Polymer Resources TP-FRG30 Polybutylene Terephthalate, 30% Glass Reinforced, Flame Retardant price 1959 per MT

Physical Properties
Specific Gravity
1.62 g/cc
Linear Mold Shrinkage
0.0040 - 0.0080 cm/cm
Melt Flow
9.0 - 20 g/10 min @Load 2.16 kg, Temperature 250 °C

Mechanical Properties
Tensile Strength at Break
114 MPa
Tensile Strength, Yield
114 MPa
Flexural Strength
176 MPa
Flexural Modulus
7.24 GPa
Izod Impact, Notched
0.641 J/cm @Temperature 22.8 °C

Thermal Properties
Deflection Temperature at 0.46 MPa (66 psi)
210 °C
Deflection Temperature at 1.8 MPa (264 psi)
199 °C
UL RTI, Electrical
140 °C @Thickness 0.851 mm
UL RTI, Electrical
140 °C @Thickness 1.60 mm
UL RTI, Electrical
140 °C @Thickness 2.30 mm
UL RTI, Electrical
140 °C @Thickness 3.00 mm
UL RTI, Mechanical with Impact
140 °C @Thickness 0.851 mm
UL RTI, Mechanical with Impact
140 °C @Thickness 1.60 mm
UL RTI, Mechanical with Impact
140 °C @Thickness 2.30 mm
UL RTI, Mechanical with Impact
140 °C @Thickness 3.00 mm
UL RTI, Mechanical without Impact
130 °C @Thickness 0.851 mm
UL RTI, Mechanical without Impact
130 °C @Thickness 1.60 mm
UL RTI, Mechanical without Impact
130 °C @Thickness 2.30 mm
UL RTI, Mechanical without Impact
130 °C @Thickness 3.00 mm
Flammability, UL94
V-0 @Thickness 0.850 mm
Flammability, UL94
V-0 - 5VA @Thickness 2.30 mm

Electrical Properties
Volume Resistivity
1.00e+16 ohm-cm
Dielectric Strength
22.8 kV/mm
Comparative Tracking Index
250 - 400 V
Hot Wire Ignition, HWI
15 - 30 sec @Thickness 0.851 mm
Hot Wire Ignition, HWI
30 - 60 sec @Thickness 1.60 mm
Hot Wire Ignition, HWI
30 - 60 sec @Thickness 2.30 mm
Hot Wire Ignition, HWI
60 - 120 sec @Thickness 3.00 mm
High Amp Arc Ignition, HAI
>= 120 arcs @Thickness 0.851 mm
High Amp Arc Ignition, HAI
>= 120 arcs @Thickness 1.60 mm
High Amp Arc Ignition, HAI
>= 120 arcs @Thickness 2.30 mm
High Amp Arc Ignition, HAI
>= 120 arcs @Thickness 3.00 mm
High Voltage Arc-Tracking Rate, HVTR
0.000 - 10.0 mm/min

Processing Properties
Rear Barrel Temperature
238 - 254 °C
Middle Barrel Temperature
243 - 260 °C
Front Barrel Temperature
249 - 266 °C
Melt Temperature
232 - 260 °C
Mold Temperature
71.1 - 87.8 °C
Drying Temperature
116 - 121 °C
Dry Time
3.00 - 4.00 hour

Descriptive Properties
Vent
0.0005

Alternative products

Polymer Resources TPSF-FRG30 Polybutylene Terephthalate, Structural Foam, 30% Glass Reinforced, Flame Retardant accurate 69%

$ 1891/MT

Specific Gravity: 1.62 g/cc
Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm
Melt Flow: 4.0 - 12 g/10 min @Load 2.16 kg, Temperature 250 °C
Tensile Strength at Break: 114 MPa
Tensile Strength, Yield: 114 MPa

ChevronTexaco 46 Heat Transfer Oil accurate 69%

$ 2438/MT

Specific Gravity: 0.3215 g/cc
Specific Gravity: 0.668 g/cc
Specific Gravity: 0.7032 g/cc
Specific Gravity: 0.7416 g/cc
Specific Gravity: 0.7763 g/cc

ACC QM 113 QSI Quantum Silicones 13 Durometer Condensation Cured Moldmaking Material accurate 69%

$ 2505/MT

Specific Gravity: 1.00 g/cc
Specific Gravity: 1.00 g/cc
Specific Gravity: 1.00 g/cc
Specific Gravity: 1.23 g/cc
Specific Gravity: 1.23 g/cc

ChevronTexaco Texatherm® accurate 89%

$ 1472/MT

Specific Gravity: 0.6215 g/cc
Specific Gravity: 0.668 g/cc
Specific Gravity: 0.7032 g/cc
Specific Gravity: 0.7416 g/cc
Specific Gravity: 0.7763 g/cc

ACC QM 2128 QSI Quantum Silicones 28 Durometer Condensation Cure Moldmaking Material accurate 79%

$ 1508/MT

Specific Gravity: 1.00 g/cc
Specific Gravity: 1.00 g/cc
Specific Gravity: 1.00 g/cc
Specific Gravity: 1.00 g/cc
Specific Gravity: 1.13 g/cc

ACC QM 2125 QSI Quantum Silicones 25 Durometer Condensation Cure Moldmaking Material accurate 79%

$ 1692/MT

Specific Gravity: 1.00 g/cc
Specific Gravity: 1.00 g/cc
Specific Gravity: 1.00 g/cc
Specific Gravity: 1.13 g/cc
Specific Gravity: 1.13 g/cc

ChevronTexaco 22 Heat Transfer Oil accurate 69%

$ 2024/MT

Specific Gravity: 0.6083 g/cc
Specific Gravity: 0.655 g/cc
Specific Gravity: 0.6916 g/cc
Specific Gravity: 0.729 g/cc
Specific Gravity: 0.7658 g/cc

ACC QM 107 QSI Quantum Silicones 7 Durometer Condensation Cure Moldmaking Material accurate 69%

$ 1982/MT

Specific Gravity: 0.950 g/cc
Specific Gravity: 1.00 g/cc
Specific Gravity: 1.03 g/cc
Specific Gravity: 1.20 g/cc
Specific Gravity: 1.20 g/cc

SABIC Innovative Plastics Valox® K4560 PBT (Europe-Africa-Middle East) accurate 69%

$ 1620/MT

Specific Gravity: 1.50 g/cc
Filler Content: 30 %
Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm
Linear Mold Shrinkage, Transverse: 0.010 - 0.012 cm/cm @Thickness 3.20 mm
Melt Index of Compound: 12 g/10 min @Load 2.16 kg, Temperature 250 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, sale cargo ship. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for Polymer Resources TP-FRG30 Polybutylene Terephthalate, 30% Glass Reinforced, Flame Retardant

Seller from Mumbai – 2021-05-13:

Seller from Mumbai work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1959 per MT