$ 1858/MT
- Thickness: 50.8 microns
- Coating Weight: >= 44.6 g/m²
- Shrinkage, MD: 19 %
- Shrinkage, TD: 2.0 %
- Haze: 2.8 %
$ 1869/MT
- Water Vapor Transmission: 0.605 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 3.57 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 601 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 605 cc/m²/day @Temperature 23.0 °C
- Thickness: 40.6 microns
$ 2013/MT
- Water Vapor Transmission: 5.10 g/m²/day
- Thickness: 25.4 microns
- Coating Weight: 22.7 g/m²
- Coefficient of Friction: 0.20
- Film Tensile Strength at Break, MD: 145 MPa
$ 1762/MT
- Density: 0.900 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 58
- Tensile Strength, Yield: 17.0 MPa
- Elongation at Yield: 4.0 %
$ 1493/MT
- Thickness: 50.8 microns
- Coating Weight: 45.6 g/m²
- Film Elongation at Break, MD: 218 %
- Film Elongation at Break, TD: 55 %
- Film Tensile Strength at Break, MD: 103 MPa
$ 1607/MT
- Thickness: 17.8 microns
- Coating Weight: 15.7 g/m²
- Film Elongation at Break, MD: 162 %
- Film Elongation at Break, TD: 47 %
- Coefficient of Friction: 0.20
$ 1512/MT
- Water Vapor Transmission: 0.807 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 4.04 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 745 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 751 cc/m²/day @Temperature 23.0 °C
- Thickness: 43.2 microns
$ 1596/MT
- Water Vapor Transmission: 8.40 g/m²/day
- Thickness: 15.2 microns
- Coating Weight: 13.6 g/m²
- Coefficient of Friction: 0.20
- Film Tensile Strength at Break, MD: 124 MPa
$ 1626/MT
- Thickness: 27.9 microns
- Coating Weight: 17.3 g/m²
- Film Elongation at Break, MD: 110 %
- Film Elongation at Break, TD: 40 %
- Coefficient of Friction: 0.36
$ 1796/MT
- Thickness: 25.4 microns
- Coating Weight: 22.7 g/m²
- Film Elongation at Break, MD: 174 %
- Film Elongation at Break, TD: 45 %
- Coefficient of Friction: 0.19
$ 1747/MT
- Water Vapor Transmission: 3.70 g/m²/day
- Thickness: 35.6 microns
- Coating Weight: 31.4 g/m²
- Coefficient of Friction: 0.34
- Coefficient of Friction: 0.39
$ 1479/MT
- Water Vapor Transmission: 0.497 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 2.95 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 650 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 652 cc/m²/day @Temperature 23.0 °C
- Thickness: 50.8 microns
$ 2133/MT
- Density: 0.900 g/cc
- Melt Flow: 50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 21.0 MPa
- Elongation at Yield: 4.7 %
- Flexural Modulus, 1% Secant: 1080 MPa
$ 1487/MT
- Water Vapor Transmission: 1.10 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 4.97 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 20.0 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 20.2 cc/m²/day @Temperature 23.0 °C
- Thickness: 21.1 microns
$ 1539/MT
- Thickness: 66.0 microns
- Coating Weight: >= 46.1 g/m²
- Film Elongation at Break, MD: 180 %
- Film Elongation at Break, TD: 65 %
- Coefficient of Friction: 0.25
$ 1555/MT
- Water Vapor Transmission: 2.50 g/m²/day
- Oxygen Transmission Rate: 6.20 cc/m²/day
- Thickness: 27.9 microns
- Coating Weight: 25.1 g/m²
- Coefficient of Friction: 0.28
$ 2287/MT
- Thickness: 50.8 microns
- Coating Weight: >= 46.1 g/m²
- Film Elongation at Break, MD: 185 %
- Film Elongation at Break, TD: 60 %
- Film Tensile Strength at Break, MD: 114 MPa
$ 1560/MT
- Melt Flow: 45 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1635/MT
- Density: 0.900 g/cc
- Melt Flow: 53 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 74
- Tensile Strength, Yield: 35.0 MPa
- Elongation at Yield: 8.0 %
$ 1505/MT
- Density: 0.900 g/cc
- Melt Flow: 35 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 25.2 MPa
- Elongation at Yield: 4.7 %
- Flexural Modulus, 1% Secant: 1350 MPa
$ 1932/MT
- Density: 0.900 g/cc
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 25.7 MPa
- Tensile Strength, Yield: 27.1 MPa
- Elongation at Yield: 5.6 %
$ 1876/MT
- Thickness: 76.2 microns
- Coating Weight: >= 51.5 g/m²
- Film Elongation at Break, MD: 200 %
- Film Elongation at Break, TD: 53 %
- Film Tensile Strength at Break, MD: 85.033 MPa
$ 1982/MT
- Thickness: 91.4 microns
- Coating Weight: >= 46.1 g/m²
- Film Elongation at Break, MD: 86 %
- Film Elongation at Break, TD: 25 %
- Film Tensile Strength at Break, MD: 42.13 MPa
$ 2366/MT
- Water Vapor Transmission: 1.40 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 6.98 g/m²/day @Temperature 38.0 °C
- Thickness: 21.1 microns
- Coating Weight: 18.7 g/m²
- Film Elongation at Break, MD: 140 %
$ 1969/MT
- Water Vapor Transmission: 0.497 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 2.95 g/m²/day @Temperature 38.0 °C
