$ 1580/MT
- Specific Gravity: 1.09 g/cc
- Linear Mold Shrinkage: 0.014 - 0.020 cm/cm
- Tensile Strength at Break: 60.0 MPa
- Tensile Strength, Yield: 62.1 MPa
- Flexural Strength: 82.7 MPa
$ 1974/MT
- Specific Gravity: 1.19 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 5.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 55.2 MPa
- Tensile Strength, Yield: 54.5 MPa
$ 1860/MT
- Specific Gravity: 1.15 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 3.0 - 14 g/10 min @Load 5.00 kg, Temperature 250 °C
- Tensile Strength at Break: 56.5 MPa
- Tensile Strength, Yield: 57.9 MPa
$ 1727/MT
- Specific Gravity: 1.15 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm
- Melt Flow: 1.0 - 8.0 g/10 min @Load 11.6 kg, Temperature 250 °C
- Hardness, Rockwell R: 104
- Tensile Strength at Break: 75.8 MPa
$ 2547/MT
- Specific Gravity: 1.23 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 3.0 - 10 g/10 min @Load 11.6 kg, Temperature 250 °C
- Tensile Strength at Break: 66.9 MPa
- Tensile Strength, Yield: 68.9 MPa
$ 1659/MT
- Specific Gravity: 1.44 g/cc
- Linear Mold Shrinkage: 0.018 - 0.021 cm/cm
- Melt Flow: 6.0 - 12 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 51.7 MPa
- Tensile Strength, Yield: 50.3 MPa
$ 1454/MT
- Specific Gravity: 1.35 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0080 cm/cm
- Tensile Strength at Break: 128 MPa
- Tensile Strength, Yield: 128 MPa
- Flexural Strength: 200 MPa
$ 2023/MT
- Specific Gravity: 1.19 g/cc
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm
- Melt Flow: 0.10 - 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Tensile Strength at Break: 86.2 MPa
- Tensile Strength, Yield: 86.2 MPa
$ 1548/MT
- Specific Gravity: 1.38 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm
- Tensile Strength at Break: 193 MPa
- Tensile Strength, Yield: 193 MPa
- Flexural Strength: 290 MPa
$ 1891/MT
- Specific Gravity: 1.62 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm
- Melt Flow: 4.0 - 12 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength at Break: 114 MPa
- Tensile Strength, Yield: 114 MPa
$ 1632/MT
- Specific Gravity: 1.15 g/cc
- Linear Mold Shrinkage: 0.012 - 0.018 cm/cm
- Tensile Strength at Break: 82.7 MPa
- Tensile Strength, Yield: 82.7 MPa
- Flexural Strength: 103 MPa
$ 1773/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 25 - 50 g/10 min @Load 5.00 kg, Temperature 250 °C
- Tensile Strength at Break: 56.5 MPa
- Tensile Strength, Yield: 57.9 MPa
$ 1589/MT
- Specific Gravity: 1.33 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm
- Tensile Strength at Break: 141 MPa
- Tensile Strength, Yield: 141 MPa
- Flexural Strength: 204 MPa
$ 2349/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm
- Tensile Strength at Break: 86.2 MPa
- Tensile Strength, Yield: 86.2 MPa
- Flexural Strength: 123 MPa
$ 1622/MT
- Specific Gravity: 1.34 g/cc
- Water Absorption: 0.21 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 1.2 %
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
- Melt Flow: 5.0 - 22 g/10 min @Load 6.70 kg, Temperature 337 °C
$ 2024/MT
- Specific Gravity: 1.54 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0090 cm/cm
- Melt Flow: 10 - 20 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength at Break: 89.6 MPa
- Tensile Strength, Yield: 89.6 MPa
$ 1867/MT
- Specific Gravity: 1.26 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm
- Melt Flow: 5.0 - 12 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 65.5 MPa
- Tensile Strength, Yield: 55.8 MPa
$ 1549/MT
- Specific Gravity: 1.05 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 1.0 - 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 112
- Tensile Strength at Break: 42.1 MPa
$ 1823/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 9.0 - 16 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 62.1 MPa
- Tensile Strength, Yield: 68.9 MPa
$ 1749/MT
- Specific Gravity: 1.27 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Flow: 5.0 - 12 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 65.5 MPa
- Tensile Strength, Yield: 63.1 MPa
$ 1634/MT
- Density: 1.09 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 20 - 40 g/10 min
- Tensile Strength at Break: 50.3 MPa
- Tensile Strength, Yield: 49.0 MPa
$ 1447/MT
- Specific Gravity: 1.19 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 20 - 30 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 53.1 MPa
- Tensile Strength, Yield: 51.7 MPa
$ 1587/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 3.0 - 14 g/10 min
- Tensile Strength at Break: 37.9 MPa
- Tensile Strength, Yield: 35.9 MPa
$ 2282/MT
- Density: 1.08 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 15 - 40 g/10 min
- Tensile Strength at Break: 56.5 MPa
- Tensile Strength, Yield: 46.9 MPa
$ 2326/MT
- Specific Gravity: 1.38 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm
- Tensile Strength at Break: 193 MPa
- Tensile Strength, Yield: 193 MPa
- Flexural Strength: 290 MPa
$ 1797/MT
- Density: 1.18 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 25 - 45 g/10 min
- Tensile Strength at Break: 55.2 MPa
- Tensile Strength, Yield: 53.8 MPa
$ 1452/MT
- Specific Gravity: 1.14 g/cc
- Linear Mold Shrinkage: 0.012 - 0.018 cm/cm
- Linear Mold Shrinkage: 0.015 - 0.021 cm/cm
- Hardness, Rockwell R: 120
- Tensile Strength at Break: 89.6 MPa
$ 1658/MT
- Density: 1.60 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm
- Melt Flow: 8.0 - 18 g/10 min
- Tensile Strength at Break: 103 MPa
- Tensile Strength, Yield: 103 MPa
$ 2107/MT
- Density: 1.33 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm
- Tensile Strength at Break: 138 MPa
- Tensile Strength, Yield: 138 MPa
- Flexural Strength: 214 MPa
$ 1769/MT
- Specific Gravity: 1.60 g/cc
- Water Absorption: 0.13 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 0.90 %
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm
- Melt Flow: 3.0 - 18 g/10 min @Load 6.70 kg, Temperature 337 °C
$ 1529/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 18 - 30 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 1794/MT
- Density: 1.15 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 14 - 15 g/10 min
- Tensile Strength at Break: 53.8 MPa
- Tensile Strength, Yield: 52.4 MPa
$ 1541/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 3.0 - 4.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 1723/MT
- Specific Gravity: 1.26 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm
- Melt Flow: 5.0 - 12 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 85
- Hardness, Rockwell R: 124
$ 1844/MT
- Specific Gravity: 1.09 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 20 - 40 g/10 min @Load 11.6 kg, Temperature 250 °C
- Tensile Strength at Break: 49.0 MPa
- Tensile Strength, Yield: 50.3 MPa
$ 1602/MT
- Specific Gravity: 1.35 g/cc
- Linear Mold Shrinkage: 0.0010 - 0.0040 cm/cm
- Melt Flow: 4.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 117 MPa
- Tensile Strength, Yield: 117 MPa
$ 2025/MT
- Specific Gravity: 1.29 g/cc
- Linear Mold Shrinkage: 0.011 - 0.013 cm/cm
- Melt Flow: 12 - 20 g/10 min @Load 2.16 kg, Temperature 265 °C
- Tensile Strength at Break: 49.0 MPa
- Tensile Strength, Yield: 42.7 MPa
$ 1837/MT
- Specific Gravity: 1.27 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Flow: 5.0 - 12 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 65.5 MPa
