$ 1895/MT
- Density: 1.10 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0013 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 109
- Tensile Strength, Yield: 55.2 MPa
$ 1525/MT
- Density: 1.28 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 138 MPa
$ 1596/MT
- Density: 1.48 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 110 MPa
$ 1975/MT
- Density: 1.49 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 103 MPa
$ 1920/MT
- Density: 1.35 g/cc
- Water Absorption: 1.0 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.015 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 68.9 MPa
$ 1983/MT
- Density: 1.47 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 122
- Tensile Strength, Yield: 183 MPa
$ 1676/MT
- Density: 1.50 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 234 MPa
$ 1836/MT
- Density: 1.33 g/cc
- Water Absorption: 1.0 %
- Linear Mold Shrinkage: 0.0010 cm/cm @Thickness 3.17 mm
- Tensile Strength, Ultimate: 228 MPa
- Flexural Yield Strength: 345 MPa
$ 2420/MT
- Density: 1.33 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0012 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 145 MPa
$ 1924/MT
- Density: 1.34 g/cc
- Water Absorption: 0.70 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 176 MPa
$ 1955/MT
- Density: 1.18 g/cc
- Water Absorption: 1.1 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.014 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 100
- Tensile Strength: 72.4 MPa
$ 2178/MT
- Density: 1.37 g/cc
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 165 MPa
$ 1746/MT
- Density: 1.38 g/cc
- Water Absorption: 1.1 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 165 MPa
$ 1793/MT
- Density: 1.60 g/cc
- Water Absorption: 1.0 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 117
- Tensile Strength, Yield: 131 MPa
$ 1588/MT
- Density: 1.48 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 122
- Tensile Strength, Yield: 119 MPa
$ 2495/MT
- Density: 1.38 g/cc
- Water Absorption: 1.1 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 186 MPa
$ 1505/MT
- Density: 3.03 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 51.7 MPa
- Elongation at Break: 1.0 %
$ 1775/MT
- Density: 1.16 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.013 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 89.6 MPa
$ 1876/MT
- Density: 1.13 g/cc
- Water Absorption: 2.8 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.011 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 90.3 MPa
$ 1945/MT
- Density: 1.54 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 124 MPa
$ 1566/MT
- Density: 1.13 g/cc
- Water Absorption: 1.6 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.012 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 79.3 MPa
$ 1727/MT
- Density: 1.37 g/cc
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 176 MPa
$ 2289/MT
- Density: 1.67 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 122
- Tensile Strength, Yield: 148 MPa
$ 1599/MT
- Density: 1.48 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.035 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 176 MPa
$ 1772/MT
- Density: 1.23 g/cc
- Water Absorption: 0.80 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 112
- Tensile Strength, Yield: 89.6 MPa
$ 1495/MT
- Density: 1.29 g/cc
- Water Absorption: 0.60 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.016 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 97
- Tensile Strength, Yield: 40.7 MPa
$ 1503/MT
- Density: 1.38 g/cc
- Water Absorption: 1.1 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 190 MPa
$ 1966/MT
- Density: 10.3 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 58.6 MPa
- Elongation at Break: 1.0 %
$ 1559/MT
- Density: 1.37 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.016 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 72.4 MPa
- Elongation at Break: 10 %
$ 1471/MT
- Density: 1.41 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.035 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 155 MPa
$ 1488/MT
- Density: 1.20 g/cc
- Water Absorption: 1.0 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.017 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 116
- Tensile Strength, Yield: 64.8 MPa
$ 1506/MT
- Density: 1.13 g/cc
- Water Absorption: 1.6 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.012 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 79.3 MPa
$ 2395/MT
- Density: 1.57 g/cc
- Water Absorption: 0.75 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0025 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 207 MPa
$ 1931/MT
- Density: 1.39 g/cc
- Water Absorption: 0.80 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 117
- Tensile Strength, Yield: 117 MPa
