$ 1478/MT
- Density: 0.943 - 0.951 g/cc @Temperature 23.0 °C
- Density: 0.945 - 0.953 g/cc @Temperature 20.0 °C
- Volatiles: <= 0.035 %
- Environmental Stress Crack Resistance: >= 20 hour @Temperature 80.0 °C
- Environmental Stress Crack Resistance: >= 165 hour @Temperature 80.0 °C
$ 1893/MT
- Density: 0.918 - 0.924 g/cc
- Environmental Stress Crack Resistance: >= 200 hour
- Melt Flow: 0.20 - 0.50 g/10 min
- Tensile Strength, Yield: >= 8.83 MPa
- Elongation at Break: >= 500 %
$ 1562/MT
- Density: 0.917 - 0.919 g/cc
- Melt Flow: 7.0 g/10 min
- Tensile Strength, Yield: >= 9.32 MPa
- Elongation at Break: >= 450 %
- Tear Strength Test: >= 9.8
$ 1936/MT
- Density: 0.917 - 0.925 g/cc
- Environmental Stress Crack Resistance: >= 3.0 hour
- Melt Flow: 1.5 - 2.5 g/10 min
- Dielectric Constant: <= 2.3 @Frequency 1000 Hz
- Dielectric Strength: >= 40.0 kV/mm
$ 2540/MT
- Environmental Stress Crack Resistance: >= 0.90 hour
- Elongation at Break: >= 450 %
- Amount of impurities [pcs]: 0.3
- Mass Content (%): 15
$ 1540/MT
- Density: 0.958 - 0.964 g/cc
- Volatiles: <= 0.10 %
- Melt Flow: 17 - 25 g/10 min
- Ash: <= 0.050 %
- Amount of impurities [pcs]: 25
$ 2561/MT
- Volatiles: <= 0.20 %
- Carbon Black Loading: 30 - 43 %
$ 1591/MT
- Volatiles: <= 0.20 %
- Carbon Black Loading: 30 - 43 %
$ 1572/MT
- Melt Flow: 0.20 - 3.0 g/10 min
- Melt Flow: 1.0 - 3.0 g/10 min
- Melt Flow: 5.0 - 8.0 g/10 min
- Dielectric Constant: <= 2.4 @Frequency 1000 Hz
- Dielectric Strength: >= 40.0 kV/mm @Frequency 50.0 Hz
$ 2263/MT
- Density: 0.943 - 0.949 g/cc
- Volatiles: <= 0.10 %
- Melt Flow: 0.40 - 0.75 g/10 min
- Ash: <= 0.060 %
- Tensile Strength, Yield: >= 13.0 MPa
$ 1765/MT
- Density: 0.918 - 0.924 g/cc
- Environmental Stress Crack Resistance: >= 100 hour
- Melt Flow: 1.0 - 2.0 g/10 min
- Tensile Strength, Yield: >= 8.34 MPa
- Elongation at Break: >= 500 %
$ 1758/MT
- Density: 0.917 - 0.919 g/cc
- Melt Flow: 7.0 g/10 min
- Tensile Strength, Yield: >= 9.30 MPa
- Elongation at Break: >= 450 %
- Tear Strength Test: >= 9.8
$ 1784/MT
- Density: 0.937 - 0.943 g/cc
- Volatiles: <= 0.090 %
- Melt Flow: 0.40 - 0.80 g/10 min
- Ash: <= 0.060 %
- Tensile Strength, Yield: >= 16.0 MPa
$ 1704/MT
- Environmental Stress Crack Resistance: >= 1.6 hour
- Elongation at Break: >= 450 %
- Amount of impurities [pcs]: 2
- Mass Content (%): 15
$ 2559/MT
- Melt Flow: 1.7 - 2.3 g/10 min
- Tensile Strength, Yield: >= 8.80 MPa
- Elongation at Break: >= 400 %
- Coefficient of Friction, Static: 0.10 - 0.25
- Tear Strength Test: >= 11.3
$ 1455/MT
- Density: 0.937 - 0.943 g/cc
- Volatiles: <= 0.090 %
- Melt Flow: 0.40 - 0.80 g/10 min
- Ash: <= 0.060 %
- Tensile Strength, Yield: >= 16.0 MPa
$ 1590/MT
