$ 1488/MT
- Density: 7.81 g/cc
- Tensile Strength at Break: 807 MPa @Temperature 704 °C
- Tensile Strength at Break: 979 MPa @Temperature 649 °C
- Tensile Strength at Break: 1034 MPa @Temperature 538 °C
- Tensile Strength at Break: 1076 MPa @Temperature 427 °C
$ 1914/MT
- Density: 8.80 g/cc
- Tensile Strength, Ultimate: 550 MPa
- Tensile Strength, Ultimate: 450 MPa @Temperature 425 °C
- Tensile Strength, Yield: 240 MPa
- Tensile Strength, Yield: 170 MPa @Temperature 425 °C
$ 1481/MT
- Density: 8.44 g/cc
- Hardness, Rockwell B: 96
- Tensile Strength, Ultimate: 1012 MPa
- Tensile Strength, Yield: 609 MPa @Strain 0.200 %
- Elongation at Break: 36 %
$ 1567/MT
- Density: 8.89 g/cc
- Tensile Strength, Ultimate: 1056 MPa
- Tensile Strength, Yield: 903.9 MPa @Strain 0.200 %
- Elongation at Break: 32 %
- Modulus of Elasticity: 205 GPa
$ 2115/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 972 MPa
- Tensile Strength, Yield: 529 MPa @Strain 0.200 %
- Elongation at Break: 42 %
- Modulus of Elasticity: 208 GPa
$ 1709/MT
- Density: 8.08 g/cc
- Tensile Strength, Ultimate: 1334 MPa
- Tensile Strength, Yield: 1114 MPa @Strain 0.200 %
- Elongation at Break: 20 %
- Reduction of Area: 38 %
$ 1479/MT
- Density: 8.19 g/cc
- Hardness, Brinell: 185 - 300
- Hardness, Rockwell B: >= 90
- Hardness, Rockwell C: <= 40
- Tensile Strength, Ultimate: 689 - 1030 MPa
$ 1698/MT
- Density: 8.89 g/cc
- Tensile Strength, Ultimate: 740.5 MPa
- Tensile Strength, Yield: 347 MPa @Strain 0.200 %
- Elongation at Break: 67 %
- Modulus of Elasticity: 205 GPa
$ 2084/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 655 MPa
- Tensile Strength, Ultimate: 550 MPa @Temperature 550 °C
- Tensile Strength, Yield: 310 MPa
- Tensile Strength, Yield: 180 MPa @Temperature 550 °C
$ 2189/MT
- Density: 8.36 g/cc
- Tensile Strength, Ultimate: 570 MPa @Temperature 650 °C
- Tensile Strength, Ultimate: 710 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 340 MPa @Strain 0.200 %
- Tensile Strength, Yield: 220 MPa @Strain 0.200 %, Temperature 650 °C
$ 2384/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 951 MPa
- Tensile Strength, Yield: 563 MPa @Strain 0.200 %
- Elongation at Break: 46 %
- Modulus of Elasticity: 208 GPa
$ 1914/MT
- Density: 8.30 g/cc
- Hardness, Rockwell C: 36
- Tensile Strength, Ultimate: 1240 MPa
- Tensile Strength, Yield: 903 MPa @Strain 0.200 %
- Tensile Strength, Yield: 917 MPa @Strain 0.200 %
$ 2169/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 630 MPa @Temperature 550 °C
- Tensile Strength, Ultimate: 825 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 375 MPa @Strain 0.200 %
- Tensile Strength, Yield: 210 MPa @Strain 0.200 %, Temperature 550 °C
$ 1662/MT
- Density: 8.11 g/cc
- Tensile Strength, Ultimate: 586 - 689 MPa
- Tensile Strength, Yield: 207 - 345 MPa @Strain 0.200 %
- Elongation at Break: 35 - 55 %
- Specific Heat Capacity: 0.448 J/g-°C
$ 2557/MT
- Density: 8.05 g/cc
- Hardness, Rockwell C: 33.6
- Tensile Strength, Ultimate: 1209 MPa
- Tensile Strength, Yield: 818.4 MPa @Strain 0.200 %
- Elongation at Break: 36.4 %
$ 1517/MT
- Density: 8.08 g/cc
- Tensile Strength, Ultimate: 1260 MPa
- Tensile Strength, Yield: 1085 MPa @Strain 0.200 %
- Elongation at Break: 22 %
- Reduction of Area: 43 %
$ 2280/MT
- Density: 8.35 g/cc
- Tensile Strength, Ultimate: 620 MPa