$ 1761/MT
- Density: 1.23 g/cc
- Water Absorption: 1.0 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.010 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 89.6 MPa
$ 1918/MT
- Density: 1.57 g/cc
- Water Absorption: 0.70 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0022 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 207 MPa
$ 1636/MT
- Density: 1.08 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.013 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 105
- Tensile Strength, Yield: 50.3 MPa
$ 1469/MT
- Density: 1.26 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.012 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 99
- Tensile Strength, Yield: 79.3 MPa
$ 1526/MT
- Density: 1.13 g/cc
- Water Absorption: 1.6 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.012 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 80.0 MPa
$ 1465/MT
- Density: 3.25 g/cc
- Water Absorption: 0.30 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 56.5 MPa
- Elongation at Break: 4.0 %
$ 1643/MT
- Density: 1.34 g/cc
- Water Absorption: 0.70 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength: 176 MPa
$ 1469/MT
- Density: 1.13 g/cc
- Water Absorption: 1.6 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.012 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 79.3 MPa
$ 2539/MT
- Density: 1.13 g/cc
- Water Absorption: 2.8 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.011 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 90.3 MPa
$ 2160/MT
- Density: 1.13 g/cc
- Water Absorption: 2.8 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.014 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 90.3 MPa
$ 1520/MT
- Density: 1.14 g/cc
- Water Absorption: 1.6 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.014 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 102
- Tensile Strength, Yield: 74.5 MPa
$ 2367/MT
- Density: 1.13 g/cc
- Water Absorption: 2.8 % @Time 86400 sec
- Viscosity Test: 75 cm³/g
- Linear Mold Shrinkage, Flow: 0.011 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 119
$ 1983/MT
- Density: 1.08 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 105
- Tensile Strength, Yield: 43.4 MPa
$ 1672/MT
- Density: 1.38 g/cc
- Water Absorption: 1.1 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 169 MPa
$ 1863/MT
- Density: 1.29 g/cc
- Water Absorption: 1.4 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 138 MPa
$ 1755/MT
- Density: 1.24 g/cc
- Water Absorption: 1.4 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0055 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 111 MPa
$ 2526/MT
- Density: 1.48 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 122
- Tensile Strength, Yield: 109 MPa
$ 1585/MT
- Density: 1.24 g/cc
- Water Absorption: 1.4 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0055 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 107 MPa
$ 1527/MT
- Density: 1.80 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 47.6 MPa
- Elongation at Break: 1.0 %
$ 1476/MT
- Density: 1.39 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.035 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 152 MPa
$ 1454/MT
- Density: 1.57 g/cc
- Water Absorption: 0.70 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0022 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 200 MPa
$ 1480/MT
- Density: 1.37 g/cc
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 176 MPa
$ 1509/MT
- Density: 1.23 g/cc
- Water Absorption: 1.0 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.010 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 96.5 MPa
$ 1722/MT
- Density: 1.49 g/cc
- Water Absorption: 1.0 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 117
- Tensile Strength, Yield: 138 MPa
$ 1678/MT
- Density: 3.88 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 44.8 MPa
- Elongation at Break: 1.0 %
$ 1461/MT
- Density: 1.06 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.013 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 105
- Tensile Strength, Yield: 50.3 MPa
$ 1925/MT
- Density: 1.24 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.017 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 116
- Tensile Strength, Yield: 65.5 MPa
$ 1905/MT
- Density: 1.07 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0080 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 41.4 MPa
- Elongation at Break: 300 %
$ 1872/MT
- Density: 1.35 g/cc
- Density: 1.37 g/cc
- Water Absorption: 0.85 % @Time 86400 sec
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
$ 1777/MT
- Density: 1.57 g/cc
- Water Absorption: 0.75 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0025 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 193 MPa
