Styron CALIBREâ„¢ MEGARAD 2081-HD-15 2 Polycarbonate Resin price 2223 per MT

Physical Properties
Density
1.20 g/cc
Water Absorption
0.32 % @Temperature 23.0 °C
Water Absorption
0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow
0.0050 - 0.0070 cm/cm
Melt Flow
15 g/10 min @Load 1.20 kg, Temperature 300 °C

Mechanical Properties
Hardness, Rockwell R
118
Tensile Strength at Break
68.0 MPa
Tensile Strength at Break
68.3 MPa
Tensile Strength, Yield
62.0 MPa
Tensile Strength, Yield
62.1 MPa
Elongation at Break
150 %
Elongation at Yield
6.0 %
Tensile Modulus
2.21 GPa
Tensile Modulus
2.30 GPa
Flexural Strength
96.5 MPa
Flexural Strength
98.0 MPa
Flexural Modulus
2.40 GPa
Flexural Modulus
2.41 GPa
Izod Impact, Notched (ISO)
75.0 kJ/m² @Temperature 23.0 °C
Izod Impact, Unnotched (ISO)
NB @Temperature 23.0 °C
Charpy Impact, Notched
2.50 J/cm² @Temperature 23.0 °C
Tensile Impact Strength
378 kJ/m²
Dart Drop, Total Energy
81.3 J
Abrasion
45

Thermal Properties
CTE, linear, Parallel to Flow
68.0 µm/m-°C @Temperature -40.0 - 82.0 °C
Deflection Temperature at 0.46 MPa (66 psi)
139 °C
Deflection Temperature at 1.8 MPa (264 psi)
120 °C
Deflection Temperature at 1.8 MPa (264 psi)
122 °C
Deflection Temperature at 1.8 MPa (264 psi)
136 °C
Vicat Softening Point
143 °C
Vicat Softening Point
148 °C @Load 5.10 kg

Optical Properties
Refractive Index
1.586
Haze
0.60 %
Transmission, Visible
89 %

Electrical Properties
Volume Resistivity
2.00e+17 ohm-cm
Dielectric Constant
3.0 @Frequency 60.0 Hz
Dielectric Constant
3.0 @Frequency 1.00e+6 Hz
Dielectric Strength
17.0 kV/mm
Dielectric Strength
17.0 kV/mm
Dissipation Factor
0.0010 @Frequency 50.0 Hz
Dissipation Factor
0.0020 @Frequency 1.00e+6 Hz

Alternative products

Styron CALIBREâ„¢ 301-6 Polycarbonate Resin accurate 62%

$ 2512/MT

Density: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C

Styron CALIBREâ„¢ 300-6 Polycarbonate Resin accurate 62%

$ 1854/MT

Density: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C

Styron CALIBREâ„¢ 201-6 Polycarbonate Resin accurate 62%

$ 1452/MT

Density: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C

Styron CALIBREâ„¢ 200-6 Polycarbonate Resin accurate 62%

$ 1502/MT

Density: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C

Styron CALIBREâ„¢ 302-6 Polycarbonate Resin accurate 67%

$ 1666/MT

Density: 1.20 g/cc
Water Absorption: 0.25 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C

Styron CALIBREâ„¢ 2061-15 Polycarbonate Resin accurate 94%

$ 1622/MT

Density: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C

Styron CALIBREâ„¢ 2061 HD 15 Polycarbonate Resin accurate 84%

$ 1923/MT

Density: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C

Styron CALIBREâ„¢ MEGARAD 2081-15 Polycarbonate Resin accurate 94%

$ 1677/MT

Density: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C

Styron CALIBREâ„¢ 201-22 Polycarbonate Resin accurate 60%

$ 1490/MT

Density: 1.20 g/cc
Water Absorption: 0.32 % @Temperature 23.0 °C
Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, cargo ship sales. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for Styron CALIBREâ„¢ MEGARAD 2081-HD-15 2 Polycarbonate Resin

Seller from Los Angeles – 2021-03-14:

Seller from Los Angeles work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2223 per MT