- Density: 0.918 - 0.923 g/cc @Temperature 23.0 °C
- Density: 0.920 - 0.925 g/cc @Temperature 20.0 °C
- Melt Flow: 1.5 - 2.4 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 30 - 84 g/10 min @Load 21.6 kg, Temperature 190 °C
- Tensile Strength, Yield: >= 9.00 MPa
$ 2457/MT
- Density: 0.9185 - 0.924 g/cc
- Environmental Stress Crack Resistance: >= 500 hour
- Melt Flow: 0.21 - 0.39 g/10 min @Load 21.6 kg
- Tensile Strength, Yield: >= 9.80 MPa
- Elongation at Break: >= 600 %
$ 1559/MT
- Density: 0.9185 - 0.924 g/cc
- Environmental Stress Crack Resistance: >= 500 hour
- Melt Flow: 0.21 - 0.39 g/10 min @Load 21.6 kg
- Tensile Strength, Yield: >= 9.80 MPa
- Elongation at Break: >= 600 %
$ 1530/MT
- Elongation at Break: >= 200 %
- Tear Strength Test: >= 4.0
- Softening Point: 100 - 120 °C
- Minimum Service Temperature, Air: <= -40.0 °C
- Amount of impurities [pcs]: 50
$ 1673/MT
- Volatiles: <= 0.070 %
- Volatiles: <= 0.10 %
- Environmental Stress Crack Resistance: >= 500 hour
- Melt Flow: 0.21 - 0.39 g/10 min @Load 21.6 kg
- Tensile Strength, Yield: >= 9.80 MPa
$ 1636/MT
- Density: 0.917 - 0.925 g/cc
- Environmental Stress Crack Resistance: >= 3.0 hour
- Melt Flow: 1.5 - 2.5 g/10 min
- Dielectric Constant: <= 2.3 @Frequency 1000 Hz
- Dielectric Strength: >= 40.0 kV/mm
$ 1514/MT
- Density: 0.9185 - 0.924 g/cc
- Environmental Stress Crack Resistance: >= 500 hour
- Melt Flow: 0.21 - 0.39 g/10 min @Load 21.6 kg
- Tensile Strength, Yield: >= 9.80 MPa
- Elongation at Break: >= 600 %
$ 1635/MT
- Density: 0.918 - 0.924 g/cc
- Environmental Stress Crack Resistance: >= 200 hour
- Melt Flow: 0.20 - 0.50 g/10 min
- Tensile Strength, Yield: >= 8.83 MPa
- Elongation at Break: >= 500 %
$ 1588/MT
- Density: 0.943 - 0.949 g/cc
- Volatiles: <= 0.10 %
- Melt Flow: 0.40 - 0.70 g/10 min
- Ash: <= 0.060 %
- Elongation at Break: >= 450 %
- Amount of impurities [pcs]: 15
$ 1998/MT
- Density: 0.917 - 0.925 g/cc
- Environmental Stress Crack Resistance: >= 3.0 hour
- Melt Flow: 1.5 - 2.5 g/10 min
- Dielectric Constant: <= 2.3 @Frequency 1000 Hz
- Dielectric Strength: >= 40.0 kV/mm
$ 2481/MT
- Density: 0.918 - 0.924 g/cc
- Environmental Stress Crack Resistance: >= 200 hour
- Melt Flow: 0.20 - 0.50 g/10 min
- Tensile Strength, Yield: >= 8.83 MPa
- Elongation at Break: >= 500 %
$ 1897/MT
- Volatiles: <= 0.10 %
- Carbon Black Loading: >= 18.5 %
- Melt Flow: 0.10 - 1.0 g/10 min
- Elongation at Break: >= 145 %
- Tear Strength Test: >= 9.5
$ 1812/MT
- Density: 0.918 - 0.924 g/cc
- Environmental Stress Crack Resistance: >= 200 hour
- Melt Flow: 0.20 - 0.50 g/10 min
- Tensile Strength, Yield: >= 8.83 MPa
- Elongation at Break: >= 500 %
$ 1623/MT
- Density: 0.943 - 0.949 g/cc
- Volatiles: <= 0.10 %
