Victrex® PEEK 90GL60 Polyetheretherketone, 60% Glass Fibre Reinforced price 2181 per MT

Physical Properties
Density
1.83 g/cc
Water Absorption at Saturation
0.40 % @Temperature 23.0 °C
Viscosity
525000 cP @Temperature 400 °C
Linear Mold Shrinkage, Flow
0.0030 cm/cm
Linear Mold Shrinkage, Transverse
0.0060 cm/cm
Spiral Flow
10.0 cm @Thickness 1.00 mm

Mechanical Properties
Hardness, Shore D
87 @Temperature 23.0 °C
Tensile Strength at Break
50.0 MPa @Temperature 275 °C
Tensile Strength at Break
90.0 MPa @Temperature 175 °C
Tensile Strength at Break
150 MPa @Temperature 125 °C
Tensile Strength at Break
240 MPa @Temperature 23.0 °C
Elongation at Break
1.5 % @Temperature 23.0 °C
Tensile Modulus
25.0 GPa @Temperature 23.0 °C
Flexural Strength
360 MPa @Temperature 23.0 °C
Flexural Modulus
23.5 GPa @Temperature 23.0 °C
Compressive Strength
65.0 MPa @Temperature 200 °C
Compressive Strength
140 MPa @Temperature 120 °C
Compressive Strength
230 MPa @Temperature 23.0 °C
Izod Impact, Notched (ISO)
11.5 kJ/m² @Temperature 23.0 °C
Izod Impact, Unnotched (ISO)
50.0 kJ/m² @Temperature 23.0 °C

Thermal Properties
CTE, linear
30.0 µm/m-°C @Temperature <=143 °C
CTE, linear
70.0 µm/m-°C @Temperature >=143 °C
CTE, linear, Parallel to Flow
13.0 µm/m-°C @Temperature <=143 °C
CTE, linear, Parallel to Flow
15.0 µm/m-°C @Temperature >=143 °C
Thermal Conductivity
0.550 W/m-K @Temperature 23.0 °C
Melting Point
343 °C
Deflection Temperature at 1.8 MPa (264 psi)
343 °C
Glass Transition Temp, Tg
143 °C
Glow Wire Test
960 °C @Thickness 2.00 mm

Electrical Properties
Volume Resistivity
1.00e+16 ohm-cm
Dielectric Constant
3.8 @Frequency 1000 Hz, Temperature 23.0 °C
Dielectric Strength
22.0 kV/mm @Thickness 2.50 mm
Dissipation Factor
0.0040 @Frequency 1.00e+6 Hz, Temperature 23.0 °C
Comparative Tracking Index
150 V

Processing Properties
Processing Temperature
<= 100 °C
Nozzle Temperature
380 °C
Mold Temperature
180 - 210 °C
Drying Temperature
120 °C @Time 18000 sec
Drying Temperature
150 °C @Time 10800 sec

Alternative products

Victrex® PEEK 90GL30 BLACK EU 30% Glass Fiber Filled, PolyEtherEtherKetone accurate 77%

$ 1470/MT

Density: 1.52 g/cc
Water Absorption at Saturation: 0.30 % @Temperature 23.0 °C
Water Absorption at Saturation: 0.45 % @Temperature 100 °C
Viscosity: 200000 cP @Temperature 400 °C
Linear Mold Shrinkage, Flow: 0.0030 cm/cm

Victrex® PEEK 450GL20 Polyetheretherketone, 20% Glass Fibre Reinforced accurate 99%

$ 1559/MT

Density: 1.43 g/cc
Water Absorption at Saturation: 0.40 % @Temperature 23.0 °C
Water Absorption at Saturation: 0.45 % @Temperature 100 °C
Viscosity: 475000 cP @Temperature 400 °C
Linear Mold Shrinkage, Flow: 0.0030 cm/cm

Lanxess Durethan® AKV 40 H2.0 901510 Nylon 66, Glass Fiber Reinforced accurate 88%

$ 2262/MT

Specific Gravity: 1.46 g/cc
Moisture Absorption at Equilibrium: 1.7 %
Water Absorption at Saturation: 4.5 %
Linear Mold Shrinkage, Flow: 0.00030 cm/cm
Linear Mold Shrinkage, Flow: 0.00050 cm/cm

Victrex® PEEK 90GL30 Polyetheretherketone, 30% Glass Fiber Reinforced accurate 88%

$ 1570/MT

Density: 1.52 g/cc
Water Absorption at Saturation: 0.30 % @Temperature 23.0 °C
Water Absorption at Saturation: 0.45 % @Temperature 100 °C
Viscosity: 200000 cP @Temperature 400 °C
Linear Mold Shrinkage, Flow: 0.0030 cm/cm

Victrex® PEEK 150GL15 Polyetheretherketone, 15% Glass Fibre Reinforced accurate 77%

$ 2187/MT

Density: 1.40 g/cc
Water Absorption at Saturation: 0.40 % @Temperature 23.0 °C
Water Absorption at Saturation: 0.50 % @Temperature 100 °C
Viscosity: 200000 cP @Temperature 400 °C
Linear Mold Shrinkage, Flow: 0.0040 cm/cm

Victrex® PEEK 650GL30 30% Glass Fiber Filled, PolyEtherEtherKetone accurate 88%

$ 1588/MT

Density: 1.51 g/cc
Water Absorption at Saturation: 0.30 % @Temperature 23.0 °C
Water Absorption at Saturation: 0.45 % @Temperature 100 °C
Viscosity: 700000 cP @Temperature 420 °C
Linear Mold Shrinkage, Flow: 0.0030 cm/cm

Victrex® PEEK 450GL15 Polyetheretherketone, 15% Glass Fibre Reinforced accurate 99%

$ 1509/MT

Density: 1.38 g/cc
Water Absorption at Saturation: 0.40 % @Temperature 23.0 °C
Water Absorption at Saturation: 0.50 % @Temperature 100 °C
Viscosity: 450000 cP @Temperature 400 °C
Linear Mold Shrinkage, Flow: 0.0050 cm/cm

Victrex® ST™ ST45GL30 Polyetherketoneetherketoneketone (PEKEKK), 30% Glass Fiber Reinforced accurate 77%

$ 2122/MT

Density: 1.53 g/cc
Water Absorption at Saturation: 0.60 % @Temperature 100 °C
Viscosity: 600000 cP @Temperature 420 °C
Linear Mold Shrinkage, Flow: 0.0030 cm/cm
Linear Mold Shrinkage, Transverse: 0.0090 cm/cm

Lanxess Durethan® BKV 35 H3.0 000000 Nylon 6, Glass Fiber Reinforced accurate 88%

$ 1985/MT

Specific Gravity: 1.41 g/cc
Moisture Absorption at Equilibrium: 1.9 %
Water Absorption at Saturation: 6.5 %
Linear Mold Shrinkage, Flow: 0.00030 cm/cm
Linear Mold Shrinkage, Flow: 0.00050 cm/cm

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lpg tanker for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for Victrex® PEEK 90GL60 Polyetheretherketone, 60% Glass Fibre Reinforced

Seller from Mexico City – 2021-03-10:

Seller from Mexico City work with company: Solvay, RTP Company, PolyOne Corporation, SABIC Innovative Plastics (GE Plastics)

Price: $2181 per MT

Seller from Philadelphia – 2021-05-01:

Seller from Philadelphia work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2362 per MT