$ 1611/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore C: 71
- Tensile Strength at Break: 22.1 MPa
- Elongation at Break: 320 %
- Maximum Service Temperature, Air: 105 °C
$ 1492/MT
- Specific Gravity: 1.30 g/cc
- Linear Mold Shrinkage: 0.015 - 0.018 cm/cm
- Hardness, Shore A: 70
- Tensile Strength at Break: 13.8 MPa
- Elongation at Break: 430 %
$ 1481/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 70
- Tensile Strength, Yield: 4.83 MPa
- Tensile Strength, Yield: 12.2 MPa
- Elongation at Break: 380 %
$ 1689/MT
- Specific Gravity: 1.25 g/cc
- Hardness, Shore A: 90
- Tensile Strength at Break: 22.1 MPa
- Elongation at Break: 330 %
- Maximum Service Temperature, Air: 60.0 °C
$ 1457/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 85
- Tensile Strength at Break: 19.0 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 50.0 °C
$ 1951/MT
- Specific Gravity: 1.23 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore A: 80
- Tensile Strength at Break: 17.0 MPa
- Elongation at Break: 340 %
$ 1604/MT
- Specific Gravity: 1.32 g/cc
- Hardness, Shore C: 86
- Tensile Strength at Break: 19.0 MPa
- Elongation at Break: 360 %
- Maximum Service Temperature, Air: 105 °C
$ 1450/MT
- Specific Gravity: 1.38 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore A: 86
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 280 %
$ 1680/MT
- Specific Gravity: 1.42 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore A: 85
- Tensile Strength at Break: 13.1 MPa
- Elongation at Break: 290 %
$ 2500/MT
- Specific Gravity: 1.39 g/cc
- Hardness, Shore C: 86
- Tensile Strength at Break: 17.6 MPa
- Elongation at Break: 280 %
- Maximum Service Temperature, Air: 60.0 °C
$ 2572/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 3.80 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 45
- Tensile Strength at Break: 6.27 MPa
- Elongation at Break: 830 %
$ 1570/MT
- Specific Gravity: 1.44 g/cc
- Hardness, Shore A: 84
- Tensile Strength, Yield: 15.02 MPa
- Tensile Strength, Yield: 16.7 MPa
- Elongation at Break: 224 %
- Elongation at Break: 280 %
$ 1447/MT
- Specific Gravity: 1.40 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 14.1 MPa
- Tensile Strength: 8.48 MPa
- Elongation at Break: 390 %
$ 1608/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 90
- Tensile Strength at Break: 17.9 MPa
- Elongation at Break: 290 %
- Maximum Service Temperature, Air: 105 °C
$ 1784/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 70
- Tensile Strength, Yield: 5.52 MPa
- Tensile Strength, Yield: 12.6 MPa
- Elongation at Break: 370 %
$ 1902/MT
- Specific Gravity: 1.43 g/cc
- Hardness, Shore C: 85
- Tensile Strength at Break: 16.5 MPa
- Elongation at Break: 320 %
- Maximum Service Temperature, Air: 75.0 °C
$ 2224/MT
- Specific Gravity: 1.54 g/cc
- Hardness, Shore C: 74
- Hardness, Shore C: 85
- Tensile Strength at Break: 18.1 MPa
- Elongation at Break: 280 %
$ 2022/MT
- Specific Gravity: 1.13 g/cc
- Hardness, Shore A: 55
- Tensile Strength, Yield: 3.31 MPa
- Tensile Strength, Yield: 10.0 MPa
- Elongation at Break: 440 %
$ 1807/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 60
- Tensile Strength, Yield: 3.86 MPa
- Tensile Strength, Yield: 10.0 MPa
- Elongation at Break: 390 %
$ 2259/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore C: 88
- Tensile Strength at Break: 24.1 MPa
- Elongation at Break: 280 %
- Maximum Service Temperature, Air: 80.0 °C
$ 1622/MT
- Specific Gravity: 1.25 g/cc
- Hardness, Shore A: 90
- Tensile Strength, Yield: 12.8 MPa
- Tensile Strength, Yield: 19.7 MPa
- Elongation at Break: 340 %
$ 2358/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 75
- Tensile Strength at Break: 15.5 MPa
- Elongation at Break: 360 %
- Brittleness Temperature: -36.0 °C
- Appearance: Opaque
$ 1949/MT
- Specific Gravity: 1.54 g/cc
- Hardness, Shore A: 86
- Tensile Strength at Break: 14.1 MPa
- Elongation at Break: 280 %
- Maximum Service Temperature, Air: 90.0 °C
$ 1658/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Yield: 7.31 MPa
- Tensile Strength, Yield: 11.0 MPa
- Elongation at Break: 240 %
$ 1951/MT
- Specific Gravity: 1.39 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore C: 82
- Tensile Strength at Break: 18.8 MPa
- Elongation at Break: 280 %
$ 1877/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Yield: 8.27 MPa
- Tensile Strength, Yield: 16.2 MPa
- Elongation at Break: 360 %
$ 1664/MT
- Specific Gravity: 1.19 g/cc
- Melt Flow: 5.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 7.93 MPa
- Elongation at Break: 550 %
$ 1478/MT
- Specific Gravity: 1.16 g/cc
- Hardness, Shore A: 55
- Tensile Strength, Yield: 3.59 MPa
- Tensile Strength, Yield: 10.3 MPa
- Elongation at Break: 460 %
$ 1774/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 16.4 MPa
- Elongation at Break: 380 %
- Maximum Service Temperature, Air: 60.0 °C
$ 1784/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 75
- Tensile Strength, Yield: 6.89 MPa
- Tensile Strength, Yield: 16.2 MPa
- Elongation at Break: 420 %
$ 2132/MT
- Specific Gravity: 1.25 g/cc
- Hardness, Shore A: 72
- Tensile Strength at Break: 14.5 MPa
- Elongation at Break: 330 %
- Maximum Service Temperature, Air: 105 °C
$ 1973/MT
- Specific Gravity: 1.17 g/cc
- Hardness, Shore A: 70
- Tensile Strength at Break: 15.2 MPa
- Elongation at Break: 430 %
- Maximum Service Temperature, Air: 50.0 °C
$ 1560/MT
- Specific Gravity: 1.26 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore A: 90
- Tensile Strength at Break: 17.8 MPa
- Elongation at Break: 240 %
$ 1469/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 86
- Tensile Strength at Break: 20.5 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 105 °C
$ 1478/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore C: 65
- Tensile Strength at Break: 20.3 MPa
