Plastcom SLOVASTER® B GF 20 FRK 3 Polybutylene Terephthalate, 20% Chemically Coupled Glass Fiber, Red Phosphorus Flame Retardant price 1535 per MT

Physical Properties
Density
1.51 g/cc
Linear Mold Shrinkage
0.0049 cm/cm
Linear Mold Shrinkage, Transverse
0.0088 cm/cm
Melt Flow
10 g/10 min @Load 2.16 kg, Temperature 230 °C

Mechanical Properties
Tensile Strength at Break
110 MPa
Elongation at Break
2.0 %
Tensile Modulus
7.10 GPa
Flexural Strength
175 MPa
Flexural Modulus
7.60 GPa
Charpy Impact Unnotched
5.00 J/cm² @Temperature 23.0 °C
Charpy Impact Unnotched
5.50 J/cm² @Temperature -20.0 °C
Charpy Impact, Notched
0.700 J/cm² @Temperature -20.0 °C
Charpy Impact, Notched
0.700 J/cm² @Temperature 23.0 °C

Thermal Properties
Melting Point
200 - 220 °C
Deflection Temperature at 1.8 MPa (264 psi)
210 °C
Vicat Softening Point
210 °C
Flammability, UL94
V-0
Glow Wire Test
960 °C

Electrical Properties
Volume Resistivity
1.00e+17 ohm-cm
Surface Resistance
1.00e+15 ohm
Dielectric Strength
32.0 kV/mm
Comparative Tracking Index
200 V

Processing Properties
Melt Temperature
250 - 280 °C
Mold Temperature
50.0 - 90.0 °C
Drying Temperature
120 °C
Dry Time
4 hour
Moisture Content
0.050 %
Injection Pressure
60.0 - 100 MPa

Alternative products

Plastcom SLOVASTER® B GF 20 FRL 4 Polybutylene Terephthalate, 20% Chemically Coupled Glass Fiber, Bromine Hydrocarbon Flame Retardant accurate 60%

$ 1830/MT

Density: 1.68 g/cc
Linear Mold Shrinkage: 0.0092 cm/cm
Linear Mold Shrinkage, Transverse: 0.0168 cm/cm
Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
Tensile Strength at Break: 110 MPa

Plastcom SLOVASTER® B GF 30 FRL 4 Polybutylene Terephthalate, 30% Chemically Coupled Glass Fiber, Bromine Hydrocarbon Flame Retardant accurate 60%

$ 1706/MT

Density: 1.73 g/cc
Linear Mold Shrinkage: 0.0111 cm/cm
Linear Mold Shrinkage, Transverse: 0.0168 cm/cm
Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
Tensile Strength at Break: 130 MPa

Plastcom SLOVASTER® B GF 30 FRK 3 Polybutylene Terephthalate, 30% Chemically Coupled Glass Fiber, Red Phosphorus Flame Retardant accurate 60%

$ 1713/MT

Density: 1.66 g/cc
Linear Mold Shrinkage: 0.0055 cm/cm
Linear Mold Shrinkage, Transverse: 0.0073 cm/cm
Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
Tensile Strength at Break: 130 MPa

Celanese Celstran® PP-GF30-0405 P10/10 PP, 30% Glass Reinforced accurate 60%

$ 1711/MT

Density: 1.13 g/cc
Tensile Strength at Break: 110 MPa
Tensile Strength: 70.0 MPa @Temperature 80.0 °C
Elongation at Break: 2.20 %
Elongation at Break: 2.30 % @Temperature 80.0 °C

Celanese Celstran® PP-GF30-0455 P10/16 PP, 30% Glass Reinforced accurate 60%

$ 1545/MT

Density: 1.13 g/cc
Tensile Strength at Break: 110 MPa
Tensile Strength: 70.0 MPa @Temperature 80.0 °C
Elongation at Break: 2.20 %
Elongation at Break: 2.30 % @Temperature 80.0 °C

Celanese Celstran® PP-GF30-0405 P10/16 PP, 30% Glass Reinforced accurate 60%

$ 1820/MT

Density: 1.13 g/cc
Tensile Strength at Break: 110 MPa
Tensile Strength: 70.0 MPa @Temperature 80.0 °C
Elongation at Break: 2.20 %
Elongation at Break: 2.30 % @Temperature 80.0 °C

Celanese Celstran® PP-GF30-0453 P10/10 PP, 30% Glass Reinforced accurate 60%

$ 2026/MT

Density: 1.12 g/cc
Tensile Strength at Break: 110 MPa
Tensile Strength: 70.0 MPa @Temperature 80.0 °C
Elongation at Break: 2.20 %
Elongation at Break: 2.30 % @Temperature 80.0 °C

Celanese Celstran® PP-GF30-0403 P10 PP, 30% Glass Reinforced accurate 55%

$ 1587/MT

Density: 1.12 g/cc
Tensile Strength at Break: 120 MPa
Tensile Strength: 80.0 MPa @Temperature 80.0 °C
Elongation at Break: 2.50 %
Elongation at Break: 2.30 % @Temperature 80.0 °C

Celanese Celstran® PP-GF30-0403 P10/10 PP, 30% Glass Reinforced accurate 60%

$ 1541/MT

Density: 1.13 g/cc
Viscosity Test: 119 cm³/g
Linear Mold Shrinkage, Flow: 0.00220 cm/cm
Linear Mold Shrinkage, Transverse: 0.00350 cm/cm
Tensile Strength at Break: 110 MPa

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng vessels for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

4 prices for Plastcom SLOVASTER® B GF 20 FRK 3 Polybutylene Terephthalate, 20% Chemically Coupled Glass Fiber, Red Phosphorus Flame Retardant

Seller from Chennai – 2021-03-09:

Seller from Chennai work with company: 3M, PolyOne Corporation, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1535 per MT

Seller from Los Angeles – 2021-08-07:

Seller from Los Angeles work with company: Solvay, SABIC Innovative Plastics (GE Plastics), BASF, ALIMEX GmbH

Price: $2231 per MT

Seller from Washington – 2021-06-05:

Seller from Washington work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1689 per MT

Seller from Mexico City – 2021-07-08:

Seller from Mexico City work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1754 per MT

Would you like to sell Plastcom SLOVASTER® B GF 20 FRK 3 Polybutylene Terephthalate, 20% Chemically Coupled Glass Fiber, Red Phosphorus Flame Retardant?