- Tensile Strength, Yield: 62.7 MPa
$ 2100/MT
- Specific Gravity: 1.08 g/cc
- Linear Mold Shrinkage: 0.0090 - 0.012 cm/cm
- Melt Flow: 20 - 40 g/10 min @Load 3.80 kg, Temperature 300 °C
- Tensile Strength at Break: 55.2 MPa
- Tensile Strength, Yield: 57.9 MPa
$ 1483/MT
- Specific Gravity: 1.14 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm
- Melt Flow: 1.0 - 8.0 g/10 min @Load 11.6 kg, Temperature 250 °C
- Hardness, Rockwell L: 104
- Tensile Strength at Break: 72.4 MPa
$ 1775/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 5.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 72.4 MPa
- Tensile Strength, Yield: 62.1 MPa
$ 1609/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 18 - 30 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 1486/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 5.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 1670/MT
- Specific Gravity: 1.19 g/cc
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm
- Melt Flow: 2.0 - 5.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 74.12 MPa
- Tensile Strength, Yield: 66.2 MPa
$ 1523/MT
- Specific Gravity: 1.50 g/cc
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm
- Melt Flow: 2.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 165 MPa
- Tensile Strength, Yield: 165 MPa
$ 1664/MT
- Density: 1.15 g/cc
- Linear Mold Shrinkage: 0.012 - 0.018 cm/cm
- Tensile Strength at Break: 82.7 MPa
- Tensile Strength, Yield: 82.7 MPa
- Flexural Strength: 103 MPa
$ 1727/MT
- Specific Gravity: 1.15 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 3.0 - 14 g/10 min @Load 5.00 kg, Temperature 250 °C
- Tensile Strength at Break: 56.5 MPa
- Tensile Strength, Yield: 57.9 MPa
$ 1993/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage: 0.018 - 0.022 cm/cm
- Melt Flow: 5.0 - 9.0 g/10 min
- Tensile Strength at Break: 61.4 MPa
- Tensile Strength, Yield: 61.4 MPa
$ 1585/MT
- Specific Gravity: 1.12 g/cc
- Linear Mold Shrinkage: 0.0060 - 0.0090 cm/cm
- Melt Flow: 25 - 50 g/10 min @Load 11.6 kg, Temperature 250 °C
- Hardness, Rockwell R: 121
- Tensile Strength at Break: 62.1 MPa
$ 1465/MT
- Specific Gravity: 1.51 g/cc
- Water Absorption: 0.16 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 0.90 %
- Linear Mold Shrinkage: 0.0010 - 0.0040 cm/cm
- Melt Flow: 5.0 - 22 g/10 min @Load 6.70 kg, Temperature 337 °C
$ 1513/MT
- Specific Gravity: 1.42 g/cc
- Linear Mold Shrinkage: 0.018 - 0.021 cm/cm
- Melt Flow: 1.0 - 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 67.6 MPa
- Tensile Strength, Yield: 67.6 MPa
$ 2228/MT
- Specific Gravity: 1.42 g/cc
- Linear Mold Shrinkage: 0.018 - 0.021 cm/cm
- Melt Flow: 14 - 16 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 67.6 MPa
- Tensile Strength, Yield: 67.6 MPa
$ 1971/MT
- Density: 1.42 g/cc
- Linear Mold Shrinkage: 0.018 - 0.021 cm/cm
- Melt Flow: 14 - 16 g/10 min
- Tensile Strength at Break: 67.6 MPa
- Tensile Strength, Yield: 67.6 MPa
$ 2438/MT
- Specific Gravity: 1.50 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm
- Melt Flow: 4.0 - 12 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength at Break: 117 MPa
- Tensile Strength, Yield: 117 MPa
$ 1620/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 15 - 35 g/10 min @Load 5.00 kg, Temperature 250 °C
- Tensile Strength at Break: 62.1 MPa
- Tensile Strength, Yield: 62.1 MPa
$ 2112/MT
- Specific Gravity: 1.05 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 3.0 - 14 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 110
- Tensile Strength at Break: 39.3 MPa
$ 1725/MT
- Specific Gravity: 1.22 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
- Tensile Strength at Break: 131 MPa
- Tensile Strength, Yield: 131 MPa
- Flexural Strength: 165 MPa
$ 1681/MT
- Specific Gravity: 1.43 g/cc
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm
- Melt Flow: 3.0 - 12 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 124 MPa
- Tensile Strength, Yield: 124 MPa
$ 2413/MT
- Specific Gravity: 1.49 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0090 cm/cm
- Tensile Strength at Break: 131 MPa
- Tensile Strength, Yield: 131 MPa
- Flexural Strength: 179 MPa
$ 1831/MT
- Specific Gravity: 1.15 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Flow: 15 - 35 g/10 min @Load 5.00 kg, Temperature 250 °C
- Tensile Strength at Break: 57.9 MPa
- Tensile Strength, Yield: 59.3 MPa
$ 2032/MT
- Specific Gravity: 1.14 g/cc
- Linear Mold Shrinkage: 0.012 - 0.018 cm/cm
- Tensile Strength at Break: 86.2 MPa
- Tensile Strength, Yield: 86.2 MPa
- Flexural Strength: 121 MPa
$ 1482/MT
- Density: 1.06 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 4.0 - 9.0 g/10 min
- Tensile Strength at Break: 55.2 MPa
- Tensile Strength, Yield: 48.3 MPa
$ 1869/MT
- Specific Gravity: 1.19 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 9.0 - 16 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 53.8 MPa
- Tensile Strength, Yield: 51.7 MPa
$ 1641/MT
- Specific Gravity: 1.48 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0090 cm/cm
- Tensile Strength at Break: 131 MPa
- Tensile Strength, Yield: 131 MPa
- Flexural Strength: 179 MPa
$ 1501/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm
- Tensile Strength at Break: 86.2 MPa
- Tensile Strength, Yield: 86.2 MPa
- Flexural Strength: 123 MPa
$ 1541/MT
- Specific Gravity: 1.26 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.010 cm/cm
- Melt Flow: 9.0 - 16 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 56.9 MPa
- Tensile Strength, Yield: 56.9 MPa
$ 1454/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 5.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 1778/MT
- Specific Gravity: 1.07 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 0.10 - 4.0 g/10 min @Load 11.6 kg, Temperature 250 °C
- Tensile Strength at Break: 63.4 MPa
- Tensile Strength, Yield: 65.5 MPa
$ 1713/MT
- Specific Gravity: 1.26 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm
- Melt Flow: 8.0 - 16 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 65.5 MPa
- Tensile Strength, Yield: 55.8 MPa
$ 1543/MT
- Specific Gravity: 1.27 g/cc
- Moisture Absorption at Equilibrium: 0.60 %
- Water Absorption at Saturation: 1.1 % @Temperature 22.8 °C
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 5.0 - 30 g/10 min @Load 6.70 kg, Temperature 337 °C
$ 1482/MT
- Specific Gravity: 1.41 g/cc
- Linear Mold Shrinkage: 0.018 - 0.022 cm/cm
- Melt Flow: 1.0 - 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 61.4 MPa
- Tensile Strength, Yield: 61.4 MPa
$ 1464/MT
- Specific Gravity: 1.41 g/cc
- Linear Mold Shrinkage: 0.018 - 0.022 cm/cm
- Melt Flow: 6.0 - 12 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 61.4 MPa
- Tensile Strength, Yield: 61.4 MPa
$ 1488/MT
- Specific Gravity: 1.31 g/cc
- Linear Mold Shrinkage: 0.016 - 0.022 cm/cm
- Melt Flow: 12 - 25 g/10 min @Load 2.16 kg, Temperature 250 °C
- Hardness, Rockwell M: 78
- Hardness, Rockwell R: 117
$ 1618/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.010 cm/cm
- Tensile Strength at Break: 96.5 MPa
- Tensile Strength, Yield: 96.5 MPa
- Flexural Strength: 159 MPa
$ 2174/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 14 - 20 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 1493/MT
- Specific Gravity: 1.30 g/cc
