$ 1493/MT
- Density: 0.970 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 10 g/10 min
- Tensile Strength, Ultimate: 29.4 MPa
- Elongation at Break: 686 %
$ 1692/MT
- Specific Gravity: 0.960 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 45
- Tensile Strength, Ultimate: 13.4 MPa
$ 1868/MT
- Specific Gravity: 0.960 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 45
- Tensile Strength, Ultimate: 13.4 MPa
$ 2214/MT
- Density: 1.25 g/cc
- Linear Mold Shrinkage: 0.0060 cm/cm
- Melt Flow: 10 g/10 min
- Tensile Strength, Yield: 40.7 MPa
- Elongation at Break: 16 %
$ 2012/MT
- Specific Gravity: 1.07 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 1.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 60
- Tensile Strength, Yield: 1.72 MPa
$ 1836/MT
- Density: 1.22 g/cc
- Melt Flow: 3.0 g/10 min
- Hardness, Shore D: 77
- Tensile Strength, Ultimate: 54.5 MPa
- Elongation at Break: 2.0 %
$ 2546/MT
- Density: 1.25 g/cc
- Linear Mold Shrinkage: 0.0060 cm/cm
- Melt Flow: 5.0 g/10 min
- Tensile Strength, Yield: 31.0 MPa
- Elongation at Break: 4.0 %
$ 1481/MT
- Density: 1.23 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 10.3 MPa
- Elongation at Break: 200 %
- Flexural Modulus: 0.224 GPa
$ 1449/MT
- Density: 0.940 g/cc
- Linear Mold Shrinkage: 0.0208 cm/cm
- Melt Flow: 0.50 g/10 min
- Hardness, Shore A: 77
- Tensile Strength, Ultimate: 1.592 MPa
$ 1510/MT
- Density: 1.72 g/cc
- Water Absorption: 0.080 %
- Melt Flow: 17 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1466/MT
- Density: 1.04 g/cc
- Melt Flow: 1.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 8.96 MPa
- Elongation at Break: 990 %
- Flexural Modulus: 0.186 GPa
$ 1459/MT
- Specific Gravity: 1.92 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 93
- Tensile Strength, Yield: 5.52 MPa
$ 1574/MT
- Density: 0.890 g/cc
- Melt Flow: 10 - 20 g/10 min
- Hardness, Shore A: 44
- Tensile Strength, Ultimate: 2.80 MPa
- Elongation at Break: 800 %
- Tear Strength Test: 17.5 - 24.5
$ 2508/MT
- Specific Gravity: 0.952 g/cc
- Melt Flow: 3.61 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 58
- Tensile Strength at Break: 4.36 MPa
- Elongation at Break: 760 %
- Tear Strength: 28.0 kN/m
$ 1582/MT
- Specific Gravity: 1.09 g/cc
- Hardness, Shore D: 52
- Tensile Strength at Break: 24.0 MPa
- Elongation at Break: 200 %
- Tear Strength: 24.5 kN/m
$ 1479/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 65
- Tensile Strength at Break: 16.0 MPa
- Elongation at Break: 500 %
- Tear Strength: 29.8 kN/m
$ 1585/MT
- Density: 1.14 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 12 g/10 min
- Hardness, Shore D: 65
- Tensile Strength, Ultimate: 19.0 MPa
$ 2163/MT
- Specific Gravity: 0.975 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 6.75 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 86
- Tensile Strength, Ultimate: 11.7 MPa
$ 1470/MT
- Specific Gravity: 1.46 g/cc
- Melt Flow: 19.2 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 93
- Tensile Strength, Yield: 4.97 MPa
- Elongation at Break: 180 %
$ 1828/MT
- Density: 1.12 g/cc
- Hardness, Shore A: 31
- Hardness, Shore A: 37
- Hardness, Shore A: 37
- Hardness, Shore A: 38
$ 2404/MT
- Specific Gravity: 1.04 g/cc @Temperature 25.0 °C
- Shelf Life: 48.0 Month
- Color: Off-White
- Physical Form: Thermoplastic Pellet
- Siloxane Content (%): 50
$ 1574/MT
- Density: 1.40 g/cc
- Melt Flow: 0.85 g/10 min
- Hardness, Shore A: 69
- Tensile Strength, Ultimate: 5.30 MPa
- Elongation at Break: 950 %
$ 1878/MT
- Specific Gravity: 1.15 g/cc
- Linear Mold Shrinkage: 0.010 - 0.030 cm/cm
- Hardness, Shore A: 63
- Tensile Strength: 5.70 MPa
- Tensile Strength, Ultimate: 3.20 MPa
$ 1589/MT
- Specific Gravity: 0.910 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 95
- Tensile Strength, Yield: 15.2 MPa
$ 1590/MT
- Specific Gravity: 1.98 g/cc
- Linear Mold Shrinkage: 0.011 cm/cm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 46
- Tensile Strength, Yield: 6.21 MPa
$ 1736/MT
- Density: 0.900 g/cc
- Linear Mold Shrinkage: 0.013 cm/cm
- Melt Flow: 10 g/10 min
- Hardness, Shore D: 65
- Tensile Strength, Ultimate: 19.3 MPa
$ 1848/MT
- Melt Flow: 12 g/10 min @Load 2.16 kg
$ 1453/MT
- Density: 1.05 g/cc
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 24.8 MPa
- Elongation at Break: 50 %
- Flexural Modulus: 1.96 GPa
$ 2003/MT
- Density: 0.910 g/cc
- Linear Mold Shrinkage: 0.017 cm/cm
- Melt Flow: 1.0 - 5.0 g/10 min
- Hardness, Shore A: 55
- Tensile Strength, Ultimate: 10.0 MPa
$ 2095/MT
- Specific Gravity: 1.07 g/cc
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 70
- Tensile Strength, Yield: 2.76 MPa
- Tensile Strength, Yield: 8.96 MPa
$ 2188/MT
- Density: 0.9616 g/cc
- Melt Flow: 3.1 g/10 min
- Hardness, Shore A: 55
- Tensile Strength, Ultimate: 13.7 MPa
- Elongation at Break: 597 %
$ 1461/MT
- Density: 1.065 g/cc
- Melt Flow: 1.5 g/10 min
- Hardness, Shore A: 80
- Tensile Strength, Ultimate: 9.00 MPa
- Elongation at Break: >= 1000 %
$ 1452/MT
- Specific Gravity: 0.932 g/cc
- Melt Flow: 1.7 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 69
- Tensile Strength at Break: 5.10 MPa
- Elongation at Break: 690 %
- Tear Strength: 36.8 kN/m
$ 1986/MT
- Density: 0.920 g/cc
- Hardness, Shore A: 73
- Tensile Strength, Ultimate: >= 7.45 MPa
- Elongation at Break: >= 400 %
- Tear Strength: >= 38.53 kN/m
$ 1492/MT
- Density: 0.910 g/cc
- Melt Flow: 8.0 g/10 min
- Hardness, Shore D: 42
- Tensile Strength, Ultimate: 10.3 - 14.5 MPa
- Elongation at Break: 500 - 700 %
$ 1594/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 10 - 14 g/10 min
- Hardness, Shore A: 60
- Tensile Strength, Ultimate: >= 3.60 MPa
$ 1787/MT
- Melt Flow: 5.8 g/10 min @Load 3.80 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 37.5 MPa
- Elongation at Break: 35.3 %
- Flexural Strength: 60.0 MPa
- Flexural Modulus: 2.232 GPa
$ 1455/MT
- Density: 1.21 g/cc
- Linear Mold Shrinkage: 0.0024 cm/cm
- Melt Flow: 3.9 g/10 min
- Tensile Strength, Ultimate: 43.3 MPa
- Elongation at Break: 16.3 %
$ 1511/MT
- Linear Mold Shrinkage: 0.0090 cm/cm
- Melt Flow: 13 g/10 min
- Tensile Strength, Ultimate: 20.7 MPa
- Elongation at Break: 200 %
- Flexural Strength: 35.9 MPa
$ 1753/MT
- Specific Gravity: 1.15 g/cc
- Hardness, Shore A: 61
- Tensile Strength at Break: 7.03 MPa
- Elongation at Break: 450 %
- Tear Strength: 29.8 kN/m
$ 1807/MT
- Hardness, Shore A: 61
- Hardness, Shore A: 74
- Hardness, Shore A: 75
- Hardness, Shore A: 77
- Tensile Strength, Ultimate: 7.012 MPa
$ 1590/MT
- Specific Gravity: 0.942 g/cc
- Hardness, Shore A: 72
- Tensile Strength, Yield: 12.8 MPa
- Elongation at Break: 750 %
- Tear Strength: 29.8 kN/m
$ 1856/MT
- Specific Gravity: 1.85 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 42
- Tensile Strength, Yield: 5.17 MPa
$ 1504/MT
- Density: 1.23 g/cc
- Linear Mold Shrinkage: 0.0070 cm/cm
- Melt Flow: 7.0 g/10 min
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Break: 80 %
$ 1789/MT
- Specific Gravity: 1.06 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 46
- Tensile Strength, Yield: 1.10 MPa
- Tensile Strength, Yield: 5.52 MPa
$ 1806/MT
- Density: 1.05 g/cc
- Melt Flow: 5.0 g/10 min
- Hardness, Rockwell R: 103
- Tensile Strength, Ultimate: 31.0 MPa
- Elongation at Break: 25 %
$ 1453/MT
- Specific Gravity: 0.962 g/cc
- Melt Flow: 1.32 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 39
- Tensile Strength, Yield: 17.1 MPa
- Elongation at Break: 630 %
$ 2548/MT
- Specific Gravity: 1.20 g/cc
- Melt Flow: 70 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 64
- Tensile Strength, Yield: 3.45 MPa
- Tensile Strength, Yield: 1.86 MPa @Strain 100 %
$ 1582/MT
- Hardness, Shore A: 35
- Hardness, Shore A: 37
- Hardness, Shore A: 40
- Tensile Strength, Ultimate: 7.412 MPa
- Tensile Strength, Ultimate: 8.115 MPa
$ 1979/MT
- Density: 0.992 g/cc
- Melt Flow: 4.3 g/10 min
- Hardness, Shore A: 83
- Tensile Strength, Ultimate: 13.7 MPa
- Elongation at Break: 730 %
$ 1657/MT
- Specific Gravity: 0.912 g/cc
- Melt Flow: 1.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 37
- Tensile Strength, Yield: 5.72 MPa
- Tensile Strength, Yield: 1.00 MPa @Strain 100 %
$ 1697/MT
- Hardness, Shore A: 48
- Hardness, Shore A: 51
- Hardness, Shore A: 55
- Tensile Strength, Ultimate: 9.825 MPa
- Tensile Strength, Ultimate: 10.63 MPa
$ 1666/MT
- Density: 1.14 g/cc
- Hardness, Shore A: 52
- Hardness, Shore A: 54
- Hardness, Shore A: 54
- Hardness, Shore A: 55
$ 1779/MT
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 1.0 g/10 min
- Hardness, Shore D: 53
- Tensile Strength, Ultimate: 22.4 MPa
- Elongation at Break: 630 %
$ 1868/MT
- Density: 1.14 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 14 g/10 min
- Tensile Strength, Yield: 23.4 MPa
- Elongation at Break: 180 %
$ 2249/MT
- Density: 1.17 g/cc
- Linear Mold Shrinkage: 0.013 cm/cm
- Melt Flow: 10 - 14 g/10 min
- Hardness, Shore A: 54
- Tensile Strength, Ultimate: >= 4.00 MPa
$ 2292/MT
- Ash: 24.46 %
- Izod Impact, Notched: 0.147 J/cm
- Deflection Temperature at 0.46 MPa (66 psi): 128 °C
- Deflection Temperature at 1.8 MPa (264 psi): 72.2 °C
- Flame Spread: 7.9 mm/min
$ 1566/MT
- Specific Gravity: 1.07 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 80
- Tensile Strength, Yield: 9.31 MPa
- Elongation at Break: 1400 %
- Tear Strength: 40.3 kN/m
$ 1515/MT
- Specific Gravity: 1.05 g/cc @Temperature 25.0 °C
- Volatiles: 0.00 %
- Shelf Life: 48.0 Month
- Color: Off-White