- Tensile Strength, Ultimate: 540 MPa @Temperature 550 °C
- Tensile Strength, Yield: 210 MPa @Strain 0.200 %
- Tensile Strength, Yield: 170 MPa @Strain 0.200 %, Temperature 550 °C
$ 1619/MT
- Density: 8.43 g/cc
- Tensile Strength, Ultimate: 735 MPa
- CTE, linear: 12.5 µm/m-°C @Temperature 20.0 - 500 °C
- Specific Heat Capacity: 0.419 J/g-°C
- Melting Point: 1400 - 1420 °C
$ 1679/MT
- Density: 8.77 g/cc
- Hardness, Brinell: 124
- Hardness, Knoop: 143
- Hardness, Rockwell A: 43
- Hardness, Rockwell B: 70
$ 1718/MT
- Density: 6.50 g/cc
- Tensile Strength, Ultimate: 1450 MPa
- Tensile Strength, Yield: 1280 MPa
- Elongation at Break: 8.0 %
- Elongation at Break: 12.5 %
$ 2289/MT
- Density: 6.50 g/cc
- Tensile Strength, Ultimate: >= 1210 MPa
- Elongation at Break: >= 5.0 %
- Melting Point: 1300 °C
- Carbon, C: <= 0.050 %
$ 2393/MT
- Density: 8.80 g/cc
- Tensile Strength, Ultimate: 550 MPa
- Tensile Strength, Yield: 240 MPa @Strain 0.200 %
- Elongation at Break: 40 %
- CTE, linear: 13.7 µm/m-°C @Temperature 20.0 - 100 °C
$ 1616/MT
- Density: 7.77 g/cc
- Tensile Strength at Break: 882.6 MPa
- Tensile Strength at Break: 937.7 MPa
- Tensile Strength, Yield: 489.5 MPa @Strain 0.200 %
- Tensile Strength, Yield: 530.9 MPa @Strain 0.200 %
$ 1668/MT
- Density: 8.19 g/cc
- Hardness, Brinell: 285 - 360
- Hardness, Rockwell C: 30 - 40
- Tensile Strength, Ultimate: 1030 - 1310 MPa
- Tensile Strength, Yield: 758 - 965 MPa @Strain 0.200 %
$ 1514/MT
- Density: 8.14 g/cc
- Tensile Strength, Ultimate: 1030 MPa @Temperature 550 °C
- Tensile Strength, Ultimate: 1200 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 875 MPa @Strain 0.200 %
- Tensile Strength, Yield: 800 MPa @Strain 0.200 %, Temperature 550 °C
$ 2187/MT
- Density: 8.08 g/cc
- Tensile Strength, Ultimate: 1300 MPa
- Tensile Strength, Yield: 1058 MPa @Strain 0.200 %
- Elongation at Break: 18 %
- Modulus of Elasticity: 210 GPa
$ 1461/MT
- Density: 8.19 g/cc
- Hardness, Brinell: 285 - 360
- Hardness, Rockwell C: 30 - 40
- Tensile Strength, Ultimate: 1030 - 1310 MPa
- Tensile Strength, Yield: 758 - 965 MPa @Strain 0.200 %
$ 2283/MT
- Density: 8.19 g/cc
- Tensile Strength, Ultimate: 1100 MPa @Temperature 650 °C
- Tensile Strength, Ultimate: 1375 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 1100 MPa @Strain 0.200 %
- Tensile Strength, Yield: 980 MPa @Strain 0.200 %, Temperature 650 °C
$ 2115/MT
- Density: 8.89 g/cc
- Tensile Strength, Ultimate: 403 MPa
- Tensile Strength, Ultimate: 350 MPa @Temperature 300 °C
- Tensile Strength, Yield: 103 MPa
- Tensile Strength, Yield: 95.0 MPa @Temperature 300 °C
$ 1851/MT
- Density: 8.72 g/cc
- Tensile Strength, Ultimate: 810.1 MPa
- Tensile Strength, Yield: 359 MPa @Strain 0.200 %
- Elongation at Break: 56 %
- Modulus of Elasticity: 207 GPa
$ 1768/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 915.6 MPa
- Tensile Strength, Yield: 462 MPa @Strain 0.200 %
- Elongation at Break: 48 %
- Modulus of Elasticity: 208 GPa
$ 1604/MT
- Density: 8.08 g/cc
- Tensile Strength, Ultimate: 1320 MPa
- Tensile Strength, Yield: 1100 MPa @Strain 0.200 %
- Elongation at Break: 20 %
- Modulus of Elasticity: 210 GPa
$ 1616/MT
- Density: 8.14 g/cc
- Tensile Strength at Break: 173 MPa @Temperature 1000 °C
- Tensile Strength at Break: 180 MPa @Temperature 1093 °C
- Tensile Strength at Break: 190 MPa @Temperature 1093 °C
- Tensile Strength at Break: 240 MPa @Temperature 982 °C
