$ 1515/MT
- Specific Gravity: 0.900 g/cc
- Hardness, Shore A: 64
- Tensile Strength, Yield: 2.76 MPa
- Tensile Strength, Yield: 4.69 MPa
- Tensile Strength, Yield: 5.52 MPa
$ 1630/MT
- Specific Gravity: 0.920 g/cc
- Melt Flow: 9.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 55
- Hardness, Shore A: 59
- Tensile Strength at Break: 4.55 MPa
$ 2153/MT
- Specific Gravity: 0.923 g/cc
- Melt Flow: 6.90 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 64
- Tensile Strength at Break: 5.63 MPa
- Elongation at Break: 280 %
$ 1511/MT
- Specific Gravity: 0.870 g/cc
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 125 °C
- Hardness, Shore OO: 50
- Tensile Strength, Yield: 2.07 MPa
- Elongation at Break: 700 %
- 300% Modulus: 0.000345 GPa
$ 1514/MT
- Specific Gravity: 0.930 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 69
- Tensile Strength, Yield: 19.8 MPa
- Elongation at Break: 650 %
$ 1932/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 4.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 75
- Tensile Strength at Break: 12.4 MPa
- Elongation at Break: 650 %
$ 2301/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 5.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 30
- Tensile Strength at Break: 4.83 MPa
- Elongation at Break: 700 %
$ 1457/MT
- Specific Gravity: 1.10 g/cc
- Hardness, Shore A: 40
- Tensile Strength, Yield: 2.21 MPa
- Tensile Strength, Yield: 6.07 MPa
- Tensile Strength, Yield: 7.72 MPa
$ 1629/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 3.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 58
- Tensile Strength at Break: 10.3 MPa
- Tensile Stress: 3.45 MPa @Strain 300 %
$ 1559/MT
- Specific Gravity: 1.00 g/cc
- Linear Mold Shrinkage: 0.020 cm/cm
- Melt Flow: 10 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 60
- Tensile Strength, Yield: 8.27 MPa
$ 1919/MT
- Specific Gravity: 0.910 g/cc
- Melt Flow: 20.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 42
- Tensile Strength at Break: 4.83 MPa
- Elongation at Break: 650 %
$ 1517/MT
- Specific Gravity: 1.05 g/cc
- Linear Mold Shrinkage: 0.017 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Melt Flow: 1.20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 2.60 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1570/MT
- Specific Gravity: 0.930 g/cc
- Melt Flow: 2.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 78
- Tensile Strength at Break: 7.03 MPa
- Elongation at Break: 310 %
$ 1492/MT
- Specific Gravity: 1.00 g/cc
- Melt Flow: 0.200 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 72
- Tensile Strength at Break: 5.86 MPa
- Elongation at Break: 620 %
$ 1600/MT
- Specific Gravity: 1.01 g/cc
- Melt Flow: 0.700 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 55
- Hardness, Shore D: 60
- Tensile Strength at Break: 15.2 MPa
$ 2325/MT
- Specific Gravity: 0.910 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 40 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 45
- Tensile Strength, Yield: 3.96 MPa
- Elongation at Break: 400 %
$ 2101/MT
- Specific Gravity: 1.30 g/cc
- Melt Flow: 1.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore C: 88
- Tensile Strength at Break: 11.7 MPa
- Elongation at Break: 600 %
$ 1522/MT
- Specific Gravity: 0.942 g/cc
- Melt Flow: 1.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 80
- Tensile Strength at Break: 6.89 MPa
- Elongation at Break: 550 %
$ 1849/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 30.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 62
- Tensile Strength at Break: 7.58 MPa
- Elongation at Break: 860 %
$ 1736/MT
- Specific Gravity: 1.06 g/cc
- Melt Flow: 10.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore D: 38
- Tensile Strength at Break: 6.89 MPa
- Tensile Stress: 9.65 MPa @Strain 300 %
$ 1617/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 5.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 11.7 MPa
- Tensile Stress: 7.93 MPa @Strain 300 %
$ 1859/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 14.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 27
- Tensile Strength at Break: 7.79 MPa
- Tensile Stress: 1.38 MPa @Strain 300 %
$ 2572/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 3.80 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 45
- Tensile Strength at Break: 6.27 MPa
- Elongation at Break: 830 %
$ 1734/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Linear Mold Shrinkage: 0.018 cm/cm
- Melt Flow: 8.7 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 91
$ 1494/MT
- Specific Gravity: 1.24 g/cc
- Melt Flow: 20.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 57
- Tensile Strength at Break: 3.45 MPa
- Elongation at Break: 700 %
$ 1567/MT
- Specific Gravity: 0.900 g/cc
- Linear Mold Shrinkage: 0.020 cm/cm
- Melt Flow: 3.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 17
- Tensile Strength at Break: 4.14 MPa
$ 1672/MT
- Specific Gravity: 0.880 g/cc
- Linear Mold Shrinkage: 0.023 cm/cm
- Linear Mold Shrinkage, Transverse: 0.027 cm/cm
- Melt Flow: 25.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 37
$ 2168/MT
- Specific Gravity: 0.930 g/cc
- Melt Flow: 15.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 53
- Tensile Strength at Break: 8.62 MPa
- Elongation at Break: 650 %
$ 2220/MT
- Specific Gravity: 0.930 g/cc
- Melt Flow: 20.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 23
- Tensile Strength at Break: 6.21 MPa
- Elongation at Break: 650 %
$ 2485/MT
- Specific Gravity: 1.25 g/cc
- Melt Flow: 1.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 47
- Tensile Strength at Break: 8.27 MPa
- Elongation at Break: 550 %
$ 2542/MT
- Density: 0.950 g/cc
- Hardness, Shore A: 62
- Hardness, Shore A: 66
- Tensile Strength at Break: 4.10 MPa
- Tensile Strength at Break: 6.20 MPa
$ 2115/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 1.50 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 53
- Tensile Strength at Break: 8.27 MPa
- Tensile Strength, Yield: 2.07 MPa @Strain 300 %
- Elongation at Break: 700 %
$ 2066/MT
- Specific Gravity: 1.28 g/cc
- Melt Flow: 3.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 58
- Tensile Strength: 8.96 MPa
- Elongation at Break: 550 %
$ 1733/MT
- Specific Gravity: 0.920 g/cc
- Linear Mold Shrinkage: 0.011 cm/cm
- Linear Mold Shrinkage: 0.013 cm/cm
- Melt Flow: 2.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 95
$ 2518/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 13.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 68
- Tensile Strength at Break: 0.758 MPa
- Elongation at Break: 700 %
$ 2314/MT
- Specific Gravity: 1.16 g/cc
- Melt Flow: 2.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 45
- Tensile Strength at Break: 3.79 MPa
- Tensile Stress: 0.827 MPa @Strain 100 %
$ 1467/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 17.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 74
- Tensile Strength at Break: 5.24 MPa
- Elongation at Break: 650 %
$ 1601/MT
- Specific Gravity: 0.930 g/cc
- Melt Flow: 7.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 37
- Tensile Strength at Break: 9.31 MPa
- Tensile Stress: 2.59 MPa @Strain 300 %
$ 1682/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 10.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 65
- Tensile Strength at Break: 11.0 MPa
- Tensile Stress: 5.52 MPa @Strain 300 %
$ 1704/MT
- Specific Gravity: 0.950 g/cc
- Melt Flow: 0.730 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 73
- Hardness, Shore A: 79
- Tensile Strength at Break: 6.55 MPa
$ 1525/MT
- Specific Gravity: 0.940 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Melt Flow: 9.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 36
$ 1768/MT
- Specific Gravity: 1.14 g/cc
- Melt Flow: 3.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 50
- Tensile Strength at Break: 17.2 MPa
- Tensile Stress: 14.5 MPa @Strain 100 %
$ 1714/MT
- Specific Gravity: 0.880 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 1.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 45
- Tensile Strength at Break: 7.58 MPa
$ 1573/MT
- Specific Gravity: 1.30 g/cc
- Melt Flow: 20.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 74
- Tensile Strength at Break: 9.79 MPa @Thickness 1.91 mm
- Elongation at Break: 680 %
$ 1776/MT
- Specific Gravity: 0.990 g/cc
- Melt Flow: 9.00 g/10 min @Load 2.16 kg, Temperature 175 °C
- Hardness, Shore A: 62
- Tensile Strength at Break: 3.79 MPa
- Elongation at Break: 500 %
$ 2340/MT
- Specific Gravity: 1.04 g/cc
- Melt Flow: 2.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 74
- Tensile Strength at Break: 8.89 MPa
- Elongation at Break: 800 %
$ 1584/MT
- Specific Gravity: 1.11 g/cc
- Melt Flow: 25.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 51
- Tensile Strength at Break: 4.14 MPa
- Elongation at Break: 500 %
$ 1585/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 8.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 45
- Tensile Strength at Break: 8.27 MPa
- Tensile Strength, Yield: 2.76 MPa @Strain 300 %
- Elongation at Break: 700 %
$ 1661/MT
- Specific Gravity: 0.920 g/cc
- Melt Flow: 13.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 45
- Hardness, Shore D: 50
- Tensile Strength at Break: 16.7 MPa
$ 1466/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.030 cm/cm
- Melt Flow: 1.50 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 45
- Tensile Strength at Break: 4.14 MPa
$ 1707/MT
- Specific Gravity: 1.00 g/cc
- Melt Flow: 0.200 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 79
- Tensile Strength at Break: 2.21 MPa
- Elongation at Break: 470 %
$ 1470/MT
- Specific Gravity: 1.03 g/cc
- Melt Flow: 13.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 60
- Tensile Strength: 4.69 MPa
- Elongation at Break: 850 %
$ 2089/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 15.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 48
- Tensile Strength at Break: 6.55 MPa
- Elongation at Break: 650 %
$ 1960/MT
- Specific Gravity: 1.04 g/cc
- Hardness, Shore A: 55
- Tensile Strength: 5.52 MPa
- Elongation at Break: 600 %
$ 1485/MT
- Specific Gravity: 0.930 g/cc
- Linear Mold Shrinkage: 0.039 cm/cm
- Linear Mold Shrinkage, Transverse: 0.028 cm/cm
- Melt Flow: 2.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 45
$ 1657/MT
- Specific Gravity: 0.930 g/cc
- Melt Flow: 5.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 50
- Tensile Strength at Break: 3.62 MPa
- Elongation at Break: 250 %
$ 1568/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 20.0 g/10 min @Load 2.16 kg, Temperature 150 °C
- Hardness, Shore A: 5.0
- Tensile Strength at Break: 2.07 MPa
- Tensile Stress: 0.345 MPa @Strain 300 %
$ 1582/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 90
- Tensile Strength, Yield: 6.89 MPa
- Elongation at Break: 400 %
$ 1635/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 12.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 75
- Tensile Strength at Break: 6.89 MPa
- Elongation at Break: 750 %
$ 1556/MT
- Specific Gravity: 1.22 g/cc
- Melt Flow: 3.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 6.21 MPa
- Tensile Stress: 4.48 MPa @Strain 300 %
$ 1556/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 1.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 37
- Tensile Strength at Break: 8.27 MPa
- Tensile Stress: 2.07 MPa @Strain 300 %
$ 1869/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 20.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 50
- Tensile Strength at Break: 6.89 MPa
$ 1868/MT
- Specific Gravity: 1.11 g/cc
- Hardness, Shore A: 45
- Tensile Strength, Yield: 2.69 MPa
- Tensile Strength, Yield: 7.31 MPa
- Tensile Strength, Yield: 8.62 MPa
$ 1483/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 25.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 30
- Tensile Strength at Break: 6.21 MPa
- Tensile Stress: 1.03 MPa @Strain 300 %
$ 1770/MT
- Specific Gravity: 1.00 g/cc
- Melt Flow: 46 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 75
- Tensile Strength, Yield: 6.21 MPa
- Elongation at Break: 615 %
$ 1646/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 70
- Tensile Strength, Yield: 6.89 MPa
- Elongation at Break: 500 %
$ 2312/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 38
- Tensile Strength at Break: 7.58 MPa
- Tensile Strength, Yield: 2.41 MPa @Strain 300 %
- Elongation at Break: 700 %
$ 1891/MT
- Specific Gravity: 1.01 g/cc
- Melt Flow: 14.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 80
- Tensile Strength: 8.34 MPa
- Elongation at Break: 890 %
$ 2092/MT
- Specific Gravity: 0.940 g/cc
- Melt Flow: 0.100 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 66
- Hardness, Shore A: 70
- Tensile Stress: 3.03 MPa @Strain 100 %
$ 1739/MT
- Specific Gravity: 1.00 g/cc
- Melt Flow: 18.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 83
- Tensile Strength at Break: 15.5 MPa
- Elongation at Break: 630 %
$ 2121/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.027 cm/cm
- Linear Mold Shrinkage, Transverse: 0.021 cm/cm
- Melt Flow: 1.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 65
$ 1734/MT
- Specific Gravity: 0.940 g/cc
- Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 67
- Tensile Strength at Break: 6.03 MPa
- Elongation at Break: 330 %
$ 1647/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.020 cm/cm
- Melt Flow: 0.200 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 75
- Tensile Strength at Break: 13.1 MPa
$ 1878/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 18.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 10.3 MPa
- Tensile Stress: 4.83 MPa @Strain 300 %
$ 1844/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 27.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 38
- Tensile Strength at Break: 5.86 MPa
- Tensile Stress: 2.07 MPa @Strain 300 %
$ 1900/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 14.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 70
- Tensile Strength: 5.86 MPa
- Elongation at Break: 700 %
$ 1956/MT
- Density: 0.960 g/cc
- Viscosity: 321000 cP @Shear Rate 206 1/s, Temperature 200 °C
- Hardness, Shore A: 53
- Hardness, Shore A: 56
- Tensile Strength at Break: 3.60 MPa
$ 1907/MT
- Specific Gravity: 1.13 g/cc
- Melt Flow: 6.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 75
- Tensile Strength at Break: 11.0 MPa
- Elongation at Break: 820 %
$ 2046/MT
- Specific Gravity: 1.12 g/cc
- Hardness, Shore A: 45
- Tensile Strength, Yield: 2.55 MPa
- Tensile Strength, Yield: 8.48 MPa
- Elongation at Break: 360 %
$ 2129/MT
- Specific Gravity: 1.09 g/cc
- Melt Flow: 12.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 70
- Tensile Strength at Break: 6.89 MPa
- Tensile Stress: 3.10 MPa @Strain 300 %
$ 1664/MT
- Specific Gravity: 1.19 g/cc
- Melt Flow: 5.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 7.93 MPa
- Elongation at Break: 550 %
$ 1642/MT
- Specific Gravity: 0.980 g/cc
- Melt Flow: 5.80 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 50
- Hardness, Shore D: 55
- Tensile Strength at Break: 17.5 MPa
$ 2105/MT
- Specific Gravity: 1.00 g/cc
- Melt Flow: 0.200 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 70
- Tensile Strength at Break: 6.00 MPa
- Elongation at Break: 670 %
$ 1541/MT
- Density: 0.940 g/cc
- Viscosity: 300000 cP @Shear Rate 206 1/s, Temperature 200 °C
- Hardness, Shore A: 71
- Hardness, Shore A: 73
- Tensile Strength at Break: 5.20 MPa
$ 1563/MT
- Specific Gravity: 1.02 g/cc
- Melt Flow: 1.50 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 53
- Tensile Strength at Break: 7.93 MPa
- Tensile Stress: 3.45 MPa @Strain 300 %
$ 2272/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 48
- Tensile Strength at Break: 6.55 MPa
- Elongation at Break: 650 %
$ 2039/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 65.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 20
- Tensile Strength at Break: 2.76 MPa
- Tensile Strength, Yield: 1.03 MPa @Strain 300 %
- Elongation at Break: 800 %
$ 1698/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 1.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 37
- Tensile Strength at Break: 8.27 MPa
- Tensile Stress: 2.07 MPa @Strain 300 %
$ 2565/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 4.50 g/10 min @Load 5.00 kg, Temperature 200 °C
- Tensile Strength at Break: 14.5 MPa
- Tensile Stress: 5.52 MPa @Strain 300 %
$ 1784/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 20.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 62
- Tensile Strength at Break: 5.17 MPa
- Tensile Stress: 3.62 MPa @Strain 300 %
$ 1710/MT
- Melt Flow: 0.100 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 55
- Hardness, Shore A: 60
- Tensile Strength at Break: 3.86 MPa
- Tensile Stress: 2.14 MPa @Strain 100 %
$ 1607/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 55
- Tensile Strength at Break: 10.0 MPa
- Elongation at Break: 630 %
$ 1448/MT
- Specific Gravity: 0.930 g/cc
- Hardness, Shore A: 55
- Tensile Strength: 6.55 MPa
- Elongation at Break: 750 %
$ 1564/MT
- Specific Gravity: 0.900 g/cc
- Melt Density: 0.785 g/cc
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm
- Linear Mold Shrinkage, Flow: 0.012 cm/cm
$ 2071/MT
- Specific Gravity: 1.02 g/cc
- Linear Mold Shrinkage: 0.032 cm/cm
- Linear Mold Shrinkage, Transverse: 0.028 cm/cm
- Melt Flow: 10.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 50
$ 1445/MT
- Density: 0.950 g/cc
- Hardness, Shore A: 80
- Hardness, Shore A: 84
- Tensile Strength at Break: 7.10 MPa
- Tensile Strength at Break: 9.301 MPa
$ 2094/MT
- Specific Gravity: 0.950 g/cc
- Linear Mold Shrinkage: 0.016 cm/cm
- Linear Mold Shrinkage, Transverse: 0.019 cm/cm
- Melt Flow: 16.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 70
$ 1713/MT
- Specific Gravity: 0.920 g/cc