- Physical Form: Particles
- Siloxane Content (%): 50
$ 2236/MT
- Density: 0.9055 g/cc
- Linear Mold Shrinkage: 0.018 - 0.022 cm/cm
- Melt Flow: 4.0 g/10 min
- Tensile Strength, Ultimate: 33.8 MPa
- Elongation at Break: 350 %
$ 1604/MT
- Specific Gravity: 1.15 g/cc
- Hardness, Shore A: 68
- Tensile Strength at Break: 11.7 MPa
- Elongation at Break: 600 %
- Tear Strength: 45.6 kN/m
$ 1501/MT
- Density: 0.920 g/cc
- Linear Mold Shrinkage: 0.0118 cm/cm
- Melt Flow: 5.3 g/10 min
- Hardness, Shore D: 40.4
- Tensile Strength, Ultimate: 10.1 MPa
$ 2087/MT
- Density: 1.33 g/cc
- Melt Flow: 2.0 g/10 min
- Tensile Strength, Ultimate: 18.3 MPa
- Elongation at Break: 500 %
- Flexural Modulus: 2.241 GPa
$ 2518/MT
- Specific Gravity: 1.15 g/cc
- Linear Mold Shrinkage: 0.0040 cm/cm
- Melt Flow: 1.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 48.3 MPa
- Elongation at Break: 20 %
$ 1934/MT
- Density: 1.13 g/cc
- Hardness, Shore A: 18
- Hardness, Shore A: 19
- Hardness, Shore A: 20
- Hardness, Shore A: 21
$ 1661/MT
- Density: 1.13 g/cc
- Hardness, Shore A: 18
- Hardness, Shore A: 19
- Hardness, Shore A: 20
- Hardness, Shore A: 21
$ 1469/MT
- Density: 1.13 g/cc
- Hardness, Shore A: 18
- Hardness, Shore A: 19
- Hardness, Shore A: 20
- Hardness, Shore A: 21
$ 1487/MT
- Density: 0.940 g/cc
- Linear Mold Shrinkage: 0.0137 cm/cm
- Melt Flow: 5.0 g/10 min
- Hardness, Shore D: 36
- Tensile Strength, Ultimate: 12.2 MPa
$ 1581/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.015 - 0.045 cm/cm
- Melt Flow: 8.5 g/10 min
- Tensile Strength, Ultimate: 20.7 MPa
- Elongation at Break: 300 %
$ 1808/MT
- Density: 1.47 g/cc
- Melt Flow: 17 g/10 min @Load 5.00 kg, Temperature 230 °C
$ 1487/MT
- Specific Gravity: 0.920 g/cc
- Linear Mold Shrinkage: 0.014 cm/cm
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 70
- Tensile Strength, Yield: 2.72 MPa
$ 1968/MT
- Density: 1.063 g/cc
- Linear Mold Shrinkage: 0.0118 cm/cm
- Melt Flow: 6.0 g/10 min
- Hardness, Shore A: 85
- Tensile Strength, Ultimate: 11.6 MPa
$ 1484/MT
- Density: 1.90 g/cc
- Melt Flow: 35 g/10 min @Load 5.00 kg, Temperature 230 °C
$ 1685/MT
- Density: 1.23 g/cc
- Melt Flow: 7.0 g/10 min
- Hardness, Shore D: 65
- Tensile Strength, Ultimate: 16.8 MPa
- Elongation at Break: 830 %
$ 1557/MT
- Specific Gravity: 1.23 g/cc @Temperature 25.0 °C
- Shelf Life: 48.0 Month
- Color: Off-White
- Physical Form: Thermoplastic Pellet
- Siloxane Content (%): 40
$ 1544/MT
- Density: 1.08 g/cc
- Linear Mold Shrinkage: 0.0090 cm/cm
- Melt Flow: 18 g/10 min
- Tensile Strength, Yield: 24.1 MPa
- Elongation at Break: 150 %
$ 1698/MT
- Density: 1.03 g/cc
- Linear Mold Shrinkage: 0.0067 cm/cm
- Melt Flow: 10 g/10 min
- Tensile Strength, Ultimate: 46.9 MPa
- Elongation at Break: 21 %
$ 1508/MT
- Specific Gravity: 0.972 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 4.7 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 44.1 MPa
- Elongation at Break: 27 %
$ 1719/MT
- Specific Gravity: 1.15 g/cc
- Hardness, Shore A: 65
- Tensile Strength at Break: 11.0 MPa
- Elongation at Break: 600 %
- Tear Strength: 45.6 kN/m
$ 1899/MT
- Density: 1.13 g/cc
- Hardness, Shore A: 18
- Hardness, Shore A: 19
- Hardness, Shore A: 20
- Hardness, Shore A: 21
$ 1954/MT
- Density: 1.06 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Melt Flow: 3.3 g/10 min
- Hardness, Rockwell R: 103
- Tensile Strength, Ultimate: 50.0 MPa
$ 1991/MT
- Density: 1.81 g/cc
- Melt Flow: 35 g/10 min @Load 5.00 kg, Temperature 230 °C
$ 1972/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage: 0.010 - 0.030 cm/cm
- Melt Flow: 10 g/10 min @Load 10.0 kg, Temperature 190 °C
- Hardness, Shore A: 64
- Tensile Strength: 8.90 MPa
$ 1898/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Hardness, Shore A: 62
- Tensile Strength, Ultimate: >= 3.62 MPa
- Elongation at Break: >= 506 %
- Tear Strength: >= 19.6 kN/m
$ 1559/MT
- Specific Gravity: 1.16 g/cc
- Linear Mold Shrinkage: 0.014 cm/cm
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 15.5 MPa
$ 1530/MT
- Specific Gravity: 1.15 g/cc
- Hardness, Shore A: 55
- Tensile Strength at Break: 3.00 MPa
- Elongation at Break: 400 %
- Tear Strength: 15.1 kN/m
$ 1776/MT
- Density: 1.21 g/cc
- Melt Flow: 2.0 g/10 min
- Tensile Strength, Ultimate: 16.5 MPa
- Elongation at Break: 200 %
- Flexural Modulus: 1.655 GPa
$ 2099/MT
- Density: 0.9375 g/cc
- Melt Flow: 0.40 g/10 min
- Hardness, Shore A: 54
- Tensile Strength, Ultimate: 9.30 MPa
- Elongation at Break: 722 %
- Tear Strength: 37.4 kN/m
$ 1752/MT
- Specific Gravity: 1.15 g/cc
- Hardness, Shore A: 63
- Tensile Strength at Break: 4.00 MPa
- Elongation at Break: 360 %
- Tear Strength: 19.3 kN/m
$ 1689/MT
- Specific Gravity: 0.900 g/cc
- Linear Mold Shrinkage: 0.018 cm/cm
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 46
- Tensile Strength, Yield: 8.27 MPa
$ 1714/MT
- Hardness, Shore A: 35
- Hardness, Shore A: 41
- Hardness, Shore A: 41
- Hardness, Shore A: 44
- Tensile Strength, Ultimate: 7.58 MPa
$ 2371/MT
- Density: 0.902 g/cc
- Melt Flow: 2.0 g/10 min
- Hardness, Shore A: 66
- Tensile Strength, Ultimate: 10.7 MPa
- Elongation at Break: 690 %
- Tear Strength: 42.4 kN/m
$ 2114/MT
- Density: 1.16 g/cc
- Melt Flow: 1.0 g/10 min
- Hardness, Shore D: 67
- Tensile Strength, Ultimate: 15.8 MPa
- Elongation at Break: 110 %
$ 1581/MT
- Density: 0.975 g/cc
- Melt Flow: 4.5 g/10 min
- Hardness, Shore A: 87
- Tensile Strength, Ultimate: 12.8 MPa
- Elongation at Break: 669 %
$ 1669/MT
- Density: 1.33 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Melt Flow: 12 g/10 min
- Tensile Strength, Ultimate: 13.4 MPa
- Elongation at Break: 82 %
$ 1509/MT
- Density: 1.13 g/cc
- Melt Flow: 14 g/10 min
- Tensile Strength, Yield: 23.5 MPa
- Elongation at Break: 220 %
- Flexural Yield Strength: 34.5 MPa
$ 1691/MT
- Density: 1.22 g/cc
- Melt Flow: 2.8 g/10 min
- Tensile Strength, Ultimate: 51.7 MPa
- Elongation at Break: 12 %
- Flexural Strength: 75.9 MPa
$ 2304/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage: 0.014 cm/cm
- Melt Flow: 2.5 - 5.0 g/10 min
- Hardness, Shore A: 59
- Tensile Strength, Ultimate: >= 4.00 MPa
$ 1469/MT
- Specific Gravity: 1.25 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 46
- Tensile Strength, Yield: 7.17 MPa
$ 1622/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Melt Flow: 5.0 g/10 min
- Hardness, Rockwell R: 98
- Tensile Strength, Ultimate: 39.3 MPa
$ 2092/MT
- Density: 1.19 g/cc
- Linear Mold Shrinkage: 0.011 cm/cm
- Melt Flow: 1.8 g/10 min
- Hardness, Shore A: 69
- Tensile Strength, Ultimate: 8.17 MPa
$ 1810/MT
- Specific Gravity: 0.892 g/cc
- Linear Mold Shrinkage: 0.0090 cm/cm
- Melt Flow: 2.75 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 51
- Tensile Strength, Ultimate: 13.4 MPa
$ 1714/MT
- Density: 1.61 g/cc
- Melt Flow: 20 g/10 min @Load 5.00 kg, Temperature 190 °C
$ 1642/MT
- Melt Flow: 6.0 g/10 min
- Hardness, Rockwell R: 106
- Tensile Strength, Ultimate: 44.1 MPa
- Elongation at Break: 30 %
- Flexural Strength: 65.5 MPa
$ 1880/MT
- Specific Gravity: 1.19 g/cc
- Linear Mold Shrinkage: 0.020 - 0.040 cm/cm
- Melt Flow: 10 g/10 min @Load 10.0 kg, Temperature 190 °C
- Hardness, Shore A: 54
- Tensile Strength: 7.00 MPa
$ 1572/MT
- Density: 0.980 g/cc
- Linear Mold Shrinkage: 0.0123 cm/cm
- Melt Flow: 1.2 g/10 min
- Hardness, Shore D: 56
- Tensile Strength, Ultimate: 19.3 - 28.3 MPa
$ 1753/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 65
- Tensile Strength at Break: 12.0 MPa
- Elongation at Break: 720 %
- Tear Strength: 45.6 kN/m
$ 1930/MT
- Density: 1.06 g/cc
- Melt Flow: 1.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 22.1 MPa
- Elongation at Break: 660 %
- Flexural Modulus: 1.94 GPa
$ 1735/MT
- Specific Gravity: 1.85 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 89
- Tensile Strength, Yield: 4.83 MPa
$ 2274/MT
- Density: 1.83 g/cc
- Melt Flow: 18 g/10 min @Load 5.00 kg, Temperature 230 °C
$ 1542/MT
- Density: 1.25 g/cc
- Linear Mold Shrinkage: 0.0060 cm/cm
- Melt Flow: 5.0 g/10 min
- Tensile Strength, Yield: 31.7 MPa
- Elongation at Break: 3.0 %
$ 1893/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0090 cm/cm
- Melt Flow: 5.0 g/10 min
- Hardness, Shore D: 73
- Tensile Strength, Ultimate: 31.0 MPa
$ 1921/MT
- Specific Gravity: 0.932 g/cc
- Linear Mold Shrinkage: 0.0090 cm/cm
- Melt Flow: 6.83 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 53
- Tensile Strength at Break: 18.8 MPa
$ 1501/MT
- Density: 0.910 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 16 g/10 min
- Hardness, Shore D: 55
- Tensile Strength, Ultimate: 16.6 MPa
$ 1616/MT
- Specific Gravity: 0.940 g/cc @Temperature 25.0 °C
- Shelf Life: 48.0 Month
- Color: Off-White
- Physical Form: Thermoplastic Pellet
- Siloxane Content (%): 50
$ 1670/MT
- Density: 1.01 g/cc
- Linear Mold Shrinkage: 0.013 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Melt Flow: 3.0 g/10 min @Load 5.00 kg, Temperature 230 °C
- Hardness, Shore A: 87
$ 1559/MT
- Hardness, Shore A: 34
- Hardness, Shore A: 37
- Hardness, Shore A: 40
- Tensile Strength, Ultimate: 7.72 MPa
- Tensile Strength, Ultimate: 8.170 MPa
$ 1448/MT
- Density: 0.990 g/cc
- Linear Mold Shrinkage: 0.014 cm/cm
- Melt Flow: 20 g/10 min
- Tensile Strength, Yield: 29.0 MPa
- Elongation at Break: 130 %
$ 1503/MT
- Specific Gravity: 1.20 g/cc
- Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 75
- Tensile Strength, Yield: 2.90 MPa
- Tensile Strength, Yield: 6.83 MPa
$ 1610/MT
