$ 2452/MT
- Density: 1.00 g/cc
- Melt Flow: 14 g/10 min @Load 2.16 kg, Temperature 235 °C
- Hardness, Shore D: 58
- Tensile Strength, Yield: 9.00 MPa
- Elongation at Break: >= 300 %
$ 1497/MT
- Oxygen Transmission Rate: 1.00 - 2.00 cc/m²/day
- Film Tensile Strength at Yield, MD: 17.0 MPa
- Film Tensile Strength at Yield, TD: 18.0 MPa
- Film Elongation at Break, MD: 440 %
- Film Elongation at Break, TD: 480 %
$ 1616/MT
- Fiber Count: 1470 dtex
- Elongation at Break: 38 %
- Elongation at Break: 38 %
- Tenacity: 0.618 N/tex
- Tenacity: 0.644 N/tex
$ 1482/MT
- Density: 1.06 g/cc
- Melt Flow: 4.2 g/10 min @Load 1.00 kg, Temperature 190 °C
- Tensile Strength at Break: >= 27.0 MPa
- Tensile Strength, Yield: 9.00 MPa
- Elongation at Break: >= 300 %
$ 2076/MT
- Tensile Strength at Break: 45.7 MPa
- Tensile Strength, Yield: 34.8 MPa
- Elongation at Break: 92 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 1546/MT
- Tensile Strength at Break: 48.2 MPa
- Tensile Strength, Yield: 31.1 MPa
- Elongation at Break: 110 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 1550/MT
- Elongation at Break: 270 %
- Impact: NB @Temperature -40.0 °C
- Impact: NB @Temperature -40.0 °C
- Processing Temperature: 230 °C
- Feed Temperature: 40.0 °C
$ 1562/MT
- Elongation at Break: 40 %
- Elongation at Break: 63 %
- Tenacity: 0.256 N/tex
- Tenacity: 0.424 N/tex
- Tenacity: 0.635 N/tex
- Appearance: Little Misty
$ 2512/MT
- Density: 1.02 g/cc
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 235 °C
- Hardness, Shore D: 73
- Tensile Strength at Break: >= 56.0 MPa
- Tensile Strength, Yield: 45.0 MPa
$ 1699/MT
- Density: 1.02 g/cc
- Melt Flow: 18 g/10 min @Load 2.16 kg, Temperature 235 °C
- Hardness, Shore D: 73
- Tensile Strength at Break: >= 56.0 MPa
- Tensile Strength, Yield: 45.0 MPa
$ 1721/MT
- Density: 1.03 g/cc
- Melt Flow: 60 g/10 min @Load 1.00 kg, Temperature 190 °C
- Tensile Strength at Break: >= 27.0 MPa
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Break: >= 300 %
$ 2403/MT
- Fiber Count: 36300 dtex
- Elongation at Break: 39 %
- Elongation at Break: 55 %
- Tenacity: 0.335 N/tex
- Tenacity: 0.459 N/tex
$ 1796/MT
- Density: 1.00 g/cc
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 235 °C
- Hardness, Shore D: 66
- Tensile Strength at Break: >= 56.0 MPa
- Tensile Strength, Yield: 28.0 MPa
$ 1528/MT
- Fiber Count: 1510 dtex
- Elongation at Break: 30 %
- Elongation at Break: 30 %
- Tenacity: 0.450 N/tex
- Tenacity: 0.653 N/tex
- Tenacity: 2.38 N/tex
$ 2213/MT
- Density: 1.02 g/cc
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 235 °C
- Hardness, Shore D: 75
- Tensile Strength at Break: >= 54.0 MPa
- Tensile Strength, Yield: 43.0 MPa
$ 1839/MT
- Density: 0.920 g/cc
- Melt Flow: 0.90 g/10 min
- Hardness, Shore D: 49
- Tensile Strength at Break: 18.0 MPa
- Elongation at Break: 700 %
$ 1572/MT
- Density: 0.918 g/cc
- Environmental Stress Crack Resistance: 1000 hour
- Melt Flow: 4.0 g/10 min
- Hardness, Shore D: 52
- Tensile Strength, Yield: 36.0 MPa
$ 1955/MT
- Fiber Count: 38800 dtex
- Elongation at Break: 34 %
- Elongation at Break: 34 %
- Tenacity: 0.344 N/tex
- Tenacity: 0.618 N/tex
$ 1700/MT
- Density: 1.02 g/cc
- Melt Flow: 3.6 g/10 min @Load 2.16 kg, Temperature 235 °C
- Hardness, Shore D: 64
- Tensile Strength at Break: >= 41.0 MPa
- Tensile Strength, Yield: 26.0 MPa
$ 1904/MT
- Tensile Strength at Break: 46.4 MPa
- Tensile Strength, Yield: 32.0 MPa
- Elongation at Break: 98 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 1580/MT
- Fiber Count: 37100 dtex
- Elongation at Break: 39 %
- Elongation at Break: 54 %
- Tenacity: 0.265 N/tex
- Tenacity: 0.388 N/tex
$ 1742/MT
- Density: 1.02 g/cc
- Melt Flow: 18 g/10 min @Load 2.16 kg, Temperature 235 °C
- Hardness, Rockwell R: 110
- Tensile Strength at Break: >= 54.0 MPa
- Tensile Strength, Yield: 41.0 MPa
$ 1596/MT
- Oxygen Transmission Rate: 90.0 cc/m²/day
- Oxygen Transmission Rate: 90.0 cc/m²/day
- Oxygen Transmission Rate: 180 cc/m²/day
- Thickness: 25.0 microns
$ 1900/MT
- Fiber Count: 37000 dtex
- Elongation at Break: 33 %
- Elongation at Break: 35 %
- Tenacity: 0.380 N/tex
- Tenacity: 0.609 N/tex
$ 1610/MT
- Density: 0.922 g/cc
- Melt Flow: 2.0 g/10 min
- Hardness, Shore D: 54
- Tensile Strength at Break: 16.0 MPa
- Elongation at Break: 600 %
$ 2251/MT
- Particle Size: 0.80 µm
- Melt Flow: 2.8 g/10 min
- Tensile Strength at Break: 31.0 MPa
- Tensile Strength, Yield: 35.0 MPa
- Elongation at Break: 7.0 %
$ 2325/MT
- Relative Viscosity: 3.71 - 3.89 cP
- Relative Viscosity: 4.0 - 4.2 cP
- Melting Point: 195 - 205 °C
- Processing Temperature: 190 - 200 °C
- Processing Temperature: 200 - 210 °C
$ 1777/MT
- Density: 1.02 g/cc
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 235 °C
- Hardness, Shore D: 68
- Tensile Strength at Break: >= 56.0 MPa
- Tensile Strength, Yield: 32.0 MPa
$ 2004/MT
- Density: 0.923 g/cc
- Melt Flow: 0.80 g/10 min
- Hardness, Shore D: 55