- Melt Flow: 0.100 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 45
- Hardness, Shore A: 50
- Tensile Strength at Break: 3.62 MPa
$ 1651/MT
- Specific Gravity: 0.890 g/cc
- Hardness, Shore A: 52
- Tensile Strength at Break: 11.0 MPa
- Tensile Stress: 3.45 MPa @Strain 300 %
- Elongation at Break: 650 %
$ 1816/MT
- Specific Gravity: 1.28 g/cc
- Melt Flow: 3.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 58
- Tensile Strength: 8.96 MPa
- Elongation at Break: 550 %
$ 2294/MT
- Specific Gravity: 1.17 g/cc
- Melt Flow: 25.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 49
- Tensile Strength at Break: 17.9 MPa
- Elongation at Break: 650 %
$ 1916/MT
- Specific Gravity: 0.920 g/cc
- Melt Flow: 3.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 55
- Tensile Strength at Break: 20.7 MPa
- Tensile Stress: 12.5 MPa @Strain 100 %
$ 1532/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 1.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 86
- Tensile Strength at Break: 20.3 MPa
- Elongation at Break: 630 %
$ 2252/MT
- Density: 0.930 g/cc
- Viscosity: 254000 cP @Shear Rate 206 1/s, Temperature 200 °C
- Hardness, Shore A: 40
- Hardness, Shore A: 46
- Tensile Strength at Break: 2.60 MPa
$ 1605/MT
- Specific Gravity: 0.950 g/cc
- Linear Mold Shrinkage: 0.024 cm/cm
- Linear Mold Shrinkage, Transverse: 0.021 cm/cm
- Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 55
$ 2241/MT
- Specific Gravity: 0.870 g/cc
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 125 °C
- Hardness, Shore OO: 40
- Tensile Strength, Yield: 1.24 MPa
- Elongation at Break: 700 %
- 300% Modulus: 0.000241 GPa
$ 1705/MT
- Specific Gravity: 0.910 g/cc
- Hardness, Shore A: 45
- Tensile Strength: 4.83 MPa
- Elongation at Break: 600 %
$ 1491/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 2.00 g/10 min @Load 2.16 kg, Temperature 150 °C
- Tensile Strength at Break: 3.10 MPa
- Tensile Stress: 0.448 MPa @Strain 300 %
- Elongation at Break: 830 %
$ 1656/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 40.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 45
$ 2271/MT
- Specific Gravity: 1.00 g/cc
- Melt Flow: 40.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 90
- Tensile Strength at Break: 13.1 MPa
- Tensile Stress: 6.21 MPa @Strain 300 %
$ 2040/MT
- Specific Gravity: 0.920 g/cc
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 15
- Tensile Strength, Yield: 1.65 MPa
- Elongation at Break: 300 %
$ 2094/MT
- Specific Gravity: 0.910 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 25
- Tensile Strength, Yield: 2.28 MPa
- Elongation at Break: 375 %
$ 1667/MT
- Specific Gravity: 0.970 g/cc
- Hardness, Shore D: 40
- Tensile Strength, Yield: 12.8 MPa
- Elongation at Break: 500 %
- 100% Modulus: 0.00862 GPa
$ 1509/MT
- Specific Gravity: 0.930 g/cc
- Hardness, Shore A: 45
- Tensile Strength, Yield: 2.48 MPa
- Elongation at Break: 290 %
- 100% Modulus: 0.00117 GPa
$ 2574/MT
- Specific Gravity: 0.980 g/cc
- Hardness, Shore D: 47
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Break: 625 %
- 100% Modulus: 0.0121 GPa
$ 1489/MT
- Specific Gravity: 0.960 g/cc
- Hardness, Shore A: 55
- Tensile Strength, Yield: 3.72 MPa
- Elongation at Break: 300 %
- 100% Modulus: 0.00207 GPa
$ 1504/MT
- Specific Gravity: 0.970 g/cc
- Hardness, Shore A: 64
- Tensile Strength, Yield: 4.83 MPa
- Elongation at Break: 300 %
- 100% Modulus: 0.00276 GPa
$ 1647/MT
- Specific Gravity: 0.920 g/cc
- Melt Flow: 0.500 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 69
- Tensile Strength at Break: 5.65 MPa
- Elongation at Break: 280 %
$ 1550/MT
- Specific Gravity: 0.960 g/cc
- Hardness, Shore A: 73
- Tensile Strength, Yield: 6.55 MPa
- Elongation at Break: 380 %
- 100% Modulus: 0.00359 GPa
$ 1488/MT
- Specific Gravity: 0.960 g/cc
- Hardness, Shore A: 87
- Tensile Strength, Yield: 8.96 MPa
- Elongation at Break: 440 %
- 100% Modulus: 0.00565 GPa
$ 1523/MT
- Specific Gravity: 0.930 g/cc
- Hardness, Shore D: 40
- Hardness, Shore D: 43
- Tensile Strength, Yield: 14.5 MPa
- Elongation at Break: 500 %
$ 1675/MT
- Specific Gravity: 0.920 g/cc
- Hardness, Shore A: 45
- Hardness, Shore A: 50
- Tensile Strength, Yield: 3.62 MPa
- Elongation at Break: 300 %
$ 1476/MT
- Specific Gravity: 0.930 g/cc
- Hardness, Shore D: 48
- Hardness, Shore D: 55
- Tensile Strength, Yield: 22.8 MPa
- Elongation at Break: 600 %
$ 1807/MT
- Specific Gravity: 0.940 g/cc
- Hardness, Shore A: 55
- Hardness, Shore A: 60
- Tensile Strength, Yield: 3.86 MPa
- Elongation at Break: 300 %
$ 1725/MT
- Specific Gravity: 0.940 g/cc
- Hardness, Shore A: 65
- Hardness, Shore A: 70
- Tensile Strength, Yield: 5.17 MPa
- Elongation at Break: 320 %
$ 1492/MT
- Specific Gravity: 0.940 g/cc
- Hardness, Shore A: 73
- Hardness, Shore A: 79
- Tensile Strength, Yield: 6.76 MPa
- Elongation at Break: 340 %
$ 1541/MT
- Specific Gravity: 0.930 g/cc
- Hardness, Shore A: 89
- Hardness, Shore A: 93
- Tensile Strength, Yield: 11.4 MPa
- Elongation at Break: 400 %
$ 1680/MT
- Specific Gravity: 0.910 g/cc
- Hardness, Shore D: 37
- Tensile Strength, Yield: 3.79 MPa
- Tensile Strength, Yield: 13.1 MPa
- Tensile Strength, Yield: 13.1 MPa
$ 2320/MT
- Specific Gravity: 0.910 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Yield: 3.79 MPa
- Tensile Strength, Yield: 8.62 MPa
- Tensile Strength, Yield: 8.62 MPa
$ 2575/MT
- Specific Gravity: 0.932 g/cc
- Melt Flow: 14.0 g/10 min @Load 2.16 kg, Temperature 200 °C
- Hardness, Shore A: 60
- Hardness, Shore A: 63
- Tensile Strength at Break: 4.48 MPa
$ 2135/MT
- Specific Gravity: 1.00 g/cc
- Melt Flow: 3.00 g/10 min @Load 5.00 kg, Temperature 230 °C
- Hardness, Shore A: 69
- Tensile Strength at Break: 9.10 MPa
- Elongation at Break: 350 %
$ 1560/MT
- Specific Gravity: 0.950 g/cc
- Melt Flow: 3.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 64
- Tensile Strength at Break: 6.00 MPa
- Tensile Stress: 3.43 MPa @Strain 100 %
$ 1741/MT
- Specific Gravity: 0.960 g/cc
- Melt Flow: 1.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 75
- Rear Barrel Temperature: 173 - 213 °C
- Middle Barrel Temperature: 179 - 219 °C
$ 1845/MT
- Specific Gravity: 0.892 g/cc
- Melt Flow: 5.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 10
- Tensile Strength at Break: 1.03 MPa
- Elongation at Break: 320 %
$ 1550/MT
- Specific Gravity: 0.910 g/cc
- Melt Flow: 2.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 25
- Tensile Stress: 0.586 MPa @Strain 100 %
- Tensile Strength, Yield: 2.28 MPa
$ 1467/MT
- Specific Gravity: 0.910 g/cc
- Melt Flow: 1.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 35
- Tensile Strength at Break: 2.93 MPa
- Tensile Stress: 0.827 MPa @Strain 100 %
$ 1724/MT
- Specific Gravity: 0.930 g/cc
- Melt Flow: 6.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 70
- Tensile Strength at Break: 7.45 MPa
- Tensile Stress: 4.31 MPa @Strain 100 %
$ 1800/MT
- Specific Gravity: 0.990 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.014 cm/cm
- Hardness, Shore A: 85
- Tensile Strength at Break: 16.5 MPa
$ 1607/MT
- Specific Gravity: 1.24 g/cc
- Melt Flow: 3.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 20
- Tensile Strength at Break: 3.10 MPa
- Elongation at Break: 400 %
$ 1646/MT
- Specific Gravity: 1.43 g/cc
- Melt Flow: 5.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 20
- Tensile Strength at Break: 2.76 MPa
- Elongation at Break: 380 %
$ 1792/MT
- Specific Gravity: 1.43 g/cc
- Melt Flow: 12.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 15
- Tensile Strength at Break: 2.07 MPa
- Elongation at Break: 480 %
$ 1976/MT
- Specific Gravity: 0.970 g/cc
- Melt Flow: 2.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 40
- Tensile Strength at Break: 14.5 MPa
- Elongation at Break: 400 %
$ 1677/MT
- Specific Gravity: 0.920 g/cc
- Melt Flow: 3.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 50
- Tensile Strength at Break: 15.2 MPa
- Elongation at Break: 500 %
$ 1755/MT
- Specific Gravity: 0.970 g/cc
- Melt Flow: 1.30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 40
- Tensile Stress: 19.3 MPa @Strain 100 %
- Tensile Stress: 20.3 MPa @Strain 300 %
$ 1676/MT
- Specific Gravity: 0.930 g/cc
- Melt Flow: 3.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 45
- Tensile Strength, Yield: 3.52 MPa
- Elongation at Break: 310 %
$ 1785/MT
- Specific Gravity: 0.927 g/cc
- Melt Flow: 2.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 73
- Tensile Strength at Break: 7.03 MPa
- Elongation at Break: 310 %
$ 1622/MT
- Specific Gravity: 0.960 g/cc
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 80
- Tensile Stress: 4.83 MPa @Strain 100 %
- Tensile Strength, Yield: 8.27 MPa
$ 1682/MT
- Specific Gravity: 0.950 g/cc
- Melt Flow: 2.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 87
- Tensile Strength at Break: 8.96 MPa
- Elongation at Break: 440 %
$ 1906/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Melt Flow: 10.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore D: 45
$ 1474/MT
- Specific Gravity: 0.900 g/cc
- Linear Mold Shrinkage, Flow: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 90
$ 1729/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 0.500 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 40
- Tensile Strength at Break: 8.27 MPa
- Tensile Stress: 2.07 MPa @Strain 300 %
$ 1935/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.033 cm/cm
- Linear Mold Shrinkage, Transverse: 0.021 cm/cm
- Melt Flow: 6.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 55
$ 1579/MT
- Density: 0.940 g/cc
- Hardness, Shore A: 90
- Hardness, Shore A: 93
- Tensile Strength at Break: 11.50 MPa
- Tensile Strength at Break: 13.50 MPa
$ 1513/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 1.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 62
- Tensile Strength at Break: 25.9 MPa
- Elongation at Break: 200 %
$ 1564/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 14.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 82
- Tensile Strength at Break: 20.7 MPa
- Elongation at Break: 700 %
$ 1719/MT
- Specific Gravity: 0.930 g/cc
- Melt Flow: 2.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 80
- Tensile Strength at Break: 8.27 MPa
- Elongation at Break: 350 %
$ 1559/MT
- Specific Gravity: 1.09 g/cc
- Melt Flow: 5.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 73
- Tensile Strength at Break: 13.1 MPa
- Elongation at Break: 650 %
$ 1752/MT
- Specific Gravity: 1.22 g/cc
- Melt Flow: 1.5 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 42
- Tensile Strength, Yield: 4.83 MPa
- Elongation at Break: 700 %
$ 1684/MT
- Specific Gravity: 0.980 g/cc
- Melt Flow: 12.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 55
- Tensile Strength at Break: 16.5 MPa
- Elongation at Break: 500 %
$ 1598/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 1.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 30
- Tensile Strength at Break: 5.17 MPa
- Tensile Stress: 1.55 MPa @Strain 300 %
$ 1706/MT
- Specific Gravity: 1.29 g/cc
- Melt Flow: 1.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 53
- Tensile Strength at Break: 8.27 MPa
- Elongation at Break: 530 %
$ 2099/MT
- Specific Gravity: 1.15 g/cc
- Linear Mold Shrinkage: 0.010 - 0.025 cm/cm
- Hardness, Shore A: 65
- Tensile Strength, Yield: 5.24 MPa
- Tensile Strength, Yield: 14.5 MPa
$ 2131/MT
- Specific Gravity: 0.980 g/cc
- Melt Flow: 13.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 92
- Tensile Strength, Yield: 9.349 MPa
- Tensile Strength, Yield: 10.91 MPa
$ 2242/MT
- Specific Gravity: 1.00 g/cc
- Linear Mold Shrinkage: 0.020 cm/cm
- Melt Flow: 15 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 45
- Tensile Strength, Yield: 6.89 MPa
$ 1530/MT
- Specific Gravity: 1.00 g/cc
- Linear Mold Shrinkage: 0.020 cm/cm
- Melt Flow: 15 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 45
- Tensile Strength, Yield: 6.89 MPa
$ 1558/MT
- Specific Gravity: 1.00 g/cc
- Linear Mold Shrinkage: 0.020 cm/cm
- Melt Flow: 15 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 45
- Tensile Strength, Yield: 6.89 MPa
$ 1549/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 4.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 35
- Tensile Strength at Break: 5.52 MPa
- Tensile Stress: 1.21 MPa @Strain 300 %
$ 1482/MT
- Specific Gravity: 0.940 g/cc
- Melt Flow: 1.90 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 35
- Hardness, Shore D: 44
- Tensile Strength at Break: 14.6 MPa
$ 1976/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 7.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 80
- Tensile Strength at Break: 7.58 MPa
- Tensile Stress: 4.83 MPa @Strain 300 %
$ 1961/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 2.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 50
- Tensile Strength at Break: 6.55 MPa
- Elongation at Break: 650 %
$ 1663/MT
- Specific Gravity: 1.11 g/cc
- Melt Flow: 1.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 87
- Tensile Strength at Break: 12.1 MPa
- Elongation at Break: 700 %
$ 1667/MT
- Specific Gravity: 1.26 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Yield: 19.5 MPa
- Elongation at Break: 270 %
- Brittleness Temperature: -29.0 °C
$ 2565/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 32.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 64
- Tensile Strength at Break: 6.55 MPa
- Elongation at Break: 750 %
$ 2057/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 1.50 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 64
- Tensile Strength at Break: 11.7 MPa
- Elongation at Break: 600 %
$ 2127/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.016 cm/cm
- Melt Flow: 0.500 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 57
- Tensile Strength at Break: 5.86 MPa
$ 1589/MT
- Density: 0.950 g/cc
- Viscosity: 310000 cP @Shear Rate 206 1/s, Temperature 200 °C
- Hardness, Shore A: 80
- Hardness, Shore A: 84
- Tensile Strength at Break: 7.10 MPa
$ 2475/MT
- Specific Gravity: 1.00 g/cc
- Linear Mold Shrinkage: 0.020 cm/cm
- Melt Flow: 15 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 45
- Tensile Strength, Yield: 6.89 MPa
$ 1838/MT
- Specific Gravity: 1.00 g/cc
- Linear Mold Shrinkage: 0.020 cm/cm
- Melt Flow: 15 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 45
- Tensile Strength, Yield: 6.89 MPa
$ 2076/MT
- Specific Gravity: 1.00 g/cc
- Linear Mold Shrinkage: 0.020 cm/cm
- Melt Flow: 15 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 45
- Tensile Strength, Yield: 6.89 MPa
$ 1845/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 45
- Tensile Strength at Break: 8.96 MPa
- Tensile Strength, Yield: 2.76 MPa @Strain 300 %
- Elongation at Break: 700 %
$ 1516/MT
- Specific Gravity: 0.970 g/cc
- Melt Flow: 35.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 40
- Tensile Strength at Break: 4.83 MPa
- Tensile Stress: 1.38 MPa @Strain 300 %
$ 1937/MT
- Specific Gravity: 1.16 g/cc
- Melt Flow: 14.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 80
- Tensile Strength at Break: 12.1 MPa
- Elongation at Break: 650 %
$ 1996/MT
- Specific Gravity: 1.09 g/cc
- Melt Flow: 2.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 73
- Tensile Strength at Break: 13.5 MPa
- Elongation at Break: 680 %
$ 2252/MT
- Specific Gravity: 1.02 g/cc
- Hardness, Shore A: 65
- Tensile Strength: 8.96 MPa
- Elongation at Break: 700 %
$ 1725/MT
- Specific Gravity: 1.02 g/cc
- Hardness, Shore A: 65
- Tensile Strength: 8.96 MPa
- Elongation at Break: 700 %
$ 1814/MT
- Specific Gravity: 0.910 g/cc
- Melt Flow: 5.4 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 70
- Tensile Strength, Yield: 9.205 MPa
- Elongation at Break: 745 %
$ 1463/MT
- Density: 0.940 g/cc
- Hardness, Shore A: 90
- Hardness, Shore A: 93
- Tensile Strength at Break: 11.50 MPa
- Tensile Strength at Break: 13.50 MPa
$ 1672/MT
- Specific Gravity: 0.900 g/cc
- Linear Mold Shrinkage: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.016 cm/cm
- Melt Flow: 0.700 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 67
$ 1722/MT
- Specific Gravity: 1.02 g/cc
- Melt Flow: 12.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 50
- Tensile Strength: 4.48 MPa
- Elongation at Break: 900 %
$ 1746/MT
- Specific Gravity: 0.920 g/cc
- Melt Flow: 10.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 65
- Tensile Strength at Break: 6.21 MPa
- Tensile Stress: 3.45 MPa @Strain 300 %
$ 1630/MT
- Specific Gravity: 1.05 g/cc
- Linear Mold Shrinkage: 0.016 cm/cm
- Linear Mold Shrinkage, Transverse: 0.017 cm/cm
- Melt Flow: 21.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 54.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1491/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 1.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 80
- Tensile Strength at Break: 11.4 MPa
- Elongation at Break: 640 %
$ 1762/MT
- Specific Gravity: 1.02 g/cc
- Melt Flow: 15.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 90
- Tensile Strength: 11.6 MPa
- Elongation at Break: 860 %
$ 2346/MT
- Specific Gravity: 1.00 g/cc
- Melt Flow: 1.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 50
- Tensile Strength at Break: 16.5 MPa
- Elongation at Break: 600 %
$ 2314/MT
- Density: 0.940 g/cc
- Viscosity: 458000 cP @Shear Rate 206 1/s, Temperature 200 °C
- Hardness, Shore D: 47
- Hardness, Shore D: 51
- Tensile Strength at Break: 18.40 MPa
$ 1955/MT
- Specific Gravity: 1.15 g/cc
- Melt Flow: 1.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 54
- Tensile Strength at Break: 10.3 MPa
- Elongation at Break: 550 %
$ 2166/MT
- Specific Gravity: 1.01 g/cc
- Melt Flow: 11.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore D: 65
- Tensile Strength at Break: 24.8 MPa
- Elongation at Break: 1.8 %
$ 1494/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 1.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 12.8 MPa
