$ 2480/MT
- Specific Gravity: 1.41 g/cc
- Tensile Strength, Yield: 49.0 MPa
- Elongation at Break: 100 %
- Izod Impact, Notched: 0.694 J/cm
- Maximum Service Temperature, Air: 190 °C @Time 1800 sec
- Vicat Softening Point: 91.1 °C
$ 1611/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore C: 71
- Tensile Strength at Break: 22.1 MPa
- Elongation at Break: 320 %
- Maximum Service Temperature, Air: 105 °C
$ 1492/MT
- Specific Gravity: 1.30 g/cc
- Linear Mold Shrinkage: 0.015 - 0.018 cm/cm
- Hardness, Shore A: 70
- Tensile Strength at Break: 13.8 MPa
- Elongation at Break: 430 %
$ 1695/MT
- Specific Gravity: 1.32 g/cc
- Hardness, Shore D: 80
- Tensile Strength at Break: 43.6 MPa
- Elongation at Break: 150 %
- Tensile Modulus: 2.48 GPa
$ 1604/MT
- Specific Gravity: 1.23 g/cc
- Hardness, Shore A: 62
- Tensile Strength, Yield: 12.3 MPa
- Elongation at Break: 380 %
- Maximum Service Temperature, Air: 190 °C @Time >=Error in fixSigDigits: @digits must be between 1 a sec
$ 1481/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 70
- Tensile Strength, Yield: 4.83 MPa
- Tensile Strength, Yield: 12.2 MPa
- Elongation at Break: 380 %
$ 1595/MT
- Specific Gravity: 1.24 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Yield: 16.0 MPa
- Elongation at Break: 320 %
- Brittleness Temperature: -35.0 °C
$ 1689/MT
- Specific Gravity: 1.25 g/cc
- Hardness, Shore A: 90
- Tensile Strength at Break: 22.1 MPa
- Elongation at Break: 330 %
- Maximum Service Temperature, Air: 60.0 °C
$ 1457/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 85
- Tensile Strength at Break: 19.0 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 50.0 °C
$ 1951/MT
- Specific Gravity: 1.23 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore A: 80
- Tensile Strength at Break: 17.0 MPa
- Elongation at Break: 340 %
$ 1604/MT
- Specific Gravity: 1.32 g/cc
- Hardness, Shore C: 86
- Tensile Strength at Break: 19.0 MPa
- Elongation at Break: 360 %
- Maximum Service Temperature, Air: 105 °C
$ 1450/MT
- Specific Gravity: 1.38 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore A: 86
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 280 %
$ 1577/MT
- Specific Gravity: 1.32 g/cc
- Hardness, Shore C: 73
- Tensile Strength at Break: 22.1 MPa
- Elongation at Break: 280 %
- Maximum Service Temperature, Air: 80.0 °C
$ 2209/MT
- Specific Gravity: 1.27 g/cc
- Hardness, Shore A: 88
- Tensile Strength, Yield: 6.69 MPa
- Elongation at Break: 110 %
- Volume Resistivity: 14 ohm-cm
$ 1680/MT
- Specific Gravity: 1.42 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore A: 85
- Tensile Strength at Break: 13.1 MPa
- Elongation at Break: 290 %
$ 2083/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 85
- Hardness, Shore A: 91
- Tensile Strength at Break: 20.2 MPa
- Tensile Strength, Yield: 10.6 MPa
$ 2500/MT
- Specific Gravity: 1.39 g/cc
- Hardness, Shore C: 86
- Tensile Strength at Break: 17.6 MPa
- Elongation at Break: 280 %
- Maximum Service Temperature, Air: 60.0 °C
$ 1683/MT
- Specific Gravity: 1.23 g/cc
- Hardness, Shore A: 68
- Tensile Strength, Yield: 13.7 MPa
- Elongation at Break: 360 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 1520/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore D: 76
- Tensile Strength, Yield: 46.1 MPa
- Elongation at Break: 110 %
- Izod Impact, Notched: 1.39 J/cm
$ 2572/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 3.80 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 45
- Tensile Strength at Break: 6.27 MPa
- Elongation at Break: 830 %
$ 1638/MT
- Specific Gravity: 1.33 g/cc
- Tensile Strength, Yield: 47.1 MPa
- Elongation at Break: 150 %
- Izod Impact, Notched: 2.46 J/cm
- Vicat Softening Point: 81.1 °C
$ 1540/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore C: 67
- Tensile Strength at Break: 17.8 MPa
- Tensile Strength, Yield: 11.9 MPa
- Elongation at Break: 330 %
- Brittleness Temperature: -16.0 °C
$ 1570/MT
- Specific Gravity: 1.44 g/cc
- Hardness, Shore A: 84
- Tensile Strength, Yield: 15.02 MPa
- Tensile Strength, Yield: 16.7 MPa
- Elongation at Break: 224 %
- Elongation at Break: 280 %
$ 1447/MT
- Specific Gravity: 1.40 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 14.1 MPa
- Tensile Strength: 8.48 MPa
- Elongation at Break: 390 %
$ 1591/MT
- Specific Gravity: 1.25 g/cc
- Hardness, Shore A: 75
- Tensile Strength, Yield: 16.2 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 190 °C @Time >=3600 sec
$ 1608/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 90
- Tensile Strength at Break: 17.9 MPa
- Elongation at Break: 290 %
- Maximum Service Temperature, Air: 105 °C
$ 1784/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 70
- Tensile Strength, Yield: 5.52 MPa
- Tensile Strength, Yield: 12.6 MPa
- Elongation at Break: 370 %
$ 2479/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore A: 70
- Hardness, Shore A: 76
- Tensile Strength at Break: 12.3 MPa
- Tensile Strength, Yield: 4.48 MPa
$ 1836/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 19.0 MPa
- Elongation at Break: 410 %
- Brittleness Temperature: -30.0 °C
- Appearance: Clear/Transparent
$ 1527/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 65
- Tensile Strength, Yield: 14.5 MPa
- Elongation at Break: 400 %
- Brittleness Temperature: -39.0 °C
- Melt Temperature: 171 °C
$ 1902/MT
- Specific Gravity: 1.43 g/cc
- Hardness, Shore C: 85
- Tensile Strength at Break: 16.5 MPa
- Elongation at Break: 320 %
- Maximum Service Temperature, Air: 75.0 °C
$ 2224/MT
- Specific Gravity: 1.54 g/cc
- Hardness, Shore C: 74
- Hardness, Shore C: 85
- Tensile Strength at Break: 18.1 MPa
- Elongation at Break: 280 %
$ 2022/MT
- Specific Gravity: 1.13 g/cc
- Hardness, Shore A: 55
- Tensile Strength, Yield: 3.31 MPa
- Tensile Strength, Yield: 10.0 MPa
- Elongation at Break: 440 %
$ 1606/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 65
- Tensile Strength, Yield: 13.0 MPa
- Elongation at Break: 370 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 1773/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore A: 89
- Tensile Strength, Yield: 13.53 MPa
- Tensile Strength, Yield: 15.0 MPa
- Elongation at Break: 104 %
$ 1807/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 60
- Tensile Strength, Yield: 3.86 MPa
- Tensile Strength, Yield: 10.0 MPa
- Elongation at Break: 390 %
$ 1605/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore A: 85
- Tensile Strength at Break: 17.2 MPa
- Elongation at Break: 360 %
- Maximum Service Temperature, Air: 105 °C
$ 2365/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 58
- Tensile Strength, Yield: 11.8 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 1801/MT
- Specific Gravity: 1.23 g/cc
- Hardness, Shore A: 62
- Tensile Strength, Yield: 12.3 MPa
- Elongation at Break: 380 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 1660/MT
- Specific Gravity: 1.19 g/cc
- Hardness, Shore A: 65
- Tensile Strength, Yield: 11.1 MPa
- Elongation at Break: 390 %
- Brittleness Temperature: -41.0 °C
$ 2259/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore C: 88
- Tensile Strength at Break: 24.1 MPa
- Elongation at Break: 280 %
- Maximum Service Temperature, Air: 80.0 °C
$ 1465/MT
- Specific Gravity: 1.16 g/cc
- Hardness, Shore A: 58
- Tensile Strength, Yield: 12.5 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 1622/MT
- Specific Gravity: 1.25 g/cc
- Hardness, Shore A: 90
- Tensile Strength, Yield: 12.8 MPa
- Tensile Strength, Yield: 19.7 MPa
- Elongation at Break: 340 %
$ 2358/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 75
- Tensile Strength at Break: 15.5 MPa
- Elongation at Break: 360 %
- Brittleness Temperature: -36.0 °C
- Appearance: Opaque
$ 1949/MT
- Specific Gravity: 1.54 g/cc
- Hardness, Shore A: 86
- Tensile Strength at Break: 14.1 MPa
- Elongation at Break: 280 %
- Maximum Service Temperature, Air: 90.0 °C
$ 1551/MT
- Specific Gravity: 1.17 g/cc
- Hardness, Shore A: 70
- Tensile Strength at Break: 13.4 MPa
- Elongation at Break: 410 %
- Brittleness Temperature: -38.0 °C
- Appearance: Clear/Transparent
$ 1799/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore A: 93
- Hardness, Shore C: 68
- Tensile Strength, Yield: 12.2 MPa
- Elongation at Break: 160 %
- Volume Resistivity: 6.5 ohm-cm
$ 1658/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Yield: 7.31 MPa
- Tensile Strength, Yield: 11.0 MPa
- Elongation at Break: 240 %
$ 1951/MT
- Specific Gravity: 1.39 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore C: 82
- Tensile Strength at Break: 18.8 MPa
- Elongation at Break: 280 %
$ 2337/MT
- Specific Gravity: 1.23 g/cc
- Hardness, Shore A: 68
- Tensile Strength, Yield: 13.7 MPa
- Elongation at Break: 260 %
- Maximum Service Temperature, Air: 190 °C @Time >=Error in fixSigDigits: @digits must be between 1 a sec
$ 2006/MT
- Specific Gravity: 1.24 g/cc
- Hardness, Shore A: 73
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 105 °C
- Appearance: Clear
$ 1838/MT
- Specific Gravity: 1.40 g/cc
- Tensile Strength, Yield: 49.0 MPa
- Elongation at Break: 150 %
- Izod Impact, Notched: 4.43 J/cm
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
- Vicat Softening Point: 80.0 °C
$ 2260/MT
- Specific Gravity: 1.45 g/cc
- Tensile Strength, Yield: 49.0 MPa
- Elongation at Break: 150 %
- Izod Impact, Notched: 0.587 J/cm
- Maximum Service Temperature, Air: 190 °C @Time Error in fixSigDigits: @digits must be between 1 a sec
- Vicat Softening Point: 96.1 °C
$ 1884/MT
- Specific Gravity: 1.44 g/cc
- Tensile Strength, Yield: 44.1 MPa
- Elongation at Break: 160 %
- Izod Impact, Notched: 1.39 J/cm
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
- Vicat Softening Point: 90.0 °C
$ 1553/MT
- Specific Gravity: 1.23 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Yield: 17.0 MPa
- Elongation at Break: 340 %
- Brittleness Temperature: -29.0 °C
$ 2110/MT
- Specific Gravity: 1.17 g/cc
- Hardness, Shore A: 52
- Tensile Strength: 9.79 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 1877/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Yield: 8.27 MPa
- Tensile Strength, Yield: 16.2 MPa
- Elongation at Break: 360 %
$ 1664/MT
- Specific Gravity: 1.19 g/cc
- Melt Flow: 5.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 7.93 MPa
- Elongation at Break: 550 %
$ 1478/MT
- Specific Gravity: 1.16 g/cc
- Hardness, Shore A: 55
- Tensile Strength, Yield: 3.59 MPa
- Tensile Strength, Yield: 10.3 MPa
- Elongation at Break: 460 %
$ 1774/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 16.4 MPa
- Elongation at Break: 380 %
- Maximum Service Temperature, Air: 60.0 °C
$ 1784/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 75
- Tensile Strength, Yield: 6.89 MPa
- Tensile Strength, Yield: 16.2 MPa
- Elongation at Break: 420 %
$ 1496/MT
- Specific Gravity: 1.28 g/cc
- Hardness, Shore A: 83
- Tensile Strength at Break: 17.9 MPa
- Elongation at Break: 250 %
- Maximum Service Temperature, Air: 105 °C
$ 1721/MT
- Specific Gravity: 1.24 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Yield: 18.1 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 1484/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 69
- Tensile Strength: 15.7 MPa
- Elongation at Break: 250 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 2175/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 69
- Tensile Strength, Yield: 9.79 MPa
- Elongation at Break: 200 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 1794/MT
- Specific Gravity: 1.44 g/cc
- Tensile Strength, Yield: 49.0 MPa
- Elongation at Break: 120 %
- Izod Impact, Notched: 0.694 J/cm
- Maximum Service Temperature, Air: 190 °C @Time >=Error in fixSigDigits: @digits must be between 1 a sec
- Vicat Softening Point: 90.0 °C
$ 2270/MT
- Specific Gravity: 1.34 g/cc
- Tensile Strength, Yield: 41.2 MPa
- Elongation at Break: 180 %
- Izod Impact, Notched: 1.17 J/cm
- Vicat Softening Point: 72.2 °C
$ 2132/MT
- Specific Gravity: 1.25 g/cc
- Hardness, Shore A: 72
- Tensile Strength at Break: 14.5 MPa
- Elongation at Break: 330 %
- Maximum Service Temperature, Air: 105 °C
$ 1973/MT
- Specific Gravity: 1.17 g/cc
- Hardness, Shore A: 70
- Tensile Strength at Break: 15.2 MPa
- Elongation at Break: 430 %
- Maximum Service Temperature, Air: 50.0 °C
$ 1560/MT
- Specific Gravity: 1.26 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore A: 90
- Tensile Strength at Break: 17.8 MPa
- Elongation at Break: 240 %
$ 1796/MT
- Specific Gravity: 1.27 g/cc
- Hardness, Shore A: 82
- Tensile Strength at Break: 18.6 MPa
- Elongation at Break: 350 %
$ 1626/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 82
- Tensile Strength, Yield: 17.7 MPa
- Elongation at Break: 310 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 1720/MT
- Specific Gravity: 0.920 g/cc
- Hardness, Shore A: 35
- Tensile Strength at Break: 2.90 MPa
- Elongation at Break: 350 %
- 100% Modulus: 0.000827 GPa
$ 1847/MT
- Specific Gravity: 0.930 g/cc
- Hardness, Shore D: 50