- Tensile Strength at Break: 18.0 MPa
- Elongation at Break: 700 %
$ 1651/MT
- Fiber Count: 37100 dtex
- Elongation at Break: 35 %
- Elongation at Break: 40 %
- Tenacity: 0.300 N/tex
- Tenacity: 0.477 N/tex
$ 1628/MT
- Particle Size: 2.1 µm
- Melt Flow: 3.6 g/10 min
- Tensile Strength at Break: 29.0 MPa
- Tensile Strength, Yield: 30.0 MPa
- Elongation at Break: 22 %
$ 1652/MT
- Density: 0.913 g/cc
- Environmental Stress Crack Resistance: 20 hour
- Melt Flow: 30 g/10 min
- Hardness, Shore D: 50
- Tensile Strength, Yield: 30.0 MPa
$ 2413/MT
- Elongation at Break: 36 %
- Elongation at Break: 39 %
- Tenacity: 0.344 N/tex
- Tenacity: 0.485 N/tex
- Tenacity: 0.856 N/tex
- Appearance: Very Clear & Glossy
$ 2348/MT
- Fiber Count: 1530 dtex
- Elongation at Break: 23 %
- Elongation at Break: 24 %
- Tenacity: 0.680 N/tex
- Tenacity: 0.865 N/tex
$ 1801/MT
- Fiber Count: 1490 dtex
- Elongation at Break: 30 %
- Elongation at Break: 31 %
- Tenacity: 0.653 N/tex
- Tenacity: 0.724 N/tex
$ 1478/MT
- Particle Size: 2.2 µm
- Melt Flow: 3.5 g/10 min
- Tensile Strength at Break: 31.0 MPa
- Tensile Strength, Yield: 32.0 MPa
- Elongation at Break: 20 %
$ 1477/MT
- Particle Size: 1.0 µm
- Melt Flow: 2.7 g/10 min
- Tensile Strength at Break: 30.0 MPa
- Tensile Strength, Yield: 33.0 MPa
- Elongation at Break: 8.0 %
$ 1872/MT
- Particle Size: 1.8 µm
- Melt Flow: 3.5 g/10 min
- Tensile Strength at Break: 30.0 MPa
- Tensile Strength, Yield: 31.0 MPa
- Elongation at Break: 20 %
$ 1613/MT
- Tensile Strength at Break: 48.8 MPa
- Tensile Strength, Yield: 38.4 MPa
- Elongation at Break: 92.5 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 1721/MT
- Tensile Strength at Break: 46.1 MPa
- Tensile Strength, Yield: 36.5 MPa
- Elongation at Break: 91 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 1799/MT
- Density: 0.940 g/cc
- Vinyl Acetate Content: 15 %
- Melt Flow: 0.80 g/10 min
- Hardness, Shore A: 93
- Tensile Strength at Break: 25.0 MPa
$ 1643/MT
- Density: 0.926 g/cc
- Environmental Stress Crack Resistance: 1000 hour
- Melt Flow: 2.5 g/10 min
- Hardness, Shore D: 57
- Tensile Strength, Yield: 36.0 MPa
$ 1458/MT
- Fiber Count: 1500 dtex
- Elongation at Break: 28 %
- Elongation at Break: 28 %
- Tenacity: 0.441 N/tex
- Tenacity: 0.706 N/tex
- Tenacity: 2.56 N/tex
$ 2360/MT
- Tensile Strength at Break: 33.9 MPa
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Break: 110 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 1568/MT
- Tensile Strength at Break: 51.3 MPa
- Tensile Strength, Yield: 44.2 MPa
- Elongation at Break: 92 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 1623/MT
- Tensile Strength at Break: 46.8 MPa
- Tensile Strength, Yield: 35.7 MPa
- Elongation at Break: 94 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 1791/MT
- Tensile Strength at Break: 48.2 MPa
- Tensile Strength, Yield: 38.7 MPa
- Elongation at Break: 94 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 1447/MT
- Particle Size: 1.6 µm
- Melt Flow: 3.6 g/10 min
- Tensile Strength at Break: 30.0 MPa
- Tensile Strength, Yield: 31.0 MPa
- Elongation at Break: 20 %
$ 1526/MT
- Density: 1.03 g/cc
- Melt Flow: 7.7 g/10 min @Load 2.16 kg, Temperature 235 °C
- Hardness, Shore D: 67
- Tensile Strength at Break: >= 56.0 MPa
- Tensile Strength, Yield: 26.0 MPa
$ 1768/MT
- Tensile Strength at Break: 34.1 MPa
- Tensile Strength, Yield: 34.3 MPa
- Elongation at Break: 117 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 1811/MT
- Density: 1.02 g/cc
- Melt Flow: 3.7 g/10 min @Load 2.16 kg, Temperature 235 °C
- Hardness, Shore D: 73
- Tensile Strength at Break: >= 65.0 MPa
- Tensile Strength, Yield: 43.0 MPa
$ 1898/MT
- Tensile Strength at Break: 36.2 MPa
- Tensile Strength, Yield: 24.3 MPa
- Elongation at Break: 113 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 1478/MT
- Density: 1.02 g/cc
- Melt Flow: 3.1 g/10 min @Load 2.16 kg, Temperature 235 °C
- Hardness, Shore D: 72
- Tensile Strength at Break: >= 63.0 MPa
- Tensile Strength, Yield: 42.0 MPa
$ 1976/MT
- Density: 1.03 g/cc
- Melt Flow: 7.4 g/10 min @Load 2.16 kg, Temperature 235 °C
- Hardness, Shore D: 65
- Tensile Strength at Break: >= 58.0 MPa
- Tensile Strength, Yield: 25.0 MPa
$ 1479/MT
- Tensile Strength at Break: 47.6 MPa
- Tensile Strength, Yield: 43.3 MPa
- Elongation at Break: 78 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 1733/MT
- Fiber Count: 38600 dtex
- Elongation at Break: 41 %
- Elongation at Break: 56 %
- Tenacity: 0.318 N/tex
- Tenacity: 0.432 N/tex
$ 1986/MT
- Tensile Strength at Break: 37.6 MPa
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Break: 110 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 1487/MT
- Tensile Strength at Break: 45.2 MPa
- Tensile Strength, Yield: 34.7 MPa
- Elongation at Break: 88 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 1562/MT
- Density: 0.919 g/cc
- Melt Flow: 20 g/10 min
- Hardness, Shore D: 47
