$ 1858/MT
- Thickness: 50.8 microns
- Coating Weight: >= 44.6 g/m²
- Shrinkage, MD: 19 %
- Shrinkage, TD: 2.0 %
- Haze: 2.8 %
$ 2013/MT
- Water Vapor Transmission: 5.10 g/m²/day
- Thickness: 25.4 microns
- Coating Weight: 22.7 g/m²
- Coefficient of Friction: 0.20
- Film Tensile Strength at Break, MD: 145 MPa
$ 1470/MT
- Density: 0.922 g/cc
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 3500 ppm
- Slip Level: 1000 ppm
- Film Tensile Strength at Yield, MD: 10.2 MPa
$ 1596/MT
- Water Vapor Transmission: 8.40 g/m²/day
- Thickness: 15.2 microns
- Coating Weight: 13.6 g/m²
- Coefficient of Friction: 0.20
- Film Tensile Strength at Break, MD: 124 MPa
$ 1796/MT
- Thickness: 25.4 microns
- Coating Weight: 22.7 g/m²
- Film Elongation at Break, MD: 174 %
- Film Elongation at Break, TD: 45 %
- Coefficient of Friction: 0.19
$ 1747/MT
- Water Vapor Transmission: 3.70 g/m²/day
- Thickness: 35.6 microns
- Coating Weight: 31.4 g/m²
- Coefficient of Friction: 0.34
- Coefficient of Friction: 0.39
$ 1589/MT
- Density: 0.924 g/cc
- Thickness: 50.8 microns
- Melt Flow: 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 4000 ppm
- Film Tensile Strength at Yield, MD: 11.0 MPa
$ 2009/MT
- Density: 0.918 g/cc
- Melt Flow: 4.5 g/10 min
- Film Tensile Strength at Yield, MD: 8.34 MPa
- Film Tensile Strength at Yield, TD: 7.31 MPa
- Film Elongation at Break, MD: 500 %
$ 1539/MT
- Thickness: 66.0 microns
- Coating Weight: >= 46.1 g/m²
- Film Elongation at Break, MD: 180 %
- Film Elongation at Break, TD: 65 %
- Coefficient of Friction: 0.25
$ 1555/MT
- Water Vapor Transmission: 2.50 g/m²/day
- Oxygen Transmission Rate: 6.20 cc/m²/day
- Thickness: 27.9 microns
- Coating Weight: 25.1 g/m²
- Coefficient of Friction: 0.28
$ 2287/MT
- Thickness: 50.8 microns
- Coating Weight: >= 46.1 g/m²
- Film Elongation at Break, MD: 185 %
- Film Elongation at Break, TD: 60 %
- Film Tensile Strength at Break, MD: 114 MPa
$ 1674/MT
- Density: 0.964 g/cc
- Thickness: 25.4 microns
- Melt Flow: 2.40 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 31.72 MPa
- Film Tensile Strength at Yield, TD: 27.58 MPa
$ 1876/MT
- Thickness: 76.2 microns
- Coating Weight: >= 51.5 g/m²
- Film Elongation at Break, MD: 200 %
- Film Elongation at Break, TD: 53 %
- Film Tensile Strength at Break, MD: 85.033 MPa
$ 1608/MT
- Density: 0.923 g/cc
- Thickness: 38.1 microns
- Melt Flow: 2.4 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 11.7 MPa
$ 1982/MT
- Thickness: 91.4 microns
- Coating Weight: >= 46.1 g/m²
- Film Elongation at Break, MD: 86 %
- Film Elongation at Break, TD: 25 %
- Film Tensile Strength at Break, MD: 42.13 MPa
$ 1599/MT
- Density: 0.900 g/cc
- Melt Flow: 2.8 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 3.38 MPa
- Elongation at Yield: 10 %
- Flexural Modulus, 1% Secant: 1430 MPa
$ 1749/MT
- Density: 0.923 g/cc
- Vinyl Acetate Content: 3.5 %
- Thickness: 38.1 microns
- Melt Flow: 1.3 g/10 min
- Antiblock Level: 3000 ppm
$ 2206/MT
- Water Vapor Transmission: 5.70 g/m²/day @Temperature 37.8 °C
- Oxygen Transmission Rate: 0.310 cc/m²/day @Temperature 22.8 °C
