$ 2185/MT
- Density: 1.10 g/cc
- Tensile Strength, Ultimate: 41.4 MPa
- Flexural Yield Strength: 68.9 MPa
- Flexural Modulus: 2.41 GPa
- Izod Impact, Notched: 0.641 J/cm @Thickness 3.17 mm
$ 1780/MT
- Density: 1.10 g/cc
- Melt Flow: 12 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 95
- Tensile Strength: 33.8 MPa
- Elongation at Yield: 3.5 %
$ 1477/MT
- Density: 1.20 g/cc
- Water Absorption: 0.14 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0015 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 108
- Tensile Strength, Yield: 96.5 MPa
$ 2330/MT
- Density: 1.11 g/cc
- Water Absorption: 0.14 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0015 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 108
- Tensile Strength, Yield: 103 MPa
$ 1778/MT
- Density: 1.23 g/cc
- Water Absorption: 0.30 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Melt Flow: 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 100
$ 1917/MT
- Density: 1.67 g/cc
- Water Absorption: 0.19 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength: 55.8 MPa
- Elongation at Yield: 2.0 %
$ 2524/MT
- Density: 1.16 g/cc
- Water Absorption: 0.18 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 107
- Tensile Strength, Yield: 45.5 MPa
$ 1543/MT
- Density: 1.20 g/cc
- Water Absorption: 0.13 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0015 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 107
- Tensile Strength, Yield: 93.8 MPa
$ 1453/MT
- Density: 1.11 g/cc
- Water Absorption: 0.16 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0035 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 72.4 MPa
- Elongation at Break: 3.0 %
$ 1638/MT
- Density: 1.28 g/cc
- Water Absorption: 0.30 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 46.9 MPa
- Elongation at Break: 2.0 %
$ 2019/MT
- Density: 1.03 g/cc
- Melt Flow: 1.5 g/10 min @Load 3.80 kg, Temperature 230 °C
- Melt Flow: 4.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 95
- Tensile Strength: 33.8 MPa
$ 1992/MT
- Density: 1.33 g/cc
- Melt Flow: 1.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 95
- Tensile Strength, Yield: 30.3 MPa
- Elongation at Break: 3.0 %
$ 1521/MT
- Density: 1.02 g/cc
- Melt Flow: 0.20 g/10 min @Load 3.80 kg, Temperature 230 °C
- Melt Flow: 2.3 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 90
- Tensile Strength, Yield: 31.0 MPa
$ 1482/MT
- Density: 1.19 g/cc
- Water Absorption: 0.14 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0015 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 110 MPa
- Elongation at Yield: 4.0 %
$ 1720/MT
- Density: 1.23 g/cc
- Water Absorption: 0.30 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Melt Flow: 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 100
$ 1580/MT
- Density: 1.10 g/cc
- Water Absorption: 0.28 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 50.3 MPa
- Elongation at Break: 4.0 %
$ 1526/MT
- Density: 1.36 g/cc
- Water Absorption: 0.16 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 124
- Tensile Strength, Yield: 60.0 MPa
$ 1514/MT
- Specific Gravity: 1.14 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.00050 cm/cm
- Tensile Strength at Break: 103 MPa
- Elongation at Break: 1.0 %
$ 2379/MT
- Specific Gravity: 1.29 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.00050 cm/cm
- Tensile Strength at Break: 100 MPa
- Elongation at Break: 1.0 %
$ 1680/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage: 0.0040 cm/cm @Thickness 3.17 mm
- Tensile Strength, Ultimate: 40.0 MPa
- Elongation at Break: 4.5 %
- Flexural Yield Strength: 78.6 MPa
$ 1942/MT
- Density: 1.06 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Melt Flow: 4.5 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 112
- Tensile Strength, Yield: 47.6 MPa
$ 2589/MT
- Density: 1.10 g/cc
- Water Absorption: 0.28 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 50.3 MPa
- Elongation at Break: 4.0 %
$ 1767/MT
- Density: 1.28 g/cc
- Water Absorption: 0.12 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 108
- Tensile Strength, Yield: 117 MPa
$ 2185/MT
- Density: 1.17 g/cc
- Water Absorption: 0.13 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 93.8 MPa
- Elongation at Break: 3.5 %
$ 1719/MT
- Density: 1.17 g/cc
- Water Absorption: 0.13 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0015 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 107
- Tensile Strength, Yield: 93.8 MPa
$ 1643/MT
- Density: 1.28 g/cc