- Tensile Strength at Break: 9.50 MPa
- Elongation at Break: 350 %
$ 1512/MT
- Density: 1.00 g/cc
- Melt Flow: 8.2 g/10 min @Load 2.16 kg, Temperature 235 °C
- Hardness, Rockwell R: 71
- Tensile Strength at Break: >= 56.0 MPa
- Tensile Strength, Yield: 23.0 MPa
$ 1513/MT
- Tensile Strength at Break: 47.2 MPa
- Tensile Strength, Yield: 41.5 MPa
- Elongation at Break: 84 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 1557/MT
- Density: 1.03 g/cc
- Melt Flow: 60 g/10 min @Load 1.00 kg, Temperature 190 °C
- Hardness, Shore D: 73
- Tensile Strength at Break: >= 27.0 MPa
- Tensile Strength, Yield: 20.0 MPa
$ 1989/MT
- Elongation at Break: 41 %
- Elongation at Break: 75 %
- Tenacity: 0.265 N/tex
- Tenacity: 0.388 N/tex
- Tenacity: 0.635 N/tex
- Appearance: Very Clear & Glossy
$ 2317/MT
- Density: 0.922 g/cc
- Melt Flow: 0.80 g/10 min
- Hardness, Shore D: 54
- Tensile Strength at Break: 18.0 MPa
- Elongation at Break: 750 %
$ 1457/MT
- Particle Size: 1.23 µm
- Melt Flow: 2.7 g/10 min
- Tensile Strength at Break: 30.0 MPa
- Tensile Strength, Yield: 31.0 MPa
- Elongation at Break: 43 %
$ 1575/MT
- Relative Viscosity: 3.8 - 3.98 cP
- Relative Viscosity: 4.1 - 4.3 cP
- Film Elongation at Break, MD: 540 %
- Film Elongation at Break, TD: 560 %
- Secant Modulus, MD: 0.210 GPa
$ 2277/MT
- Tensile Strength at Break: 34.0 MPa
- Tensile Strength, Yield: 18.0 MPa
- Elongation at Break: 115 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 1602/MT
- Oxygen Transmission Rate: 52.0 cc/m²/day
- Oxygen Transmission Rate: 55.0 cc/m²/day
- Oxygen Transmission Rate: 198 cc/m²/day
- Thickness: 25.0 microns
$ 2092/MT
- Tensile Strength at Break: 44.8 MPa
- Tensile Strength, Yield: 30.3 MPa
- Elongation at Break: 99 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 1482/MT
- Density: 0.917 g/cc
- Melt Flow: 10 g/10 min
- Hardness, Shore D: 47
- Tensile Strength at Break: 12.0 MPa
- Elongation at Break: 450 %
$ 1747/MT
- Tensile Strength at Break: 44.0 MPa
- Tensile Strength, Yield: 34.7 MPa
- Elongation at Break: 84.3 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 1794/MT
- Density: 1.16 g/cc
- Melt Flow: 4.6 g/10 min @Load 2.16 kg, Temperature 235 °C
- Hardness, Rockwell R: 111
- Tensile Strength at Break: 127 MPa
- Elongation at Break: 6.0 %
$ 2324/MT
- Tensile Strength at Break: 48.5 MPa
- Tensile Strength, Yield: 36.7 MPa
- Elongation at Break: 88 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 1444/MT
- Density: 0.990 g/cc
- Melt Flow: 3.6 g/10 min @Load 2.16 kg, Temperature 235 °C
- Hardness, Shore D: 67
- Tensile Strength at Break: >= 40.0 MPa
- Tensile Strength, Yield: 20.0 MPa
$ 1637/MT
- Tensile Strength at Break: 48.2 MPa
- Tensile Strength, Yield: 44.5 MPa
- Elongation at Break: 86 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 2352/MT
- Tensile Strength at Break: 49.9 MPa
- Tensile Strength, Yield: 32.7 MPa
- Elongation at Break: 124 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 1747/MT
- Density: 1.02 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 235 °C
- Hardness, Rockwell R: 110
- Tensile Strength at Break: >= 54.0 MPa
- Tensile Strength, Yield: 42.0 MPa
$ 2454/MT
- Fiber Count: 1510 dtex
- Elongation at Break: 27 %
- Elongation at Break: 31 %
- Tenacity: 0.671 N/tex
- Tenacity: 0.777 N/tex
$ 1837/MT
- Oxygen Transmission Rate: 50.0 cc/m²/day
- Oxygen Transmission Rate: 54.0 cc/m²/day
- Oxygen Transmission Rate: 192 cc/m²/day
- Thickness: 25.0 microns
$ 1471/MT
- Fiber Count: 1510 dtex
- Elongation at Break: 32 %
- Elongation at Break: 32 %
- Tenacity: 0.424 N/tex
- Tenacity: 0.653 N/tex
- Tenacity: 1.85 N/tex
$ 2172/MT
- Density: 0.922 g/cc
- Melt Flow: 5.0 g/10 min
- Hardness, Shore D: 52
- Tensile Strength at Break: 14.0 MPa
- Elongation at Break: 550 %
$ 2356/MT
- Particle Size: 1.0 µm
- Melt Flow: 2.7 g/10 min
- Tensile Strength at Break: 29.0 MPa
- Tensile Strength, Yield: 33.0 MPa
- Elongation at Break: 8.0 %
$ 1951/MT
- Tensile Strength at Break: 33.6 MPa
- Tensile Strength, Yield: 33.8 MPa
- Elongation at Break: 94 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 2108/MT
- Relative Viscosity: 3.99 - 4.17 cP
- Relative Viscosity: 4.3 - 4.5 cP
- Film Elongation at Break, MD: 510 %
- Film Elongation at Break, TD: 560 %
- Secant Modulus, MD: 0.190 GPa
$ 1447/MT
- Tensile Strength at Break: 47.8 MPa
- Tensile Strength, Yield: 33.0 MPa
- Elongation at Break: 97.9 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 1744/MT
- Tensile Strength at Break: 34.8 MPa
- Tensile Strength, Yield: 19.5 MPa
- Elongation at Break: 111 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 2048/MT
- Density: 0.918 g/cc
- Melt Flow: 7.5 g/10 min
- Hardness, Shore D: 48
- Tensile Strength at Break: 13.0 MPa
- Elongation at Break: 500 %
$ 1821/MT
- Elongation at Break: 260 %
- Impact: NB @Temperature -40.0 °C
- Impact: NB @Temperature -40.0 °C
- Processing Temperature: 230 °C