- Density: 1.18 g/cc
- Linear Mold Shrinkage: 0.014 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Melt Flow: 10 g/10 min @Load 5.00 kg, Temperature 230 °C
- Hardness, Shore A: 68
$ 1781/MT
- Density: 0.968 g/cc
- Linear Mold Shrinkage: 0.01225 cm/cm
- Melt Flow: 5.5 g/10 min
- Hardness, Shore A: 87
- Tensile Strength, Ultimate: 17.4 MPa
$ 1588/MT
- Density: 1.86 g/cc
- Linear Mold Shrinkage: 0.0108 cm/cm
- Melt Flow: 0.90 g/10 min
- Hardness, Shore A: 91
- Tensile Strength, Ultimate: 6.40 MPa
$ 1740/MT
- Density: 1.985 g/cc
- Melt Flow: 7.9 g/10 min
- Hardness, Shore A: 90
- Elongation at Break: 379 %
- Flexural Modulus: 0.113 GPa
- Tear Strength: 62.9 kN/m
$ 1474/MT
- Density: 0.904 g/cc
- Linear Mold Shrinkage: 0.0124 cm/cm
- Melt Flow: 2.7 g/10 min
- Hardness, Shore D: 39
- Tensile Strength, Ultimate: 15.8 MPa
$ 1926/MT
- Density: 1.08 g/cc
- Linear Mold Shrinkage: 0.011 cm/cm
- Melt Flow: 16.5 g/10 min
- Tensile Strength, Yield: 24.7 MPa
- Elongation at Break: 150 %
$ 2144/MT
- Density: 1.19 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 2.0 - 10 g/10 min
- Hardness, Shore A: 45
- Tensile Strength, Ultimate: >= 2.50 MPa
$ 1545/MT
- Specific Gravity: 0.892 g/cc
- Linear Mold Shrinkage: 0.00010 cm/cm
- Melt Flow: 128 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 55
- Tensile Strength, Yield: 2.12 MPa
$ 2015/MT
- Specific Gravity: 1.15 g/cc
- Hardness, Shore A: 70
- Tensile Strength at Break: 15.0 MPa
- Elongation at Break: 600 %
- Tear Strength: 45.6 kN/m
$ 2196/MT
- Specific Gravity: 0.920 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 90
- Tensile Strength, Ultimate: 10.3 MPa
$ 1446/MT
- Specific Gravity: 0.910 g/cc
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 57
- Tensile Strength, Yield: 1.97 MPa
- Tensile Strength, Yield: 10.0 MPa
$ 1723/MT
- Specific Gravity: 1.07 g/cc
- Water Absorption: 0.060 %
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 33
$ 1540/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0080 cm/cm
- Melt Flow: 6.0 g/10 min
- Tensile Strength, Yield: 31.1 MPa
- Elongation at Break: 62 %
$ 1522/MT
- Hardness, Shore A: 38
- Hardness, Shore A: 42
- Hardness, Shore A: 43
- Hardness, Shore A: 44
- Tensile Strength, Ultimate: 6.89 MPa
$ 1544/MT
- Specific Gravity: 1.06 g/cc
- Melt Flow: 40 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 15
- Tensile Strength, Yield: 2.76 MPa
- Tensile Strength, Yield: 0.310 MPa @Strain 100 %
$ 1601/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 40
- Tensile Strength, Yield: 11.0 MPa
- Elongation at Break: 900 %
$ 1937/MT
- Density: 1.01 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 10 - 15 g/10 min
- Hardness, Shore A: 78
- Tensile Strength, Ultimate: 7.60 MPa
$ 2494/MT
- Specific Gravity: 0.942 g/cc
- Linear Mold Shrinkage: 0.016 cm/cm
- Melt Flow: 75 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 40
- Hardness, Shore A: 45
$ 1475/MT
- Density: 1.06 g/cc
- Linear Mold Shrinkage: 0.011 cm/cm
- Melt Flow: 9.5 g/10 min
- Tensile Strength, Ultimate: 30.3 MPa
- Elongation at Break: 30 %
$ 1496/MT
- Density: 1.007 g/cc
- Melt Flow: 2.8 g/10 min
- Hardness, Shore A: 83
- Tensile Strength, Ultimate: 9.30 MPa
- Elongation at Break: 675 %
$ 2265/MT
- Specific Gravity: 0.970 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 29.3 MPa
- Elongation at Break: 26 %
$ 1690/MT
- Specific Gravity: 1.15 g/cc
- Hardness, Shore A: 84
- Tensile Strength at Break: 11.9 MPa
- Elongation at Break: 280 %
- Tear Strength: 50.8 kN/m
$ 1458/MT
- Density: 1.13 g/cc
- Linear Mold Shrinkage: 0.011 cm/cm
- Melt Flow: 2.0 - 5.0 g/10 min
- Hardness, Shore A: 80
- Tensile Strength, Ultimate: >= 9.00 MPa
$ 2539/MT
- Specific Gravity: 0.952 g/cc
- Melt Flow: 2.8 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 53
- Tensile Strength, Ultimate: 4.32 MPa
- Tensile Strength, Ultimate: 18.3 MPa
$ 2529/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage: 0.010 - 0.030 cm/cm
- Melt Flow: 19 g/10 min @Load 10.0 kg, Temperature 190 °C
- Hardness, Shore A: 63
- Tensile Strength: 6.30 MPa
$ 1466/MT
- Density: 0.980 g/cc
- Melt Flow: 4.0 g/10 min
- Hardness, Shore A: 54
- Tensile Strength, Ultimate: 3.80 MPa
- Elongation at Break: >= 1000 %
$ 1475/MT
- Density: 1.074 g/cc
- Linear Mold Shrinkage: 0.0093 cm/cm
- Melt Flow: 1.1 g/10 min
- Hardness, Shore A: 84
- Tensile Strength, Ultimate: 4.30 MPa
$ 1855/MT
- Density: 1.229 g/cc
- Linear Mold Shrinkage: 0.013 cm/cm
- Hardness, Shore A: 70
- Tensile Strength, Ultimate: 3.50 MPa
- Elongation at Break: 696 %
$ 1908/MT
- Specific Gravity: 0.980 g/cc
- Melt Flow: 3.2 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 72
- Hardness, Shore A: 74
- Tensile Strength, Yield: 3.45 MPa
$ 1627/MT
- Density: 0.920 g/cc
- Melt Flow: 2.2 g/10 min
- Hardness, Shore A: 65
- Tensile Strength, Ultimate: >= 7.45 MPa
- Elongation at Break: >= 400 %
- Tear Strength: >= 24.5 kN/m
$ 1796/MT
- Density: 1.25 g/cc
- Linear Mold Shrinkage: 0.0090 cm/cm
- Melt Flow: 15 g/10 min
- Tensile Strength, Yield: 29.6 MPa
- Elongation at Break: 20 %
$ 1963/MT
- Density: 1.16 g/cc
- Hardness, Shore A: 44
- Hardness, Shore A: 46
- Hardness, Shore A: 49
- Hardness, Shore A: 50
$ 2061/MT
- Hardness, Shore A: 36
- Hardness, Shore A: 50
- Hardness, Shore A: 50
- Hardness, Shore A: 50
- Tensile Strength, Ultimate: 8.198 MPa
$ 2146/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0080 cm/cm
- Melt Flow: 2.0 g/10 min
- Tensile Strength, Ultimate: 41.4 MPa
- Elongation at Break: 50 %
$ 1554/MT
- Density: 0.900 g/cc
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 76
- Tensile Strength, Ultimate: 31.0 MPa
- Tensile Strength, Yield: 34.5 MPa
$ 2180/MT
- Density: 1.87 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 15 g/10 min
- Hardness, Shore D: 50
- Tensile Strength, Ultimate: 7.50 MPa
$ 1651/MT
- Density: 1.07 g/cc
- Linear Mold Shrinkage: 0.0030 cm/cm
- Melt Flow: 7.0 g/10 min
- Tensile Strength, Ultimate: 46.0 MPa
- Flexural Strength: 61.0 MPa
$ 2413/MT
- Density: 1.02 g/cc
- Water Absorption: 0.030 %
- Linear Mold Shrinkage: 0.013 cm/cm
- Melt Flow: 6.9 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 31.7 MPa
$ 1472/MT
- Density: 0.900 g/cc
- Melt Flow: 12 g/10 min
- Tensile Strength, Ultimate: 31.0 MPa
- Elongation at Break: 570 %
- Flexural Modulus: 1.379 GPa
- Gardner Impact: 3.40 J
$ 1481/MT
- Density: 1.16 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 5.0 - 9.0 g/10 min
- Hardness, Shore D: 63
- Tensile Strength, Ultimate: >= 15.2 MPa
$ 1835/MT
- Density: 0.970 g/cc
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 25.5 MPa
- Elongation at Break: 480 %
- Flexural Modulus: 1.08 GPa
$ 1535/MT
- Specific Gravity: 1.35 g/cc
- Water Absorption: 0.65 %
- Linear Mold Shrinkage: 0.020 cm/cm
- Melt Flow: 0.71 g/10 min
- Melt Flow: 2.8 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2056/MT
- Specific Gravity: 1.04 g/cc
- Linear Mold Shrinkage: 0.017 cm/cm
- Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 30
- Tensile Strength, Yield: 4.48 MPa
$ 1670/MT
- Specific Gravity: 1.03 g/cc
- Linear Mold Shrinkage: 0.013 cm/cm
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 83
- Tensile Strength, Yield: 4.55 MPa
$ 1822/MT
- Density: 1.03 g/cc
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 22.1 MPa
- Elongation at Break: 380 %
- Flexural Modulus: 0.552 GPa
$ 1531/MT
- Specific Gravity: 1.92 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 93
- Hardness, Shore D: 41
$ 1794/MT
- Density: 1.15 g/cc
- Hardness, Shore A: 65
- Hardness, Shore A: 66
- Hardness, Shore A: 67
- Hardness, Shore A: 67
$ 1752/MT
- Specific Gravity: 0.970 g/cc @Temperature 25.0 °C
- Shelf Life: 48.0 Month
- Color: Off-White
- Physical Form: Thermoplastic Pellet
- Siloxane Content (%): 50
$ 1874/MT
- Specific Gravity: 1.22 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 78
- Tensile Strength, Yield: 8.27 MPa
- Elongation at Break: 500 %
$ 2418/MT
- Density: 0.890 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 2.5 g/10 min
- Hardness, Shore D: 46
- Tensile Strength, Ultimate: 12.8 MPa
$ 1673/MT
- Specific Gravity: 1.11 g/cc
- Linear Mold Shrinkage: 0.010 - 0.030 cm/cm
- Melt Flow: 13 g/10 min @Load 10.0 kg, Temperature 190 °C
- Hardness, Shore A: 76
- Tensile Strength: 8.80 MPa
$ 2078/MT
- Density: 0.966 g/cc
- Melt Flow: 10 g/10 min
- Hardness, Shore A: 50
- Tensile Strength, Ultimate: 3.90 MPa
- Elongation at Break: 870 %
- Tear Strength: 23.7 kN/m
$ 1980/MT
- Density: 1.49 g/cc
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 230 °C
$ 1460/MT
- Density: 1.24 g/cc
- Linear Mold Shrinkage: 0.0080 cm/cm
- Melt Flow: 5.0 g/10 min
- Hardness, Shore D: 77
- Tensile Strength, Ultimate: 30.3 MPa
$ 2528/MT
- Melt Flow: 12 g/10 min @Load 2.16 kg
$ 1687/MT
- Density: 0.950 g/cc
- Melt Flow: 15.51 g/10 min
- Hardness, Shore A: 91.4
- Tensile Strength, Ultimate: 14.5 MPa
- Elongation at Break: 675 %
$ 1709/MT
- Hardness, Shore A: 34
- Hardness, Shore A: 38
- Hardness, Shore A: 41
- Tensile Strength, Ultimate: 6.27 MPa
- Tensile Strength, Ultimate: 8.48 MPa
$ 1930/MT
- Hardness, Shore A: 29
- Hardness, Shore A: 32
- Hardness, Shore A: 35
- Tensile Strength, Ultimate: 5.14 MPa
- Tensile Strength, Ultimate: 8.20 MPa
$ 2136/MT
- Hardness, Shore A: 33
- Hardness, Shore A: 34
- Hardness, Shore A: 39
- Tensile Strength, Ultimate: 5.93 MPa
- Tensile Strength, Ultimate: 8.34 MPa
$ 2323/MT
- Hardness, Shore A: 51
- Hardness, Shore A: 51