- Thickness: 21.3 microns
- Coating Weight: 19.4 g/m²
- Coefficient of Friction: 0.26
$ 1844/MT
- Water Vapor Transmission: 4.80 g/m²/day
- Thickness: 43.2 microns
- Coating Weight: 24.8 g/m²
- Coefficient of Friction: 0.36
- Film Tensile Strength at Break, MD: 78.600 MPa
$ 2205/MT
- Thickness: 86.4 microns
- Coating Weight: >= 42.2 g/m²
- Film Elongation at Break, MD: 86 %
- Film Elongation at Break, TD: 25 %
- Film Tensile Strength at Break, MD: 44.62 MPa
$ 2347/MT
- Water Vapor Transmission: 3.10 g/m²/day
- Oxygen Transmission Rate: 6.20 cc/m²/day
- Thickness: 20.8 microns
- Coating Weight: 19.7 g/m²
- Coefficient of Friction: 0.29
$ 1791/MT
- Density: 0.917 g/cc
- Thickness: 25.4 microns
- Melt Flow: 0.90 g/10 min
- Antiblock Level: 6500 ppm
- Slip Level: 1400 ppm
$ 1741/MT
- Density: 0.924 g/cc
- Vinyl Acetate Content: 2.0 %
- Melt Flow: 2.2 g/10 min
- Antiblock Level: 2100 ppm
- Slip Level: 700 ppm
$ 2356/MT
- Density: 0.924 g/cc
- Vinyl Acetate Content: 2.0 %
- Melt Flow: 2.2 g/10 min
- Antiblock Level: 2100 ppm
- Slip Level: 700 ppm
$ 2410/MT
- Density: 0.924 g/cc
- Vinyl Acetate Content: 2.0 %
- Melt Flow: 2.2 g/10 min
- Antiblock Level: 2100 ppm
- Slip Level: 700 ppm
$ 2463/MT
- Density: 0.924 g/cc
- Vinyl Acetate Content: 2.0 %
- Melt Flow: 2.2 g/10 min
- Antiblock Level: 2100 ppm
- Slip Level: 700 ppm
$ 1893/MT
- Density: 0.924 g/cc
- Vinyl Acetate Content: 2.0 %
- Melt Flow: 2.2 g/10 min
- Antiblock Level: 2100 ppm
- Slip Level: 700 ppm
$ 1951/MT
- Density: 0.936 g/cc
- Thickness: 50.8 microns
- Melt Flow: 0.20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 4.0 g/10 min @Load 10.0 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.6 MPa
$ 1500/MT
- Density: 0.900 g/cc
- Melt Flow: 17 g/10 min
- Neck In: 4.83 cm
- Neck In: 4.83 cm
- Neck In: 6.86 cm
$ 1449/MT
- Density: 0.923 g/cc
- Thickness: 38.1 microns
- Melt Flow: 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 2000 ppm
- Slip Level: 400 ppm
$ 1831/MT
- Water Vapor Transmission: 7.00 g/m²/day
- Thickness: 30.5 microns
- Coating Weight: >= 28.3 g/m²
- Coefficient of Friction: 0.30
- Film Tensile Strength at Break, MD: 33.1 MPa
$ 2256/MT
- Thickness: 96.5 microns
- Coating Weight: >= 64.6 g/m²
- Coefficient of Friction: 0.55
- Shrinkage, MD: 5.0 %
- Shrinkage, TD: 5.0 %
$ 1483/MT
- Density: 0.918 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 5000 ppm
- Slip Level: 1700 ppm
- Film Tensile Strength at Yield, MD: 9.65 MPa
$ 1958/MT
- Density: 0.9180 g/cc
- Melt Flow: 3.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 6.89 MPa
- Film Tensile Strength at Yield, TD: 6.76 MPa
- Film Elongation at Break, MD: 560 %
$ 1681/MT
- Water Vapor Transmission: 10.9 g/m²/day
- Thickness: 12.7 microns
- Coating Weight: 11.4 g/m²
- Coefficient of Friction: 0.35
- Film Tensile Strength at Break, MD: 131 MPa
$ 2380/MT
- Water Vapor Transmission: 7.00 g/m²/day
- Thickness: 30.0 microns
- Coating Weight: >= 27.5 g/m²
- Coefficient of Friction: 0.30
- Film Tensile Strength at Break, MD: 34.5 MPa
$ 2281/MT
- Density: 0.919 g/cc
- Thickness: 38.1 microns