- Water Absorption: 0.12 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Thickness 3.17 mm
- Melt Flow: 3.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 108
$ 1656/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm @Thickness 3.17 mm
- Melt Flow: 4.5 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 103
- Tensile Strength, Yield: 30.3 MPa
$ 1821/MT
- Density: 1.28 g/cc
- Water Absorption: 0.12 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 108
- Tensile Strength, Yield: 100 MPa
$ 1505/MT
- Density: 1.09 g/cc
- Water Absorption: 0.14 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 108
- Tensile Strength, Yield: 103 MPa
$ 1580/MT
- Density: 1.26 g/cc
- Water Absorption: 0.14 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00070 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 108
- Tensile Strength, Yield: 89.6 MPa
$ 1471/MT
- Density: 1.03 g/cc
- Melt Flow: 0.10 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 95
- Tensile Strength, Yield: 33.8 MPa
- Elongation at Break: 30 %
$ 2146/MT
- Density: 1.19 g/cc
- Water Absorption: 0.13 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0015 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 107
- Tensile Strength: 73.1 MPa
$ 2465/MT
- Density: 1.20 g/cc
- Water Absorption: 0.30 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Melt Flow: 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 100
$ 1596/MT
- Density: 1.10 g/cc
- Water Absorption: 0.28 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 50.3 MPa
- Elongation at Break: 4.0 %
$ 1594/MT
- Density: 1.09 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm @Thickness 3.17 mm
- Melt Flow: 4.5 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 103
- Tensile Strength, Yield: 27.6 MPa
$ 2188/MT
- Density: 1.30 g/cc
- Linear Mold Shrinkage: 0.0040 cm/cm @Thickness 3.17 mm
- Tensile Strength, Ultimate: 36.5 MPa
- Elongation at Break: 4.0 %
- Flexural Yield Strength: 59.3 MPa
$ 1767/MT
- Density: 1.13 g/cc
- Water Absorption: 0.14 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0015 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 108
- Tensile Strength, Yield: 110 MPa
$ 1520/MT
- Density: 1.12 g/cc
- Water Absorption: 0.30 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 100
- Tensile Strength: 44.8 MPa
$ 1627/MT
- Density: 1.19 g/cc
- Water Absorption: 0.13 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0015 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 107
- Tensile Strength, Yield: 73.1 MPa
$ 1470/MT
- Density: 1.19 g/cc
- Water Absorption: 0.30 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 77.9 MPa
- Elongation at Break: 11 %
$ 1471/MT
- Density: 1.27 g/cc
- Water Absorption: 0.16 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 56.5 MPa
- Elongation at Break: 3.0 %
$ 1829/MT
- Density: 1.15 g/cc
- Water Absorption: 0.14 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 108
- Tensile Strength, Yield: 124 MPa
$ 1714/MT
- Density: 1.33 g/cc
- Water Absorption: 0.28 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 37.9 MPa
- Elongation at Break: 4.0 %
$ 1523/MT
- Density: 3.00 g/cc
- Water Absorption: 0.14 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength: 49.0 MPa
- Elongation at Yield: 2.0 %
$ 1945/MT
- Density: 3.50 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength: 42.1 MPa
- Elongation at Yield: 2.0 %
$ 2444/MT
- Density: 1.16 g/cc
- Water Absorption: 0.16 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 34.5 MPa
- Elongation at Yield: 1.8 %
$ 2494/MT
- Density: 1.24 g/cc
- Water Absorption: 0.14 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0015 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 117 MPa
- Elongation at Yield: 2.0 %
$ 2120/MT
- Density: 1.17 g/cc
- Water Absorption: 0.13 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 107
- Tensile Strength, Yield: 47.6 MPa
$ 1742/MT
- Density: 1.28 g/cc
- Water Absorption: 0.12 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 108
- Tensile Strength, Yield: 96.5 MPa
$ 1566/MT
- Density: 1.22 g/cc
- Water Absorption: 0.30 % @Time 86400 sec
- Hardness, Rockwell R: 90
- Tensile Strength, Yield: 28.3 MPa
- Elongation at Yield: 15 %
$ 2338/MT
- Density: 1.19 g/cc
- Water Absorption: 0.17 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 107
- Tensile Strength, Yield: 59.3 MPa
$ 1710/MT
- Density: 1.10 g/cc
- Water Absorption: 0.28 % @Time 86400 sec
- Hardness, Rockwell R: 112
- Tensile Strength, Yield: 50.3 MPa
- Elongation at Yield: 4.0 %