- Hardness, Shore A: 51
- Tensile Strength, Ultimate: 6.83 MPa
- Tensile Strength, Ultimate: 9.404 MPa
$ 2165/MT
- Specific Gravity: 1.15 g/cc
- Hardness, Shore A: 70
- Hardness, Shore A: 60 @Treatment Temp. 140 °C, Time 3.629e+6 sec
- Hardness, Shore A: 67 @Treatment Temp. 120 °C, Time 3.629e+6 sec
- Hardness, Shore A: 75 @Treatment Temp. 100 °C, Time 3.60e+6 sec
$ 1528/MT
- Specific Gravity: 1.19 g/cc
- Linear Mold Shrinkage: 0.010 - 0.030 cm/cm
- Melt Flow: 13 g/10 min @Load 10.0 kg, Temperature 190 °C
- Hardness, Shore A: 72
- Tensile Strength: 11.4 MPa
$ 1536/MT
- Specific Gravity: 1.14 g/cc
- Hardness, Shore A: 58
- Tensile Strength at Break: 11.0 MPa
- Elongation at Break: 680 %
- Tear Strength: 40.3 kN/m
$ 2042/MT
- Specific Gravity: 0.910 g/cc
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 46
- Tensile Strength, Yield: 13.1 MPa
- Tensile Strength, Yield: 11.0 MPa @Strain 100 %
$ 2421/MT
- Density: 1.04 g/cc
- Melt Flow: 4.0 g/10 min
- Hardness, Shore A: 72
- Tensile Strength, Ultimate: 7.60 MPa
- Elongation at Break: 800 %
$ 1513/MT
- Density: 1.20 g/cc
- Melt Flow: 11.5 g/10 min
- Hardness, Shore A: 74
- Tensile Strength, Ultimate: 7.10 MPa
- Elongation at Break: >= 750 %
- Tear Strength: 32.2 kN/m
$ 1962/MT
- Density: 0.905 g/cc
- Linear Mold Shrinkage: 0.018 cm/cm
- Melt Flow: 0.50 g/10 min
- Hardness, Shore A: 51
- Tensile Strength, Ultimate: 8.30 MPa
$ 1933/MT
- Density: 0.901 g/cc
- Linear Mold Shrinkage: 0.0106 cm/cm
- Melt Flow: 0.79 g/10 min
- Hardness, Shore D: 53
- Tensile Strength, Ultimate: 16.7 MPa
$ 1527/MT
- Specific Gravity: 1.20 g/cc
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 62
- Tensile Strength at Break: 6.21 MPa
- Elongation at Break: 700 %
- Tear Strength: 28.0 kN/m
$ 2096/MT
- Density: 1.02 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 3.0 g/10 min
- Hardness, Shore D: 65
- Tensile Strength, Ultimate: 20.7 MPa
$ 1490/MT
- Melt Flow: 2.4 g/10 min @Load 3.80 kg, Temperature 230 °C
- Melt Flow: 3.14 g/10 min @Load 3.80 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 29.8 MPa
- Elongation at Break: 31.8 %
- Flexural Strength: 47.8 MPa
$ 2103/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 30 g/10 min
- Hardness, Shore A: 86
- Tensile Strength, Ultimate: 4.00 MPa
$ 1896/MT
- Density: 1.14 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 3.0 g/10 min
- Hardness, Shore A: 87
- Tensile Strength, Ultimate: 10.3 MPa
$ 1682/MT
- Density: 1.10 g/cc
- Hardness, Shore A: 58
- Hardness, Shore A: 58
- Hardness, Shore A: 59
- Hardness, Shore A: 59
$ 1881/MT
- Density: 0.950 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 8.0 g/10 min
- Tensile Strength, Yield: 24.8 MPa
- Elongation at Break: 110 %
$ 1846/MT
- Melt Flow: 12 g/10 min @Load 2.16 kg
$ 1605/MT
- Density: 1.71 g/cc
- Melt Flow: 31 g/10 min @Load 5.00 kg, Temperature 230 °C
$ 1832/MT
- Melt Flow: 5.0 g/10 min @Load 2.16 kg
$ 2277/MT
- Density: 2.08 g/cc
- Melt Flow: 22.5 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1989/MT
- Density: 1.89 g/cc
- Melt Flow: 5.0 g/10 min
- Hardness, Shore A: 89
- Tensile Strength, Ultimate: 4.30 MPa
- Elongation at Break: 350 %
- Tear Strength: 30.0 kN/m
$ 1841/MT
- Density: 1.35 g/cc
- Linear Mold Shrinkage: 0.0090 cm/cm
- Melt Flow: 18 g/10 min
- Tensile Strength, Yield: 18.6 MPa
- Elongation at Break: 300 %
$ 1829/MT
- Density: 0.970 g/cc
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 22.8 MPa
- Elongation at Break: 70 %
- Flexural Modulus: 1.12 GPa
$ 1693/MT
- Density: 1.17 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 20.7 MPa
- Elongation at Break: 900 %
- Flexural Modulus: 0.689 GPa
$ 1562/MT
- Density: 1.02 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Break: 990 %
- Flexural Modulus: 0.503 GPa
$ 1963/MT
- Specific Gravity: 1.25 g/cc
- Melt Flow: 35 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 85
- Tensile Strength, Yield: 7.58 MPa
- Elongation at Break: 600 %
$ 2000/MT
- Specific Gravity: 0.892 g/cc
- Melt Flow: 100 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 32
- Tensile Strength, Yield: 5.83 MPa
- Elongation at Break: 690 %
$ 1556/MT
- Specific Gravity: 0.892 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 91 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 59
- Tensile Strength at Break: 7.45 MPa
$ 2144/MT
- Density: 0.900 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 3.0 g/10 min
- Hardness, Shore D: 41
- Tensile Strength, Ultimate: 12.8 MPa
$ 2132/MT
- Specific Gravity: 0.902 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 40
- Tensile Strength, Ultimate: 12.5 MPa
$ 2452/MT
- Specific Gravity: 1.26 g/cc
- Water Absorption: 0.050 %
- Linear Mold Shrinkage: 0.0090 - 0.013 cm/cm
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 39.6 MPa
$ 1787/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage: 0.013 cm/cm
- Melt Flow: 16.1 g/10 min
- Hardness, Shore A: 59
- Tensile Strength, Ultimate: >= 3.62 MPa
$ 1662/MT
- Specific Gravity: 0.950 g/cc
- Linear Mold Shrinkage: 0.013 cm/cm
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 90
- Tensile Strength, Ultimate: 11.0 MPa
$ 2469/MT
- Specific Gravity: 1.20 g/cc
- Melt Flow: 70 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 64
- Tensile Strength at Break: 3.45 MPa
- Tensile Strength, Yield: 1.86 MPa @Strain 100 %
$ 1530/MT
- Density: 0.970 - 1.03 g/cc
- Linear Mold Shrinkage: 0.013 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Melt Flow: 3.5 - 8.5 g/10 min
- Hardness, Shore A: 85
$ 1594/MT
- Density: 1.85 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 4.2 g/10 min
- Hardness, Shore D: 42
- Tensile Strength, Ultimate: 5.20 MPa
$ 2137/MT
- Density: 1.15 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 14 g/10 min
- Hardness, Shore D: 66
- Tensile Strength, Yield: 22.1 MPa
$ 2419/MT
- Density: 0.982 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 8.7 g/10 min
- Hardness, Shore A: 91
- Tensile Strength, Ultimate: 13.1 MPa
$ 1620/MT
- Density: 0.908 g/cc
- Linear Mold Shrinkage: 0.0096 cm/cm
- Melt Flow: 4.5 g/10 min
- Hardness, Shore A: 83
- Tensile Strength, Ultimate: 8.90 MPa
$ 1703/MT
- Density: 0.997 g/cc
- Melt Flow: 2.35 g/10 min
- Hardness, Shore A: 72
- Tensile Strength, Ultimate: 8.80 MPa
- Elongation at Break: 795 %
$ 1476/MT
- Density: 0.940 g/cc
- Linear Mold Shrinkage: 0.016 cm/cm
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 70
- Tensile Strength, Yield: 29.6 MPa
$ 2077/MT
- Specific Gravity: 0.910 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 55
- Tensile Strength, Yield: 21.7 MPa
- Elongation at Break: 850 %
$ 1870/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Melt Flow: 5.0 g/10 min
- Hardness, Rockwell R: 106
- Tensile Strength, Ultimate: 42.7 MPa
$ 1481/MT
- Density: 1.15 g/cc
- Melt Flow: 1.0 g/10 min @Load 5.00 kg, Temperature 230 °C
- Hardness, Shore A: 58
- Tensile Strength, Ultimate: 6.60 MPa
- Elongation at Break: 900 %
$ 2147/MT
- Density: 1.13 g/cc
- Hardness, Shore A: 40
- Hardness, Shore A: 42
- Hardness, Shore A: 43
- Hardness, Shore A: 44
$ 1714/MT
- Density: 1.06 g/cc
- Melt Flow: 7.0 g/10 min
- Hardness, Shore D: 58
- Flexural Modulus: 0.998 GPa
- Tear Strength: 61.0 kN/m
$ 1952/MT
- Density: 1.06 g/cc
- Melt Flow: 7.0 g/10 min
- Hardness, Shore D: 58
- Flexural Modulus: 0.998 GPa
- Tear Strength: 61.0 kN/m
$ 1589/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage: 0.0085 cm/cm
- Melt Flow: 18 g/10 min
- Tensile Strength, Yield: 29.0 MPa
- Elongation at Break: 25 %
$ 1480/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage: 0.0085 cm/cm
- Melt Flow: 18 g/10 min
- Tensile Strength, Yield: 29.0 MPa
- Elongation at Break: 25 %
$ 1451/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage: 0.0085 cm/cm
- Melt Flow: 18 g/10 min
- Tensile Strength, Yield: 29.0 MPa
- Elongation at Break: 25 %
$ 1968/MT
- Density: 1.23 g/cc
- Linear Mold Shrinkage: 0.0090 cm/cm
- Melt Flow: 8.0 g/10 min
- Tensile Strength, Yield: 29.0 MPa
- Elongation at Break: 30 %
$ 2077/MT
- Density: 0.980 g/cc
- Melt Flow: 6.0 g/10 min
- Hardness, Shore D: 62
- Tensile Strength, Ultimate: 17.2 MPa
- Elongation at Break: 475 %
$ 1624/MT
- Density: 1.32 g/cc
- Linear Mold Shrinkage: 0.0070 - 0.0090 cm/cm
- Melt Flow: 2.25 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 19.3 MPa
- Elongation at Break: 900 %
$ 1627/MT
- Specific Gravity: 0.920 g/cc
- Linear Mold Shrinkage: 0.016 cm/cm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 67
- Tensile Strength, Yield: 2.14 MPa
$ 1500/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 49
- Tensile Strength, Yield: 5.17 MPa
$ 1557/MT
- Specific Gravity: 1.00 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 95
- Tensile Strength, Yield: 12.4 MPa
$ 1635/MT
- Density: 1.06 g/cc
- Melt Flow: 7.0 g/10 min
- Hardness, Shore A: 50
- Tensile Strength, Ultimate: 6.90 MPa
- Elongation at Break: 550 %
- Tear Strength: 22.0 kN/m
$ 1453/MT
- Density: 1.00 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 10 - 15 g/10 min
- Hardness, Shore A: 78
- Tensile Strength, Ultimate: 8.30 MPa
$ 1689/MT
- Density: 0.9176 g/cc
- Linear Mold Shrinkage: 0.0115 cm/cm
- Melt Flow: 2.2 g/10 min
- Tensile Strength, Ultimate: 22.3 MPa
- Elongation at Break: 887 %
$ 1481/MT
- Density: 1.72 g/cc
- Melt Flow: 20 g/10 min @Load 5.00 kg, Temperature 230 °C
$ 2282/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.65 %
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 2.25 g/10 min
