Polymer Resources PEI-G30 Polyetherimide, 30% Glass Reinforced price 1465 per MT

Physical Properties
Specific Gravity
1.51 g/cc
Water Absorption
0.16 % @Time 86400 sec
Moisture Absorption at Equilibrium
0.90 %
Linear Mold Shrinkage
0.0010 - 0.0040 cm/cm
Melt Flow
5.0 - 22 g/10 min @Load 6.70 kg, Temperature 337 °C

Mechanical Properties
Hardness, Rockwell R
114
Tensile Strength at Break
162 MPa
Tensile Strength, Yield
162 MPa
Elongation at Break
3.0 %
Tensile Modulus
9.31 GPa
Flexural Strength
221 MPa
Flexural Modulus
8.27 GPa
Izod Impact, Notched
0.801 J/cm @Temperature 22.8 °C
Izod Impact, Unnotched
4.27 J/cm @Temperature 22.8 °C

Thermal Properties
CTE, linear, Parallel to Flow
18.0 µm/m-°C @Temperature -20.0 - 150 °C
CTE, linear, Transverse to Flow
41.4 µm/m-°C @Temperature -20.0 - 150 °C
Deflection Temperature at 0.46 MPa (66 psi)
211 °C
Deflection Temperature at 1.8 MPa (264 psi)
210 °C
Vicat Softening Point
227 °C
UL RTI, Electrical
105 °C @Thickness 1.50 mm
UL RTI, Electrical
105 °C @Thickness 3.00 mm
UL RTI, Mechanical with Impact
105 °C @Thickness 1.50 mm
UL RTI, Mechanical with Impact
105 °C @Thickness 3.00 mm
UL RTI, Mechanical without Impact
105 °C @Thickness 1.50 mm
UL RTI, Mechanical without Impact
105 °C @Thickness 3.00 mm
Flammability, UL94
V-0 @Thickness 1.50 mm
Flammability, UL94
V-0 @Thickness 3.00 mm

Electrical Properties
Volume Resistivity
3.00e+16 ohm-cm
Dielectric Constant
3.7 @Frequency 1000 Hz
Dielectric Strength
24.4 kV/mm
Dielectric Strength
29.9 kV/mm
Dissipation Factor
0.0015 @Frequency 1000 Hz
Dissipation Factor
0.0053 @Frequency 1.00e+9 Hz

Processing Properties
Rear Barrel Temperature
332 - 399 °C
Middle Barrel Temperature
338 - 399 °C
Front Barrel Temperature
343 - 399 °C
Melt Temperature
338 - 399 °C
Mold Temperature
107 - 177 °C
Drying Temperature
143 - 149 °C
Dry Time
3.00 - 4.00 hour

Descriptive Properties
Vent
0.001

Alternative products

BASF Ultramid® 8233G HS 33% Glass Filled PA6 (Dry) accurate 85%

$ 1456/MT

Density: 1.136 g/cc
Density: 1.39 g/cc
Water Absorption: 1.1 %
Water Absorption: 6.4 %
Moisture Absorption at Equilibrium: 1.8 %

BASF Ultramid® 8233G HS BK-102 33% Glass Filled PA6 (Dry) accurate 70%

$ 1445/MT

Density: 1.39 g/cc
Water Absorption: 1.1 %
Water Absorption: 6.4 %
Moisture Absorption at Equilibrium: 1.8 %
Relative Viscosity: 2.6 cP

BASF Ultramid® 8333G HI 33% Glass Filled PA6 (Dry) accurate 70%

$ 1528/MT

Density: 1.16 g/cc
Density: 1.34 g/cc
Water Absorption: 0.90 %
Water Absorption: 5.5 %
Moisture Absorption at Equilibrium: 1.5 %

BASF Ultramid® 8333G HI HS BK-102 33% Glass Filled PA6 (Dry) accurate 70%

$ 1876/MT

Density: 1.34 g/cc
Water Absorption: 0.90 %
Water Absorption: 5.5 %
Moisture Absorption at Equilibrium: 1.5 %
Linear Mold Shrinkage: 0.0030 cm/cm

BASF Capron® 8233G 33% Glass-Filled Nylon 6 (Dry) (discontinued **) accurate 70%

$ 1642/MT

Density: 1.38 g/cc
Water Absorption: 1.1 %
Moisture Absorption at Equilibrium: 1.8 %
Water Absorption at Saturation: 6.4 %
Viscosity Measurement: 50

SABIC Innovative Plastics ULTEM 2300F PEI accurate 78%

$ 1614/MT

Specific Gravity: 1.51 g/cc
Density: 1.51 g/cc
Water Absorption: 0.16 % @Time 86400 sec
Moisture Absorption: 0.500 %
Moisture Absorption at Equilibrium: 0.90 %

Celanese Celstran® PA66-GF30-02 Nylon 66, 30% Glass Reinforced accurate 70%

$ 1459/MT

Specific Gravity: 1.36 g/cc
Density: 1.36 g/cc
Linear Mold Shrinkage, Flow: 0.00100 - 0.00200 cm/cm
Linear Mold Shrinkage, Transverse: 0.00300 - 0.00400 cm/cm
Tensile Strength at Break: 170 MPa

BASF Capron® 8333G HI Impact Modified, 33% Glass-Filled Nylon 6 (Dry) (discontinued **) accurate 70%

$ 1782/MT

Density: 1.16 g/cc
Density: 1.34 g/cc
Water Absorption: 0.90 %
Moisture Absorption at Equilibrium: 1.5 %
Water Absorption at Saturation: 5.5 %

SABIC Innovative Plastics LNP Thermocomp XF006S accurate 70%

$ 1486/MT

Specific Gravity: 1.36 g/cc
Density: 1.36 g/cc
Moisture Absorption at Equilibrium: 0.28 %
Moisture Absorption at Equilibrium: 0.22 % @Time 86400 sec
Linear Mold Shrinkage, Transverse: 0.0020 - 0.0040 cm/cm @Time 86400 sec

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lpg ship for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for Polymer Resources PEI-G30 Polyetherimide, 30% Glass Reinforced

Seller from Jakarta – 2021-07-14:

Seller from Jakarta work with company: Solvay, RTP Company, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics)

Price: $1977 per MT

Seller from Kinshasa – 2021-04-05:

Seller from Kinshasa work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1465 per MT

Seller from Guangzhou – 2021-03-10:

Seller from Guangzhou work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2445 per MT