- Elongation at Break: 380 %
$ 1553/MT
- Specific Gravity: 0.960 g/cc
- Melt Flow: 0.900 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 65
- Tensile Strength at Break: 8.96 MPa
- Elongation at Break: 750 %
$ 2089/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 4.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 35
- Tensile Strength at Break: 8.27 MPa
- Tensile Strength, Yield: 1.72 MPa @Strain 300 %
- Elongation at Break: 600 %
$ 1812/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 40.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 8.48 MPa
- Elongation at Break: 500 %
$ 1738/MT
- Specific Gravity: 1.00 g/cc
- Melt Flow: 1.10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 64
- Tensile Strength at Break: 6.07 MPa
- Elongation at Break: 960 %
$ 1754/MT
- Specific Gravity: 1.30 g/cc
- Melt Flow: 1.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore C: 82
- Tensile Strength at Break: 12.3 MPa
- Elongation at Break: 600 %
$ 2432/MT
- Specific Gravity: 0.900 g/cc
- Linear Mold Shrinkage: 0.013 cm/cm
- Melt Flow: 1.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 70
- Tensile Strength at Break: 8.62 MPa
$ 1644/MT
- Specific Gravity: 1.16 g/cc
- Melt Flow: 10.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 70
- Tensile Strength at Break: 6.89 MPa
- Tensile Strength, Yield: 2.76 MPa @Strain 300 %
- Elongation at Break: 700 %
$ 1711/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 12.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 32
- Tensile Strength at Break: 6.89 MPa
- Tensile Stress: 2.21 MPa @Strain 300 %
$ 1448/MT
- Specific Gravity: 0.920 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 55
- Tensile Strength, Yield: 5.52 MPa
- Elongation at Break: 600 %
$ 2236/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 10.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 38
- Tensile Strength at Break: 4.14 MPa
- Tensile Strength, Yield: 2.07 MPa @Strain 300 %
- Elongation at Break: 650 %
$ 1466/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 0.500 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 88
- Tensile Strength at Break: 12.4 MPa
- Elongation at Break: 500 %
$ 1792/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 1.50 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 55
- Tensile Strength at Break: 11.7 MPa
- Tensile Stress: 4.14 MPa @Strain 300 %
$ 1721/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 3.10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 60
- Tensile Strength at Break: 9.24 MPa
- Elongation at Break: 880 %
$ 2117/MT
- Specific Gravity: 1.13 g/cc
- Hardness, Shore A: 50
- Tensile Strength, Yield: 3.17 MPa
- Tensile Strength, Yield: 9.72 MPa
- Elongation at Break: 360 %
$ 1446/MT
- Specific Gravity: 1.00 g/cc
- Linear Mold Shrinkage: 0.020 cm/cm
- Melt Flow: 15 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 45
- Tensile Strength, Yield: 6.89 MPa
$ 1869/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 8.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 41
- Tensile Strength at Break: 3.45 MPa
- Elongation at Break: 730 %
$ 2066/MT
- Specific Gravity: 1.23 g/cc
- Melt Flow: 6.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore C: 82
- Tensile Strength at Break: 11.0 MPa
- Elongation at Break: 460 %
$ 2528/MT
- Specific Gravity: 1.23 g/cc
- Melt Flow: 6.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore C: 82
- Tensile Strength at Break: 11.0 MPa
- Elongation at Break: 460 %
$ 1662/MT
- Specific Gravity: 1.23 g/cc
- Melt Flow: 6.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore C: 82
- Tensile Strength at Break: 11.0 MPa
- Elongation at Break: 460 %
$ 2221/MT
- Specific Gravity: 1.23 g/cc
- Melt Flow: 6.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore C: 82
- Tensile Strength at Break: 11.0 MPa
- Elongation at Break: 460 %
$ 1728/MT
- Specific Gravity: 1.23 g/cc
- Melt Flow: 6.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore C: 82
- Tensile Strength at Break: 11.0 MPa
- Elongation at Break: 460 %
$ 1666/MT
- Specific Gravity: 1.23 g/cc
- Melt Flow: 6.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore C: 82
- Tensile Strength at Break: 11.0 MPa
- Elongation at Break: 460 %
$ 1548/MT
- Specific Gravity: 1.23 g/cc
- Melt Flow: 6.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore C: 82
- Tensile Strength at Break: 11.0 MPa
- Elongation at Break: 460 %
$ 1930/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 18 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 40
- Tensile Strength, Yield: 8.27 MPa
- Elongation at Break: 600 %
$ 1521/MT
- Specific Gravity: 1.28 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Yield: 19.7 MPa
- Elongation at Break: 370 %
- Brittleness Temperature: -25.0 °C
$ 1532/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 12.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 36
- Hardness, Shore OO: 50
- Tensile Strength at Break: 7.24 MPa
$ 2190/MT
- Specific Gravity: 0.980 g/cc
- Melt Flow: 1.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 90
- Hardness, Shore A: 94
- Tensile Strength at Break: 8.07 MPa
$ 1976/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Melt Flow: 17.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 57.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1996/MT
- Specific Gravity: 1.00 g/cc
- Linear Mold Shrinkage: 0.033 cm/cm
- Linear Mold Shrinkage, Transverse: 0.026 cm/cm
- Melt Flow: 0.400 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 65
$ 1689/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 10.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 80
- Tensile Strength: 11.7 MPa
- Elongation at Break: 700 %
$ 2240/MT
- Specific Gravity: 1.11 g/cc
- Melt Flow: 7.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 53
- Tensile Strength at Break: 4.27 MPa
- Elongation at Break: 700 %
$ 1469/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 20.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 78
- Tensile Strength at Break: 17.2 MPa
- Tensile Stress: 6.89 MPa @Strain 300 %
$ 1547/MT
- Specific Gravity: 1.24 g/cc
- Linear Mold Shrinkage: 0.010 - 0.025 cm/cm
- Hardness, Shore A: 70
- Tensile Strength, Yield: 7.58 MPa
- Tensile Strength, Yield: 16.4 MPa
$ 1658/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 5.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 76
- Tensile Strength at Break: 15.9 MPa
- Tensile Stress: 5.52 MPa @Strain 300 %
$ 1672/MT
- Specific Gravity: 1.02 g/cc
- Melt Flow: 11.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 71
- Tensile Strength: 5.93 MPa
- Elongation at Break: 890 %
$ 1519/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 0.500 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 44
- Tensile Strength at Break: 4.83 MPa
$ 1476/MT
- Specific Gravity: 1.16 g/cc
- Melt Flow: 3.0 g/10 min
- Hardness, Shore A: 42
- Tensile Strength at Break: 4.14 MPa
- Tensile Stress: 0.896 MPa @Strain 100 %
$ 2112/MT
- Specific Gravity: 1.11 g/cc
- Melt Flow: 24 g/10 min @Load 5.00 kg, Temperature 177 °C
- Hardness, Shore A: 50
- Tensile Strength, Yield: 5.93 MPa
- Tensile Strength, Yield: 9.487 MPa
$ 1536/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 5.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 55
- Tensile Strength at Break: 10.1 MPa
- Tensile Stress: 3.31 MPa @Strain 300 %
$ 2283/MT
- Specific Gravity: 1.12 g/cc
- Melt Flow: 40.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 69
- Tensile Strength at Break: 3.62 MPa
- Elongation at Break: 280 %
$ 1771/MT
- Specific Gravity: 1.18 g/cc
- Hardness, Shore A: 70
- Tensile Strength, Yield: 7.24 MPa
- Tensile Strength, Yield: 16.5 MPa
- Tensile Strength, Yield: 17.9 MPa
$ 1514/MT
- Specific Gravity: 1.04 g/cc
- Linear Mold Shrinkage: 0.016 cm/cm
- Melt Flow: 16.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 60
- Hardness, Shore D: 70
$ 1815/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 42
- Tensile Strength at Break: 8.27 MPa
- Tensile Strength, Yield: 2.76 MPa @Strain 300 %
- Elongation at Break: 700 %
$ 1582/MT
- Specific Gravity: 1.06 g/cc
- Melt Flow: 4.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 65
- Tensile Strength at Break: 6.89 MPa
- Tensile Stress: 4.14 MPa @Strain 300 %
$ 1518/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 10.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 83
- Tensile Strength at Break: 6.55 MPa
- Elongation at Break: 600 %
$ 1538/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 12.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 32
- Tensile Strength at Break: 5.52 MPa
- Elongation at Break: 600 %
$ 2382/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 2.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 55
- Tensile Strength at Break: 9.17 MPa
- Elongation at Break: 920 %
$ 1479/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 4.50 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 70
- Tensile Strength at Break: 14.5 MPa
- Tensile Stress: 5.52 MPa @Strain 300 %
$ 1868/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 30.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 58
- Tensile Strength at Break: 8.48 MPa
- Tensile Stress: 3.45 MPa @Strain 300 %
$ 1494/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 0.200 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 83
- Tensile Strength at Break: 11.0 MPa
- Elongation at Break: 640 %
$ 2091/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 8.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 82
- Tensile Strength at Break: 19.3 MPa
- Tensile Stress: 8.96 MPa @Strain 300 %
$ 1705/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 1.50 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 55
- Tensile Strength at Break: 11.7 MPa
- Tensile Stress: 4.14 MPa @Strain 300 %
$ 1527/MT
- Specific Gravity: 1.01 g/cc
- Melt Flow: 17.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 80
- Tensile Strength at Break: 7.93 MPa
- Elongation at Break: 550 %
$ 1770/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 35.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 75
- Tensile Strength at Break: 8.14 MPa
- Elongation at Break: 700 %
$ 1595/MT
- Specific Gravity: 1.16 g/cc
- Melt Flow: 1.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 42
- Tensile Strength at Break: 4.21 MPa
- Tensile Stress: 0.758 MPa @Strain 100 %
$ 1616/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 0.500 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 77
- Tensile Strength at Break: 13.8 MPa
- Tensile Stress: 6.21 MPa @Strain 300 %
$ 1961/MT
- Specific Gravity: 0.920 g/cc
- Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 42
- Tensile Strength at Break: 8.62 MPa
- Tensile Stress: 2.41 MPa @Strain 300 %
$ 1702/MT
- Specific Gravity: 0.940 g/cc
- Melt Flow: 15.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 50
- Tensile Strength at Break: 3.59 MPa
- Elongation at Break: 330 %
$ 1552/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 75
- Tensile Strength, Yield: 8.41 MPa
- Tensile Strength, Yield: 16.7 MPa
- Elongation at Break: 370 %
$ 1851/MT
- Specific Gravity: 1.11 g/cc
- Hardness, Shore A: 45
- Tensile Strength, Yield: 8.55 MPa
- Elongation at Break: 280 %
- Compression Set: 32 %
$ 1944/MT
- Specific Gravity: 1.14 g/cc
- Melt Flow: 1.40 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 95
- Hardness, Shore A: 96
- Tensile Strength at Break: 10.8 MPa
$ 1651/MT
- Specific Gravity: 0.900 g/cc
- Linear Mold Shrinkage, Flow: 0.016 cm/cm
- Linear Mold Shrinkage, Flow: 0.019 cm/cm
- Linear Mold Shrinkage, Transverse: 0.015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.016 cm/cm
$ 1516/MT
- Specific Gravity: 1.31 g/cc
- Melt Flow: 7.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 89
- Tensile Strength at Break: 6.76 MPa
- Elongation at Break: 770 %
$ 1844/MT
- Specific Gravity: 1.10 g/cc
- Melt Flow: 20.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 49
- Tensile Strength at Break: 9.65 MPa
- Elongation at Break: 600 %
$ 2338/MT
- Specific Gravity: 1.12 g/cc
- Linear Mold Shrinkage: 0.010 - 0.025 cm/cm
- Hardness, Shore A: 55
- Tensile Strength, Yield: 3.79 MPa
- Tensile Strength, Yield: 11.7 MPa
$ 1729/MT
- Density: 0.940 g/cc
- Hardness, Shore D: 38
- Hardness, Shore D: 41
- Tensile Strength at Break: 14.60 MPa
- Tensile Strength at Break: 16.2 MPa
$ 1567/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 2.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 25.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 72
- Tensile Strength at Break: 8.27 MPa
$ 2280/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 1.20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 50
- Tensile Strength at Break: 16.5 MPa
- Elongation at Break: 550 %
$ 2191/MT
- Specific Gravity: 0.880 g/cc
- Linear Mold Shrinkage: 0.045 cm/cm
- Melt Flow: 10.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 10
- Tensile Strength at Break: 1.38 MPa
$ 1881/MT
- Density: 0.960 g/cc
- Viscosity: 349000 cP @Shear Rate 206 1/s, Temperature 200 °C
- Hardness, Shore A: 63
- Hardness, Shore A: 65
- Tensile Strength at Break: 4.70 MPa
$ 1445/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.014 cm/cm
- Linear Mold Shrinkage, Transverse: 0.015 cm/cm
- Melt Flow: 70.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 55
$ 1716/MT
- Specific Gravity: 1.07 g/cc
- Hardness, Shore A: 55
- Tensile Strength: 6.38 MPa
- Elongation at Break: 880 %
$ 1672/MT
- Specific Gravity: 1.31 g/cc
- Melt Flow: 31.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 70
- Tensile Strength: 8.96 MPa
- Elongation at Break: 550 %
$ 1500/MT
- Density: 0.940 g/cc
- Hardness, Shore A: 54
- Hardness, Shore A: 57
- Tensile Strength at Break: 3.30 MPa
- Tensile Strength at Break: 4.70 MPa
$ 1590/MT
- Specific Gravity: 0.920 g/cc
- Melt Flow: 3.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 55
- Tensile Strength at Break: 20.7 MPa
- Tensile Stress: 12.5 MPa @Strain 100 %
$ 1498/MT
- Specific Gravity: 0.950 g/cc
- Melt Flow: 6.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 75
- Tensile Strength at Break: 8.83 MPa
- Tensile Stress: 6.55 MPa @Strain 300 %
$ 1656/MT
- Specific Gravity: 1.01 g/cc
- Melt Flow: 8.50 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 77
- Tensile Strength at Break: 11.0 MPa
- Tensile Stress: 4.83 MPa @Strain 300 %
$ 1675/MT
- Specific Gravity: 1.05 g/cc
- Melt Flow: 10.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 73
- Tensile Strength at Break: 7.58 MPa
- Tensile Stress: 2.59 MPa @Strain 300 %
$ 1762/MT
- Density: 0.950 g/cc
- Viscosity: 391000 cP @Shear Rate 206 1/s, Temperature 200 °C
- Hardness, Shore D: 39
- Hardness, Shore D: 40
- Tensile Strength at Break: 16.10 MPa
$ 1572/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 12.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 70
- Tensile Strength at Break: 6.89 MPa
- Tensile Stress: 3.45 MPa @Strain 300 %
$ 2061/MT
- Density: 0.960 g/cc
- Viscosity: 356000 cP @Shear Rate 206 1/s, Temperature 200 °C
- Hardness, Shore A: 72
- Hardness, Shore A: 75
- Tensile Strength at Break: 5.90 MPa
$ 2288/MT
- Specific Gravity: 1.13 g/cc
- Melt Flow: 22.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 55
- Tensile Strength at Break: 6.21 MPa
- Elongation at Break: 700 %
$ 1488/MT
- Specific Gravity: 0.930 g/cc
- Melt Flow: 5.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 55
- Tensile Strength at Break: 3.93 MPa
- Elongation at Break: 630 %
$ 1498/MT
- Specific Gravity: 1.02 g/cc
- Melt Flow: 23.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 60
- Hardness, Shore A: 65
- Tensile Strength at Break: 4.83 MPa
$ 1541/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 37.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 80
- Tensile Strength at Break: 8.83 MPa
- Elongation at Break: 650 %
$ 2345/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 1.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 45
- Tensile Strength at Break: 8.62 MPa
$ 1823/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 2.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 55
- Tensile Strength at Break: 11.7 MPa
- Elongation at Break: 650 %
$ 1886/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 1.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 70
- Tensile Strength at Break: 14.5 MPa
$ 1805/MT
- Specific Gravity: 1.30 g/cc
- Melt Flow: 18.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 82
- Tensile Strength: 10.3 MPa
- Elongation at Break: 550 %
$ 1919/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 2.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 80
- Tensile Strength at Break: 8.62 MPa
- Elongation at Break: 700 %
$ 1794/MT
- Specific Gravity: 0.930 g/cc
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 73
- Tensile Strength at Break: 7.17 MPa
- Elongation at Break: 320 %
$ 1870/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.020 cm/cm
- Melt Flow: 1.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 48
- Tensile Strength at Break: 7.58 MPa
$ 1582/MT
- Specific Gravity: 0.962 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 55
- Tensile Strength at Break: 17.6 MPa
$ 1759/MT
- Specific Gravity: 1.09 g/cc
- Hardness, Shore A: 40
- Tensile Strength, Yield: 6.96 MPa
- Elongation at Break: 300 %
- Compression Set: 32 %
$ 1685/MT
- Density: 0.950 g/cc
- Hardness, Shore A: 87
- Hardness, Shore A: 91
- Tensile Strength at Break: 13.00 MPa
- Tensile Strength at Break: 14.80 MPa
$ 1750/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 27.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 20
- Tensile Strength at Break: 3.45 MPa
- Tensile Stress: 0.689 MPa @Strain 300 %
