Solvay TECHNYL® A 218W V30 Natural PA66, 30% glass fiber, DRY price 1814 per MT

Physical Properties
Density
1.35 g/cc
Water Absorption
0.80 % @Temperature 23.0 °C, Time 86400 sec
Viscosity
120 cP @Shear Rate 100 1/s, Temperature 290 °C
Viscosity
150 cP @Shear Rate 100 1/s, Temperature 280 °C
Viscosity
200 cP @Shear Rate 100 1/s, Temperature 270 °C
Viscosity
205 cP @Shear Rate 10.0 1/s, Temperature 290 °C
Viscosity
300 cP @Shear Rate 10.0 1/s, Temperature 280 °C
Viscosity
500 cP @Shear Rate 10.0 1/s, Temperature 270 °C
Linear Mold Shrinkage
0.0062 cm/cm
Linear Mold Shrinkage, Flow
0.0050 cm/cm
Linear Mold Shrinkage, Transverse
0.0080 cm/cm

Mechanical Properties
Tensile Strength at Break
190 MPa
Tensile Stress
85.0 MPa @Strain 1.00 %
Tensile Stress
155 MPa @Strain 2.00 %
Tensile Stress
180 MPa @Strain 3.00 %
Elongation at Break
3.2 %
Tensile Modulus
1.00 GPa
Flexural Strength
270 MPa
Flexural Modulus
8.60 GPa
Flexural Modulus
9.00 GPa
Izod Impact, Notched
1.05 J/cm
Izod Impact, Notched (ISO)
10.0 kJ/m²
Charpy Impact Unnotched
8.50 J/cm²
Charpy Impact, Notched
1.10 J/cm²

Thermal Properties
CTE, linear, Parallel to Flow
28.0 µm/m-°C @Temperature 23.0 - 85.0 °C
CTE, linear, Transverse to Flow
2.80 µm/m-°C @Temperature 23.0 - 85.0 °C
Melting Point
262 °C
Deflection Temperature at 1.8 MPa (264 psi)
250 °C
Deflection Temperature at 1.8 MPa (264 psi)
254 °C
Flammability, UL94
HB @Thickness 1.60 mm
Glow Wire Test
700 °C @Thickness 1.60 mm

Electrical Properties
Volume Resistivity
1.00e+14 ohm-cm
Surface Resistance
1.00e+15 ohm
Dielectric Constant
3.7
Dielectric Strength
35.0 kV/mm
Dissipation Factor
0.020
Comparative Tracking Index
600 V

Processing Properties
Feed Temperature
265 - 275 °C
Mold Temperature
70.0 - 100 °C
Drying Temperature
80.0 °C
Moisture Content
<= 0.20 %

Descriptive Properties
Compression Zone
270-280°C
Mixing Zone
280-290°C

Alternative products

Solvay TECHNYL® C 218 V 30 PA6, 30% glass fiber, DRY accurate 60%

$ 1723/MT

Density: 1.36 g/cc
Water Absorption: 1.05 % @Temperature 23.0 °C, Time 86400 sec
Viscosity: 30 cP @Shear Rate 10000 1/s, Temperature 240 °C
Viscosity: 30 cP @Shear Rate 10000 1/s, Temperature 250 °C
Viscosity: 30 cP @Shear Rate 10000 1/s, Temperature 260 °C

BASF Ultramid® 8233G HS 33% Glass Filled PA6 (Dry) accurate 60%

$ 1456/MT

Density: 1.136 g/cc
Density: 1.39 g/cc
Water Absorption: 1.1 %
Water Absorption: 6.4 %
Moisture Absorption at Equilibrium: 1.8 %

Solvay TECHNYLSTARâ„¢ S 218 V30 PA6, 30% glass filled, DRY accurate 56%

$ 1895/MT

Density: 1.34 g/cc
Water Absorption: 0.95 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage: 0.0054 cm/cm
Linear Mold Shrinkage, Flow: 0.0035 cm/cm
Linear Mold Shrinkage, Transverse: 0.0065 cm/cm

Solvay Technyl® A 60G1 V25 25% Glass Reinforced Nylon 66, Flame Retardant accurate 56%

$ 1605/MT

Density: 1.38 g/cc
Water Absorption: 0.83 % @Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0045 cm/cm
Linear Mold Shrinkage, Transverse: 0.0085 cm/cm
Linear Mold Shrinkage, Transverse: 0.0090 cm/cm

Solvay TECHNYL® A 216 V33 PA66, 33% glass fiber, DRY accurate 56%

$ 1524/MT

Density: 1.38 g/cc
Water Absorption: 0.78 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage: 0.0062 cm/cm
Linear Mold Shrinkage, Flow: 0.0050 cm/cm
Linear Mold Shrinkage, Transverse: 0.0080 cm/cm

Solvay TECHNYL® A 216 V30 PA66, 33% glass fiber, DRY accurate 63%

$ 1537/MT

Density: 1.37 g/cc
Water Absorption: 0.80 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage: 0.0062 cm/cm
Linear Mold Shrinkage, Flow: 0.0050 cm/cm
Linear Mold Shrinkage, Transverse: 0.0080 cm/cm

Solvay TECHNYL® A 218 V30 BK 34 NG PA66, 30% glass fiber, DRY accurate 74%

$ 1554/MT

Density: 1.37 g/cc
Water Absorption: 0.80 % @Temperature 23.0 °C, Time 86400 sec
Viscosity: 20 cP @Shear Rate 1000 1/s, Temperature 280 °C
Viscosity: 20 cP @Shear Rate 1000 1/s, Temperature 290 °C
Viscosity: 20 cP @Shear Rate 1000 1/s, Temperature 300 °C

Solvay TECHNYL® A 218G1 V30 Black 34N PA66, 30% glass fiber, DRY accurate 67%

$ 1556/MT

Density: 1.37 g/cc
Water Absorption: 0.80 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0050 cm/cm
Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
Tensile Strength at Break: 195 MPa

Solvay TECHNYL® A 218W V30 Black FA PA66, 30% glass fiber, DRY accurate 67%

$ 1605/MT

Density: 1.35 g/cc
Water Absorption: 0.80 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage: 0.0062 cm/cm
Linear Mold Shrinkage, Flow: 0.0050 cm/cm
Linear Mold Shrinkage, Transverse: 0.0080 cm/cm

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale netherlands. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

4 prices for Solvay TECHNYL® A 218W V30 Natural PA66, 30% glass fiber, DRY

Seller from Lagos – 2021-06-25:

Seller from Lagos work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1814 per MT

Seller from Ankara – 2021-07-08:

Seller from Ankara work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1916 per MT

Seller from Miami – 2021-07-16:

Seller from Miami work with company: RTP Company, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1905 per MT

Seller from Ōsaka – 2021-07-21:

Seller from Ōsaka work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1954 per MT