$ 2475/MT
- Density: 7.94 g/cc
- Tensile Strength, Ultimate: 62.0 MPa @Temperature 1100 °C
- Tensile Strength, Ultimate: 92.0 MPa @Temperature 980 °C
- Tensile Strength, Ultimate: 132 MPa @Temperature 870 °C
- Tensile Strength, Ultimate: 652 MPa @Temperature 22.0 °C
$ 2251/MT
- Density: 8.72 g/cc
- Tensile Strength, Ultimate: 803.2 MPa
- Tensile Strength, Yield: 421 MPa @Strain 0.200 %
- Elongation at Break: 59 %
- Modulus of Elasticity: 207 GPa
$ 1699/MT
- Density: 8.89 g/cc
- Tensile Strength, Ultimate: 796.3 MPa
- Tensile Strength, Yield: 376 MPa @Strain 0.200 %
- Elongation at Break: 60 %
- Modulus of Elasticity: 205 GPa
$ 1452/MT
- Density: 8.19 g/cc
- Tensile Strength, Ultimate: 689 MPa
- Tensile Strength, Yield: 334 MPa @Strain 0.200 %
- Elongation at Break: 50 %
- Modulus of Elasticity: 211 GPa
$ 1489/MT
- Density: 8.28 g/cc
- Tensile Strength, Ultimate: 1120 MPa @Temperature 550 °C
- Tensile Strength, Ultimate: 1250 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 850 MPa @Strain 0.200 %
- Tensile Strength, Yield: 760 MPa @Strain 0.200 %, Temperature 550 °C
$ 1567/MT
- Density: 8.20 g/cc
- Tensile Strength, Ultimate: 520 MPa
- Tensile Strength, Ultimate: 470 MPa @Temperature 300 °C
- Tensile Strength, Yield: 260 MPa @Strain 0.200 %
- Tensile Strength, Yield: 160 MPa @Strain 0.200 %, Temperature 300 °C
$ 2544/MT
- Density: 8.08 g/cc
- Tensile Strength, Ultimate: 1300 MPa
- Tensile Strength, Yield: 1010 MPa @Strain 0.200 %
- Elongation at Break: 18 %
- Reduction of Area: 28 %
$ 1554/MT
- Density: 8.31 g/cc
- Tensile Strength, Ultimate: 760 MPa
- Tensile Strength, Ultimate: 580 MPa @Temperature 550 °C
- Tensile Strength, Yield: 330 MPa @Strain 0.200 %
- Tensile Strength, Yield: 210 MPa @Strain 0.200 %, Temperature 550 °C
$ 1780/MT
- Density: 8.30 g/cc
- Tensile Strength, Ultimate: 950 MPa
- Tensile Strength, Ultimate: 730 MPa @Temperature 550 °C
- Tensile Strength, Yield: 570 MPa
- Tensile Strength, Yield: 500 MPa @Temperature 550 °C
$ 2074/MT
- Density: 8.19 g/cc
- Hardness, Brinell: 135 - 185
- Hardness, Rockwell B: 75 - 90
- Tensile Strength, Ultimate: 621 - 827 MPa
- Tensile Strength, Yield: 207 - 414 MPa @Strain 0.200 %
$ 1709/MT
- Density: 8.19 g/cc
- Hardness, Rockwell C: 25 - 34
- Tensile Strength, Ultimate: 896 - 1070 MPa
- Elongation at Break: 3.0 - 15 %
- Modulus of Elasticity: 207 GPa
$ 1510/MT
- Density: 8.19 g/cc
- Hardness, Brinell: 300 - 375
- Hardness, Rockwell C: 32 - 42
- Tensile Strength, Ultimate: 1100 - 1380 MPa
- Tensile Strength, Yield: 793 - 1030 MPa @Strain 0.200 %
$ 2215/MT
- Density: 8.19 g/cc
- Hardness, Brinell: 140 - 240
- Hardness, Rockwell B: >= 75
- Hardness, Rockwell C: <= 22
- Tensile Strength, Ultimate: 621 - 896 MPa
$ 2114/MT
- Density: 8.19 g/cc
- Hardness, Rockwell C: 35 - 45
- Tensile Strength, Ultimate: 1240 - 1590 MPa
- Elongation at Break: 5.0 - 15 %
- Modulus of Elasticity: 207 GPa
$ 2220/MT
- Density: 8.19 g/cc
- Tensile Strength, Ultimate: 1100 - 1380 MPa
- Elongation at Break: 2.0 - 5.0 %
- Modulus of Elasticity: 207 GPa
- Poissons Ratio: 0.31
$ 1628/MT
- Density: 8.19 g/cc
- Tensile Strength, Ultimate: 1380 - 1650 MPa
- Elongation at Break: 5.0 - 10 %
- Modulus of Elasticity: 207 GPa
- Poissons Ratio: 0.31
$ 2206/MT
- Density: 8.19 g/cc
- Rupture Strength: 69.0 MPa @Temperature 871 °C, Time 3.60e+6 sec