- Melt Flow: 3.9 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2049/MT
- Density: 1.01 g/cc
- Melt Flow: 1.0 g/10 min
- Hardness, Shore D: 34
- Tensile Strength, Ultimate: 8.30 MPa
- Elongation at Break: 560 %
$ 1767/MT
- Linear Mold Shrinkage: 0.0126 cm/cm
- Melt Flow: 2.6 g/10 min
- Hardness, Shore D: 51.1
- Tensile Strength, Ultimate: 18.6 MPa
- Elongation at Break: 156 %
$ 1923/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage: 0.014 cm/cm
- Melt Flow: 15.8 g/10 min
- Hardness, Shore A: 60
- Tensile Strength, Ultimate: >= 3.62 MPa
$ 2241/MT
- Density: 1.13 g/cc
- Linear Mold Shrinkage: 0.0055 - 0.010 cm/cm
- Melt Flow: 4.0 g/10 min
- Ash: 30 - 35 %
- Tensile Strength, Ultimate: 0.365 MPa
$ 1866/MT
- Melt Flow: 12 g/10 min @Load 2.16 kg
$ 2436/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Melt Flow: 2.0 g/10 min
- Hardness, Rockwell R: 103
- Tensile Strength, Ultimate: 31.0 MPa
$ 1500/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 71
- Tensile Strength at Break: 16.0 MPa
- Elongation at Break: 600 %
- Tear Strength: 45.6 kN/m
$ 1737/MT
- Density: 1.08 g/cc
- Melt Flow: 7.0 g/10 min
- Hardness, Shore D: 58
- Tensile Strength, Ultimate: >= 20.69 MPa
- Elongation at Break: >= 18 %
$ 1737/MT
- Density: 0.948 g/cc
- Linear Mold Shrinkage: 0.0090 cm/cm
- Melt Flow: 4.0 g/10 min
- Tensile Strength, Ultimate: 44.8 MPa
- Elongation at Break: 34 %
$ 2378/MT
- Density: 0.920 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 7.0 g/10 min
- Hardness, Shore A: 89
- Tensile Strength, Ultimate: 8.90 MPa
$ 1446/MT
- Density: 1.18 g/cc
- Linear Mold Shrinkage: 0.014 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Melt Flow: 10 g/10 min @Load 5.00 kg, Temperature 230 °C
- Hardness, Shore A: 68
$ 1990/MT
- Density: 1.20 g/cc
- Melt Flow: 30 - 50 g/10 min
- Hardness, Shore A: 75
- Tensile Strength, Ultimate: >= 3.00 MPa
- Elongation at Break: >= 250 %
$ 1662/MT
- Density: 1.16 - 1.22 g/cc
- Linear Mold Shrinkage: 0.013 cm/cm
- Melt Flow: 37.5 g/10 min
- Hardness, Shore A: 60
- Tensile Strength, Ultimate: >= 3.62 MPa
$ 1491/MT
- Density: 0.870 g/cc
- Hardness, Shore D: 41
- Tensile Strength, Ultimate: >= 11.0 MPa
- Elongation at Break: >= 50 %
- Flexural Modulus: 0.0600 GPa
$ 1906/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 cm/cm
- Melt Flow: 5.0 g/10 min
- Hardness, Shore D: 77
- Tensile Strength, Ultimate: 58.6 MPa
$ 2166/MT
- Density: 1.14 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 19 g/10 min
- Tensile Strength, Yield: 26.9 MPa
- Elongation at Break: 90 %
$ 1496/MT
- Density: 1.15 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 18 g/10 min
- Tensile Strength, Yield: 23.4 MPa
- Elongation at Break: 110 %
$ 1520/MT
- Density: 1.17 g/cc
- Linear Mold Shrinkage: 0.014 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Hardness, Shore A: 43
- Tensile Strength, Ultimate: >= 5.17 MPa
$ 1652/MT
- Density: 1.28 g/cc
- Linear Mold Shrinkage: 0.013 cm/cm
- Melt Flow: 14 - 16 g/10 min
- Hardness, Shore A: 60
- Tensile Strength, Ultimate: >= 3.62 MPa
$ 1741/MT
- Density: 1.72 g/cc
- Melt Flow: 12 g/10 min @Load 5.00 kg, Temperature 230 °C
$ 1847/MT
- Specific Gravity: 1.14 g/cc
- Linear Mold Shrinkage: 0.0020 cm/cm
- Melt Flow: 1.01 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 51.4 MPa
- Elongation at Break: 17 %
$ 2187/MT
- Density: 0.890 g/cc
- Linear Mold Shrinkage: 0.0090 cm/cm
- Melt Flow: 2.8 g/10 min
- Hardness, Shore D: 46
- Tensile Strength, Ultimate: 12.8 MPa
$ 1615/MT
- Density: 0.890 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 1.8 g/10 min
- Hardness, Shore D: 41
- Tensile Strength, Ultimate: 12.3 MPa
$ 1738/MT
- Density: 0.910 g/cc
- Linear Mold Shrinkage: 0.0129 cm/cm
- Melt Flow: 7.5 g/10 min
- Hardness, Shore D: 51
- Tensile Strength, Ultimate: 17.2 MPa
$ 1474/MT
- Density: 1.06 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 2.9 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 19.8 MPa
- Elongation at Break: 930 %
$ 1561/MT
- Density: 1.74 g/cc
- Melt Flow: 10 g/10 min @Load 5.00 kg, Temperature 230 °C
$ 2289/MT
- Specific Gravity: 1.25 g/cc
- Melt Flow: 5.97 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 43
- Tensile Strength, Yield: 10.1 MPa
- Elongation at Break: 480 %
$ 1536/MT
- Specific Gravity: 0.962 g/cc
- Melt Flow: 9.55 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 86
- Tensile Strength, Ultimate: 8.41 MPa
- Elongation at Break: 820 %
$ 1706/MT
- Specific Gravity: 1.01 g/cc
- Water Absorption: 0.65 %
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 35.2 MPa
$ 2119/MT
- Density: 0.900 g/cc
- Linear Mold Shrinkage: 0.0090 cm/cm
- Melt Flow: 2.7 g/10 min
- Hardness, Shore D: 46
- Tensile Strength, Ultimate: 11.7 - 13.8 MPa
$ 1625/MT
- Density: 1.19 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 2.0 - 10 g/10 min
- Hardness, Shore A: 44
- Tensile Strength, Ultimate: >= 2.48 MPa
$ 1525/MT
- Density: 1.82 g/cc
- Melt Flow: 1.3 g/10 min
- Hardness, Shore A: 85
- Tensile Strength, Ultimate: 3.30 MPa
- Elongation at Break: 130 %
- Tear Strength: 23.6 kN/m
$ 1883/MT
- Specific Gravity: 0.940 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 56
- Tensile Strength, Yield: 16.5 MPa
$ 1764/MT
- Density: 0.918 g/cc
- Melt Flow: 18 g/10 min
- Hardness, Shore A: 56
- Tensile Strength, Ultimate: 2.90 MPa
- Elongation at Break: 820 %
- Tear Strength: 24.5 kN/m
$ 1878/MT
- Density: 1.26 g/cc
- Linear Mold Shrinkage: 0.050 cm/cm
- Melt Flow: 14 g/10 min
- Tensile Strength, Yield: 25.1 MPa
- Elongation at Break: 15 %
$ 1762/MT
- Specific Gravity: 0.930 g/cc @Temperature 25.0 °C
- Shelf Life: 48.0 Month
- Color: White to Off-White
- Physical Form: Solid
- Siloxane Content (%): 25
$ 1672/MT
- Density: 0.910 g/cc
- Melt Flow: 9.0 g/10 min
- Hardness, Shore D: 55
- Tensile Strength, Ultimate: 20.7 MPa
- Elongation at Break: 1200 %
$ 1916/MT
- Density: 1.07 g/cc
- Melt Flow: 1.5 g/10 min
- Hardness, Shore A: 80
- Tensile Strength, Ultimate: 9.10 MPa
- Elongation at Break: 1600 %
$ 1460/MT
- Density: 0.910 g/cc
- Melt Flow: 6.0 - 12 g/10 min
- Hardness, Shore D: 41
- Tensile Strength, Ultimate: 10.3 - 14.5 MPa
- Elongation at Break: 500 - 700 %
$ 1469/MT
- Density: 1.00 g/cc
- Linear Mold Shrinkage: 0.014 cm/cm
- Melt Flow: 6.0 g/10 min
- Hardness, Shore D: 38
- Tensile Strength, Ultimate: 12.0 MPa
$ 2421/MT
- Density: 0.940 g/cc
- Linear Mold Shrinkage: 0.018 cm/cm
- Melt Flow: 9.0 g/10 min
- Hardness, Shore D: 65
- Tensile Strength, Ultimate: 9.00 MPa
$ 1578/MT
- Density: 1.01 g/cc
- Linear Mold Shrinkage: 0.016 cm/cm
- Melt Flow: 1.0 - 3.0 g/10 min
- Hardness, Shore D: 54
- Tensile Strength, Ultimate: 14.3 MPa
$ 1575/MT
- Density: 0.890 g/cc
- Melt Flow: 2.0 g/10 min
- Hardness, Shore A: 64
- Tensile Strength, Ultimate: >= 9.38 MPa
- Elongation at Break: >= 625 %
- Tear Strength: >= 30.3 kN/m
$ 2126/MT
- Melt Flow: 9.0 g/10 min
- Hardness, Shore A: 50
- Tensile Strength, Ultimate: 11.9 MPa
- Elongation at Break: 850 %
- Flexural Modulus: 0.370 GPa
$ 2329/MT
- Density: 1.49 g/cc
- Linear Mold Shrinkage: 0.0052 cm/cm
- Melt Flow: 1.7 g/10 min
- Hardness, Shore A: 76
- Tensile Strength, Ultimate: 2.30 MPa
$ 1644/MT
- Density: 1.19 g/cc
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 15.9 MPa
- Elongation at Break: 40 %
- Flexural Modulus: 0.689 GPa
$ 2163/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 16 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 57
- Tensile Strength, Yield: 1.31 MPa
$ 1645/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0080 cm/cm
- Melt Flow: 5.0 g/10 min
- Hardness, Shore D: 76
- Tensile Strength, Ultimate: 33.8 MPa
$ 1516/MT
- Density: 1.24 g/cc
- Linear Mold Shrinkage: 0.0080 cm/cm
- Melt Flow: 6.0 g/10 min
- Tensile Strength, Yield: 30.3 MPa
- Elongation at Break: 25 %
$ 1540/MT
- Specific Gravity: 0.892 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 91 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 59
- Tensile Strength, Yield: 7.45 MPa
$ 2463/MT
- Density: 1.075 g/cc
- Linear Mold Shrinkage: 0.013 cm/cm
- Melt Flow: 2.0 - 5.0 g/10 min
- Hardness, Shore A: 50
- Tensile Strength, Ultimate: >= 3.62 MPa
$ 1569/MT
- Specific Gravity: 1.88 g/cc
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 77
- Tensile Strength, Yield: 2.76 MPa
- Elongation at Break: 500 %
$ 2131/MT
- Density: 0.910 g/cc
- Linear Mold Shrinkage: 0.016 cm/cm
- Melt Flow: 1.3 g/10 min
- Hardness, Shore A: 73
- Tensile Strength, Ultimate: >= 1.17 MPa
$ 1490/MT
- Specific Gravity: 1.09 g/cc
- Linear Mold Shrinkage: 0.010 - 0.030 cm/cm
- Melt Flow: 21 g/10 min @Load 10.0 kg, Temperature 190 °C
- Hardness, Shore A: 67
- Tensile Strength: 5.60 MPa
$ 1480/MT
- Density: 1.21 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Melt Flow: 5.0 g/10 min
- Tensile Strength, Ultimate: 38.6 MPa
- Elongation at Break: 40 %
$ 1990/MT
- Specific Gravity: 0.920 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 43
- Tensile Strength, Ultimate: 13.4 MPa
$ 1449/MT
- Density: 1.09 g/cc
- Linear Mold Shrinkage: 0.0080 cm/cm
- Melt Flow: 18 g/10 min
- Tensile Strength, Yield: 29.6 MPa
- Elongation at Break: 45 %
$ 1996/MT
- Specific Gravity: 0.982 g/cc
- Linear Mold Shrinkage: 0.014 cm/cm
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 87
- Tensile Strength, Yield: 11.7 MPa
$ 1685/MT
- Density: 0.920 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 1.3 g/10 min
- Hardness, Shore A: 73
- Tensile Strength, Ultimate: >= 7.45 MPa