- Melt Flow: 0.40 - 0.75 g/10 min
- Ash: <= 0.060 %
- Tensile Strength, Yield: >= 13.0 MPa
$ 1777/MT
- Density: 0.919 - 0.922 g/cc
- Environmental Stress Crack Resistance: >= 500 hour
- Melt Flow: 0.30 g/10 min
- Tensile Strength, Yield: >= 9.80 MPa
- Elongation at Break: >= 600 %
$ 1574/MT
- Environmental Stress Crack Resistance: >= 0.90 hour
- Elongation at Break: >= 450 %
- Amount of impurities [pcs]: 2
- Mass Content (%): 15
$ 1539/MT
- Free Water: <= 1.0 %
- Iron, Fe: <= 0.0010 %
- Appearance: Colorless or slightly yellowish liquid, free of mechanical impurities
- Color: 5
- Hydroxyl Number, mg of KOH/g of PEG-4: 500-550
$ 1512/MT
- Density: 0.917 - 0.925 g/cc
- Environmental Stress Crack Resistance: >= 3.0 hour
- Melt Flow: 1.5 - 2.5 g/10 min
- Dielectric Constant: <= 2.3 @Frequency 1000 Hz
- Dielectric Strength: >= 40.0 kV/mm
$ 1528/MT
- Melt Flow: 9.8 - 10.8 g/10 min @Load 1.20 kg, Temperature 250 °C
- Tensile Strength, Yield: >= 60.0 MPa
- Elongation at Break: >= 50 %
- Flexural Modulus: 2.25 GPa
- Transverse Strength: >= 90.0 MPa
$ 1696/MT
- Density: 0.948 - 0.955 g/cc @Temperature 23.0 °C
- Density: 0.950 - 0.957 g/cc @Temperature 20.0 °C
- Environmental Stress Crack Resistance: >= 30 hour
- Melt Flow: 4.0 - 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 80 - 245 g/10 min @Load 21.6 kg, Temperature 190 °C
$ 1537/MT
- Density: 0.943 - 0.949 g/cc
- Volatiles: <= 0.10 %
- Melt Flow: 0.40 - 0.70 g/10 min
- Ash: <= 0.060 %
- Elongation at Break: >= 450 %
- Amount of impurities [pcs]: 15
$ 1480/MT
- Melt Flow: 0.60 - 0.90 g/10 min
- Tensile Strength, Yield: >= 9.80 MPa
- Elongation at Break: >= 500 %
- Coefficient of Friction, Static: 0.10 - 0.25
- Tear Strength Test: >= 13.3
$ 1656/MT
- Volatiles: <= 0.070 %
- Volatiles: <= 0.10 %
- Environmental Stress Crack Resistance: >= 500 hour
- Melt Flow: 0.21 - 0.39 g/10 min @Load 21.6 kg
- Tensile Strength, Yield: >= 9.80 MPa
$ 1573/MT
- Density: 0.950 - 0.956 g/cc @Temperature 23.0 °C
- Density: 0.952 - 0.958 g/cc @Temperature 20.0 °C
- Environmental Stress Crack Resistance: >= 30 hour
- Melt Flow: 1.8 - 2.6 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: >= 26.0 MPa
$ 1619/MT
- Melt Flow: 7.3 - 8.3 g/10 min @Load 1.20 kg, Temperature 250 °C
- Tensile Strength, Yield: >= 60.0 MPa
- Elongation at Break: >= 50 %
- Flexural Modulus: 2.25 GPa
- Transverse Strength: >= 90.0 MPa
$ 2057/MT
- Density: 0.917 - 0.925 g/cc
- Environmental Stress Crack Resistance: >= 3.0 hour
- Melt Flow: 1.5 - 2.5 g/10 min
- Dielectric Constant: <= 2.3 @Frequency 1000 Hz
- Dielectric Strength: >= 40.0 kV/mm
$ 2349/MT
- Density: 0.928 - 0.935 g/cc
- Melt Flow: >= 2.5 g/10 min @Load 2.16 kg
- Tensile Strength, Yield: >= 10.5 MPa