- Rupture Strength: 145 MPa @Temperature 816 °C, Time 3.60e+6 sec
- Rupture Strength: 250 MPa @Temperature 760 °C, Time 3.60e+6 sec
- Rupture Strength: 380 MPa @Temperature 704 °C, Time 3.60e+6 sec
$ 1481/MT
- Density: 8.30 g/cc
- Hardness, Rockwell C: 5.0
- Tensile Strength, Ultimate: 783.2 MPa
- Tensile Strength, Yield: 334 MPa @Strain 0.200 %
- Elongation at Break: 60 %
$ 1467/MT
- Density: 8.91 g/cc
- Thickness: 203 microns
- Hardness, Vickers: 102
- Tensile Strength, Ultimate: 352 MPa
- Tensile Strength, Ultimate: 359 MPa
$ 2344/MT
- Density: 8.19 g/cc
- Tensile Strength, Ultimate: 1030 MPa @Temperature 650 °C
- Tensile Strength, Ultimate: 1250 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 780 MPa @Strain 0.200 %
- Tensile Strength, Yield: 710 MPa @Strain 0.200 %, Temperature 650 °C
$ 1453/MT
- Density: 8.89 g/cc
- Tensile Strength, Ultimate: 415 MPa
- Tensile Strength, Yield: 145 MPa @Strain 0.200 %
- Elongation at Break: 32 %
- CTE, linear: 14.7 µm/m-°C @Temperature 20.0 - 100 °C
$ 1488/MT
- Density: 8.08 g/cc
- Tensile Strength, Ultimate: 1280 MPa
- Tensile Strength, Yield: 1024 MPa @Strain 0.200 %
- Elongation at Break: 22 %
- Modulus of Elasticity: 210 GPa
$ 1746/MT
- Density: 8.44 g/cc
- Hardness, Rockwell B: 100
- Tensile Strength, Ultimate: 1040 MPa
- Tensile Strength, Yield: 835.6 MPa @Strain 0.200 %
- Elongation at Break: 31 %
$ 1733/MT
- Density: 8.21 g/cc
- Tensile Strength at Break: 350 MPa @Temperature 950 °C
- Tensile Strength at Break: 1150 MPa @Temperature 700 °C
- Tensile Strength at Break: 1250 MPa @Temperature 400 °C
- Tensile Strength at Break: 1300 MPa @Temperature 50.0 °C
$ 2540/MT
- Density: 8.89 g/cc
- Tensile Strength, Ultimate: 1100 MPa
- Tensile Strength, Yield: 921.1 MPa @Strain 0.200 %
- Elongation at Break: 29 %
- Modulus of Elasticity: 205 GPa
$ 1458/MT
- Density: 8.02 g/cc
- Hardness, Rockwell B: 82 @Temperature 20.0 °C
- Tensile Strength at Break: 161.3 MPa @Temperature 871 °C
- Tensile Strength at Break: 282 MPa @Temperature 759 °C
- Tensile Strength at Break: 402.7 MPa @Temperature 538 °C
$ 1521/MT
- Density: 8.30 g/cc
- Tensile Strength, Ultimate: >= 621 MPa
- Tensile Strength, Yield: >= 241 MPa @Strain 0.200 %
- Elongation at Break: >= 45 %
- Modulus of Elasticity: 199 GPa
$ 1465/MT
- Density: 8.44 g/cc
- Hardness, Rockwell B: 96
- Tensile Strength, Ultimate: 957.0 MPa
- Tensile Strength, Yield: 535 MPa @Strain 0.200 %
- Elongation at Break: 45 %
$ 1450/MT
- Density: 8.89 g/cc
- Tensile Strength, Ultimate: 1149 MPa
- Tensile Strength, Yield: 987.3 MPa @Strain 0.200 %
- Elongation at Break: 28 %
- Modulus of Elasticity: 205 GPa
$ 1727/MT
- Density: 8.89 g/cc
- Tensile Strength, Ultimate: 345 MPa
- Tensile Strength, Yield: 110 MPa @Strain 0.200 %
- Elongation at Break: 50 %
- CTE, linear: 13.3 µm/m-°C @Temperature 20.0 - 100 °C
$ 1491/MT
- Density: 8.30 g/cc
- Hardness, Rockwell C: 39
- Tensile Strength, Ultimate: 1346 MPa
- Tensile Strength, Yield: 991.5 MPa @Strain 0.200 %
- Elongation at Break: 27 %
$ 1698/MT
- Density: 8.18 g/cc
- Tensile Strength, Ultimate: 1030 MPa @Temperature 550 °C
- Tensile Strength, Ultimate: 1150 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 725 MPa @Strain 0.200 %
- Tensile Strength, Yield: 690 MPa @Strain 0.200 %, Temperature 550 °C
$ 1481/MT
- Density: 8.08 g/cc