$ 1514/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 40.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 90
- Tensile Strength at Break: 9.31 MPa
- Elongation at Break: 500 %
$ 1601/MT
- Specific Gravity: 1.26 g/cc
- Melt Flow: 25.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 70
- Tensile Strength at Break: 8.41 MPa
- Elongation at Break: 680 %
$ 1775/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 25.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 60
- Tensile Strength at Break: 6.21 MPa
- Tensile Stress: 1.03 MPa @Strain 300 %
$ 1973/MT
- Specific Gravity: 1.15 g/cc
- Melt Flow: 25.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 75
- Tensile Strength at Break: 6.89 MPa
- Tensile Stress: 2.76 MPa @Strain 300 %
$ 2052/MT
- Specific Gravity: 0.950 g/cc
- Melt Flow: 7.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 55
- Hardness, Shore A: 60
- Hardness, Shore A: 60
$ 1941/MT
- Specific Gravity: 1.02 g/cc
- Melt Flow: 1.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 65
- Tensile Strength at Break: 11.7 MPa
- Elongation at Break: 680 %
$ 1595/MT
- Density: 0.960 g/cc
- Hardness, Shore A: 44
- Hardness, Shore A: 48
- Tensile Strength at Break: 2.70 MPa
- Tensile Strength at Break: 4.00 MPa
$ 2027/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 0.500 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 79
- Tensile Strength at Break: 7.58 MPa
- Elongation at Break: 450 %
$ 1468/MT
- Specific Gravity: 0.902 g/cc
- Hardness, Shore D: 65
- Tensile Strength at Break: 27.6 MPa
- Elongation at Break: 650 %
- Rear Barrel Temperature: 171 - 193 °C
$ 1583/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 16.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 50
- Tensile Strength at Break: 6.89 MPa
- Tensile Stress: 1.41 MPa @Strain 100 %
$ 1963/MT
- Specific Gravity: 0.930 g/cc
- Melt Flow: 1.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 50
- Tensile Strength at Break: 22.8 MPa
- Elongation at Break: 600 %
$ 1563/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 15.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 19
- Tensile Strength at Break: 3.45 MPa
- Elongation at Break: 650 %
$ 1840/MT
- Specific Gravity: 1.15 g/cc
- Hardness, Shore A: 55
- Tensile Strength, Yield: 3.79 MPa
- Tensile Strength, Yield: 11.0 MPa
- Elongation at Break: 380 %
$ 2514/MT
- Specific Gravity: 0.960 g/cc
- Linear Mold Shrinkage: 0.020 cm/cm
- Melt Flow: 5.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 65
- Tensile Strength, Yield: 8.96 MPa
$ 1648/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 1.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 62
- Tensile Strength at Break: 4.21 MPa
- Elongation at Break: 720 %
$ 1546/MT
- Specific Gravity: 1.16 g/cc
- Melt Flow: 0.500 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 45
- Tensile Strength at Break: 4.55 MPa
- Tensile Stress: 0.862 MPa @Strain 100 %
$ 1964/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 31.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 60
- Tensile Strength at Break: 7.58 MPa
- Elongation at Break: 550 %
$ 1663/MT
- Specific Gravity: 0.980 g/cc
- Melt Flow: 30.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 8.27 MPa
- Elongation at Break: 600 %
$ 1657/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 1.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 78
- Tensile Strength at Break: 7.58 MPa
- Elongation at Break: 450 %
$ 1864/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 27.0 g/10 min @Load 2.16 kg, Temperature 150 °C
- Hardness, Shore A: 55
- Tensile Strength at Break: 2.76 MPa
- Tensile Strength, Yield: 0.414 MPa @Strain 300 %
- Elongation at Break: 700 %
$ 1904/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.026 cm/cm
- Linear Mold Shrinkage: 0.031 cm/cm
- Melt Flow: 0.500 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 58
$ 2492/MT
- Specific Gravity: 0.920 g/cc
- Melt Flow: 19.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 68
- Tensile Strength at Break: 7.72 MPa
- Elongation at Break: 400 %
$ 2025/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 60
- Tensile Strength, Yield: 8.83 MPa
- Elongation at Break: 725 %
$ 1663/MT
- Specific Gravity: 0.940 g/cc
- Melt Flow: 0.200 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 78
- Tensile Strength: 6.89 MPa
- Elongation at Break: 545 %
$ 2088/MT
- Specific Gravity: 0.900 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 15.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 82
- Tensile Strength at Break: 9.65 MPa
$ 1858/MT
- Specific Gravity: 1.17 g/cc
- Melt Flow: 14.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 80
- Tensile Strength at Break: 11.7 MPa
- Elongation at Break: 600 %
$ 1673/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 2.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 44
- Tensile Strength at Break: 6.89 MPa
- Tensile Stress: 2.76 MPa @Strain 300 %
$ 1757/MT
- Specific Gravity: 1.07 g/cc
- Melt Flow: 5.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 50
- Tensile Strength at Break: 4.14 MPa
- Tensile Stress: 2.62 MPa @Strain 300 %
$ 2445/MT
- Specific Gravity: 0.892 g/cc
- Melt Flow: 15.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 80
- Tensile Strength at Break: 12.4 MPa
- Tensile Stress: 6.89 MPa @Strain 300 %
$ 1557/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 20.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 62
- Tensile Strength at Break: 6.89 MPa
- Elongation at Break: 650 %
$ 1470/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 24.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 54
- Tensile Strength at Break: 8.62 MPa
- Elongation at Break: 750 %
$ 2320/MT
- Specific Gravity: 1.09 g/cc
- Melt Flow: 0.200 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 75
- Tensile Strength at Break: 6.89 MPa
- Tensile Stress: 2.28 MPa @Strain 100 %
$ 1486/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 10.0 g/10 min @Load 5.00 kg, Temperature 250 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 37.7 MPa
- Elongation at Break: 540 %
$ 2082/MT
- Specific Gravity: 1.13 g/cc
- Melt Flow: 12.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 77
- Tensile Strength at Break: 7.24 MPa
- Elongation at Break: 550 %
$ 2217/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 17.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 67
- Tensile Strength at Break: 9.65 MPa
- Tensile Strength, Yield: 4.83 MPa @Strain 300 %
- Elongation at Break: 600 %
$ 1486/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 5.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 60
- Tensile Strength at Break: 10.0 MPa
- Tensile Stress: 3.28 MPa @Strain 300 %
$ 2252/MT
- Specific Gravity: 0.960 g/cc
- Melt Flow: 5.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 58
- Tensile Strength at Break: 8.96 MPa
- Elongation at Break: 650 %
$ 1448/MT
- Specific Gravity: 1.14 g/cc
- Hardness, Shore A: 55
- Tensile Strength, Yield: 4.00 MPa
- Tensile Strength, Yield: 10.2 MPa
- Tensile Strength, Yield: 12.8 MPa
$ 1486/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 12.0 g/10 min @Load 2.16 kg, Temperature 175 °C
- Hardness, Shore A: 60
- Tensile Strength at Break: 6.31 MPa
- Elongation at Break: 760 %
$ 1805/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 1.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 45
- Tensile Strength at Break: 7.58 MPa
- Tensile Strength, Yield: 2.76 MPa @Strain 300 %
- Elongation at Break: 700 %
$ 2530/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.013 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Melt Flow: 2.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 70
$ 1808/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 1.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 52
- Tensile Strength at Break: 18.6 MPa
- Elongation at Break: 750 %
$ 2518/MT
- Specific Gravity: 1.00 g/cc
- Melt Flow: 0.300 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 80
- Hardness, Shore A: 85
- Tensile Strength at Break: 6.41 MPa
$ 2387/MT
- Specific Gravity: 1.32 g/cc
- Melt Flow: 11.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 58
- Tensile Strength at Break: 10.0 MPa
- Elongation at Break: 470 %
$ 1930/MT
- Specific Gravity: 2.18 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 12.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 70
- Tensile Strength at Break: 2.76 MPa
$ 2148/MT
- Density: 0.940 g/cc
- Viscosity: 285000 cP @Shear Rate 206 1/s, Temperature 200 °C
- Hardness, Shore A: 54
- Hardness, Shore A: 57
- Tensile Strength at Break: 3.30 MPa
$ 2526/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 20.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 53
- Tensile Strength at Break: 8.96 MPa
- Tensile Strength, Yield: 2.07 MPa @Strain 300 %
- Elongation at Break: 800 %
$ 1647/MT
- Specific Gravity: 1.30 g/cc
- Melt Flow: 1.30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore C: 82
- Tensile Strength at Break: 11.7 MPa
- Elongation at Break: 450 %
$ 1612/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 0.500 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 25
- Tensile Strength at Break: 2.07 MPa
- Tensile Stress: 1.38 MPa @Strain 300 %
$ 1746/MT
- Specific Gravity: 0.940 g/cc
- Hardness, Shore A: 35
- Tensile Strength: 5.86 MPa
- Elongation at Break: 600 %
$ 2303/MT
- Specific Gravity: 0.892 g/cc
- Melt Flow: 7.50 g/10 min @Load 2.16 kg, Temperature 175 °C
- Hardness, Shore A: 78
- Tensile Strength at Break: 8.96 MPa
- Elongation at Break: 540 %
$ 2135/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Yield: 10.3 MPa
- Tensile Strength, Yield: 20.7 MPa
- Elongation at Break: 280 %
$ 2377/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 5.60 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 40
- Tensile Strength at Break: 12.8 MPa
- Tensile Stress: 8.48 MPa @Strain 100 %
$ 1991/MT
- Specific Gravity: 0.900 g/cc
- Hardness, Shore D: 50
- Tensile Strength: 16.5 MPa
- Elongation at Break: 550 %
- Brittleness Temperature: <= -50.0 °C
$ 2378/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 55
- Tensile Strength at Break: 10.0 MPa
- Elongation at Break: 650 %
$ 2195/MT
- Specific Gravity: 1.02 g/cc
- Melt Flow: 10.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 45
- Tensile Strength at Break: 5.86 MPa
- Elongation at Break: 700 %
$ 1613/MT
- Specific Gravity: 1.02 g/cc
- Melt Flow: 0.900 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 66
- Tensile Strength at Break: 6.89 MPa
- Elongation at Break: 790 %
$ 2515/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.016 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Melt Flow: 1.50 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 87
$ 2233/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 15.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 50
- Tensile Strength: 4.48 MPa
- Elongation at Break: 950 %
$ 2530/MT
- Specific Gravity: 0.892 g/cc
- Melt Flow: 1.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 92
- Tensile Strength at Break: 13.8 MPa
- Elongation at Break: 600 %
$ 1567/MT
- Specific Gravity: 0.880 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 10.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 40
- Tensile Strength at Break: 8.27 MPa
$ 1568/MT
- Specific Gravity: 1.44 g/cc
- Melt Flow: 25.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 75
- Tensile Strength at Break: 2.93 MPa
- Tensile Stress: 2.07 MPa @Strain 100 %
$ 1954/MT
- Specific Gravity: 1.25 g/cc
- Melt Flow: 18.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore D: 37
- Tensile Strength: 11.0 MPa
- Elongation at Break: 600 %
$ 2160/MT
- Density: 0.960 g/cc
- Viscosity: 348000 cP @Shear Rate 206 1/s, Temperature 200 °C
- Hardness, Shore A: 79
- Hardness, Shore A: 83
- Tensile Strength at Break: 8.00 MPa
$ 2301/MT
- Specific Gravity: 0.902 g/cc
- Linear Mold Shrinkage: 0.016 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Melt Flow: 3.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 38
$ 2412/MT
- Specific Gravity: 0.900 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 2.00 g/10 min @Load 2.16 kg, Temperature 150 °C
- Hardness, Shore A: 45
- Tensile Strength at Break: 7.58 MPa
$ 2518/MT
- Specific Gravity: 0.970 g/cc
- Linear Mold Shrinkage: 0.020 cm/cm
- Melt Flow: 20 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 50
- Tensile Strength, Yield: 7.58 MPa
$ 2321/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.023 cm/cm
- Linear Mold Shrinkage, Transverse: 0.023 cm/cm
- Melt Flow: 6.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 53
$ 2211/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 1.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 25
- Tensile Strength at Break: 5.00 MPa
- Elongation at Break: 900 %
$ 2263/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 12.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 8.96 MPa
- Tensile Strength, Yield: 6.89 MPa @Strain 300 %
- Elongation at Break: 500 %
$ 2257/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 1.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 45
- Tensile Strength at Break: 7.58 MPa
- Tensile Strength, Yield: 2.76 MPa @Strain 300 %
- Elongation at Break: 700 %
$ 1660/MT
- Specific Gravity: 1.12 g/cc
- Melt Flow: 3.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 30
- Tensile Strength at Break: 4.14 MPa
- Tensile Strength, Yield: 1.03 MPa @Strain 300 %
- Elongation at Break: 800 %
$ 1745/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 3.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 33
- Tensile Strength at Break: 6.55 MPa
- Elongation at Break: 930 %
$ 1711/MT
- Specific Gravity: 1.03 g/cc
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 80
- Tensile Strength at Break: 10.8 MPa
- Tensile Stress: 3.52 MPa @Strain 50.0 %
$ 1490/MT
- Specific Gravity: 1.22 g/cc
- Melt Flow: 6.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 52
- Tensile Strength at Break: 6.89 MPa
- Tensile Stress: 2.07 MPa @Strain 300 %
$ 1455/MT
- Specific Gravity: 1.24 g/cc
- Melt Flow: 16.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 86
- Tensile Strength at Break: 12.4 MPa
- Elongation at Break: 550 %
$ 1510/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Linear Mold Shrinkage: 0.018 cm/cm
- Melt Flow: 8.7 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 91
$ 1623/MT
- Specific Gravity: 1.01 g/cc
- Hardness, Shore A: 30
- Tensile Strength: 3.45 MPa
- Elongation at Break: 550 %
$ 1604/MT
- Specific Gravity: 1.01 g/cc
- Hardness, Shore A: 30
- Tensile Strength: 3.45 MPa
- Elongation at Break: 550 %
$ 1668/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 16.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 61
- Tensile Strength at Break: 20.7 MPa
- Elongation at Break: 300 %
$ 1825/MT
- Specific Gravity: 0.910 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 18.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 50
- Tensile Strength at Break: 5.17 MPa
$ 1922/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 20.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 50
- Tensile Strength at Break: 6.55 MPa
- Elongation at Break: 830 %
$ 1586/MT
- Specific Gravity: 0.950 g/cc
- Melt Flow: 15.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 88
- Tensile Strength at Break: 21.4 MPa
- Elongation at Break: 680 %
$ 1654/MT
- Specific Gravity: 0.970 g/cc
- Linear Mold Shrinkage: 0.020 cm/cm
- Melt Flow: 20 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 50
- Tensile Strength, Yield: 7.58 MPa
$ 1682/MT
- Specific Gravity: 0.980 g/cc
- Melt Flow: 13.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 78
- Tensile Strength at Break: 8.27 MPa
- Tensile Strength, Yield: 4.83 MPa @Strain 300 %
- Elongation at Break: 650 %
$ 1525/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
- Melt Flow: 20.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 50
$ 1484/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 6.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 65
- Tensile Strength at Break: 6.55 MPa
- Tensile Stress: 4.31 MPa @Strain 300 %
$ 1682/MT
- Specific Gravity: 0.930 g/cc
- Melt Flow: 0.100 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 76
- Hardness, Shore A: 80
- Tensile Strength at Break: 6.47 MPa
$ 1857/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 2.40 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 45
- Tensile Strength at Break: 15.2 MPa
- Elongation at Break: 600 %
$ 1563/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 25.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 72
- Tensile Strength at Break: 8.27 MPa
- Elongation at Break: 600 %
$ 1704/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 37.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 80
- Tensile Strength at Break: 8.62 MPa
- Elongation at Break: 680 %
$ 1534/MT
- Density: 1.30 g/cc
- Hardness, Shore A: 82
- Tensile Strength at Break: 7.398 MPa
- Elongation at Break: 450 %
- 100% Modulus: 0.00360 GPa
$ 1512/MT
- Specific Gravity: 0.910 g/cc
- Melt Flow: 3.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 35
- Tensile Strength at Break: 12.1 MPa
- Tensile Stress: 2.41 MPa @Strain 300 %
$ 1500/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 15.0 g/10 min @Load 2.16 kg, Temperature 175 °C
- Hardness, Shore A: 90
- Tensile Strength at Break: 7.58 MPa
- Elongation at Break: 500 %
$ 2250/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 7.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 30
- Tensile Strength at Break: 5.52 MPa
- Tensile Stress: 1.21 MPa @Strain 300 %
$ 2205/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 7.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 30
- Tensile Strength at Break: 5.52 MPa
- Tensile Stress: 1.21 MPa @Strain 300 %
