Premix Thermoplastics PRE-ELEC® PE 1299 Conductive Thermoplastic Compound price 1808 per MT

Physical Properties
Density
1.12 g/cc
Thickness
102 microns
Linear Mold Shrinkage
0.025 - 0.035 cm/cm
Melt Flow
1.5 g/10 min @Load 21.6 kg, Temperature 190 °C

Mechanical Properties
Hardness, Shore A
95
Hardness, Shore D
65
Tensile Strength
11.0 MPa
Tensile Strength, Yield
21.0 MPa
Elongation at Break
90 %
Elongation at Yield
12 %
Flexural Modulus
1.00 GPa
Izod Impact, Notched (ISO)
20.0 kJ/m² @Thickness 4.00 mm, Temperature -20.0 °C
Izod Impact, Notched (ISO)
NB @Thickness 4.00 mm, Temperature 23.0 °C
Izod Impact, Unnotched (ISO)
NB @Thickness 4.00 mm, Temperature 23.0 °C
Izod Impact, Unnotched (ISO)
NB @Thickness 4.00 mm, Temperature -20.0 °C
Charpy Impact Unnotched
NB @Thickness 102 mm, Temperature 23.0 °C
Charpy Impact Unnotched
NB @Thickness 102 mm, Temperature -20.0 °C
Charpy Impact, Notched
1.70 J/cm² @Thickness 102 mm, Temperature -20.0 °C
Charpy Impact, Notched
5.50 J/cm² @Thickness 102 mm, Temperature 23.0 °C

Thermal Properties
Deflection Temperature at 0.46 MPa (66 psi)
65.0 °C
Deflection Temperature at 1.8 MPa (264 psi)
43.0 °C
Vicat Softening Point
58.0 °C
Vicat Softening Point
123 °C

Electrical Properties
Volume Resistivity
<= 1000 ohm-cm
Surface Resistance
<= 1e+05

Processing Properties
Zone 1
200 °C
Zone 1
240 °C
Zone 2
210 °C
Zone 2
230 °C
Zone 3
220 °C
Zone 3
220 °C
Zone 4
220 °C
Zone 4
230 °C
Zone 5
230 °C
Zone 5
240 °C
Melt Temperature
180 - 280 °C
Mold Temperature
40.0 - 80.0 °C
Roll Temperature
50.0 °C
Roll Temperature
60.0 °C
Roll Temperature
70.0 °C
Drying Temperature
60.0 - 80.0 °C
Dry Time
2 - 4 hour
Injection Pressure
60.0 - 80.0 MPa
Shelf Life
12.0 Month

Descriptive Properties
Injection Speed
Moderate

Alternative products

UBE UBESTA® 3024NUX Short Cycle Time Electronic Grade Nylon 12 accurate 41%

$ 2213/MT

Density: 1.02 g/cc
Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 235 °C
Hardness, Shore D: 75
Tensile Strength at Break: >= 54.0 MPa
Tensile Strength, Yield: 43.0 MPa

Premix Thermoplastics PRE-ELEC® PE 1200 Conductive Thermoplastic Compound accurate 70%

$ 1797/MT

Density: 1.12 g/cc
Thickness: 102 microns
Linear Mold Shrinkage: 0.025 - 0.035 cm/cm
Melt Flow: 1.0 g/10 min @Load 21.6 kg, Temperature 190 °C
Hardness, Shore A: 95

Premix Thermoplastics PRE-ELEC® PE 1297 Conductive Thermoplastic Compound accurate 62%

$ 2146/MT

Density: 1.04 g/cc
Thickness: 102 microns
Linear Mold Shrinkage: 0.025 - 0.035 cm/cm
Melt Flow: 1.1 g/10 min @Load 10.0 kg, Temperature 190 °C
Melt Flow: 7.0 g/10 min @Load 21.6 kg, Temperature 190 °C

Premix Thermoplastics PRE-ELEC® PP 1391 Conductive Thermoplastic Compound accurate 37%

$ 1444/MT

Density: 0.980 g/cc
Thickness: 102 microns
Linear Mold Shrinkage: 0.013 - 0.019 cm/cm
Melt Flow: 0.40 g/10 min @Load 2.16 kg, Temperature 230 °C
Melt Flow: 2.0 g/10 min @Load 5.00 kg, Temperature 230 °C

UBE UBESTA® 3024U Rigid Electronic Grade Nylon 12 accurate 41%

$ 1554/MT

Density: 1.02 g/cc
Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 235 °C
Hardness, Shore D: 73
Tensile Strength at Break: >= 54.0 MPa
Tensile Strength, Yield: 42.0 MPa

Premix Thermoplastics PRE-ELEC® PE 1296 Conductive Thermoplastic Compound accurate 78%

$ 2164/MT

Density: 1.12 g/cc
Thickness: 102 microns
Linear Mold Shrinkage: 0.025 - 0.035 cm/cm
Melt Flow: 0.60 g/10 min @Load 21.6 kg, Temperature 190 °C
Hardness, Shore A: 95

Premix Thermoplastics PRE-ELEC® ABS 1415 Conductive Thermoplastic Compound accurate 45%

$ 1611/MT

Density: 1.10 g/cc
Thickness: 102 microns
Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm
Melt Flow: 2.5 g/10 min @Load 10.0 kg, Temperature 220 °C
Hardness, Shore D: 77

UBE UBESTA® 3035JU5 Plasticized Industrial Grade Nylon 12 accurate 41%

$ 2208/MT

Density: 1.03 g/cc
Melt Flow: 14 g/10 min @Load 2.16 kg, Temperature 235 °C
Hardness, Shore D: 54
Tensile Strength at Break: >= 30.0 MPa
Tensile Strength, Yield: 13.0 MPa

Premix Thermoplastics PRE-ELEC® PP 1397 Conductive Thermoplastic Compound accurate 37%

$ 1451/MT

Density: 0.980 g/cc
Thickness: 102 microns
Linear Mold Shrinkage: 0.013 - 0.019 cm/cm
Melt Flow: 1.2 g/10 min @Load 2.16 kg, Temperature 230 °C
Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 230 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tanker for sale price. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for Premix Thermoplastics PRE-ELEC® PE 1299 Conductive Thermoplastic Compound

Seller from Kinshasa – 2021-08-07:

Seller from Kinshasa work with company: Solvay, PolyOne Corporation, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1978 per MT

Seller from Nanjing – 2021-05-16:

Seller from Nanjing work with company: Solvay, PolyOne Corporation, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1808 per MT

Seller from Lima – 2021-08-18:

Seller from Lima work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), BASF

Price: $2549 per MT