Polymer Resources PC-UV3-D-[color]-1 Polycarbonate, UV-stabilized, High Flow with Mold Release

Seller in Lagos price: $2305 per MT
Seller in Beijing price: $2397 per MT

Polymer Resources PC-UV3-D-[color]-1 Polycarbonate, UV-stabilized, High Flow with Mold Release in Polymer, Thermoplastic, Molded, Polycarbonate (PC), Polycarbonate

  • Physical Properties
  • Specific Gravity
  • 1.20 g/cc
  • Linear Mold Shrinkage
  • 0.0050 - 0.0070 cm/cm
  • Melt Flow
  • 14 - 20 g/10 min @Load 1.20 kg, Temperature 300 °C
  • Mechanical Properties
  • Hardness, Rockwell M
  • 70
  • Hardness, Rockwell R
  • 118
  • Tensile Strength at Break
  • 68.9 MPa
  • Tensile Strength, Yield
  • 62.1 MPa
  • Elongation at Break
  • 120 %
  • Elongation at Yield
  • 6.0 %
  • Flexural Strength
  • 95.8 MPa
  • Flexural Modulus
  • 2.31 GPa
  • Izod Impact, Notched
  • 6.94 J/cm @Temperature 22.8 °C
  • Gardner Impact
  • 36.2 J
  • Thermal Properties
  • Deflection Temperature at 0.46 MPa (66 psi)
  • 132 °C
  • Deflection Temperature at 1.8 MPa (264 psi)
  • 127 °C
  • Vicat Softening Point
  • 149 °C
  • UL RTI, Electrical
  • 120 °C @Thickness 1.50 mm
  • UL RTI, Electrical
  • 120 °C @Thickness 3.00 mm
  • UL RTI, Mechanical with Impact
  • 120 °C @Thickness 1.50 mm
  • UL RTI, Mechanical with Impact
  • 120 °C @Thickness 3.00 mm
  • UL RTI, Mechanical without Impact
  • 105 °C @Thickness 1.50 mm
  • UL RTI, Mechanical without Impact
  • 110 °C @Thickness 3.00 mm
  • Flammability, UL94
  • V-2 @Thickness 1.50 mm
  • Flammability, UL94
  • V-2 @Thickness 3.00 mm
  • Optical Properties
  • Haze
  • 1.0 %
  • UV Transmittance
  • 88 %
  • Electrical Properties
  • Volume Resistivity
  • 1.00e+15 ohm-cm
  • Dielectric Strength
  • 11.8 kV/mm
  • Comparative Tracking Index
  • 175 - 250 V
  • Hot Wire Ignition, HWI
  • 30 - 60 sec @Thickness 1.50 mm
  • Hot Wire Ignition, HWI
  • 30 - 60 sec @Thickness 3.00 mm
  • High Amp Arc Ignition, HAI
  • >= 120 arcs @Thickness 1.50 mm
  • High Amp Arc Ignition, HAI
  • >= 120 arcs @Thickness 3.00 mm
  • High Voltage Arc-Tracking Rate, HVTR
  • 25.4 - 80.0 mm/min
  • Processing Properties
  • Rear Barrel Temperature
  • 260 - 282 °C
  • Middle Barrel Temperature
  • 271 - 293 °C
  • Front Barrel Temperature
  • 282 - 304 °C
  • Melt Temperature
  • 288 - 316 °C
  • Mold Temperature
  • 71.1 - 93.3 °C
  • Drying Temperature
  • 118 - 124 °C
  • Dry Time
  • 3.00 - 4.00 hour
  • Descriptive Properties
  • Outdoor Suitability
  • f1
  • Vent
  • 0.0005

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, cruise ships on sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for Polymer Resources PC-UV3-D-[color]-1 Polycarbonate, UV-stabilized, High Flow with Mold Release

Seller from Lagos – 2021-03-26:

Seller from Lagos work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2305 per MT

Seller from Beijing – 2021-03-25:

Seller from Beijing work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2397 per MT

Share on Pinterest
Share on LinkedIn
Share on Reddit

Would you like to sell Polymer Resources PC-UV3-D-[color]-1 Polycarbonate, UV-stabilized, High Flow with Mold Release?

Plastic warehouse

Find a direct plastic supplier if you're interested in a supplier or Shelter in Singapore open-nearme.com