- Elongation at Break: 4.0 %
$ 2559/MT
- Density: 1.30 g/cc
- Water Absorption: 1.4 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 124 MPa
$ 2365/MT
- Density: 1.34 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 186 MPa
$ 1542/MT
- Density: 1.31 g/cc
- Water Absorption: 1.4 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 152 MPa
$ 2578/MT
- Density: 1.49 g/cc
- Water Absorption: 0.95 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 90
- Tensile Strength, Yield: 137 MPa
$ 1864/MT
- Density: 1.34 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.035 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 152 MPa
$ 1454/MT
- Density: 1.37 g/cc
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 165 MPa
$ 1672/MT
- Density: 1.39 g/cc
- Water Absorption: 0.80 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 117
- Tensile Strength, Yield: 120 MPa
$ 2125/MT
- Density: 1.24 g/cc
- Water Absorption: 1.4 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0055 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 107 MPa
$ 1623/MT
- Density: 1.04 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.016 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 70
- Tensile Strength, Yield: 44.8 MPa
$ 1479/MT
- Density: 1.24 g/cc
- Water Absorption: 1.4 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0080 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 107 MPa
$ 1810/MT
- Density: 1.41 g/cc
- Water Absorption: 0.82 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 122
- Tensile Strength, Yield: 162 MPa
$ 1778/MT
- Density: 1.68 g/cc
- Water Absorption: 0.55 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 186 MPa
$ 1778/MT
- Density: 1.46 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.035 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 176 MPa
$ 1485/MT
- Density: 1.23 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 191 MPa
$ 1772/MT
- Density: 1.37 g/cc
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 165 MPa
$ 1459/MT
- Density: 1.37 g/cc
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 165 MPa
$ 2056/MT
- Density: 1.06 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0013 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 105
- Tensile Strength, Yield: 50.3 MPa
$ 1503/MT
- Density: 1.27 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 112
- Tensile Strength, Yield: 124 MPa
$ 1464/MT
- Density: 1.56 g/cc
- Water Absorption: 0.55 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0025 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 203 MPa
- Elongation at Break: 3.2 %
$ 1902/MT
- Density: 1.37 g/cc
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 165 MPa
$ 1627/MT
- Density: 1.33 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 116
- Tensile Strength, Yield: 159 MPa
$ 1694/MT
- Density: 1.49 g/cc
- Water Absorption: 0.85 %
- Linear Mold Shrinkage: 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength, Ultimate: 172 MPa
- Flexural Yield Strength: 221 MPa
$ 1947/MT
- Density: 1.25 g/cc
- Water Absorption: 0.20 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 100 MPa
- Elongation at Break: 4.5 %
$ 1805/MT
- Density: 1.18 g/cc
- Water Absorption: 0.95 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.012 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 112
- Tensile Strength, Yield: 65.5 MPa
$ 2009/MT
- Density: 1.07 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 70
- Tensile Strength, Yield: 51.7 MPa
$ 1767/MT
- Density: 1.28 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.015 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 97
- Tensile Strength, Yield: 39.3 MPa
$ 1543/MT
- Density: 1.26 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.012 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 99
- Tensile Strength, Yield: 79.3 MPa
$ 1782/MT
- Density: 3.65 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 44.8 MPa
- Elongation at Break: 1.0 %
$ 1644/MT
- Density: 1.28 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 138 MPa
$ 2360/MT
- Density: 1.48 g/cc
- Water Absorption: 0.95 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 86.2 MPa
$ 1748/MT
- Density: 1.33 g/cc
- Water Absorption: 1.1 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 117
- Tensile Strength, Yield: 75.8 MPa
$ 2545/MT
- Density: 1.57 g/cc
- Water Absorption: 0.75 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0025 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 207 MPa
$ 2049/MT
- Density: 1.23 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.017 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 116
- Tensile Strength, Yield: 62.1 MPa
$ 2483/MT
- Specific Gravity: 1.25 g/cc
- Water Absorption: 0.11 %