- Elongation at Break: 360 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1590/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 75
- Tensile Strength, Yield: 7.03 MPa
- Tensile Strength, Yield: 14.5 MPa
- Elongation at Break: 370 %
$ 2165/MT
- Specific Gravity: 1.58 g/cc
- Hardness, Shore C: 86
- Tensile Strength at Break: 19.3 MPa
- Elongation at Break: 230 %
- Maximum Service Temperature, Air: 75.0 °C
$ 2144/MT
- Specific Gravity: 1.24 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore A: 85
- Tensile Strength at Break: 15.0 MPa
- Elongation at Break: 250 %
$ 1864/MT
- Specific Gravity: 1.40 g/cc
- Hardness, Shore A: 91
- Tensile Strength, Yield: 17.00 MPa
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Break: 192 %
$ 1627/MT
- Specific Gravity: 1.59 g/cc
- Hardness, Shore C: 87
- Hardness, Shore C: 92
- Tensile Strength at Break: 17.9 MPa
- Elongation at Break: 200 %
$ 1706/MT
- Specific Gravity: 1.29 g/cc
- Melt Flow: 1.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 53
- Tensile Strength at Break: 8.27 MPa
- Elongation at Break: 530 %
$ 1810/MT
- Specific Gravity: 1.17 g/cc
- Hardness, Shore A: 60
- Tensile Strength, Yield: 3.86 MPa
- Tensile Strength, Yield: 10.7 MPa
- Elongation at Break: 450 %
$ 1518/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 85
- Tensile Strength at Break: 19.7 MPa
- Elongation at Break: 360 %
- Maximum Service Temperature, Air: 105 °C
$ 2057/MT
- Specific Gravity: 1.56 g/cc
- Hardness, Shore A: 86
- Tensile Strength at Break: 16.9 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 75.0 °C
$ 2226/MT
- Specific Gravity: 1.23 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Yield: 10.3 MPa
- Tensile Strength, Yield: 17.6 MPa
- Elongation at Break: 350 %
$ 1624/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore C: 84
- Tensile Strength at Break: 24.3 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 60.0 °C
$ 1580/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore C: 82
- Tensile Strength at Break: 17.9 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1721/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore A: 86
- Tensile Strength at Break: 17.9 MPa
- Elongation at Break: 360 %
- Maximum Service Temperature, Air: 105 °C
$ 1501/MT
- Specific Gravity: 1.60 g/cc
- Hardness, Shore C: 83
- Tensile Strength at Break: 17.2 MPa
- Elongation at Break: 200 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1996/MT
- Specific Gravity: 1.09 g/cc
- Melt Flow: 2.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 73
- Tensile Strength at Break: 13.5 MPa
- Elongation at Break: 680 %
$ 1518/MT
- Specific Gravity: 1.43 g/cc
- Hardness, Shore A: 85
- Tensile Strength at Break: 15.4 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 80.0 °C
$ 1469/MT
- Specific Gravity: 1.13 g/cc
- Hardness, Shore A: 45
- Tensile Strength, Yield: 2.24 MPa
- Tensile Strength, Yield: 7.58 MPa
- Elongation at Break: 480 %
$ 2007/MT
- Specific Gravity: 1.17 g/cc
- Hardness, Shore A: 60
- Tensile Strength, Yield: 3.86 MPa
- Tensile Strength, Yield: 10.7 MPa
- Elongation at Break: 450 %
$ 1448/MT
- Specific Gravity: 1.42 g/cc
- Hardness, Shore C: 73
- Tensile Strength at Break: 19.3 MPa
- Elongation at Break: 280 %
- Maximum Service Temperature, Air: 75.0 °C
$ 2572/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore A: 72
- Tensile Strength at Break: 15.2 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 105 °C
$ 1596/MT
- Specific Gravity: 1.41 g/cc
- Hardness, Shore A: 83
- Tensile Strength, Yield: 16.8 MPa
- Tensile Strength, Yield: 18.6 MPa
- Elongation at Break: 238 %
- Elongation at Break: 280 %
$ 1553/MT
- Specific Gravity: 0.960 g/cc
- Melt Flow: 0.900 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 65
- Tensile Strength at Break: 8.96 MPa
- Elongation at Break: 750 %
$ 1810/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore A: 65
- Tensile Strength at Break: 13.1 MPa
- Elongation at Break: 390 %
- Maximum Service Temperature, Air: 105 °C
$ 2045/MT
- Specific Gravity: 1.21 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore A: 80
- Tensile Strength at Break: 15.5 MPa
- Elongation at Break: 380 %
$ 1903/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 90
- Tensile Strength, Yield: 15.2 MPa
- Tensile Strength, Yield: 20.7 MPa
- Elongation at Break: 310 %
$ 1721/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 3.10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 60
- Tensile Strength at Break: 9.24 MPa
- Elongation at Break: 880 %
$ 1830/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore C: 90
- Tensile Strength at Break: 24.1 MPa
- Elongation at Break: 270 %
- Brittleness Temperature: -10.0 °C
$ 1869/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 8.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 41
- Tensile Strength at Break: 3.45 MPa
- Elongation at Break: 730 %
$ 1451/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore C: 69
- Tensile Strength at Break: 21.0 MPa
- Elongation at Break: 320 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1650/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore C: 69
- Tensile Strength at Break: 21.0 MPa
- Elongation at Break: 320 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1580/MT
- Specific Gravity: 1.36 g/cc
- Hardness, Shore A: 74
- Tensile Strength at Break: 14.2 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1852/MT
- Specific Gravity: 1.23 g/cc
- Hardness, Shore A: 75
- Tensile Strength at Break: 15.9 MPa
- Elongation at Break: 360 %
- Maximum Service Temperature, Air: 60.0 °C
$ 1610/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore C: 70
- Tensile Strength at Break: 22.4 MPa
- Elongation at Break: 270 %
- Maximum Service Temperature, Air: 80.0 °C
$ 1598/MT
- Specific Gravity: 1.65 g/cc
- Viscosity: 473000 cP @Frequency 1000 Hz, Temperature 177 °C
- Hardness, Shore C: 86
