Polymer Resources PC-HM-FR1-[color]-1 Polycarbonate, 10% Glass Reinforced, Flame Retardant with Mold Release

Seller in Hanoi price: $2527 per MT

Polymer Resources PC-HM-FR1-[color]-1 Polycarbonate, 10% Glass Reinforced, Flame Retardant with Mold Release in Polymer, Thermoplastic, Flame Retardant, Glass Fiber Filled, Polycarbonate (PC), Polycarbonate, 10% Glass Filled

  • Physical Properties
  • Specific Gravity
  • 1.26 g/cc
  • Linear Mold Shrinkage
  • 0.0020 - 0.0050 cm/cm
  • Melt Flow
  • 5.0 - 12 g/10 min @Load 1.20 kg, Temperature 300 °C
  • Mechanical Properties
  • Hardness, Rockwell M
  • 85
  • Hardness, Rockwell R
  • 124
  • Tensile Strength at Break
  • 65.5 MPa
  • Tensile Strength, Yield
  • 55.8 MPa
  • Elongation at Break
  • 15 %
  • Elongation at Yield
  • 6.0 %
  • Flexural Strength
  • 103 MPa
  • Flexural Modulus
  • 3.38 GPa
  • Izod Impact, Notched
  • 1.07 J/cm @Temperature 22.8 °C
  • Thermal Properties
  • Deflection Temperature at 0.46 MPa (66 psi)
  • 143 °C
  • Deflection Temperature at 1.8 MPa (264 psi)
  • 138 °C
  • Vicat Softening Point
  • 152 °C
  • UL RTI, Electrical
  • 80.0 °C @Thickness 1.50 mm
  • UL RTI, Electrical
  • 80.0 °C @Thickness 3.00 mm
  • UL RTI, Mechanical with Impact
  • 80.0 °C @Thickness 1.50 mm
  • UL RTI, Mechanical with Impact
  • 80.0 °C @Thickness 3.00 mm
  • UL RTI, Mechanical without Impact
  • 80.0 °C @Thickness 1.50 mm
  • UL RTI, Mechanical without Impact
  • 80.0 °C @Thickness 3.00 mm
  • Flammability, UL94
  • V-0 @Thickness 1.50 mm
  • Flammability, UL94
  • V-0 - 5VA @Thickness 3.00 mm
  • Electrical Properties
  • Comparative Tracking Index
  • 175 - 250 V
  • Hot Wire Ignition, HWI
  • 30 - 60 sec @Thickness 1.50 mm
  • Hot Wire Ignition, HWI
  • 60 - 120 sec @Thickness 3.00 mm
  • High Amp Arc Ignition, HAI
  • 60 - 120 arcs @Thickness 1.50 mm
  • High Amp Arc Ignition, HAI
  • 60 - 120 arcs @Thickness 3.00 mm
  • Processing Properties
  • Rear Barrel Temperature
  • 293 - 316 °C
  • Middle Barrel Temperature
  • 304 - 327 °C
  • Front Barrel Temperature
  • 316 - 338 °C
  • Melt Temperature
  • 302 - 329 °C
  • Mold Temperature
  • 82.2 - 116 °C
  • Drying Temperature
  • 118 - 124 °C
  • Dry Time
  • 3.00 - 4.00 hour
  • Descriptive Properties
  • Vent
  • 0.0005

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tanker for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for Polymer Resources PC-HM-FR1-[color]-1 Polycarbonate, 10% Glass Reinforced, Flame Retardant with Mold Release

Seller from Hanoi – 2021-05-22:

Seller from Hanoi work with company: Solvay, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2527 per MT

Share on Pinterest
Share on LinkedIn
Share on Reddit

Would you like to sell Polymer Resources PC-HM-FR1-[color]-1 Polycarbonate, 10% Glass Reinforced, Flame Retardant with Mold Release?

Plastic warehouse

Find a direct plastic supplier if you're interested in a supplier or Animal rescue service in Singapore open-nearme.com