- Tensile Strength at Break: 22.8 MPa
- Elongation at Break: 600 %
- 100% Modulus: 0.0145 GPa
$ 1838/MT
- Specific Gravity: 0.940 g/cc
- Hardness, Shore A: 55
- Tensile Strength at Break: 3.86 MPa
- Elongation at Break: 300 %
- 100% Modulus: 0.00214 GPa
$ 2066/MT
- Specific Gravity: 0.940 g/cc
- Hardness, Shore A: 73
- Tensile Strength at Break: 6.76 MPa
- Elongation at Break: 340 %
- 100% Modulus: 0.00393 GPa
$ 1510/MT
- Specific Gravity: 0.930 g/cc
- Hardness, Shore A: 87
- Tensile Strength at Break: 11.4 MPa
- Elongation at Break: 400 %
- 100% Modulus: 0.00655 GPa
$ 1469/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 86
- Tensile Strength at Break: 20.5 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 105 °C
$ 1478/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore C: 65
- Tensile Strength at Break: 20.3 MPa
- Elongation at Break: 360 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1494/MT
- Specific Gravity: 1.33 g/cc
- Tensile Strength, Yield: 34.3 MPa
- Elongation at Break: 150 %
- Izod Impact, Notched: 0.491 J/cm
- Vicat Softening Point: 75.0 °C
$ 1590/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 75
- Tensile Strength, Yield: 7.03 MPa
- Tensile Strength, Yield: 14.5 MPa
- Elongation at Break: 370 %
$ 2165/MT
- Specific Gravity: 1.58 g/cc
- Hardness, Shore C: 86
- Tensile Strength at Break: 19.3 MPa
- Elongation at Break: 230 %
- Maximum Service Temperature, Air: 75.0 °C
$ 2144/MT
- Specific Gravity: 1.24 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore A: 85
- Tensile Strength at Break: 15.0 MPa
- Elongation at Break: 250 %
$ 1864/MT
- Specific Gravity: 1.40 g/cc
- Hardness, Shore A: 91
- Tensile Strength, Yield: 17.00 MPa
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Break: 192 %
$ 1684/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 70
- Tensile Strength at Break: 14.8 MPa
- Elongation at Break: 380 %
- Appearance: Clear
$ 1627/MT
- Specific Gravity: 1.59 g/cc
- Hardness, Shore C: 87
- Hardness, Shore C: 92
- Tensile Strength at Break: 17.9 MPa
- Elongation at Break: 200 %
$ 1534/MT
- Specific Gravity: 1.29 g/cc
- Hardness, Shore A: 70
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 410 %
- Brittleness Temperature: -38.0 °C
- Appearance: Opaque
$ 1687/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 70
- Tensile Strength at Break: 15.5 MPa
- Elongation at Break: 300 %
- Brittleness Temperature: -20.0 °C
$ 2440/MT
- Specific Gravity: 1.23 g/cc
- Hardness, Shore A: 82
- Tensile Strength, Yield: 16.7 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 170 °C @Time >=Error in fixSigDigits: @digits must be between 1 a sec
$ 1706/MT
- Specific Gravity: 1.29 g/cc
- Melt Flow: 1.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 53
- Tensile Strength at Break: 8.27 MPa
- Elongation at Break: 530 %
$ 1447/MT
- Specific Gravity: 1.24 g/cc
- Hardness, Shore A: 79
- Tensile Strength, Yield: 17.7 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 1837/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 75
- Tensile Strength at Break: 17.2 MPa
- Elongation at Break: 430 %
- Brittleness Temperature: -38.0 °C
- Appearance: Clear/Transparent
$ 2445/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 70
- Tensile Strength, Yield: 12.1 MPa
- Elongation at Break: 330 %
- Brittleness Temperature: -41.0 °C
$ 2184/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore A: 75
- Hardness, Shore A: 81
- Tensile Strength at Break: 16.1 MPa
- Tensile Strength, Yield: 6.45 MPa
$ 1507/MT
- Specific Gravity: 1.43 g/cc
- Tensile Strength, Yield: 50.0 MPa
- Elongation at Break: 160 %
- Izod Impact, Notched: 0.801 J/cm
- Maximum Service Temperature, Air: 190 °C @Time >=3600 sec
- Vicat Softening Point: 96.1 °C
$ 1810/MT
- Specific Gravity: 1.17 g/cc
- Hardness, Shore A: 60
- Tensile Strength, Yield: 3.86 MPa
- Tensile Strength, Yield: 10.7 MPa
- Elongation at Break: 450 %
$ 1518/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 85
- Tensile Strength at Break: 19.7 MPa
- Elongation at Break: 360 %
- Maximum Service Temperature, Air: 105 °C
$ 2057/MT
- Specific Gravity: 1.56 g/cc
- Hardness, Shore A: 86
- Tensile Strength at Break: 16.9 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1534/MT
- Specific Gravity: 1.28 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Yield: 18.1 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 2226/MT
- Specific Gravity: 1.23 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Yield: 10.3 MPa
- Tensile Strength, Yield: 17.6 MPa
- Elongation at Break: 350 %
$ 1878/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 67
- Tensile Strength: 15.7 MPa
- Elongation at Break: 250 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 2319/MT
- Specific Gravity: 1.18 g/cc
- Hardness, Shore A: 70
- Tensile Strength at Break: 14.5 MPa
- Elongation at Break: 400 %
- Brittleness Temperature: -44.0 °C
- Appearance: Clear/Transparent
$ 1682/MT
- Specific Gravity: 1.27 g/cc
- Hardness, Shore A: 90
- Tensile Strength, Yield: 21.0 MPa
- Elongation at Break: 290 %
- Brittleness Temperature: -24.0 °C
$ 1711/MT
- Specific Gravity: 1.16 g/cc
- Hardness, Shore A: 60
- Tensile Strength at Break: 9.65 MPa
- Elongation at Break: 400 %
- Brittleness Temperature: -44.0 °C
- Appearance: Clear/Transparent
$ 1624/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore C: 84
- Tensile Strength at Break: 24.3 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 60.0 °C
$ 1544/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore D: 75
- Tensile Strength, Yield: 43.2 MPa
- Elongation at Break: 170 %
- Izod Impact, Notched: 9.08 J/cm
- Vicat Softening Point: 77.2 °C
$ 1580/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore C: 82
- Tensile Strength at Break: 17.9 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1827/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 75
- Tensile Strength at Break: 16.5 MPa
- Elongation at Break: 400 %
- Brittleness Temperature: -40.0 °C
- Appearance: Clear/Transparent
$ 1721/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore A: 86
- Tensile Strength at Break: 17.9 MPa
- Elongation at Break: 360 %
- Maximum Service Temperature, Air: 105 °C
$ 1501/MT
- Specific Gravity: 1.60 g/cc
- Hardness, Shore C: 83
- Tensile Strength at Break: 17.2 MPa
- Elongation at Break: 200 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1996/MT
- Specific Gravity: 1.09 g/cc
- Melt Flow: 2.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 73
- Tensile Strength at Break: 13.5 MPa
- Elongation at Break: 680 %
$ 2099/MT
- Specific Gravity: 1.31 g/cc
- Hardness, Shore C: 71
- Tensile Strength at Break: 11.0 MPa
- Elongation at Break: 100 %
- Volume Resistivity: 5.0 ohm-cm @Temperature 50.0 °C
$ 1518/MT
- Specific Gravity: 1.43 g/cc
- Hardness, Shore A: 85
- Tensile Strength at Break: 15.4 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 80.0 °C
$ 1469/MT
- Specific Gravity: 1.13 g/cc
- Hardness, Shore A: 45
- Tensile Strength, Yield: 2.24 MPa
- Tensile Strength, Yield: 7.58 MPa
- Elongation at Break: 480 %
$ 1820/MT
- Specific Gravity: 1.16 g/cc
- Hardness, Shore A: 60
- Tensile Strength, Yield: 10.7 MPa
- Elongation at Break: 450 %
- Melt Temperature: 168 °C
$ 2007/MT
- Specific Gravity: 1.17 g/cc
- Hardness, Shore A: 60
- Tensile Strength, Yield: 3.86 MPa
- Tensile Strength, Yield: 10.7 MPa
- Elongation at Break: 450 %
$ 1526/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Yield: 16.2 MPa
- Elongation at Break: 350 %
- Brittleness Temperature: -28.0 °C
$ 1448/MT
- Specific Gravity: 1.42 g/cc
- Hardness, Shore C: 73
- Tensile Strength at Break: 19.3 MPa
- Elongation at Break: 280 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1584/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 55
- Tensile Strength, Yield: 11.8 MPa
- Elongation at Break: 390 %
- Maximum Service Temperature, Air: 190 °C @Time >=3600 sec
$ 2193/MT
- Specific Gravity: 1.32 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Yield: 15.9 MPa
- Elongation at Break: 230 %
- Brittleness Temperature: -20.0 °C
$ 2572/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore A: 72
- Tensile Strength at Break: 15.2 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 105 °C
$ 1596/MT
- Specific Gravity: 1.41 g/cc
- Hardness, Shore A: 83
- Tensile Strength, Yield: 16.8 MPa
- Tensile Strength, Yield: 18.6 MPa
- Elongation at Break: 238 %
- Elongation at Break: 280 %
$ 1553/MT
- Specific Gravity: 0.960 g/cc
- Melt Flow: 0.900 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 65
- Tensile Strength at Break: 8.96 MPa
- Elongation at Break: 750 %
$ 1810/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore A: 65
- Tensile Strength at Break: 13.1 MPa
- Elongation at Break: 390 %
- Maximum Service Temperature, Air: 105 °C
$ 2045/MT
- Specific Gravity: 1.21 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore A: 80
- Tensile Strength at Break: 15.5 MPa
- Elongation at Break: 380 %
$ 1903/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 90
- Tensile Strength, Yield: 15.2 MPa
- Tensile Strength, Yield: 20.7 MPa
- Elongation at Break: 310 %
$ 1721/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 3.10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 60
- Tensile Strength at Break: 9.24 MPa
- Elongation at Break: 880 %
$ 1830/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore C: 90
- Tensile Strength at Break: 24.1 MPa
- Elongation at Break: 270 %
- Brittleness Temperature: -10.0 °C
$ 1869/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 8.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 41
- Tensile Strength at Break: 3.45 MPa
- Elongation at Break: 730 %
$ 1817/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 75
- Tensile Strength, Yield: 16.5 MPa
- Elongation at Break: 360 %
- Brittleness Temperature: -31.0 °C
- Melt Temperature: 177 °C
$ 1451/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore C: 69
- Tensile Strength at Break: 21.0 MPa
- Elongation at Break: 320 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1650/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore C: 69
- Tensile Strength at Break: 21.0 MPa
- Elongation at Break: 320 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1566/MT
- Apparent Bulk Density: 0.650 g/cc
- Flexural Modulus: 0.220 GPa
- Maximum Service Temperature, Air: 190 °C @Time >=3600 sec
- Vicat Softening Point: 78.9 °C
$ 1580/MT
- Specific Gravity: 1.36 g/cc
- Hardness, Shore A: 74
- Tensile Strength at Break: 14.2 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1463/MT
- Specific Gravity: 1.26 g/cc
- Hardness, Shore A: 90
- Tensile Strength, Yield: 17.8 MPa
- Elongation at Break: 240 %
- Brittleness Temperature: -15.0 °C
$ 1455/MT
- Specific Gravity: 1.52 g/cc
- Tensile Strength, Yield: 44.1 MPa
- Elongation at Break: 120 %
- Izod Impact, Notched: 0.390 J/cm
- Maximum Service Temperature, Air: 190 °C @Time >=Error in fixSigDigits: @digits must be between 1 a sec
- Vicat Softening Point: 97.8 °C
$ 1773/MT
- Specific Gravity: 1.26 g/cc
- Hardness, Shore A: 79
- Hardness, Shore A: 85
- Tensile Strength at Break: 6.89 MPa
- Elongation at Break: 300 %
$ 2563/MT
- Specific Gravity: 1.27 g/cc
- Hardness, Shore A: 85
- Hardness, Shore A: 91
- Tensile Strength at Break: 20.0 MPa
- Elongation at Break: 310 %
- Brittleness Temperature: -26.0 °C
$ 2165/MT
- Specific Gravity: 1.12 g/cc
- Hardness, Shore A: 45
- Tensile Strength, Yield: 7.10 MPa
- Elongation at Break: 480 %
- Brittleness Temperature: -52.0 °C
$ 2248/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore A: 75
- Tensile Strength, Yield: 15.4 MPa
- Elongation at Break: 280 %
- Brittleness Temperature: -33.0 °C
$ 1852/MT
- Specific Gravity: 1.23 g/cc
- Hardness, Shore A: 75
- Tensile Strength at Break: 15.9 MPa
- Elongation at Break: 360 %
- Maximum Service Temperature, Air: 60.0 °C
$ 1610/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore C: 70
- Tensile Strength at Break: 22.4 MPa
- Elongation at Break: 270 %
- Maximum Service Temperature, Air: 80.0 °C
$ 1598/MT
- Specific Gravity: 1.65 g/cc
- Viscosity: 473000 cP @Frequency 1000 Hz, Temperature 177 °C
- Hardness, Shore C: 86
- Hardness, Shore C: 91
- Tensile Strength at Break: 15.9 MPa
$ 2112/MT
- Specific Gravity: 1.11 g/cc
- Melt Flow: 24 g/10 min @Load 5.00 kg, Temperature 177 °C
- Hardness, Shore A: 50
- Tensile Strength, Yield: 5.93 MPa
- Tensile Strength, Yield: 9.487 MPa
$ 1600/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore A: 86
- Tensile Strength, Yield: 17.62 MPa
- Tensile Strength, Yield: 19.6 MPa
- Elongation at Break: 221 %
- Elongation at Break: 260 %
$ 1449/MT
- Specific Gravity: 1.25 g/cc
- Hardness, Shore A: 74
- Tensile Strength at Break: 13.8 MPa
- Tensile Strength: 6.65 MPa
- Elongation at Break: 320 %
$ 1908/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 75
- Tensile Strength at Break: 16.2 MPa
- Tensile Strength: 6.89 MPa @Strain 100 %