- Melt Flow: 1.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 3000 ppm
- Film Tensile Strength at Yield, MD: 11.0 MPa
$ 1630/MT
- Water Vapor Transmission: 7.30 g/m²/day
- Thickness: 20.3 microns
- Coating Weight: 18.2 g/m²
- Coefficient of Friction: 0.25
- Film Tensile Strength at Break, MD: 138 MPa
$ 2093/MT
- Density: 0.925 g/cc
- Vinyl Acetate Content: 3.0 %
- Thickness: 38.1 microns
- Melt Flow: 2.5 g/10 min
- Antiblock Level: 2500 ppm
$ 1720/MT
- Density: 0.929 g/cc
- Thickness: 38.1 microns
- Melt Flow: 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 1000 ppm
- Film Tensile Strength at Yield, MD: 14.5 MPa
$ 1672/MT
- Density: 0.925 g/cc
- Vinyl Acetate Content: 6.1 %
- Thickness: 50.8 microns
- Melt Flow: 0.25 g/10 min
- Film Tensile Strength at Yield, MD: 8.76 MPa
$ 1456/MT
- Water Vapor Transmission: 5.00 g/m²/day
- Thickness: 30.5 microns
- Coating Weight: 27.0 g/m²
- Coefficient of Friction: 0.23
- Film Tensile Strength at Break, MD: 117 MPa
$ 1822/MT
- Water Vapor Transmission: 5.70 g/m²/day
- Thickness: 25.4 microns
- Coating Weight: 22.2 g/m²
- Coefficient of Friction: 0.24
- Film Tensile Strength at Break, MD: 137 MPa
$ 1609/MT
- Density: 0.917 g/cc
- Thickness: 25.4 microns
- Melt Flow: 0.90 g/10 min
- Antiblock Level: 8000 ppm
- Slip Level: 850 ppm
$ 1520/MT
- Thickness: 91.4 microns
- Coating Weight: >= 43.7 g/m²
- Film Elongation at Break, MD: 86 %
- Film Elongation at Break, TD: 25 %
- Film Tensile Strength at Break, MD: 42.13 MPa
$ 2210/MT
- Water Vapor Transmission: 4.30 g/m²/day
- Thickness: 30.5 microns
- Coating Weight: 27.4 g/m²
- Coefficient of Friction: 0.20
- Film Tensile Strength at Break, MD: 124 MPa
$ 1678/MT
- Density: 0.942 g/cc
- Vinyl Acetate Content: 18.5 %
- Melt Flow: 2.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 320 %
- Film Elongation at Break, TD: 740 %
$ 2527/MT
- Water Vapor Transmission: 5.90 g/m²/day
- Thickness: 33.0 microns
- Coating Weight: 20.0 g/m²
- Film Tensile Strength at Break, MD: 74.463 MPa
- Film Tensile Strength at Break, TD: 179.26 MPa
$ 1826/MT
- Water Vapor Transmission: 7.10 g/m²/day
- Thickness: 17.8 microns
- Coating Weight: 15.7 g/m²
- Coefficient of Friction: 0.40
- Coefficient of Friction: 0.40
$ 1689/MT
- Density: 0.941 g/cc
- Vinyl Acetate Content: 18.5 %
- Melt Flow: 1.60 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 180 %
- Film Elongation at Break, TD: 650 %
$ 2357/MT
- Density: 0.917 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 8.41 MPa
- Film Tensile Strength at Yield, TD: 7.72 MPa
- Film Elongation at Break, MD: 340 %
$ 1604/MT
- Water Vapor Transmission: 4.00 g/m²/day
- Oxygen Transmission Rate: 14.0 cc/m²/day
- Thickness: 38.1 microns
- Coating Weight: 21.6 g/m²
- Coefficient of Friction: 0.53
$ 1650/MT
- Density: 0.882 g/cc
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 84
- Melting Point: 75.0 °C
- Vicat Softening Point: 45.0 °C
$ 1937/MT
- Density: 0.926 g/cc
- Vinyl Acetate Content: 5.8 %
- Thickness: 38.1 microns
- Melt Flow: 2.0 g/10 min
- Film Tensile Strength at Yield, MD: 7.58 MPa
$ 1591/MT
- Thickness: 19.0 microns
