulus
28.0 GPa @Temperature 20.0 °C

Thermal Properties
CTE, linear
22.9 - 23.9 µm/m-°C @Temperature 20.0 - 100 °C
CTE, linear
23.7 - 24.7 µm/m-°C @Temperature 20.0 - 200 °C
CTE, linear
24.5 - 25.5 µm/m-°C @Temperature 20.0 - 300 °C
Thermal Conductivity
121.9 W/m-K @Temperature 30.0 °C
Thermal Conductivity
130.9 W/m-K @Temperature 100 °C
Thermal Conductivity
144.6 W/m-K @Temperature 200 °C
Thermal Conductivity
155.7 W/m-K @Temperature 300 °C
Thermal Conductivity
156.1 W/m-K @Temperature 400 °C
Melting Point
512 - 659 °C
Solidus
512.3 - 518.3 °C
Liquidus
653.6 - 659.3 °C

Component Elements Properties
Aluminum, Al
94 %
Copper, Cu
5.0 %
Titanium, Ti
1.0 %

Electrical Properties
Electrical Resistivity
0.00000570 - 0.00000610 ohm-cm

Alternative products

CLAL-MSX SICLANIC S® TD4 Quenched Copper Alloy, 4/4 Hard accurate 99%

$ 1814/MT

Density: 8.90 g/cc
Hardness, Vickers: 195 - 250
Hardness, Vickers: 200 @Time 18000 sec
Hardness, Vickers: 203 @Time 14400 sec
Hardness, Vickers: 210 @Time 10800 sec

TIMCAL TIMREX® SFG75 Primary Synthetic Graphite accurate 56%

$ 1671/MT

Particle Size: 5.0 µm
Particle Size: 5.0 µm
Particle Size: 10 µm
Particle Size: 42 µm
Particle Size: 75 µm

CLAL-MSX SICLANIC S® TH3 Quenched Copper Alloy, 1/2 Hard, precipitation treated accurate 85%

$ 2464/MT

Density: 8.90 g/cc
Hardness, Vickers: 190 - 215
Hardness, Vickers: 180 @Time 3600 sec
Hardness, Vickers: 190 @Time 7200 sec
Hardness, Vickers: 200 @Time 10800 sec

CLAL-MSX SICLANIC S® TB Quenched Copper Alloy accurate 99%

$ 1791/MT

Density: 8.90 g/cc
Hardness, Vickers: 79 - 85
Hardness, Vickers: 173 @Time 3600 sec
Hardness, Vickers: 195 @Time 7200 sec
Hardness, Vickers: 195 @Time 18000 sec

TIMCAL TIMREX® SFG15 Primary Synthetic Graphite accurate 56%

$ 1504/MT

Bulk Density: 0.0900 g/cc
Particle Size: 5.0 µm
Particle Size: 5.0 µm
Particle Size: 10 µm
Particle Size: 15.5 - 20 µm

CLAL-MSX SICLANIC S® TF Quenched Copper Alloy, precipitation treated accurate 99%

$ 1671/MT

Density: 8.90 g/cc
Hardness, Vickers: 170 - 190
Hardness, Vickers: 150 @Time 3600 sec
Hardness, Vickers: 170 @Time 7200 sec
Hardness, Vickers: 180 @Time 10800 sec

Haynes 282® Nickel Alloy Plate, Solution Annealed and Age-Hardened, after long term high temperature exposure accurate 70%

$ 1454/MT

Density: 8.27 g/cc
Density: 8.29 g/cc
Tensile Strength, Ultimate: 1152 MPa
Tensile Strength, Ultimate: 978 MPa @Treatment Temp. 871 °C, Time 5.76e+7 sec
Tensile Strength, Ultimate: 1006 MPa @Treatment Temp. 871 °C, Time 2.88e+7 sec

TIMCAL TIMREX® SFG6 Primary Synthetic Graphite accurate 56%

$ 1493/MT

Bulk Density: 0.0700 g/cc
Particle Size: 5.0 µm
Particle Size: 5.0 µm
Particle Size: 5.5 - 7.5 µm
Particle Size: 10 µm

TIMCAL TIMREX® SFG150 Primary Synthetic Graphite accurate 56%

$ 1615/MT

Oil Absorption: 45 %
Particle Size: 5.0 µm
Particle Size: 5.0 µm
Particle Size: 10 µm
Particle Size: 42 µm

CLAL-MSX SICLANIC S® TH4 Quenched Copper Alloy, 4/4 Hard, precipitation treated accurate 99%

$ 1526/MT

Density: 8.90 g/cc
Hardness, Vickers: 195 - 250
Hardness, Vickers: 200 @Time 3600 sec
Hardness, Vickers: 212 @Time 7200 sec
Hardness, Vickers: 220 @Time 10800 sec

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, new cruise ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for PEAK Werkstoff DISPAL S693 Aluminum Alloy, AlCu5Ti, Condition T6

Seller from Hāora – 2021-08-11:

Seller from Hāora work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1863 per MT

Seller from Shenzhen – 2021-03-23:

Seller from Shenzhen work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), Lehmann & Voss & Co.

Price: $2247 per MT

Seller from Melbourne – 2021-06-15:

Seller from Melbourne work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1614 per MT