- Feed Temperature: 40.0 °C
$ 1694/MT
- Elongation at Break: 260 %
- Impact: NB @Temperature -40.0 °C
- Impact: NB @Temperature -40.0 °C
- Processing Temperature: 230 °C
- Feed Temperature: 40.0 °C
$ 1756/MT
- Elongation at Break: 260 %
- Impact: NB @Temperature -40.0 °C
- Impact: NB @Temperature -40.0 °C
- Processing Temperature: 230 °C
- Feed Temperature: 40.0 °C
$ 1539/MT
- Tensile Strength at Break: 30.5 MPa
- Tensile Strength, Yield: 14.1 MPa
- Elongation at Break: 124 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 1727/MT
- Particle Size: 0.94 µm
- Melt Flow: 2.8 g/10 min
- Tensile Strength at Break: 30.0 MPa
- Tensile Strength, Yield: 34.0 MPa
- Elongation at Break: 9.0 %
$ 1487/MT
- Tensile Strength at Break: 50.4 MPa
- Tensile Strength, Yield: 37.0 MPa
- Elongation at Break: 96 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 2076/MT
- Density: 1.01 g/cc
- Melt Flow: 18 g/10 min @Load 2.16 kg, Temperature 235 °C
- Hardness, Shore D: 71
- Tensile Strength at Break: >= 45.0 MPa
- Tensile Strength, Yield: 38.0 MPa
$ 2219/MT
- Density: 1.03 g/cc
- Melt Flow: 4.3 g/10 min @Load 2.16 kg, Temperature 235 °C
- Hardness, Shore D: 69
- Tensile Strength at Break: >= 46.0 MPa
- Tensile Strength, Yield: 28.0 MPa
$ 2158/MT
- Relative Viscosity: 3.62 - 3.8 cP
- Relative Viscosity: 3.88 - 4.08 cP
- Thickness: 40.0 microns
- Film Elongation at Break, MD: 460 %
- Secant Modulus, TD: 0.470 GPa
$ 2162/MT
- Tensile Strength at Break: 46.4 MPa
- Tensile Strength, Yield: 32.1 MPa
- Elongation at Break: 97 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 1784/MT
- Density: 1.02 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 235 °C
- Hardness, Rockwell R: 110
- Tensile Strength at Break: >= 54.0 MPa
- Tensile Strength, Yield: 42.0 MPa
$ 2584/MT
- Density: 1.00 g/cc
- Melt Flow: 14 g/10 min @Load 1.00 kg, Temperature 190 °C
- Hardness, Shore D: 56
- Tensile Strength at Break: >= 19.0 MPa
- Tensile Strength, Yield: 9.00 MPa
$ 1598/MT
- Tensile Strength at Break: 41.6 MPa
- Tensile Strength, Yield: 34.3 MPa
- Elongation at Break: 84 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 1527/MT
- Density: 0.927 g/cc
- Melt Flow: 0.40 g/10 min
- Hardness, Shore D: 57
- Tensile Strength at Break: 19.0 MPa
- Elongation at Break: 700 %
$ 1490/MT
- Oxygen Transmission Rate: 25.0 cc/m²/day
- Oxygen Transmission Rate: 26.0 cc/m²/day
- Oxygen Transmission Rate: 114 cc/m²/day
- Thickness: 25.0 microns
$ 1722/MT
- Relative Viscosity: 3.28 - 3.4 cP
- Relative Viscosity: 3.49 - 3.63 cP
- Thickness: 55.0 - 59.0 microns
- Film Elongation at Break, MD: 460 %
- Film Elongation at Break, TD: 480 %
$ 1733/MT
- Relative Viscosity: 3.31 - 3.43 cP
- Relative Viscosity: 3.53 - 3.67 cP
- Thickness: 40.0 microns
- Film Elongation at Break, MD: 440 %
- Secant Modulus, MD: 0.470 GPa
$ 1730/MT
- Density: 1.02 g/cc
- Melt Flow: 70 g/10 min @Load 2.16 kg, Temperature 235 °C
- Hardness, Shore D: 73
- Tensile Strength at Break: >= 54.0 MPa
- Tensile Strength, Yield: 42.0 MPa
$ 1554/MT
- Density: 1.02 g/cc
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 235 °C
- Hardness, Shore D: 73
- Tensile Strength at Break: >= 54.0 MPa
- Tensile Strength, Yield: 42.0 MPa
$ 1514/MT
- Fiber Count: 39300 dtex
- Elongation at Break: 38 %
- Elongation at Break: 45 %
- Tenacity: 0.344 N/tex
- Tenacity: 0.494 N/tex
$ 1512/MT
- Tensile Strength at Break: 49.3 MPa
- Tensile Strength, Yield: 44.9 MPa
- Elongation at Break: 84 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 1664/MT
- Fiber Count: 1500 dtex
- Elongation at Break: 37 %
- Elongation at Break: 40 %
- Tenacity: 0.653 N/tex
- Tenacity: 0.697 N/tex
$ 1699/MT
- Tensile Strength at Break: 50.3 MPa
- Tensile Strength, Yield: 44.5 MPa
- Elongation at Break: 90 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 2398/MT
- Fiber Count: 37100 dtex
- Elongation at Break: 39 %
- Elongation at Break: 40 %
- Tenacity: 0.371 N/tex
- Tenacity: 0.503 N/tex
$ 1600/MT
- Density: 1.00 g/cc
- Melt Flow: 8.6 g/10 min @Load 2.16 kg, Temperature 235 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 19.0 MPa
- Elongation at Break: >= 300 %
$ 1518/MT
- Elongation at Break: 34 %
- Elongation at Break: 38 %
- Tenacity: 0.388 N/tex
- Tenacity: 0.565 N/tex
- Tenacity: 0.883 N/tex
- Appearance: Very Clear & Glossy
$ 1543/MT
- Fiber Count: 1510 dtex
- Elongation at Break: 24 %
- Elongation at Break: 26 %
- Tenacity: 0.671 N/tex
- Tenacity: 0.794 N/tex
$ 1829/MT
- Tensile Strength at Break: 46.8 MPa
- Tensile Strength, Yield: 33.7 MPa
- Elongation at Break: 102 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 1994/MT
- Particle Size: 0.90 µm
- Melt Flow: 2.8 g/10 min
- Tensile Strength at Break: 30.0 MPa
- Tensile Strength, Yield: 34.0 MPa
- Elongation at Break: 7.0 %
$ 1502/MT
- Particle Size: 0.82 µm
- Melt Flow: 2.8 g/10 min
- Tensile Strength at Break: 32.0 MPa
- Tensile Strength, Yield: 35.0 MPa
- Elongation at Break: 6.0 %