- Hardness, Shore C: 91
- Tensile Strength at Break: 15.9 MPa
$ 2112/MT
- Specific Gravity: 1.11 g/cc
- Melt Flow: 24 g/10 min @Load 5.00 kg, Temperature 177 °C
- Hardness, Shore A: 50
- Tensile Strength, Yield: 5.93 MPa
- Tensile Strength, Yield: 9.487 MPa
$ 1600/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore A: 86
- Tensile Strength, Yield: 17.62 MPa
- Tensile Strength, Yield: 19.6 MPa
- Elongation at Break: 221 %
- Elongation at Break: 260 %
$ 1449/MT
- Specific Gravity: 1.25 g/cc
- Hardness, Shore A: 74
- Tensile Strength at Break: 13.8 MPa
- Tensile Strength: 6.65 MPa
- Elongation at Break: 320 %
$ 1712/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 70
- Tensile Strength at Break: 14.5 MPa
- Elongation at Break: 410 %
- Maximum Service Temperature, Air: 75.0 °C
$ 2382/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 2.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 55
- Tensile Strength at Break: 9.17 MPa
- Elongation at Break: 920 %
$ 1783/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 16.5 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 80.0 °C
$ 1717/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 15.2 MPa
- Elongation at Break: 380 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1461/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore C: 90
- Tensile Strength at Break: 24.1 MPa
- Elongation at Break: 240 %
- Maximum Service Temperature, Air: 105 °C
$ 2180/MT
- Specific Gravity: 1.19 g/cc
- Linear Mold Shrinkage: 0.015 - 0.018 cm/cm
- Hardness, Shore A: 70
- Tensile Strength at Break: 13.1 MPa
- Elongation at Break: 450 %
$ 1851/MT
- Specific Gravity: 1.11 g/cc
- Hardness, Shore A: 45
- Tensile Strength, Yield: 8.55 MPa
- Elongation at Break: 280 %
- Compression Set: 32 %
$ 1725/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 85
- Tensile Strength at Break: 16.5 MPa
- Elongation at Break: 370 %
- Maximum Service Temperature, Air: 105 °C
$ 1553/MT
- Specific Gravity: 1.26 g/cc
- Linear Mold Shrinkage: 0.015 - 0.018 cm/cm
- Hardness, Shore A: 60
- Tensile Strength at Break: 11.4 MPa
- Elongation at Break: 440 %
$ 1859/MT
- Specific Gravity: 1.13 g/cc
- Hardness, Shore A: 45
- Tensile Strength, Yield: 2.24 MPa
- Tensile Strength, Yield: 7.58 MPa
- Elongation at Break: 480 %
$ 1944/MT
- Specific Gravity: 1.52 g/cc
- Hardness, Shore A: 91
- Tensile Strength, Yield: 17.62 MPa
- Tensile Strength, Yield: 19.6 MPa
- Elongation at Break: 170 %
$ 1560/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 60
- Tensile Strength, Yield: 3.31 MPa
- Tensile Strength, Yield: 8.96 MPa
- Elongation at Break: 400 %
$ 2222/MT
- Specific Gravity: 1.26 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 20.0 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 80.0 °C
$ 2485/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 65
- Tensile Strength, Yield: 4.76 MPa
- Tensile Strength, Yield: 11.6 MPa
- Elongation at Break: 390 %
$ 2385/MT
- Specific Gravity: 1.36 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 17.2 MPa
- Elongation at Break: 320 %
- Maximum Service Temperature, Air: 80.0 °C
$ 1752/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore A: 90
- Tensile Strength at Break: 21.4 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 105 °C
$ 1662/MT
- Specific Gravity: 1.59 g/cc
- Hardness, Shore C: 85
- Hardness, Shore C: 92
- Tensile Strength at Break: 17.6 MPa
- Elongation at Break: 200 %
$ 1682/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore A: 83
- Tensile Strength: 17.4 MPa
- Elongation at Break: 360 %
- Brittleness Temperature: -30.0 °C
- Oxygen Index: 29 %
$ 1759/MT
- Specific Gravity: 1.09 g/cc
- Hardness, Shore A: 40
- Tensile Strength, Yield: 6.96 MPa
- Elongation at Break: 300 %
- Compression Set: 32 %
$ 1697/MT
- Specific Gravity: 1.39 g/cc
- Hardness, Shore A: 90
- Tensile Strength at Break: 16.8 MPa
- Elongation at Break: 340 %
- Maximum Service Temperature, Air: 105 °C
$ 1499/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore A: 72
- Tensile Strength at Break: 14.5 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 105 °C
$ 1726/MT
- Specific Gravity: 1.35 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore C: 69
- Tensile Strength at Break: 14.3 MPa
- Elongation at Break: 230 %
$ 1490/MT
- Specific Gravity: 1.23 g/cc
- Linear Mold Shrinkage: 0.015 - 0.018 cm/cm
- Hardness, Shore A: 55
- Tensile Strength at Break: 10.7 MPa
- Elongation at Break: 480 %
$ 2243/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 105 °C
$ 2038/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 105 °C
$ 1638/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 105 °C
$ 1777/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 105 °C
$ 1866/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 105 °C
$ 2248/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 105 °C
$ 1726/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 105 °C
$ 1592/MT
- Specific Gravity: 1.47 g/cc
- Hardness, Shore A: 79
- Tensile Strength, Yield: 15.33 MPa
- Tensile Strength, Yield: 17.0 MPa
- Elongation at Break: 240 %
$ 1966/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 105 °C
$ 1831/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 105 °C
$ 1938/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 105 °C
$ 2288/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 105 °C
$ 2117/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 105 °C
$ 1608/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 105 °C
$ 1648/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 1.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 62
- Tensile Strength at Break: 4.21 MPa
- Elongation at Break: 720 %
$ 2030/MT
- Specific Gravity: 1.39 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore C: 71
- Tensile Strength at Break: 18.3 MPa
- Elongation at Break: 280 %
$ 2288/MT