$ 1577/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 7.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 30
- Tensile Strength at Break: 5.52 MPa
- Tensile Stress: 1.21 MPa @Strain 300 %
$ 1695/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 10.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 13.3 MPa
- Elongation at Break: 590 %
$ 1458/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 5.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 75
- Tensile Strength at Break: 10.3 MPa
- Tensile Stress: 3.10 MPa @Strain 100 %
$ 1750/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 10.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 13.3 MPa
- Elongation at Break: 590 %
$ 2425/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 10.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 13.3 MPa
- Elongation at Break: 590 %
$ 1604/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 30.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 54
- Tensile Strength at Break: 8.27 MPa
- Elongation at Break: 750 %
$ 2025/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 10.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 13.3 MPa
- Elongation at Break: 590 %
$ 2180/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 10.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 13.3 MPa
- Elongation at Break: 590 %
$ 2373/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 10.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 13.3 MPa
- Elongation at Break: 590 %
$ 1940/MT
- Specific Gravity: 0.960 g/cc
- Melt Flow: 0.800 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 55
- Tensile Stress: 2.07 MPa @Strain 100 %
- Tensile Strength, Yield: 3.72 MPa
$ 1853/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 3.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 52
- Tensile Strength at Break: 9.65 MPa
- Tensile Stress: 3.10 MPa @Strain 300 %
$ 2592/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 1.50 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 57
- Tensile Strength at Break: 9.65 MPa
- Tensile Stress: 2.07 MPa @Strain 300 %
$ 1775/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
- Melt Flow: 20.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 50
$ 1704/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 6.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 42
- Tensile Strength at Break: 7.58 MPa
- Tensile Stress: 2.24 MPa @Strain 300 %
$ 1873/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 5.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 76
- Tensile Strength at Break: 15.9 MPa
- Tensile Stress: 5.52 MPa @Strain 300 %
$ 1617/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 1.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 56
- Tensile Strength at Break: 9.65 MPa
- Tensile Strength, Yield: 2.76 MPa @Strain 300 %
- Elongation at Break: 700 %
$ 2213/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage, Transverse: 0.025 cm/cm
- Melt Flow: 6.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 30
- Tensile Strength at Break: 5.86 MPa
$ 1545/MT
- Specific Gravity: 0.870 g/cc
- Melt Flow: 12.0 g/10 min @Load 2.16 kg, Temperature 125 °C
- Hardness, Shore A: 2.0
- Hardness, Shore OO: 35
- Tensile Strength at Break: 0.965 MPa
$ 1597/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 45
- Tensile Strength at Break: 8.96 MPa
$ 1608/MT
- Specific Gravity: 0.892 g/cc
- Melt Flow: 0.20 g/10 min
- Hardness, Shore A: 90
- Tensile Strength at Break: 11.7 MPa
- Elongation at Break: 600 %
$ 1801/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 1.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 25
- Tensile Strength at Break: 4.83 MPa
- Elongation at Break: 930 %
$ 2269/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 35.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 75
- Tensile Strength at Break: 8.27 MPa
- Elongation at Break: 680 %
$ 1605/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 12.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 90
- Tensile Strength at Break: 6.89 MPa
- Tensile Strength, Yield: 4.83 MPa @Strain 300 %
- Elongation at Break: 700 %
$ 1551/MT
- Specific Gravity: 0.870 g/cc
- Melt Flow: 13.0 g/10 min @Load 2.16 kg, Temperature 125 °C
- Hardness, Shore A: 5.0
- Hardness, Shore OO: 50
- Tensile Strength at Break: 2.07 MPa
$ 1585/MT
- Density: 0.940 g/cc
- Hardness, Shore A: 71
- Hardness, Shore A: 74
- Tensile Strength at Break: 5.20 MPa
- Tensile Strength at Break: 7.701 MPa
$ 1752/MT
- Specific Gravity: 0.920 g/cc
- Linear Mold Shrinkage: 0.011 cm/cm
- Linear Mold Shrinkage: 0.013 cm/cm
- Melt Flow: 2.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 42
$ 1519/MT
- Specific Gravity: 0.930 g/cc
- Hardness, Shore A: 45
- Tensile Strength: 6.89 MPa
- Elongation at Break: 750 %
$ 2045/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 1.70 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 70
- Tensile Strength at Break: 5.10 MPa
- Elongation at Break: 700 %
$ 1793/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 1.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 37
- Tensile Strength at Break: 8.27 MPa
- Tensile Strength, Yield: 2.07 MPa @Strain 300 %
- Elongation at Break: 700 %
$ 1829/MT
- Specific Gravity: 1.20 g/cc
- Melt Flow: 30.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 43
- Tensile Strength at Break: 4.31 MPa
- Elongation at Break: 700 %
$ 2160/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 3.40 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 60
- Tensile Strength at Break: 15.2 MPa
- Elongation at Break: 630 %
$ 1616/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 4.8 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 25
- Tensile Strength, Yield: 5.45 MPa
- Elongation at Break: 840 %
$ 1586/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 18.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 50
- Tensile Strength at Break: 5.24 MPa
- Tensile Stress: 1.59 MPa @Strain 100 %
$ 1919/MT
- Specific Gravity: 1.02 g/cc
- Hardness, Shore A: 65
- Tensile Strength: 8.96 MPa
- Elongation at Break: 700 %
$ 2154/MT
- Specific Gravity: 1.31 g/cc
- Melt Flow: 16.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 80
- Tensile Strength: 10.0 MPa
- Elongation at Break: 550 %
$ 1650/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 33.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 38
- Tensile Strength at Break: 6.03 MPa
- Tensile Stress: 2.07 MPa @Strain 300 %
$ 1686/MT
- Specific Gravity: 0.970 g/cc
- Melt Flow: 0.300 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 75
- Tensile Strength: 6.55 MPa
- Elongation at Break: 545 %
$ 1444/MT
- Specific Gravity: 1.14 g/cc
- Melt Flow: 12 g/10 min
- Hardness, Shore A: 80
- Tensile Strength, Yield: 7.58 MPa
- Elongation at Break: 600 %
- 300% Modulus: 0.00345 GPa
$ 1479/MT
- Density: 0.940 g/cc
- Hardness, Shore D: 48
- Hardness, Shore D: 52
- Tensile Strength at Break: 18.40 MPa
- Tensile Strength at Break: 22.00 MPa
$ 1860/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 18.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 30
- Tensile Strength at Break: 6.21 MPa
- Tensile Strength, Yield: 1.38 MPa @Strain 300 %
- Elongation at Break: 700 %
$ 2029/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 30.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 71
- Tensile Strength at Break: 8.96 MPa
- Elongation at Break: 650 %
$ 1840/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 20.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 50
- Tensile Strength at Break: 6.38 MPa
- Elongation at Break: 860 %
$ 1750/MT
- Specific Gravity: 0.930 g/cc
- Hardness, Shore A: 60
- Tensile Strength: 7.93 MPa
- Elongation at Break: 300 %
$ 1509/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 1.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 90
- Tensile Strength at Break: 4.83 MPa
- Elongation at Break: 400 %
$ 1803/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 1.50 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 87
- Tensile Strength at Break: 17.2 MPa
- Tensile Strength, Yield: 7.58 MPa @Strain 300 %
- Elongation at Break: 700 %
$ 1460/MT
- Specific Gravity: 0.900 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 15.0 g/10 min @Load 2.16 kg, Temperature 125 °C
- Hardness, Shore A: 82
- Tensile Strength at Break: 8.96 MPa
$ 2008/MT
- Specific Gravity: 1.11 g/cc
- Hardness, Shore A: 60
- Tensile Strength: 8.27 MPa
- Elongation at Break: 650 %
$ 1672/MT
- Specific Gravity: 0.950 g/cc
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 57
- Tensile Strength at Break: 6.72 MPa
- Elongation at Break: 900 %
$ 1455/MT
- Specific Gravity: 0.940 g/cc
- Hardness, Shore A: 65
- Hardness, Shore A: 70
- Tensile Strength at Break: 5.17 MPa
- Tensile Stress: 2.96 MPa @Strain 100 %
$ 1640/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 25.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 55
- Tensile Strength at Break: 7.10 MPa
- Elongation at Break: 780 %
$ 1680/MT
- Density: 0.950 g/cc
- Hardness, Shore A: 62
- Hardness, Shore A: 66
- Tensile Strength at Break: 4.20 MPa
- Tensile Strength at Break: 6.20 MPa
$ 1604/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 16.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 50
- Tensile Strength: 4.14 MPa
- Elongation at Break: 730 %
$ 1535/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 0.500 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 50
- Tensile Strength at Break: 6.38 MPa
- Tensile Stress: 2.07 MPa @Strain 300 %
$ 1630/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.022 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
- Melt Flow: 1.50 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 87
$ 1919/MT
- Specific Gravity: 1.00 g/cc
- Melt Flow: 1.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 80
- Tensile Strength at Break: 11.2 MPa
- Tensile Strength: 0.302 MPa
$ 1583/MT
- Specific Gravity: 1.30 g/cc
- Melt Flow: 13.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 88
- Tensile Strength at Break: 10.8 MPa @Thickness 1.91 mm
- Elongation at Break: 600 %
$ 1508/MT
- Specific Gravity: 0.930 g/cc
- Melt Flow: 5.0 g/10 min
- Hardness, Shore A: 87
- Tensile Strength at Break: 11.4 MPa
- Elongation at Break: 400 %
$ 1987/MT
- Specific Gravity: 1.24 g/cc
- Melt Flow: 10.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 86
- Tensile Strength: 12.4 MPa
- Elongation at Break: 590 %
$ 1559/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.016 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Melt Flow: 1.50 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 87
$ 1831/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 3.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 60
- Tensile Strength at Break: 8.96 MPa
- Tensile Strength, Yield: 2.76 MPa @Strain 300 %
- Elongation at Break: 700 %
$ 1646/MT
- Density: 0.960 g/cc
- Viscosity: 318000 cP @Shear Rate 206 1/s, Temperature 200 °C
- Hardness, Shore A: 45
- Hardness, Shore A: 48
- Tensile Strength at Break: 2.70 MPa
$ 1472/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 12.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 96
- Hardness, Shore D: 40
$ 1901/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 14.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 80
- Tensile Strength: 6.89 MPa
- Elongation at Break: 620 %
$ 1513/MT
- Specific Gravity: 1.22 g/cc
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 52
- Tensile Strength, Yield: 6.89 MPa
- Elongation at Break: 700 %
$ 1592/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 25.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 35
- Tensile Strength at Break: 5.86 MPa
- Elongation at Break: 680 %
$ 2037/MT
- Specific Gravity: 0.880 g/cc
- Linear Mold Shrinkage: 0.028 cm/cm
- Linear Mold Shrinkage, Transverse: 0.024 cm/cm
- Melt Flow: 15.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 18
$ 1603/MT
- Specific Gravity: 1.23 g/cc
- Melt Flow: 2.20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 55
- Tensile Strength at Break: 8.27 MPa
- Tensile Stress: 1.17 MPa @Strain 100 %
$ 2090/MT
- Density: 0.940 g/cc
- Hardness, Shore A: 71
- Hardness, Shore A: 74
- Tensile Strength at Break: 5.20 MPa
- Tensile Strength at Break: 7.701 MPa
$ 1728/MT
- Specific Gravity: 1.00 g/cc
- Melt Flow: 6.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 45
- Tensile Strength at Break: 4.14 MPa
- Elongation at Break: 550 %
$ 1496/MT
- Specific Gravity: 1.19 g/cc
- Melt Flow: 1.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 78
- Tensile Strength at Break: 8.96 MPa
- Tensile Stress: 2.76 MPa @Strain 100 %
$ 2326/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 3.00 g/10 min @Load 2.16 kg, Temperature 150 °C
- Hardness, Shore A: 45
- Tensile Strength at Break: 7.58 MPa
- Tensile Strength, Yield: 3.45 MPa @Strain 300 %
- Elongation at Break: 700 %
$ 1796/MT
- Specific Gravity: 0.900 g/cc
- Linear Mold Shrinkage: 0.016 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Melt Flow: 2.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 90
$ 1641/MT
- Specific Gravity: 1.16 g/cc
- Melt Flow: 20.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 70
- Tensile Strength at Break: 6.89 MPa
- Tensile Stress: 2.07 MPa @Strain 300 %
$ 2081/MT
- Specific Gravity: 1.10 g/cc
- Hardness, Shore A: 35
- Tensile Strength, Yield: 1.59 MPa
- Tensile Strength, Yield: 5.65 MPa
- Elongation at Break: 400 %
$ 1448/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 5.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 55
- Tensile Strength at Break: 10.1 MPa
- Elongation at Break: 730 %
$ 1463/MT
- Specific Gravity: 1.11 g/cc
- Hardness, Shore A: 87
- Tensile Strength: 12.1 MPa
- Elongation at Break: 700 %
- Brittleness Temperature: <= -60.0 °C
$ 1743/MT
- Specific Gravity: 0.882 g/cc
- Melt Flow: 50.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 35
- Tensile Strength at Break: 3.45 MPa
- Tensile Stress: 1.55 MPa @Strain 300 %
$ 1487/MT
- Specific Gravity: 1.02 g/cc
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 72
- Tensile Strength at Break: 9.65 MPa
- Elongation at Break: 700 %
$ 1807/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 12.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 88
- Tensile Strength at Break: 14.8 MPa
- Tensile Stress: 8.48 MPa @Strain 300 %
$ 1514/MT
- Specific Gravity: 0.870 g/cc
- Melt Flow: 19.0 g/10 min @Load 2.16 kg, Temperature 150 °C
- Hardness, Shore A: 9.0
- Tensile Strength at Break: 2.07 MPa
- Tensile Stress: 0.345 MPa @Strain 300 %
$ 2185/MT
- Specific Gravity: 1.00 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 7.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 89
- Tensile Strength at Break: 11.7 MPa
$ 1566/MT
- Specific Gravity: 1.10 g/cc
- Melt Flow: 2.50 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 65
- Tensile Strength at Break: 8.96 MPa
- Elongation at Break: 700 %
$ 2054/MT
- Specific Gravity: 1.02 g/cc
- Melt Flow: 1.20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 59
- Tensile Strength at Break: 13.8 MPa
- Elongation at Break: 550 %
$ 1469/MT
- Specific Gravity: 1.16 g/cc
- Melt Flow: 40.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 45
- Tensile Strength at Break: 4.14 MPa
- Tensile Stress: 2.07 MPa @Strain 300 %
$ 1694/MT
- Density: 0.930 g/cc
- Hardness, Shore A: 40
- Hardness, Shore A: 44
- Tensile Strength at Break: 2.60 MPa
- Tensile Strength at Break: 3.80 MPa
$ 2369/MT
- Specific Gravity: 0.910 g/cc
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 45
- Tensile Strength at Break: 9.65 MPa
- Tensile Stress: 3.10 MPa @Strain 300 %
$ 1547/MT
- Specific Gravity: 0.920 g/cc
- Melt Flow: 2.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 43
- Tensile Stress: 1.52 MPa @Strain 100 %
- Tensile Strength, Yield: 3.62 MPa
$ 1891/MT
- Specific Gravity: 1.01 g/cc
- Melt Flow: 0.800 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 73
- Tensile Strength at Break: 7.52 MPa
- Elongation at Break: 800 %
$ 2169/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 54
- Tensile Strength at Break: 4.14 MPa
- Tensile Stress: 3.62 MPa @Strain 300 %
$ 1659/MT
- Specific Gravity: 1.09 g/cc
- Melt Flow: 30 g/10 min @Load 5.00 kg, Temperature 177 °C
- Hardness, Shore A: 45
- Tensile Strength, Yield: 5.72 MPa
- Tensile Strength, Yield: 6.29 MPa
$ 1693/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 40
- Tensile Strength, Yield: 6.21 MPa
- Elongation at Break: 750 %
- Flexural Modulus: 0.00793 GPa
$ 1467/MT
- Specific Gravity: 0.910 g/cc
- Linear Mold Shrinkage: 0.030 cm/cm
- Melt Flow: 80.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 42
- Tensile Strength at Break: 7.24 MPa
$ 2013/MT
- Specific Gravity: 0.900 g/cc
- Linear Mold Shrinkage: 0.018 cm/cm
- Linear Mold Shrinkage, Transverse: 0.017 cm/cm
- Melt Flow: 0.100 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 68
$ 1631/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 5.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 75
- Tensile Strength at Break: 9.65 MPa
- Tensile Stress: 3.79 MPa @Strain 300 %
$ 2056/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 30
- Tensile Strength, Yield: 6.21 MPa
- Elongation at Break: 600 %
$ 1544/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 2.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 50
- Tensile Strength at Break: 12.59 MPa
- Tensile Strength at Break: 15.2 MPa
$ 1529/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 6.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 84
- Tensile Strength at Break: 17.9 MPa
- Elongation at Break: 600 %
$ 1828/MT
- Specific Gravity: 0.960 g/cc
- Melt Flow: 5.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 57
- Tensile Strength at Break: 8.96 MPa