- Tensile Strength at Break: 89.6 MPa
- Elongation at Break: 3.0 %
- Flexural Strength: 131 MPa
$ 1507/MT
- Density: 1.34 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.019 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 69.6 MPa
$ 1753/MT
- Density: 1.13 g/cc
- Water Absorption: 2.8 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.014 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 90.3 MPa
$ 1594/MT
- Density: 1.24 g/cc
- Water Absorption: 1.1 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.017 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 68.9 MPa
$ 1539/MT
- Density: 1.58 g/cc
- Water Absorption: 0.75 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 221 MPa
$ 2099/MT
- Density: 1.19 g/cc
- Water Absorption: 0.70 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.012 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 112
- Tensile Strength, Yield: 65.5 MPa
$ 1989/MT
- Density: 4.25 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 44.8 MPa
- Elongation at Break: 1.0 %
$ 2079/MT
- Specific Gravity: 1.21 g/cc
- Linear Mold Shrinkage: 0.013 cm/cm
- Tensile Strength at Break: 72.4 MPa
- Elongation at Break: 5.0 %
- Flexural Strength: 107 MPa
$ 2391/MT
- Density: 1.38 g/cc
- Water Absorption: 1.1 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 183 MPa
$ 1774/MT
- Density: 1.24 g/cc
- Water Absorption: 1.4 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0055 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 107 MPa
$ 1486/MT
- Density: 2.01 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 46.9 MPa
- Elongation at Break: 1.0 %
$ 1995/MT
- Density: 1.38 g/cc
- Water Absorption: 1.1 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 172 MPa
$ 1590/MT
- Density: 1.21 g/cc
- Water Absorption: 1.1 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.017 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 116
- Tensile Strength, Yield: 62.7 MPa
$ 2015/MT
- Density: 1.10 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.014 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 109
- Tensile Strength, Yield: 55.2 MPa
$ 1835/MT
- Density: 1.01 g/cc
- Water Absorption: 0.70 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0019 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 78
- Tensile Strength: 47.6 MPa
$ 1756/MT
- Density: 1.25 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 122
- Tensile Strength, Yield: 96.5 MPa
$ 1697/MT
- Density: 3.88 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 44.8 MPa
- Elongation at Break: 1.0 %
$ 2125/MT
- Density: 1.28 g/cc
- Water Absorption: 1.0 %
- Linear Mold Shrinkage: 0.0010 cm/cm @Thickness 3.17 mm
- Tensile Strength, Ultimate: 228 MPa
- Elongation at Break: 3.3 %
$ 1695/MT
- Density: 1.48 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 122
- Tensile Strength, Yield: 123 MPa
$ 1657/MT
- Density: 1.23 g/cc
- Water Absorption: 0.20 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 112
- Tensile Strength, Yield: 89.6 MPa
$ 1775/MT
- Density: 1.57 g/cc
- Water Absorption: 0.75 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0025 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 193 MPa
- Elongation at Break: 4.0 %
$ 1767/MT
- Density: 1.19 g/cc
- Water Absorption: 0.70 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.012 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 112
- Tensile Strength, Yield: 65.5 MPa
$ 2161/MT
- Density: 1.40 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 122
- Tensile Strength, Yield: 103 MPa
$ 1555/MT
- Density: 1.37 g/cc
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 176 MPa
$ 2594/MT
- Density: 1.37 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0035 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 122
- Tensile Strength, Yield: 119 MPa
$ 1865/MT
- Density: 1.57 g/cc
- Water Absorption: 0.75 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0025 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 221 MPa
$ 2120/MT
- Density: 3.48 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 44.8 MPa
- Elongation at Break: 1.0 %
$ 2226/MT
- Density: 1.06 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0013 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 105
- Tensile Strength, Yield: 50.3 MPa
$ 1766/MT
- Density: 1.46 g/cc
- Water Absorption: 0.80 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 122
- Tensile Strength, Yield: 105 MPa
$ 1773/MT
- Density: 1.27 g/cc
- Water Absorption: 1.0 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 214 MPa
$ 2271/MT
- Density: 1.22 g/cc
- Water Absorption: 0.80 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 96.5 MPa
- Elongation at Break: 7.5 %
$ 1535/MT
- Density: 1.13 g/cc