- Specific Gravity: 1.39 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 15.9 MPa
- Elongation at Break: 330 %
- Maximum Service Temperature, Air: 80.0 °C
$ 2293/MT
- Specific Gravity: 1.24 g/cc
- Hardness, Shore A: 72
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 390 %
- Maximum Service Temperature, Air: 80.0 °C
$ 2262/MT
- Specific Gravity: 1.25 g/cc
- Hardness, Shore A: 72
- Tensile Strength at Break: 14.5 MPa
- Elongation at Break: 330 %
- Maximum Service Temperature, Air: 105 °C
$ 1560/MT
- Specific Gravity: 1.44 g/cc
- Hardness, Shore A: 73
- Tensile Strength, Yield: 13.96 MPa
- Tensile Strength, Yield: 15.5 MPa
- Elongation at Break: 240 %
- Elongation at Break: 300 %
$ 1471/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 65
- Tensile Strength, Yield: 4.62 MPa
- Tensile Strength, Yield: 11.0 MPa
- Elongation at Break: 380 %
$ 2030/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 75
- Tensile Strength, Yield: 5.52 MPa
- Tensile Strength, Yield: 13.1 MPa
- Elongation at Break: 370 %
$ 1741/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore A: 86
- Tensile Strength at Break: 17.9 MPa
- Elongation at Break: 310 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1480/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 55
- Tensile Strength, Yield: 2.69 MPa
- Tensile Strength, Yield: 6.89 MPa
- Elongation at Break: 390 %
$ 1468/MT
- Specific Gravity: 1.19 g/cc
- Hardness, Shore A: 70
- Tensile Strength, Yield: 5.52 MPa
- Tensile Strength, Yield: 11.4 MPa
- Elongation at Break: 390 %
$ 1490/MT
- Specific Gravity: 1.46 g/cc
- Hardness, Shore A: 85
- Tensile Strength at Break: 15.2 MPa
- Elongation at Break: 290 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1765/MT
- Specific Gravity: 1.37 g/cc
- Melt Flow: 1.60 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 80
- Tensile Strength at Break: 15.9 MPa
- Elongation at Break: 350 %
$ 1496/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore C: 76
- Tensile Strength at Break: 20.0 MPa
- Elongation at Break: 290 %
- Maximum Service Temperature, Air: 105 °C
$ 1542/MT
- Specific Gravity: 1.14 g/cc
- Hardness, Shore A: 50
- Tensile Strength, Yield: 2.55 MPa
- Tensile Strength, Yield: 8.41 MPa
- Elongation at Break: 460 %
$ 1501/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore C: 89
- Tensile Strength at Break: 17.6 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 80.0 °C
$ 1526/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Yield: 11.7 MPa
- Tensile Strength, Yield: 17.9 MPa
- Elongation at Break: 330 %
$ 1660/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 79
- Tensile Strength at Break: 14.8 MPa
- Elongation at Break: 390 %
- Maximum Service Temperature, Air: 105 °C
$ 1908/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore A: 73
- Tensile Strength at Break: 13.8 MPa
- Elongation at Break: 370 %
- Maximum Service Temperature, Air: 80.0 °C
$ 1570/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore C: 69
- Tensile Strength at Break: 22.8 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 80.0 °C
$ 1711/MT
- Specific Gravity: 1.03 g/cc
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 80
- Tensile Strength at Break: 10.8 MPa
- Tensile Stress: 3.52 MPa @Strain 50.0 %
$ 2353/MT
- Specific Gravity: 1.17 g/cc
- Hardness, Shore A: 65
- Tensile Strength, Yield: 4.48 MPa
- Tensile Strength, Yield: 11.7 MPa
- Elongation at Break: 430 %
$ 1523/MT
- Specific Gravity: 1.11 g/cc
- Hardness, Shore A: 50
- Tensile Strength, Yield: 2.76 MPa
- Tensile Strength, Yield: 8.27 MPa
- Elongation at Break: 450 %
$ 1599/MT
- Specific Gravity: 1.44 g/cc
- Hardness, Shore C: 85
- Tensile Strength at Break: 14.8 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 75.0 °C
$ 2162/MT
- Specific Gravity: 1.44 g/cc
- Hardness, Shore C: 85
- Tensile Strength at Break: 14.8 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 75.0 °C
$ 2223/MT
- Specific Gravity: 1.53 g/cc
- Hardness, Shore C: 67
- Tensile Strength at Break: 15.5 MPa
- Elongation at Break: 290 %
- Maximum Service Temperature, Air: 80.0 °C
$ 2239/MT
- Specific Gravity: 1.42 g/cc
- Hardness, Shore C: 72
- Tensile Strength at Break: 21.4 MPa
- Elongation at Break: 340 %
- Flexural Modulus: 0.0752 GPa
$ 1534/MT
- Density: 1.30 g/cc
- Hardness, Shore A: 82
- Tensile Strength at Break: 7.398 MPa
- Elongation at Break: 450 %
- 100% Modulus: 0.00360 GPa
$ 1845/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore C: 73
- Tensile Strength at Break: 14.7 MPa
- Elongation at Break: 310 %
- Maximum Service Temperature, Air: 80.0 °C
$ 1911/MT
- Specific Gravity: 1.39 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore C: 75
- Tensile Strength at Break: 17.2 MPa
- Elongation at Break: 160 %
$ 1986/MT
- Specific Gravity: 1.31 g/cc
- Hardness, Shore A: 73
- Tensile Strength, Yield: 9.3596 MPa
- Tensile Strength, Yield: 12.5 MPa
- Elongation at Break: 97.5 %
- Elongation at Break: 150 %
$ 1473/MT
- Specific Gravity: 1.18 g/cc
- Hardness, Shore A: 68
- Tensile Strength, Yield: 4.76 MPa
- Tensile Strength, Yield: 12.8 MPa
- Elongation at Break: 430 %
$ 1545/MT
- Specific Gravity: 1.42 g/cc
- Hardness, Shore A: 84
- Tensile Strength, Yield: 13.53 MPa
- Tensile Strength, Yield: 15.0 MPa
- Elongation at Break: 200 %
$ 1896/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore C: 88
- Tensile Strength at Break: 17.2 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 105 °C
$ 1514/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore C: 90
- Tensile Strength at Break: 24.1 MPa
- Elongation at Break: 240 %
- Maximum Service Temperature, Air: 105 °C
$ 1789/MT
- Specific Gravity: 1.36 g/cc
- Hardness, Shore C: 70
- Tensile Strength at Break: 19.7 MPa
- Elongation at Break: 320 %
- Maximum Service Temperature, Air: 80.0 °C
$ 1531/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Yield: 8.00 MPa