- Elongation at Break: >= 500 %
- Tear Strength Test: >= 12
$ 1916/MT
- Density: 0.918 - 0.924 g/cc
- Environmental Stress Crack Resistance: >= 200 hour
- Melt Flow: 0.20 - 0.50 g/10 min
- Tensile Strength, Yield: >= 8.83 MPa
- Elongation at Break: >= 500 %
$ 1482/MT
- Volatiles: <= 0.15 % @Temperature 195 - 205 °C
- Carbon Black Loading: >= 18.5 %
- Elongation at Break: >= 80 %
- Tear Strength Test: >= 6.86
- Brittleness Temperature: -60.0 °C
- Volume Resistivity: <= 10000 ohm-cm
$ 1543/MT
- Density: 0.950 - 0.955 g/cc
- Volatiles: <= 0.10 %
- Melt Flow: 0.40 - 0.65 g/10 min
- Ash: <= 0.060 %
- Tensile Strength, Yield: >= 22.6 MPa
$ 1985/MT
- Density: 0.937 - 0.945 g/cc
- Volatiles: <= 0.10 %
- Melt Flow: 0.30 - 0.70 g/10 min
- Ash: <= 0.050 %
- Tensile Strength, Yield: >= 14.0 MPa
$ 1500/MT
- Melt Flow: 5.3 - 10.3 g/10 min @Load 1.20 kg, Temperature 250 °C
- Tensile Strength, Yield: >= 60.0 MPa
- Elongation at Break: >= 50 %
- Flexural Modulus: 2.25 GPa
- Transverse Strength: >= 90.0 MPa
$ 1935/MT
- Density: 0.950 - 0.955 g/cc
- Volatiles: <= 0.090 %
- Volatiles: <= 0.10 %
- Melt Flow: 0.40 - 0.65 g/10 min
- Ash: <= 0.040 %
$ 1754/MT
- Density: 0.9185 - 0.924 g/cc
- Environmental Stress Crack Resistance: >= 500 hour
- Melt Flow: 0.21 - 0.39 g/10 min @Load 21.6 kg
- Tensile Strength, Yield: >= 9.80 MPa
- Elongation at Break: >= 600 %
$ 2542/MT
- Density: 0.950 - 0.955 g/cc
- Volatiles: <= 0.000010 %
- Volatiles: <= 0.000015 %
- Environmental Stress Crack Resistance: >= 500 hour
- Melt Flow: 0.30 - 0.65 g/10 min @Load 5.00 kg
$ 1681/MT
- Melt Flow: 7.8 - 12.8 g/10 min @Load 1.20 kg, Temperature 250 °C
- Tensile Strength, Yield: >= 60.0 MPa
- Elongation at Break: >= 50 %
- Flexural Modulus: 2.25 GPa
- Transverse Strength: >= 90.0 MPa
$ 1650/MT
- Density: 0.928 - 0.932 g/cc
- Melt Flow: 2.5 g/10 min
- Tensile Strength, Yield: >= 11.0 MPa
- Elongation at Break: >= 500 %
- Tear Strength Test: >= 12
$ 1653/MT
- Density: 0.949 - 0.952 g/cc
- Volatiles: <= 0.090 %
- Volatiles: <= 0.10 %
- Melt Flow: 0.30 - 0.60 g/10 min
- Ash: <= 0.040 %
$ 1476/MT
- Density: 0.918 - 0.924 g/cc
- Environmental Stress Crack Resistance: >= 100 hour
- Melt Flow: 1.0 - 2.0 g/10 min
- Tensile Strength, Yield: >= 8.34 MPa
- Elongation at Break: >= 500 %
$ 1454/MT
- Density: 0.918 - 0.924 g/cc
- Environmental Stress Crack Resistance: >= 200 hour
- Melt Flow: 0.20 - 0.50 g/10 min
- Tensile Strength, Yield: >= 8.83 MPa
- Elongation at Break: >= 500 %
$ 1711/MT
- Density: 0.9185 - 0.922 g/cc
- Density: 0.9185 - 0.992 g/cc
- Environmental Stress Crack Resistance: >= 500 hour
- Melt Flow: 0.21 - 0.39 g/10 min
- Tensile Strength, Yield: >= 11.3 MPa
$ 1970/MT
- Density: 0.958 - 0.963 g/cc