$ 1514/MT
- Density: 1.02 g/cc
- Melt Flow: 5.0 - 7.0 g/10 min
- Hardness, Shore A: 86
- Tensile Strength, Ultimate: 7.60 MPa
- Elongation at Break: 780 %
$ 1734/MT
- Specific Gravity: 0.892 g/cc
- Linear Mold Shrinkage: 0.013 cm/cm
- Melt Flow: 96 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 45
- Tensile Strength, Yield: 2.95 MPa
$ 1532/MT
- Melt Flow: 2.96 g/10 min
- Flexural Strength: 35.6 MPa
- Flexural Modulus: 1.17 GPa
- Izod Impact, Notched: 0.531 J/cm
- Gardner Impact: 2.316 J
$ 1832/MT
- Density: 1.83 g/cc
- Melt Flow: 5.0 g/10 min
- Hardness, Shore A: 82
- Tensile Strength, Ultimate: 2.90 MPa
- Elongation at Break: 600 %
$ 2180/MT
- Specific Gravity: 0.892 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 45
- Tensile Strength, Yield: 12.8 MPa
$ 1569/MT
- Specific Gravity: 0.980 g/cc
- Linear Mold Shrinkage: 0.011 - 0.013 cm/cm
- Melt Flow: 9.7 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 29.6 MPa
- Elongation at Break: 38 %
$ 1939/MT
- Specific Gravity: 1.04 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 1.2 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 66
- Tensile Strength at Break: 10.3 MPa
$ 1595/MT
- Density: 1.02 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 8.5 g/10 min
- Tensile Strength, Yield: 34.6 MPa
- Elongation at Break: 36 %
$ 1449/MT
- Density: 1.35 g/cc
- Melt Flow: 18 g/10 min
- Tensile Strength, Ultimate: 18.6 MPa
- Elongation at Break: 300 %
- Flexural Strength: 35.9 MPa
$ 1591/MT
- Density: 1.96 g/cc
- Melt Flow: 43 g/10 min @Load 5.00 kg, Temperature 190 °C
$ 1505/MT
- Density: 1.00 g/cc
- Linear Mold Shrinkage: 0.014 cm/cm
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 70
- Tensile Strength, Yield: 27.9 MPa
$ 1542/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0090 cm/cm
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 67
- Tensile Strength, Yield: 1.82 MPa
$ 1982/MT
- Specific Gravity: 0.942 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 40
- Tensile Strength, Yield: 12.1 MPa
$ 1736/MT
- Specific Gravity: 1.01 g/cc
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 54
- Tensile Strength, Yield: 14.3 MPa
- Elongation at Break: 630 %
$ 1529/MT
- Density: 1.23 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 17 g/10 min
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Break: 150 %
$ 1624/MT
- Density: 0.920 g/cc
- Linear Mold Shrinkage: 0.016 cm/cm
- Melt Flow: 1.0 - 5.0 g/10 min
- Hardness, Shore A: 73
- Tensile Strength, Ultimate: >= 0.740 MPa
$ 1769/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Melt Flow: 5.0 g/10 min
- Tensile Strength, Yield: 58.6 MPa
- Elongation at Break: 5.0 %
$ 1497/MT
- Density: 0.920 g/cc
- Melt Flow: 2.0 g/10 min
- Hardness, Shore D: 45
- Tensile Strength, Ultimate: 14.5 MPa
- Elongation at Break: >= 1000 %
$ 1682/MT
- Specific Gravity: 1.20 g/cc @Temperature 25.0 °C
- Shelf Life: 24.0 Month
- Color: White
- Physical Form: Coarse Powder
$ 1671/MT
- Density: 1.32 g/cc
- Melt Flow: 15.2 g/10 min
- Tensile Strength, Ultimate: 12.8 MPa
- Elongation at Break: 20 %
- Flexural Strength: 22.5 MPa
$ 1628/MT
- Specific Gravity: 1.00 g/cc
- Linear Mold Shrinkage: 0.013 cm/cm
- Melt Flow: 5.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 85
- Tensile Strength, Yield: 10.9 MPa
$ 1901/MT
- Density: 1.34 g/cc
- Linear Mold Shrinkage: 0.0080 cm/cm
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 26.9 MPa
- Elongation at Break: 2.0 %
$ 1636/MT
- Density: 0.900 g/cc
- Melt Flow: 2.0 g/10 min
- Hardness, Shore D: 45
- Tensile Strength, Ultimate: 14.5 MPa
- Elongation at Break: >= 1300 %
$ 1506/MT
- Melt Flow: 7.0 g/10 min
- Hardness, Rockwell R: 101
- Tensile Strength, Ultimate: 40.0 MPa
- Elongation at Break: 40 %
- Flexural Strength: 58.6 MPa
$ 1651/MT
- Specific Gravity: 0.950 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 20.7 MPa
- Elongation at Break: 160 %
$ 1832/MT
- Density: 1.03 g/cc
- Melt Flow: 1.5 g/10 min
- Hardness, Shore A: 80
- Tensile Strength, Ultimate: 5.00 MPa
- Elongation at Break: 300 %
$ 1631/MT
- Specific Gravity: 1.20 g/cc @Temperature 25.0 °C
- Shelf Life: 24.0 Month
- Color: White
- Physical Form: Coarse Powder
$ 1459/MT
- Specific Gravity: 0.882 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 29.0 MPa
$ 1672/MT
- Specific Gravity: 0.892 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 46
- Tensile Strength, Yield: 12.8 MPa
$ 2343/MT
- Density: 0.910 g/cc
- Linear Mold Shrinkage: 0.014 cm/cm
- Melt Flow: 2.0 - 5.0 g/10 min
- Hardness, Shore A: 55
- Tensile Strength, Ultimate: 10.0 MPa
$ 1963/MT
- Density: 1.15 g/cc
- Linear Mold Shrinkage: 0.011 cm/cm
- Melt Flow: 11 g/10 min
- Hardness, Shore D: 70
- Tensile Strength, Yield: 15.2 MPa
$ 1505/MT
- Specific Gravity: 0.972 g/cc
- Linear Mold Shrinkage: 0.013 cm/cm
- Melt Flow: 2.8 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 89
- Tensile Strength, Ultimate: 10.0 MPa
$ 1646/MT
- Specific Gravity: 1.07 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 33
- Tensile Strength, Yield: 5.50 MPa
$ 1923/MT
- Specific Gravity: 1.20 g/cc
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 45
- Tensile Strength, Yield: 1.17 MPa
- Tensile Strength, Yield: 5.00 MPa
$ 2500/MT
- Specific Gravity: 0.912 g/cc
- Linear Mold Shrinkage: 0.019 cm/cm
- Melt Flow: 7.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 72
- Tensile Strength, Yield: 6.76 MPa
$ 2116/MT
- Hardness, Shore A: 48
- Hardness, Shore A: 55
- Hardness, Shore A: 55
- Hardness, Shore A: 57
- Tensile Strength, Ultimate: 8.27 MPa
$ 2127/MT
- Density: 0.910 g/cc
- Linear Mold Shrinkage: 0.011 cm/cm
- Melt Flow: 8.0 g/10 min
- Hardness, Shore D: 40
- Tensile Strength, Ultimate: >= 10.13 MPa
$ 1546/MT
- Density: 0.890 g/cc
- Linear Mold Shrinkage: 0.0090 cm/cm
- Melt Flow: 2.8 g/10 min
- Hardness, Shore D: 50
- Tensile Strength, Ultimate: 11.7 - 15.1 MPa
$ 1521/MT
- Density: 1.15 g/cc
- Melt Flow: 8.0 g/10 min
- Tensile Strength, Ultimate: 49.3 MPa
- Elongation at Break: 16 %
- Flexural Strength: 70.0 MPa
$ 1916/MT
- Density: 1.15 g/cc
- Hardness, Shore A: 89
- Tensile Strength, Ultimate: 11.2 MPa
- Elongation at Break: 600 %
- 300% Modulus: 0.00750 GPa
- Tear Strength: 56.0 kN/m
$ 1504/MT
- Density: 1.24 g/cc
- Linear Mold Shrinkage: 0.0090 cm/cm
- Melt Flow: 10 g/10 min
- Tensile Strength, Yield: 26.4 MPa
- Elongation at Break: 150 %
$ 1858/MT
- Specific Gravity: 0.932 g/cc
- Melt Flow: 172 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 19
- Tensile Strength, Ultimate: 2.18 MPa
- Elongation at Break: 940 %
- Tear Strength: 12.8 kN/m
$ 2188/MT
- Density: 1.09 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Melt Flow: 2.05 g/10 min
- Tensile Strength, Ultimate: 19.3 MPa
- Elongation at Break: 450 %
$ 1798/MT
- Density: 0.950 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 15 g/10 min
- Tensile Strength, Ultimate: 20.7 MPa
- Elongation at Break: 860 %
$ 1726/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Melt Flow: 2.5 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 96
- Tensile Strength, Ultimate: 44.8 MPa
$ 1698/MT
- Density: 1.18 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.012 cm/cm
- Melt Flow: 12 g/10 min
- Hardness, Shore A: 55
$ 1549/MT
- Density: 0.910 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 1.6 g/10 min
- Hardness, Shore A: 73
- Tensile Strength, Ultimate: >= 10.62 MPa
$ 1695/MT
- Specific Gravity: 0.892 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 50
- Tensile Strength, Yield: 13.4 MPa
$ 1496/MT
- Density: 0.980 g/cc
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 25.9 MPa
- Elongation at Break: 150 %
- Flexural Modulus: 1.10 GPa
$ 1561/MT
- Specific Gravity: 1.89 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 14 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ash: 65.6 %
- Hardness, Shore A: 80
$ 1913/MT
- Density: 1.69 g/cc
- Melt Flow: 15 g/10 min @Load 5.00 kg, Temperature 230 °C
$ 2113/MT
- Density: 1.06 g/cc
- Melt Flow: 5.0 g/10 min
- Hardness, Shore D: 54
- Tensile Strength, Ultimate: 17.9 MPa
- Elongation at Break: 260 %
$ 2108/MT
- Specific Gravity: 2.11 g/cc
- Melt Flow: 6.6 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 91
- Tensile Strength, Yield: 3.45 MPa
- Elongation at Break: 300 %
$ 1736/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0060 cm/cm
- Melt Flow: 5.0 g/10 min
- Tensile Strength, Yield: 40.7 MPa
- Elongation at Break: 4.0 %
$ 1737/MT
- Specific Gravity: 0.890 g/cc
- Water Absorption: 0.040 %
- Melt Flow: 30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 52.6 g/10 min @Load 5.00 kg, Temperature 230 °C
- Hardness, Shore A: 3.0
$ 1591/MT
- Specific Gravity: 1.19 g/cc
- Linear Mold Shrinkage: 0.010 - 0.030 cm/cm
- Melt Flow: 54 g/10 min @Load 10.0 kg, Temperature 190 °C
- Hardness, Shore A: 83
- Tensile Strength: 15.4 MPa
$ 1730/MT
- Hardness, Shore A: 50
- Hardness, Shore A: 59
- Hardness, Shore A: 60
- Hardness, Shore A: 61
- Tensile Strength, Ultimate: 9.115 MPa
$ 1880/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 10 - 15 g/10 min
- Hardness, Shore A: 55
- Tensile Strength, Ultimate: >= 2.60 MPa
$ 1994/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Melt Flow: 2.5 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 96
- Tensile Strength, Ultimate: 39.3 MPa
$ 1866/MT
- Density: 1.08 g/cc
- Linear Mold Shrinkage: 0.0090 cm/cm
- Melt Flow: 18 g/10 min
- Hardness, Shore D: 72