- Tensile Strength, Yield: 11.9 MPa
- Elongation at Break: 270 %
$ 2045/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 1.70 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 70
- Tensile Strength at Break: 5.10 MPa
- Elongation at Break: 700 %
$ 2392/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore C: 70
- Tensile Strength at Break: 21.7 MPa
- Elongation at Break: 320 %
- Maximum Service Temperature, Air: 80.0 °C
$ 1662/MT
- Specific Gravity: 1.58 g/cc
- Hardness, Shore C: 81
- Tensile Strength at Break: 19.7 MPa
- Elongation at Break: 240 %
- Maximum Service Temperature, Air: 105 °C
$ 2281/MT
- Specific Gravity: 1.24 g/cc
- Hardness, Shore A: 86
- Tensile Strength at Break: 22.6 MPa
- Elongation at Break: 380 %
- Maximum Service Temperature, Air: 75.0 °C
$ 2067/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 55
- Tensile Strength, Yield: 3.24 MPa
- Tensile Strength, Yield: 8.00 MPa
- Elongation at Break: 410 %
$ 1834/MT
- Specific Gravity: 1.40 g/cc
- Hardness, Shore C: 75
- Tensile Strength at Break: 19.3 MPa
- Elongation at Break: 330 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1517/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 75
- Tensile Strength at Break: 15.0 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 50.0 °C
$ 1576/MT
- Specific Gravity: 1.43 g/cc
- Hardness, Shore C: 85
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 80.0 °C
$ 1454/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 65
- Tensile Strength, Yield: 4.07 MPa
- Tensile Strength, Yield: 10.3 MPa
- Elongation at Break: 390 %
$ 1692/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Yield: 7.24 MPa
- Tensile Strength, Yield: 15.9 MPa
- Elongation at Break: 370 %
$ 2083/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 70
- Tensile Strength, Yield: 5.58 MPa
- Tensile Strength, Yield: 13.4 MPa
- Elongation at Break: 390 %
$ 1583/MT
- Specific Gravity: 1.30 g/cc
- Melt Flow: 13.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 88
- Tensile Strength at Break: 10.8 MPa @Thickness 1.91 mm
- Elongation at Break: 600 %
$ 1688/MT
- Specific Gravity: 1.36 g/cc
- Hardness, Shore A: 83
- Tensile Strength at Break: 17.4 MPa
- Elongation at Break: 360 %
- Maximum Service Temperature, Air: 80.0 °C
$ 2047/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore C: 80
- Tensile Strength at Break: 17.6 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 105 °C
$ 1932/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 50
- Tensile Strength, Yield: 2.28 MPa
- Tensile Strength, Yield: 6.89 MPa
- Elongation at Break: 430 %
$ 1562/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 75
- Tensile Strength, Yield: 6.21 MPa
- Tensile Strength, Yield: 11.9 MPa
- Elongation at Break: 290 %
$ 2033/MT
- Specific Gravity: 1.23 g/cc
- Hardness, Shore A: 65
- Tensile Strength at Break: 14.5 MPa
- Elongation at Break: 390 %
- Maximum Service Temperature, Air: 105 °C
$ 1455/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore C: 71
- Tensile Strength at Break: 22.8 MPa
- Elongation at Break: 330 %
- Maximum Service Temperature, Air: 105 °C
$ 1496/MT
- Specific Gravity: 1.17 g/cc
- Hardness, Shore A: 65
- Tensile Strength, Yield: 3.86 MPa
- Tensile Strength, Yield: 11.7 MPa
- Elongation at Break: 430 %
$ 1524/MT
- Specific Gravity: 1.23 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Yield: 10.8 MPa
- Tensile Strength, Yield: 19.3 MPa
- Elongation at Break: 380 %
$ 1506/MT
- Specific Gravity: 1.23 g/cc
- Hardness, Shore A: 83
- Tensile Strength at Break: 17.2 MPa
- Elongation at Break: 360 %
- Maximum Service Temperature, Air: 105 °C
$ 2576/MT
- Specific Gravity: 1.24 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore C: 65
- Tensile Strength at Break: 20.7 MPa
- Elongation at Break: 230 %
$ 1621/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Yield: 10.3 MPa
- Tensile Strength, Yield: 13.1 MPa
- Elongation at Break: 240 %
$ 1460/MT
- Specific Gravity: 1.28 g/cc
- Hardness, Shore A: 72
- Tensile Strength at Break: 13.3 MPa
- Elongation at Break: 390 %
- Maximum Service Temperature, Air: 105 °C
$ 2597/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 90
- Tensile Strength, Yield: 13.1 MPa
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Break: 330 %
$ 1686/MT
- Specific Gravity: 1.31 g/cc
- Hardness, Shore C: 73
- Tensile Strength at Break: 22.1 MPa
- Elongation at Break: 340 %
- Brittleness Temperature: -28.0 °C
$ 1659/MT
- Specific Gravity: 1.09 g/cc
- Melt Flow: 30 g/10 min @Load 5.00 kg, Temperature 177 °C
- Hardness, Shore A: 45
- Tensile Strength, Yield: 5.72 MPa
- Tensile Strength, Yield: 6.29 MPa
$ 1673/MT
- Specific Gravity: 1.15 g/cc
- Hardness, Shore A: 60
- Tensile Strength, Yield: 3.79 MPa
- Tensile Strength, Yield: 10.3 MPa
- Elongation at Break: 450 %
$ 1621/MT
- Specific Gravity: 1.48 g/cc
- Hardness, Shore A: 83
- Tensile Strength, Yield: 15.33 MPa
- Tensile Strength, Yield: 17.0 MPa
- Elongation at Break: 240 %
- Elongation at Break: 300 %
$ 1613/MT
- Specific Gravity: 1.58 g/cc
- Hardness, Shore C: 87
- Hardness, Shore C: 92
- Tensile Strength at Break: 17.7 MPa
- Elongation at Break: 190 %
$ 2056/MT
- Specific Gravity: 1.36 g/cc
- Hardness, Shore A: 85
- Tensile Strength at Break: 18.6 MPa
- Elongation at Break: 320 %
- Maximum Service Temperature, Air: 60.0 °C
$ 2178/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 75
- Tensile Strength, Yield: 6.21 MPa
- Tensile Strength, Yield: 14.8 MPa
- Elongation at Break: 420 %
$ 1883/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 55
- Tensile Strength, Yield: 3.10 MPa
- Tensile Strength, Yield: 8.96 MPa
- Elongation at Break: 410 %
$ 1648/MT
- Specific Gravity: 1.40 g/cc
- Hardness, Shore C: 67
- Tensile Strength at Break: 23.4 MPa
- Elongation at Break: 340 %
- Maximum Service Temperature, Air: 105 °C