- Volatiles: <= 0.090 %
- Environmental Stress Crack Resistance: >= 25 hour
- Melt Flow: 2.6 - 3.2 g/10 min
- Ash: <= 0.030 %
$ 2031/MT
- pH: >= 9.0
- Kinematic Viscosity: >= 110 cSt
- Flash Point: >= 130 °C
- Free Water: <= 5.0 %
- Appearance: Dark-brown liquid, free from mechanical impurities
$ 1635/MT
- Density: 0.917 - 0.920 g/cc
- Environmental Stress Crack Resistance: >= 2.0 hour
- Melt Flow: 2.0 g/10 min
- Tensile Strength, Yield: >= 9.30 MPa
- Elongation at Break: >= 550 %
$ 1778/MT
- Density: <= 0.792 g/cc
- Melt Flow: 1.5 - 3.5 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Yield: >= 55.0 MPa
- Tensile Strength, Yield: >= 58.0 MPa
- Tensile Strength, Yield: >= 60.0 MPa
$ 1680/MT
- Density: 0.917 - 0.925 g/cc
- Environmental Stress Crack Resistance: >= 3.0 hour
- Melt Flow: 1.5 - 2.5 g/10 min
- Dielectric Constant: <= 2.3 @Frequency 1000 Hz
- Dielectric Strength: >= 40.0 kV/mm
$ 1887/MT
- Melt Flow: 20 - 24 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Yield: >= 55.0 MPa
- Tensile Strength, Yield: >= 58.0 MPa
- Tensile Strength, Yield: >= 60.0 MPa
- Elongation at Break: >= 50 %
$ 1952/MT
- Density: 0.928 - 0.932 g/cc
- Melt Flow: 2.5 g/10 min
- Tensile Strength, Yield: >= 11.0 MPa
- Elongation at Break: >= 500 %
- Tear Strength Test: >= 12
$ 1988/MT
- Density: 0.937 - 0.943 g/cc
- Volatiles: <= 0.090 %
- Melt Flow: 0.40 - 0.80 g/10 min
- Ash: <= 0.060 %
- Tensile Strength, Yield: >= 16.0 MPa
$ 1491/MT
- Melt Flow: 6.0 - 8.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Yield: >= 55.0 MPa
- Tensile Strength, Yield: >= 58.0 MPa
- Tensile Strength, Yield: >= 60.0 MPa
- Elongation at Break: >= 80 %
$ 1682/MT
- Density: 0.918 - 0.924 g/cc
- Environmental Stress Crack Resistance: >= 100 hour
- Melt Flow: 1.0 - 2.0 g/10 min
- Tensile Strength, Yield: >= 8.34 MPa
- Elongation at Break: >= 500 %
$ 2016/MT
- pH: 7.0 - 9.0
- Free Water: <= 0.30 %
- Appearance: At 18°C to 22°C: Vaseline-like dough of light yellow color Melt Appearance: Transparent solution of light yellow color
- Color: 4
- Hydroxyl Number, mg of KOH/g of PEG-13: 176-190
$ 2439/MT
- Melt Flow: 1.5 - 2.5 g/10 min
- Tensile Strength, Yield: >= 8.80 MPa
- Elongation at Break: >= 500 %
- Coefficient of Friction, Static: 0.10 - 0.25
- Tear Strength Test: >= 10.3
$ 2517/MT
- Melt Flow: 8.5 - 11.5 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Yield: >= 55.0 MPa
- Tensile Strength, Yield: >= 58.0 MPa
- Tensile Strength, Yield: >= 60.0 MPa
- Elongation at Break: >= 80 %
$ 1942/MT
- Density: 0.918 - 0.924 g/cc
- Environmental Stress Crack Resistance: >= 200 hour
- Melt Flow: 0.20 - 0.50 g/10 min
- Tensile Strength, Yield: >= 8.83 MPa
- Elongation at Break: >= 500 %
