Premix Thermoplastics PRE-ELEC® PP 1397 Conductive Thermoplastic Compound price 1451 per MT

Physical Properties
Density
0.980 g/cc
Thickness
102 microns
Linear Mold Shrinkage
0.013 - 0.019 cm/cm
Melt Flow
1.2 g/10 min @Load 2.16 kg, Temperature 230 °C
Melt Flow
6.0 g/10 min @Load 5.00 kg, Temperature 230 °C

Mechanical Properties
Hardness, Shore A
99
Hardness, Shore D
74
Film Tensile Strength at Yield, MD
23.0 MPa @Thickness 0.400 mm
Film Tensile Strength at Yield, TD
22.0 MPa @Thickness 0.400 mm
Film Elongation at Break, MD
500 % @Thickness 0.400 mm
Film Elongation at Break, TD
480 % @Thickness 0.400 mm
Film Elongation at Yield, MD
17 % @Thickness 0.400 mm
Film Elongation at Yield, TD
16 % @Thickness 0.400 mm
Flexural Modulus
1.40 GPa
Izod Impact, Notched (ISO)
NB @Thickness 4.00 mm, Temperature 23.0 °C
Izod Impact, Notched (ISO)
NB @Thickness 4.00 mm, Temperature -20.0 °C
Izod Impact, Unnotched (ISO)
NB @Thickness 4.00 mm, Temperature 23.0 °C
Izod Impact, Unnotched (ISO)
NB @Thickness 4.00 mm, Temperature -20.0 °C
Charpy Impact Unnotched
NB @Thickness 102 mm, Temperature 23.0 °C
Charpy Impact Unnotched
NB @Thickness 102 mm, Temperature -20.0 °C
Charpy Impact, Notched
1.80 J/cm² @Thickness 102 mm, Temperature -20.0 °C
Charpy Impact, Notched
4.50 J/cm² @Thickness 102 mm, Temperature 23.0 °C
Film Tensile Strength at Break, MD
25.0 MPa @Thickness 0.400 mm
Film Tensile Strength at Break, TD
23.0 MPa @Thickness 0.400 mm

Thermal Properties
Deflection Temperature at 0.46 MPa (66 psi)
90.0 °C
Deflection Temperature at 1.8 MPa (264 psi)
53.0 °C
Vicat Softening Point
151 °C

Electrical Properties
Volume Resistivity
<= 1000 ohm-cm @Thickness 0.400 mm
Surface Resistance
<= 10000 ohm @Thickness 0.400 mm

Processing Properties
Zone 1
210 °C
Zone 1
230 °C
Zone 2
220 °C
Zone 2
230 °C
Zone 3
220 °C
Zone 3
220 °C
Zone 4
230 °C
Zone 4
230 °C
Zone 5
230 °C
Zone 5
230 °C
Roll Temperature
60.0 °C
Roll Temperature
80.0 °C
Roll Temperature
90.0 °C
Drying Temperature
60.0 - 80.0 °C
Dry Time
2 - 4 hour
Shelf Life
12.0 Month

Alternative products

UBE UBESTA® 3024NUX Short Cycle Time Electronic Grade Nylon 12 accurate 46%

$ 2213/MT

Density: 1.02 g/cc
Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 235 °C
Hardness, Shore D: 75
Tensile Strength at Break: >= 54.0 MPa
Tensile Strength, Yield: 43.0 MPa

Premix Thermoplastics PRE-ELEC® PE 1200 Conductive Thermoplastic Compound accurate 59%

$ 1797/MT

Density: 1.12 g/cc
Thickness: 102 microns
Linear Mold Shrinkage: 0.025 - 0.035 cm/cm
Melt Flow: 1.0 g/10 min @Load 21.6 kg, Temperature 190 °C
Hardness, Shore A: 95

Premix Thermoplastics PRE-ELEC® PE 1299 Conductive Thermoplastic Compound accurate 59%

$ 1808/MT

Density: 1.12 g/cc
Thickness: 102 microns
Linear Mold Shrinkage: 0.025 - 0.035 cm/cm
Melt Flow: 1.5 g/10 min @Load 21.6 kg, Temperature 190 °C
Hardness, Shore A: 95

Premix Thermoplastics PRE-ELEC® PE 1297 Conductive Thermoplastic Compound accurate 52%

$ 2146/MT

Density: 1.04 g/cc
Thickness: 102 microns
Linear Mold Shrinkage: 0.025 - 0.035 cm/cm
Melt Flow: 1.1 g/10 min @Load 10.0 kg, Temperature 190 °C
Melt Flow: 7.0 g/10 min @Load 21.6 kg, Temperature 190 °C

Premix Thermoplastics PRE-ELEC® PP 1391 Conductive Thermoplastic Compound accurate 99%

$ 1444/MT

Density: 0.980 g/cc
Thickness: 102 microns
Linear Mold Shrinkage: 0.013 - 0.019 cm/cm
Melt Flow: 0.40 g/10 min @Load 2.16 kg, Temperature 230 °C
Melt Flow: 2.0 g/10 min @Load 5.00 kg, Temperature 230 °C

UBE UBESTA® 3024U Rigid Electronic Grade Nylon 12 accurate 46%

$ 1554/MT

Density: 1.02 g/cc
Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 235 °C
Hardness, Shore D: 73
Tensile Strength at Break: >= 54.0 MPa
Tensile Strength, Yield: 42.0 MPa

Premix Thermoplastics PRE-ELEC® PP 1394 Conductive Thermoplastic Compound accurate 72%

$ 1674/MT

Density: 1.06 g/cc
Thickness: 102 microns
Linear Mold Shrinkage: 0.012 - 0.017 cm/cm
Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C
Melt Flow: 15 g/10 min @Load 5.00 kg, Temperature 230 °C

Premix Thermoplastics PRE-ELEC® PE 1296 Conductive Thermoplastic Compound accurate 59%

$ 2164/MT

Density: 1.12 g/cc
Thickness: 102 microns
Linear Mold Shrinkage: 0.025 - 0.035 cm/cm
Melt Flow: 0.60 g/10 min @Load 21.6 kg, Temperature 190 °C
Hardness, Shore A: 95

Premix Thermoplastics PRE-ELEC® ABS 1415 Conductive Thermoplastic Compound accurate 66%

$ 1611/MT

Density: 1.10 g/cc
Thickness: 102 microns
Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm
Melt Flow: 2.5 g/10 min @Load 10.0 kg, Temperature 220 °C
Hardness, Shore D: 77

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, vessels for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for Premix Thermoplastics PRE-ELEC® PP 1397 Conductive Thermoplastic Compound

Seller from Hong Kong – 2021-08-16:

Seller from Hong Kong work with company: Techmer ES, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2301 per MT

Seller from Saint Petersburg – 2021-04-19:

Seller from Saint Petersburg work with company: Solvay, Arlon, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1451 per MT