- Elongation at Break: 470 %
$ 1712/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 70
- Tensile Strength at Break: 14.5 MPa
- Elongation at Break: 410 %
- Maximum Service Temperature, Air: 75.0 °C
$ 2242/MT
- Specific Gravity: 1.42 g/cc
- Tensile Strength, Yield: 51.0 MPa
- Elongation at Break: 160 %
- Izod Impact, Notched: 0.801 J/cm
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
- Vicat Softening Point: 93.9 °C
$ 1505/MT
- Specific Gravity: 1.25 g/cc
- Hardness, Shore A: 85
- Hardness, Shore A: 91
- Tensile Strength, Yield: 18.1 MPa
- Elongation at Break: 320 %
- Brittleness Temperature: -31.0 °C
$ 2082/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore D: 75
- Tensile Strength, Yield: 40.2 MPa
- Elongation at Break: 130 %
- Izod Impact, Notched: 9.08 J/cm
- Vicat Softening Point: 77.2 °C
$ 2382/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 2.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 55
- Tensile Strength at Break: 9.17 MPa
- Elongation at Break: 920 %
$ 1478/MT
- Specific Gravity: 1.24 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Yield: 19.0 MPa
- Elongation at Break: 360 %
- Brittleness Temperature: -21.0 °C
- Melt Temperature: 179 °C
$ 1450/MT
- Specific Gravity: 1.12 g/cc
- Hardness, Shore A: 39
- Tensile Strength at Break: 7.17 MPa
- Tensile Strength, Yield: 2.07 MPa
- Elongation at Break: 460 %
- Brittleness Temperature: -56.0 °C
$ 1795/MT
- Specific Gravity: 1.31 g/cc
- Hardness, Shore A: 76
- Tensile Strength, Yield: 7.4980 MPa
- Tensile Strength, Yield: 10.0 MPa
- Elongation at Break: 135 %
$ 1464/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 76
- Tensile Strength, Yield: 16.2 MPa
- Elongation at Break: 340 %
- Maximum Service Temperature, Air: 190 °C @Time >=Error in fixSigDigits: @digits must be between 1 a sec
$ 1998/MT
- Specific Gravity: 1.16 g/cc
- Hardness, Shore A: 60
- Tensile Strength, Yield: 10.2 MPa
- Elongation at Break: 370 %
- Melt Temperature: 168 °C
$ 1502/MT
- Specific Gravity: 1.29 g/cc
- Hardness, Shore A: 70
- Hardness, Shore A: 76
- Tensile Strength at Break: 14.3 MPa
- Tensile Strength, Yield: 5.07 MPa
$ 1489/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 76
- Tensile Strength, Yield: 13.7 MPa
- Elongation at Break: 260 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 1783/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 16.5 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 80.0 °C
$ 1833/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore A: 79
- Tensile Strength, Yield: 9.93 MPa
- Tensile Strength, Yield: 11.0 MPa
- Elongation at Break: 184 %
$ 1717/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 15.2 MPa
- Elongation at Break: 380 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1461/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore C: 90
- Tensile Strength at Break: 24.1 MPa
- Elongation at Break: 240 %
- Maximum Service Temperature, Air: 105 °C
$ 2180/MT
- Specific Gravity: 1.19 g/cc
- Linear Mold Shrinkage: 0.015 - 0.018 cm/cm
- Hardness, Shore A: 70
- Tensile Strength at Break: 13.1 MPa
- Elongation at Break: 450 %
$ 1851/MT
- Specific Gravity: 1.11 g/cc
- Hardness, Shore A: 45
- Tensile Strength, Yield: 8.55 MPa
- Elongation at Break: 280 %
- Compression Set: 32 %
$ 2394/MT
- Specific Gravity: 1.25 g/cc
- Hardness, Shore A: 86
- Tensile Strength at Break: 17.9 MPa
- Elongation at Break: 300 %
$ 1725/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 85
- Tensile Strength at Break: 16.5 MPa
- Elongation at Break: 370 %
- Maximum Service Temperature, Air: 105 °C
$ 1553/MT
- Specific Gravity: 1.26 g/cc
- Linear Mold Shrinkage: 0.015 - 0.018 cm/cm
- Hardness, Shore A: 60
- Tensile Strength at Break: 11.4 MPa
- Elongation at Break: 440 %
$ 1971/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 75
- Tensile Strength at Break: 16.5 MPa
- Elongation at Break: 410 %
- Appearance: Clear
$ 1647/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore D: 83
- Tensile Strength at Break: 45.0 MPa
- Elongation at Break: 56 %
- Tensile Modulus: 2.75 GPa
$ 1859/MT
- Specific Gravity: 1.13 g/cc
- Hardness, Shore A: 45
- Tensile Strength, Yield: 2.24 MPa
- Tensile Strength, Yield: 7.58 MPa
- Elongation at Break: 480 %
$ 1727/MT
- Specific Gravity: 1.19 g/cc
- Hardness, Shore A: 70
- Tensile Strength at Break: 12.8 MPa
- Elongation at Break: 400 %
- Brittleness Temperature: -43.0 °C
- Appearance: Clear/Transparent
$ 1611/MT
- Specific Gravity: 1.23 g/cc
- Hardness, Shore A: 76
- Tensile Strength, Yield: 16.2 MPa
- Elongation at Break: 330 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 2382/MT
- Specific Gravity: 1.31 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 17.9 MPa
- Elongation at Break: 350 %
- Brittleness Temperature: -31.0 °C
- Appearance: Opaque
$ 1944/MT
- Specific Gravity: 1.52 g/cc
- Hardness, Shore A: 91
- Tensile Strength, Yield: 17.62 MPa
- Tensile Strength, Yield: 19.6 MPa
- Elongation at Break: 170 %
$ 1560/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 60
- Tensile Strength, Yield: 3.31 MPa
- Tensile Strength, Yield: 8.96 MPa
- Elongation at Break: 400 %
$ 2222/MT
- Specific Gravity: 1.26 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 20.0 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 80.0 °C
$ 1459/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 68
- Tensile Strength, Yield: 13.9 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 2485/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 65
- Tensile Strength, Yield: 4.76 MPa
- Tensile Strength, Yield: 11.6 MPa
- Elongation at Break: 390 %
$ 1791/MT
- Specific Gravity: 1.26 g/cc
- Hardness, Shore A: 90
- Tensile Strength at Break: 23.1 MPa
- Elongation at Break: 380 %
- Brittleness Temperature: -28.0 °C
- Appearance: Clear/Transparent
$ 2385/MT
- Specific Gravity: 1.36 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 17.2 MPa
- Elongation at Break: 320 %
- Maximum Service Temperature, Air: 80.0 °C
$ 2170/MT
- Specific Gravity: 1.41 g/cc
- Hardness, Shore D: 70
- Tensile Strength, Yield: 48.6 MPa
- Elongation at Break: 100 %
- Maximum Service Temperature, Air: 190 °C @Time >=3600 sec
- Vicat Softening Point: 58.9 °C
$ 1802/MT
- Specific Gravity: 1.23 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Yield: 19.3 MPa
- Elongation at Break: 380 %
- Melt Temperature: 182 °C
$ 1877/MT
- Specific Gravity: 1.33 g/cc
- Tensile Strength, Yield: 41.0 MPa
- Elongation at Break: 190 %
- Izod Impact, Notched: 1.17 J/cm
- Vicat Softening Point: 72.2 °C
$ 1752/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore A: 90
- Tensile Strength at Break: 21.4 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 105 °C
$ 1662/MT
- Specific Gravity: 1.59 g/cc
- Hardness, Shore C: 85
- Hardness, Shore C: 92
- Tensile Strength at Break: 17.6 MPa
- Elongation at Break: 200 %
$ 1682/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore A: 83
- Tensile Strength: 17.4 MPa
- Elongation at Break: 360 %
- Brittleness Temperature: -30.0 °C
- Oxygen Index: 29 %
$ 1964/MT
- Specific Gravity: 1.17 g/cc
- Hardness, Shore A: 49
- Tensile Strength: 13.1 MPa
- Elongation at Break: 200 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 2194/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 70
- Tensile Strength: 9.79 MPa
- Elongation at Break: 200 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 1759/MT
- Specific Gravity: 1.09 g/cc
- Hardness, Shore A: 40
- Tensile Strength, Yield: 6.96 MPa
- Elongation at Break: 300 %
- Compression Set: 32 %
$ 1697/MT
- Specific Gravity: 1.39 g/cc
- Hardness, Shore A: 90
- Tensile Strength at Break: 16.8 MPa
- Elongation at Break: 340 %
- Maximum Service Temperature, Air: 105 °C
$ 1499/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore A: 72
- Tensile Strength at Break: 14.5 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 105 °C
$ 1480/MT
- Specific Gravity: 1.44 g/cc
- Tensile Strength, Yield: 49.0 MPa
- Elongation at Break: 150 %
- Izod Impact, Notched: 0.587 J/cm
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
- Vicat Softening Point: 95.0 °C
$ 1726/MT
- Specific Gravity: 1.35 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore C: 69
- Tensile Strength at Break: 14.3 MPa
- Elongation at Break: 230 %
$ 1490/MT
- Specific Gravity: 1.23 g/cc
- Linear Mold Shrinkage: 0.015 - 0.018 cm/cm
- Hardness, Shore A: 55
- Tensile Strength at Break: 10.7 MPa
- Elongation at Break: 480 %
$ 2243/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 105 °C
$ 2038/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 105 °C
$ 1638/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 105 °C
$ 1777/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 105 °C
$ 1866/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 105 °C
$ 2248/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 105 °C
$ 1726/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 105 °C
$ 1592/MT
- Specific Gravity: 1.47 g/cc
- Hardness, Shore A: 79
- Tensile Strength, Yield: 15.33 MPa
- Tensile Strength, Yield: 17.0 MPa
- Elongation at Break: 240 %
$ 1966/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 105 °C
$ 1831/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 105 °C
$ 1938/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 105 °C
$ 2288/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 105 °C
$ 2117/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 105 °C
$ 1608/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 105 °C
$ 2186/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore A: 65
- Tensile Strength, Yield: 11.2 MPa
- Elongation at Break: 380 %
- Brittleness Temperature: -40.0 °C
$ 1648/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 1.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 62
- Tensile Strength at Break: 4.21 MPa
- Elongation at Break: 720 %
$ 2030/MT
- Specific Gravity: 1.39 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore C: 71
- Tensile Strength at Break: 18.3 MPa
- Elongation at Break: 280 %
$ 1819/MT
- Specific Gravity: 1.43 g/cc
- Tensile Strength, Yield: 44.1 MPa
- Elongation at Break: 150 %
- Izod Impact, Notched: 0.801 J/cm
- Maximum Service Temperature, Air: 190 °C @Time >=Error in fixSigDigits: @digits must be between 1 a sec
- Vicat Softening Point: 93.9 °C
$ 2288/MT
- Specific Gravity: 1.39 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 15.9 MPa
- Elongation at Break: 330 %
- Maximum Service Temperature, Air: 80.0 °C
$ 2293/MT
- Specific Gravity: 1.24 g/cc
- Hardness, Shore A: 72
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 390 %
- Maximum Service Temperature, Air: 80.0 °C
$ 1479/MT
- Specific Gravity: 1.17 g/cc
- Hardness, Shore A: 65
- Tensile Strength at Break: 13.1 MPa
- Elongation at Break: 430 %
- Brittleness Temperature: -43.0 °C
- Appearance: Clear/Transparent
$ 2262/MT
- Specific Gravity: 1.25 g/cc
- Hardness, Shore A: 72
- Tensile Strength at Break: 14.5 MPa
- Elongation at Break: 330 %
- Maximum Service Temperature, Air: 105 °C
$ 1560/MT
- Specific Gravity: 1.44 g/cc
- Hardness, Shore A: 73
- Tensile Strength, Yield: 13.96 MPa
- Tensile Strength, Yield: 15.5 MPa
- Elongation at Break: 240 %
- Elongation at Break: 300 %
$ 1471/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 65
- Tensile Strength, Yield: 4.62 MPa
- Tensile Strength, Yield: 11.0 MPa
- Elongation at Break: 380 %
$ 1767/MT
- Specific Gravity: 1.32 g/cc
- Hardness, Shore C: 88
- Tensile Strength at Break: 23.6 MPa
- Elongation at Break: 290 %
- Maximum Service Temperature, Air: 105 °C
$ 2030/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 75
- Tensile Strength, Yield: 5.52 MPa
- Tensile Strength, Yield: 13.1 MPa
- Elongation at Break: 370 %
$ 1779/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 75
- Tensile Strength at Break: 15.9 MPa
- Elongation at Break: 390 %
- Maximum Service Temperature, Air: 90.0 °C
$ 1518/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore D: 77
- Tensile Strength at Break: 46.8 MPa
- Elongation at Break: 120 %
- Tensile Modulus: 2.35 GPa
$ 1621/MT
- Specific Gravity: 1.16 g/cc
- Hardness, Shore A: 55
- Tensile Strength, Yield: 8.62 MPa
- Elongation at Break: 420 %
- Brittleness Temperature: -45.0 °C
$ 1741/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore A: 86
- Tensile Strength at Break: 17.9 MPa
- Elongation at Break: 310 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1678/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 17.4 MPa
- Elongation at Break: 350 %
- Appearance: Opaque
$ 1565/MT
- Specific Gravity: 1.32 g/cc
- Hardness, Shore A: 82
- Tensile Strength, Yield: 17.7 MPa
- Elongation at Break: 280 %
- Maximum Service Temperature, Air: 190 °C @Time >=Error in fixSigDigits: @digits must be between 1 a sec
$ 1711/MT
- Specific Gravity: 1.52 g/cc
- Tensile Strength, Yield: 46.1 MPa
- Elongation at Break: 110 %
- Izod Impact, Notched: 0.390 J/cm