$ 1591/MT
- Density: 0.917 - 0.921 g/cc
- Melt Flow: 2.0 g/10 min
- Tensile Strength, Yield: >= 9.30 MPa
- Elongation at Break: >= 600 %
- Tear Strength Test: >= 11.3
$ 2062/MT
- Density: 0.917 - 0.925 g/cc
- Environmental Stress Crack Resistance: >= 3.0 hour
- Melt Flow: 1.5 - 2.5 g/10 min
- Dielectric Constant: <= 2.3 @Frequency 1000 Hz
- Dielectric Strength: >= 40.0 kV/mm
$ 1483/MT
- Density: 0.917 - 0.925 g/cc
- Environmental Stress Crack Resistance: >= 3.0 hour
- Melt Flow: 1.5 - 2.5 g/10 min
- Dielectric Constant: <= 2.3 @Frequency 1000 Hz
- Dielectric Strength: >= 40.0 kV/mm
$ 2238/MT
- Density: 0.917 - 0.925 g/cc
- Environmental Stress Crack Resistance: >= 3.0 hour
- Melt Flow: 1.5 - 2.5 g/10 min
- Dielectric Constant: <= 2.3 @Frequency 1000 Hz
- Dielectric Strength: >= 40.0 kV/mm
$ 1556/MT
- Volatiles: <= 0.070 %
- Volatiles: <= 0.10 %
- Environmental Stress Crack Resistance: >= 500 hour
- Melt Flow: 0.21 - 0.39 g/10 min @Load 21.6 kg
- Tensile Strength, Yield: >= 9.80 MPa
$ 1970/MT
- Free Water: 35 - 40 %
- Acid Value: <= 0.10
- Appearance: Transparent liquid, free of mechanical impurities
- Color: 35
- Hydroxyl Number, mg of KOH/g of PEG-35: 72-78
$ 1770/MT
- Density: 0.958 - 0.963 g/cc
- Volatiles: <= 0.10 %
- Melt Flow: 2.6 - 3.2 g/10 min
- Ash: <= 0.050 %
- Tensile Strength, Yield: >= 25.5 MPa
$ 1631/MT
- Density: 0.918 - 0.924 g/cc
- Environmental Stress Crack Resistance: >= 200 hour
- Melt Flow: 0.20 - 0.50 g/10 min
- Tensile Strength, Yield: >= 8.83 MPa
- Elongation at Break: >= 500 %
$ 1659/MT
- Density: 0.918 - 0.923 g/cc @Temperature 23.0 °C
- Density: 0.920 - 0.925 g/cc @Temperature 20.0 °C
- Melt Flow: 3.5 - 5.28 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 105.6 - 122.5 g/10 min @Load 21.6 kg, Temperature 190 °C
- Tensile Strength, Yield: >= 9.00 MPa
$ 2213/MT
- Density: 0.918 - 0.924 g/cc
- Environmental Stress Crack Resistance: >= 200 hour
- Melt Flow: 0.20 - 0.50 g/10 min
- Tensile Strength, Yield: >= 8.83 MPa
- Elongation at Break: >= 500 %
$ 1620/MT
- Density: 0.918 - 0.923 g/cc @Temperature 23.0 °C
- Density: 0.920 - 0.925 g/cc @Temperature 20.0 °C
- Melt Flow: 0.70 - 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 14 - 42 g/10 min @Load 21.6 kg, Temperature 190 °C
- Tensile Strength, Yield: >= 9.00 MPa
$ 1779/MT
- Melt Flow: 4.0 - 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Yield: >= 55.0 MPa
- Tensile Strength, Yield: >= 58.0 MPa
- Tensile Strength, Yield: >= 60.0 MPa
- Elongation at Break: >= 80 %
$ 1878/MT
- Density: 0.947 - 0.950 g/cc @Temperature 23.0 °C
- Density: 0.949 - 0.952 g/cc @Temperature 20.0 °C
- Volatiles: <= 0.035 %
- Melt Flow: 5.0 - 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: >= 20.0 MPa