- Water Absorption: 2.8 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.013 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 90.3 MPa
$ 1453/MT
- Density: 1.13 g/cc
- Water Absorption: 1.6 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.012 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 77.9 MPa
$ 1476/MT
- Density: 1.06 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.015 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 105
- Tensile Strength, Yield: 50.3 MPa
$ 1531/MT
- Density: 1.30 g/cc
- Water Absorption: 1.4 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 141 MPa
$ 1941/MT
- Density: 1.46 g/cc
- Water Absorption: 0.80 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 122
- Tensile Strength, Yield: 200 MPa
$ 1543/MT
- Density: 1.19 g/cc
- Water Absorption: 1.0 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.010 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 72.4 MPa
$ 1856/MT
- Density: 1.31 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 122
- Tensile Strength, Yield: 75.8 MPa
$ 1599/MT
- Density: 1.27 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 214 MPa
$ 1932/MT
- Density: 1.48 g/cc
- Water Absorption: 0.95 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 86.9 MPa
$ 2061/MT
- Density: 1.30 g/cc
- Water Absorption: 1.4 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 138 MPa
$ 1593/MT
- Density: 1.28 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 115
- Tensile Strength: 13.8 MPa
$ 1758/MT
- Density: 1.24 g/cc
- Water Absorption: 1.4 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0055 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 110 MPa
$ 2050/MT
- Density: 1.38 g/cc
- Water Absorption: 1.1 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 165 MPa
$ 1785/MT
- Density: 1.34 g/cc
- Water Absorption: 1.2 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 89.6 MPa
$ 1779/MT
- Density: 1.48 g/cc
- Water Absorption: 0.75 %
- Linear Mold Shrinkage: 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength, Ultimate: 165 MPa
- Flexural Yield Strength: 228 MPa
$ 1578/MT
- Density: 1.37 g/cc
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 165 MPa
$ 1504/MT
- Density: 1.57 g/cc
- Water Absorption: 0.75 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0025 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 186 MPa
- Elongation at Break: 4.0 %
$ 1551/MT
- Density: 1.16 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.013 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 87.6 MPa
$ 2475/MT
- Density: 1.55 g/cc
- Water Absorption: 0.65 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0022 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 172 MPa
$ 2232/MT
- Density: 1.36 g/cc
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 176 MPa
$ 1628/MT
- Density: 1.30 g/cc
- Water Absorption: 1.4 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 138 MPa
$ 1792/MT
- Density: 1.10 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.016 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 110
- Tensile Strength at Break: 73.8 MPa
$ 1701/MT
- Density: 1.32 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 221 MPa
$ 2341/MT
- Density: 1.06 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.013 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 105
- Tensile Strength: 50.3 MPa
$ 1847/MT
- Density: 1.24 g/cc
- Water Absorption: 1.4 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0055 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 107 MPa
$ 1699/MT
- Density: 1.34 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.035 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 152 MPa
$ 1723/MT
- Density: 1.63 g/cc
- Water Absorption: 0.75 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 122
- Tensile Strength, Yield: 149 MPa
$ 1964/MT
- Density: 1.63 g/cc
- Water Absorption: 0.75 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 125 MPa
- Elongation at Break: 4.5 %
$ 2397/MT
- Density: 1.13 g/cc
- Water Absorption: 1.6 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.011 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 79.3 MPa
$ 1937/MT
- Density: 1.68 g/cc
- Water Absorption: 0.65 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 221 MPa
$ 1596/MT
- Specific Gravity: 1.23 g/cc
- Water Absorption: 1.0 %
- Linear Mold Shrinkage: 0.0020 cm/cm
- Tensile Strength at Break: 193 MPa
- Elongation at Break: 3.0 %
$ 1723/MT
- Density: 1.10 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.016 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 110
- Tensile Strength at Break: 66.9 MPa
$ 1608/MT
- Density: 1.37 g/cc
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 176 MPa
$ 1497/MT