- Linear Mold Shrinkage: 0.011 - 0.015 cm/cm
- Melt Flow: 8.0 - 16 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength at Break: 49.6 MPa
- Tensile Strength, Yield: 49.6 MPa
$ 1616/MT
- Specific Gravity: 1.16 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.010 cm/cm
- Melt Flow: 2.0 - 8.0 g/10 min @Load 3.80 kg, Temperature 300 °C
- Tensile Strength at Break: 86.2 MPa
- Tensile Strength, Yield: 86.2 MPa
$ 1530/MT
- Specific Gravity: 1.22 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
- Tensile Strength at Break: 110 MPa
- Tensile Strength, Yield: 110 MPa
- Flexural Strength: 159 MPa
$ 1771/MT
- Density: 1.07 g/cc
- Linear Mold Shrinkage: 0.017 - 0.020 cm/cm
- Tensile Strength at Break: 41.4 MPa
- Tensile Strength, Yield: 41.4 MPa
- Flexural Strength: 51.7 MPa
$ 1445/MT
- Specific Gravity: 1.19 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 5.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 55.2 MPa
- Tensile Strength, Yield: 54.5 MPa
$ 1606/MT
- Density: 1.38 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm
- Tensile Strength at Break: 183 MPa
- Tensile Strength, Yield: 183 MPa
- Flexural Strength: 248 MPa
$ 2088/MT
- Specific Gravity: 1.49 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0090 cm/cm
- Tensile Strength at Break: 131 MPa
- Tensile Strength, Yield: 131 MPa
- Flexural Strength: 179 MPa
$ 1678/MT
- Specific Gravity: 1.43 g/cc
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm
- Melt Flow: 1.0 - 9.0 g/10 min @Load 11.6 kg, Temperature 250 °C
- Hardness, Rockwell M: 90
- Tensile Strength at Break: 126 MPa
$ 2464/MT
- Specific Gravity: 1.50 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm
- Tensile Strength at Break: 200 MPa
- Tensile Strength, Yield: 200 MPa
- Flexural Strength: 276 MPa
$ 1486/MT
- Specific Gravity: 1.26 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm
- Melt Flow: 8.0 - 16 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 65.5 MPa
- Tensile Strength, Yield: 55.8 MPa
$ 1933/MT
- Specific Gravity: 1.58 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0090 cm/cm
- Tensile Strength at Break: 219 MPa
- Tensile Strength, Yield: 219 MPa
- Flexural Strength: 318.9 MPa
$ 1483/MT
- Specific Gravity: 1.07 g/cc
- Linear Mold Shrinkage: 0.017 - 0.020 cm/cm
- Tensile Strength at Break: 50.3 MPa
- Tensile Strength, Yield: 51.7 MPa
- Flexural Strength: 62.1 MPa
$ 1651/MT
- Specific Gravity: 1.22 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 4.0 - 16 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 100
- Tensile Strength at Break: 37.9 MPa
$ 1446/MT
- Specific Gravity: 1.48 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0090 cm/cm
- Tensile Strength at Break: 131 MPa
- Tensile Strength, Yield: 131 MPa
- Flexural Strength: 179 MPa
$ 1507/MT
- Specific Gravity: 1.54 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0090 cm/cm
- Tensile Strength at Break: 207 MPa
- Tensile Strength, Yield: 207 MPa
- Flexural Strength: 193 MPa
$ 2346/MT
- Specific Gravity: 1.32 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm
- Tensile Strength at Break: 177 MPa
- Tensile Strength, Yield: 177 MPa
- Flexural Strength: 265.1 MPa
$ 1856/MT
- Specific Gravity: 1.41 g/cc
- Linear Mold Shrinkage: 0.018 - 0.022 cm/cm
- Melt Flow: 6.0 - 12 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 61.4 MPa
- Tensile Strength, Yield: 61.4 MPa
$ 1909/MT
- Specific Gravity: 1.21 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 14 - 20 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 1874/MT
- Specific Gravity: 1.57 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Flow: 5.0 - 15 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength at Break: 107 MPa
- Tensile Strength, Yield: 107 MPa
$ 1585/MT
- Specific Gravity: 1.12 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm
- Melt Flow: 5.0 - 10 g/10 min @Load 11.6 kg, Temperature 250 °C
- Tensile Strength at Break: 68.9 MPa
- Tensile Strength, Yield: 68.9 MPa
$ 1952/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 14 - 20 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 62.1 MPa
- Tensile Strength, Yield: 62.1 MPa
$ 1774/MT
- Specific Gravity: 1.49 g/cc
- Linear Mold Shrinkage: 0.010 - 0.015 cm/cm
- Melt Flow: 1.0 - 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 48.3 MPa
- Tensile Strength, Yield: 48.3 MPa
$ 2073/MT
- Specific Gravity: 1.21 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 14 - 20 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 2170/MT
- Density: 1.49 g/cc
- Linear Mold Shrinkage: 0.0070 - 0.010 cm/cm
- Tensile Strength at Break: 96.5 MPa
- Tensile Strength, Yield: 96.5 MPa
- Flexural Strength: 159 MPa
$ 1890/MT
- Specific Gravity: 1.49 g/cc
- Linear Mold Shrinkage: 0.0070 - 0.010 cm/cm
- Tensile Strength at Break: 89.6 MPa
- Tensile Strength, Yield: 89.6 MPa
- Flexural Strength: 128 MPa
$ 1525/MT
- Specific Gravity: 1.05 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 12 - 18 g/10 min @Load 11.6 kg, Temperature 250 °C
- Hardness, Rockwell R: 114
- Tensile Strength at Break: 43.4 MPa
$ 2305/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 14 - 20 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 1879/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
- Melt Flow: 40 - 60 g/10 min @Load 5.00 kg, Temperature 250 °C
- Tensile Strength at Break: 56.5 MPa
- Tensile Strength, Yield: 57.9 MPa
$ 1792/MT
- Specific Gravity: 1.13 g/cc
- Linear Mold Shrinkage: 0.0080 - 0.012 cm/cm
- Tensile Strength at Break: 89.6 MPa
- Tensile Strength, Yield: 89.6 MPa
- Flexural Strength: 108 MPa
$ 1663/MT
- Specific Gravity: 1.47 g/cc
- Linear Mold Shrinkage: 0.018 - 0.021 cm/cm
- Melt Flow: 7.0 - 13 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 58.6 MPa
- Tensile Strength, Yield: 58.6 MPa
$ 1845/MT
- Specific Gravity: 1.52 g/cc
- Linear Mold Shrinkage: 0.0060 - 0.0090 cm/cm
- Melt Flow: 2.0 - 8.0 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength at Break: 86.2 MPa
- Tensile Strength, Yield: 86.2 MPa
$ 2507/MT
- Specific Gravity: 1.29 g/cc
- Linear Mold Shrinkage: 0.0010 - 0.0040 cm/cm
- Melt Flow: 1.0 - 10 g/10 min @Load 5.00 kg, Temperature 250 °C
- Tensile Strength at Break: 82.7 MPa
- Tensile Strength, Yield: 82.7 MPa
$ 1584/MT
- Specific Gravity: 1.21 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 5.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 2552/MT
- Specific Gravity: 1.25 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 1.0 - 4.0 g/10 min @Load 3.80 kg, Temperature 300 °C
- Tensile Strength at Break: 114 MPa
- Tensile Strength, Yield: 114 MPa
$ 1620/MT
- Specific Gravity: 1.10 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 35 - 50 g/10 min @Load 11.6 kg, Temperature 250 °C
- Hardness, Rockwell R: 117
- Tensile Strength at Break: 46.9 MPa
$ 2386/MT
- Specific Gravity: 1.23 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm
- Melt Flow: 1.0 - 8.0 g/10 min @Load 11.6 kg, Temperature 250 °C
- Hardness, Rockwell R: 106
- Tensile Strength at Break: 96.5 MPa
$ 1758/MT
- Density: 1.33 g/cc
- Linear Mold Shrinkage: 0.010 - 0.014 cm/cm
- Melt Flow: 8.0 - 15 g/10 min
- Tensile Strength at Break: 37.9 MPa
- Tensile Strength, Yield: 37.9 MPa
$ 2523/MT
- Specific Gravity: 1.19 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 9.0 - 16 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell L: 89