- Maximum Service Temperature, Air: 190 °C @Time 1800 sec
- Vicat Softening Point: 97.8 °C
$ 2090/MT
- Specific Gravity: 1.18 g/cc
- Hardness, Shore A: 56
- Tensile Strength: 12.8 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 1480/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 55
- Tensile Strength, Yield: 2.69 MPa
- Tensile Strength, Yield: 6.89 MPa
- Elongation at Break: 390 %
$ 1540/MT
- Specific Gravity: 1.23 g/cc
- Hardness, Shore A: 85
- Tensile Strength at Break: 19.3 MPa
- Elongation at Break: 380 %
- Appearance: Clear/Transparent
$ 1468/MT
- Specific Gravity: 1.19 g/cc
- Hardness, Shore A: 70
- Tensile Strength, Yield: 5.52 MPa
- Tensile Strength, Yield: 11.4 MPa
- Elongation at Break: 390 %
$ 1766/MT
- Specific Gravity: 1.23 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 18.5 MPa
- Elongation at Break: 380 %
- Appearance: Clear/Transparent
$ 1777/MT
- Specific Gravity: 1.28 g/cc
- Hardness, Shore A: 75
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Break: 220 %
- Melt Temperature: 191 °C
$ 2300/MT
- Specific Gravity: 1.39 g/cc
- Hardness, Shore C: 90
- Tensile Strength at Break: 19.3 MPa
- Elongation at Break: 330 %
- Maximum Service Temperature, Air: 105 °C
$ 2545/MT
- Specific Gravity: 1.27 g/cc
- Hardness, Shore A: 60
- Tensile Strength at Break: 10.7 MPa
- Elongation at Break: 410 %
- Appearance: Opaque
$ 1830/MT
- Specific Gravity: 1.27 g/cc
- Hardness, Shore A: 90
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Break: 310 %
- Melt Temperature: 188 °C
$ 1490/MT
- Specific Gravity: 1.46 g/cc
- Hardness, Shore A: 85
- Tensile Strength at Break: 15.2 MPa
- Elongation at Break: 290 %
- Maximum Service Temperature, Air: 75.0 °C
$ 2050/MT
- Specific Gravity: 1.27 g/cc
- Hardness, Shore A: 95
- Tensile Strength, Yield: 23.1 MPa
- Elongation at Break: 230 %
- Melt Temperature: 191 °C
$ 2070/MT
- Specific Gravity: 1.44 g/cc
- Tensile Strength, Yield: 45.0 MPa
- Elongation at Break: 110 %
- Izod Impact, Notched: 1.55 J/cm
$ 1765/MT
- Specific Gravity: 1.37 g/cc
- Melt Flow: 1.60 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 80
- Tensile Strength at Break: 15.9 MPa
- Elongation at Break: 350 %
$ 1496/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore C: 76
- Tensile Strength at Break: 20.0 MPa
- Elongation at Break: 290 %
- Maximum Service Temperature, Air: 105 °C
$ 1468/MT
- Specific Gravity: 1.31 g/cc
- Hardness, Shore C: 82
- Tensile Strength at Break: 23.8 MPa
- Elongation at Break: 330 %
- Flexural Modulus: 0.290 GPa
$ 1542/MT
- Specific Gravity: 1.14 g/cc
- Hardness, Shore A: 50
- Tensile Strength, Yield: 2.55 MPa
- Tensile Strength, Yield: 8.41 MPa
- Elongation at Break: 460 %
$ 1668/MT
- Specific Gravity: 1.45 g/cc
- Tensile Strength, Yield: 48.0 MPa
- Elongation at Break: 100 %
- Izod Impact, Notched: 0.587 J/cm
- Vicat Softening Point: 88.9 °C
$ 2163/MT
- Specific Gravity: 1.31 g/cc
- Hardness, Shore A: 90
- Tensile Strength, Yield: 19.5 MPa
- Elongation at Break: 220 %
- Brittleness Temperature: -14.0 °C
$ 1675/MT
- Specific Gravity: 1.17 g/cc
- Hardness, Shore A: 65
- Tensile Strength, Yield: 11.0 MPa
- Elongation at Break: 370 %
- Melt Temperature: 171 °C
$ 2166/MT
- Specific Gravity: 1.29 g/cc
- Hardness, Shore A: 70
- Tensile Strength at Break: 13.8 MPa
- Elongation at Break: 370 %
- Brittleness Temperature: -40.0 °C
- Appearance: Opaque
$ 1501/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore C: 89
- Tensile Strength at Break: 17.6 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 80.0 °C
$ 1526/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Yield: 11.7 MPa
- Tensile Strength, Yield: 17.9 MPa
- Elongation at Break: 330 %
$ 1660/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 79
- Tensile Strength at Break: 14.8 MPa
- Elongation at Break: 390 %
- Maximum Service Temperature, Air: 105 °C
$ 1908/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore A: 73
- Tensile Strength at Break: 13.8 MPa
- Elongation at Break: 370 %
- Maximum Service Temperature, Air: 80.0 °C
$ 2534/MT
- Specific Gravity: 1.17 g/cc
- Hardness, Shore A: 50
- Tensile Strength, Yield: 7.86 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 1570/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore C: 69
- Tensile Strength at Break: 22.8 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 80.0 °C
$ 1554/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 55
- Hardness, Shore A: 61
- Tensile Strength at Break: 8.14 MPa
- Tensile Strength, Yield: 2.55 MPa
$ 1676/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore A: 83
- Tensile Strength, Yield: 13.53 MPa
- Tensile Strength, Yield: 15.0 MPa
- Elongation at Break: 200 %
$ 2209/MT
- Specific Gravity: 1.40 g/cc
- Tensile Strength, Yield: 47.1 MPa
- Elongation at Break: 110 %
- Izod Impact, Notched: 0.801 J/cm
- Maximum Service Temperature, Air: 190 °C @Time >=7200 sec
- Vicat Softening Point: 87.2 °C
$ 1711/MT
- Specific Gravity: 1.03 g/cc
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 80
- Tensile Strength at Break: 10.8 MPa
- Tensile Stress: 3.52 MPa @Strain 50.0 %
$ 2353/MT
- Specific Gravity: 1.17 g/cc
- Hardness, Shore A: 65
- Tensile Strength, Yield: 4.48 MPa
- Tensile Strength, Yield: 11.7 MPa
- Elongation at Break: 430 %
$ 1523/MT
- Specific Gravity: 1.11 g/cc
- Hardness, Shore A: 50
- Tensile Strength, Yield: 2.76 MPa
- Tensile Strength, Yield: 8.27 MPa
- Elongation at Break: 450 %
$ 1484/MT
- Specific Gravity: 1.36 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 15.2 MPa
- Tensile Strength: 7.24 MPa @Strain 100 %
- Elongation at Break: 360 %
$ 1599/MT
- Specific Gravity: 1.44 g/cc
- Hardness, Shore C: 85
- Tensile Strength at Break: 14.8 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 75.0 °C
$ 2162/MT
- Specific Gravity: 1.44 g/cc
- Hardness, Shore C: 85
- Tensile Strength at Break: 14.8 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1652/MT
- Specific Gravity: 1.27 g/cc
- Hardness, Shore A: 90
- Tensile Strength, Yield: 23.1 MPa
- Elongation at Break: 360 %
- Melt Temperature: 191 °C
$ 2223/MT
- Specific Gravity: 1.53 g/cc
- Hardness, Shore C: 67
- Tensile Strength at Break: 15.5 MPa
- Elongation at Break: 290 %
- Maximum Service Temperature, Air: 80.0 °C
$ 1798/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 75
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 430 %
- Brittleness Temperature: -40.0 °C
- Appearance: Clear/Transparent
$ 1643/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 85
- Tensile Strength at Break: 20.0 MPa
- Elongation at Break: 330 %
- Brittleness Temperature: -29.0 °C
- Appearance: Opaque
$ 1917/MT
- Specific Gravity: 1.18 g/cc
- Hardness, Shore A: 65
- Tensile Strength at Break: 11.5 MPa
- Elongation at Break: 410 %
- Brittleness Temperature: -38.0 °C
- Appearance: Clear/Transparent
$ 1799/MT
- Specific Gravity: 1.18 g/cc
- Hardness, Shore A: 70
- Tensile Strength at Break: 13.1 MPa
- Elongation at Break: 430 %
- Appearance: Clear/Transparent
$ 1717/MT
- Specific Gravity: 1.23 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Yield: 18.1 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 170 °C @Time >=Error in fixSigDigits: @digits must be between 1 a sec
$ 1470/MT
- Specific Gravity: 1.19 g/cc
- Hardness, Shore A: 65
- Tensile Strength, Yield: 10.0 MPa
- Elongation at Break: 330 %
- Brittleness Temperature: -43.0 °C
$ 2239/MT
- Specific Gravity: 1.42 g/cc
- Hardness, Shore C: 72
- Tensile Strength at Break: 21.4 MPa
- Elongation at Break: 340 %
- Flexural Modulus: 0.0752 GPa
$ 1604/MT
- Specific Gravity: 1.26 g/cc
- Hardness, Shore A: 90
- Tensile Strength at Break: 22.8 MPa
- Elongation at Break: 350 %
- Brittleness Temperature: -24.0 °C
- Appearance: Clear/Transparent
$ 1534/MT
- Density: 1.30 g/cc
- Hardness, Shore A: 82
- Tensile Strength at Break: 7.398 MPa
- Elongation at Break: 450 %
- 100% Modulus: 0.00360 GPa
$ 1845/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore C: 73
- Tensile Strength at Break: 14.7 MPa
- Elongation at Break: 310 %
- Maximum Service Temperature, Air: 80.0 °C
$ 1911/MT
- Specific Gravity: 1.39 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore C: 75
- Tensile Strength at Break: 17.2 MPa
- Elongation at Break: 160 %
$ 1625/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore A: 91
- Tensile Strength, Yield: 13.22 MPa
- Tensile Strength, Yield: 14.7 MPa
- Elongation at Break: 104 %
- Elongation at Break: 130 %
$ 1611/MT
- Specific Gravity: 1.25 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 19.2 MPa
- Elongation at Break: 390 %
- Maximum Service Temperature, Air: 105 °C
$ 1986/MT
- Specific Gravity: 1.31 g/cc
- Hardness, Shore A: 73
- Tensile Strength, Yield: 9.3596 MPa
- Tensile Strength, Yield: 12.5 MPa
- Elongation at Break: 97.5 %
- Elongation at Break: 150 %
$ 2091/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore D: 64
- Hardness, Shore D: 74
- Tensile Strength at Break: 23.9 MPa
- Elongation at Break: 260 %
- Brittleness Temperature: -16.0 °C
$ 1473/MT
- Specific Gravity: 1.18 g/cc
- Hardness, Shore A: 68
- Tensile Strength, Yield: 4.76 MPa
- Tensile Strength, Yield: 12.8 MPa
- Elongation at Break: 430 %
$ 1605/MT
- Specific Gravity: 1.40 g/cc
- Tensile Strength, Yield: 44.1 MPa
- Elongation at Break: 100 %
- Izod Impact, Notched: 1.17 J/cm
- Maximum Service Temperature, Air: 190 °C @Time >=Error in fixSigDigits: @digits must be between 1 a sec
- Vicat Softening Point: 90.0 °C
$ 2060/MT
- Specific Gravity: 1.27 g/cc
- Hardness, Shore A: 90
- Tensile Strength, Yield: 22.1 MPa
- Elongation at Break: 310 %
- Brittleness Temperature: -11.0 °C
- Melt Temperature: 185 °C
$ 1545/MT
- Specific Gravity: 1.42 g/cc
- Hardness, Shore A: 84
- Tensile Strength, Yield: 13.53 MPa
- Tensile Strength, Yield: 15.0 MPa
- Elongation at Break: 200 %
$ 1896/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore C: 88
- Tensile Strength at Break: 17.2 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 105 °C
$ 1958/MT
- Specific Gravity: 1.16 g/cc
- Hardness, Shore A: 62
- Tensile Strength, Yield: 12.5 MPa
- Elongation at Break: 380 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 1870/MT
- Specific Gravity: 1.16 g/cc
- Hardness, Shore A: 62
- Tensile Strength, Yield: 12.5 MPa
- Elongation at Break: 380 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 2547/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 75
- Tensile Strength at Break: 15.5 MPa
- Tensile Strength: 6.21 MPa @Strain 100 %
- Elongation at Break: 400 %
$ 1955/MT
- Specific Gravity: 1.26 g/cc
- Hardness, Shore A: 79
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Break: 320 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 1514/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore C: 90
- Tensile Strength at Break: 24.1 MPa
- Elongation at Break: 240 %
- Maximum Service Temperature, Air: 105 °C
$ 1778/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore C: 75
- Tensile Strength at Break: 21.2 MPa
- Elongation at Break: 290 %
- Maximum Service Temperature, Air: 105 °C
$ 2057/MT
- Specific Gravity: 1.28 g/cc
- Hardness, Shore A: 65
- Tensile Strength at Break: 14.5 MPa
- Elongation at Break: 410 %
- Brittleness Temperature: -41.0 °C
- Appearance: Opaque
$ 1789/MT
- Specific Gravity: 1.36 g/cc
- Hardness, Shore C: 70
- Tensile Strength at Break: 19.7 MPa
- Elongation at Break: 320 %
- Maximum Service Temperature, Air: 80.0 °C
$ 1458/MT
- Specific Gravity: 1.36 g/cc
- Hardness, Shore A: 88
- Tensile Strength, Yield: 17.7 MPa
- Elongation at Break: 280 %
- Maximum Service Temperature, Air: 190 °C @Time >=Error in fixSigDigits: @digits must be between 1 a sec
$ 1531/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Yield: 8.00 MPa
- Tensile Strength, Yield: 11.9 MPa
- Elongation at Break: 270 %
$ 2045/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 1.70 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 70
- Tensile Strength at Break: 5.10 MPa
- Elongation at Break: 700 %
$ 1571/MT
- Specific Gravity: 1.19 g/cc
- Hardness, Shore A: 65
- Tensile Strength, Yield: 13.2 MPa
- Elongation at Break: 360 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 2392/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore C: 70
- Tensile Strength at Break: 21.7 MPa
- Elongation at Break: 320 %
- Maximum Service Temperature, Air: 80.0 °C
$ 1563/MT
- Specific Gravity: 1.17 g/cc
- Hardness, Shore A: 65
- Tensile Strength at Break: 12.4 MPa
- Elongation at Break: 430 %
- Maximum Service Temperature, Air: 105 °C
- Appearance: Clear
$ 1662/MT
- Specific Gravity: 1.58 g/cc
- Hardness, Shore C: 81
- Tensile Strength at Break: 19.7 MPa
- Elongation at Break: 240 %
- Maximum Service Temperature, Air: 105 °C
$ 2281/MT
- Specific Gravity: 1.24 g/cc
- Hardness, Shore A: 86
- Tensile Strength at Break: 22.6 MPa
- Elongation at Break: 380 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1703/MT
- Specific Gravity: 1.42 g/cc