$ 2088/MT
- Specific Gravity: 1.19 g/cc
- Hardness, Shore A: 70
- Tensile Strength, Yield: 5.52 MPa
- Tensile Strength, Yield: 13.1 MPa
- Elongation at Break: 420 %
$ 1889/MT
- Specific Gravity: 1.18 g/cc
- Hardness, Shore A: 68
- Tensile Strength, Yield: 4.76 MPa
- Tensile Strength, Yield: 12.8 MPa
- Elongation at Break: 430 %
- Brittleness Temperature: -37.2 °C
$ 1564/MT
- Specific Gravity: 1.39 g/cc
- Hardness, Shore A: 90
- Tensile Strength at Break: 20.0 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 75.0 °C
$ 2492/MT
- Specific Gravity: 1.25 g/cc
- Hardness, Shore A: 90
- Tensile Strength, Yield: 14.5 MPa
- Tensile Strength, Yield: 21.7 MPa
- Elongation at Break: 350 %
$ 1831/MT
- Specific Gravity: 1.39 g/cc
- Hardness, Shore A: 85
- Tensile Strength at Break: 15.6 MPa
- Elongation at Break: 300 %
- Maximum Service Temperature, Air: 80.0 °C
$ 2433/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 1.70 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 80
- Tensile Strength at Break: 5.86 MPa
- Elongation at Break: 540 %
$ 1563/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 60
- Tensile Strength, Yield: 3.31 MPa
- Tensile Strength, Yield: 8.27 MPa
- Elongation at Break: 390 %
$ 2203/MT
- Specific Gravity: 1.68 g/cc
- Hardness, Shore C: 78
- Tensile Strength at Break: 13.8 MPa
- Elongation at Break: 230 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1474/MT
- Specific Gravity: 1.13 g/cc
- Hardness, Shore A: 55
- Tensile Strength, Yield: 3.31 MPa
- Tensile Strength, Yield: 10.0 MPa
- Elongation at Break: 450 %
$ 1455/MT
- Density: 1.26 g/cc
- Hardness, Shore D: 40
- Tensile Strength at Break: 13.60 MPa
- Elongation at Break: 510 %
- 100% Modulus: 0.00740 GPa
$ 1855/MT
- Specific Gravity: 1.21 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore A: 74
- Tensile Strength at Break: 15.4 MPa
- Elongation at Break: 350 %
$ 1799/MT
- Specific Gravity: 1.12 g/cc
- Hardness, Shore A: 50
- Tensile Strength, Yield: 9.10 MPa
- Elongation at Break: 390 %
- Compression Set: 35 %
$ 1828/MT
- Specific Gravity: 1.17 g/cc
- Linear Mold Shrinkage: 0.015 - 0.018 cm/cm
- Hardness, Shore A: 70
- Tensile Strength at Break: 12.6 MPa
- Elongation at Break: 420 %
$ 1536/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 50
- Tensile Strength, Yield: 2.48 MPa
- Tensile Strength, Yield: 7.93 MPa
- Elongation at Break: 410 %
$ 1459/MT
- Specific Gravity: 1.24 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Yield: 11.0 MPa
- Tensile Strength, Yield: 19.1 MPa
- Elongation at Break: 410 %
$ 1759/MT
- Specific Gravity: 1.30 g/cc
- Hardness, Shore C: 71
- Tensile Strength at Break: 22.1 MPa
- Elongation at Break: 320 %
- Maximum Service Temperature, Air: 105 °C
$ 2062/MT
- Specific Gravity: 1.39 g/cc
- Hardness, Shore A: 83
- Tensile Strength, Yield: 12.60 MPa
- Tensile Strength, Yield: 14.0 MPa
- Elongation at Break: 160 %
$ 1891/MT
- Specific Gravity: 1.25 g/cc
- Hardness, Shore A: 72
- Tensile Strength at Break: 14.5 MPa
- Elongation at Break: 330 %
- Maximum Service Temperature, Air: 105 °C
$ 2393/MT
- Specific Gravity: 1.39 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore C: 82
- Tensile Strength at Break: 20.7 MPa
- Elongation at Break: 250 %
$ 1669/MT
- Specific Gravity: 1.58 g/cc
- Hardness, Shore C: 85
- Tensile Strength at Break: 19.0 MPa
- Elongation at Break: 260 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1920/MT
- Specific Gravity: 1.51 g/cc
- Hardness, Shore C: 70
- Tensile Strength at Break: 15.9 MPa
- Elongation at Break: 250 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1451/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 17.2 MPa
- Elongation at Break: 380 %
- Maximum Service Temperature, Air: 50.0 °C
$ 1967/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 55
- Tensile Strength, Yield: 2.76 MPa
- Tensile Strength, Yield: 7.58 MPa
- Elongation at Break: 410 %
$ 1496/MT
- Specific Gravity: 1.39 g/cc
- Hardness, Shore A: 79
- Tensile Strength at Break: 15.7 MPa
- Elongation at Break: 340 %
- Maximum Service Temperature, Air: 80.0 °C
$ 1582/MT
- Specific Gravity: 1.37 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore A: 86
- Tensile Strength at Break: 11.7 MPa
- Elongation at Break: 260 %
$ 2087/MT
- Specific Gravity: 1.16 g/cc
- Hardness, Shore A: 55
- Tensile Strength, Yield: 3.59 MPa
- Tensile Strength, Yield: 10.3 MPa
- Elongation at Break: 460 %
$ 1560/MT
- Specific Gravity: 1.46 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Yield: 14.40 MPa
- Tensile Strength, Yield: 16.0 MPa
- Elongation at Break: 200 %
$ 1976/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 1.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 70
- Tensile Strength at Break: 11.4 MPa
- Elongation at Break: 850 %
$ 1529/MT
- Specific Gravity: 1.13 g/cc
- Melt Flow: 3.6 g/10 min @Load 5.00 kg, Temperature 177 °C
- Hardness, Shore A: 60
- Tensile Strength, Yield: 8.34 MPa
- Tensile Strength, Yield: 12.51 MPa
$ 1614/MT
- Specific Gravity: 0.930 g/cc
- Melt Flow: 2.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 69
- Tensile Strength at Break: 19.3 MPa
- Elongation at Break: 650 %
$ 1810/MT
- Specific Gravity: 1.31 g/cc
- Hardness, Shore C: 71
- Tensile Strength at Break: 21.4 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 105 °C
$ 1620/MT
- Specific Gravity: 1.41 g/cc
- Hardness, Shore A: 90
- Tensile Strength, Yield: 13.22 MPa
- Tensile Strength, Yield: 14.7 MPa
- Elongation at Break: 160 %
$ 1547/MT
- Specific Gravity: 1.32 g/cc
- Hardness, Shore A: 70
- Tensile Strength at Break: 11.2 MPa
- Elongation at Break: 380 %
- Maximum Service Temperature, Air: 90.0 °C
$ 1527/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 90
- Tensile Strength, Yield: 14.1 MPa
- Tensile Strength, Yield: 17.7 MPa
- Elongation at Break: 260 %
- Melt Temperature: 191 °C
$ 2110/MT