- Density: 2.66 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 44.8 MPa
- Elongation at Break: 1.0 %
$ 1705/MT
- Density: 1.50 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 131 MPa
$ 1493/MT
- Density: 3.65 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 44.8 MPa
- Elongation at Break: 1.0 %
$ 1990/MT
- Density: 1.23 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 122
- Tensile Strength, Yield: 89.6 MPa
$ 1619/MT
- Density: 1.37 g/cc
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 165 MPa
$ 1457/MT
- Density: 1.70 g/cc
- Water Absorption: 0.70 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0015 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 231 MPa
$ 1699/MT
- Density: 1.35 g/cc
- Water Absorption: 1.1 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 79.3 MPa
$ 1669/MT
- Density: 1.50 g/cc
- Water Absorption: 1.0 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 200 MPa
$ 1828/MT
- Density: 1.35 g/cc
- Water Absorption: 1.1 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 80.0 MPa
$ 1687/MT
- Density: 1.22 g/cc
- Water Absorption: 0.80 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 112
- Tensile Strength, Yield: 103 MPa
$ 1905/MT
- Density: 1.25 g/cc
- Linear Mold Shrinkage, Flow: 0.010 cm/cm @Thickness 3.17 mm
- Melt Flow: 1.0 g/10 min @Load 10.0 kg, Temperature 230 °C
- Hardness, Rockwell R: 89
- Tensile Strength, Yield: 82.7 MPa
$ 2330/MT
- Density: 1.31 g/cc
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 148 MPa
$ 1755/MT
- Density: 1.49 g/cc
- Water Absorption: 0.95 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 193 MPa
- Elongation at Break: 2.0 %
$ 2101/MT
- Density: 1.55 g/cc
- Water Absorption: 0.65 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0022 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 152 MPa
- Elongation at Break: 3.8 %
$ 1688/MT
- Density: 1.24 g/cc
- Water Absorption: 1.4 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0055 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 110 MPa
$ 1464/MT
- Density: 3.90 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 44.8 MPa
- Elongation at Break: 1.0 %
$ 1638/MT
- Density: 1.24 g/cc
- Water Absorption: 1.4 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 101 MPa
$ 1733/MT
- Density: 1.22 g/cc
- Water Absorption: 1.4 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 103 MPa
$ 1519/MT
- Density: 1.05 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0080 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 70
- Tensile Strength, Yield: 35.9 - 51.7 MPa
$ 2301/MT
- Density: 2.40 g/cc
- Water Absorption: 0.40 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Tensile Strength: 59.3 MPa
- Elongation at Yield: 4.0 %
$ 1788/MT
- Density: 1.41 g/cc
- Water Absorption: 1.0 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0025 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 195 MPa
$ 1811/MT
- Density: 1.48 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 122
- Tensile Strength, Yield: 119 MPa
$ 2147/MT
- Density: 1.38 g/cc
- Water Absorption: 1.1 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 172 MPa
$ 2236/MT
- Density: 1.70 g/cc
- Water Absorption: 0.70 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0015 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 231 MPa
$ 1746/MT
- Density: 1.16 g/cc
- Water Absorption: 1.4 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.012 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 75.8 MPa
$ 1929/MT
- Density: 1.06 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.015 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 105
- Tensile Strength, Yield: 50.3 MPa
$ 1848/MT
- Density: 1.47 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 122
- Tensile Strength, Yield: 183 MPa
$ 1747/MT
- Density: 1.18 g/cc
- Water Absorption: 1.0 %
- Linear Mold Shrinkage: 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength, Ultimate: 131 MPa
- Tensile Modulus: 7.93 GPa
$ 1730/MT
- Density: 1.19 g/cc
- Water Absorption: 0.70 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.010 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 112
- Tensile Strength, Yield: 51.7 MPa
$ 2492/MT
- Density: 1.13 g/cc
- Water Absorption: 1.6 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.012 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 79.3 MPa
$ 1451/MT
- Density: 2.32 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0025 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 45.5 MPa
- Elongation at Break: 1.0 %
$ 1515/MT
- Density: 1.34 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.010 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 122
- Tensile Strength, Yield: 75.8 MPa
$ 1777/MT