- Hardness, Shore D: 78
- Tensile Strength, Yield: 40.0 MPa
- Elongation at Break: 150 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
- Vicat Softening Point: 93.9 °C
$ 1599/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 96
- Tensile Strength, Yield: 19.6 MPa
- Elongation at Break: 250 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 2067/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 55
- Tensile Strength, Yield: 3.24 MPa
- Tensile Strength, Yield: 8.00 MPa
- Elongation at Break: 410 %
$ 2075/MT
- Specific Gravity: 1.19 g/cc
- Hardness, Shore A: 70
- Tensile Strength at Break: 14.8 MPa
- Elongation at Break: 450 %
- Brittleness Temperature: -40.0 °C
- Appearance: Clear/Transparent
$ 1834/MT
- Specific Gravity: 1.40 g/cc
- Hardness, Shore C: 75
- Tensile Strength at Break: 19.3 MPa
- Elongation at Break: 330 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1536/MT
- Specific Gravity: 1.16 g/cc
- Hardness, Shore A: 54
- Tensile Strength, Yield: 9.79 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 1517/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 75
- Tensile Strength at Break: 15.0 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 50.0 °C
$ 1615/MT
- Specific Gravity: 1.18 g/cc
- Hardness, Shore A: 70
- Tensile Strength, Yield: 12.0 MPa
- Elongation at Break: 360 %
- Melt Temperature: 174 °C
$ 1576/MT
- Specific Gravity: 1.43 g/cc
- Hardness, Shore C: 85
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 80.0 °C
$ 1454/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 65
- Tensile Strength, Yield: 4.07 MPa
- Tensile Strength, Yield: 10.3 MPa
- Elongation at Break: 390 %
$ 1573/MT
- Specific Gravity: 1.29 g/cc
- Hardness, Shore A: 89
- Tensile Strength, Yield: 18.6 MPa
- Elongation at Break: 280 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 1692/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Yield: 7.24 MPa
- Tensile Strength, Yield: 15.9 MPa
- Elongation at Break: 370 %
$ 2083/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 70
- Tensile Strength, Yield: 5.58 MPa
- Tensile Strength, Yield: 13.4 MPa
- Elongation at Break: 390 %
$ 1748/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 70
- Tensile Strength, Yield: 11.9 MPa
- Elongation at Break: 370 %
- Brittleness Temperature: -38.0 °C
$ 1452/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 75
- Tensile Strength, Yield: 14.8 MPa
- Elongation at Break: 420 %
- Melt Temperature: 177 °C
$ 1520/MT
- Specific Gravity: 1.27 g/cc
- Hardness, Shore A: 60
- Hardness, Shore A: 66
- Tensile Strength at Break: 11.3 MPa
- Tensile Strength, Yield: 3.45 MPa
$ 1708/MT
- Specific Gravity: 1.24 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Yield: 8.27 MPa
- Tensile Strength, Yield: 19.0 MPa
- Elongation at Break: 360 %
$ 1983/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore D: 75
- Tensile Strength, Yield: 45.1 MPa
- Elongation at Break: 160 %
- Izod Impact, Notched: 1.98 J/cm
- Vicat Softening Point: 80.0 °C
$ 1583/MT
- Specific Gravity: 1.30 g/cc
- Melt Flow: 13.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 88
- Tensile Strength at Break: 10.8 MPa @Thickness 1.91 mm
- Elongation at Break: 600 %
$ 1857/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Yield: 15.5 MPa
- Elongation at Break: 350 %
- Melt Temperature: 179 °C
$ 1502/MT
- Specific Gravity: 1.28 g/cc
- Hardness, Shore C: 80
- Tensile Strength at Break: 19.9 MPa
- Tensile Strength, Yield: 16.1 MPa
- Elongation at Break: 320 %
- Brittleness Temperature: -6.00 °C
$ 2219/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 75
- Hardness, Shore A: 81
- Tensile Strength, Yield: 13.7 MPa
- Elongation at Break: 320 %
- Brittleness Temperature: -37.0 °C
$ 1688/MT
- Specific Gravity: 1.36 g/cc
- Hardness, Shore A: 83
- Tensile Strength at Break: 17.4 MPa
- Elongation at Break: 360 %
- Maximum Service Temperature, Air: 80.0 °C
$ 2047/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore C: 80
- Tensile Strength at Break: 17.6 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 105 °C
$ 2330/MT
- Specific Gravity: 1.31 g/cc
- Hardness, Shore A: 78
- Tensile Strength, Yield: 12.8 MPa
- Elongation at Break: 310 %
- Maximum Service Temperature, Air: 190 °C @Time >=Error in fixSigDigits: @digits must be between 1 a sec
$ 1932/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 50
- Tensile Strength, Yield: 2.28 MPa
- Tensile Strength, Yield: 6.89 MPa
- Elongation at Break: 430 %
$ 1562/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 75
- Tensile Strength, Yield: 6.21 MPa
- Tensile Strength, Yield: 11.9 MPa
- Elongation at Break: 290 %
$ 2033/MT
- Specific Gravity: 1.23 g/cc
- Hardness, Shore A: 65
- Tensile Strength at Break: 14.5 MPa
- Elongation at Break: 390 %
- Maximum Service Temperature, Air: 105 °C
$ 1786/MT
- Specific Gravity: 1.25 g/cc
- Hardness, Shore A: 85
- Tensile Strength at Break: 17.9 MPa
- Elongation at Break: 320 %
- Brittleness Temperature: -24.0 °C
- Appearance: Clear/Transparent
$ 2199/MT
- Specific Gravity: 1.17 g/cc
- Hardness, Shore A: 65
- Tensile Strength, Yield: 12.1 MPa
- Elongation at Break: 440 %
- Melt Temperature: 171 °C
$ 1455/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore C: 71
- Tensile Strength at Break: 22.8 MPa
- Elongation at Break: 330 %
- Maximum Service Temperature, Air: 105 °C
$ 1496/MT
- Specific Gravity: 1.17 g/cc
- Hardness, Shore A: 65
- Tensile Strength, Yield: 3.86 MPa
- Tensile Strength, Yield: 11.7 MPa
- Elongation at Break: 430 %
$ 1779/MT
- Specific Gravity: 1.12 g/cc
- Hardness, Shore A: 50
- Tensile Strength, Yield: 7.93 MPa
- Elongation at Break: 450 %
- Brittleness Temperature: -50.0 °C
$ 1524/MT
- Specific Gravity: 1.23 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Yield: 10.8 MPa
- Tensile Strength, Yield: 19.3 MPa
- Elongation at Break: 380 %
$ 1955/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 75
- Hardness, Shore A: 81
- Tensile Strength at Break: 16.5 MPa
- Elongation at Break: 340 %
- Brittleness Temperature: -35.0 °C
$ 2106/MT
- Specific Gravity: 1.25 g/cc
- Hardness, Shore A: 60
- Tensile Strength, Yield: 12.3 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 190 °C @Time >=3600 sec
$ 1701/MT
- Specific Gravity: 1.26 g/cc
- Hardness, Shore A: 87
- Tensile Strength at Break: 18.6 MPa
- Elongation at Break: 300 %
- Brittleness Temperature: -17.0 °C
$ 1506/MT
- Specific Gravity: 1.23 g/cc
- Hardness, Shore A: 83
- Tensile Strength at Break: 17.2 MPa
- Elongation at Break: 360 %
- Maximum Service Temperature, Air: 105 °C
$ 2576/MT
- Specific Gravity: 1.24 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore C: 65
- Tensile Strength at Break: 20.7 MPa
- Elongation at Break: 230 %
$ 2041/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 73
- Tensile Strength, Yield: 14.7 MPa
- Elongation at Break: 340 %
- Maximum Service Temperature, Air: 190 °C @Time Error in fixSigDigits: @digits must be between 1 a sec
$ 1621/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Yield: 10.3 MPa
- Tensile Strength, Yield: 13.1 MPa
- Elongation at Break: 240 %
$ 1742/MT
- Specific Gravity: 1.19 g/cc
- Hardness, Shore A: 56
- Tensile Strength, Yield: 7.58 MPa
- Elongation at Break: 230 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 1460/MT
- Specific Gravity: 1.28 g/cc
- Hardness, Shore A: 72
- Tensile Strength at Break: 13.3 MPa
- Elongation at Break: 390 %
- Maximum Service Temperature, Air: 105 °C
$ 1762/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 90
- Tensile Strength at Break: 23.4 MPa
- Elongation at Break: 360 %
- Brittleness Temperature: -25.0 °C
- Appearance: Opaque
$ 2597/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 90
- Tensile Strength, Yield: 13.1 MPa
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Break: 330 %
$ 1686/MT
- Specific Gravity: 1.31 g/cc
- Hardness, Shore C: 73
- Tensile Strength at Break: 22.1 MPa
- Elongation at Break: 340 %
- Brittleness Temperature: -28.0 °C
$ 1834/MT
- Specific Gravity: 1.25 g/cc
- Hardness, Shore A: 75
- Tensile Strength, Yield: 17.0 MPa
- Elongation at Break: 300 %
$ 1534/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore A: 78
- Tensile Strength at Break: 17.9 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 105 °C
$ 1659/MT
- Specific Gravity: 1.09 g/cc
- Melt Flow: 30 g/10 min @Load 5.00 kg, Temperature 177 °C
- Hardness, Shore A: 45
- Tensile Strength, Yield: 5.72 MPa
- Tensile Strength, Yield: 6.29 MPa
$ 1758/MT
- Specific Gravity: 1.43 g/cc
- Tensile Strength, Yield: 45.1 MPa
- Elongation at Break: 150 %
- Izod Impact, Notched: 0.908 J/cm
- Maximum Service Temperature, Air: 190 °C @Time >=7200 sec
- Vicat Softening Point: 88.9 °C
$ 1703/MT
- Specific Gravity: 1.27 g/cc
- Hardness, Shore A: 95
- Tensile Strength at Break: 23.4 MPa
- Elongation at Break: 340 %
- Brittleness Temperature: -22.0 °C
- Appearance: Clear/Transparent
$ 1787/MT
- Specific Gravity: 1.22 g/cc
- Tensile Strength, Yield: 9.79 MPa
- Elongation at Break: 200 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 2213/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 60
- Hardness, Shore A: 66
- Tensile Strength at Break: 8.96 MPa
- Tensile Strength, Yield: 2.90 MPa
$ 1449/MT
- Specific Gravity: 1.15 g/cc
- Hardness, Shore A: 55
- Hardness, Shore A: 61
$ 1653/MT
- Specific Gravity: 1.29 g/cc
- Hardness, Shore A: 91
- Hardness, Shore C: 66
- Tensile Strength, Yield: 7.58 MPa
- Elongation at Break: 90 %
- Volume Resistivity: 2.5 ohm-cm
$ 2349/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 62
- Tensile Strength, Yield: 12.5 MPa
- Elongation at Break: 380 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 1546/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 65
- Tensile Strength, Yield: 14.7 MPa
- Elongation at Break: 320 %
- Maximum Service Temperature, Air: 190 °C @Time >=Error in fixSigDigits: @digits must be between 1 a sec
$ 1705/MT
- Specific Gravity: 1.25 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Yield: 16.7 MPa
- Elongation at Break: 320 %
- Maximum Service Temperature, Air: 190 °C @Time >=Error in fixSigDigits: @digits must be between 1 a sec
$ 1687/MT
- Specific Gravity: 1.45 g/cc
- Tensile Strength, Yield: 49.0 MPa
- Elongation at Break: 150 %
- Izod Impact, Notched: 0.801 J/cm
- Maximum Service Temperature, Air: 190 °C @Time >=Error in fixSigDigits: @digits must be between 1 a sec
- Vicat Softening Point: 97.8 °C
$ 1673/MT
- Specific Gravity: 1.15 g/cc
- Hardness, Shore A: 60
- Tensile Strength, Yield: 3.79 MPa
- Tensile Strength, Yield: 10.3 MPa
- Elongation at Break: 450 %
$ 1621/MT
- Specific Gravity: 1.48 g/cc
- Hardness, Shore A: 83
- Tensile Strength, Yield: 15.33 MPa
- Tensile Strength, Yield: 17.0 MPa
- Elongation at Break: 240 %
- Elongation at Break: 300 %
$ 1613/MT
- Specific Gravity: 1.58 g/cc
- Hardness, Shore C: 87
- Hardness, Shore C: 92
- Tensile Strength at Break: 17.7 MPa
- Elongation at Break: 190 %
$ 1846/MT
- Specific Gravity: 1.18 g/cc
- Hardness, Shore A: 70
- Tensile Strength, Yield: 13.1 MPa
- Elongation at Break: 430 %
- Melt Temperature: 174 °C
$ 2056/MT
- Specific Gravity: 1.36 g/cc
- Hardness, Shore A: 85
- Tensile Strength at Break: 18.6 MPa
- Elongation at Break: 320 %
- Maximum Service Temperature, Air: 60.0 °C
$ 2178/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 75
- Tensile Strength, Yield: 6.21 MPa
- Tensile Strength, Yield: 14.8 MPa
- Elongation at Break: 420 %
$ 1520/MT
- Specific Gravity: 1.16 g/cc
- Hardness, Shore A: 62
- Tensile Strength, Yield: 12.8 MPa
- Elongation at Break: 380 %
- Maximum Service Temperature, Air: 190 °C @Time >=Error in fixSigDigits: @digits must be between 1 a sec
$ 1883/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 55
- Tensile Strength, Yield: 3.10 MPa
- Tensile Strength, Yield: 8.96 MPa
- Elongation at Break: 410 %
$ 1752/MT
- Specific Gravity: 1.32 g/cc
- Hardness, Shore D: 74
- Tensile Strength: 3.92 MPa
- Elongation at Break: 50 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
- Vicat Softening Point: 48.9 °C
$ 1648/MT
- Specific Gravity: 1.40 g/cc
- Hardness, Shore C: 67
- Tensile Strength at Break: 23.4 MPa
- Elongation at Break: 340 %
- Maximum Service Temperature, Air: 105 °C
$ 2088/MT
- Specific Gravity: 1.19 g/cc
- Hardness, Shore A: 70
- Tensile Strength, Yield: 5.52 MPa
- Tensile Strength, Yield: 13.1 MPa
- Elongation at Break: 420 %
$ 1889/MT
- Specific Gravity: 1.18 g/cc
- Hardness, Shore A: 68
- Tensile Strength, Yield: 4.76 MPa
- Tensile Strength, Yield: 12.8 MPa
- Elongation at Break: 430 %
- Brittleness Temperature: -37.2 °C
$ 1564/MT
- Specific Gravity: 1.39 g/cc
- Hardness, Shore A: 90
- Tensile Strength at Break: 20.0 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 75.0 °C
$ 2492/MT
- Specific Gravity: 1.25 g/cc
- Hardness, Shore A: 90
- Tensile Strength, Yield: 14.5 MPa
- Tensile Strength, Yield: 21.7 MPa
- Elongation at Break: 350 %
$ 1831/MT