- Rupture Strength: 68.0 MPa @Temperature 982 °C, Time 3.60e+6 sec
- Rupture Strength: 219 MPa @Temperature 871 °C, Time 3.60e+6 sec
- Rupture Strength: 480 MPa @Temperature 760 °C, Time 3.60e+6 sec
- Rupture Strength: 500 MPa @Temperature 704 °C, Time 3.60e+6 sec
$ 1986/MT
- Density: 8.08 g/cc
- Rupture Strength: 68.0 MPa @Temperature 982 °C, Time 3.60e+6 sec
- Rupture Strength: 219 MPa @Temperature 871 °C, Time 3.60e+6 sec
- Rupture Strength: 480 MPa @Temperature 760 °C, Time 3.60e+6 sec
- Rupture Strength: 500 MPa @Temperature 704 °C, Time 3.60e+6 sec
$ 2514/MT
- Density: 8.08 g/cc
- Rupture Strength: 68.0 MPa @Temperature 982 °C, Time 3.60e+6 sec
- Rupture Strength: 219 MPa @Temperature 871 °C, Time 3.60e+6 sec
- Rupture Strength: 480 MPa @Temperature 760 °C, Time 3.60e+6 sec
- Rupture Strength: 500 MPa @Temperature 704 °C, Time 3.60e+6 sec
$ 1605/MT
- Density: 8.08 g/cc
- Rupture Strength: 68.0 MPa @Temperature 982 °C, Time 3.60e+6 sec
- Rupture Strength: 219 MPa @Temperature 871 °C, Time 3.60e+6 sec
- Rupture Strength: 480 MPa @Temperature 760 °C, Time 3.60e+6 sec
- Rupture Strength: 500 MPa @Temperature 704 °C, Time 3.60e+6 sec
$ 1509/MT
- Density: 8.08 g/cc
- Rupture Strength: 68.0 MPa @Temperature 982 °C, Time 3.60e+6 sec
- Rupture Strength: 219 MPa @Temperature 871 °C, Time 3.60e+6 sec
- Rupture Strength: 480 MPa @Temperature 760 °C, Time 3.60e+6 sec
- Rupture Strength: 500 MPa @Temperature 704 °C, Time 3.60e+6 sec
$ 1580/MT
- Density: 8.86 g/cc
- CTE, linear: 12.9 µm/m-°C @Temperature 20.0 - 100 °C
- Specific Heat Capacity: 0.430 J/g-°C
- Thermal Conductivity: 44.0 W/m-K
- Melting Point: 1435 - 1446 °C
$ 1847/MT
- Density: 8.91 g/cc
- Thickness: 102 microns
- Hardness, Vickers: 205
- Tensile Strength, Ultimate: 572 MPa
- Elongation at Break: 9.0 %
$ 1767/MT
- Density: 8.54 g/cc
- Tensile Strength, Ultimate: 620 MPa @Temperature 650 °C
- Tensile Strength, Ultimate: 825 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 410 MPa @Strain 0.200 %
- Tensile Strength, Yield: 240 MPa @Strain 0.200 %, Temperature 650 °C
$ 2208/MT
- Density: 8.89 g/cc
- Tensile Strength, Ultimate: 345 MPa
- Tensile Strength, Yield: 90.0 MPa @Strain 0.200 %
- Elongation at Break: 45 %
- CTE, linear: 13.3 µm/m-°C @Temperature 20.0 - 100 °C
$ 1458/MT
- Density: 8.44 g/cc
- Hardness, Rockwell B: 84
- Tensile Strength, Ultimate: 769.5 MPa
- Tensile Strength, Yield: 319 MPa @Strain 0.200 %
- Elongation at Break: 63 %
$ 1493/MT
- Density: 6.50 g/cc
- Tensile Strength, Ultimate: >= 1450 MPa
- Elongation at Break: 8.0 %
- Elongation at Break: >= 10 %
- Tensile Set: 0.50 %
$ 1586/MT
- Density: 8.21 g/cc
- Tensile Strength, Ultimate: 1020 MPa @Temperature 650 °C
- Tensile Strength, Ultimate: 1150 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 750 MPa @Strain 0.200 %
- Tensile Strength, Yield: 720 MPa @Strain 0.200 %, Temperature 650 °C
$ 2130/MT
- Density: 8.91 g/cc
- Thickness: 12.7 microns
- Hardness, Vickers: 60
- Tensile Strength, Ultimate: 290 MPa
- Tensile Strength, Ultimate: 300 MPa
$ 1462/MT
- Density: 8.19 g/cc
- Tensile Strength, Ultimate: 648 MPa
- Tensile Strength, Yield: 282 MPa @Strain 0.200 %
- Elongation at Break: 52 %
- Modulus of Elasticity: 211 GPa
$ 1965/MT
- Density: 8.72 g/cc
- Tensile Strength, Ultimate: 721.9 MPa
- Tensile Strength, Yield: 364 MPa @Strain 0.200 %
- Elongation at Break: 71 %
- Modulus of Elasticity: 207 GPa