- Specific Gravity: 1.21 g/cc
- Melt Flow: 0.500 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 18.6 MPa
- Elongation at Break: 340 %
$ 2068/MT
- Specific Gravity: 1.11 g/cc
- Melt Flow: 15 g/10 min @Load 5.00 kg, Temperature 177 °C
- Hardness, Shore A: 55
- Tensile Strength, Yield: 7.10 MPa
- Tensile Strength, Yield: 11.789 MPa
$ 1609/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 75
- Tensile Strength, Yield: 5.52 MPa
- Tensile Strength, Yield: 10.0 MPa
- Elongation at Break: 260 %
$ 2257/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 75
- Tensile Strength, Yield: 6.89 MPa
- Tensile Strength, Yield: 12.2 MPa
- Elongation at Break: 370 %
$ 2028/MT
- Specific Gravity: 1.36 g/cc
- Hardness, Shore A: 85
- Tensile Strength at Break: 20.0 MPa
- Elongation at Break: 310 %
- Maximum Service Temperature, Air: 105 °C
$ 2301/MT
- Specific Gravity: 1.40 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore C: 82
- Tensile Strength at Break: 17.6 MPa
- Elongation at Break: 150 %
$ 1944/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore A: 88
- Tensile Strength at Break: 19.3 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 105 °C
$ 1526/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Yield: 11.0 MPa
- Tensile Strength, Yield: 14.5 MPa
- Elongation at Break: 270 %
$ 1689/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 50
- Tensile Strength, Yield: 2.69 MPa
- Tensile Strength, Yield: 6.83 MPa
- Elongation at Break: 420 %
$ 1678/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 65
- Tensile Strength, Yield: 4.00 MPa
- Tensile Strength, Yield: 9.65 MPa
- Elongation at Break: 380 %
$ 1489/MT
- Specific Gravity: 1.27 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore C: 80
- Tensile Strength at Break: 20.7 MPa
- Elongation at Break: 280 %
$ 1563/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore C: 70
- Tensile Strength at Break: 23.1 MPa
- Elongation at Break: 260 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1515/MT
- Specific Gravity: 1.41 g/cc
- Hardness, Shore A: 82
- Tensile Strength at Break: 16.2 MPa
- Elongation at Break: 360 %
- Brittleness Temperature: -37.0 °C
$ 1567/MT
- Specific Gravity: 1.26 g/cc
- Hardness, Shore C: 83
- Tensile Strength at Break: 17.2 MPa
- Elongation at Break: 360 %
- Maximum Service Temperature, Air: 90.0 °C
$ 1516/MT
- Specific Gravity: 1.21 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore A: 85
- Tensile Strength at Break: 17.2 MPa
- Elongation at Break: 220 %
$ 1497/MT
- Specific Gravity: 1.20 g/cc
- Hardness, Shore A: 75
- Tensile Strength, Yield: 6.21 MPa
- Tensile Strength, Yield: 14.8 MPa
- Elongation at Break: 420 %
$ 2077/MT
- Specific Gravity: 0.990 g/cc
- Melt Flow: 1.20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 75
- Tensile Strength at Break: 9.17 MPa
- Elongation at Break: 750 %
$ 1504/MT
- Specific Gravity: 1.08 g/cc
- Melt Flow: 7.0 g/10 min @Load 5.00 kg, Temperature 177 °C
- Hardness, Shore A: 40
- Tensile Strength, Yield: 4.59 MPa
- Tensile Strength, Yield: 9.17 MPa
$ 1473/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Yield: 7.24 MPa
- Tensile Strength, Yield: 15.2 MPa
- Elongation at Break: 360 %
$ 1573/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 50
- Tensile Strength, Yield: 2.07 MPa
- Tensile Strength, Yield: 5.52 MPa
- Elongation at Break: 400 %
$ 1822/MT
- Specific Gravity: 1.31 g/cc
- Melt Flow: 18.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 83
- Tensile Strength at Break: 9.5113 MPa
- Tensile Strength at Break: 10.26 MPa
$ 1673/MT
- Specific Gravity: 1.33 g/cc
- Hardness, Shore C: 88
- Tensile Strength at Break: 23.4 MPa
- Elongation at Break: 280 %
- Maximum Service Temperature, Air: 80.0 °C
$ 1636/MT
- Specific Gravity: 1.34 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Yield: 8.55 MPa
- Tensile Strength, Yield: 15.8 MPa
- Elongation at Break: 360 %
$ 2125/MT
- Specific Gravity: 1.24 g/cc
- Melt Flow: 10.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 86
- Tensile Strength at Break: 10.24 MPa
- Tensile Strength at Break: 11.4 MPa
$ 1859/MT
- Specific Gravity: 1.41 g/cc
- Hardness, Shore A: 86
- Tensile Strength, Yield: 13.60 MPa
- Tensile Strength, Yield: 16.0 MPa
- Elongation at Break: 224 %
$ 1653/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore C: 67
- Tensile Strength at Break: 17.7 MPa
- Elongation at Break: 250 %
- Maximum Service Temperature, Air: 90.0 °C
$ 1990/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 2.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 65
- Tensile Strength at Break: 9.58 MPa
- Elongation at Break: 860 %
$ 1911/MT
- Specific Gravity: 1.36 g/cc
- Hardness, Shore A: 78
- Tensile Strength, Yield: 14.9 MPa
- Tensile Strength, Yield: 18.6 MPa
- Elongation at Break: 196 %
$ 1726/MT
- Specific Gravity: 1.62 g/cc
- Hardness, Shore C: 80
- Hardness, Shore C: 89
- Tensile Strength at Break: 14.5 MPa
- Elongation at Break: 270 %
$ 1643/MT
- Specific Gravity: 1.28 g/cc
- Melt Flow: 3.00 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 56
- Tensile Strength at Break: 9.65 MPa
- Elongation at Break: 600 %
$ 2369/MT
- Specific Gravity: 1.15 g/cc
- Hardness, Shore A: 60
- Tensile Strength, Yield: 3.79 MPa
- Tensile Strength, Yield: 10.3 MPa
- Elongation at Break: 440 %
$ 1615/MT
- Specific Gravity: 1.54 g/cc
- Hardness, Shore C: 74
- Tensile Strength at Break: 17.2 MPa
- Elongation at Break: 290 %
- Maximum Service Temperature, Air: 90.0 °C
$ 1724/MT
- Specific Gravity: 1.54 g/cc
- Hardness, Shore C: 72
- Tensile Strength at Break: 17.0 MPa
- Elongation at Break: 290 %
- Maximum Service Temperature, Air: 75.0 °C
$ 1609/MT
- Specific Gravity: 1.22 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Yield: 8.96 MPa
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Break: 420 %
$ 2020/MT
- Specific Gravity: 1.29 g/cc