$ 2163/MT
- Particle Size: 2.7 µm
- Melt Flow: 3.6 g/10 min
- Tensile Strength at Break: 30.0 MPa
- Tensile Strength, Yield: 29.0 MPa
- Elongation at Break: 25 %
$ 2062/MT
- Particle Size: 0.80 µm
- Melt Flow: 2.8 g/10 min
- Tensile Strength at Break: 32.0 MPa
- Tensile Strength, Yield: 35.0 MPa
- Elongation at Break: 6.0 %
$ 2199/MT
- Density: 0.933 g/cc
- Melt Flow: 1.0 g/10 min
- Hardness, Shore D: 60
- Tensile Strength at Break: 14.0 MPa
- Elongation at Break: 600 %
$ 1490/MT
- Density: 1.02 g/cc
- Melt Flow: 19 g/10 min @Load 1.00 kg, Temperature 190 °C
- Hardness, Shore D: 73
- Tensile Strength at Break: 60.0 MPa
- Tensile Strength, Yield: 37.0 MPa
$ 1794/MT
- Tensile Strength at Break: 47.6 MPa
- Tensile Strength, Yield: 33.9 MPa
- Elongation at Break: 102 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 2128/MT
- Fiber Count: 39200 dtex
- Elongation at Break: 40 %
- Elongation at Break: 43 %
- Tenacity: 0.371 N/tex
- Tenacity: 0.547 N/tex
$ 2309/MT
- Relative Viscosity: 2.57 - 2.69 cP
- Relative Viscosity: 2.73 - 2.87 cP
- Melting Point: 195 - 205 °C
- Processing Temperature: 190 - 200 °C
- Processing Temperature: 200 - 210 °C
$ 1977/MT
- Density: 0.916 g/cc
- Melt Flow: 35 g/10 min
- Hardness, Shore D: 44
- Tensile Strength at Break: 8.50 MPa
- Elongation at Break: 300 %
$ 1576/MT
- Fiber Count: 1480 dtex
- Elongation at Break: 28 %
- Elongation at Break: 39 %
- Tenacity: 0.441 N/tex
- Tenacity: 0.556 N/tex
- Tenacity: 1.94 N/tex
$ 1453/MT
- Density: 0.922 g/cc
- Melt Flow: 5.0 g/10 min
- Hardness, Shore D: 52
- Tensile Strength at Break: 14.0 MPa
- Elongation at Break: 550 %
$ 1852/MT
- Tensile Strength at Break: 50.5 MPa
- Tensile Strength, Yield: 41.9 MPa
- Elongation at Break: 80 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 1581/MT
- Particle Size: 0.90 µm
- Melt Flow: 2.8 g/10 min
- Tensile Strength at Break: 30.0 MPa
- Tensile Strength, Yield: 34.0 MPa
- Elongation at Break: 7.0 %
$ 1927/MT
- Density: 0.923 g/cc
- Environmental Stress Crack Resistance: 1000 hour
- Melt Flow: 4.0 g/10 min
- Hardness, Shore D: 56
- Tensile Strength, Yield: 36.0 MPa
$ 2019/MT
- Density: 0.913 g/cc
- Environmental Stress Crack Resistance: 1000 hour
- Melt Flow: 4.0 g/10 min
- Hardness, Shore D: 51
- Tensile Strength, Yield: 39.0 MPa
$ 1461/MT
- Density: 0.913 g/cc
- Environmental Stress Crack Resistance: 1000 hour
- Melt Flow: 2.0 g/10 min
- Hardness, Shore D: 51
- Tensile Strength, Yield: 40.0 MPa
$ 2211/MT
- Density: 0.904 g/cc
- Environmental Stress Crack Resistance: 1000 hour
- Melt Flow: 4.0 g/10 min
- Hardness, Shore D: 44
- Tensile Strength, Yield: 42.0 MPa
$ 1941/MT
- Density: 0.922 g/cc
- Melt Flow: 2.0 g/10 min
- Hardness, Shore D: 54
- Tensile Strength at Break: 16.0 MPa
- Elongation at Break: 600 %
$ 2340/MT
- Density: 1.00 g/cc
- Melt Flow: 11 g/10 min @Load 2.16 kg, Temperature 235 °C
- Hardness, Shore D: 50
- Tensile Strength at Break: >= 30.0 MPa
- Tensile Strength, Yield: 16.0 MPa
$ 2435/MT
- Density: 1.16 g/cc
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 235 °C
- Hardness, Rockwell R: 113
- Tensile Strength at Break: 100 MPa
- Elongation at Break: 6.0 %
$ 2527/MT
- Tensile Strength at Break: 37.2 MPa
- Tensile Strength, Yield: 19.3 MPa
- Elongation at Break: 112 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 2297/MT
- Elongation at Break: 280 %
- Impact: NB @Temperature -40.0 °C
- Impact: NB @Temperature -40.0 °C
- Processing Temperature: 230 °C
- Feed Temperature: 40.0 °C
$ 1545/MT
- Tensile Strength at Break: 34.0 MPa
- Tensile Strength, Yield: 15.5 MPa
- Elongation at Break: 132 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 2118/MT
- Fiber Count: 1500 dtex
- Elongation at Break: 35 %
- Elongation at Break: 35 %
- Tenacity: 0.424 N/tex
- Tenacity: 0.583 N/tex
- Tenacity: 2.12 N/tex
$ 2320/MT
- Density: 1.02 g/cc
- Melt Flow: 1.3 g/10 min @Load 2.16 kg, Temperature 235 °C
- Hardness, Rockwell R: 112
- Tensile Strength at Break: >= 56.0 MPa
- Tensile Strength, Yield: 46.0 MPa
$ 1485/MT
- Tensile Strength at Break: 44.8 MPa
- Tensile Strength, Yield: 29.3 MPa
- Elongation at Break: 102 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 2010/MT
- Tensile Strength at Break: 40.9 MPa
- Tensile Strength, Yield: 26.7 MPa
- Elongation at Break: 94 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 1940/MT
- Tensile Strength at Break: 51.6 MPa
- Tensile Strength, Yield: 42.9 MPa
- Elongation at Break: 93 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 1534/MT
- Tensile Strength at Break: 45.5 MPa
- Tensile Strength, Yield: 34.2 MPa
- Elongation at Break: 98 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 2065/MT
- Density: 0.922 g/cc
- Melt Flow: 0.50 g/10 min
- Hardness, Shore D: 55
- Tensile Strength at Break: 20.0 MPa
- Elongation at Break: 750 %
$ 1683/MT
- Tensile Strength at Break: 50.9 MPa
- Tensile Strength, Yield: 34.2 MPa