- Tensile Stress: 4.83 MPa @Strain 300 %
$ 1886/MT
- Density: 0.950 g/cc
- Viscosity: 360000 cP @Shear Rate 206 1/s, Temperature 200 °C
- Hardness, Shore A: 86
- Hardness, Shore A: 90
- Tensile Strength at Break: 13.00 MPa
$ 2187/MT
- Specific Gravity: 0.920 g/cc
- Linear Mold Shrinkage: 0.037 cm/cm
- Linear Mold Shrinkage, Transverse: 0.036 cm/cm
- Melt Flow: 5.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 15
$ 1714/MT
- Specific Gravity: 1.30 g/cc
- Melt Flow: 1.30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore C: 82
- Tensile Strength at Break: 11.7 MPa
- Elongation at Break: 450 %
$ 1626/MT
- Specific Gravity: 0.880 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 1.50 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 50
- Tensile Strength at Break: 8.27 MPa
$ 1770/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 2.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 50
- Tensile Strength at Break: 8.62 MPa
- Tensile Stress: 2.41 MPa @Strain 300 %
$ 1600/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.020 cm/cm
- Melt Flow: 8.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 60
- Tensile Strength at Break: 8.14 MPa
$ 1808/MT
- Specific Gravity: 1.00 g/cc
- Melt Flow: 0.500 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 8.27 MPa
- Elongation at Break: 550 %
$ 1892/MT
- Specific Gravity: 0.900 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 1.50 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 70
- Tensile Strength at Break: 12.4 MPa
$ 1955/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 25.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 37
- Tensile Strength at Break: 7.58 MPa
- Tensile Strength, Yield: 2.07 MPa @Strain 300 %
- Elongation at Break: 700 %
$ 1733/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 50
- Tensile Strength, Yield: 8.96 MPa
- Elongation at Break: 700 %
$ 1707/MT
- Specific Gravity: 1.22 g/cc
- Melt Flow: 1.50 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 42
- Tensile Strength at Break: 4.83 MPa
- Tensile Stress: 1.38 MPa @Strain 300 %
$ 1737/MT
- Specific Gravity: 1.18 g/cc
- Hardness, Shore A: 81
- Tensile Strength, Yield: 11.4 MPa
- Elongation at Break: 690 %
- Maximum Service Temperature, Air: 105 °C
$ 1603/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 5.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 47
- Tensile Strength at Break: 5.93 MPa
- Elongation at Break: 700 %
$ 1539/MT
- Density: 0.940 g/cc
- Hardness, Shore D: 46
- Hardness, Shore D: 50
- Tensile Strength at Break: 16.50 MPa
- Tensile Strength at Break: 18.00 MPa
$ 1626/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 2.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 25
- Tensile Strength at Break: 3.45 MPa
- Tensile Stress: 1.03 MPa @Strain 300 %
$ 2168/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 75 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 20
- Tensile Strength, Yield: 4.83 MPa
- Elongation at Break: 600 %
- 300% Modulus: 0.000621 GPa
$ 1675/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 40
- Tensile Strength at Break: 6.72 MPa
- Elongation at Break: 900 %
$ 1614/MT
- Specific Gravity: 1.11 g/cc
- Melt Flow: 1.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 62
- Tensile Strength at Break: 9.65 MPa
- Tensile Stress: 3.79 MPa @Strain 300 %
$ 1846/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 12.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 70
- Tensile Strength: 6.83 MPa
- Elongation at Break: 320 %
$ 1445/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 2.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 43
- Tensile Strength at Break: 11.7 MPa
- Tensile Stress: 0.621 MPa @Strain 100 %
$ 2270/MT
- Specific Gravity: 1.16 g/cc
- Hardness, Shore A: 60
- Tensile Strength, Yield: 4.27 MPa
- Tensile Strength, Yield: 13.1 MPa
- Elongation at Break: 350 %
$ 1669/MT
- Specific Gravity: 1.05 g/cc
- Melt Flow: 18.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 30
- Tensile Strength at Break: 3.96 MPa
- Elongation at Break: 750 %
$ 1482/MT
- Specific Gravity: 1.07 g/cc
- Hardness, Shore A: 76
- Hardness, Shore C: 55
- Hardness, Shore C: 64
- Tensile Strength at Break: 17.2 MPa
$ 1515/MT
- Specific Gravity: 1.05 g/cc
- Melt Flow: 2.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 55
- Tensile Strength at Break: 5.52 MPa
- Tensile Stress: 2.76 MPa @Strain 300 %
$ 1509/MT
- Specific Gravity: 0.892 g/cc
- Melt Flow: 7.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 82
- Tensile Strength at Break: 20.3 MPa
- Tensile Stress: 3.59 MPa @Strain 100 %
$ 2117/MT
- Specific Gravity: 0.980 g/cc
- Melt Flow: 13.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 65
- Tensile Strength at Break: 7.24 MPa
- Tensile Stress: 3.79 MPa @Strain 300 %
$ 1809/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 16.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 62
- Tensile Strength: 4.83 MPa
- Elongation at Break: 720 %
$ 1616/MT
- Specific Gravity: 1.13 g/cc
- Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 55
- Tensile Strength at Break: 6.21 MPa
- Elongation at Break: 630 %
$ 2433/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 1.70 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 80
- Tensile Strength at Break: 5.86 MPa
- Elongation at Break: 540 %
$ 2378/MT
- Specific Gravity: 1.25 g/cc
- Melt Flow: 15.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 80
- Tensile Strength at Break: 5.86 MPa
- Elongation at Break: 440 %
$ 1499/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 20.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 45
- Tensile Strength at Break: 5.86 MPa
- Elongation at Break: 500 %
$ 1486/MT
- Specific Gravity: 0.910 g/cc
- Linear Mold Shrinkage: 0.035 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Melt Flow: 3.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 45
$ 2113/MT
- Specific Gravity: 1.13 g/cc
- Melt Flow: 1.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 30
- Tensile Strength, Yield: 2.76 MPa
- Elongation at Break: 600 %
$ 1698/MT
- Specific Gravity: 1.08 g/cc
- Melt Flow: 2.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 82
- Tensile Strength at Break: 6.21 MPa
- Elongation at Break: 750 %
$ 1669/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 4.50 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 70
- Tensile Strength at Break: 14.5 MPa
$ 1461/MT
- Specific Gravity: 1.16 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.014 cm/cm
- Melt Flow: 10.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 70
$ 1452/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 40.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 8.48 MPa
- Elongation at Break: 500 %
$ 1904/MT
- Specific Gravity: 1.13 g/cc
- Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 90
- Tensile Strength, Yield: 9.65 MPa
- Elongation at Break: 600 %
$ 1570/MT
- Specific Gravity: 1.15 g/cc
- Melt Flow: 12.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 6.89 MPa
- Elongation at Break: 530 %
$ 1455/MT
- Density: 1.26 g/cc
- Hardness, Shore D: 40
- Tensile Strength at Break: 13.60 MPa
- Elongation at Break: 510 %
- 100% Modulus: 0.00740 GPa
$ 1799/MT
- Specific Gravity: 1.12 g/cc
- Hardness, Shore A: 50
- Tensile Strength, Yield: 9.10 MPa
- Elongation at Break: 390 %
- Compression Set: 35 %
$ 1535/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 20.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 45
- Tensile Strength at Break: 5.86 MPa
- Elongation at Break: 500 %
$ 1444/MT
- Specific Gravity: 0.900 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 12.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 60
- Tensile Strength at Break: 8.27 MPa
$ 2181/MT
- Specific Gravity: 1.31 g/cc
- Melt Flow: 1.60 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore C: 90
- Tensile Strength at Break: 11.0 MPa
- Tensile Stress: 7.58 MPa @Strain 100 %
$ 2239/MT
- Specific Gravity: 0.910 g/cc
- Melt Flow: 43.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 57
- Tensile Strength at Break: 13.4 MPa
- Tensile Stress: 4.83 MPa @Strain 300 %
$ 1519/MT
- Specific Gravity: 1.22 g/cc
- Melt Flow: 10.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 52
- Tensile Strength at Break: 6.89 MPa
- Tensile Strength, Yield: 1.72 MPa @Strain 300 %
- Elongation at Break: 770 %
$ 1774/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 12 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 70
- Tensile Strength, Yield: 10.3 MPa
- Elongation at Break: 700 %
$ 1743/MT
- Specific Gravity: 1.15 g/cc
- Melt Flow: 2.1 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 42
- Tensile Strength, Yield: 18.5 MPa
- Elongation at Break: 490 %
$ 2104/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 20.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 53
- Tensile Strength at Break: 8.96 MPa
$ 1813/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 60
- Tensile Strength, Yield: 9.65 MPa
- Elongation at Break: 600 %
$ 1695/MT
- Specific Gravity: 0.990 g/cc
- Melt Flow: 4.60 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 75
- Tensile Strength at Break: 8.14 MPa
- Tensile Stress: 2.55 MPa @Strain 100 %
$ 2262/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 33.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 7.93 MPa
- Elongation at Break: 530 %
$ 1567/MT
- Specific Gravity: 1.20 g/cc
- Melt Flow: 5.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 55
- Tensile Strength at Break: 6.89 MPa
- Tensile Stress: 2.07 MPa @Strain 300 %
$ 1989/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 2.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 75
- Tensile Strength at Break: 8.96 MPa
- Tensile Stress: 6.89 MPa @Strain 300 %
$ 1513/MT
- Specific Gravity: 1.16 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 60
- Tensile Strength, Yield: 6.89 MPa
- Elongation at Break: 700 %
$ 1632/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.025 cm/cm
- Linear Mold Shrinkage, Transverse: 0.024 cm/cm
- Melt Flow: 0.500 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 50
$ 1624/MT
- Specific Gravity: 1.00 g/cc
- Linear Mold Shrinkage: 0.020 cm/cm
- Melt Flow: 10 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 60
- Tensile Strength, Yield: 8.27 MPa
$ 1682/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 15.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 60
- Hardness, Shore OO: 40
- Tensile Strength at Break: 7.58 MPa
$ 1462/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 30.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 40
- Tensile Strength at Break: 4.14 MPa
- Tensile Stress: 2.07 MPa @Strain 300 %
$ 1487/MT
- Specific Gravity: 0.910 g/cc
- Linear Mold Shrinkage: 0.041 cm/cm
- Linear Mold Shrinkage, Transverse: 0.033 cm/cm
- Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 25
$ 1457/MT
- Specific Gravity: 1.05 g/cc
- Melt Flow: 69.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 40
- Tensile Strength at Break: 4.96 MPa
- Tensile Stress: 2.07 MPa @Strain 100 %
$ 1871/MT
- Density: 0.950 g/cc
- Hardness, Shore A: 80
- Hardness, Shore A: 84
- Tensile Strength at Break: 7.10 MPa
- Tensile Strength at Break: 9.301 MPa
$ 1500/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.018 cm/cm
- Linear Mold Shrinkage, Transverse: 0.015 cm/cm
- Melt Flow: 4.00 g/10 min @Load 10.0 kg, Temperature 230 °C
- Hardness, Shore A: 55
$ 1920/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 7.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 50
- Tensile Strength at Break: 7.58 MPa
$ 1672/MT
- Hardness, Shore A: 75
- Tensile Strength: 14.5 MPa
- Elongation at Break: 700 %
- Appearance: Translucent
$ 1646/MT
- Specific Gravity: 1.15 g/cc
- Hardness, Shore A: 60
- Tensile Strength, Yield: 4.34 MPa
- Tensile Strength, Yield: 11.2 MPa
- Tensile Strength, Yield: 13.8 MPa
$ 1656/MT
- Specific Gravity: 0.992 g/cc
- Melt Flow: 0.700 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 75
- Tensile Strength at Break: 4.14 MPa
- Elongation at Break: 520 %
$ 1767/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 7.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 60
- Tensile Strength at Break: 11.7 MPa
- Tensile Stress: 2.76 MPa @Strain 300 %
$ 1622/MT
- Specific Gravity: 1.13 g/cc
- Melt Flow: 5.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 95
- Tensile Strength at Break: 16.5 MPa
- Elongation at Break: 650 %
$ 1546/MT
- Specific Gravity: 1.00 g/cc
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 80
- Hardness, Shore A: 85
- Tensile Strength, Yield: 6.41 MPa
$ 2200/MT
- Specific Gravity: 1.24 g/cc
- Melt Flow: 9.7 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 86
- Tensile Strength, Yield: 12.4 MPa
- Elongation at Break: 590 %
$ 1814/MT
- Specific Gravity: 1.27 g/cc
- Melt Flow: 1.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 75
- Tensile Strength at Break: 6.21 MPa
- Elongation at Break: 350 %
$ 1589/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 4.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 75
- Tensile Strength at Break: 15.2 MPa
- Tensile Stress: 5.52 MPa @Strain 300 %
$ 1680/MT
- Specific Gravity: 1.02 g/cc
- Melt Flow: 1.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 76
- Tensile Strength at Break: 7.17 MPa
- Elongation at Break: 710 %
$ 1667/MT
- Specific Gravity: 0.950 g/cc
- Melt Flow: 2.50 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 52
- Tensile Strength at Break: 10.3 MPa
- Tensile Stress: 4.14 MPa @Strain 300 %
$ 2347/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 1.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 75
- Tensile Strength at Break: 14.5 MPa
- Tensile Stress: 5.52 MPa @Strain 300 %
$ 1643/MT
- Specific Gravity: 1.00 g/cc
- Hardness, Shore A: 82
- Tensile Strength: 16.7 MPa
- Elongation at Break: 650 %
- Brittleness Temperature: <= -60.0 °C
$ 1910/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.031 cm/cm
- Linear Mold Shrinkage, Transverse: 0.026 cm/cm
- Melt Flow: 2.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 35
$ 2167/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 7.00 g/10 min @Load 2.16 kg, Temperature 125 °C
- Hardness, Shore A: 12
- Hardness, Shore OO: 60
- Tensile Strength at Break: 2.41 MPa
$ 2074/MT
- Specific Gravity: 0.990 g/cc
- Melt Flow: 0.500 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 8.27 MPa
- Elongation at Break: 550 %
$ 2138/MT
- Specific Gravity: 1.01 g/cc
- Melt Flow: 0.200 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 74
- Tensile Strength at Break: 6.48 MPa
- Elongation at Break: 560 %
$ 1670/MT
- Specific Gravity: 0.920 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 65
- Tensile Strength, Yield: 6.89 MPa
- Elongation at Break: 600 %
$ 2373/MT
- Specific Gravity: 0.900 g/cc
- Linear Mold Shrinkage: 0.016 cm/cm
- Linear Mold Shrinkage, Transverse: 0.019 cm/cm
- Melt Flow: 25.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 53
$ 2425/MT
- Specific Gravity: 1.00 g/cc
- Melt Flow: 3.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 70
- Tensile Strength at Break: 6.00 MPa
- Elongation at Break: 670 %
$ 1754/MT
- Specific Gravity: 0.902 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Melt Flow: 5.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 39
$ 2051/MT
- Specific Gravity: 1.03 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 11.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 59
- Hardness, Shore A: 63
$ 1602/MT
- Specific Gravity: 0.910 g/cc
- Melt Flow: 15.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 82
- Tensile Strength at Break: 11.7 MPa
- Elongation at Break: 600 %
$ 1750/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 14.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 82
- Tensile Strength at Break: 12.6 MPa
- Tensile Stress: 7.24 MPa @Strain 300 %
$ 1787/MT
- Specific Gravity: 0.960 g/cc
- Linear Mold Shrinkage: 0.023 cm/cm
- Melt Flow: 3.90 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 59
- Tensile Strength at Break: 10.3 MPa
$ 2054/MT
- Specific Gravity: 1.22 g/cc
- Melt Flow: 1.50 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 42
- Tensile Strength at Break: 4.83 MPa
- Tensile Stress: 1.38 MPa @Strain 300 %
$ 2270/MT
- Specific Gravity: 2.18 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 12.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 70
- Tensile Strength at Break: 2.76 MPa
$ 1976/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 1.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 70
- Tensile Strength at Break: 11.4 MPa
- Elongation at Break: 850 %
$ 1717/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 10.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 70
- Tensile Strength at Break: 6.89 MPa
- Elongation at Break: 600 %
$ 1529/MT
- Specific Gravity: 1.13 g/cc
- Melt Flow: 3.6 g/10 min @Load 5.00 kg, Temperature 177 °C
- Hardness, Shore A: 60
- Tensile Strength, Yield: 8.34 MPa
- Tensile Strength, Yield: 12.51 MPa
$ 1726/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 9.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 38
- Tensile Strength at Break: 8.96 MPa
- Tensile Stress: 2.59 MPa @Strain 300 %
$ 2083/MT
- Specific Gravity: 0.930 g/cc
- Hardness, Shore A: 48
- Hardness, Shore A: 56
- Tensile Strength at Break: 6.21 MPa
- Tensile Stress: 1.48 MPa @Strain 100 %
$ 1562/MT
- Specific Gravity: 0.880 g/cc
- Linear Mold Shrinkage: 0.044 cm/cm
- Linear Mold Shrinkage, Transverse: 0.037 cm/cm
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 45
$ 1614/MT
- Specific Gravity: 0.930 g/cc
- Melt Flow: 2.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 69
- Tensile Strength at Break: 19.3 MPa
- Elongation at Break: 650 %