- Coating Weight: 17.0 g/m²
- Film Elongation at Break, MD: 150 %
- Film Elongation at Break, TD: 50 %
- Coefficient of Friction: 0.20
$ 1576/MT
- Thickness: 30.5 microns
- Coating Weight: >= 27.2 g/m²
- Shrinkage, MD: 26 %
- Shrinkage, TD: 0.00 %
- Haze: 2.0 %
$ 1685/MT
- Water Vapor Transmission: 5.10 g/m²/day
- Oxygen Transmission Rate: 70.0 cc/m²/day
- Thickness: 27.9 microns
- Coating Weight: 25.9 g/m²
- Coefficient of Friction: 0.23
$ 2432/MT
- Water Vapor Transmission: 6.70 g/m²/day
- Thickness: 21.6 microns
- Coating Weight: 19.5 g/m²
- Coefficient of Friction: 0.24
- Film Tensile Strength at Break, MD: 138 MPa
$ 1563/MT
- Density: 0.948 g/cc
- Methyl Acrylate Content: 18 %
- Thickness: 31.8 microns
- Melt Flow: 3.20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 14000 ppm
$ 1863/MT
- Density: 0.918 g/cc
- Thickness: 20.3 microns
- Melt Flow: 3.5 g/10 min
- Film Tensile Strength at Yield, MD: 8.27 MPa
- Film Tensile Strength at Yield, TD: 7.58 MPa
$ 1504/MT
- Thickness: 66.0 microns
- Coating Weight: >= 47.7 g/m²
- Film Elongation at Break, MD: 200 %
- Film Elongation at Break, TD: 50 %
- Film Tensile Strength at Break, MD: 84.861 MPa
$ 1905/MT
- Density: 0.900 g/cc
- Thickness: 20.3 microns
- Melt Flow: 3.5 g/10 min
- Film Tensile Strength at Yield, MD: 6.27 MPa
- Film Tensile Strength at Yield, TD: 4.30 MPa
$ 1781/MT
- Thickness: 17.8 microns
- Coating Weight: >= 15.7 g/m²
- Film Elongation at Break, MD: 200 %
- Film Elongation at Break, TD: 60 %
- Film Tensile Strength at Break, MD: 118.20 MPa
$ 2211/MT
- Density: 0.932 g/cc
- Vinyl Acetate Content: 10.1 %
- Melt Flow: 0.190 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 300 %
- Film Elongation at Break, TD: 620 %
$ 1545/MT
- Density: 0.917 g/cc
- Thickness: 25.4 microns
- Melt Flow: 0.90 g/10 min
- Antiblock Level: 6500 ppm
- Film Tensile Strength at Yield, MD: 10.3 MPa
$ 1839/MT
- Density: 0.924 g/cc
- Vinyl Acetate Content: 5.5 %
- Thickness: 38.1 microns
- Melt Flow: 2.0 g/10 min
- Antiblock Level: 4000 ppm
$ 1478/MT
- Density: 0.924 g/cc
- Vinyl Acetate Content: 4.2 %
- Melt Flow: 1.25 g/10 min
- Antiblock Level: 4000 ppm
- Film Tensile Strength at Yield, MD: 8.07 MPa
$ 1488/MT
- Density: 0.924 g/cc
- Vinyl Acetate Content: 4.2 %
- Melt Flow: 1.25 g/10 min
- Antiblock Level: 4000 ppm
- Slip Level: 800 ppm
$ 2108/MT
- Water Vapor Transmission: 4.20 g/m²/day
- Thickness: 33.0 microns
- Coating Weight: 28.2 g/m²
- Coefficient of Friction: 0.34
- Coefficient of Friction: 0.39
$ 1923/MT
- Density: 0.923 g/cc
- Thickness: 38.1 microns
- Melt Flow: 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 1500 ppm
- Slip Level: 750 ppm
$ 1463/MT
- Density: 0.941 g/cc
- Thickness: 50.8 microns
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 5.8 g/10 min @Load 10.0 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 14.0 MPa
$ 2245/MT
- Density: 0.929 g/cc
- Thickness: 38.1 microns
- Melt Flow: 1.6 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 1000 ppm
- Slip Level: 250 ppm
$ 1664/MT
- Water Vapor Transmission: 5.70 g/m²/day
- Thickness: 25.4 microns