- Tensile Strength, Ultimate: 24.1 MPa
$ 1501/MT
- Hardness, Shore A: 64
- Hardness, Shore A: 70
- Hardness, Shore A: 71
- Hardness, Shore A: 73
- Tensile Strength, Ultimate: 7.58 MPa
$ 1739/MT
- Specific Gravity: 1.05 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 44
- Tensile Strength, Yield: 11.7 MPa
- Tensile Strength, Yield: 15.9 MPa
$ 1858/MT
- Density: 1.18 g/cc
- Melt Flow: 10 g/10 min
- Hardness, Shore A: 79
- Tensile Strength, Ultimate: 6.20 MPa
- Elongation at Break: 850 %
$ 1520/MT
- Density: 0.987 g/cc
- Linear Mold Shrinkage: 0.010 - 0.013 cm/cm
- Melt Flow: 2.9 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 20.0 MPa
- Elongation at Break: 900 %
$ 2067/MT
- Density: 1.135 g/cc
- Melt Flow: 14 g/10 min
- Tensile Strength, Ultimate: 23.5 MPa
- Elongation at Break: 220 %
- Flexural Strength: 34.5 MPa
$ 2118/MT
- Specific Gravity: 1.10 g/cc @Temperature 25.0 °C
- Volatiles: 0.00 %
- Shelf Life: 48.0 Month
- Color: Off-White
- Physical Form: Particles
- Siloxane Content (%): 50
$ 2170/MT
- Specific Gravity: 1.25 g/cc
- Linear Mold Shrinkage: 0.0030 cm/cm
- Melt Flow: 1.3 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 68.9 MPa
- Elongation at Break: 15 %
$ 1986/MT
- Specific Gravity: 1.16 g/cc
- Melt Flow: 60 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 89
- Tensile Strength, Yield: 10.3 MPa
- Elongation at Break: 550 %
$ 1666/MT
- Density: 1.10 g/cc
- Melt Flow: 2.0 g/10 min
- Hardness, Shore A: 78
- Tensile Strength, Ultimate: 8.30 MPa
- Elongation at Break: 1000 %
$ 1654/MT
- Density: 1.83 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 5.0 - 22 g/10 min
- Hardness, Shore A: 89
- Tensile Strength, Ultimate: >= 4.80 MPa
$ 1726/MT
- Density: 1.24 g/cc
- Linear Mold Shrinkage: 0.0080 cm/cm
- Melt Flow: 12 g/10 min
- Tensile Strength, Yield: 30.3 MPa
- Elongation at Break: 25 %
$ 1983/MT
- Specific Gravity: 0.970 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 42.1 MPa
- Elongation at Break: 80 %
$ 1994/MT
- Density: 1.30 g/cc
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Melt Flow: 16.5 g/10 min
- Tensile Strength, Ultimate: 22.8 MPa
- Elongation at Break: 25 %
$ 1762/MT
- Density: 1.06 g/cc
- Melt Flow: 7.8 g/10 min
- Hardness, Shore D: 57
- Flexural Modulus: 1.00 GPa
- Gardner Impact: 15.3 J @Temperature -6.67 °C
- Tear Strength: 60.9 kN/m
$ 1548/MT
- Specific Gravity: 0.922 g/cc
- Linear Mold Shrinkage: 0.0090 cm/cm
- Melt Flow: 5.8 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 51
- Tensile Strength at Break: 22.0 MPa
$ 1638/MT
- Density: 1.06 g/cc
- Water Absorption: 0.020 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Melt Flow: 1.37 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 88
$ 1480/MT
- Specific Gravity: 1.12 g/cc
- Hardness, Shore A: 52
- Tensile Strength at Break: 7.10 MPa
- Elongation at Break: 470 %
- Tear Strength: 24.5 kN/m
$ 1652/MT
- Specific Gravity: 1.06 g/cc
- Linear Mold Shrinkage: 0.014 cm/cm
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 32
- Tensile Strength, Yield: 8.62 MPa
$ 1514/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage: 0.013 cm/cm
- Melt Flow: 1.2 g/10 min
- Hardness, Shore D: 59
- Tensile Strength, Ultimate: >= 3.62 MPa
$ 1754/MT
- Density: 1.85 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 5.0 g/10 min
- Hardness, Shore A: 89
- Tensile Strength, Ultimate: 4.80 MPa
$ 1902/MT
- Density: 1.25 g/cc
- Linear Mold Shrinkage: 0.0060 cm/cm
- Melt Flow: 5.0 g/10 min
- Hardness, Shore D: 77
- Tensile Strength, Ultimate: 31.0 MPa
$ 2149/MT
- Specific Gravity: 1.09 g/cc
- Linear Mold Shrinkage: 0.010 - 0.030 cm/cm
- Melt Flow: 20 g/10 min @Load 10.0 kg, Temperature 190 °C
- Hardness, Shore A: 62
- Tensile Strength: 5.10 MPa
$ 1455/MT
- Density: 1.01 g/cc
- Melt Flow: 3.9 g/10 min
- Hardness, Shore A: 83
- Tensile Strength, Ultimate: 14.0 MPa
- Elongation at Break: 725 %
$ 2087/MT
- Density: 1.74 g/cc
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1519/MT
- Density: 1.02 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 16.5 MPa
- Elongation at Break: 900 %
- Flexural Modulus: 0.214 GPa
$ 1504/MT
- Density: 1.80 g/cc
- Melt Flow: 25 g/10 min @Load 5.00 kg, Temperature 230 °C
$ 1655/MT
- Melt Flow: 20 g/10 min @Load 2.16 kg
$ 1907/MT
- Density: 0.960 g/cc
- Melt Flow: 5.4 g/10 min
- Hardness, Shore A: 88
- Tensile Strength, Ultimate: 9.20 MPa
- Elongation at Break: 505 %
$ 2543/MT
- Density: 1.06 g/cc
- Melt Flow: 3.0 g/10 min
- Hardness, Shore A: 39
- Tensile Strength, Ultimate: 3.90 MPa
- Elongation at Break: 778 %
- Tear Strength: 17.0 kN/m
$ 1942/MT
- Density: 1.03 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 5.0 - 10 g/10 min
- Hardness, Shore D: 50
- Tensile Strength, Ultimate: >= 10.3 MPa
$ 1488/MT
- Viscosity: 400 cP
- Viscosity: 400 cP
- Penetration: 245 - 275
$ 2255/MT
- Specific Gravity: 0.922 g/cc
- Melt Flow: 26 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 53
- Tensile Strength, Ultimate: 13.79 MPa
- Elongation at Break: 120 %
$ 1660/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 32
- Tensile Strength, Yield: 5.86 MPa
- Elongation at Break: 690 %
$ 2096/MT
- Density: 1.18 g/cc
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 19.3 MPa
- Elongation at Break: 800 %
- Flexural Modulus: 1.01 GPa
$ 1445/MT
- Density: 1.08 g/cc
- Linear Mold Shrinkage: 0.0096 cm/cm
- Melt Flow: 4.0 g/10 min
- Hardness, Shore A: 87
- Tensile Strength, Ultimate: 9.00 MPa
$ 2598/MT
- Specific Gravity: 1.08 g/cc
- Hardness, Shore A: 56
- Hardness, Shore A: 60
- Tensile Strength at Break: 3.79 MPa
- Tensile Strength, Yield: 0.931 MPa @Strain 300 %
$ 1733/MT
- Density: 1.08 g/cc
- Melt Flow: 6.5 g/10 min
- Tensile Strength, Ultimate: 2.30 MPa
- Elongation at Break: 50 %
- Flexural Strength: 4.50 MPa
$ 1455/MT
- Density: 1.15 g/cc
- Linear Mold Shrinkage: 0.0081 cm/cm
- Melt Flow: 5.25 g/10 min
- Tensile Strength, Ultimate: 16.8 MPa
- Elongation at Break: 140 %
$ 2330/MT
- Density: 1.74 g/cc
- Melt Flow: 10 g/10 min @Load 5.00 kg, Temperature 190 °C
$ 1751/MT
- Density: 1.11 g/cc
- Linear Mold Shrinkage: 0.0030 cm/cm
- Melt Flow: 7.0 g/10 min
- Hardness, Shore D: 83
- Tensile Strength, Yield: 40.5 MPa
$ 1531/MT
- Specific Gravity: 0.920 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 39
- Tensile Strength, Ultimate: 12.4 MPa
$ 2171/MT
- Melt Flow: 12 g/10 min @Load 2.16 kg
$ 1878/MT
- Specific Gravity: 1.08 g/cc
- Melt Flow: 2.68 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 50.3 MPa
- Elongation at Break: 16 %
- Flexural Strength: 68.9 MPa
$ 1583/MT
- Density: 1.079 g/cc
- Melt Flow: 6.0 g/10 min
- Hardness, Shore A: 80
- Tensile Strength, Ultimate: 6.70 MPa
- Elongation at Break: 730 %
- Tear Strength: 41.2 kN/m
$ 1556/MT
- Density: 1.21 g/cc
- Melt Flow: 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 35.2 MPa
- Elongation at Break: 30 %
- Flexural Modulus: 2.00 GPa
$ 1561/MT
- Specific Gravity: 0.950 g/cc @Temperature 25.0 °C
- Shelf Life: 48.0 Month
- Color: Off-White
- Physical Form: Thermoplastic Pellet
- Siloxane Content (%): 50
$ 1962/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0090 cm/cm
- Melt Flow: 10 g/10 min
- Tensile Strength, Yield: 30.3 MPa
- Elongation at Break: 30 %
$ 1563/MT
- Specific Gravity: 0.940 g/cc
- Linear Mold Shrinkage: 0.020 cm/cm
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 57
- Tensile Strength, Yield: 4.32 MPa
$ 1567/MT
- Specific Gravity: 1.22 g/cc
- Linear Mold Shrinkage: 0.0090 cm/cm
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 42.7 MPa
- Elongation at Break: 40 %
$ 1608/MT
- Specific Gravity: 0.952 g/cc
- Linear Mold Shrinkage: 0.013 cm/cm
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 60
- Tensile Strength, Yield: 20.7 MPa
$ 1662/MT
- Specific Gravity: 1.12 g/cc
- Hardness, Shore A: 57
- Tensile Strength, Yield: 11.7 MPa
- Elongation at Break: 750 %
- Tear Strength: 26.3 kN/m
$ 1968/MT
- Density: 1.22 g/cc
- Linear Mold Shrinkage: 0.0020 cm/cm
- Melt Flow: 8.5 g/10 min
- Hardness, Shore D: 85
- Tensile Strength, Ultimate: 70.3 MPa
$ 1634/MT
- Specific Gravity: 0.902 g/cc
- Melt Flow: 26 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 46
- Tensile Strength, Yield: 3.79 MPa
- Elongation at Break: 760 %
$ 1857/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Melt Flow: 4.0 g/10 min
- Tensile Strength, Yield: 44.8 MPa
- Elongation at Break: 4.0 %
$ 2086/MT
- Melt Flow: 44 g/10 min @Load 2.16 kg
$ 1707/MT
- Density: 0.880 g/cc
- Melt Flow: 1.0 g/10 min
- Hardness, Shore D: 65
- Tensile Strength, Ultimate: 29.0 MPa
- Elongation at Yield: 30 %
$ 1859/MT
- Hardness, Shore A: 70
- Hardness, Shore A: 72
- Hardness, Shore A: 73
- Hardness, Shore A: 75
- Tensile Strength, Ultimate: 7.58 MPa
$ 1764/MT
- Density: 1.046 g/cc
- Linear Mold Shrinkage: 0.0132 cm/cm
- Melt Flow: 0.60 g/10 min
- Hardness, Shore A: 83
- Tensile Strength, Ultimate: 11.8 MPa
$ 1921/MT
- Specific Gravity: 1.15 g/cc
- Hardness, Shore A: 82
- Tensile Strength at Break: 16.0 MPa
- Elongation at Break: 600 %
- Tear Strength: 45.6 kN/m
$ 1502/MT
- Hardness, Shore A: 56
- Hardness, Shore A: 58
- Hardness, Shore A: 58
- Hardness, Shore A: 60
- Tensile Strength, Ultimate: 7.58 MPa
$ 1521/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage: 0.014 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 62
$ 1571/MT
- Specific Gravity: 0.982 g/cc
- Melt Flow: 39.1 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 62
- Tensile Strength, Yield: 12.1 MPa