$ 2518/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 10.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 62
- Tensile Strength at Break: 9.65 MPa
- Tensile Stress: 3.45 MPa @Strain 300 %
$ 1842/MT
- Specific Gravity: 1.04 g/cc
- Melt Flow: 18.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 75
- Tensile Strength at Break: 7.58 MPa
- Elongation at Break: 650 %
$ 1545/MT
- Linear Mold Shrinkage: 0.030 cm/cm
- Melt Flow: 10.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 18
- Tensile Strength at Break: 2.76 MPa
- Tensile Stress: 0.689 MPa @Strain 300 %
$ 1448/MT
- Specific Gravity: 0.920 g/cc
- Linear Mold Shrinkage: 0.038 cm/cm
- Linear Mold Shrinkage, Transverse: 0.024 cm/cm
- Melt Flow: 2.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 42
$ 1753/MT
- Specific Gravity: 0.910 g/cc
- Linear Mold Shrinkage: 0.013 cm/cm
- Melt Flow: 3.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 45
- Tensile Strength at Break: 10.3 MPa
$ 1502/MT
- Density: 0.930 g/cc
- Viscosity: 253000 cP @Shear Rate 206 1/s, Temperature 200 °C
- Hardness, Shore A: 37
- Hardness, Shore A: 43
- Tensile Strength at Break: 2.10 MPa
$ 1892/MT
- Specific Gravity: 0.870 g/cc
- Melt Flow: 10.0 g/10 min @Load 2.16 kg, Temperature 125 °C
- Hardness, Shore A: 40
- Tensile Strength at Break: 1.24 MPa
- Tensile Strength, Yield: 0.241 MPa @Strain 300 %
- Elongation at Break: 700 %
$ 1451/MT
- Specific Gravity: 1.18 g/cc
- Hardness, Shore A: 70
- Tensile Strength, Yield: 6.55 MPa
- Tensile Strength, Yield: 18.1 MPa
- Elongation at Break: 330 %
$ 2355/MT
- Specific Gravity: 1.15 g/cc
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 44
- Tensile Strength, Yield: 14.3 MPa
- Elongation at Break: 530 %
$ 2064/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 85
- Tensile Strength, Yield: 6.89 MPa
- Elongation at Break: 600 %
- 300% Modulus: 0.00345 GPa
$ 1795/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 7.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 75
- Tensile Strength at Break: 7.58 MPa
- Elongation at Break: 450 %
$ 1533/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 21.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 82
- Tensile Strength at Break: 13.1 MPa
- Tensile Stress: 5.93 MPa @Strain 300 %
$ 2068/MT
- Specific Gravity: 1.11 g/cc
- Melt Flow: 15 g/10 min @Load 5.00 kg, Temperature 177 °C
- Hardness, Shore A: 55
- Tensile Strength, Yield: 7.10 MPa
- Tensile Strength, Yield: 11.789 MPa
$ 1619/MT
- Specific Gravity: 0.940 g/cc
- Melt Flow: 0.100 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 80
- Hardness, Shore A: 85
- Tensile Strength at Break: 8.27 MPa
$ 2227/MT
- Specific Gravity: 0.980 g/cc
- Melt Flow: 3.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 70
- Tensile Strength at Break: 7.58 MPa
- Tensile Stress: 4.48 MPa @Strain 300 %
$ 1494/MT
- Specific Gravity: 1.01 g/cc
- Melt Flow: 3.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 76
- Tensile Strength at Break: 10.0 MPa
- Tensile Stress: 3.10 MPa @Strain 100 %
$ 1563/MT
- Specific Gravity: 1.30 g/cc
- Melt Flow: 1.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore C: 82
- Tensile Strength at Break: 12.3 MPa
- Elongation at Break: 600 %
$ 1940/MT
- Specific Gravity: 0.990 g/cc
- Melt Flow: 1.60 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 73
- Hardness, Shore A: 78
- Tensile Strength at Break: 3.59 MPa
$ 2422/MT
- Specific Gravity: 0.980 g/cc
- Melt Flow: 18.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 52
- Tensile Strength at Break: 10.3 MPa
- Elongation at Break: 650 %
$ 1624/MT
- Specific Gravity: 1.06 g/cc
- Melt Flow: 15.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 35
- Tensile Strength at Break: 5.86 MPa
- Elongation at Break: 600 %
$ 1667/MT
- Specific Gravity: 1.06 g/cc
- Melt Flow: 15.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 35
- Tensile Strength at Break: 5.86 MPa
- Elongation at Break: 600 %
$ 2170/MT
- Specific Gravity: 0.910 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 30.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 45
$ 1541/MT
- Specific Gravity: 0.920 g/cc
- Melt Flow: 25.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 63
- Tensile Strength at Break: 6.55 MPa
- Elongation at Break: 680 %
$ 2268/MT
- Specific Gravity: 0.920 g/cc
- Melt Flow: 1.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 46
- Hardness, Shore D: 51
- Tensile Strength at Break: 16.5 MPa
$ 1723/MT
- Specific Gravity: 0.880 g/cc
- Linear Mold Shrinkage: 0.035 cm/cm
- Melt Flow: 130 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 15
- Tensile Strength at Break: 2.86 MPa
$ 1544/MT
- Specific Gravity: 1.14 g/cc
- Melt Flow: 12.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 60
- Tensile Strength at Break: 21.4 MPa
- Elongation at Break: 4.0 %
$ 1623/MT
- Specific Gravity: 1.10 g/cc
- Melt Flow: 1.50 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 75
- Tensile Strength at Break: 9.65 MPa
- Elongation at Break: 600 %
$ 1951/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 15.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 8.62 MPa
- Elongation at Break: 580 %
$ 1793/MT
- Specific Gravity: 1.16 g/cc
- Melt Flow: 55.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 45
- Tensile Strength at Break: 4.14 MPa
- Tensile Stress: 2.07 MPa @Strain 300 %
$ 1883/MT
- Specific Gravity: 0.870 g/cc
- Linear Mold Shrinkage: 0.026 cm/cm
- Linear Mold Shrinkage, Transverse: 0.041 cm/cm
- Melt Flow: 10.0 g/10 min @Load 2.16 kg, Temperature 125 °C
- Hardness, Shore A: 5.0
$ 2064/MT
- Specific Gravity: 0.880 g/cc
- Linear Mold Shrinkage: 0.039 cm/cm
- Linear Mold Shrinkage, Transverse: 0.034 cm/cm
- Melt Flow: 1.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 37
$ 1521/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.047 cm/cm
- Linear Mold Shrinkage, Transverse: 0.040 cm/cm
- Melt Flow: 9.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 38
$ 1698/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.026 cm/cm
- Linear Mold Shrinkage, Transverse: 0.026 cm/cm
- Melt Flow: 0.500 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 45
$ 2016/MT
- Specific Gravity: 0.910 g/cc
- Linear Mold Shrinkage: 0.021 cm/cm
- Linear Mold Shrinkage, Transverse: 0.022 cm/cm
- Melt Flow: 1.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 35
$ 1980/MT
- Specific Gravity: 0.960 g/cc
- Linear Mold Shrinkage: 0.023 cm/cm
- Linear Mold Shrinkage, Transverse: 0.022 cm/cm
- Melt Flow: 2.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 55
$ 1884/MT
- Specific Gravity: 0.970 g/cc
- Linear Mold Shrinkage: 0.023 cm/cm
- Linear Mold Shrinkage, Transverse: 0.021 cm/cm
- Melt Flow: 18.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 64
$ 1773/MT
- Hardness, Shore A: 73
- Tensile Strength: 2.62 MPa
- Elongation at Break: 380 %
- Appearance: Opaque
$ 1533/MT
- Specific Gravity: 0.960 g/cc
- Linear Mold Shrinkage: 0.026 cm/cm
- Linear Mold Shrinkage, Transverse: 0.019 cm/cm
- Melt Flow: 18.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 30
$ 2105/MT
- Specific Gravity: 0.930 g/cc
- Linear Mold Shrinkage: 0.017 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Melt Flow: 45.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 45
$ 1626/MT
- Specific Gravity: 0.910 g/cc
- Linear Mold Shrinkage: 0.018 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
- Melt Flow: 0.200 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 45
$ 1911/MT
- Specific Gravity: 0.880 g/cc
- Hardness, Shore A: 86
- Hardness, Shore A: 88
- Tensile Strength: 16.35 MPa
- Tensile Stress: 7.191 MPa @Strain 100 %
$ 2124/MT
- Specific Gravity: 0.880 g/cc
- Hardness, Shore A: 53
- Hardness, Shore A: 55
- Tensile Strength: 9.191 MPa
- Tensile Stress: 1.84 MPa @Strain 100 %
$ 2135/MT
- Specific Gravity: 0.880 g/cc
- Hardness, Shore A: 72
- Hardness, Shore A: 74
- Tensile Strength: 13.52 MPa
- Tensile Stress: 4.30 MPa @Strain 100 %
$ 1783/MT
- Specific Gravity: 0.880 g/cc
- Hardness, Shore A: 83
- Hardness, Shore A: 85
- Tensile Strength: 15.84 MPa
- Tensile Stress: 5.91 MPa @Strain 100 %
$ 1594/MT
- Specific Gravity: 1.00 g/cc
- Melt Flow: 1.20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 55
- Tensile Strength at Break: 6.07 MPa
- Elongation at Break: 980 %
$ 1667/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 60
- Tensile Strength at Break: 8.96 MPa
$ 1680/MT
- Specific Gravity: 1.00 g/cc
- Melt Flow: 0.200 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 65
- Tensile Strength at Break: 4.83 MPa
- Elongation at Break: 540 %
$ 1563/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 13.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 50
- Tensile Strength at Break: 4.83 MPa
- Tensile Stress: 1.69 MPa @Strain 100 %
$ 2155/MT
- Specific Gravity: 0.880 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 45
- Tensile Strength at Break: 8.96 MPa
$ 2224/MT
- Specific Gravity: 0.910 g/cc
- Hardness, Shore A: 50
- Tensile Strength: 5.00 MPa
- Elongation at Break: 600 %
$ 2077/MT
- Specific Gravity: 0.990 g/cc
- Melt Flow: 1.20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 75
- Tensile Strength at Break: 9.17 MPa
- Elongation at Break: 750 %
$ 1774/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 14.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 90
- Tensile Strength: 8.62 MPa
- Elongation at Break: 610 %
$ 1562/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 6.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 90
- Tensile Strength at Break: 10.3 MPa
- Tensile Stress: 4.14 MPa @Strain 300 %
$ 1571/MT
- Specific Gravity: 1.01 g/cc
- Melt Flow: 3.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 70
- Hardness, Shore A: 75
- Tensile Strength at Break: 9.65 MPa
$ 2223/MT
- Specific Gravity: 1.22 g/cc
- Linear Mold Shrinkage: 0.010 - 0.025 cm/cm
- Hardness, Shore A: 60
- Tensile Strength, Yield: 4.69 MPa
- Tensile Strength, Yield: 14.8 MPa
$ 1788/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 5.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 50
- Tensile Strength at Break: 6.89 MPa
- Tensile Strength, Yield: 2.07 MPa @Strain 300 %
- Elongation at Break: 700 %
$ 1972/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 5.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 35.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 40
- Tensile Strength at Break: 8.27 MPa
$ 2220/MT
- Specific Gravity: 1.19 g/cc
- Hardness, Shore A: 75
- Tensile Strength, Yield: 8.96 MPa
- Tensile Strength, Yield: 19.1 MPa
- Tensile Strength, Yield: 20.0 MPa
$ 1712/MT
- Specific Gravity: 1.17 g/cc
- Hardness, Shore A: 65
- Tensile Strength, Yield: 4.83 MPa
- Tensile Strength, Yield: 15.2 MPa
- Elongation at Break: 340 %
$ 1926/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.016 cm/cm
- Melt Flow: 1.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 65
- Tensile Strength at Break: 14.5 MPa
$ 1789/MT
- Specific Gravity: 1.01 g/cc
- Melt Flow: 3.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 71
- Tensile Strength at Break: 10.0 MPa
- Elongation at Break: 680 %
$ 1504/MT
- Specific Gravity: 1.08 g/cc
- Melt Flow: 7.0 g/10 min @Load 5.00 kg, Temperature 177 °C
- Hardness, Shore A: 40
- Tensile Strength, Yield: 4.59 MPa
- Tensile Strength, Yield: 9.17 MPa
$ 1854/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 17.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 90
- Tensile Strength: 12.2 MPa
- Elongation at Break: 850 %
$ 1639/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 17.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 59
- Tensile Strength: 5.38 MPa
- Elongation at Break: 930 %
$ 1524/MT
- Specific Gravity: 1.02 g/cc
- Hardness, Shore A: 50
- Tensile Strength: 3.79 MPa
- Elongation at Break: 400 %
$ 1885/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.016 cm/cm
- Melt Flow: 1.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 65
- Tensile Strength at Break: 14.5 MPa
$ 2132/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 76
- Tensile Strength at Break: 6.55 MPa
- Elongation at Break: 400 %
$ 2132/MT
- Specific Gravity: 1.04 g/cc
- Melt Flow: 5.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 65
- Hardness, Shore A: 70
- Tensile Strength at Break: 6.55 MPa
$ 1581/MT
- Specific Gravity: 0.920 g/cc
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 42
- Tensile Strength at Break: 3.45 MPa
- Tensile Stress: 2.76 MPa @Strain 300 %
$ 1653/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 6.00 g/10 min @Load 2.16 kg, Temperature 150 °C
- Hardness, Shore A: 60
- Tensile Strength at Break: 3.45 MPa
- Tensile Strength, Yield: 0.552 MPa @Strain 300 %
- Elongation at Break: 700 %
$ 1471/MT
- Specific Gravity: 0.950 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 3.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 63
- Tensile Strength at Break: 10.3 MPa
$ 1831/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 1.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 70
- Tensile Strength at Break: 14.5 MPa
$ 1445/MT
- Specific Gravity: 0.910 g/cc
- Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 35
- Tensile Strength at Break: 9.65 MPa
- Tensile Stress: 3.10 MPa @Strain 300 %
$ 1636/MT
- Specific Gravity: 1.04 g/cc
- Melt Flow: 3.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 60
- Tensile Strength at Break: 2.76 MPa
- Tensile Stress: 2.41 MPa @Strain 200 %
$ 1882/MT
- Specific Gravity: 1.13 g/cc
- Melt Flow: 12.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 97
- Hardness, Shore D: 40
- Tensile Strength at Break: 12.4 MPa
$ 1648/MT
- Specific Gravity: 1.05 g/cc
- Melt Flow: 12.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 95
- Tensile Strength at Break: 14.0 MPa
- Elongation at Break: 670 %
$ 1608/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 25.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 30
- Tensile Strength at Break: 6.21 MPa
- Tensile Stress: 1.03 MPa @Strain 300 %
$ 1910/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 5.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 70
- Tensile Strength at Break: 6.89 MPa
- Tensile Strength, Yield: 3.45 MPa @Strain 300 %
- Elongation at Break: 600 %
$ 1822/MT
- Specific Gravity: 1.31 g/cc
- Melt Flow: 18.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 83
- Tensile Strength at Break: 9.5113 MPa
- Tensile Strength at Break: 10.26 MPa
$ 1643/MT
- Specific Gravity: 0.880 g/cc
- Linear Mold Shrinkage: 0.020 cm/cm
- Melt Flow: 1.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 37
- Tensile Strength at Break: 8.27 MPa
$ 2110/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 45.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 35
- Tensile Strength at Break: 3.45 MPa
- Tensile Stress: 1.38 MPa @Strain 300 %
$ 1937/MT
- Specific Gravity: 1.13 g/cc
- Hardness, Shore A: 50
- Tensile Strength, Yield: 3.17 MPa
- Tensile Strength, Yield: 8.27 MPa
- Tensile Strength, Yield: 11.0 MPa
$ 1467/MT
- Specific Gravity: 1.29 g/cc
- Melt Flow: 12.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 42
- Tensile Strength at Break: 8.83 MPa
- Elongation at Break: 620 %
$ 1797/MT
- Specific Gravity: 0.940 g/cc
- Melt Flow: 2.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 35
- Tensile Strength at Break: 8.62 MPa
- Tensile Stress: 3.28 MPa @Strain 300 %
$ 2252/MT
- Specific Gravity: 1.05 g/cc
- Melt Flow: 1.40 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 10.3 MPa
- Tensile Stress: 6.48 MPa @Strain 100 %
$ 1656/MT
- Specific Gravity: 1.13 g/cc
- Melt Flow: 1.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 20
- Tensile Strength, Yield: 2.07 MPa
- Elongation at Break: 800 %
$ 2125/MT
- Specific Gravity: 1.24 g/cc
- Melt Flow: 10.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 86
- Tensile Strength at Break: 10.24 MPa
- Tensile Strength at Break: 11.4 MPa
$ 2411/MT
- Specific Gravity: 0.922 g/cc
- Melt Flow: 11.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 54
- Tensile Strength at Break: 16.5 MPa
- Elongation at Break: 650 %
$ 1990/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 2.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 65
- Tensile Strength at Break: 9.58 MPa
- Elongation at Break: 860 %
$ 1505/MT
- Specific Gravity: 0.930 g/cc
- Melt Flow: 1.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 61
- Tensile Strength: 7.826 MPa
- Elongation at Break: 935 %
$ 1449/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.015 cm/cm
- Melt Flow: 1.50 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 53
$ 1885/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 4.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 80
- Tensile Strength at Break: 15.2 MPa
$ 1563/MT
- Specific Gravity: 1.16 g/cc
- Melt Flow: 25.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 64
- Tensile Strength at Break: 8.27 MPa
- Tensile Stress: 3.10 MPa @Strain 300 %
$ 1767/MT
- Specific Gravity: 1.16 g/cc
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 70
- Tensile Strength, Yield: 7.58 MPa
- Elongation at Break: 400 %
$ 1746/MT
- Specific Gravity: 0.920 g/cc
- Melt Flow: 9.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 46
- Tensile Strength at Break: 15.9 MPa
- Elongation at Break: 700 %
$ 1478/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 2.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 50
- Tensile Strength at Break: 10.3 MPa
- Tensile Stress: 4.14 MPa @Strain 300 %
$ 1786/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 3.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 65
- Tensile Strength at Break: 7.93 MPa
$ 1764/MT
- Specific Gravity: 0.970 g/cc
- Hardness, Shore A: 62
- Tensile Strength: 8.27 MPa
- Elongation at Break: 750 %
$ 1643/MT
- Specific Gravity: 1.28 g/cc
- Melt Flow: 3.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 56