- Coating Weight: 22.2 g/m²
- Coefficient of Friction: 0.24
- Film Tensile Strength at Break, MD: 137 MPa
$ 1716/MT
- Density: 0.921 g/cc
- Melt Flow: 6.8 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 3000 ppm
- Slip Level: 1200 ppm
- Film Tensile Strength at Yield, MD: 9.65 MPa
$ 1528/MT
- Density: 0.900 g/cc
- Thickness: 25.4 microns
- Melt Flow: 3.5 g/10 min
- Film Tensile Strength at Yield, MD: 5.24 MPa
- Film Tensile Strength at Yield, TD: 4.55 MPa
$ 1578/MT
- Density: 0.918 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 7000 ppm
- Film Tensile Strength at Yield, MD: 9.65 MPa
- Film Tensile Strength at Yield, TD: 9.65 MPa
$ 1980/MT
- Thickness: 22.9 microns
- Coating Weight: >= 21.6 g/m²
- Coefficient of Friction: 0.25
- Coefficient of Friction: 0.25
- Film Tensile Strength at Break, MD: 141 MPa
$ 1773/MT
- Specific Gravity: 0.863 g/cc
- Melt Flow: 20 g/10 min
- Melt Flow: 9.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 66 @Time 15.0 sec
- Tensile Stress: 1.90 MPa @Strain 100 %
$ 1909/MT
- Density: 0.921 g/cc
- Vinyl Acetate Content: 2.0 %
- Melt Flow: 2.0 g/10 min
- Antiblock Level: 3500 ppm
- Slip Level: 725 ppm
$ 2275/MT
- Density: 0.925 g/cc
- Vinyl Acetate Content: 6.1 %
- Thickness: 50.8 microns
- Melt Flow: 0.25 g/10 min
- Antiblock Level: 6000 ppm
$ 1515/MT
- Water Vapor Transmission: 3.60 g/m²/day
- Oxygen Transmission Rate: 70.0 cc/m²/day
- Thickness: 38.1 microns
- Coating Weight: 35.5 g/m²
- Coefficient of Friction: 0.23
$ 1559/MT
- Water Vapor Transmission: 5.00 g/m²/day
- Thickness: 30.5 microns
- Coating Weight: 26.6 g/m²
- Coefficient of Friction: 0.25
- Coefficient of Friction: 0.52
$ 1501/MT
- Water Vapor Transmission: 5.70 g/m²/day
- Thickness: 25.4 microns
- Coating Weight: 22.6 g/m²
- Coefficient of Friction: 0.23
- Film Tensile Strength at Break, MD: 138 MPa
$ 1591/MT
- Water Vapor Transmission: 6.70 g/m²/day
- Thickness: 19.0 microns
- Coating Weight: 17.0 g/m²
- Coefficient of Friction: 0.20
- Film Tensile Strength at Break, MD: 124 MPa
$ 1626/MT
- Density: 0.918 g/cc
- Melt Flow: 2.0 g/10 min
- Antiblock Level: 7500 ppm
- Slip Level: 1350 ppm
- Film Tensile Strength at Yield, MD: 8.48 MPa
$ 1829/MT
- Density: 0.958 g/cc
- Melt Flow: 0.45 g/10 min @Load 2.16 kg, Temperature 190 °C
- High Load Melt Index: 30 g/10 min @Load 21.6 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 34.5 MPa
- Film Tensile Strength at Yield, TD: 13.1 MPa
$ 1688/MT
- Density: 0.925 g/cc
- Vinyl Acetate Content: 4.6 %
- Thickness: 38.1 microns
- Melt Flow: 1.0 g/10 min
- Antiblock Level: 4000 ppm
$ 1959/MT
- Density: 0.900 g/cc
- Melt Flow: 2.7 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 34.7 MPa
- Elongation at Yield: 10 %
- Flexural Modulus, 1% Secant: 1460 MPa
$ 2010/MT
- Water Vapor Transmission: 0.190 g/m²/day
- Oxygen Transmission Rate: 26.0 cc/m²/day
- Thickness: 17.8 microns
- Coating Weight: 15.7 g/m²
- Film Tensile Strength at Break, MD: 152 MPa
$ 2099/MT
- Thickness: 50.8 microns
- Coating Weight: >= 44.6 g/m²
- Film Elongation at Break, MD: 185 %
- Film Elongation at Break, TD: 60 %