$ 1844/MT
- Density: 1.20 g/cc
- Water Absorption: 0.20 %
- Linear Mold Shrinkage: 0.00050 cm/cm @Thickness 3.17 mm
- Tensile Strength, Ultimate: 103 MPa
- Elongation at Break: 1.0 %
$ 1707/MT
- Density: 1.28 g/cc
- Water Absorption: 0.30 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 46.9 MPa
- Elongation at Break: 2.0 %
$ 1831/MT
- Density: 1.10 g/cc
- Water Absorption: 0.16 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0035 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 58.6 MPa
- Elongation at Break: 3.0 %
$ 1466/MT
- Density: 1.03 g/cc
- Melt Flow: 12 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 95
- Tensile Strength, Yield: 33.1 MPa
- Elongation at Break: 3.5 %
$ 1464/MT
- Density: 1.16 g/cc
- Water Absorption: 0.28 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 50.3 MPa
- Elongation at Break: 4.0 %
$ 1471/MT
- Density: 3.50 g/cc
- Water Absorption: 0.025 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Melt Flow: 0.80 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 95
$ 1578/MT
- Density: 1.07 g/cc
- Water Absorption: 0.16 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 65.5 MPa
- Elongation at Break: 3.0 %
$ 2136/MT
- Density: 1.33 g/cc
- Water Absorption: 0.30 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 47.6 MPa
- Elongation at Break: 2.0 %
$ 2528/MT
- Density: 1.33 g/cc
- Water Absorption: 0.30 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 47.6 MPa
- Elongation at Break: 2.0 %
$ 2010/MT
- Density: 1.12 g/cc
- Water Absorption: 0.28 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 50.3 MPa
- Elongation at Break: 4.0 %
$ 1846/MT
- Density: 1.44 g/cc
- Water Absorption: 0.12 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 108
- Tensile Strength, Yield: 72.4 MPa
$ 1598/MT
- Density: 1.23 g/cc
- Water Absorption: 0.30 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Melt Flow: 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 100
$ 1659/MT
- Density: 1.10 g/cc
- Water Absorption: 0.40 %
- Linear Mold Shrinkage: 0.0060 cm/cm @Thickness 3.17 mm
- Tensile Strength, Ultimate: 82.7 MPa
- Elongation at Break: 1.7 %
$ 2458/MT
- Density: 1.20 g/cc
- Water Absorption: 0.13 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0015 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 107
- Tensile Strength, Yield: 93.8 MPa
$ 1517/MT
- Density: 2.30 g/cc
- Water Absorption: 0.19 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength: 55.8 MPa
- Elongation at Yield: 2.0 %
$ 1683/MT
- Density: 1.28 g/cc
- Water Absorption: 0.12 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 108
- Tensile Strength, Yield: 100 MPa
$ 1541/MT
- Density: 1.22 g/cc
- Water Absorption: 0.30 % @Time 86400 sec
- Hardness, Rockwell R: 90
- Tensile Strength, Yield: 28.3 MPa
- Elongation at Break: 15 %
$ 1703/MT
- Density: 1.36 g/cc
- Water Absorption: 0.16 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 124
- Tensile Strength: 60.0 MPa
$ 2354/MT
- Density: 1.28 g/cc
- Water Absorption: 0.12 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 108
- Tensile Strength, Yield: 100 MPa
$ 1861/MT
- Density: 1.33 g/cc
- Water Absorption: 0.30 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 47.6 MPa
- Elongation at Break: 2.0 %
$ 1500/MT
- Density: 1.10 g/cc
- Water Absorption: 0.28 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 50.3 MPa
- Elongation at Break: 4.0 %
$ 1867/MT
- Density: 1.00 g/cc
- Water Absorption: 0.010 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.017 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 80
- Tensile Strength, Yield: 32.4 MPa
$ 2100/MT
- Density: 1.26 g/cc
- Water Absorption: 0.12 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 108
- Tensile Strength, Yield: 93.1 MPa
$ 1501/MT
- Density: 1.11 g/cc
- Water Absorption: 0.16 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0035 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 44.8 MPa
- Elongation at Break: 3.0 %
$ 1748/MT
- Density: 1.23 g/cc
- Water Absorption: 0.30 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Melt Flow: 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 100
$ 1785/MT
- Density: 1.10 g/cc
- Water Absorption: 0.28 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 50.3 MPa
- Elongation at Break: 4.0 %
Delivery Acrylonitrile Butadiene Styrene (ABS) Techmer ES
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
lpg tankers for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.