- Tensile Strength at Break: 9.65 MPa
- Elongation at Break: 600 %
$ 2220/MT
- Density: 0.940 g/cc
- Hardness, Shore D: 38
- Hardness, Shore D: 41
- Tensile Strength at Break: 14.60 MPa
- Tensile Strength at Break: 16.2 MPa
$ 1546/MT
- Specific Gravity: 1.01 g/cc
- Melt Flow: 0.900 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 73
- Tensile Strength at Break: 6.21 MPa
- Elongation at Break: 900 %
$ 1486/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 7.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 89
- Tensile Strength at Break: 12.4 MPa
- Tensile Stress: 8.27 MPa @Strain 300 %
$ 2287/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 85.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 40
- Tensile Strength at Break: 3.45 MPa
- Tensile Stress: 1.38 MPa @Strain 100 %
$ 1552/MT
- Specific Gravity: 0.910 g/cc
- Melt Flow: 6.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 65
- Tensile Strength at Break: 24.8 MPa
- Tensile Stress: 6.21 MPa @Strain 300 %
$ 1450/MT
- Specific Gravity: 0.920 g/cc
- Melt Flow: 2.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 48
- Tensile Strength at Break: 12.8 MPa
- Tensile Stress: 3.96 MPa @Strain 300 %
$ 2111/MT
- Specific Gravity: 0.940 g/cc
- Melt Flow: 1.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 73
- Hardness, Shore A: 79
- Tensile Strength at Break: 6.76 MPa
$ 1809/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 40.0 g/10 min @Load 2.16 kg, Temperature 125 °C
- Hardness, Shore A: 32
- Tensile Strength at Break: 1.03 MPa
- Elongation at Break: 650 %
$ 1452/MT
- Specific Gravity: 0.880 g/cc
- Linear Mold Shrinkage: 0.020 cm/cm
- Melt Flow: 2.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 25
- Tensile Strength at Break: 6.21 MPa
$ 1931/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.025 cm/cm
- Melt Flow: 12.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 70
- Tensile Strength at Break: 8.96 MPa
$ 1924/MT
- Specific Gravity: 1.30 g/cc
- Melt Flow: 1.30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore C: 82
- Tensile Strength at Break: 11.7 MPa
- Elongation at Break: 450 %
$ 1779/MT
- Density: 0.960 g/cc
- Hardness, Shore A: 80
- Hardness, Shore A: 83
- Tensile Strength at Break: 8.00 MPa
- Tensile Strength at Break: 10.50 MPa
$ 1671/MT
- Specific Gravity: 0.920 g/cc
- Linear Mold Shrinkage: 0.011 cm/cm
- Linear Mold Shrinkage: 0.013 cm/cm
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 42
$ 1594/MT
- Density: 0.960 g/cc
- Hardness, Shore A: 63
- Hardness, Shore A: 65
- Tensile Strength at Break: 4.70 MPa
- Tensile Strength at Break: 6.50 MPa
$ 1697/MT
- Specific Gravity: 0.880 g/cc
- Linear Mold Shrinkage: 0.025 cm/cm
- Melt Flow: 3.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 37
- Tensile Strength at Break: 8.96 MPa
$ 1893/MT
- Density: 0.960 g/cc
- Hardness, Shore A: 72
- Hardness, Shore A: 75
- Tensile Strength at Break: 5.90 MPa
- Tensile Strength at Break: 8.101 MPa
$ 1826/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 5.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 10.3 MPa
- Elongation at Break: 600 %
$ 1850/MT
- Specific Gravity: 0.910 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 35
- Tensile Strength, Yield: 2.93 MPa
- Elongation at Break: 400 %
$ 1570/MT
- Specific Gravity: 0.880 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 30.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 55
- Tensile Strength at Break: 8.96 MPa
$ 1450/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.017 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
- Melt Flow: 3.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 50
$ 1764/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 12.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 23
- Tensile Strength at Break: 3.45 MPa
- Tensile Stress: 0.965 MPa @Strain 300 %
$ 1719/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 2.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 40
- Tensile Strength at Break: 8.96 MPa
- Tensile Strength, Yield: 2.76 MPa @Strain 300 %
- Elongation at Break: 700 %
$ 1642/MT
- Specific Gravity: 0.920 g/cc
- Linear Mold Shrinkage: 0.011 cm/cm
- Linear Mold Shrinkage: 0.013 cm/cm
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 42
$ 1495/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 7.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 65
- Tensile Strength at Break: 6.89 MPa
- Tensile Stress: 2.07 MPa @Strain 300 %
$ 1948/MT
- Specific Gravity: 1.10 g/cc
- Melt Flow: 10.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 45
- Tensile Strength at Break: 6.21 MPa
- Tensile Stress: 1.72 MPa @Strain 300 %
$ 1549/MT
- Specific Gravity: 0.970 g/cc
- Melt Flow: 0.200 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 70
- Tensile Strength at Break: 8.62 MPa
- Elongation at Break: 850 %
$ 1878/MT
- Specific Gravity: 0.940 g/cc
- Melt Flow: 4.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 64
- Hardness, Shore A: 69
- Tensile Strength at Break: 5.04 MPa
$ 1677/MT
- Specific Gravity: 0.930 g/cc
- Melt Flow: 0.440 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 40
- Tensile Strength at Break: 14.5 MPa
- Elongation at Break: 500 %
$ 2576/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 14.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 78
- Tensile Strength at Break: 11.7 MPa
- Elongation at Break: 640 %
$ 2566/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 27.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 10
- Tensile Strength at Break: 1.72 MPa
- Tensile Stress: 0.414 MPa @Strain 300 %
$ 1502/MT
- Specific Gravity: 1.11 g/cc
- Melt Flow: 1.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 55
- Tensile Strength at Break: 8.96 MPa
- Tensile Stress: 3.45 MPa @Strain 300 %
$ 1596/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 2.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 55
- Tensile Strength at Break: 6.34 MPa
- Elongation at Break: 680 %
$ 1815/MT
- Specific Gravity: 1.23 g/cc
- Hardness, Shore A: 65
- Tensile Strength, Yield: 16.5 MPa
- Elongation at Break: 330 %
- Brittleness Temperature: -40.0 °C
$ 1457/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 25
- Tensile Strength at Break: 7.10 MPa
- Tensile Stress: 1.55 MPa @Strain 300 %
$ 2588/MT
- Specific Gravity: 1.02 g/cc
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 12.0 MPa
- Tensile Stress: 4.69 MPa @Strain 50.0 %
$ 1891/MT
- Specific Gravity: 1.02 g/cc
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 12.0 MPa
- Tensile Stress: 4.69 MPa @Strain 50.0 %
$ 1595/MT
- Specific Gravity: 1.02 g/cc
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 12.0 MPa
- Tensile Stress: 4.69 MPa @Strain 50.0 %
$ 1467/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 15.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 65
- Tensile Strength at Break: 4.14 MPa
- Tensile Strength, Yield: 0.689 MPa @Strain 300 %
- Elongation at Break: 600 %
$ 2309/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 10.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 70
- Tensile Strength at Break: 6.55 MPa
- Elongation at Break: 650 %
$ 1628/MT
- Specific Gravity: 0.870 g/cc
- Melt Flow: 20.0 g/10 min @Load 2.16 kg, Temperature 125 °C
- Hardness, Shore OO: 25
- Tensile Strength at Break: 0.689 MPa
- Tensile Stress: 0.172 MPa @Strain 300 %
$ 1634/MT
- Specific Gravity: 1.25 g/cc
- Melt Flow: 5.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore D: 67
- Tensile Strength: 22.4 MPa
- Elongation at Break: 420 %
$ 2156/MT
- Specific Gravity: 1.13 g/cc
- Hardness, Shore A: 60
- Tensile Strength, Yield: 11.4 MPa
- Elongation at Break: 240 %
- Compression Set: 35 %
$ 1466/MT
- Specific Gravity: 1.05 g/cc
- Melt Flow: 20.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 25
- Tensile Strength at Break: 3.79 MPa
- Elongation at Break: 750 %
$ 2538/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 0.50 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 40
- Tensile Strength, Yield: 6.21 MPa
- Elongation at Break: 700 %
$ 1474/MT
- Specific Gravity: 1.12 g/cc
- Hardness, Shore A: 55
- Tensile Strength, Yield: 9.65 MPa
- Elongation at Break: 300 %
- Compression Set: 35 %
$ 1941/MT
- Specific Gravity: 1.09 g/cc
- Melt Flow: 1.9 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 73
- Tensile Strength, Yield: 13.5 MPa
- Elongation at Break: 680 %
$ 2371/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 0.50 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 45
- Tensile Strength, Yield: 6.89 MPa
- Elongation at Break: 700 %
$ 1916/MT
- Specific Gravity: 1.28 g/cc
- Hardness, Shore A: 85
- Tensile Strength: 10.7 MPa
- Elongation at Break: 550 %
- Brittleness Temperature: <= -50.0 °C
$ 1589/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.016 cm/cm
- Melt Flow: 17.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 67
- Tensile Strength at Break: 9.65 MPa
$ 1737/MT
- Specific Gravity: 1.09 g/cc
- Hardness, Shore A: 35
- Tensile Strength, Yield: 1.79 MPa
- Tensile Strength, Yield: 4.83 MPa
- Tensile Strength, Yield: 6.83 MPa
$ 1461/MT
- Specific Gravity: 1.02 g/cc
- Melt Flow: 14.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 79
- Tensile Strength at Break: 8.27 MPa
- Elongation at Break: 550 %
$ 1463/MT
- Specific Gravity: 0.890 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Flow: 20.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 60
- Tensile Strength at Break: 8.62 MPa
$ 1717/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 0.360 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 75
- Tensile Strength at Break: 14.8 MPa
- Elongation at Break: 620 %
$ 1717/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 20.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 55
- Tensile Strength at Break: 6.89 MPa
- Elongation at Break: 600 %
$ 1963/MT
- Specific Gravity: 0.910 g/cc
- Melt Flow: 3.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 92
- Tensile Strength at Break: 14.1 MPa
- Elongation at Break: 550 %
$ 2113/MT
- Specific Gravity: 1.00 g/cc
- Melt Flow: 1.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 75
- Hardness, Shore A: 80
- Tensile Strength at Break: 8.00 MPa
$ 1745/MT
- Specific Gravity: 0.920 g/cc
- Melt Flow: 3.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 48
- Tensile Strength at Break: 20.7 MPa
- Elongation at Break: 550 %
$ 1455/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 25.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 30
- Tensile Strength at Break: 6.21 MPa
- Tensile Stress: 1.03 MPa @Strain 300 %
$ 1761/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 6.00 g/10 min @Load 2.16 kg, Temperature 150 °C
- Hardness, Shore A: 18
- Hardness, Shore OO: 65
- Tensile Strength at Break: 3.79 MPa
$ 1795/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 2.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 61
- Tensile Strength at Break: 8.96 MPa
- Tensile Strength, Yield: 3.45 MPa @Strain 300 %
- Elongation at Break: 700 %
$ 1617/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 2.30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 65
- Tensile Strength at Break: 6.62 MPa
- Elongation at Break: 760 %
$ 1866/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 4.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 75
- Tensile Strength at Break: 15.2 MPa
- Tensile Stress: 5.52 MPa @Strain 300 %
$ 1569/MT
- Specific Gravity: 0.990 g/cc
- Hardness, Shore A: 45
- Tensile Strength: 4.48 MPa
- Elongation at Break: 500 %
$ 2459/MT
- Specific Gravity: 0.900 g/cc
- Linear Mold Shrinkage: 0.013 cm/cm
- Melt Flow: 2.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 90
- Tensile Strength at Break: 23.4 MPa
$ 1976/MT
- Specific Gravity: 1.19 g/cc
- Melt Flow: 0.200 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 65
- Tensile Strength at Break: 6.21 MPa
- Elongation at Break: 740 %
$ 1812/MT
- Specific Gravity: 1.05 g/cc
- Linear Mold Shrinkage: 0.013 cm/cm
- Linear Mold Shrinkage, Transverse: 0.015 cm/cm
- Melt Flow: 26.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 68.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1790/MT
- Density: 0.950 g/cc
- Hardness, Shore D: 38
- Hardness, Shore D: 41
- Tensile Strength at Break: 16.10 MPa
- Tensile Strength at Break: 18.40 MPa
$ 1700/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 3.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 33
- Tensile Strength at Break: 6.72 MPa
- Elongation at Break: 900 %
$ 2372/MT
- Density: 0.940 g/cc
- Hardness, Shore D: 46
- Hardness, Shore D: 50
- Tensile Strength at Break: 16.50 MPa
- Tensile Strength at Break: 18.00 MPa
$ 1729/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 2.50 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 92
- Tensile Strength at Break: 17.9 MPa
- Tensile Stress: 8.27 MPa @Strain 300 %
$ 1820/MT
- Specific Gravity: 0.900 g/cc
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm
- Linear Mold Shrinkage, Flow: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
$ 1487/MT
- Specific Gravity: 1.01 g/cc
- Melt Flow: 0.800 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 60
- Tensile Strength at Break: 6.17 MPa
- Elongation at Break: 650 %
$ 1840/MT
- Specific Gravity: 1.16 g/cc
- Hardness, Shore A: 65
- Tensile Strength, Yield: 5.52 MPa
- Tensile Strength, Yield: 14.5 MPa
- Tensile Strength, Yield: 16.2 MPa
$ 1509/MT
- Specific Gravity: 1.22 g/cc
- Melt Flow: 5.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 45
- Tensile Strength at Break: 5.52 MPa
- Tensile Stress: 2.07 MPa @Strain 300 %
$ 1711/MT
- Specific Gravity: 1.00 g/cc
- Melt Flow: 0.200 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 70
- Tensile Strength at Break: 6.21 MPa
- Elongation at Break: 570 %
$ 1969/MT
- Specific Gravity: 1.16 g/cc
- Melt Flow: 10.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 32
- Tensile Strength at Break: 2.76 MPa
- Tensile Stress: 1.38 MPa @Strain 300 %
$ 2164/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 1.5 g/10 min
- Rear Barrel Temperature: 171 - 193 °C
- Middle Barrel Temperature: 177 - 199 °C
- Front Barrel Temperature: 182 - 204 °C
$ 1476/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 12.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 87
- Tensile Strength at Break: 11.0 MPa
- Elongation at Break: 600 %
$ 1726/MT
- Specific Gravity: 1.10 g/cc
- Melt Flow: 30.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 77
- Tensile Strength at Break: 4.31 MPa
- Elongation at Break: 600 %
$ 1578/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 17.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 83
- Tensile Strength: 9.03 MPa
- Elongation at Break: 860 %
$ 1898/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 75
- Tensile Strength at Break: 13.8 MPa
- Tensile Stress: 6.89 MPa @Strain 300 %
$ 1893/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 1.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 65
- Tensile Strength at Break: 14.5 MPa
- Tensile Strength, Yield: 5.52 MPa @Strain 300 %
- Elongation at Break: 600 %
$ 1592/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 16.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 45
- Tensile Strength at Break: 7.45 MPa
- Elongation at Break: 890 %
$ 1809/MT
- Specific Gravity: 0.880 g/cc
- Linear Mold Shrinkage: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.017 cm/cm
- Melt Flow: 10.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 38
$ 1693/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 83
- Tensile Strength at Break: 5.52 MPa
- Elongation at Break: 890 %
$ 2398/MT
- Specific Gravity: 0.900 g/cc
- Hardness, Shore A: 88
- Tensile Strength: 12.4 MPa
- Elongation at Break: 750 %
- Brittleness Temperature: <= -50.0 °C
$ 1603/MT
- Density: 1.29 g/cc
- Hardness, Shore A: 90
- Tensile Strength at Break: 9.797 MPa
- Elongation at Break: 450 %
- 100% Modulus: 0.00530 GPa
$ 1979/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 5.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 50
- Tensile Strength at Break: 10.3 MPa
- Tensile Stress: 4.31 MPa @Strain 300 %
$ 1593/MT
- Specific Gravity: 1.16 g/cc
- Melt Flow: 28.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 40
- Tensile Strength at Break: 4.83 MPa
- Tensile Stress: 1.38 MPa @Strain 300 %
$ 1595/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 25.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 55
- Tensile Strength at Break: 6.89 MPa
- Elongation at Break: 800 %
$ 1790/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage: 0.010 - 0.025 cm/cm
- Hardness, Shore A: 75
- Tensile Strength, Yield: 8.27 MPa
- Tensile Strength, Yield: 17.2 MPa
$ 2251/MT
- Specific Gravity: 0.940 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Melt Flow: 9.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 36
$ 1890/MT
- Specific Gravity: 0.980 g/cc
- Linear Mold Shrinkage: 0.025 cm/cm
- Melt Flow: 35 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 35
- Tensile Strength, Yield: 6.21 MPa
- Elongation at Break: 400 %
$ 1494/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 3.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 35
- Tensile Strength at Break: 5.52 MPa
- Tensile Stress: 1.21 MPa @Strain 300 %
$ 1497/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 32.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 64
- Tensile Strength at Break: 6.72 MPa
- Elongation at Break: 720 %
$ 1595/MT
- Density: 0.960 g/cc
- Hardness, Shore A: 53
- Hardness, Shore A: 56
- Tensile Strength at Break: 3.60 MPa
- Tensile Strength at Break: 5.20 MPa
Delivery Elastomer Teknor Apex Company
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
container vessels for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.