Physical Properties
Specific Gravity
1.75 - 1.80 g/cc
Water Absorption
<= 0.040 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow
0.020 - 0.030 cm/cm
Melt Flow
3.0 - 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C

Mechanical Properties
Hardness, Shore D
53 @Thickness 2.00 mm
Tensile Strength at Break
14.0 - 30.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C
Tensile Strength, Yield
14.0 - 35.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C
Elongation at Break
350 - 600 % @Thickness 2.00 mm, Temperature 23.0 °C
Elongation at Yield
10 - 12 % @Thickness 2.00 mm, Temperature 23.0 °C
Tensile Modulus
0.400 - 0.600 GPa @Thickness 2.00 mm, Temperature 23.0 °C
Izod Impact, Notched
10.0 J/cm @Thickness 4.00 mm, Temperature 23.0 °C
Coefficient of Friction, Dynamic
0.20 - 0.30
Coefficient of Friction, Static
0.20 - 0.40
Taber Abrasion, mg/1000 Cycles
5.0 - 10 @Load 1.00 kg

Thermal Properties
Heat of Fusion
22.0 - 28.0 J/g
Heat of Fusion
23.0 - 29.0 J/g
CTE, linear, Parallel to Flow
130 - 150 µm/m-°C @Temperature 0.000 - 40.0 °C
Specific Heat Capacity
1.20 J/g-°C @Temperature 23.0 °C
Specific Heat Capacity
1.60 J/g-°C @Temperature 100 °C
Thermal Conductivity
0.200 W/m-K @Temperature 23.0 °C
Melting Point
167 - 171 °C
Crystallization Temperature
125 - 131 °C
Vicat Softening Point
110 °C
Glass Transition Temp, Tg
-28.0 °C
Flammability, UL94
V-0 @Thickness 0.100 mm
Oxygen Index
48 % @Thickness 3.00 mm

Electrical Properties
Volume Resistivity
>= 1.00e+14 ohm-cm
Surface Resistance
>= 1.00e+14 ohm
Dielectric Constant
7.0 @Frequency 1000 Hz, Temperature 23.0 °C
Dielectric Strength
20.0 - 25.0 kV/mm @Thickness 1.00 mm, Temperature 23.0 °C

Descriptive Properties
Availability
Africa & Middle East
Availability
Asia Pacific
Availability
Europe
Availability
North America
Availability
South America
Features
Copolymer
Features
Good Flexibility
Features
Low Viscosity
Forms
Granules
Generic
PVDF
Uses
Wire & Cable Applications

Alternative products

DSM Akulon® K224-HG5 (Cond.) 25% Glass Reinforced Nylon 6 (North America) (discontinued **) accurate 74%

$ 1734/MT

Density: 1.30 g/cc
Water Absorption: 6.8 %
Moisture Absorption at Equilibrium: 2.0 %
Tensile Strength at Break: 100 MPa
Elongation at Break: 5.0 %

Celanese Hostaform® C 9021 GV1/10 POM, 10% Glass Reinforced accurate 74%

$ 1567/MT

Density: 1.48 g/cc
Water Absorption at Saturation: 0.850 %
Melt Flow: 6.00 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength at Break: 90.0 MPa
Elongation at Break: 4.00 %

Azoty Tarnow™ TARNOFORM 300 HI6 POM accurate 74%

$ 1950/MT

Density: 1.33 g/cc
Linear Mold Shrinkage: 0.0265 cm/cm
Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C
Hardness, Rockwell R: 87
Ball Indentation Hardness: 52.0 MPa

Solvay Specialty Polymers Solef® 9007 Polyvinylidene Fluoride (PVDF) accurate 74%

$ 1505/MT

Density: 1.75 - 1.80 g/cc
Water Absorption: <= 0.040 % @Time 86400 sec
Linear Mold Shrinkage, Flow: 0.020 - 0.030 cm/cm
Melt Flow: 16 - 26 g/10 min @Load 3.80 kg, Temperature 230 °C
Melt Flow: 20 - 38 g/10 min @Load 5.00 kg, Temperature 230 °C

Celanese Hostaform® C 27021 LS colored POM, UV Resistant accurate 74%

$ 2476/MT

Density: 1.41 g/cc
Density of Compound: 1.20 g/cc
Water Absorption at Saturation: 0.650 %
Linear Mold Shrinkage, Flow: 0.0190 cm/cm
Linear Mold Shrinkage, Transverse: 0.0180 cm/cm

Celanese Vandar® 8000 PBT (Unverified Data**) accurate 74%

$ 1631/MT

Specific Gravity: 1.37 g/cc
Density: 1.37 g/cc
Moisture Absorption: 0.200 %
Linear Mold Shrinkage, Flow: 0.025 - 0.028 cm/cm
Linear Mold Shrinkage, Flow: 0.025 - 0.028 cm/cm

Supreme Petrochem SP 6450 High Heat Polystyrene accurate 74%

$ 2130/MT

Specific Gravity: 1.04 g/cc
Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm
Melt Flow: 10 g/10 min @Load 10.0 kg, Temperature 200 °C
Tensile Strength at Break: 36.8 MPa
Elongation at Break: 50 %

Celanese Hostaform® C 9021 XAP2 LS POM, UV Resistant accurate 74%

$ 1530/MT

Density: 1.41 g/cc
Water Absorption at Saturation: 0.650 %
Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength, Yield: 63.0 MPa
Elongation at Break: 30.0 %

Solvay Specialty Polymers Solef® 31508 Polyvinylidene Fluoride (PVDF) accurate 99%

$ 1520/MT

Density: 1.75 - 1.80 g/cc
Water Absorption: <= 0.040 % @Time 86400 sec
Linear Mold Shrinkage, Flow: 0.020 - 0.030 cm/cm
Melt Flow: 3.0 - 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
Hardness, Shore D: 53

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, cargo ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for Solvay Specialty Polymers Solef® 31508 Polyvinylidene Fluoride (PVDF) (Unverified Data**)

Seller from Taipei – 2021-05-06:

Seller from Taipei work with company: RTP Company, SABIC Innovative Plastics (GE Plastics), LG Chemical, ALIMEX GmbH

Price: $2080 per MT

Seller from Barcelona – 2021-03-14:

Seller from Barcelona work with company: RTP Company, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2357 per MT

Seller from Ōsaka – 2021-03-25:

Seller from Ōsaka work with company: RTP Company, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2453 per MT