- Hardness, Rockwell R: 121
$ 1877/MT
- Specific Gravity: 1.65 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0090 cm/cm
- Melt Flow: 1.0 - 5.0 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength at Break: 114 MPa
- Tensile Strength, Yield: 114 MPa
$ 1512/MT
- Specific Gravity: 1.10 g/cc
- Linear Mold Shrinkage: 0.0010 - 0.0040 cm/cm
- Melt Flow: 0.10 - 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Tensile Strength at Break: 46.2 MPa
- Tensile Strength, Yield: 47.6 MPa
$ 1599/MT
- Specific Gravity: 1.26 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm
- Melt Flow: 8.0 - 16 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 65.5 MPa
- Tensile Strength, Yield: 55.8 MPa
$ 2290/MT
- Density: 1.19 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 5.0 - 10 g/10 min
- Tensile Strength at Break: 53.8 MPa
- Tensile Strength, Yield: 53.8 MPa
$ 1505/MT
- Specific Gravity: 1.50 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm
- Tensile Strength at Break: 200 MPa
- Tensile Strength, Yield: 200 MPa
- Flexural Strength: 276 MPa
$ 1870/MT
- Specific Gravity: 1.21 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 5.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 2236/MT
- Density: 1.34 g/cc
- Linear Mold Shrinkage: 0.010 - 0.014 cm/cm
- Melt Flow: 3.0 - 9.0 g/10 min
- Tensile Strength at Break: 44.8 MPa
- Tensile Strength, Yield: 44.8 MPa
$ 1445/MT
- Specific Gravity: 1.22 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 14 - 20 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 55.2 MPa
- Tensile Strength, Yield: 55.2 MPa
$ 2421/MT
- Specific Gravity: 1.49 g/cc
- Linear Mold Shrinkage: 0.0070 - 0.010 cm/cm
- Tensile Strength at Break: 96.5 MPa
- Tensile Strength, Yield: 96.5 MPa
- Flexural Strength: 159 MPa
$ 1520/MT
- Density: 1.09 g/cc
- Linear Mold Shrinkage: 0.016 - 0.020 cm/cm
- Tensile Strength at Break: 62.1 MPa
- Tensile Strength, Yield: 62.1 MPa
- Flexural Strength: 75.8 MPa
$ 1883/MT
- Specific Gravity: 1.19 g/cc
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm
- Melt Flow: 2.0 - 5.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 74.12 MPa
- Tensile Strength, Yield: 66.2 MPa
$ 1488/MT
- Specific Gravity: 1.65 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0080 cm/cm
- Tensile Strength at Break: 159 MPa
- Tensile Strength, Yield: 159 MPa
- Flexural Strength: 200 MPa
$ 2227/MT
- Specific Gravity: 1.09 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 20 - 40 g/10 min @Load 11.6 kg, Temperature 250 °C
- Hardness, Rockwell R: 115
- Tensile Strength at Break: 49.0 MPa
$ 1556/MT
- Specific Gravity: 1.24 g/cc
- Linear Mold Shrinkage: 0.013 - 0.018 cm/cm
- Melt Flow: 6.0 - 12 g/10 min @Load 2.16 kg, Temperature 265 °C
- Tensile Strength at Break: 42.4 MPa
- Tensile Strength, Yield: 42.4 MPa
$ 1471/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 5.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 1461/MT
- Specific Gravity: 1.10 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Flow: 2.0 - 10 g/10 min @Load 11.6 kg, Temperature 250 °C
- Tensile Strength at Break: 62.1 MPa
- Tensile Strength, Yield: 63.8 MPa
$ 2271/MT
- Specific Gravity: 1.35 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Flow: 5.0 - 10 g/10 min @Load 2.16 kg, Temperature 265 °C
- Tensile Strength at Break: 72.4 MPa
- Tensile Strength, Yield: 72.4 MPa
$ 1571/MT
- Specific Gravity: 1.31 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm
- Melt Flow: 5.0 - 12 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 68.9 MPa
- Tensile Strength, Yield: 65.5 MPa
$ 1458/MT
- Density: 1.18 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm
- Tensile Strength at Break: 96.5 MPa
- Tensile Strength, Yield: 96.5 MPa
- Flexural Strength: 138 MPa
$ 1892/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Flow: 3.0 - 14 g/10 min @Load 5.00 kg, Temperature 250 °C
- Tensile Strength at Break: 60.0 MPa
- Tensile Strength, Yield: 64.8 MPa
$ 2231/MT
- Specific Gravity: 1.13 g/cc
- Linear Mold Shrinkage: 0.0080 - 0.012 cm/cm
- Tensile Strength at Break: 89.6 MPa
- Tensile Strength, Yield: 89.6 MPa
- Flexural Strength: 108 MPa
$ 1518/MT
- Specific Gravity: 1.33 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 1.0 - 4.0 g/10 min @Load 3.80 kg, Temperature 300 °C
- Tensile Strength at Break: 148 MPa
- Tensile Strength, Yield: 148 MPa
$ 1885/MT
- Specific Gravity: 1.38 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm
- Tensile Strength at Break: 193 MPa
- Tensile Strength, Yield: 193 MPa
- Flexural Strength: 290 MPa
$ 1486/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 5.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 1648/MT
- Specific Gravity: 1.28 g/cc
- Linear Mold Shrinkage: 0.0010 - 0.0040 cm/cm
- Melt Flow: 1.0 - 8.0 g/10 min @Load 11.6 kg, Temperature 250 °C
- Hardness, Rockwell L: 108
- Tensile Strength at Break: 103 MPa
$ 1602/MT
- Specific Gravity: 1.05 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 3.0 - 14 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 110
- Tensile Strength at Break: 39.3 MPa
$ 1523/MT
- Specific Gravity: 1.26 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm
- Melt Flow: 5.0 - 12 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 65.5 MPa
- Tensile Strength, Yield: 55.8 MPa
$ 1907/MT
- Specific Gravity: 1.21 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 5.0 - 12 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 58.6 MPa
- Tensile Strength, Yield: 55.8 MPa
$ 1481/MT
- Specific Gravity: 1.25 g/cc
- Linear Mold Shrinkage: 0.0060 - 0.0090 cm/cm
- Melt Flow: 5.0 - 12 g/10 min @Load 2.16 kg, Temperature 265 °C
- Tensile Strength at Break: 48.3 MPa
- Tensile Strength, Yield: 50.3 MPa
$ 1986/MT
- Specific Gravity: 1.06 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 20 - 30 g/10 min @Load 11.6 kg, Temperature 250 °C
- Tensile Strength at Break: 34.5 MPa
- Tensile Strength, Yield: 34.5 MPa
$ 1466/MT
- Specific Gravity: 1.22 g/cc
- Linear Mold Shrinkage: 0.0060 - 0.0090 cm/cm
- Linear Mold Shrinkage: 0.0070 - 0.010 cm/cm
- Melt Flow: 6.0 - 12 g/10 min @Load 2.16 kg, Temperature 265 °C
- Tensile Strength at Break: 50.3 MPa
$ 1815/MT
- Specific Gravity: 1.32 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0090 cm/cm
- Tensile Strength at Break: 162 MPa
- Tensile Strength, Yield: 162 MPa
- Flexural Strength: 255 MPa
$ 1854/MT
- Specific Gravity: 1.05 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 12 - 18 g/10 min @Load 11.6 kg, Temperature 250 °C
- Tensile Strength at Break: 43.4 MPa
- Tensile Strength, Yield: 46.9 MPa
$ 1460/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 9.0 - 16 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 1833/MT
- Specific Gravity: 1.05 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 18 - 24 g/10 min @Load 11.6 kg, Temperature 250 °C
- Tensile Strength at Break: 43.4 MPa
- Tensile Strength, Yield: 46.9 MPa
$ 1662/MT
- Specific Gravity: 1.75 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Flow: 2.0 - 8.0 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength at Break: 96.5 MPa
- Tensile Strength, Yield: 96.5 MPa
$ 2216/MT