- Specific Gravity: 1.39 g/cc
- Hardness, Shore A: 85
- Tensile Strength at Break: 15.6 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 80.0 °C
$ 2433/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 1.70 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 80
- Tensile Strength at Break: 5.86 MPa
- Elongation at Break: 540 %
$ 1563/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 60
- Tensile Strength, Yield: 3.31 MPa
- Tensile Strength, Yield: 8.27 MPa
- Elongation at Break: 390 %
$ 1563/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 70
- Hardness, Shore A: 76
- Tensile Strength at Break: 15.2 MPa
- Elongation at Break: 350 %
- Brittleness Temperature: -37.0 °C
$ 1814/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore C: 75
- Tensile Strength at Break: 19.3 MPa
- Elongation at Break: 290 %
- Maximum Service Temperature, Air: 105 °C
$ 1559/MT
- Specific Gravity: 1.28 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Yield: 18.1 MPa
- Elongation at Break: 290 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 2203/MT
- Specific Gravity: 1.68 g/cc
- Hardness, Shore C: 78
- Tensile Strength at Break: 13.8 MPa
- Elongation at Break: 230 %
- Maximum Service Temperature, Air: 75.0 °C
$ 2294/MT
- Specific Gravity: 1.17 g/cc
- Hardness, Shore A: 65
- Tensile Strength at Break: 14.5 MPa
- Elongation at Break: 460 %
- Brittleness Temperature: -43.0 °C
- Appearance: Clear/Transparent
$ 1637/MT
- Specific Gravity: 1.39 g/cc
- Hardness, Shore D: 79
- Tensile Strength, Yield: 48.5 MPa
- Elongation at Break: 150 %
- Izod Impact, Notched: 0.801 J/cm
- Vicat Softening Point: 82.8 °C
$ 1808/MT
- Specific Gravity: 1.18 g/cc
- Hardness, Shore A: 60
- Tensile Strength, Yield: 11.7 MPa
- Elongation at Break: 400 %
- Brittleness Temperature: -43.0 °C
- Melt Temperature: 168 °C
$ 1474/MT
- Specific Gravity: 1.13 g/cc
- Hardness, Shore A: 55
- Tensile Strength, Yield: 3.31 MPa
- Tensile Strength, Yield: 10.0 MPa
- Elongation at Break: 450 %
$ 1455/MT
- Density: 1.26 g/cc
- Hardness, Shore D: 40
- Tensile Strength at Break: 13.60 MPa
- Elongation at Break: 510 %
- 100% Modulus: 0.00740 GPa
$ 1855/MT
- Specific Gravity: 1.21 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore A: 74
- Tensile Strength at Break: 15.4 MPa
- Elongation at Break: 350 %
$ 1799/MT
- Specific Gravity: 1.12 g/cc
- Hardness, Shore A: 50
- Tensile Strength, Yield: 9.10 MPa
- Elongation at Break: 390 %
- Compression Set: 35 %
$ 1498/MT
- Specific Gravity: 1.17 g/cc
- Hardness, Shore A: 60
- Tensile Strength, Yield: 10.3 MPa
- Elongation at Break: 420 %
- Brittleness Temperature: -43.0 °C
$ 2344/MT
- Specific Gravity: 1.33 g/cc
- Tensile Strength, Yield: 44.1 MPa
- Elongation at Break: 160 %
- Izod Impact, Notched: 1.49 J/cm
- Vicat Softening Point: 77.8 °C
$ 1828/MT
- Specific Gravity: 1.17 g/cc
- Linear Mold Shrinkage: 0.015 - 0.018 cm/cm
- Hardness, Shore A: 70
- Tensile Strength at Break: 12.6 MPa
- Elongation at Break: 420 %
$ 1536/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 50
- Tensile Strength, Yield: 2.48 MPa
- Tensile Strength, Yield: 7.93 MPa
- Elongation at Break: 410 %
$ 1665/MT
- Specific Gravity: 1.31 g/cc
- Hardness, Shore A: 83
- Tensile Strength at Break: 17.9 MPa
- Elongation at Break: 250 %
- Maximum Service Temperature, Air: 105 °C
$ 1476/MT
- Specific Gravity: 1.24 g/cc
- Hardness, Shore A: 89
- Tensile Strength, Yield: 18.6 MPa
- Elongation at Break: 280 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 1459/MT
- Specific Gravity: 1.24 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Yield: 11.0 MPa
- Tensile Strength, Yield: 19.1 MPa
- Elongation at Break: 410 %
$ 1913/MT
- Specific Gravity: 1.19 g/cc
- Hardness, Shore A: 70
- Tensile Strength, Yield: 5.17 MPa
- Tensile Strength, Yield: 13.3 MPa
- Elongation at Break: 430 %
$ 1503/MT
- Specific Gravity: 1.27 g/cc
- Hardness, Shore A: 82
- Tensile Strength, Yield: 18.6 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 1773/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore D: 77
- Tensile Strength, Yield: 47.1 MPa
- Elongation at Break: 150 %
- Izod Impact, Notched: 0.961 J/cm
- Vicat Softening Point: 82.8 °C
$ 2009/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 65
- Hardness, Shore A: 71
- Tensile Strength at Break: 11.0 MPa
- Tensile Strength, Yield: 3.72 MPa
$ 1828/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore C: 70
- Hardness, Shore C: 81
- Tensile Strength at Break: 22.8 MPa
- Tensile Strength, Yield: 16.0 MPa
$ 1570/MT
- Specific Gravity: 1.19 g/cc
- Hardness, Shore A: 65
- Hardness, Shore A: 70
- Tensile Strength at Break: 12.4 MPa
- Elongation at Break: 380 %
- Brittleness Temperature: -39.0 °C
$ 1451/MT
- Specific Gravity: 1.36 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 13.8 MPa
- Elongation at Break: 400 %
- Appearance: Opaque
$ 1759/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore C: 71
- Tensile Strength at Break: 22.1 MPa
- Elongation at Break: 320 %
- Maximum Service Temperature, Air: 105 °C
$ 2062/MT
- Specific Gravity: 1.39 g/cc
- Hardness, Shore A: 83
- Tensile Strength, Yield: 12.60 MPa
- Tensile Strength, Yield: 14.0 MPa
- Elongation at Break: 160 %
$ 2047/MT
- Specific Gravity: 1.19 g/cc
- Hardness, Shore A: 70
- Tensile Strength at Break: 14.8 MPa
- Elongation at Break: 450 %
- Brittleness Temperature: -40.0 °C
- Appearance: Clear/Transparent
$ 2513/MT
- Specific Gravity: 1.19 g/cc
- Hardness, Shore A: 70
- Tensile Strength at Break: 14.8 MPa
- Elongation at Break: 450 %
- Brittleness Temperature: -40.0 °C
- Appearance: Clear/Transparent
$ 2119/MT
- Specific Gravity: 1.19 g/cc
- Hardness, Shore A: 70
- Tensile Strength at Break: 14.8 MPa
- Elongation at Break: 450 %
- Brittleness Temperature: -40.0 °C
- Appearance: Clear/Transparent
$ 1891/MT
- Specific Gravity: 1.25 g/cc
- Hardness, Shore A: 72
- Tensile Strength at Break: 14.5 MPa
- Elongation at Break: 330 %
- Maximum Service Temperature, Air: 105 °C
$ 1622/MT
- Specific Gravity: 1.24 g/cc
- Hardness, Shore A: 83
- Tensile Strength at Break: 20.0 MPa
- Tensile Strength, Yield: 8.27 MPa
- Elongation at Break: 280 %
- Brittleness Temperature: -17.0 °C
$ 1905/MT
- Specific Gravity: 1.34 g/cc
- Melt Flow: 3.50 g/10 min @Load 21.6 kg, Temperature 190 °C
- Hardness, Shore D: 77
- Tensile Strength, Yield: 44.6 MPa
- Elongation at Break: 140 %
$ 2393/MT
- Specific Gravity: 1.39 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore C: 82
- Tensile Strength at Break: 20.7 MPa
- Elongation at Break: 250 %
$ 1888/MT
- Specific Gravity: 1.16 g/cc
- Hardness, Shore A: 60
- Tensile Strength at Break: 10.7 MPa
- Elongation at Break: 450 %
- Appearance: Clear/Transparent
$ 1669/MT
- Specific Gravity: 1.58 g/cc
- Hardness, Shore C: 85
- Tensile Strength at Break: 19.0 MPa
- Elongation at Break: 260 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1920/MT
- Specific Gravity: 1.51 g/cc
- Hardness, Shore C: 70
- Tensile Strength at Break: 15.9 MPa
- Elongation at Break: 250 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1559/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 14.5 MPa
- Elongation at Break: 380 %
- Brittleness Temperature: -32.0 °C
- Appearance: Clear/Transparent
$ 1451/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 17.2 MPa
- Elongation at Break: 380 %
- Maximum Service Temperature, Air: 50.0 °C
$ 1445/MT
- Specific Gravity: 1.16 g/cc
- Hardness, Shore A: 60
- Hardness, Shore A: 66
- Tensile Strength at Break: 10.7 MPa
- Elongation at Break: 380 %
- Brittleness Temperature: -42.0 °C
$ 1968/MT
- Specific Gravity: 1.23 g/cc
- Hardness, Shore A: 85
- Tensile Strength at Break: 21.7 MPa
- Elongation at Break: 390 %
- Brittleness Temperature: -32.0 °C
- Appearance: Clear/Transparent
$ 1742/MT
- Specific Gravity: 1.24 g/cc
- Hardness, Shore A: 72
- Tensile Strength, Yield: 15.2 MPa
- Elongation at Break: 340 %
- Maximum Service Temperature, Air: 190 °C @Time >=Error in fixSigDigits: @digits must be between 1 a sec
$ 1967/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 55
- Tensile Strength, Yield: 2.76 MPa
- Tensile Strength, Yield: 7.58 MPa
- Elongation at Break: 410 %
$ 2249/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 75
- Tensile Strength: 14.8 MPa
- Tensile Stress: 6.21 MPa @Strain 100 %
- Elongation at Break: 420 %
$ 2562/MT
- Specific Gravity: 1.25 g/cc
- Hardness, Shore A: 76
- Tensile Strength, Yield: 4.31 MPa
- Elongation at Break: 140 %
- Volume Resistivity: 8.5 ohm-cm
$ 2584/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 68
- Tensile Strength, Yield: 14.7 MPa
- Elongation at Break: 320 %
- Maximum Service Temperature, Air: 190 °C @Time >=Error in fixSigDigits: @digits must be between 1 a sec
$ 1496/MT
- Specific Gravity: 1.39 g/cc
- Hardness, Shore A: 79
- Tensile Strength at Break: 15.7 MPa
- Elongation at Break: 340 %
- Maximum Service Temperature, Air: 80.0 °C
$ 1506/MT
- Specific Gravity: 1.44 g/cc
- Hardness, Shore A: 94
- Tensile Strength, Yield: 15.89 MPa
- Tensile Strength, Yield: 17.7 MPa
- Elongation at Break: 128 %
- Elongation at Break: 160 %
$ 1768/MT
- Specific Gravity: 1.42 g/cc
- Hardness, Shore A: 85
- Hardness, Shore A: 91
- Tensile Strength at Break: 17.7 MPa
- Tensile Strength, Yield: 9.51 MPa
$ 2287/MT
- Specific Gravity: 1.45 g/cc
- Tensile Strength, Yield: 44.1 MPa
- Elongation at Break: 90 %
- Izod Impact, Notched: 0.961 J/cm
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
- Vicat Softening Point: 92.2 °C
$ 1582/MT
- Specific Gravity: 1.37 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore A: 86
- Tensile Strength at Break: 11.7 MPa
- Elongation at Break: 260 %
$ 2087/MT
- Specific Gravity: 1.16 g/cc
- Hardness, Shore A: 55
- Tensile Strength, Yield: 3.59 MPa
- Tensile Strength, Yield: 10.3 MPa
- Elongation at Break: 460 %
$ 2055/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 63
- Tensile Strength at Break: 12.5 MPa
- Elongation at Break: 370 %
- Maximum Service Temperature, Air: 105 °C
- Appearance: Clear
$ 2144/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 18.3 MPa
- Elongation at Break: 410 %
- Brittleness Temperature: -33.0 °C
- Appearance: Clear/Transparent
$ 1456/MT
- Specific Gravity: 1.17 g/cc
- Hardness, Shore A: 70
- Tensile Strength at Break: 15.2 MPa
- Elongation at Break: 420 %
- Brittleness Temperature: -38.0 °C
- Appearance: Clear/Transparent
$ 1652/MT
- Specific Gravity: 1.31 g/cc
- Hardness, Shore A: 76
- Tensile Strength, Yield: 8.998 MPa
- Tensile Strength, Yield: 10.0 MPa
- Elongation at Break: 80 %
$ 2259/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore A: 68
- Tensile Strength, Yield: 8.998 MPa
- Tensile Strength, Yield: 10.0 MPa
- Elongation at Break: 135 %
$ 1560/MT
- Specific Gravity: 1.46 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Yield: 14.40 MPa
- Tensile Strength, Yield: 16.0 MPa
- Elongation at Break: 200 %
$ 1562/MT
- Specific Gravity: 1.15 g/cc
- Hardness, Shore A: 55
- Tensile Strength, Yield: 9.65 MPa
- Elongation at Break: 370 %
- Melt Temperature: 166 °C
$ 2268/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore A: 85
- Tensile Strength at Break: 20.7 MPa
- Elongation at Break: 360 %
- Brittleness Temperature: -27.0 °C
- Appearance: Opaque
$ 2112/MT
- Specific Gravity: 1.44 g/cc
- Tensile Strength, Yield: 40.0 MPa
- Elongation at Break: 120 %
- Izod Impact, Notched: 0.694 J/cm
- Maximum Service Temperature, Air: 190 °C @Time >=7200 sec
- Vicat Softening Point: 90.0 °C
$ 1979/MT
- Specific Gravity: 1.41 g/cc
- Hardness, Shore C: 70
- Hardness, Shore C: 81
- Tensile Strength at Break: 20.0 MPa
- Elongation at Break: 300 %
- Brittleness Temperature: -10.0 °C
$ 1976/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 1.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 70
- Tensile Strength at Break: 11.4 MPa
- Elongation at Break: 850 %
$ 1733/MT
- Specific Gravity: 1.19 g/cc
- Hardness, Shore A: 45
- Tensile Strength, Yield: 7.86 MPa
- Elongation at Break: 420 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 1529/MT
- Specific Gravity: 1.13 g/cc
- Melt Flow: 3.6 g/10 min @Load 5.00 kg, Temperature 177 °C
- Hardness, Shore A: 60
- Tensile Strength, Yield: 8.34 MPa
- Tensile Strength, Yield: 12.51 MPa
$ 1813/MT
- Specific Gravity: 1.28 g/cc
- Hardness, Shore A: 65
- Hardness, Shore A: 71
- Tensile Strength at Break: 12.9 MPa
- Tensile Strength, Yield: 4.07 MPa
$ 1614/MT
- Specific Gravity: 0.930 g/cc
- Melt Flow: 2.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 69
- Tensile Strength at Break: 19.3 MPa
- Elongation at Break: 650 %
$ 1474/MT
- Specific Gravity: 1.24 g/cc
- Hardness, Shore A: 83
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 330 %
- Brittleness Temperature: -23.0 °C
$ 1810/MT
- Specific Gravity: 1.31 g/cc
- Hardness, Shore C: 71
- Tensile Strength at Break: 21.4 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 105 °C
$ 1620/MT
- Specific Gravity: 1.41 g/cc