- Elongation at Break: 115 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 1456/MT
- Density: 0.928 g/cc
- Melt Flow: 1.0 g/10 min
- Hardness, Shore D: 58
- Tensile Strength at Break: 18.0 MPa
- Elongation at Break: 600 %
$ 1809/MT
- Fiber Count: 38100 dtex
- Elongation at Break: 39 %
- Elongation at Break: 45 %
- Tenacity: 0.318 N/tex
- Tenacity: 0.450 N/tex
$ 1825/MT
- Fiber Count: 1490 dtex
- Elongation at Break: 22 %
- Elongation at Break: 32 %
- Tenacity: 0.468 N/tex
- Tenacity: 0.609 N/tex
- Tenacity: 2.12 N/tex
$ 1536/MT
- Tensile Strength at Break: 42.0 MPa
- Tensile Strength, Yield: 27.5 MPa
- Elongation at Break: 97 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 1767/MT
- Particle Size: 2.5 µm
- Melt Flow: 3.5 g/10 min
- Tensile Strength at Break: 29.0 MPa
- Tensile Strength, Yield: 29.0 MPa
- Elongation at Break: 23 %
$ 1677/MT
- Density: 1.07 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 235 °C
- Hardness, Shore D: 63
- Tensile Strength at Break: >= 17.0 MPa
- Tensile Strength, Yield: 18.0 MPa
$ 2520/MT
- Tensile Strength at Break: 43.8 MPa
- Tensile Strength, Yield: 42.0 MPa
- Elongation at Break: 80 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 1710/MT
- Fiber Count: 1500 dtex
- Elongation at Break: 36 %
- Elongation at Break: 36 %
- Tenacity: 0.406 N/tex
- Tenacity: 0.583 N/tex
- Tenacity: 1.68 N/tex
$ 1614/MT
- Fiber Count: 1500 dtex
- Elongation at Break: 36 %
- Elongation at Break: 36 %
- Tenacity: 0.406 N/tex
- Tenacity: 0.583 N/tex
- Tenacity: 1.68 N/tex
$ 1475/MT
- Fiber Count: 37400 dtex
- Elongation at Break: 35 %
- Elongation at Break: 38 %
- Tenacity: 0.353 N/tex
- Tenacity: 0.574 N/tex
$ 2234/MT
- Fiber Count: 1480 dtex
- Elongation at Break: 48 %
- Elongation at Break: 49 %
- Tenacity: 0.565 N/tex
- Tenacity: 0.600 N/tex
$ 1756/MT
- Oxygen Transmission Rate: 27.0 cc/m²/day
- Oxygen Transmission Rate: 28.0 cc/m²/day
- Oxygen Transmission Rate: 117 cc/m²/day
- Thickness: 25.0 microns
$ 1598/MT
- Density: 0.940 g/cc
- Vinyl Acetate Content: 15 %
- Melt Flow: 2.0 g/10 min
- Hardness, Shore A: 92
- Tensile Strength at Break: 21.0 MPa
$ 1703/MT
- Relative Viscosity: 3.84 - 4.02 cP
- Relative Viscosity: 4.2 - 4.4 cP
- Film Elongation at Break, MD: 540 %
- Film Elongation at Break, TD: 550 %
- Secant Modulus, MD: 0.190 GPa
$ 1976/MT
- Tensile Strength at Break: 46.9 MPa
- Tensile Strength, Yield: 35.4 MPa
- Elongation at Break: 97 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 1489/MT
- Density: 0.920 g/cc
- Vinyl Acetate Content: 6.0 %
- Melt Flow: 0.40 g/10 min
- Hardness, Shore A: 96
- Tensile Strength at Break: 22.0 MPa
$ 1796/MT
- Particle Size: 0.90 µm
- Melt Flow: 2.8 g/10 min
- Tensile Strength at Break: 33.0 MPa
- Tensile Strength, Yield: 36.0 MPa
- Elongation at Break: 6.0 %
$ 1761/MT
- Density: 0.922 g/cc
- Melt Flow: 0.80 g/10 min
- Hardness, Shore D: 54
- Tensile Strength at Break: 18.0 MPa
- Elongation at Break: 750 %
$ 1523/MT
- Fiber Count: 40600 dtex
- Elongation at Break: 37 %
- Elongation at Break: 38 %
- Tenacity: 0.388 N/tex
- Tenacity: 0.591 N/tex
$ 2217/MT
- Fiber Count: 36400 dtex
- Elongation at Break: 35 %
- Elongation at Break: 44 %
- Tenacity: 0.265 N/tex
- Tenacity: 0.397 N/tex
$ 1731/MT
- Density: 1.02 g/cc
- Melt Flow: 70 g/10 min @Load 2.16 kg, Temperature 235 °C
- Hardness, Shore D: 73
- Tensile Strength at Break: >= 54.0 MPa
- Tensile Strength, Yield: 42.0 MPa
$ 1959/MT
- Tensile Strength at Break: 48.9 MPa
- Tensile Strength, Yield: 32.6 MPa
- Elongation at Break: 102 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 2100/MT
- Density: 0.921 g/cc
- Melt Flow: 3.5 g/10 min
- Hardness, Shore D: 50
- Tensile Strength at Break: 15.0 MPa
- Elongation at Break: 550 %
$ 1711/MT
- Density: 0.920 g/cc
- Vinyl Acetate Content: 6.0 %
- Melt Flow: 2.0 g/10 min
- Hardness, Shore A: 96
- Tensile Strength at Break: 19.0 MPa
$ 1627/MT
- Density: 0.919 g/cc
- Melt Flow: 50 g/10 min
- Hardness, Shore D: 45
- Tensile Strength at Break: 8.00 MPa
- Elongation at Break: 250 %
$ 2056/MT
- Relative Viscosity: 3.8 cP
- Relative Viscosity: 4.1 cP
- Film Elongation at Break, MD: 540 %
- Film Elongation at Break, TD: 550 %
- Secant Modulus, MD: 0.210 GPa
$ 1888/MT
- Tensile Strength at Break: 48.4 MPa
- Tensile Strength, Yield: 43.4 MPa
- Elongation at Break: 84 %
- Processing Temperature: 230 °C
- Zone 1: 190 °C
$ 2208/MT
- Density: 1.03 g/cc
- Melt Flow: 14 g/10 min @Load 2.16 kg, Temperature 235 °C
- Hardness, Shore D: 54
- Tensile Strength at Break: >= 30.0 MPa
- Tensile Strength, Yield: 13.0 MPa
$ 1915/MT
- Density: 0.920 g/cc
- Melt Flow: 1.2 g/10 min
- Hardness, Shore D: 54
- Tensile Strength at Break: 18.0 MPa
- Elongation at Break: 750 %
$ 1478/MT
- Elongation at Break: 250 %
- Impact: NB @Temperature -40.0 °C
- Impact: NB @Temperature -40.0 °C
- Processing Temperature: 230 °C
- Feed Temperature: 40.0 °C
$ 2031/MT
- Elongation at Break: 250 %