- Elongation at Break: 890 %
$ 2116/MT
- Specific Gravity: 0.940 g/cc @Temperature 25.0 °C
- Shelf Life: 48.0 Month
- Color: Off-White
- Physical Form: Particles
- Siloxane Content (%): 50
$ 1850/MT
- Specific Gravity: 0.940 g/cc @Temperature 25.0 °C
- Shelf Life: 48.0 Month
- Color: Off-White
- Physical Form: Particles
- Siloxane Content (%): 50
$ 1491/MT
- Density: 1.32 g/cc
- Linear Mold Shrinkage: 0.011 - 0.014 cm/cm
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 13.8 MPa
- Elongation at Break: 170 %
$ 1465/MT
- Density: 0.9164 g/cc
- Linear Mold Shrinkage: 0.016 cm/cm
- Melt Flow: 13 g/10 min
- Hardness, Shore A: 48
- Tensile Strength, Ultimate: 4.00 MPa
$ 1454/MT
- Density: 1.13 g/cc
- Hardness, Shore A: 30
- Hardness, Shore A: 31
- Hardness, Shore A: 32
- Hardness, Shore A: 33
$ 1465/MT
- Density: 0.940 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 8.8 g/10 min
- Hardness, Shore A: 93
- Tensile Strength, Ultimate: 9.40 MPa
$ 1543/MT
- Specific Gravity: 0.950 g/cc @Temperature 25.0 °C
- Volatiles: 0.00 %
- Melting Point: 160 °C
- Shelf Life: 48.0 Month
- Color: Off-White
$ 2082/MT
- Specific Gravity: 0.950 g/cc @Temperature 25.0 °C
- Volatiles: 0.00 %
- Melting Point: 160 °C
- Shelf Life: 48.0 Month
- Color: Off-White
$ 1602/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage: 0.010 - 0.030 cm/cm
- Melt Flow: 27 g/10 min @Load 10.0 kg, Temperature 190 °C
- Hardness, Shore A: 73
- Tensile Strength: 14.5 MPa
$ 2060/MT
- Density: 0.900 g/cc
- Melt Flow: 25 g/10 min
- Hardness, Shore A: 46
- Tensile Strength, Ultimate: 3.00 MPa
- Elongation at Break: >= 700 %
- Tear Strength: 17.5 kN/m
$ 1489/MT
- Specific Gravity: 1.16 g/cc
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 69
- Tensile Strength, Yield: 2.07 MPa
- Tensile Strength, Yield: 7.58 MPa
$ 1577/MT
- Density: 1.20 g/cc
- Melt Flow: 16.1 g/10 min
- Hardness, Shore A: 59
- Tensile Strength, Ultimate: >= 3.62 MPa
- Elongation at Break: >= 500 %
- Tear Strength: >= 19.26 kN/m
$ 2410/MT
- Density: 1.15 g/cc
- Hardness, Shore A: 49
- Hardness, Shore A: 56
- Hardness, Shore A: 56
- Hardness, Shore A: 57
$ 2267/MT
- Specific Gravity: 1.07 g/cc
- Water Absorption: 0.060 %
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 33
$ 1474/MT
- Density: 1.02 g/cc
- Linear Mold Shrinkage: 0.011 - 0.014 cm/cm
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 13.8 MPa
- Elongation at Break: 50 %
$ 1570/MT
- Density: 1.25 g/cc
- Melt Flow: 1.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 22.8 MPa
- Elongation at Break: 180 %
- Flexural Modulus: 1.83 GPa
$ 1699/MT
- Density: 1.17 - 1.23 g/cc
- Linear Mold Shrinkage: 0.013 cm/cm
- Melt Flow: 6.0 - 12 g/10 min
- Hardness, Shore A: 60
- Tensile Strength, Ultimate: >= 3.62 MPa
$ 2426/MT
- Density: 1.23 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Melt Flow: 5.0 g/10 min
- Tensile Strength, Ultimate: 38.6 MPa
- Elongation at Break: 40 %
$ 1938/MT
- Specific Gravity: 1.12 g/cc
$ 1673/MT
- Density: 1.17 g/cc
- Linear Mold Shrinkage: 0.014 cm/cm
- Melt Flow: 10 - 14 g/10 min
- Hardness, Shore A: 62
- Tensile Strength, Ultimate: >= 4.00 MPa
$ 2532/MT
- Density: 1.33 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Melt Flow: 12 g/10 min
- Tensile Strength, Ultimate: 13.5 MPa
- Elongation at Break: 82 %
$ 1991/MT
- Density: 0.990 g/cc
- Melt Flow: 11 g/10 min
- Tensile Strength, Ultimate: 26.2 MPa
- Elongation at Break: 150 %
- Flexural Strength: 36.9 MPa
$ 1472/MT
- Specific Gravity: 1.15 g/cc
- Hardness, Shore A: 55
- Tensile Strength at Break: 5.00 MPa
- Elongation at Break: 450 %
- Tear Strength: 24.5 kN/m
$ 2232/MT
- Specific Gravity: 1.06 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 46
- Tensile Strength, Yield: 5.52 MPa
- Elongation at Break: 600 %
$ 2194/MT
- Density: 1.07 g/cc
- Linear Mold Shrinkage: 0.013 cm/cm
- Melt Flow: 1.0 g/10 min
- Hardness, Shore D: 47
- Tensile Strength, Ultimate: >= 14.5 MPa
$ 1552/MT
- Specific Gravity: 1.08 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 80
- Tensile Strength, Yield: 8.96 MPa
- Tensile Strength, Yield: 4.65 MPa @Strain 100 %
$ 1565/MT
- Density: 1.87 g/cc
- Linear Mold Shrinkage: 0.013 cm/cm
- Melt Flow: 8.0 - 15 g/10 min
- Hardness, Shore D: 38
- Tensile Strength, Ultimate: >= 4.50 MPa
$ 1444/MT
- Density: 1.01 g/cc
- Linear Mold Shrinkage: 0.013 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Melt Flow: 2.0 g/10 min @Load 5.00 kg, Temperature 230 °C
- Hardness, Shore A: 80
$ 1510/MT
- Specific Gravity: 1.15 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 90
- Tensile Strength, Yield: 12.4 MPa
$ 1584/MT
- Density: 1.08 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 14 g/10 min
- Hardness, Shore D: 70
- Tensile Strength, Ultimate: 26.6 MPa
$ 1503/MT
- Specific Gravity: 0.960 g/cc
- Water Absorption: 0.65 %
- Linear Mold Shrinkage: 0.0050 cm/cm
- Melt Flow: 0.95 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 21.0 MPa
$ 1518/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 43
- Tensile Strength, Yield: 6.55 MPa
- Elongation at Break: 780 %
- Tear Strength: 22.8 kN/m
$ 2438/MT
- Density: 1.04 g/cc
- Melt Flow: 5.0 g/10 min
- Hardness, Rockwell R: 105
- Tensile Strength, Ultimate: 37.2 MPa
- Elongation at Break: 25 %
$ 1672/MT
- Specific Gravity: 1.13 g/cc
- Linear Mold Shrinkage: 0.020 - 0.040 cm/cm
- Melt Flow: 55 g/10 min @Load 10.0 kg, Temperature 190 °C
- Hardness, Shore A: 48
- Tensile Strength: 4.40 MPa
$ 2407/MT
- Density: 1.17 g/cc
- Melt Flow: 8.0 g/10 min
- Hardness, Shore D: 64
- Tensile Strength, Ultimate: >= 15.2 MPa
- Elongation at Break: >= 100 %
$ 2476/MT
- Specific Gravity: 0.912 g/cc
- Linear Mold Shrinkage: 0.014 cm/cm
- Melt Flow: 3.8 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 47
- Tensile Strength, Yield: 18.8 MPa
$ 1664/MT
- Specific Gravity: 0.910 g/cc
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 35
- Tensile Strength, Yield: 0.862 MPa
- Tensile Strength, Yield: 6.89 MPa
$ 1715/MT
- Specific Gravity: 0.940 g/cc @Temperature 25.0 °C
- Shelf Life: 48.0 Month
- Color: Off-White
- Physical Form: Solid
- Siloxane Content (%): 50
$ 1496/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.011 cm/cm
- Melt Flow: 3.0 g/10 min
- Tensile Strength, Yield: 31.0 MPa
- Elongation at Break: 100 %
$ 1922/MT
- Density: 1.07 g/cc
- Linear Mold Shrinkage: 0.0108 cm/cm
- Melt Flow: 1.8 g/10 min
- Hardness, Shore A: 88
- Tensile Strength, Ultimate: 9.00 MPa
$ 1646/MT
- Specific Gravity: 1.05 g/cc
- Linear Mold Shrinkage: 0.018 cm/cm
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 25
- Tensile Strength, Yield: 0.689 MPa
$ 1515/MT
- Specific Gravity: 0.970 g/cc @Temperature 25.0 °C
- Shelf Life: 48.0 Month
- Color: Off-White
- Physical Form: Thermoplastic Pellet
- Siloxane Content (%): 50
$ 1554/MT
- Specific Gravity: 0.970 g/cc @Temperature 25.0 °C
- Shelf Life: 48.0 Month
- Color: Off-White
- Physical Form: Thermoplastic Pellet
- Siloxane Content (%): 50
$ 2100/MT
- Specific Gravity: 0.970 g/cc @Temperature 25.0 °C
- Shelf Life: 48.0 Month
- Color: Off-White
- Physical Form: Thermoplastic Pellet
- Siloxane Content (%): 50
$ 1687/MT
- Hardness, Shore A: 55
- Hardness, Shore A: 56
- Hardness, Shore A: 57
- Tensile Strength, Ultimate: 9.729 MPa
- Tensile Strength, Ultimate: 10.17 MPa
$ 1709/MT
- Density: 1.08 g/cc
- Linear Mold Shrinkage: 0.011 cm/cm
- Melt Flow: 14 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 26.5 MPa
- Elongation at Break: 150 %
$ 1651/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Melt Flow: 3.0 g/10 min
- Hardness, Shore D: 103
- Tensile Strength, Ultimate: 33.1 MPa
$ 1834/MT
- Density: 1.23 g/cc
- Melt Flow: 11 g/10 min
- Tensile Strength, Ultimate: 15.2 MPa
- Elongation at Break: >= 500 %
- Flexural Strength: 20.0 MPa
$ 1983/MT
- Density: 1.165 g/cc
- Hardness, Shore A: 43
- Tensile Strength, Ultimate: >= 4.00 MPa
- Elongation at Break: >= 698 %
- Tear Strength: 17.4 kN/m
$ 1802/MT
- Density: 1.16 g/cc
- Melt Flow: 39 g/10 min
- Hardness, Shore A: 79
- Tensile Strength, Ultimate: 5.40 MPa
- Elongation at Break: 565 %
$ 1516/MT
- Hardness, Shore A: 77
- Hardness, Shore A: 82
- Hardness, Shore A: 83
- Hardness, Shore A: 85
- Tensile Strength, Ultimate: 6.61 MPa
$ 1569/MT
- Density: 0.9987 g/cc
- Melt Flow: 16 g/10 min
- Hardness, Shore D: 54.5
- Tensile Strength, Ultimate: 11.4 MPa
- Elongation at Break: 710 %
$ 1783/MT
- Density: 0.900 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 2.5 g/10 min
- Hardness, Shore D: 35
- Tensile Strength, Ultimate: 13.1 MPa
$ 1510/MT
- Density: 1.10 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 14 g/10 min
- Tensile Strength, Yield: 26.2 MPa
- Elongation at Break: 130 %
$ 2591/MT
- Density: 1.49 g/cc
- Linear Mold Shrinkage: 0.0080 cm/cm
- Melt Flow: 1.1 g/10 min
- Hardness, Shore A: 86
- Tensile Strength, Ultimate: 3.70 MPa
$ 1580/MT
- Specific Gravity: 1.23 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 76
- Tensile Strength, Yield: 3.31 MPa
$ 1671/MT
- Density: 1.34 g/cc
- Linear Mold Shrinkage: 0.0090 cm/cm
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 15.2 MPa
- Elongation at Break: 10 %
$ 1476/MT
- Density: 0.8995 g/cc
- Linear Mold Shrinkage: 0.011 cm/cm
- Melt Flow: 0.95 g/10 min
- Hardness, Shore D: 58
- Tensile Strength, Ultimate: 26.3 MPa
Delivery Thermoplastic Multibase
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
lng ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.