- Density: 1.13 g/cc
- Water Absorption: 1.6 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.012 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 79.3 MPa
$ 1605/MT
- Density: 1.63 g/cc
- Water Absorption: 0.75 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 125 MPa
- Elongation at Break: 4.5 %
$ 1903/MT
- Density: 1.37 g/cc
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 176 MPa
$ 1568/MT
- Density: 1.38 g/cc
- Water Absorption: 1.1 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 165 MPa
$ 1538/MT
- Density: 1.30 g/cc
- Water Absorption: 1.4 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 138 MPa
$ 1815/MT
- Density: 1.55 g/cc
- Water Absorption: 0.65 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0022 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 172 MPa
$ 1742/MT
- Density: 1.21 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 86.2 MPa
$ 1966/MT
- Density: 1.49 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 234 MPa
$ 1987/MT
- Density: 1.57 g/cc
- Water Absorption: 0.75 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0025 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 221 MPa
$ 1813/MT
- Density: 1.22 g/cc
- Water Absorption: 0.85 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.015 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 75.8 MPa
$ 1616/MT
- Density: 4.45 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 34.5 MPa
- Elongation at Break: 1.0 %
$ 1687/MT
- Density: 1.33 g/cc
- Water Absorption: 1.1 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 117
- Tensile Strength, Yield: 75.8 MPa
$ 2054/MT
- Density: 1.23 g/cc
- Water Absorption: 0.20 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 112
- Tensile Strength, Yield: 89.6 MPa
$ 1504/MT
- Density: 1.57 g/cc
- Water Absorption: 0.75 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0025 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 221 MPa
$ 1524/MT
- Density: 1.34 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0035 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 152 MPa
$ 1903/MT
- Density: 1.34 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0035 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 152 MPa
$ 1839/MT
- Density: 1.34 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0035 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 152 MPa
$ 1655/MT
- Density: 1.34 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0035 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 152 MPa
$ 1702/MT
- Density: 1.13 g/cc
- Water Absorption: 2.8 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.011 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 49.0 MPa
- Elongation at Break: 85 %
$ 2181/MT
- Density: 1.70 g/cc
- Water Absorption: 0.70 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0015 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 231 MPa
$ 1537/MT
- Density: 1.54 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength: 124 MPa
$ 1561/MT
- Density: 1.33 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0012 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 100 MPa
- Elongation at Break: 8.0 %
$ 1626/MT
- Density: 1.13 g/cc
- Water Absorption: 2.8 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.011 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 90.3 MPa
$ 1507/MT
- Density: 1.30 g/cc
- Water Absorption: 1.4 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 138 MPa
$ 2153/MT
- Density: 1.06 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.013 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 105
- Tensile Strength, Yield: 50.3 MPa
$ 1613/MT
- Density: 1.13 g/cc
- Water Absorption: 2.8 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.011 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 49.0 MPa
- Elongation at Break: 85 %
$ 2413/MT
- Density: 5.02 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 46.2 MPa
- Elongation at Break: 1.0 %
$ 1849/MT
- Density: 1.70 g/cc
- Water Absorption: 0.70 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0015 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 230 MPa
$ 1499/MT
- Density: 1.78 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 44.1 MPa
- Elongation at Break: 1.0 %
$ 2480/MT
- Density: 1.58 g/cc
- Water Absorption: 0.75 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 221 MPa
$ 1910/MT
- Density: 1.32 g/cc
- Water Absorption: 0.97 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 132 MPa
$ 1662/MT
- Density: 2.99 g/cc
- Water Absorption: 0.30 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 57.9 MPa
- Elongation at Break: 4.0 %
$ 1715/MT
- Density: 1.13 g/cc
- Water Absorption: 2.8 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 90.3 MPa