- Specific Gravity: 1.62 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Flow: 2.0 - 10 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength at Break: 72.4 MPa
- Tensile Strength, Yield: 72.4 MPa
$ 1586/MT
- Specific Gravity: 1.24 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 10 - 20 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 58.6 MPa
- Tensile Strength, Yield: 58.6 MPa
$ 1486/MT
- Specific Gravity: 1.17 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm
- Melt Flow: 1.0 - 8.0 g/10 min @Load 11.6 kg, Temperature 250 °C
- Hardness, Rockwell L: 105
- Tensile Strength at Break: 82.7 MPa
$ 1806/MT
- Specific Gravity: 1.64 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm
- Melt Flow: 8.0 - 20 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength at Break: 110 MPa
- Tensile Strength, Yield: 110 MPa
$ 1492/MT
- Density: 1.22 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm
- Melt Flow: 5.0 - 15 g/10 min
- Tensile Strength at Break: 55.2 MPa
- Tensile Strength, Yield: 54.5 MPa
$ 1833/MT
- Specific Gravity: 1.31 g/cc
- Linear Mold Shrinkage: 0.0010 - 0.0040 cm/cm
- Melt Flow: 1.0 - 8.0 g/10 min @Load 11.6 kg, Temperature 250 °C
- Hardness, Rockwell R: 108
- Tensile Strength at Break: 110 MPa
$ 1512/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 14 - 20 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 62.1 MPa
- Tensile Strength, Yield: 62.1 MPa
$ 2165/MT
- Specific Gravity: 1.14 g/cc
- Linear Mold Shrinkage: 0.012 - 0.018 cm/cm
- Tensile Strength at Break: 82.7 MPa
- Tensile Strength, Yield: 82.7 MPa
- Flexural Strength: 117 MPa
$ 1757/MT
- Specific Gravity: 1.50 g/cc
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm
- Melt Flow: 2.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 165 MPa
- Tensile Strength, Yield: 165 MPa
$ 1967/MT
- Specific Gravity: 1.06 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 4.0 - 9.0 g/10 min @Load 11.6 kg, Temperature 250 °C
- Tensile Strength at Break: 62.1 MPa
- Tensile Strength, Yield: 64.1 MPa
$ 1641/MT
- Specific Gravity: 1.64 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm
- Melt Flow: 25 - 35 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength at Break: 138 MPa
- Tensile Strength, Yield: 138 MPa
$ 1676/MT
- Specific Gravity: 1.22 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
- Tensile Strength at Break: 110 MPa
- Tensile Strength, Yield: 110 MPa
- Flexural Strength: 159 MPa
$ 1548/MT
- Specific Gravity: 1.15 g/cc
- Linear Mold Shrinkage: 0.0010 - 0.0040 cm/cm
- Melt Flow: 0.10 - 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Tensile Strength at Break: 68.9 MPa
- Tensile Strength, Yield: 68.9 MPa
$ 1653/MT
- Specific Gravity: 1.26 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
- Melt Flow: 8.0 - 18 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength at Break: 72.4 MPa
- Tensile Strength, Yield: 72.4 MPa
$ 1584/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 14 - 20 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 1959/MT
- Specific Gravity: 1.62 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Flow: 9.0 - 20 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength at Break: 114 MPa
- Tensile Strength, Yield: 114 MPa
$ 1495/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 18 - 30 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 62.1 MPa
- Tensile Strength, Yield: 62.1 MPa
$ 1900/MT
- Density: 1.35 g/cc
- Linear Mold Shrinkage: 0.0010 - 0.0040 cm/cm
- Melt Flow: 4.0 - 10 g/10 min
- Tensile Strength at Break: 107 MPa
- Flexural Strength: 112 MPa
$ 1507/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm
- Melt Flow: 1.0 - 5.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 1755/MT
- Specific Gravity: 1.08 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 15 - 40 g/10 min @Load 11.6 kg, Temperature 250 °C
- Hardness, Rockwell R: 113
- Tensile Strength at Break: 46.9 MPa
$ 1677/MT
- Specific Gravity: 1.30 g/cc
- Linear Mold Shrinkage: 0.0070 - 0.010 cm/cm
- Melt Flow: 2.0 - 10 g/10 min @Load 2.16 kg, Temperature 265 °C
- Tensile Strength at Break: 62.1 MPa
- Tensile Strength, Yield: 62.1 MPa
$ 1953/MT
- Specific Gravity: 1.42 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0080 cm/cm
- Tensile Strength at Break: 190 MPa
- Tensile Strength, Yield: 190 MPa
- Flexural Strength: 269 MPa
$ 1618/MT
- Specific Gravity: 1.21 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 5.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 1705/MT
- Specific Gravity: 1.22 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm
- Melt Flow: 5.0 - 15 g/10 min @Load 2.16 kg, Temperature 265 °C
- Tensile Strength at Break: 54.5 MPa
- Tensile Strength, Yield: 55.2 MPa
$ 1618/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 5.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 1544/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 9.0 - 16 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 1710/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 14 - 20 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 1667/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 20 - 30 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 1821/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 9.0 - 16 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 1512/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 18 - 30 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 1904/MT
- Specific Gravity: 1.21 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 9.0 - 16 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 1623/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 18 - 30 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 1710/MT
- Specific Gravity: 1.09 g/cc
- Linear Mold Shrinkage: 0.0060 - 0.0090 cm/cm
- Melt Flow: 25 - 45 g/10 min @Load 11.6 kg, Temperature 250 °C
- Tensile Strength at Break: 51.7 MPa
- Tensile Strength, Yield: 52.4 MPa
$ 1815/MT
- Specific Gravity: 1.42 g/cc
- Water Absorption: 0.19 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 1.1 %
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm
- Melt Flow: 5.0 - 22 g/10 min @Load 6.70 kg, Temperature 337 °C
$ 1470/MT
- Specific Gravity: 1.09 g/cc
- Linear Mold Shrinkage: 0.016 - 0.020 cm/cm
- Tensile Strength at Break: 62.1 MPa
- Tensile Strength, Yield: 62.1 MPa
- Flexural Strength: 75.8 MPa
$ 1575/MT
- Specific Gravity: 1.58 g/cc
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm
- Melt Flow: 0.30 - 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 110 MPa
- Tensile Strength, Yield: 48.3 MPa
$ 1445/MT
- Specific Gravity: 1.06 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 2.0 - 7.0 g/10 min @Load 11.6 kg, Temperature 250 °C
- Tensile Strength at Break: 60.0 MPa
- Tensile Strength, Yield: 62.1 MPa
$ 1861/MT
- Specific Gravity: 1.21 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 9.0 - 16 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 1829/MT
- Specific Gravity: 1.40 g/cc
- Linear Mold Shrinkage: 0.0060 - 0.010 cm/cm
- Melt Flow: 8.0 - 16 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength at Break: 89.6 MPa
- Tensile Strength, Yield: 89.6 MPa
$ 1466/MT
- Specific Gravity: 1.21 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 14 - 20 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 1739/MT
- Specific Gravity: 1.61 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm
- Melt Flow: 5.0 - 10 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength at Break: 124 MPa
- Tensile Strength, Yield: 124 MPa
$ 1513/MT
- Specific Gravity: 1.05 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 6.0 - 10 g/10 min @Load 11.6 kg, Temperature 250 °C
- Hardness, Rockwell R: 118
- Tensile Strength at Break: 53.4 MPa
$ 1910/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 9.0 - 16 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 1601/MT
- Specific Gravity: 1.21 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 9.0 - 16 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 1941/MT
- Specific Gravity: 1.45 g/cc
- Linear Mold Shrinkage: 0.0060 - 0.010 cm/cm
- Melt Flow: 10 - 20 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength at Break: 89.6 MPa
- Tensile Strength, Yield: 89.6 MPa
$ 1783/MT
- Specific Gravity: 1.22 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm
- Melt Flow: 15 - 20 g/10 min @Load 2.16 kg, Temperature 265 °C
- Tensile Strength at Break: 51.7 MPa
- Tensile Strength, Yield: 51.7 MPa
$ 1928/MT
- Specific Gravity: 1.50 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Flow: 5.0 - 15 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength at Break: 107 MPa
- Tensile Strength, Yield: 107 MPa
$ 1869/MT
- Density: 1.06 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 4.0 - 8.0 g/10 min
- Tensile Strength at Break: 64.1 MPa
- Tensile Strength, Yield: 62.1 MPa
$ 1471/MT
- Specific Gravity: 1.44 g/cc
- Linear Mold Shrinkage: 0.0060 - 0.010 cm/cm
- Melt Flow: 10 - 15 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength at Break: 48.3 MPa
- Tensile Strength, Yield: 51.0 MPa
$ 1578/MT
- Specific Gravity: 1.08 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm
- Melt Flow: 0.50 - 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Tensile Strength at Break: 42.7 MPa
- Tensile Strength, Yield: 45.5 MPa
$ 1506/MT
- Specific Gravity: 1.31 g/cc
- Linear Mold Shrinkage: 0.016 - 0.022 cm/cm
- Melt Flow: 12 - 20 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength at Break: 48.3 MPa
- Tensile Strength, Yield: 48.3 MPa
$ 1927/MT
- Specific Gravity: 1.22 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
- Tensile Strength at Break: 131 MPa
- Tensile Strength, Yield: 131 MPa
- Flexural Strength: 179 MPa
$ 1712/MT
- Specific Gravity: 1.24 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Flow: 5.0 - 12 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 56.5 MPa
- Tensile Strength, Yield: 56.5 MPa
$ 1450/MT
- Specific Gravity: 1.14 g/cc
- Linear Mold Shrinkage: 0.012 - 0.018 cm/cm
- Tensile Strength at Break: 82.7 MPa
- Tensile Strength, Yield: 82.7 MPa
- Flexural Strength: 117 MPa
$ 1590/MT
- Specific Gravity: 1.25 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 5.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 58.6 MPa
- Tensile Strength, Yield: 58.6 MPa
$ 1452/MT
- Specific Gravity: 1.35 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0080 cm/cm
- Tensile Strength at Break: 128 MPa
- Tensile Strength, Yield: 128 MPa
- Flexural Strength: 200 MPa
$ 1744/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 14 - 20 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 1934/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm
- Melt Flow: 1.0 - 5.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 2398/MT
- Specific Gravity: 1.22 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm
- Melt Flow: 9.0 - 16 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 58.6 MPa
- Tensile Strength, Yield: 58.6 MPa
$ 1821/MT
- Specific Gravity: 1.26 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm
- Melt Flow: 8.0 - 16 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 65.5 MPa
- Tensile Strength, Yield: 55.8 MPa
$ 1843/MT
- Specific Gravity: 1.09 g/cc
- Linear Mold Shrinkage: 0.016 - 0.020 cm/cm
- Tensile Strength at Break: 62.1 MPa
- Tensile Strength, Yield: 62.1 MPa
- Flexural Strength: 75.8 MPa
$ 2560/MT
- Specific Gravity: 1.21 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 4.0 - 11 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 56.9 MPa
- Tensile Strength, Yield: 55.2 MPa
$ 1449/MT
- Specific Gravity: 1.13 g/cc
- Linear Mold Shrinkage: 0.011 - 0.015 cm/cm
- Tensile Strength at Break: 75.8 MPa
- Tensile Strength, Yield: 75.8 MPa
- Flexural Strength: 106 MPa
$ 1643/MT
- Specific Gravity: 1.30 g/cc
- Linear Mold Shrinkage: 0.016 - 0.022 cm/cm
- Melt Flow: 10 - 20 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength at Break: 46.9 MPa
- Tensile Strength, Yield: 46.9 MPa
$ 1479/MT
- Density: 1.38 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm
- Tensile Strength at Break: 193 MPa
- Tensile Strength, Yield: 193 MPa
- Flexural Strength: 290 MPa
$ 1944/MT
- Density: 1.42 g/cc
- Linear Mold Shrinkage: 0.018 - 0.021 cm/cm
- Melt Flow: 24 - 26 g/10 min
- Tensile Strength at Break: 67.6 MPa
- Tensile Strength, Yield: 67.6 MPa
$ 1490/MT
- Specific Gravity: 1.43 g/cc
- Linear Mold Shrinkage: 0.0060 - 0.0090 cm/cm
- Melt Flow: 8.0 - 20 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength at Break: 123.8 MPa
- Tensile Strength, Yield: 123.8 MPa
$ 1841/MT
- Specific Gravity: 1.06 g/cc
- Linear Mold Shrinkage: 0.0010 - 0.0040 cm/cm
- Tensile Strength at Break: 56.5 MPa
- Tensile Strength, Yield: 56.5 MPa
- Flexural Strength: 49.0 MPa
$ 1455/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm
- Melt Flow: 3.0 - 7.0 g/10 min
- Tensile Strength at Break: 68.9 MPa
- Tensile Strength, Yield: 68.9 MPa
$ 1704/MT
- Specific Gravity: 1.08 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 25 - 50 g/10 min @Load 11.6 kg, Temperature 250 °C
- Hardness, Rockwell R: 118
- Tensile Strength at Break: 41.4 MPa
$ 2102/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 18 - 30 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 62.1 MPa
- Tensile Strength, Yield: 62.1 MPa
$ 1483/MT
- Density: 1.09 g/cc
- Linear Mold Shrinkage: 0.014 - 0.020 cm/cm
- Tensile Strength at Break: 62.1 MPa
- Tensile Strength, Yield: 60.0 MPa
- Flexural Strength: 82.7 MPa
$ 1881/MT
- Specific Gravity: 1.15 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 3.0 - 14 g/10 min @Load 5.00 kg, Temperature 250 °C
- Tensile Strength at Break: 56.5 MPa
- Tensile Strength, Yield: 57.9 MPa
$ 1547/MT
- Specific Gravity: 1.08 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 15 - 21 g/10 min @Load 11.6 kg, Temperature 250 °C
- Tensile Strength at Break: 48.3 MPa
- Tensile Strength, Yield: 48.3 MPa
$ 2527/MT
- Specific Gravity: 1.26 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm
- Melt Flow: 5.0 - 12 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 85
- Hardness, Rockwell R: 124
$ 1853/MT
- Density: 1.15 g/cc
- Linear Mold Shrinkage: 0.012 - 0.018 cm/cm
- Tensile Strength at Break: 82.7 MPa
- Tensile Strength, Yield: 82.7 MPa
- Flexural Strength: 103 MPa
$ 2371/MT
- Specific Gravity: 1.04 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 14 - 20 g/10 min @Load 11.6 kg, Temperature 250 °C
- Tensile Strength at Break: 44.8 MPa
- Tensile Strength, Yield: 44.8 MPa
$ 1471/MT
- Specific Gravity: 1.39 g/cc
- Linear Mold Shrinkage: 0.015 - 0.020 cm/cm
- Melt Flow: 10 - 18 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength at Break: 57.2 MPa