- Hardness, Shore A: 90
- Tensile Strength, Yield: 13.22 MPa
- Tensile Strength, Yield: 14.7 MPa
- Elongation at Break: 160 %
$ 1547/MT
- Specific Gravity: 1.32 g/cc
- Hardness, Shore A: 70
- Tensile Strength at Break: 11.2 MPa
- Elongation at Break: 380 %
- Maximum Service Temperature, Air: 90.0 °C
$ 1627/MT
- Specific Gravity: 1.36 g/cc
- Hardness, Shore C: 79
- Tensile Strength at Break: 22.1 MPa
- Tensile Strength at Break: 23.83 MPa
- Elongation at Break: 218.4 %
$ 1527/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 90
- Tensile Strength, Yield: 14.1 MPa
- Tensile Strength, Yield: 17.7 MPa
- Elongation at Break: 260 %
- Melt Temperature: 191 °C
$ 1808/MT
- Specific Gravity: 1.23 g/cc
- Hardness, Shore A: 85
- Tensile Strength at Break: 20.0 MPa
- Elongation at Break: 410 %
- Brittleness Temperature: -28.0 °C
- Appearance: Clear/Transparent
$ 2110/MT
- Specific Gravity: 1.21 g/cc
- Melt Flow: 0.500 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 18.6 MPa
- Elongation at Break: 340 %
$ 2068/MT
- Specific Gravity: 1.11 g/cc
- Melt Flow: 15 g/10 min @Load 5.00 kg, Temperature 177 °C
- Hardness, Shore A: 55
- Tensile Strength, Yield: 7.10 MPa
- Tensile Strength, Yield: 11.789 MPa
$ 1879/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 72
- Tensile Strength, Yield: 14.7 MPa
- Elongation at Break: 320 %
- Maximum Service Temperature, Air: 190 °C @Time >=Error in fixSigDigits: @digits must be between 1 a sec
$ 1967/MT
- Specific Gravity: 1.46 g/cc
- Tensile Strength, Yield: 45.1 MPa
- Elongation at Break: 110 %
- Izod Impact, Notched: 0.587 J/cm
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
- Vicat Softening Point: 92.8 °C
$ 1701/MT
- Specific Gravity: 1.16 g/cc
- Hardness, Shore A: 48
- Tensile Strength, Yield: 9.79 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 2485/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore D: 75
- Tensile Strength, Yield: 39.2 MPa
- Elongation at Break: 170 %
- Izod Impact, Notched: 9.08 J/cm
- Vicat Softening Point: 77.2 °C
$ 2191/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore A: 75
- Tensile Strength at Break: 15.9 MPa
- Elongation at Break: 370 %
- Brittleness Temperature: -35.0 °C
- Appearance: Opaque
$ 1609/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 75
- Tensile Strength, Yield: 5.52 MPa
- Tensile Strength, Yield: 10.0 MPa
- Elongation at Break: 260 %
$ 2257/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 75
- Tensile Strength, Yield: 6.89 MPa
- Tensile Strength, Yield: 12.2 MPa
- Elongation at Break: 370 %
$ 2028/MT
- Specific Gravity: 1.36 g/cc
- Hardness, Shore A: 85
- Tensile Strength at Break: 20.0 MPa
- Elongation at Break: 310 %
- Maximum Service Temperature, Air: 105 °C
$ 2301/MT
- Specific Gravity: 1.40 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore C: 82
- Tensile Strength at Break: 17.6 MPa
- Elongation at Break: 150 %
$ 2147/MT
- Specific Gravity: 1.36 g/cc
- Hardness, Shore A: 90
- Tensile Strength at Break: 22.1 MPa
- Elongation at Break: 310 %
- Brittleness Temperature: -22.0 °C
- Appearance: Opaque
$ 1520/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore C: 65
- Tensile Strength at Break: 20.0 MPa
- Elongation at Break: 340 %
- Maximum Service Temperature, Air: 105 °C
$ 1944/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore A: 88
- Tensile Strength at Break: 19.3 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 105 °C
$ 1522/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore C: 70
- Hardness, Shore C: 83
- Tensile Strength at Break: 24.1 MPa
- Elongation at Break: 350 %
$ 1472/MT
- Specific Gravity: 1.51 g/cc
- Tensile Strength, Yield: 46.1 MPa
- Elongation at Break: 130 %
- Izod Impact, Notched: 0.491 J/cm
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
- Vicat Softening Point: 95.0 °C
$ 2391/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 58
- Tensile Strength, Yield: 12.1 MPa
- Elongation at Break: 380 %
- Maximum Service Temperature, Air: 190 °C @Time >=3600 sec
$ 2018/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 75
- Tensile Strength at Break: 17.2 MPa
- Elongation at Break: 410 %
- Brittleness Temperature: -35.0 °C
- Appearance: Clear/Transparent
$ 1680/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore A: 78
- Tensile Strength, Yield: 11.73 MPa
- Tensile Strength, Yield: 13.0 MPa
- Elongation at Break: 160 %
$ 1558/MT
- Specific Gravity: 1.13 g/cc
- Hardness, Shore A: 45
- Tensile Strength at Break: 8.41 MPa
- Tensile Strength, Yield: 2.45 MPa
- Elongation at Break: 450 %
- Brittleness Temperature: -53.0 °C
$ 1471/MT
- Specific Gravity: 1.25 g/cc
- Hardness, Shore A: 55
- Hardness, Shore A: 61
- Tensile Strength at Break: 10.1 MPa
- Tensile Strength, Yield: 2.93 MPa
$ 1864/MT
- Specific Gravity: 1.32 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 20.0 MPa
- Elongation at Break: 390 %
- Brittleness Temperature: -33.0 °C
- Appearance: Opaque
$ 1867/MT
- Specific Gravity: 1.27 g/cc
- Hardness, Shore A: 90
- Tensile Strength, Yield: 14.5 MPa
- Tensile Strength, Yield: 23.4 MPa
- Elongation at Break: 340 %
$ 1795/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 75
- Tensile Strength, Yield: 15.4 MPa
- Elongation at Break: 350 %
- Brittleness Temperature: -35.0 °C
$ 1526/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Yield: 11.0 MPa
- Tensile Strength, Yield: 14.5 MPa
- Elongation at Break: 270 %
$ 1597/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore A: 80
- Hardness, Shore A: 86
- Tensile Strength at Break: 18.3 MPa
- Tensile Strength, Yield: 8.34 MPa
$ 2274/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 72
- Tensile Strength at Break: 15.2 MPa
- Elongation at Break: 350 %
- Brittleness Temperature: -34.0 °C
$ 1519/MT
- Specific Gravity: 1.19 g/cc
- Hardness, Shore A: 55
- Tensile Strength, Yield: 7.86 MPa
- Elongation at Break: 340 %
- Brittleness Temperature: -45.0 °C
$ 2424/MT
- Specific Gravity: 1.41 g/cc
- Hardness, Shore A: 90
- Hardness, Shore A: 95
- Tensile Strength at Break: 20.1 MPa
- Tensile Strength, Yield: 12.1 MPa
$ 1689/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 50
- Tensile Strength, Yield: 2.69 MPa
- Tensile Strength, Yield: 6.83 MPa
- Elongation at Break: 420 %
$ 1599/MT
- Specific Gravity: 1.44 g/cc
- Hardness, Shore D: 80
- Tensile Strength at Break: 44.9 MPa
- Tensile Strength, Yield: 45.0 MPa
- Elongation at Break: 54 %
$ 1678/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 65
- Tensile Strength, Yield: 4.00 MPa
- Tensile Strength, Yield: 9.65 MPa
- Elongation at Break: 380 %
$ 1489/MT
- Specific Gravity: 1.27 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore C: 80
- Tensile Strength at Break: 20.7 MPa
- Elongation at Break: 280 %
$ 1452/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 65
- Tensile Strength, Yield: 12.8 MPa
- Elongation at Break: 370 %
- Maximum Service Temperature, Air: 190 °C @Time >=3600 sec
$ 1563/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore C: 70
- Tensile Strength at Break: 23.1 MPa
- Elongation at Break: 260 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1515/MT
- Specific Gravity: 1.41 g/cc
- Hardness, Shore A: 82
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 360 %
- Brittleness Temperature: -37.0 °C
$ 1567/MT
- Specific Gravity: 1.26 g/cc
- Hardness, Shore C: 83
- Tensile Strength at Break: 17.2 MPa
- Elongation at Break: 360 %
- Maximum Service Temperature, Air: 90.0 °C
$ 1557/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore A: 75
- Tensile Strength at Break: 18.3 MPa
- Elongation at Break: 400 %
- Brittleness Temperature: -37.0 °C
- Appearance: Opaque
$ 1516/MT
- Specific Gravity: 1.21 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore A: 85
- Tensile Strength at Break: 17.2 MPa
- Elongation at Break: 220 %
$ 1497/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 75
- Tensile Strength, Yield: 6.21 MPa
- Tensile Strength, Yield: 14.8 MPa
- Elongation at Break: 420 %
$ 2077/MT
- Specific Gravity: 0.990 g/cc
- Melt Flow: 1.20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 75
- Tensile Strength at Break: 9.17 MPa
- Elongation at Break: 750 %
$ 1682/MT
- Specific Gravity: 1.25 g/cc
- Hardness, Shore A: 47
- Tensile Strength, Yield: 9.10 MPa
- Elongation at Break: 430 %
- Maximum Service Temperature, Air: 190 °C @Time >=Error in fixSigDigits: @digits must be between 1 a sec
$ 1941/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore A: 67
- Tensile Strength, Yield: 17.7 MPa
- Elongation at Break: 220 %
- Maximum Service Temperature, Air: 190 °C @Time >=Error in fixSigDigits: @digits must be between 1 a sec
$ 1643/MT
- Specific Gravity: 1.27 g/cc
- Hardness, Shore A: 72
- Tensile Strength, Yield: 14.7 MPa
- Elongation at Break: 340 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 1461/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore A: 90
- Hardness, Shore A: 95
- Tensile Strength at Break: 22.1 MPa
- Tensile Strength, Yield: 13.2 MPa
$ 1504/MT
- Specific Gravity: 1.08 g/cc
- Melt Flow: 7.0 g/10 min @Load 5.00 kg, Temperature 177 °C
- Hardness, Shore A: 40
- Tensile Strength, Yield: 4.59 MPa
- Tensile Strength, Yield: 9.17 MPa
$ 1693/MT
- Specific Gravity: 1.18 g/cc
- Hardness, Shore A: 70
- Tensile Strength at Break: 13.1 MPa
- Elongation at Break: 430 %
$ 1473/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Yield: 7.24 MPa
- Tensile Strength, Yield: 15.2 MPa
- Elongation at Break: 360 %
$ 1788/MT
- Specific Gravity: 1.02 g/cc
- Hardness, Shore A: 69
- Tensile Strength: 17.7 MPa
- Elongation at Break: 300 %
$ 1561/MT
- Specific Gravity: 1.32 g/cc
- Hardness, Shore A: 60
- Tensile Strength, Yield: 9.51 MPa
- Elongation at Break: 380 %
- Brittleness Temperature: -41.0 °C
$ 1749/MT
- Specific Gravity: 1.23 g/cc
- Hardness, Shore A: 80
- Hardness, Shore A: 86
- Tensile Strength at Break: 17.7 MPa
- Elongation at Break: 330 %
- Brittleness Temperature: -31.0 °C
$ 1573/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 50
- Tensile Strength, Yield: 2.07 MPa
- Tensile Strength, Yield: 5.52 MPa
- Elongation at Break: 400 %
$ 1822/MT
- Specific Gravity: 1.31 g/cc
- Melt Flow: 18.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 83
- Tensile Strength at Break: 9.5113 MPa
- Tensile Strength at Break: 10.26 MPa
$ 1673/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore C: 88
- Tensile Strength at Break: 23.4 MPa
- Elongation at Break: 280 %
- Maximum Service Temperature, Air: 80.0 °C
$ 2416/MT
- Specific Gravity: 1.25 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Yield: 19.3 MPa
- Elongation at Break: 320 %
- Brittleness Temperature: -17.0 °C
- Melt Temperature: 182 °C
$ 1636/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Yield: 8.55 MPa
- Tensile Strength, Yield: 15.8 MPa
- Elongation at Break: 360 %
$ 1926/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 19.7 MPa
- Elongation at Break: 390 %
- Brittleness Temperature: -34.0 °C
- Appearance: Clear/Transparent
$ 2125/MT
- Specific Gravity: 1.24 g/cc
- Melt Flow: 10.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 86
- Tensile Strength at Break: 10.24 MPa
- Tensile Strength at Break: 11.4 MPa
$ 1859/MT
- Specific Gravity: 1.41 g/cc
- Hardness, Shore A: 86
- Tensile Strength, Yield: 13.60 MPa
- Tensile Strength, Yield: 16.0 MPa
- Elongation at Break: 224 %
$ 1653/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore C: 67
- Tensile Strength at Break: 17.7 MPa
- Elongation at Break: 250 %
- Maximum Service Temperature, Air: 90.0 °C
$ 1628/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 55
- Tensile Strength, Yield: 11.8 MPa
- Elongation at Break: 420 %
- Maximum Service Temperature, Air: 190 °C @Time >=3600 sec
$ 1990/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 2.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 65
- Tensile Strength at Break: 9.58 MPa
- Elongation at Break: 860 %
$ 1911/MT
- Specific Gravity: 1.36 g/cc
- Hardness, Shore A: 78
- Tensile Strength, Yield: 14.9 MPa
- Tensile Strength, Yield: 18.6 MPa
- Elongation at Break: 196 %
$ 1726/MT
- Specific Gravity: 1.62 g/cc
- Hardness, Shore C: 80
- Hardness, Shore C: 89
- Tensile Strength at Break: 14.5 MPa
- Elongation at Break: 270 %
$ 2369/MT
- Specific Gravity: 1.23 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 19.4 MPa
- Elongation at Break: 410 %
- Brittleness Temperature: -34.0 °C
- Appearance: Clear/Transparent
$ 1527/MT
- Specific Gravity: 1.24 g/cc
- Hardness, Shore A: 85
- Tensile Strength at Break: 20.0 MPa
- Elongation at Break: 390 %
- Brittleness Temperature: -30.0 °C
- Appearance: Clear/Transparent
$ 2547/MT
- Specific Gravity: 1.42 g/cc
- Tensile Strength, Yield: 45.1 MPa
- Elongation at Break: 100 %
- Izod Impact, Notched: 0.587 J/cm
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
- Vicat Softening Point: 85.0 °C
$ 1643/MT
- Specific Gravity: 1.28 g/cc
- Melt Flow: 3.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 56
