Polymer Resources PPX-FR1-[color]-EN Modified-PPO, V-0 Flame Retardant, Extrusion Grade price 1755 per MT

Physical Properties
Specific Gravity
1.08 g/cc
Linear Mold Shrinkage
0.0050 - 0.0070 cm/cm
Melt Flow
15 - 40 g/10 min @Load 11.6 kg, Temperature 250 °C

Mechanical Properties
Hardness, Rockwell R
113
Tensile Strength at Break
46.9 MPa
Tensile Strength, Yield
56.5 MPa
Elongation at Break
50 %
Flexural Strength
89.6 MPa
Flexural Modulus
2.28 GPa
Izod Impact, Notched
1.60 J/cm @Temperature -40.0 °C
Izod Impact, Notched
3.74 J/cm @Temperature 22.8 °C
Gardner Impact
16.9 J

Thermal Properties
Deflection Temperature at 0.46 MPa (66 psi)
87.8 °C
Deflection Temperature at 1.8 MPa (264 psi)
82.2 °C
UL RTI, Electrical
110 °C @Thickness 1.50 mm
UL RTI, Electrical
110 °C @Thickness 1.70 mm
UL RTI, Electrical
110 °C @Thickness 3.00 mm
UL RTI, Mechanical with Impact
110 °C @Thickness 1.50 mm
UL RTI, Mechanical with Impact
110 °C @Thickness 1.70 mm
UL RTI, Mechanical with Impact
110 °C @Thickness 3.00 mm
UL RTI, Mechanical without Impact
95.0 °C @Thickness 1.50 mm
UL RTI, Mechanical without Impact
95.0 °C @Thickness 1.70 mm
UL RTI, Mechanical without Impact
95.0 °C @Thickness 3.00 mm
Flammability, UL94
V-0 @Thickness 1.50 mm
Flammability, UL94
V-0 @Thickness 3.00 mm

Electrical Properties
Volume Resistivity
1.00e+17 ohm-cm
Dielectric Strength
22.0 kV/mm
Comparative Tracking Index
250 - 400 V
Hot Wire Ignition, HWI
>= 120 sec @Thickness 1.50 mm
Hot Wire Ignition, HWI
>= 120 sec @Thickness 1.70 mm
Hot Wire Ignition, HWI
>= 120 sec @Thickness 3.00 mm
High Amp Arc Ignition, HAI
60 - 120 arcs @Thickness 1.50 mm
High Amp Arc Ignition, HAI
60 - 120 arcs @Thickness 1.70 mm
High Amp Arc Ignition, HAI
60 - 120 arcs @Thickness 3.00 mm
High Voltage Arc-Tracking Rate, HVTR
80.0 - 150 mm/min

Processing Properties
Rear Barrel Temperature
>= 171 °C
Middle Barrel Temperature
>= 188 °C
Front Barrel Temperature
>= 188 °C
Melt Temperature
193 - 216 °C
Drying Temperature
71.1 - 82.2 °C
Dry Time
3.00 - 4.00 hour

Descriptive Properties
Vent
0.001

Alternative products

SABIC Innovative Plastics NORYL N190X PPE+PS accurate 59%

$ 2081/MT

Specific Gravity: 1.13 g/cc
Water Absorption: 0.080 % @Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
Melt Flow: 20 g/10 min @Load 5.00 kg, Temperature 280 °C
Melt Index of Compound: 23 g/10 min @Load 5.00 kg, Temperature 280 °C

ChevronTexaco Texatherm® accurate 59%

$ 1472/MT

Specific Gravity: 0.6215 g/cc
Specific Gravity: 0.668 g/cc
Specific Gravity: 0.7032 g/cc
Specific Gravity: 0.7416 g/cc
Specific Gravity: 0.7763 g/cc

Polymer Resources PC-FR1-D-[color]-3 Polycarbonate, Improved Flame Retardant, Low Flow, UV-stabilized accurate 52%

$ 1584/MT

Specific Gravity: 1.21 g/cc
Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
Melt Flow: 5.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C
Hardness, Rockwell M: 70
Hardness, Rockwell R: 118

ACC QM 2128 QSI Quantum Silicones 28 Durometer Condensation Cure Moldmaking Material accurate 52%

$ 1508/MT

Specific Gravity: 1.00 g/cc
Specific Gravity: 1.00 g/cc
Specific Gravity: 1.00 g/cc
Specific Gravity: 1.00 g/cc
Specific Gravity: 1.13 g/cc

SABIC Innovative Plastics LNP LUBRICOMP KL004L Acetal Copoly (Asia Pacific) accurate 66%

$ 1533/MT

Density: 1.51 g/cc
Density: 1.52 g/cc
Moisture Absorption: 0.100 %
Linear Mold Shrinkage, Flow: 0.034 cm/cm
Linear Mold Shrinkage, Flow: 0.025 - 0.040 cm/cm @Time 86400 sec

Polymer Resources PC-FR2-D Polycarbonate, Improved Flame Retardant, Medium Flow accurate 52%

$ 1904/MT

Specific Gravity: 1.21 g/cc
Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
Melt Flow: 9.0 - 16 g/10 min @Load 1.20 kg, Temperature 300 °C
Hardness, Rockwell M: 70
Hardness, Rockwell R: 118

SABIC Innovative Plastics NORYL PX1005X PPE+PS accurate 52%

$ 1743/MT

Specific Gravity: 1.12 g/cc
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm
Melt Flow: 37 g/10 min @Load 5.00 kg, Temperature 280 °C
Melt Index of Compound: 37 g/10 min @Load 5.00 kg, Temperature 280 °C

Polymer Resources PPX-FR1 Modified-PPO, V-0 Flame Retardant accurate 72%

$ 1704/MT

Specific Gravity: 1.08 g/cc
Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
Melt Flow: 25 - 50 g/10 min @Load 11.6 kg, Temperature 250 °C
Hardness, Rockwell R: 118
Tensile Strength at Break: 41.4 MPa

Polymer Resources PC-FR1-D Polycarbonate, Improved Flame Retardant, Low Flow accurate 52%

$ 2351/MT

Specific Gravity: 1.21 g/cc
Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
Melt Flow: 5.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C
Hardness, Rockwell M: 70
Hardness, Rockwell R: 118

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tanker for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for Polymer Resources PPX-FR1-[color]-EN Modified-PPO, V-0 Flame Retardant, Extrusion Grade

Seller from Sūrat – 2021-05-17:

Seller from Sūrat work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2415 per MT

Seller from Hāora – 2021-06-08:

Seller from Hāora work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1755 per MT