Styron CALIBREâ„¢ 2061-6 Polycarbonate Resin price 1651 per MT

Physical Properties
Density
1.20 g/cc
Water Absorption
0.32 % @Temperature 23.0 °C
Water Absorption
0.15 % @Temperature 23.0 °C, Time 86400 sec
Maximum Moisture Content
0.020
Linear Mold Shrinkage, Flow
0.0050 - 0.0070 cm/cm
Melt Flow
6.0 g/10 min @Load 1.20 kg, Temperature 300 °C

Mechanical Properties
Hardness, Rockwell M
73
Hardness, Rockwell R
118
Tensile Strength at Break
68.3 MPa
Tensile Strength, Yield
62.1 MPa
Elongation at Break
150 %
Elongation at Yield
6.0 %
Tensile Modulus
2.41 GPa
Flexural Strength
96.5 MPa
Flexural Modulus
2.41 GPa
Izod Impact, Notched
8.50 J/cm @Temperature 23.0 °C
Izod Impact, Unnotched (ISO)
NB @Temperature 23.0 °C
Tensile Impact Strength
567 kJ/m²
Dart Drop, Total Energy
89.3 J
Abrasion
45

Thermal Properties
CTE, linear, Parallel to Flow
68.0 µm/m-°C @Temperature -40.0 - 82.0 °C
Deflection Temperature at 0.46 MPa (66 psi)
145 °C
Deflection Temperature at 1.8 MPa (264 psi)
129 °C
Deflection Temperature at 1.8 MPa (264 psi)
142 °C
Vicat Softening Point
156 °C @Load 5.10 kg
Oxygen Index
26 %

Electrical Properties
Volume Resistivity
2.00e+17 ohm-cm
Dielectric Constant
3.0 @Frequency 60.0 Hz
Dielectric Constant
3.0 @Frequency 1.00e+6 Hz
Dielectric Strength
17.0 kV/mm
Dissipation Factor
0.0010 @Frequency 50.0 Hz
Dissipation Factor
0.0020 @Frequency 1.00e+6 Hz

Processing Properties
Rear Barrel Temperature
271 - 288 °C
Middle Barrel Temperature
277 - 299 °C
Front Barrel Temperature
299 - 327 °C
Nozzle Temperature
299 - 327 °C
Melt Temperature
299 - 327 °C
Mold Temperature
76.7 - 110 °C
Drying Temperature
121 °C
Dry Time
3.00 hour
Screw Speed
40 - 70 rpm

Alternative products

Styron CALIBREâ„¢ 301V-6 Polycarbonate Resin accurate 69%

$ 1938/MT

Density: 1.20 g/cc
Water Absorption: 0.25 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C

Styron CALIBREâ„¢ 301-6 Polycarbonate Resin accurate 84%

$ 2512/MT

Density: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C

Styron CALIBREâ„¢ 300-6 Polycarbonate Resin accurate 84%

$ 1854/MT

Density: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C

Styron CALIBREâ„¢ 201-6 Polycarbonate Resin accurate 80%

$ 1452/MT

Density: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C

Styron CALIBREâ„¢ 300-10 Polycarbonate Resin accurate 73%

$ 1526/MT

Density: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C

Styron CALIBREâ„¢ 200-6 Polycarbonate Resin accurate 80%

$ 1502/MT

Density: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C

Styron CALIBREâ„¢ 302-6 Polycarbonate Resin accurate 88%

$ 1666/MT

Density: 1.20 g/cc
Water Absorption: 0.25 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C

Styron CALIBREâ„¢ MEGARAD 2081-15 Polycarbonate Resin accurate 69%

$ 1677/MT

Density: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C

Styron CALIBREâ„¢ 302-10 Polycarbonate Resin accurate 73%

$ 1494/MT

Density: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, cruise ship sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for Styron CALIBREâ„¢ 2061-6 Polycarbonate Resin

Seller from Hāora – 2021-08-06:

Seller from Hāora work with company: Solvay, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2343 per MT

Seller from Hanoi – 2021-03-30:

Seller from Hanoi work with company: Solvay, Exxon Chemical, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1651 per MT