$ 1506/MT
- Density: 1.07 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0080 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 125
- Tensile Strength, Yield: 48.3 MPa
$ 1515/MT
- Density: 1.06 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0013 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 105
- Tensile Strength, Yield: 50.3 MPa
$ 1765/MT
- Density: 1.59 g/cc
- Water Absorption: 0.80 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 122
- Tensile Strength, Yield: 112 MPa
$ 2313/MT
- Density: 2.54 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 44.8 MPa
- Elongation at Break: 1.0 %
$ 1702/MT
- Density: 1.36 g/cc
- Water Absorption: 0.95 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 90
- Tensile Strength, Yield: 88.3 MPa
$ 1496/MT
- Density: 1.16 g/cc
- Water Absorption: 1.6 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.012 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 79.3 MPa
$ 2087/MT
- Density: 1.14 g/cc
- Water Absorption: 1.6 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.010 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 86.2 MPa
$ 1763/MT
- Density: 1.37 g/cc
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 176 MPa
$ 1796/MT
- Density: 1.13 g/cc
- Water Absorption: 1.6 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.016 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 79.3 MPa
$ 2296/MT
- Density: 1.20 g/cc
- Water Absorption: 0.60 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.014 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 97
- Tensile Strength, Yield: 44.8 MPa
$ 2105/MT
- Density: 1.26 g/cc
- Water Absorption: 1.4 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 96.5 MPa
$ 1605/MT
- Density: 1.17 g/cc
- Water Absorption: 1.8 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.015 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 82.7 MPa
$ 1709/MT
- Density: 1.49 g/cc
- Water Absorption: 0.92 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 117 MPa
$ 1672/MT
- Density: 1.34 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 172 MPa
$ 1712/MT
- Density: 1.37 g/cc
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 148 MPa
$ 2085/MT
- Density: 1.28 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 140 MPa
$ 1665/MT
- Density: 1.30 g/cc
- Water Absorption: 1.4 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 131 MPa
$ 1917/MT
- Density: 1.63 g/cc
- Water Absorption: 0.75 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 122
- Tensile Strength, Yield: 149 MPa
$ 1564/MT
- Density: 1.57 g/cc
- Water Absorption: 0.75 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0025 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 193 MPa
- Elongation at Break: 4.0 %
$ 2056/MT
- Density: 1.22 g/cc
- Water Absorption: 0.80 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 112
- Tensile Strength, Yield: 103 MPa
$ 2028/MT
- Density: 1.57 g/cc
- Water Absorption: 0.75 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0025 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 221 MPa
$ 1765/MT
- Density: 1.36 g/cc
- Water Absorption: 0.88 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 157 MPa
$ 1805/MT
- Density: 1.20 g/cc
- Water Absorption: 0.60 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength: 69.6 MPa
$ 1987/MT
- Density: 1.16 g/cc
- Water Absorption: 1.6 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.012 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 79.3 MPa
$ 1548/MT
- Density: 1.24 g/cc
- Water Absorption: 1.4 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0055 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 86.2 MPa
$ 1646/MT
- Density: 6.85 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 44.8 MPa
- Elongation at Break: 1.0 %
$ 1629/MT
- Density: 1.24 g/cc
- Water Absorption: 1.4 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0055 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 107 MPa
$ 1641/MT
- Density: 1.56 g/cc
- Water Absorption: 0.55 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0025 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 214 MPa
$ 1544/MT
- Density: 1.22 g/cc
- Water Absorption: 1.0 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 65.5 MPa
$ 1545/MT
- Density: 1.22 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 3.17 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 186 MPa
$ 1521/MT
- Density: 2.54 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Thickness 3.17 mm
- Tensile Strength, Yield: 44.8 MPa
- Elongation at Break: 1.0 %
Delivery Nylon 6 Techmer ES
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
ship tankers for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.