- Tensile Strength at Break: 9.65 MPa
- Elongation at Break: 600 %
$ 1468/MT
- Specific Gravity: 1.16 g/cc
- Hardness, Shore A: 55
- Tensile Strength: 15.7 MPa
- Elongation at Break: 300 %
$ 2445/MT
- Specific Gravity: 1.19 g/cc
- Hardness, Shore A: 70
- Tensile Strength at Break: 13.8 MPa
- Elongation at Break: 420 %
- Appearance: Clear
$ 2056/MT
- Specific Gravity: 1.16 g/cc
- Hardness, Shore A: 60
- Tensile Strength at Break: 9.65 MPa
- Elongation at Break: 400 %
- Brittleness Temperature: -44.0 °C
- Appearance: Clear/Transparent
$ 2369/MT
- Specific Gravity: 1.15 g/cc
- Hardness, Shore A: 60
- Tensile Strength, Yield: 3.79 MPa
- Tensile Strength, Yield: 10.3 MPa
- Elongation at Break: 440 %
$ 1501/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore C: 77
- Tensile Strength at Break: 23.8 MPa
- Elongation at Break: 270 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1615/MT
- Specific Gravity: 1.54 g/cc
- Hardness, Shore C: 74
- Tensile Strength at Break: 17.2 MPa
- Elongation at Break: 290 %
- Maximum Service Temperature, Air: 90.0 °C
$ 1724/MT
- Specific Gravity: 1.54 g/cc
- Hardness, Shore C: 72
- Tensile Strength at Break: 17.0 MPa
- Elongation at Break: 290 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1803/MT
- Specific Gravity: 1.38 g/cc
- Melt Flow: 1.80 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 81
- Tensile Strength at Break: 15.0 MPa
- Elongation at Break: 350 %
$ 1609/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Yield: 8.96 MPa
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Break: 420 %
$ 1618/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 70
- Tensile Strength: 11.8 MPa
- Elongation at Break: 300 %
$ 2020/MT
- Specific Gravity: 1.29 g/cc
- Hardness, Shore A: 91
- Hardness, Shore C: 66
- Tensile Strength at Break: 8.27 MPa
- Elongation at Break: 80 %
$ 1599/MT
- Maximum Service Temperature, Air: 190 °C @Time >=3600 sec
- Vicat Softening Point: 75.0 °C
$ 1529/MT
- Specific Gravity: 1.13 g/cc
- Hardness, Shore A: 50
- Tensile Strength at Break: 9.58 MPa
- Tensile Strength, Yield: 2.83 MPa
- Elongation at Break: 450 %
- Brittleness Temperature: -50.0 °C
$ 1624/MT
- Specific Gravity: 1.16 g/cc
- Hardness, Shore A: 60
- Tensile Strength at Break: 10.6 MPa
- Elongation at Break: 380 %
- Brittleness Temperature: -43.0 °C
- Appearance: Clear/Transparent
$ 1981/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore A: 50
- Hardness, Shore A: 55
- Tensile Strength at Break: 5.86 MPa
- Tensile Strength, Yield: 1.72 MPa
$ 2082/MT
- Specific Gravity: 1.26 g/cc
- Hardness, Shore A: 90
- Tensile Strength at Break: 20.0 MPa
- Elongation at Break: 300 %
- Brittleness Temperature: -20.0 °C
- Appearance: Clear/Transparent
$ 1507/MT
- Specific Gravity: 1.40 g/cc
- Hardness, Shore A: 84
- Tensile Strength, Yield: 14.40 MPa
- Tensile Strength, Yield: 18.0 MPa
- Elongation at Break: 154 %
$ 1740/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 78
- Tensile Strength at Break: 15.9 MPa
- Elongation at Break: 390 %
- Brittleness Temperature: -37.0 °C
$ 1504/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Yield: 10.1 MPa
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Break: 340 %
$ 2499/MT
- Specific Gravity: 1.40 g/cc
- Hardness, Shore A: 75
- Hardness, Shore A: 81
- Tensile Strength at Break: 12.1 MPa
- Elongation at Break: 360 %
$ 1760/MT
- Specific Gravity: 1.21 g/cc
- Tensile Strength, Yield: 5.58 MPa
- Tensile Strength, Yield: 15.5 MPa
- Elongation at Break: 380 %
- Brittleness Temperature: -35.0 °C
- Melt Temperature: 174 °C
$ 2483/MT
- Specific Gravity: 1.31 g/cc
- Hardness, Shore A: 84
- Tensile Strength, Yield: 18.9 MPa
- Elongation at Break: 350 %
- Brittleness Temperature: -25.0 °C
$ 1610/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 73
- Tensile Strength: 17.7 MPa
- Elongation at Break: 150 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 1702/MT
- Specific Gravity: 1.26 g/cc
- Hardness, Shore A: 90
- Tensile Strength at Break: 23.2 MPa
- Elongation at Break: 360 %
- Brittleness Temperature: -23.0 °C
- Appearance: Clear/Transparent
$ 2281/MT
- Specific Gravity: 1.43 g/cc
- Hardness, Shore A: 89
- Tensile Strength, Yield: 16.8 MPa
- Tensile Strength, Yield: 18.6 MPa
- Elongation at Break: 200 %
- Elongation at Break: 250 %
$ 2077/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 54
- Tensile Strength, Yield: 9.79 MPa
- Elongation at Break: 410 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 1549/MT
- Specific Gravity: 0.970 g/cc
- Melt Flow: 0.200 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 70
- Tensile Strength at Break: 8.62 MPa
- Elongation at Break: 850 %
$ 1698/MT
- Specific Gravity: 1.28 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore C: 80
- Tensile Strength at Break: 20.7 MPa
- Elongation at Break: 280 %
$ 1595/MT
- Specific Gravity: 1.29 g/cc
- Hardness, Shore A: 63
- Tensile Strength, Yield: 9.79 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 190 °C @Time >=Error in fixSigDigits: @digits must be between 1 a sec
$ 2257/MT
- Specific Gravity: 1.36 g/cc
- Hardness, Shore C: 67
- Tensile Strength at Break: 18.3 MPa
- Elongation at Break: 310 %
- Maximum Service Temperature, Air: 90.0 °C
$ 1596/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 2.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 55
- Tensile Strength at Break: 6.34 MPa
- Elongation at Break: 680 %
$ 1927/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore C: 70
- Tensile Strength at Break: 23.1 MPa
- Elongation at Break: 260 %
- Maximum Service Temperature, Air: 80.0 °C
$ 2588/MT
- Specific Gravity: 1.02 g/cc
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 12.0 MPa
- Tensile Stress: 4.69 MPa @Strain 50.0 %
$ 1891/MT
- Specific Gravity: 1.02 g/cc
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 12.0 MPa
- Tensile Stress: 4.69 MPa @Strain 50.0 %
$ 1595/MT
- Specific Gravity: 1.02 g/cc
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 12.0 MPa
- Tensile Stress: 4.69 MPa @Strain 50.0 %
$ 1704/MT
- Specific Gravity: 1.42 g/cc
- Hardness, Shore A: 73
- Tensile Strength at Break: 9.31 MPa
- Elongation at Break: 280 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1610/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 75
- Tensile Strength, Yield: 6.89 MPa
- Tensile Strength, Yield: 16.5 MPa
- Elongation at Break: 360 %
$ 2156/MT
- Specific Gravity: 1.13 g/cc
- Hardness, Shore A: 60
- Tensile Strength, Yield: 11.4 MPa
- Elongation at Break: 240 %
- Compression Set: 35 %
$ 1625/MT
- Specific Gravity: 1.41 g/cc
- Hardness, Shore A: 93
- Tensile Strength, Yield: 17.62 MPa
- Tensile Strength, Yield: 19.6 MPa
- Elongation at Break: 212.5 %
$ 1474/MT
- Specific Gravity: 1.12 g/cc
- Hardness, Shore A: 55
- Tensile Strength, Yield: 9.65 MPa
- Elongation at Break: 300 %
- Compression Set: 35 %
$ 1654/MT
- Specific Gravity: 1.27 g/cc
- Hardness, Shore A: 82
- Tensile Strength, Yield: 17.7 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 1956/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 65
- Tensile Strength, Yield: 13.2 MPa
- Elongation at Break: 370 %
- Maximum Service Temperature, Air: 190 °C @Time >=1800 sec
$ 1647/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Yield: 9.10 MPa
- Tensile Strength, Yield: 16.5 MPa
- Elongation at Break: 420 %
$ 1587/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Yield: 9.10 MPa
- Tensile Strength, Yield: 16.5 MPa
- Elongation at Break: 420 %
$ 1472/MT
- Specific Gravity: 1.17 g/cc
- Hardness, Shore A: 65
- Tensile Strength at Break: 12.1 MPa
- Elongation at Break: 440 %
- Appearance: Clear/Transparent
$ 1446/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 85
- Tensile Strength at Break: 18.6 MPa
- Elongation at Break: 360 %
- Appearance: Opaque
$ 1753/MT
- Specific Gravity: 1.39 g/cc
- Hardness, Shore C: 70
- Tensile Strength at Break: 21.4 MPa
- Elongation at Break: 320 %
- Maximum Service Temperature, Air: 80.0 °C
$ 2043/MT
- Specific Gravity: 1.39 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore C: 77
- Tensile Strength at Break: 19.3 MPa
- Elongation at Break: 280 %
$ 1738/MT
- Specific Gravity: 1.45 g/cc
- Hardness, Shore A: 82
- Tensile Strength at Break: 14.5 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 105 °C
$ 2297/MT
- Specific Gravity: 1.31 g/cc
- Hardness, Shore C: 75
- Tensile Strength at Break: 21.4 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 105 °C
$ 1617/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 2.30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 65
- Tensile Strength at Break: 6.62 MPa
- Elongation at Break: 760 %
$ 1701/MT
- Specific Gravity: 1.32 g/cc
- Hardness, Shore A: 90
- Tensile Strength at Break: 16.5 MPa
- Elongation at Break: 300 %
- Tear Strength: 43.8 kN/m
- Brittleness Temperature: -28.0 °C
$ 1619/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 75
- Tensile Strength at Break: 14.8 MPa
- Elongation at Break: 420 %
- Appearance: Clear/Transparent
$ 2379/MT
- Specific Gravity: 1.41 g/cc
- Hardness, Shore D: 78
- Tensile Strength, Yield: 39.2 MPa
- Elongation at Break: 150 %
- Izod Impact, Notched: 1.39 J/cm
$ 1544/MT
- Specific Gravity: 1.33 g/cc
- Tensile Strength, Yield: 43.2 MPa
- Elongation at Break: 170 %
- Izod Impact, Notched: 0.961 J/cm
- Vicat Softening Point: 76.1 °C
$ 2169/MT
- Specific Gravity: 1.33 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore C: 70
- Tensile Strength at Break: 21.4 MPa
- Elongation at Break: 320 %
$ 1461/MT
- Specific Gravity: 1.17 g/cc
- Hardness, Shore A: 65
- Tensile Strength at Break: 11.7 MPa
- Elongation at Break: 390 %
- Brittleness Temperature: -40.0 °C
- Appearance: Clear/Transparent
$ 2297/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore A: 81
- Tensile Strength at Break: 17.6 MPa
- Elongation at Break: 380 %
- Maximum Service Temperature, Air: 105 °C
$ 1977/MT
- Specific Gravity: 1.31 g/cc
- Hardness, Shore C: 82
- Tensile Strength at Break: 23.2 MPa
- Elongation at Break: 280 %
- Maximum Service Temperature, Air: 80.0 °C
$ 1592/MT
- Specific Gravity: 1.26 g/cc
- Hardness, Shore A: 90
- Tensile Strength at Break: 21.4 MPa
- Elongation at Break: 380 %
- Brittleness Temperature: -27.0 °C
- Appearance: Clear/Transparent
$ 1769/MT
- Specific Gravity: 1.25 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Yield: 18.5 MPa
- Elongation at Break: 330 %
- Melt Temperature: 182 °C
$ 1620/MT
- Specific Gravity: 1.42 g/cc
- Hardness, Shore C: 65
- Tensile Strength at Break: 19.3 MPa
- Elongation at Break: 330 %
- Maximum Service Temperature, Air: 90.0 °C
$ 2385/MT
- Specific Gravity: 1.19 g/cc
- Hardness, Shore A: 75
- Tensile Strength at Break: 16.9 MPa
- Elongation at Break: 450 %
- Brittleness Temperature: -38.0 °C
- Appearance: Clear/Transparent
$ 1679/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 13.1 MPa
- Elongation at Break: 390 %
- Brittleness Temperature: -35.0 °C
$ 1821/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 70
- Tensile Strength, Yield: 14.8 MPa
- Elongation at Break: 370 %
- Brittleness Temperature: -35.0 °C
- Melt Temperature: 174 °C
$ 2428/MT
- Specific Gravity: 1.49 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Yield: 16.8 MPa
- Tensile Strength, Yield: 18.6 MPa
- Elongation at Break: 195.5 %
- Elongation at Break: 230 %
$ 1603/MT
- Density: 1.29 g/cc
- Hardness, Shore A: 90
- Tensile Strength at Break: 9.797 MPa
- Elongation at Break: 450 %
- 100% Modulus: 0.00530 GPa
$ 1835/MT
- Specific Gravity: 1.40 g/cc
- Melt Flow: 17.0 g/10 min @Load 21.6 kg, Temperature 190 °C
- Tensile Strength, Yield: 57.8 MPa
- Elongation at Break: 40 %
- Izod Impact, Notched: 0.390 J/cm
$ 1725/MT
- Specific Gravity: 1.55 g/cc
- Hardness, Shore C: 70
- Tensile Strength at Break: 16.8 MPa
- Elongation at Break: 310 %
- Maximum Service Temperature, Air: 75.0 °C
$ 2329/MT
- Specific Gravity: 1.39 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 16.5 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 105 °C
$ 1546/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 65
- Tensile Strength, Yield: 5.17 MPa
- Tensile Strength, Yield: 14.5 MPa
- Elongation at Break: 400 %
$ 1450/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore C: 67
- Tensile Strength at Break: 19.3 MPa
- Elongation at Break: 310 %
- Maximum Service Temperature, Air: 90.0 °C
$ 1637/MT
- Specific Gravity: 1.19 g/cc
- Hardness, Shore A: 70
- Tensile Strength at Break: 13.8 MPa
- Elongation at Break: 410 %
- Brittleness Temperature: -40.0 °C
- Appearance: Clear/Transparent
$ 1499/MT
- Specific Gravity: 1.40 g/cc
- Hardness, Shore A: 83
- Tensile Strength, Yield: 14.15 MPa
- Tensile Strength, Yield: 15.7 MPa
- Elongation at Break: 224 %
- Elongation at Break: 280 %
Delivery PVC Teknor Apex Company
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
lng carrier vessel for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.