$ 1721/MT
- Density: 8.02 g/cc
- Tensile Strength, Ultimate: 720 MPa @Temperature 550 °C
- Tensile Strength, Ultimate: 900 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 450 MPa @Strain 0.200 %
- Tensile Strength, Yield: 380 MPa @Strain 0.200 %, Temperature 550 °C
$ 1793/MT
- Density: 8.19 g/cc
- Hardness, Rockwell B: <= 90
- Tensile Strength, Ultimate: 621 - 827 MPa
- Tensile Strength, Yield: 241 - 414 MPa @Strain 0.200 %
- Elongation at Break: 30 - 50 %
$ 1509/MT
- Density: 6.50 g/cc
- Tensile Strength, Ultimate: 1070 MPa
- Tensile Strength, Yield: 814 MPa
- Elongation at Break: 8.0 %
- Elongation at Break: 17.5 %
$ 1681/MT
- Density: 8.02 g/cc
- Tensile Strength, Ultimate: 950 MPa @Temperature 650 °C
- Tensile Strength, Ultimate: 1060 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 700 MPa @Strain 0.200 %
- Tensile Strength, Yield: 680 MPa @Strain 0.200 %, Temperature 650 °C
$ 2068/MT
- Density: 8.19 g/cc
- Tensile Strength, Ultimate: 758 MPa
- Tensile Strength, Yield: 461 MPa @Strain 0.200 %
- Elongation at Break: 39 %
- Modulus of Elasticity: 211 GPa
$ 1774/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 973.5 MPa
- Tensile Strength, Yield: 527 MPa @Strain 0.200 %
- Elongation at Break: 42 %
- Modulus of Elasticity: 208 GPa
$ 2400/MT
- Density: 8.01 g/cc
- Tensile Strength, Ultimate: 1030 MPa @Temperature 650 °C
- Tensile Strength, Ultimate: 1150 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 770 MPa @Strain 0.200 %
- Tensile Strength, Yield: 720 MPa @Strain 0.200 %, Temperature 650 °C
$ 1848/MT
- Density: 8.08 g/cc
- Tensile Strength, Ultimate: 1280 MPa
- Tensile Strength, Yield: 993 MPa @Strain 0.200 %
- Elongation at Break: 19 %
- Reduction of Area: 28 %
$ 1730/MT
- Density: 8.89 g/cc
- Tensile Strength, Ultimate: 790 MPa
- Tensile Strength, Ultimate: 620 MPa @Temperature 550 °C
- Tensile Strength, Yield: 415 MPa
- Tensile Strength, Yield: 230 MPa @Temperature 550 °C
$ 1447/MT
- Density: 8.19 g/cc
- Tensile Strength, Ultimate: 703 MPa
- Tensile Strength, Yield: 352 MPa @Strain 0.200 %
- Elongation at Break: 46 %
- Modulus of Elasticity: 211 GPa
$ 1991/MT
- Density: 8.19 g/cc
- Hardness, Rockwell C: 30 - 40
- Tensile Strength, Ultimate: 1100 - 1310 MPa
- Elongation at Break: 10 - 25 %
- Modulus of Elasticity: 207 GPa
$ 1959/MT
- Density: 8.19 g/cc
- Tensile Strength, Ultimate: 621 - 827 MPa
- Elongation at Break: 25 - 50 %
- Modulus of Elasticity: 207 GPa
- Poissons Ratio: 0.31
$ 1480/MT
- Density: 8.91 g/cc
- Rupture Strength: 62.1 MPa @Temperature 927 °C, Time 270000 sec
- Modulus of Elasticity: 167 GPa @Temperature 800 °C
- Modulus of Elasticity: 175 GPa @Temperature 700 °C
- Modulus of Elasticity: 183 GPa @Temperature 600 °C
$ 2032/MT
- Density: 8.19 g/cc
- Tensile Strength, Ultimate: 738 MPa
- Tensile Strength, Yield: 372 MPa @Strain 0.200 %
- Elongation at Break: 44 %
- Modulus of Elasticity: 211 GPa
$ 2169/MT
- Density: 8.72 g/cc
- Tensile Strength, Ultimate: 732.9 MPa
- Tensile Strength, Yield: 399 MPa @Strain 0.200 %
- Elongation at Break: 68 %
- Modulus of Elasticity: 207 GPa
$ 1665/MT
- Density: 8.22 g/cc
- Hardness, Rockwell C: 45
- Tensile Strength, Ultimate: 1550 MPa
- Tensile Strength, Yield: 1390 MPa @Strain 0.200 %
- Elongation at Break: 16 %
$ 1911/MT
- Density: 8.06 g/cc
- Tensile Strength, Ultimate: 830 MPa @Temperature 650 °C