- Film Tensile Strength at Break, MD: 114 MPa
$ 1714/MT
- Density: 0.900 g/cc
- Thickness: 25.4 microns
- Melt Flow: 7.5 g/10 min
- Film Tensile Strength at Yield, MD: 5.24 MPa
- Film Tensile Strength at Yield, TD: 4.48 MPa
$ 2011/MT
- Density: 0.924 g/cc
- Vinyl Acetate Content: 5.0 %
- Melt Flow: 2.0 g/10 min
- Antiblock Level: 5050 ppm
- Slip Level: 1500 ppm
$ 1471/MT
- Density: 0.924 g/cc
- Vinyl Acetate Content: 5.5 %
- Thickness: 38.1 microns
- Melt Flow: 2.0 g/10 min
- Antiblock Level: 3000 ppm
$ 2380/MT
- Density: 0.917 g/cc
- Thickness: 25.4 microns
- Melt Flow: 0.90 g/10 min
- Antiblock Level: 8000 ppm
- Slip Level: 1400 ppm
$ 1614/MT
- Water Vapor Transmission: 6.70 g/m²/day
- Thickness: 19.0 microns
- Coating Weight: 17.0 g/m²
- Coefficient of Friction: 0.20
- Film Tensile Strength at Break, MD: 124 MPa
$ 1532/MT
- Density: 0.895 g/cc
- Thickness: 25.4 microns
- Melt Flow: 2.2 g/10 min
- Film Tensile Strength at Yield, MD: 5.45 MPa
- Film Tensile Strength at Yield, TD: 4.07 MPa
$ 2319/MT
- Density: 0.933 g/cc
- Vinyl Acetate Content: 14.4 %
- Melt Flow: 3.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 190 %
- Film Elongation at Break, TD: 870 %
$ 1897/MT
- Density: 0.926 g/cc
- Thickness: 38.1 microns
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 5000 ppm
- Film Tensile Strength at Yield, MD: 11.7 MPa
$ 1457/MT
- Water Vapor Transmission: 0.390 g/m²/day
- Thickness: 12.7 microns
- Coating Weight: 11.4 g/m²
- Film Tensile Strength at Break, MD: 131 MPa
- Film Tensile Strength at Break, TD: 262 MPa
$ 1784/MT
- Density: 0.926 g/cc
- Vinyl Acetate Content: 5.8 %
- Thickness: 38.1 microns
- Melt Flow: 2.0 g/10 min
- Film Tensile Strength at Yield, MD: 7.58 MPa
$ 1445/MT
- Density: 0.873 g/cc
- Melt Flow: 4.5 g/10 min
- Melting Point: 52.8 °C
- Crystallization Temperature: 41.0 °C
- Vicat Softening Point: 55.0 °C
- Features: Thermal Stabilizer
$ 2055/MT
- Thickness: 12.7 microns
- Coating Weight: >= 11.4 g/m²
- Film Elongation at Break, MD: 160 %
- Film Elongation at Break, TD: 45 %
- Coefficient of Friction: 0.32
$ 2232/MT
- Water Vapor Transmission: 4.20 g/m²/day
- Thickness: 43.2 microns
- Coating Weight: 28.2 g/m²
- Film Tensile Strength at Break, MD: 88.942 MPa
- Film Tensile Strength at Break, TD: 162.03 MPa
$ 1606/MT
- Density: 0.942 g/cc
- Methyl Acrylate Content: 21.5 %
- Thickness: 31.8 microns
- Melt Flow: 2.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 370 %
$ 1778/MT
- Water Vapor Transmission: 7.60 g/m²/day
- Thickness: 17.8 microns
- Coating Weight: 16.5 g/m²
- Coefficient of Friction: 0.22
- Film Tensile Strength at Break, MD: 138 MPa
$ 1529/MT
- Thickness: 15.2 microns
- Coating Weight: 13.6 g/m²
- Film Elongation at Break, MD: 153 %
- Film Elongation at Break, TD: 46 %
- Coefficient of Friction: 0.21
$ 1951/MT
- Density: 0.952 g/cc
- Melt Flow: 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C
- High Load Melt Index: 10 g/10 min @Load 21.6 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 37.9 MPa
- Film Tensile Strength at Yield, TD: 33.1 MPa
$ 1945/MT
- Thickness: 66.0 microns