$ 1891/MT
- Melt Flow: 13.5 - 16.5 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Yield: >= 55.0 MPa
- Tensile Strength, Yield: >= 58.0 MPa
- Tensile Strength, Yield: >= 60.0 MPa
- Elongation at Break: >= 80 %
$ 2007/MT
- Free Water: 35 - 40 %
- Acid Value: <= 0.10
- Appearance: Transparent liquid without mechanical impurities
- Color: 40
- Hydroxyl Number, mg of KOH/g of PEG-68: 34-40
$ 2281/MT
- Free Water: 35 - 40 %
- Acid Value: <= 0.10
- Appearance: Transparent liquid without mechanical impurities
- Color: 40
- Hydroxyl Number, mg of KOH/g of PEG-68: 34-40
$ 1455/MT
- Volatiles: <= 0.50 %
- Viscosity: 20 - 400 cP
- Ash: <= 0.10 %
- Melting Point: 55.0 - 90.0 °C
- Appearance: Balm-type or waxen mass with possible existence of liquid of light-gray to brown colors
$ 1527/MT
- Melt Flow: 1.5 - 2.5 g/10 min
- Tensile Strength, Yield: >= 8.80 MPa
- Elongation at Break: >= 500 %
- Coefficient of Friction, Static: 0.10 - 0.25
- Tear Strength Test: >= 10.3
$ 2163/MT
- Volatiles: <= 0.070 %
- Volatiles: <= 0.10 %
- Environmental Stress Crack Resistance: >= 500 hour
- Melt Flow: 0.21 - 0.39 g/10 min @Load 21.6 kg
- Tensile Strength, Yield: >= 9.80 MPa
$ 1588/MT
- Elongation at Break: >= 250 %
- Tear Strength Test: >= 5.0
- Softening Point: 100 - 120 °C
- Minimum Service Temperature, Air: <= -50.0 °C
- Amount of impurities [pcs]: 50
$ 2115/MT
- Density: 0.917 - 0.925 g/cc
- Environmental Stress Crack Resistance: >= 3.0 hour
- Melt Flow: 1.5 - 2.5 g/10 min
- Dielectric Constant: <= 2.3 @Frequency 1000 Hz
- Dielectric Strength: >= 40.0 kV/mm
$ 1907/MT
- Melt Flow: 1.7 - 2.3 g/10 min
- Tensile Strength, Yield: >= 8.80 MPa
- Elongation at Break: >= 400 %
- Coefficient of Friction, Static: 0.10 - 0.25
- Tear Strength Test: >= 11.3
$ 1474/MT
- Melt Flow: 0.40 - 0.70 g/10 min
- Tensile Strength, Yield: >= 8.83 MPa
- Elongation at Break: >= 550 %
- Tear Strength Test: >= 115
- Dielectric Constant: <= 2.4 @Frequency 1000 Hz
$ 1621/MT
- Density: 0.943 - 0.949 g/cc
- Volatiles: <= 0.10 %
- Melt Flow: 0.40 - 0.70 g/10 min
- Ash: <= 0.060 %
- Elongation at Break: >= 450 %
- Amount of impurities [pcs]: 15
$ 1699/MT
- Density: 0.918 - 0.924 g/cc
- Environmental Stress Crack Resistance: >= 100 hour
- Melt Flow: 1.0 - 2.0 g/10 min
- Tensile Strength, Yield: >= 8.34 MPa
- Elongation at Break: >= 500 %
$ 1679/MT
- Density: 0.918 - 0.923 g/cc @Temperature 23.0 °C
- Density: 0.920 - 0.925 g/cc @Temperature 20.0 °C
- Melt Flow: 1.5 - 2.4 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 30 - 84 g/10 min @Load 21.6 kg, Temperature 190 °C
- Tensile Strength, Yield: >= 9.00 MPa
$ 2179/MT
- Volatiles: <= 0.50 %
- Viscosity: 320 - 7400 cP
- Ash: <= 0.10 %
