Special Metals Nitinol High-Strength Superelastic Ni-Ti alloy price 1718 per MT

Physical Properties
Density
6.50 g/cc

Mechanical Properties
Tensile Strength, Ultimate
1450 MPa
Tensile Strength, Yield
1280 MPa
Elongation at Break
8.0 %
Elongation at Break
12.5 %
Tensile Set
0.10 %

Thermal Properties
Melting Point
1300 °C

Component Elements Properties
Carbon, C
<= 0.050 %
Iron, Fe
<= 0.050 %
Nickel, Ni
55.4 - 56.4 %
Oxygen, O
<= 0.050 %
Titanium, Ti
43.54 - 44.6 %

Descriptive Properties
Lower superelastic plateau stress, ksi
30
Upper superelastic plateau stress, ksi
70

Alternative products

Kazanorgsintez Bisphenol A, Diphenylpropane accurate 99%

$ 2323/MT

Crystallization Temperature: >= 154 °C
Crystallization Temperature: >= 155 °C
Crystallization Temperature: >= 156.4 °C
Crystallization Temperature: >= 156.6 °C
Crystallization Temperature: >= 156.7 °C

Osprey Metals 80/20 Ni Cr Powder (Grade 80% - 22) accurate 49%

$ 1940/MT

Particle Size: 12 µm
Carbon, C: 0.020 %
Carbon, C: <= 0.10 %
Chromium, Cr: 19 - 21 %
Iron, Fe: <= 0.50 %

SABIC Innovative Plastics LNP LUBRICOMP ZL003 PPE+PS (Asia Pacific) accurate 66%

$ 1720/MT

Density: 1.15 g/cc
Density: 1.15 g/cc
Linear Mold Shrinkage, Flow: 0.0080 cm/cm @Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0083 cm/cm @Time 86400 sec
Linear Mold Shrinkage, Transverse: 0.0087 cm/cm @Time 86400 sec

TIMET TIMETAL® 21S Titanium Alloy (Ti-15Mo-3Nb-3Al-0.2Si, ASTM Grade 21); Aged at 538°C accurate 49%

$ 1695/MT

Density: 4.94 g/cc
Tensile Strength, Ultimate: 1310 MPa
Tensile Strength, Yield: 1210 MPa @Strain 0.200 %
Elongation at Break: 8.0 %
Modulus of Elasticity: 103 - 110 GPa

TIMET TIMETAL® 3-2.5 Titanium Alloy (Ti-3Al-2.5V; ASTM Grade 9) Aged accurate 49%

$ 1719/MT

Density: 4.51 g/cc
Tensile Strength, Ultimate: >= 828 MPa
Tensile Strength, Yield: >= 690 MPa
Elongation at Break: >= 8.0 %
Modulus of Elasticity: 105 - 120 GPa

H.C. Starck Pure Molybdenum WMPP Pellets (99.0%) accurate 66%

$ 1787/MT

Density: >= 7.00 g/cc
Carbon, C: 0.010 %
Carbon, C: <= 0.020 %
Chromium, Cr: 0.025 %
Chromium, Cr: <= 0.050 %

Haynes Hastelloy® W alloy, shielded metal arc welds, aged 1000 hours at 650°C (1200°F) accurate 49%

$ 1706/MT

Density: 9.00 g/cc
Tensile Strength, Ultimate: 885 MPa
Tensile Strength, Ultimate: 535 MPa @Temperature 760 °C
Tensile Strength, Yield: 745 MPa
Tensile Strength, Yield: 390 MPa @Temperature 760 °C

Special Metals Nitinol Body-Temperature Ni-Ti alloy accurate 49%

$ 1511/MT

Density: 6.50 g/cc
Tensile Strength, Ultimate: >= 1240 MPa
Elongation at Break: 8.0 %
Elongation at Break: >= 12 %
Tensile Set: 0.50 %

H.C. Starck Pure Molybdenum OMPP Pellets (99.8%) accurate 66%

$ 2379/MT

Density: >= 7.00 g/cc
Aluminum, Al: 0.0020 %
Aluminum, Al: <= 0.010 %
Calcium, Ca: 0.0010 %
Calcium, Ca: <= 0.010 %

Osprey Metals Co212-e Cobalt Alloy Powder (Grade 80% - 22) accurate 49%

$ 2148/MT

Particle Size: 12 µm
Carbon, C: 0.050 %
Carbon, C: <= 0.20 %
Chromium, Cr: 27 - 30 %
Cobalt, Co: 62.85 %

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, ships for sale norway. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for Special Metals Nitinol High-Strength Superelastic Ni-Ti alloy

Seller from Tokyo – 2021-07-08:

Seller from Tokyo work with company: Solvay, Techmer ES, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1718 per MT