PTS Tristar® PC-10GFR-(V) 10% Glass Reinforced UV Stabilized Polycarbonate With Release price 2536 per MT

Physical Properties
Density
1.25 g/cc
Water Absorption
0.12 %
Linear Mold Shrinkage
0.0020 - 0.0040 cm/cm @Thickness 3.17 mm

Mechanical Properties
Hardness, Rockwell R
120
Tensile Strength, Yield
62.0 MPa @Thickness 3.17 mm
Elongation at Break
15 % @Thickness 3.17 mm
Flexural Yield Strength
96.5 MPa @Thickness 3.17 mm
Flexural Modulus
3.10 GPa @Thickness 3.17 mm
Izod Impact, Notched
1.07 J/cm @Thickness 3.17 mm
Tensile Impact Strength
53.3 kJ/m² @Thickness 3.17 mm

Thermal Properties
Deflection Temperature at 1.8 MPa (264 psi)
138 °C
UL RTI, Electrical
80.0 °C
UL RTI, Electrical
125 °C
UL RTI, Mechanical with Impact
80.0 °C
UL RTI, Mechanical with Impact
115 °C
UL RTI, Mechanical without Impact
80.0 °C
UL RTI, Mechanical without Impact
125 °C
Flammability, UL94
V-0 @Thickness 3.00 mm
Flammability, UL94
V-0 @Thickness 1.50 mm
Flammability, UL94
5VA @Thickness 2.40 mm
Oxygen Index
37.1 %
Glow Wire Test
875 °C
Glow Wire Test
960 °C

Electrical Properties
Volume Resistivity
3.00e+15 ohm-cm
Volume Resistivity
6.00e+15 ohm-cm
Dielectric Strength
19.0 kV/mm @Thickness 3.00 mm
Arc Resistance
0.00 - 60 sec
Arc Resistance
60 - 120 sec
Comparative Tracking Index
100 - 175 V
Comparative Tracking Index
175 - 250 V
Hot Wire Ignition, HWI
30 - 60 sec
Hot Wire Ignition, HWI
60 - 120 sec
High Amp Arc Ignition, HAI
>= 120 arcs
High Amp Arc Ignition, HAI
>= 120 arcs
High Voltage Arc-Tracking Rate, HVTR
80.0 - 150 mm/min

Descriptive Properties
Suitability for Outdoor Use (all colors except WT)
(f1)
Suitability for Outdoor Use (WT)
(f2)

Alternative products

PTS Tristar® PC-10R-(V22) 22 MFI UV Stabilized Polycarbonate With Release accurate 42%

$ 1515/MT

Density: 1.20 g/cc
Water Absorption: 0.15 %
Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C
Hardness, Rockwell R: 120
Tensile Strength, Yield: 60.3 MPa @Thickness 3.17 mm

PTS Tristar® PC-10R-CL(6) 6 MFI Clear Polycarbonate with Release accurate 42%

$ 1780/MT

Density: 1.20 g/cc
Water Absorption: 0.15 %
Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C
Hardness, Rockwell R: 120
Tensile Strength, Yield: 62.1 MPa @Thickness 3.17 mm

PTS Tristar® PC-10FRN 15 MFI Flame Retardant Polycarbonate With Release accurate 42%

$ 1760/MT

Density: 1.23 g/cc
Water Absorption: 0.18 %
Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
Hardness, Rockwell R: 120
Tensile Strength, Yield: 62.1 MPa @Thickness 3.17 mm

PTS Tristar® PC-10GFR 10% Glass Reinforced Polycarbonate With Release accurate 99%

$ 1584/MT

Density: 1.25 g/cc
Water Absorption: 0.12 %
Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm @Thickness 3.17 mm
Hardness, Rockwell R: 120
Tensile Strength, Yield: 62.0 MPa @Thickness 3.17 mm

PTS Tristar® PC-10R-(22) 22 MFI Polycarbonate With Release accurate 42%

$ 1951/MT

Density: 1.20 g/cc
Water Absorption: 0.15 %
Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C
Hardness, Rockwell R: 120
Tensile Strength, Yield: 60.3 MPa @Thickness 3.17 mm

PTS Tristar® PC-10FR-(VIK) 16 MFI Flame Retardant, UV Stabilized Polycarbonate With Impact Modifier and Release accurate 47%

$ 2115/MT

Density: 1.23 g/cc
Water Absorption: 0.18 %
Melt Flow: 16 g/10 min @Load 1.20 kg, Temperature 300 °C
Hardness, Rockwell R: 120
Tensile Strength, Yield: 55.2 MPa @Thickness 3.17 mm

PTS Tristar® PC-05GFR 5% Glass Reinforced Polycarbonate With Release accurate 51%

$ 1742/MT

Density: 1.20 g/cc
Water Absorption: 0.15 %
Hardness, Rockwell R: 120
Tensile Strength, Yield: 58.6 MPa @Thickness 3.17 mm
Elongation at Break: 15 % @Thickness 3.17 mm

PTS Tristar® PC-10R-(V) 10 MFI UV Stabilized Polycarbonate With Release accurate 42%

$ 1532/MT

Density: 1.20 g/cc
Water Absorption: 0.15 %
Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
Hardness, Rockwell R: 120
Tensile Strength, Yield: 62.1 MPa @Thickness 3.17 mm

PTS Tristar® PC-10R-CL(V22) 22 MFI UV Stabilized Clear Polycarbonate with Release accurate 42%

$ 1614/MT

Density: 1.20 g/cc
Water Absorption: 0.15 %
Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C
Hardness, Rockwell R: 120
Tensile Strength, Yield: 60.3 MPa @Thickness 3.17 mm

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, ship for sale norway. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for PTS Tristar® PC-10GFR-(V) 10% Glass Reinforced UV Stabilized Polycarbonate With Release

Seller from Miami – 2021-05-15:

Seller from Miami work with company: 3M, PolyOne Corporation, Exxon Chemical, SABIC Innovative Plastics (GE Plastics)

Price: $2536 per MT