Raschig Group 5567 DAP Diallyl Phthalate (DAP), Cast, Mineral Filler price 1480 per MT

Physical Properties
Specific Gravity
1.90 - 2.10 g/cc
Apparent Bulk Density
0.750 - 0.900 g/cc
Water Absorption
<= 0.200 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow
0.00300 - 0.00400 cm/cm
Linear Mold Shrinkage, Flow
0.00500 - 0.00600 cm/cm

Mechanical Properties
Tensile Strength
35.0 - 60.0 MPa
Tensile Strength
40.0 - 70.0 MPa
Modulus of Elasticity
6.00 - 9.00 GPa
Modulus of Elasticity
9.00 - 11.0 GPa
Flexural Strength
80.0 - 100 MPa
Flexural Strength
100 - 140 MPa
Flexural Modulus
8.00 - 12.0 GPa
Flexural Modulus
13.0 - 16.0 GPa
Compressive Strength
150 - 200 MPa
Charpy Impact Unnotched
0.500 - 1.00 J/cm²
Charpy Impact Unnotched
0.800 - 1.10 J/cm²
Charpy Impact, Notched
0.250 - 0.350 J/cm²
Charpy Impact, Notched
0.350 - 0.500 J/cm²

Thermal Properties
CTE, linear, Parallel to Flow
5.00 - 10.0 µm/m-°C @Temperature 50.0 - 100 °C
Thermal Conductivity
0.900 - 1.10 W/m-K
Deflection Temperature at 1.8 MPa (264 psi)
>= 200 °C
Deflection Temperature at 8.0 MPa
>= 180 °C
Flammability, UL94
V-0 @Thickness 0.800 mm
Shrinkage
<= 0.0500 % @Temperature 110 °C, Time 605000 sec

Electrical Properties
Volume Resistivity
1.00e+14 - 1.00e+15 ohm-cm
Surface Resistance
1.00e+14 - 1.00e+15 ohm
Dielectric Constant
4.00 - 4.50 @Frequency 1.00e+6 Hz
Dielectric Constant
4.50 - 5.00 @Frequency 100 Hz
Dielectric Strength
35.0 - 40.0 kV/mm
Dissipation Factor
0.0100 - 0.0300 @Frequency 1.00e+6 Hz
Dissipation Factor
0.0100 - 0.0300 @Frequency 100 Hz
Arc Resistance
180 - 240 sec
Comparative Tracking Index
600 V

Processing Properties
Shelf Life
6.00 Month @Temperature 15.0 - 25.0 °C

Descriptive Properties
Glow wire flammability test
960/1
Glow wire ignitability test
930/1
Water Absorption
<15 mg

Alternative products

Raschig Group 2557 AMC Polyester accurate 74%

$ 1942/MT

Specific Gravity: 2.00 - 2.20 g/cc
Apparent Bulk Density: 0.700 - 0.850 g/cc
Water Absorption: <= 0.300 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.00300 - 0.00500 cm/cm
Tensile Strength: 50.0 - 70.0 MPa

Raschig Group AMPLA® 2000 melamine-modified polyester accurate 74%

$ 1649/MT

Specific Gravity: 1.70 - 1.80 g/cc
Apparent Bulk Density: 0.750 - 0.950 g/cc
Water Absorption: <= 0.80 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage: 0.0070 - 0.010 cm/cm
Tensile Strength, Yield: 30.0 - 50.0 MPa

Raschig Group 2567 AMC accurate 74%

$ 2281/MT

Specific Gravity: 2.00 - 2.20 g/cc
Apparent Bulk Density: 0.700 - 0.850 g/cc
Water Absorption: <= 0.30 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage: 0.0015 - 0.0045 cm/cm
Tensile Strength, Yield: 35.0 - 60.0 MPa

Solvay Specialty Polymers Ixef® 1524 Polyarylamide (PARA), 50% Glass Fiber (Dry) accurate 74%

$ 1761/MT

Density: 1.68 g/cc
Filler Content: 50 %
Water Absorption: 0.30 % @Time 86400 sec
Water Absorption at Saturation: 1.0 %
Water Absorption at Saturation: 1.3 %

Raschig Group 2572 AMC accurate 74%

$ 1563/MT

Specific Gravity: 1.90 - 2.10 g/cc
Apparent Bulk Density: 0.700 - 0.850 g/cc
Water Absorption: <= 0.30 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage: 0.0020 - 0.0045 cm/cm
Tensile Strength, Yield: 60.0 - 70.0 MPa

Raschig Group RALUPOL® 8602 UP accurate 74%

$ 1894/MT

Specific Gravity: 1.90 - 2.10 g/cc
Apparent Bulk Density: 0.750 - 1.00 g/cc
Water Absorption: <= 0.55 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage: 0.0060 - 0.0090 cm/cm
Tensile Strength, Yield: 40.0 - 70.0 MPa

Raschig Group 2568 AMC accurate 74%

$ 1472/MT

Specific Gravity: 2.00 - 2.20 g/cc
Apparent Bulk Density: 0.800 - 0.950 g/cc
Water Absorption: <= 0.30 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage: 0.0025 - 0.0045 cm/cm
Tensile Strength, Yield: 35.0 - 60.0 MPa

Zell-Metall Engineering Plastics Zellamid 202 (PA 6) at 50% RH accurate 74%

$ 1678/MT

Density: 1.13 - 1.15 g/cc
Moisture Absorption at Equilibrium: 2.6 - 3.4 %
Water Absorption at Saturation: 9.0 - 10 %
Ball Indentation Hardness: 70.0 MPa
Tensile Strength at Break: 50.0 MPa

Raschig Group MELOPAS® 156 MF Melamine accurate 74%

$ 1627/MT

Specific Gravity: 1.80 - 1.90 g/cc
Apparent Bulk Density: 0.600 - 0.800 g/cc
Water Absorption: <= 1.00 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.00500 - 0.00900 cm/cm
Tensile Strength: 40.0 - 50.0 MPa

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale in usa. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

4 prices for Raschig Group 5567 DAP Diallyl Phthalate (DAP), Cast, Mineral Filler

Seller from Bengalūru – 2021-07-16:

Seller from Bengalūru work with company: PolyOne Corporation, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2083 per MT

Seller from Mexico City – 2021-06-07:

Seller from Mexico City work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1480 per MT

Seller from Ōsaka – 2021-02-27:

Seller from Ōsaka work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), BASF

Price: $1701 per MT

Seller from Hong Kong – 2021-04-22:

Seller from Hong Kong work with company: Solvay, PolyOne Corporation, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2249 per MT