- Impact: NB @Temperature -40.0 °C
- Impact: NB @Temperature -40.0 °C
- Processing Temperature: 230 °C
- Feed Temperature: 40.0 °C
$ 1502/MT
- Fiber Count: 1490 dtex
- Elongation at Break: 20 %
- Elongation at Break: 31 %
- Tenacity: 0.485 N/tex
- Tenacity: 0.644 N/tex
- Tenacity: 2.21 N/tex
$ 1620/MT
- Elongation at Break: 39 %
- Elongation at Break: 50 %
- Tenacity: 0.282 N/tex
- Tenacity: 0.415 N/tex
- Tenacity: 0.786 N/tex
- Appearance: Very Clear & Glossy
Delivery Thermoplastic UBE
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):| Country | 20’ Container | 40’ Container | 5,000 MT |
|---|---|---|---|
| 🇦🇺 Australia | $3345 | $4181 | $401400 |
| 🇦🇹 Austria | $2825 | $3531 | $339000 |
| 🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
| 🇦🇱 Albania | $2500 | $3125 | $300000 |
| 🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
| 🇦🇴 Angola | $2762.5 | $3453 | $331500 |
| 🇦🇷 Argentina | $3230 | $4038 | $387600 |
| 🇦🇲 Armenia | $2625 | $3281 | $315000 |
| 🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
| 🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
| 🇧🇭 Bahrain | $3095 | $3869 | $371400 |
| 🇧🇾 Belarus | $2825 | $3531 | $339000 |
| 🇧🇿 Belize | $3155 | $3944 | $378600 |
| 🇧🇪 Belgium | $2575 | $3219 | $309000 |
| 🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
| 🇧🇴 Bolivia | $3230 | $4038 | $387600 |
| 🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
| 🇧🇷 Brazil | $3120 | $3900 | $374400 |
| 🇭🇺 Hungary | $2575 | $3219 | $309000 |
| 🇻🇪 Venezuela | $3230 | $4038 | $387600 |
| 🇻🇳 Vietnam | $2625 | $3281 | $315000 |
| 🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
| 🇬🇹 Guatemala | $3230 | $4038 | $387600 |
| 🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
| 🇩🇪 Germany | $2475 | $3094 | $297000 |
| 🇭🇳 Honduras | $3230 | $4038 | $387600 |
| 🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
| 🇬🇷 Greece | $2575 | $3219 | $309000 |
| 🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
| 🇩🇰 Denmark | $2400 | $3000 | $288000 |
| 🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
| 🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
| 🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
| 🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
| 🇮🇱 Israel | $2625 | $3281 | $315000 |
| 🇮🇳 India | $3712.5 | $4641 | $445500 |
| 🇮🇩 Indonesia | $3095 | $3869 | $371400 |
| 🇯🇴 Jordan | $2625 | $3281 | $315000 |
| 🇮🇶 Iraq | $2625 | $3281 | $315000 |
| 🇮🇷 Iran | $3095 | $3869 | $371400 |
| 🇮🇪 Ireland | $2500 | $3125 | $300000 |
| 🇮🇸 Iceland | $2575 | $3219 | $309000 |
| 🇪🇸 Spain | $2500 | $3125 | $300000 |
| 🇮🇹 Italy | $2400 | $3000 | $288000 |
| 🇾🇪 Yemen | $2625 | $3281 | $315000 |
| 🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
| 🇰🇭 Cambodia | $3095 | $3869 | $371400 |
| 🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
| 🇨🇦 Canada | $3230 | $4038 | $387600 |
| 🇶🇦 Qatar | $2625 | $3281 | $315000 |
| 🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
| 🇨🇾 Cyprus | $2625 | $3281 | $315000 |
| 🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
| 🇨🇳 China | $3712.5 | $4641 | $445500 |
| 🇨🇴 Colombia | $3230 | $4038 | $387600 |
| 🇰🇷 Korea South | $2625 | $3281 | $315000 |
| 🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
| 🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
| 🇨🇺 Cuba | $3230 | $4038 | $387600 |
| 🇰🇼 Kuwait | $2625 | $3281 | $315000 |
| 🇱🇻 Latvia | $2575 | $3219 | $309000 |
| 🇱🇧 Lebanon | $2625 | $3281 | $315000 |
| 🇱🇾 Libya | $2762.5 | $3453 | $331500 |
| 🇱🇹 Lithuania | $2500 | $3125 | $300000 |
| 🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
| 🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
| 🇲🇾 Malaysia | $2625 | $3281 | $315000 |
| 🇲🇹 Malta | $2500 | $3125 | $300000 |
| 🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
| 🇲🇽 Mexico | $3155 | $3944 | $378600 |
| 🇲🇩 Moldova | $2400 | $3000 | $288000 |
| 🇲🇨 Monaco | $2475 | $3094 | $297000 |
| 🇲🇳 Mongolia | $2625 | $3281 | $315000 |
| 🇲🇲 Myanmar | $2625 | $3281 | $315000 |
| 🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
| 🇳🇵 Nepal | $2625 | $3281 | $315000 |
| 🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
| 🇳🇱 Netherlands | $2575 | $3219 | $309000 |
| 🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
| 🇳🇿 New Zealand | $3345 | $4181 | $401400 |
| 🇳🇴 Norway | $2400 | $3000 | $288000 |
| 🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
| 🇴🇲 Oman | $2625 | $3281 | $315000 |
| 🇵🇰 Pakistan | $2625 | $3281 | $315000 |
| 🇵🇦 Panama | $3230 | $4038 | $387600 |
| 🇵🇾 Paraguay | $3155 | $3944 | $378600 |
| 🇵🇪 Peru | $3230 | $4038 | $387600 |
| 🇵🇱 Poland | $2575 | $3219 | $309000 |
| 🇵🇹 Portugal | $2500 | $3125 | $300000 |
| 🇷🇺 Russia | $2575 | $3219 | $309000 |
| 🇷🇴 Romania | $2475 | $3094 | $297000 |
| 🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
| 🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
| 🇷🇸 Serbia | $2575 | $3219 | $309000 |