- Melting Point: 90.0 - 105 °C
- Melt Temperature: 90.0 - 105 °C
- Appearance: Waxen mass or slipcast blocks of pieces of different size from light-gray to brown colors
$ 1560/MT
- Density: 0.955 - 0.961 g/cc @Temperature 23.0 °C
- Density: 0.957 - 0.963 g/cc @Temperature 20.0 °C
- Volatiles: <= 0.0000090 %
- Environmental Stress Crack Resistance: >= 30 hour
- Melt Flow: 2.3 - 3.3 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1789/MT
- Free Water: <= 0.70 %
- Appearance: At 18°C to 22°C: Liquid from slightly yellow to yellow color with light characteristic odor
- Color: 3
- Hydroxyl Number, mg of KOH/g of PEG-9: 260-290
$ 1535/MT
- Density: 0.917 - 0.925 g/cc
- Environmental Stress Crack Resistance: >= 3.0 hour
- Melt Flow: 1.5 - 2.5 g/10 min
- Dielectric Constant: <= 2.3 @Frequency 1000 Hz
- Dielectric Strength: >= 40.0 kV/mm
$ 1990/MT
- Volatiles: <= 0.070 %
- Volatiles: <= 0.10 %
- Environmental Stress Crack Resistance: >= 500 hour
- Melt Flow: 0.21 - 0.39 g/10 min
- Tensile Strength, Yield: >= 9.80 MPa
$ 1952/MT
- Volatiles: <= 0.070 %
- Volatiles: <= 0.10 %
- Environmental Stress Crack Resistance: >= 500 hour
- Melt Flow: 0.21 - 0.39 g/10 min
- Tensile Strength, Yield: >= 9.80 MPa
$ 1599/MT
- Melt Flow: 0.60 - 0.90 g/10 min
- Tensile Strength, Yield: >= 9.80 MPa
- Elongation at Break: >= 500 %
- Coefficient of Friction, Static: 0.10 - 0.25
- Tear Strength Test: >= 13.3
$ 1696/MT
- Density: 0.958 - 0.965 g/cc @Temperature 23.0 °C
- Density: 0.960 - 0.966 g/cc @Temperature 20.0 °C
- Melt Flow: 6.0 - 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 120 - 315 g/10 min @Load 21.6 kg, Temperature 190 °C
- Tensile Strength, Yield: >= 28.0 MPa
$ 1817/MT
- Free Water: <= 1.5 %
- Free Water: <= 10 %
- Acid Value: <= 1.0
- Appearance: Viscous oily brown liquid
- Saponification Number, mg of KOH: 65-85
$ 1564/MT
- Volatiles: <= 0.50 %
- Viscosity: 4.0 - 750 cP
- Ash: <= 0.10 %
- Melting Point: <= 105 °C
- Melt Temperature: <= 90.0 °C
- Appearance: Liquid, waxen or balm-type mass in mixture of light-gray to brown colors
$ 1911/MT
- Density: 0.948 - 0.955 g/cc @Temperature 23.0 °C
- Density: 0.950 - 0.957 g/cc @Temperature 20.0 °C
- Environmental Stress Crack Resistance: >= 50 hour
- Melt Flow: 0.80 - 1.6 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 16 - 56 g/10 min @Load 21.6 kg, Temperature 190 °C
$ 2134/MT
- Elongation at Break: >= 300 %
- Tear Strength Test: >= 6.5
- Softening Point: 105 - 120 °C
- Minimum Service Temperature, Air: <= -60.0 °C
- Amount of impurities [pcs]: 50
Delivery Thermoplastic Kazanorgsintez
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
shipsforsale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.