- Tensile Strength, Yield: 57.2 MPa
$ 2172/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 14 - 20 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 1775/MT
- Specific Gravity: 1.10 g/cc
- Linear Mold Shrinkage: 0.010 - 0.013 cm/cm
- Melt Flow: 10 - 30 g/10 min @Load 3.80 kg, Temperature 300 °C
- Tensile Strength at Break: 55.2 MPa
- Tensile Strength, Yield: 57.9 MPa
$ 1573/MT
- Specific Gravity: 1.27 g/cc
- Water Absorption: 0.25 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 1.3 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 6.0 - 22 g/10 min @Load 6.70 kg, Temperature 337 °C
$ 2184/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 18 - 30 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 62.1 MPa
- Tensile Strength, Yield: 62.1 MPa
$ 1637/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 18 - 30 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 62.1 MPa
- Tensile Strength, Yield: 62.1 MPa
$ 1453/MT
- Specific Gravity: 1.09 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 15 - 25 g/10 min @Load 11.6 kg, Temperature 250 °C
- Tensile Strength at Break: 53.1 MPa
- Tensile Strength, Yield: 55.2 MPa
$ 1754/MT
- Specific Gravity: 1.34 g/cc
- Linear Mold Shrinkage: 0.010 - 0.014 cm/cm
- Melt Flow: 3.0 - 9.0 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength at Break: 44.8 MPa
- Tensile Strength, Yield: 44.8 MPa
$ 1471/MT
- Specific Gravity: 1.41 g/cc
- Linear Mold Shrinkage: 0.018 - 0.022 cm/cm
- Melt Flow: 22 - 32 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 61.4 MPa
- Tensile Strength, Yield: 61.4 MPa
$ 1570/MT
- Specific Gravity: 1.24 g/cc
- Linear Mold Shrinkage: 0.013 - 0.018 cm/cm
- Melt Flow: 6.0 - 12 g/10 min @Load 2.16 kg, Temperature 265 °C
- Tensile Strength at Break: 44.1 MPa
- Tensile Strength, Yield: 46.2 MPa
$ 1634/MT
- Specific Gravity: 1.30 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Flow: 2.0 - 10 g/10 min @Load 2.16 kg, Temperature 265 °C
- Tensile Strength at Break: 65.5 MPa
- Tensile Strength, Yield: 65.5 MPa
$ 1819/MT
- Specific Gravity: 1.22 g/cc
- Linear Mold Shrinkage: 0.023 - 0.027 cm/cm
- Melt Flow: 2.0 - 8.0 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength at Break: 37.9 MPa
- Tensile Strength, Yield: 37.9 MPa
$ 1561/MT
- Specific Gravity: 1.49 g/cc
- Linear Mold Shrinkage: 0.0070 - 0.010 cm/cm
- Tensile Strength at Break: 96.5 MPa
- Tensile Strength, Yield: 96.5 MPa
- Flexural Strength: 159 MPa
$ 1593/MT
- Specific Gravity: 1.39 g/cc
- Linear Mold Shrinkage: 0.015 - 0.020 cm/cm
- Melt Flow: 10 - 18 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength at Break: 57.2 MPa
- Tensile Strength, Yield: 57.2 MPa
$ 1603/MT
- Specific Gravity: 1.40 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Tensile Strength at Break: 131 MPa
- Elongation at Break: 3.0 %
- Flexural Strength: 190 MPa
$ 1700/MT
- Density: 1.14 g/cc
- Linear Mold Shrinkage: 0.012 - 0.018 cm/cm
- Tensile Strength at Break: 82.7 MPa
- Tensile Strength, Yield: 82.7 MPa
- Flexural Strength: 114 MPa
$ 1608/MT
- Specific Gravity: 1.06 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 4.0 - 8.0 g/10 min @Load 11.6 kg, Temperature 250 °C
- Hardness, Rockwell R: 119
- Tensile Strength at Break: 62.1 MPa
$ 1727/MT
- Specific Gravity: 1.10 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 25 - 35 g/10 min @Load 11.6 kg, Temperature 250 °C
- Tensile Strength at Break: 36.5 MPa
- Tensile Strength, Yield: 36.5 MPa
$ 1457/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 5.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 1997/MT
- Specific Gravity: 1.15 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 3.0 - 14 g/10 min @Load 5.00 kg, Temperature 250 °C
- Tensile Strength at Break: 56.5 MPa
- Tensile Strength, Yield: 57.9 MPa
$ 1491/MT
- Specific Gravity: 1.44 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
- Melt Flow: 1.0 - 8.0 g/10 min @Load 2.16 kg, Temperature 265 °C
- Tensile Strength at Break: 89.6 MPa
- Tensile Strength, Yield: 89.6 MPa
$ 2054/MT
- Specific Gravity: 1.43 g/cc
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm
- Melt Flow: 3.0 - 12 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 124 MPa
- Tensile Strength, Yield: 124 MPa
$ 1935/MT
- Specific Gravity: 1.25 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm
- Melt Flow: 2.0 - 12 g/10 min @Load 5.00 kg, Temperature 250 °C
- Tensile Strength at Break: 72.4 MPa
- Tensile Strength, Yield: 72.4 MPa
$ 2125/MT
- Specific Gravity: 1.26 g/cc
- Linear Mold Shrinkage: 0.0010 - 0.0020 cm/cm
- Melt Flow: 0.10 - 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Tensile Strength at Break: 96.5 MPa
- Tensile Strength, Yield: 96.5 MPa
$ 1735/MT
- Density: 1.22 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
- Tensile Strength at Break: 131 MPa
- Tensile Strength, Yield: 131 MPa
- Flexural Strength: 179 MPa
$ 1623/MT
- Specific Gravity: 1.38 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm
- Tensile Strength at Break: 183 MPa
- Tensile Strength, Yield: 183 MPa
- Flexural Strength: 248 MPa
$ 1530/MT
- Specific Gravity: 1.30 g/cc
- Linear Mold Shrinkage: 0.010 - 0.014 cm/cm
- Melt Flow: 4.0 - 12 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength at Break: 37.9 MPa
- Tensile Strength, Yield: 37.9 MPa
$ 1657/MT
- Specific Gravity: 1.19 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 14 - 20 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell L: 89
- Hardness, Rockwell R: 121
$ 2548/MT
- Specific Gravity: 1.50 g/cc
- Linear Mold Shrinkage: 0.0060 - 0.0090 cm/cm
- Melt Flow: 8.0 - 20 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength at Break: 103 MPa
- Tensile Strength, Yield: 103 MPa
$ 1546/MT
- Specific Gravity: 1.35 g/cc
- Linear Mold Shrinkage: 0.0010 - 0.0040 cm/cm
- Melt Flow: 4.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 117 MPa
- Tensile Strength, Yield: 117 MPa
$ 1459/MT
- Specific Gravity: 1.40 g/cc
- Linear Mold Shrinkage: 0.0060 - 0.010 cm/cm
- Melt Flow: 8.0 - 16 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength at Break: 82.7 MPa
- Tensile Strength, Yield: 84.8 MPa
$ 1481/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 25 - 50 g/10 min @Load 5.00 kg, Temperature 250 °C
- Tensile Strength at Break: 56.5 MPa
- Tensile Strength, Yield: 57.9 MPa
$ 1691/MT
- Specific Gravity: 1.24 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 15 - 25 g/10 min @Load 11.6 kg, Temperature 250 °C
- Hardness, Rockwell R: 121
- Tensile Strength at Break: 61.4 MPa
$ 2175/MT
- Density: 1.13 g/cc
- Linear Mold Shrinkage: 0.011 - 0.015 cm/cm
- Tensile Strength at Break: 75.8 MPa
- Tensile Strength, Yield: 75.8 MPa
- Flexural Strength: 106 MPa
$ 1602/MT
- Density: 1.18 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm
- Tensile Strength at Break: 96.5 MPa
- Tensile Strength, Yield: 96.5 MPa
- Flexural Strength: 138 MPa
$ 1663/MT
- Specific Gravity: 1.06 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 4.0 - 9.0 g/10 min @Load 11.6 kg, Temperature 250 °C
- Hardness, Rockwell R: 119
- Tensile Strength at Break: 48.3 MPa
$ 1503/MT
- Specific Gravity: 1.37 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm
- Melt Flow: 5.0 - 15 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 65.5 MPa
- Tensile Strength, Yield: 55.8 MPa