- Tensile Strength, Ultimate: 1050 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 600 MPa @Strain 0.200 %
- Tensile Strength, Yield: 520 MPa @Strain 0.200 %, Temperature 650 °C
$ 2206/MT
- Density: 8.22 g/cc
- Hardness, Rockwell B: 90
- Tensile Strength, Ultimate: 793 MPa
- Tensile Strength, Yield: 345 MPa @Strain 0.200 %
- Elongation at Break: 45.5 %
$ 2311/MT
- Density: 6.50 g/cc
- Tensile Strength, Ultimate: >= 1550 MPa
- Elongation at Break: 8.0 %
- Elongation at Break: >= 10 %
- Tensile Set: 0.10 %
$ 1892/MT
- Density: 7.85 g/cc
- Tensile Strength, Ultimate: 1140 MPa @Temperature 550 °C
- Tensile Strength, Ultimate: 1300 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 850 MPa @Strain 0.200 %
- Tensile Strength, Yield: 720 MPa @Strain 0.200 %, Temperature 550 °C
$ 1828/MT
- Density: 8.19 g/cc
- Tensile Strength, Ultimate: 1100 - 1310 MPa
- Elongation at Break: 10 - 25 %
- Modulus of Elasticity: 207 GPa
- Poissons Ratio: 0.31
$ 1539/MT
- Density: 8.89 g/cc
- Tensile Strength, Ultimate: 726.7 MPa
- Tensile Strength, Yield: 313 MPa @Strain 0.200 %
- Elongation at Break: 70 %
- Modulus of Elasticity: 205 GPa
$ 1863/MT
- Density: 8.91 g/cc
- Tensile Strength at Break: 483 MPa
- Tensile Strength at Break: 655 MPa
- Tensile Strength at Break: 758 MPa
- Tensile Strength, Yield: 172 MPa
$ 1897/MT
- Density: 8.61 g/cc
- Hardness, Rockwell B: 89
- Hardness, Rockwell B: 89
- Hardness, Rockwell B: 93
- Tensile Strength at Break: 772 MPa
$ 1790/MT
- Density: 8.11 g/cc
- Tensile Strength, Ultimate: 620 MPa @Temperature 550 °C
- Tensile Strength, Ultimate: 760 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 450 MPa @Strain 0.200 %
- Tensile Strength, Yield: 330 MPa @Strain 0.200 %, Temperature 550 °C
$ 1511/MT
- Density: 6.50 g/cc
- Tensile Strength, Ultimate: >= 1240 MPa
- Elongation at Break: 8.0 %
- Elongation at Break: >= 12 %
- Tensile Set: 0.50 %
$ 2048/MT
- Density: 8.72 g/cc
- Tensile Strength, Ultimate: 848 MPa
- Tensile Strength, Yield: 408 MPa @Strain 0.200 %
- Elongation at Break: 59 %
- Modulus of Elasticity: 207 GPa
$ 1938/MT
- Density: 8.89 g/cc
- Tensile Strength, Ultimate: 758 MPa
- Tensile Strength, Yield: 363 MPa @Strain 0.200 %
- Elongation at Break: 62 %
- Modulus of Elasticity: 205 GPa
$ 1531/MT
- Density: 8.19 g/cc
- Tensile Strength, Ultimate: 724 MPa
- Tensile Strength, Yield: 348 MPa @Strain 0.200 %
- Elongation at Break: 41 %
- Modulus of Elasticity: 211 GPa
$ 1674/MT
- Density: 8.89 g/cc
- Tensile Strength, Ultimate: 441 MPa
- Tensile Strength, Yield: 134 MPa @Strain 0.200 %
- Elongation at Break: 51 %
- CTE, linear: 13.7 µm/m-°C @Temperature 20.0 - 100 °C
$ 1472/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 880 MPa
- Tensile Strength, Ultimate: 760 MPa @Temperature 650 °C
- Tensile Strength, Yield: 460 MPa
- Tensile Strength, Yield: 290 MPa @Temperature 650 °C
$ 1723/MT
- Density: 8.25 g/cc
- Rupture Strength: 76.0 MPa @Temperature 927 °C, Time 3.60e+6 sec
- Rupture Strength: 117 MPa @Temperature 871 °C, Time 3.60e+6 sec
- Rupture Strength: 200 MPa @Temperature 816 °C, Time 3.60e+6 sec
- Rupture Strength: 345 MPa @Temperature 760 °C, Time 3.60e+6 sec
$ 1894/MT
- Density: 8.44 g/cc
- Hardness, Rockwell B: 95
- Tensile Strength, Ultimate: 836.3 MPa
- Tensile Strength, Yield: 390 MPa @Strain 0.200 %
- Elongation at Break: 50 %
$ 1623/MT