- Coating Weight: >= 46.1 g/m²
- Film Elongation at Break, MD: 200 %
- Film Elongation at Break, TD: 50 %
- Film Tensile Strength at Break, MD: 90.163 MPa
$ 1905/MT
- Density: 0.924 g/cc
- Thickness: 50.8 microns
- Antiblock Level: 2000 ppm
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 11.8 MPa
$ 1890/MT
- Density: 0.918 g/cc
- Thickness: 20.3 microns
- Melt Flow: 3.5 g/10 min
- Film Tensile Strength at Yield, MD: 8.27 MPa
- Film Tensile Strength at Yield, TD: 7.58 MPa
$ 1506/MT
- Density: 0.883 g/cc
- Thickness: 31.8 microns
- Melt Flow: 2.2 g/10 min
- Film Tensile Strength at Yield, MD: 3.45 MPa
- Film Tensile Strength at Yield, TD: 2.90 MPa
$ 1471/MT
- Density: 0.923 g/cc
- Vinyl Acetate Content: 3.5 %
- Thickness: 38.1 microns
- Melt Flow: 1.3 g/10 min
- Antiblock Level: 3000 ppm
$ 1978/MT
- Water Vapor Transmission: 8.20 g/m²/day
- Thickness: 19.0 microns
- Coating Weight: 17.3 g/m²
- Coefficient of Friction: 0.23
- Film Tensile Strength at Break, MD: 124 MPa
$ 2066/MT
- Density: 0.936 g/cc
- Thickness: 50.8 microns
- Melt Flow: 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 2.6 g/10 min @Load 10.0 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.9 MPa
$ 2015/MT
- Thickness: 17.8 microns
- Coating Weight: 15.7 g/m²
- Film Elongation at Break, MD: 162 %
- Film Elongation at Break, TD: 47 %
- Coefficient of Friction: 0.20
$ 1553/MT
- Water Vapor Transmission: 0.190 g/m²/day
- Thickness: 17.8 microns
- Coating Weight: 15.7 g/m²
- Film Tensile Strength at Break, MD: 152 MPa
- Film Tensile Strength at Break, TD: 234 MPa
$ 2093/MT
- Water Vapor Transmission: 5.10 g/m²/day
- Thickness: 25.4 microns
- Coating Weight: 22.7 g/m²
- Coefficient of Friction: 0.20
- Film Tensile Strength at Break, MD: 124 MPa
$ 1457/MT
- Water Vapor Transmission: 4.20 g/m²/day
- Oxygen Transmission Rate: 15.0 cc/m²/day
- Thickness: 17.8 microns
- Coating Weight: 16.8 g/m²
- Film Tensile Strength at Break, MD: 121 MPa
$ 1598/MT
- Density: 0.912 g/cc
- Thickness: 20.3 microns
- Melt Flow: 3.5 g/10 min
- Film Tensile Strength at Yield, MD: 7.52 MPa
- Film Tensile Strength at Yield, TD: 5.72 MPa
$ 1813/MT
- Density: 0.902 g/cc
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 38
- Melting Point: 97.2 °C
- Vicat Softening Point: 75.0 °C
$ 1991/MT
- Density: 0.941 g/cc
- Vinyl Acetate Content: 18.5 %
- Melt Flow: 1.60 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 10000 ppm
- Slip Level: 7050 ppm
$ 1662/MT
- Density: 0.905 g/cc
- Thickness: 25.4 microns
- Melt Flow: 4.5 g/10 min
- Film Tensile Strength at Yield, MD: 5.72 MPa
- Film Tensile Strength at Yield, TD: 4.96 MPa
$ 1531/MT
- Density: 0.922 g/cc
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 3500 ppm
- Slip Level: 1700 ppm
- Film Tensile Strength at Yield, MD: 10.3 MPa
$ 1803/MT
- Density: 0.923 g/cc
- Vinyl Acetate Content: 3.5 %
- Thickness: 38.1 microns
- Melt Flow: 1.3 g/10 min
- Antiblock Level: 2300 ppm
$ 1818/MT
- Water Vapor Transmission: 4.00 g/m²/day
- Thickness: 30.5 microns
- Coating Weight: >= 27.2 g/m²
- Coefficient of Friction: 0.24
- Film Tensile Strength at Break, MD: 138 MPa