- Hardness, Shore A: 91
- Hardness, Shore C: 66
- Tensile Strength at Break: 8.27 MPa
- Elongation at Break: 80 %
$ 1507/MT
- Specific Gravity: 1.40 g/cc
- Hardness, Shore A: 84
- Tensile Strength, Yield: 14.40 MPa
- Tensile Strength, Yield: 18.0 MPa
- Elongation at Break: 154 %
$ 1740/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 78
- Tensile Strength at Break: 15.9 MPa
- Elongation at Break: 390 %
- Brittleness Temperature: -37.0 °C
$ 1504/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Yield: 10.1 MPa
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Break: 340 %
$ 2281/MT
- Specific Gravity: 1.43 g/cc
- Hardness, Shore A: 89
- Tensile Strength, Yield: 16.8 MPa
- Tensile Strength, Yield: 18.6 MPa
- Elongation at Break: 200 %
- Elongation at Break: 250 %
$ 1549/MT
- Specific Gravity: 0.970 g/cc
- Melt Flow: 0.200 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 70
- Tensile Strength at Break: 8.62 MPa
- Elongation at Break: 850 %
$ 1698/MT
- Specific Gravity: 1.28 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore C: 80
- Tensile Strength at Break: 20.7 MPa
- Elongation at Break: 280 %
$ 2257/MT
- Specific Gravity: 1.36 g/cc
- Hardness, Shore C: 67
- Tensile Strength at Break: 18.3 MPa
- Elongation at Break: 310 %
- Maximum Service Temperature, Air: 90.0 °C
$ 1596/MT
- Specific Gravity: 1.18 g/cc
- Melt Flow: 2.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 55
- Tensile Strength at Break: 6.34 MPa
- Elongation at Break: 680 %
$ 2588/MT
- Specific Gravity: 1.02 g/cc
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 12.0 MPa
- Tensile Stress: 4.69 MPa @Strain 50.0 %
$ 1891/MT
- Specific Gravity: 1.02 g/cc
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 12.0 MPa
- Tensile Stress: 4.69 MPa @Strain 50.0 %
$ 1595/MT
- Specific Gravity: 1.02 g/cc
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 12.0 MPa
- Tensile Stress: 4.69 MPa @Strain 50.0 %
$ 1704/MT
- Specific Gravity: 1.42 g/cc
- Hardness, Shore A: 73
- Tensile Strength at Break: 9.31 MPa
- Elongation at Break: 280 %
- Maximum Service Temperature, Air: 75.0 °C
$ 2156/MT
- Specific Gravity: 1.13 g/cc
- Hardness, Shore A: 60
- Tensile Strength, Yield: 11.4 MPa
- Elongation at Break: 240 %
- Compression Set: 35 %
$ 1625/MT
- Specific Gravity: 1.41 g/cc
- Hardness, Shore A: 93
- Tensile Strength, Yield: 17.62 MPa
- Tensile Strength, Yield: 19.6 MPa
- Elongation at Break: 212.5 %
$ 1474/MT
- Specific Gravity: 1.12 g/cc
- Hardness, Shore A: 55
- Tensile Strength, Yield: 9.65 MPa
- Elongation at Break: 300 %
- Compression Set: 35 %
$ 1647/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Yield: 9.10 MPa
- Tensile Strength, Yield: 16.5 MPa
- Elongation at Break: 420 %
$ 1587/MT
- Specific Gravity: 1.21 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Yield: 9.10 MPa
- Tensile Strength, Yield: 16.5 MPa
- Elongation at Break: 420 %
$ 1753/MT
- Specific Gravity: 1.39 g/cc
- Hardness, Shore C: 70
- Tensile Strength at Break: 21.4 MPa
- Elongation at Break: 320 %
- Maximum Service Temperature, Air: 80.0 °C
$ 2043/MT
- Specific Gravity: 1.39 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore C: 77
- Tensile Strength at Break: 19.3 MPa
- Elongation at Break: 280 %
$ 1738/MT
- Specific Gravity: 1.45 g/cc
- Hardness, Shore A: 82
- Tensile Strength at Break: 14.5 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 105 °C
$ 2297/MT
- Specific Gravity: 1.31 g/cc
- Hardness, Shore C: 75
- Tensile Strength at Break: 21.4 MPa
- Elongation at Break: 350 %
- Maximum Service Temperature, Air: 105 °C
$ 1617/MT
- Specific Gravity: 0.880 g/cc
- Melt Flow: 2.30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 65
- Tensile Strength at Break: 6.62 MPa
- Elongation at Break: 760 %
$ 2169/MT
- Specific Gravity: 1.33 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore C: 70
- Tensile Strength at Break: 21.4 MPa
- Elongation at Break: 320 %
$ 2297/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore A: 81
- Tensile Strength at Break: 17.6 MPa
- Elongation at Break: 380 %
- Maximum Service Temperature, Air: 105 °C
$ 1977/MT
- Specific Gravity: 1.31 g/cc
- Hardness, Shore C: 82
- Tensile Strength at Break: 23.2 MPa
- Elongation at Break: 280 %
- Maximum Service Temperature, Air: 80.0 °C
$ 1620/MT
- Specific Gravity: 1.42 g/cc
- Hardness, Shore C: 65
- Tensile Strength at Break: 19.3 MPa
- Elongation at Break: 330 %
- Maximum Service Temperature, Air: 90.0 °C
$ 1679/MT
- Specific Gravity: 1.37 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 13.1 MPa
- Elongation at Break: 390 %
- Brittleness Temperature: -35.0 °C
$ 2428/MT
- Specific Gravity: 1.49 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Yield: 16.8 MPa
- Tensile Strength, Yield: 18.6 MPa
- Elongation at Break: 195.5 %
- Elongation at Break: 230 %
$ 1603/MT
- Density: 1.29 g/cc
- Hardness, Shore A: 90
- Tensile Strength at Break: 9.797 MPa
- Elongation at Break: 450 %
- 100% Modulus: 0.00530 GPa
$ 1725/MT
- Specific Gravity: 1.55 g/cc
- Hardness, Shore C: 70
- Tensile Strength at Break: 16.8 MPa
- Elongation at Break: 310 %
- Maximum Service Temperature, Air: 75.0 °C
$ 2329/MT
- Specific Gravity: 1.39 g/cc
- Hardness, Shore A: 80
- Tensile Strength at Break: 16.5 MPa
- Elongation at Break: 400 %
- Maximum Service Temperature, Air: 105 °C
$ 1450/MT
- Specific Gravity: 1.38 g/cc
- Hardness, Shore C: 67
- Tensile Strength at Break: 19.3 MPa
- Elongation at Break: 310 %
- Maximum Service Temperature, Air: 90.0 °C
$ 1499/MT
- Specific Gravity: 1.40 g/cc
- Hardness, Shore A: 83
- Tensile Strength, Yield: 14.15 MPa
- Tensile Strength, Yield: 15.7 MPa
- Elongation at Break: 224 %
- Elongation at Break: 280 %
Delivery Wire and Cable Grade Teknor Apex Company
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
tankers for sale turkey. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.