- Density: 8.19 g/cc
- Hardness, Rockwell C: 30 - 40
- Tensile Strength, Ultimate: 1070 - 1310 MPa
- Elongation at Break: 2.0 - 10 %
- Modulus of Elasticity: 207 GPa
$ 2052/MT
- Density: 6.50 g/cc
- Tensile Strength, Ultimate: >= 1240 MPa
- Elongation at Break: 8.0 %
- Elongation at Break: >= 12 %
- Melting Point: 1300 °C
$ 1633/MT
- Density: 7.86 g/cc
- Tensile Strength at Break: 552 - 621 MPa
- Tensile Strength at Break: 572 - 607 MPa
- Tensile Strength at Break: 572 - 607 MPa
- Tensile Strength at Break: 586 - 627 MPa
$ 1751/MT
- Density: 8.37 g/cc
- Tensile Strength, Ultimate: 750 MPa
- Tensile Strength, Ultimate: 660 MPa @Temperature 550 °C
- Tensile Strength, Yield: 275 MPa
- Tensile Strength, Yield: 210 MPa @Temperature 550 °C
$ 2111/MT
- Density: 8.14 g/cc
- CTE, linear: 12.47 µm/m-°C @Temperature 25.0 - 92.0 °C
- CTE, linear: 13.18 µm/m-°C @Temperature 25.0 - 316 °C
- CTE, linear: 14.11 µm/m-°C @Temperature 25.0 - 482 °C
- CTE, linear: 15.03 µm/m-°C @Temperature 25.0 - 760 °C
$ 1530/MT
- Density: 8.08 g/cc
- Tensile Strength, Ultimate: 1330 MPa
- Tensile Strength, Yield: 1090 MPa @Strain 0.200 %
- Elongation at Break: 21 %
- Reduction of Area: 55 %
$ 1527/MT
- Density: 8.91 g/cc
- Thickness: 6.10 microns
- Tensile Strength, Ultimate: 827 MPa
- Elongation at Break: <= 0.50 %
- Carbon, C: <= 0.010 %
$ 2418/MT
- Density: 8.36 g/cc
- Tensile Strength, Ultimate: 760 MPa @Temperature 650 °C
- Tensile Strength, Ultimate: 940 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 550 MPa @Strain 0.200 %
- Tensile Strength, Yield: 450 MPa @Strain 0.200 %, Temperature 650 °C
$ 1718/MT
- Density: 8.08 g/cc
- Tensile Strength at Break: 96.0 MPa @Temperature 1000 °C
- Tensile Strength at Break: 365 MPa @Temperature 900 °C
- Tensile Strength at Break: 644 MPa @Temperature 800 °C
- Tensile Strength at Break: 947 MPa @Temperature 700 °C
$ 2292/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 971.5 MPa
- Tensile Strength, Yield: 525 MPa @Strain 0.200 %
- Elongation at Break: 46 %
- Modulus of Elasticity: 208 GPa
$ 1542/MT
- Density: 8.19 g/cc
- Hardness, Rockwell C: 33 - 42
- Tensile Strength, Ultimate: 1170 - 1450 MPa
- Elongation at Break: 7.0 - 20 %
- Modulus of Elasticity: 207 GPa
$ 1491/MT
- Density: 8.05 g/cc
- Tensile Strength, Ultimate: 745 MPa
- Tensile Strength, Yield: 288 MPa @Strain 0.200 %
- Elongation at Break: 50 %
- Reduction of Area: 55 %
$ 2119/MT
- Density: 8.30 g/cc
- Hardness, Rockwell C: 5.0
- Tensile Strength, Ultimate: 855 MPa
- Tensile Strength, Yield: 427 MPa @Strain 0.200 %
- Elongation at Break: 57 %
$ 1755/MT
- Density: 8.19 g/cc
- Hardness, Brinell: 300 - 380
- Hardness, Rockwell C: 32 - 42
- Tensile Strength, Ultimate: 1170 - 1450 MPa
- Tensile Strength, Yield: 862 - 1210 MPa @Strain 0.200 %
$ 1704/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 931 MPa
- Tensile Strength, Yield: 478 MPa @Strain 0.200 %
- Elongation at Break: 48 %
- Modulus of Elasticity: 208 GPa
$ 1637/MT
- Density: 8.19 g/cc
- Hardness, Rockwell C: 24
- Tensile Strength, Ultimate: 1120 MPa
- Tensile Strength, Yield: 827 MPa @Strain 0.200 %
- Elongation at Break: 31 %
Delivery Nickel Alloy Special Metals (includes the former Inco Alloys International Inc.)
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
cruise ship sales. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.