$ 1537/MT
- Density: 0.888 g/cc
- Thickness: 25.4 microns
- Melt Flow: 2.2 g/10 min
- Film Tensile Strength at Yield, MD: 3.52 MPa
- Film Tensile Strength at Yield, TD: 3.10 MPa
$ 1741/MT
- Thickness: 76.2 microns
- Coating Weight: >= 51.5 g/m²
- Film Elongation at Break, MD: 165 %
- Film Elongation at Break, TD: 40 %
- Film Tensile Strength at Break, MD: 73.546 MPa
$ 1543/MT
- Density: 0.918 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 9.65 MPa
- Film Tensile Strength at Yield, TD: 9.65 MPa
- Film Elongation at Break, MD: 570 %
$ 2364/MT
- Water Vapor Transmission: 2.50 g/m²/day
- Oxygen Transmission Rate: 4.70 cc/m²/day
- Thickness: 17.8 microns
- Coating Weight: 17.4 g/m²
- Film Tensile Strength at Break, MD: 114 MPa
$ 1485/MT
- Density: 0.925 g/cc
- Thickness: 38.1 microns
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.7 MPa
- Film Tensile Strength at Yield, TD: 13.8 MPa
$ 1577/MT
- Density: 0.923 g/cc
- Vinyl Acetate Content: 3.5 %
- Thickness: 38.1 microns
- Melt Flow: 1.3 g/10 min
- Antiblock Level: 2500 ppm
$ 2314/MT
- Density: 0.9180 g/cc
- Melt Flow: 3.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 6.89 MPa
- Film Tensile Strength at Yield, TD: 6.76 MPa
- Film Elongation at Break, MD: 530 %
$ 1530/MT
- Density: 0.895 g/cc
- Thickness: 20.3 microns
- Melt Flow: 3.5 g/10 min
- Film Tensile Strength at Yield, MD: 4.76 MPa
- Film Tensile Strength at Yield, TD: 4.21 MPa
$ 1452/MT
- Density: 0.925 g/cc
- Vinyl Acetate Content: 4.6 %
- Thickness: 38.1 microns
- Melt Flow: 1.0 g/10 min
- Film Tensile Strength at Yield, MD: 8.27 MPa
$ 1505/MT
- Density: 0.933 g/cc
- Vinyl Acetate Content: 14.4 %
- Thickness: 31.8 microns
- Melt Flow: 3.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 300 %
$ 1484/MT
- Thickness: 12.7 microns
- Coating Weight: >= 11.4 g/m²
- Film Elongation at Break, MD: 160 %
- Film Elongation at Break, TD: 45 %
- Film Tensile Strength at Break, MD: 138 MPa
$ 2021/MT
- Density: 0.923 g/cc
- Thickness: 38.1 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 1000 ppm
- Slip Level: 750 ppm
$ 1474/MT
- Density: 0.923 g/cc
- Thickness: 38.1 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 1000 ppm
- Slip Level: 750 ppm
$ 1452/MT
- Density: 0.923 g/cc
- Thickness: 38.1 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 1000 ppm
- Film Tensile Strength at Yield, MD: 11.0 MPa
$ 1629/MT
- Thickness: 30.0 microns
- Coating Weight: >= 27.5 g/m²
- Coefficient of Friction: 0.30
- Film Tensile Strength at Break, MD: 34.5 MPa
- Film Tensile Strength at Break, TD: 150 MPa
$ 1777/MT
- Density: 0.902 g/cc
- Melt Flow: 30 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 38
- Melting Point: 97.2 °C
- Vicat Softening Point: 71.11 °C
- Brittleness Temperature: <= -76.1 °C
$ 2284/MT
- Density: 0.917 g/cc
- Thickness: 25.4 microns
- Melt Flow: 0.90 g/10 min
- Film Tensile Strength at Yield, MD: 9.10 MPa
- Film Tensile Strength at Yield, TD: 9.38 MPa
Delivery Film Exxon Chemical
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
lng ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.