| 🇸🇬 Singapore | $3095 | $3869 | $371400 |
| 🇸🇾 Syria | $3095 | $3869 | $371400 |
| 🇸🇰 Slovakia | $2500 | $3125 | $300000 |
| 🇸🇮 Slovenia | $2500 | $3125 | $300000 |
| 🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
| 🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
| 🇺🇸 United States | $2902.5 | $3628 | $348300 |
| 🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
| 🇹🇭 Thailand | $2625 | $3281 | $315000 |
| 🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
| 🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
| 🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
| 🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
| 🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
| 🇹🇷 Turkey | $2625 | $3281 | $315000 |
| 🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
| 🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
| 🇺🇦 Ukraine | $2500 | $3125 | $300000 |
| 🇺🇾 Uruguay | $2675 | $3344 | $321000 |
| 🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
| 🇵🇭 Philippines | $2625 | $3281 | $315000 |
| 🇫🇮 Finland | $2500 | $3125 | $300000 |
| 🇫🇷 France | $2575 | $3219 | $309000 |
| 🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
| 🇲🇪 Montenegro | $2575 | $3219 | $309000 |
| 🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
| 🇨🇱 Chile | $3355 | $4194 | $402600 |
| 🇨🇭 Switzerland | $2575 | $3219 | $309000 |
| 🇸🇪 Sweden | $2500 | $3125 | $300000 |
| 🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
| 🇪🇨 Ecuador | $3155 | $3944 | $378600 |
| 🇦🇸 American Samoa | $3345 | $4181 | $401400 |
| 🇸🇻 El Salvador | $3230 | $4038 | $387600 |
| 🇪🇪 Estonia | $2575 | $3219 | $309000 |
| 🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
| 🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
| 🇯🇵 Japan | $3095 | $3869 | $371400 |
| 🇦🇩 Andorra | $2500 | $3125 | $300000 |
| 🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
| 🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
| 🇧🇧 Barbados | $3230 | $4038 | $387600 |
| 🇧🇹 Bhutan | $3095 | $3869 | $371400 |
| 🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
| 🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
| 🇧🇳 Brunei | $2625 | $3281 | $315000 |
| 🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
| 🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
| 🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
| 🇹🇩 Chad | $2762.5 | $3453 | $331500 |
| 🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
| 🇧🇯 Benin | $2762.5 | $3453 | $331500 |
| 🇩🇲 Dominica | $3230 | $4038 | $387600 |
| 🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
| 🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
| 🇫🇯 Fiji | $3345 | $4181 | $401400 |
| 🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
| 🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
| 🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
| 🇰🇮 Kiribati | $3345 | $4181 | $401400 |
| 🇬🇩 Grenada | $3355 | $4194 | $402600 |
| 🇬🇺 Guam | $3345 | $4181 | $401400 |
| 🇬🇾 Guyana | $3230 | $4038 | $387600 |
| 🇭🇹 Haiti | $3120 | $3900 | $374400 |
| 🇯🇲 Jamaica | $3230 | $4038 | $387600 |
| 🇰🇵 Korea, North | $2625 | $3281 | $315000 |
| 🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
| 🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
| 🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
| 🇲🇻 Maldives | $2625 | $3281 | $315000 |
| 🇲🇱 Mali | $2762.5 | $3453 | $331500 |
| 🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
| 🇨🇼 Curaçao | $3230 | $4038 | $387600 |
| 🇦🇼 Aruba | $3120 | $3900 | $374400 |
| 🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
| 🇳🇪 Niger | $2762.5 | $3453 | $331500 |
| 🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
| 🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
| 🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
| 🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
| 🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
| 🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
| 🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
| 🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
| 🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
| 🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
| 🇸🇲 San Marino | $2500 | $3125 | $300000 |
| 🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
| 🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
| 🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
| 🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
| 🇸🇷 Suriname | $3230 | $4038 | $387600 |
| 🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
| 🇹🇬 Togo | $2762.5 | $3453 | $331500 |
| 🇹🇴 Tonga | $3345 | $4181 | $401400 |
| 🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
| 🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
| 🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale romania. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.