$ 2083/MT
- Specific Gravity: 1.22 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm
- Melt Flow: 5.0 - 15 g/10 min @Load 2.16 kg, Temperature 265 °C
- Hardness, Rockwell R: 120
- Tensile Strength at Break: 54.5 MPa
$ 1698/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 9.0 - 16 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 2315/MT
- Specific Gravity: 1.15 g/cc
- Linear Mold Shrinkage: 0.012 - 0.018 cm/cm
- Tensile Strength at Break: 82.7 MPa
- Tensile Strength, Yield: 82.7 MPa
- Flexural Strength: 103 MPa
$ 1537/MT
- Specific Gravity: 1.27 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Flow: 5.0 - 12 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 65.5 MPa
- Tensile Strength, Yield: 62.7 MPa
$ 1836/MT
- Density: 1.33 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm
- Tensile Strength at Break: 138 MPa
- Tensile Strength, Yield: 138 MPa
- Flexural Strength: 214 MPa
$ 1882/MT
- Specific Gravity: 1.34 g/cc
- Linear Mold Shrinkage: 0.0010 - 0.0040 cm/cm
- Melt Flow: 1.0 - 10 g/10 min @Load 5.00 kg, Temperature 250 °C
- Tensile Strength at Break: 89.6 MPa
- Tensile Strength, Yield: 89.6 MPa
$ 2155/MT
- Specific Gravity: 1.71 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.012 cm/cm
- Tensile Strength at Break: 227 MPa
- Tensile Strength, Yield: 227 MPa
- Flexural Strength: 341 MPa
$ 1675/MT
- Specific Gravity: 1.14 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 8.0 - 18 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength at Break: 51.7 MPa
- Tensile Strength, Yield: 58.6 MPa
$ 2111/MT
- Specific Gravity: 1.22 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 7.0 - 12 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 55.2 MPa
- Tensile Strength, Yield: 55.2 MPa
$ 1603/MT
- Specific Gravity: 1.37 g/cc
- Linear Mold Shrinkage: 0.0060 - 0.010 cm/cm
- Melt Flow: 10 - 20 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength at Break: 90.3 MPa
- Tensile Strength, Yield: 90.3 MPa
$ 1706/MT
- Specific Gravity: 1.07 g/cc
- Linear Mold Shrinkage: 0.017 - 0.020 cm/cm
- Tensile Strength at Break: 50.3 MPa
- Tensile Strength, Yield: 51.7 MPa
- Flexural Strength: 62.1 MPa
$ 1519/MT
- Specific Gravity: 1.06 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 0.10 - 4.0 g/10 min @Load 11.6 kg, Temperature 250 °C
- Tensile Strength at Break: 58.6 MPa
- Tensile Strength, Yield: 61.4 MPa
$ 1738/MT
- Specific Gravity: 1.42 g/cc
- Linear Mold Shrinkage: 0.018 - 0.021 cm/cm
- Melt Flow: 24 - 26 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 67.6 MPa
- Tensile Strength, Yield: 67.6 MPa
$ 2189/MT
- Specific Gravity: 1.38 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm
- Tensile Strength at Break: 183 MPa
- Tensile Strength, Yield: 183 MPa
- Flexural Strength: 248 MPa
$ 2315/MT
- Specific Gravity: 1.08 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm
- Melt Flow: 0.10 - 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Tensile Strength at Break: 42.7 MPa
- Tensile Strength, Yield: 45.5 MPa
$ 1875/MT
- Specific Gravity: 1.15 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 12 - 30 g/10 min @Load 5.00 kg, Temperature 250 °C
- Tensile Strength at Break: 56.2 MPa
- Tensile Strength, Yield: 57.6 MPa
$ 2034/MT
- Specific Gravity: 1.45 g/cc
- Linear Mold Shrinkage: 0.0060 - 0.0090 cm/cm
- Melt Flow: 10 - 20 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength at Break: 82.7 MPa
- Tensile Strength, Yield: 82.7 MPa
$ 1547/MT
- Specific Gravity: 1.49 g/cc
- Linear Mold Shrinkage: 0.0070 - 0.010 cm/cm
- Tensile Strength at Break: 89.6 MPa
- Tensile Strength, Yield: 89.6 MPa
- Flexural Strength: 128 MPa
$ 1672/MT
- Specific Gravity: 1.52 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Flow: 5.0 - 18 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength at Break: 114 MPa
- Tensile Strength, Yield: 114 MPa
$ 1527/MT
- Specific Gravity: 1.35 g/cc
- Linear Mold Shrinkage: 0.0010 - 0.0040 cm/cm
- Melt Flow: 4.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 117 MPa
- Tensile Strength, Yield: 117 MPa
$ 2151/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
- Melt Flow: 4.0 - 12 g/10 min
- Tensile Strength at Break: 49.0 MPa
- Tensile Strength, Yield: 49.0 MPa
$ 2166/MT
- Specific Gravity: 1.43 g/cc
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm
- Melt Flow: 3.0 - 12 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 124 MPa
- Tensile Strength, Yield: 124 MPa
$ 1681/MT
- Specific Gravity: 1.05 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 3.0 - 14 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 110
- Tensile Strength at Break: 39.3 MPa
$ 2116/MT
- Specific Gravity: 1.02 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 1.0 - 3.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Melt Flow: 7.0 - 11 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength at Break: 37.9 MPa
$ 1831/MT
- Density: 1.50 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm
- Tensile Strength at Break: 200 MPa
- Tensile Strength, Yield: 200 MPa
- Flexural Strength: 276 MPa
$ 2309/MT
- Specific Gravity: 1.33 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm
- Tensile Strength at Break: 141 MPa
- Tensile Strength, Yield: 141 MPa
- Flexural Strength: 204 MPa
$ 2351/MT
- Specific Gravity: 1.21 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 5.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 1499/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.010 cm/cm
- Tensile Strength at Break: 96.5 MPa
- Tensile Strength, Yield: 96.5 MPa
- Flexural Strength: 159 MPa
$ 1456/MT
- Specific Gravity: 1.27 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
- Melt Flow: 8.0 - 18 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength at Break: 68.9 MPa
- Tensile Strength, Yield: 68.9 MPa
$ 1932/MT
- Specific Gravity: 1.07 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 1.0 - 3.0 g/10 min @Load 11.6 kg, Temperature 250 °C
- Tensile Strength at Break: 66.9 MPa
- Tensile Strength, Yield: 70.3 MPa
$ 1797/MT
- Specific Gravity: 1.09 g/cc
- Linear Mold Shrinkage: 0.014 - 0.020 cm/cm
- Tensile Strength at Break: 60.0 MPa
- Tensile Strength, Yield: 62.1 MPa
- Flexural Strength: 82.7 MPa
$ 1625/MT
- Specific Gravity: 1.10 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 4.0 - 8.0 g/10 min @Load 11.6 kg, Temperature 250 °C
- Tensile Strength at Break: 55.2 MPa
- Tensile Strength, Yield: 62.1 MPa
$ 2566/MT
- Specific Gravity: 1.21 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 14 - 20 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 2257/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm
- Melt Flow: 1.0 - 5.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 70
- Hardness, Rockwell R: 118
$ 2297/MT
- Specific Gravity: 1.06 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 4.0 - 9.0 g/10 min @Load 11.6 kg, Temperature 250 °C
- Hardness, Rockwell R: 119
- Tensile Strength at Break: 48.3 MPa
$ 1997/MT
- Specific Gravity: 1.14 g/cc
- Linear Mold Shrinkage: 0.012 - 0.018 cm/cm
- Tensile Strength at Break: 89.6 MPa
- Tensile Strength, Yield: 89.6 MPa
- Flexural Strength: 117 MPa
Delivery Polymer Polymer Resources, LTD
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
crude oil tanker for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.