- Thickness: 50.8 microns
- Coating Weight: 35.7 g/m²
- Film Elongation at Break, MD: 170 %
$ 1599/MT
- Density: 0.900 g/cc
- Melt Flow: 2.8 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 3.38 MPa
- Elongation at Yield: 10 %
- Flexural Modulus, 1% Secant: 1430 MPa
$ 1990/MT
- Water Vapor Transmission: 0.807 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 4.04 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 650 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 652 cc/m²/day @Temperature 23.0 °C
- Thickness: 35.6 microns
$ 2206/MT
- Water Vapor Transmission: 5.70 g/m²/day @Temperature 37.8 °C
- Oxygen Transmission Rate: 0.310 cc/m²/day @Temperature 22.8 °C
- Thickness: 21.3 microns
- Coating Weight: 19.4 g/m²
- Coefficient of Friction: 0.26
$ 2068/MT
- Water Vapor Transmission: 0.101 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 15.1 cc/m²/day @Temperature 23.0 °C
- Thickness: 15.0 microns
- Coating Weight: 13.4 g/m²
- Modulus of Elasticity: 2.50 GPa
$ 1844/MT
- Water Vapor Transmission: 4.80 g/m²/day
- Thickness: 43.2 microns
- Coating Weight: 24.8 g/m²
- Coefficient of Friction: 0.36
- Film Tensile Strength at Break, MD: 78.600 MPa
$ 2205/MT
- Thickness: 86.4 microns
- Coating Weight: >= 42.2 g/m²
- Film Elongation at Break, MD: 86 %
- Film Elongation at Break, TD: 25 %
- Film Tensile Strength at Break, MD: 44.62 MPa
$ 1550/MT
- Thickness: 30.5 microns
- Coating Weight: 27.7 g/m²
- Film Elongation at Break, MD: 200 %
- Film Elongation at Break, TD: 65 %
- Modulus of Elasticity: 2.20 GPa
$ 1643/MT
- Water Vapor Transmission: 1.10 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 4.97 g/m²/day @Temperature 38.0 °C
- Thickness: 35.6 microns
- Coating Weight: 25.0 g/m²
- Film Elongation at Break, MD: 190 %
$ 2347/MT
- Water Vapor Transmission: 3.10 g/m²/day
- Oxygen Transmission Rate: 6.20 cc/m²/day
- Thickness: 20.8 microns
- Coating Weight: 19.7 g/m²
- Coefficient of Friction: 0.29
$ 1846/MT
- Thickness: 76.2 microns
- Coating Weight: 52.8 g/m²
- Film Elongation at Break, MD: 190 %
- Film Elongation at Break, TD: 50 %
- Film Tensile Strength at Break, MD: 84.8 MPa
$ 2326/MT
- Water Vapor Transmission: 1.01 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 4.50 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 745 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 751 cc/m²/day @Temperature 23.0 °C
- Thickness: 30.5 microns
$ 1936/MT
- Thickness: 50.8 microns
- Coating Weight: 44.8 g/m²
- Film Elongation at Break, MD: 175 %
- Film Elongation at Break, TD: 65 %
- Modulus of Elasticity: 2.00 GPa
$ 1501/MT
- Water Vapor Transmission: 1.10 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 5.28 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 801 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 807 cc/m²/day @Temperature 23.0 °C
- Thickness: 40.6 microns
$ 1668/MT
- Water Vapor Transmission: 0.101 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 0.0931 cc/m²/day
- Thickness: 27.9 microns
- Coating Weight: 20.3 g/m²
- Film Tensile Strength at Break, MD: 82.7 MPa
$ 1504/MT
- Thickness: 35.6 microns
- Coating Weight: 31.2 g/m²
- Film Elongation at Break, MD: 175 %
- Film Elongation at Break, TD: 65 %
- Modulus of Elasticity: 2.00 GPa
$ 1926/MT
- Density: 0.970 g/cc
- Melt Flow: 28 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 50
- Tensile Strength, Yield: 20.0 MPa
- Flexural Modulus: 1.400 GPa
$ 2077/MT
- Density: 0.900 g/cc
- Melt Flow: 54 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 62
- Tensile Strength, Yield: 23.0 MPa
- Elongation at Yield: 4.0 %
$ 2256/MT
- Thickness: 96.5 microns
- Coating Weight: >= 64.6 g/m²
- Coefficient of Friction: 0.55
- Shrinkage, MD: 5.0 %
- Shrinkage, TD: 5.0 %
$ 1445/MT
- Density: 0.900 g/cc
- Melt Flow: 0.83 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 32.0 MPa
- Elongation at Yield: 13 %
- Flexural Modulus, 1% Secant: 1190 MPa
$ 1588/MT
- Water Vapor Transmission: 4.97 g/m²/day @Temperature 38.0 °C
- Thickness: 25.4 microns
- Coating Weight: 22.7 g/m²
- Coefficient of Friction: 0.25
- Coefficient of Friction: 0.52
$ 1681/MT
- Water Vapor Transmission: 10.9 g/m²/day
- Thickness: 12.7 microns
- Coating Weight: 11.4 g/m²
- Coefficient of Friction: 0.35
- Film Tensile Strength at Break, MD: 131 MPa
$ 1791/MT
- Melt Flow: 1550 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2173/MT
- Water Vapor Transmission: 1.10 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 4.97 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 2.95 cc/m²/day @Temperature 23.0 °C
- Thickness: 24.9 microns
- Coating Weight: 22.1 g/m²
$ 1630/MT
- Water Vapor Transmission: 7.30 g/m²/day
- Thickness: 20.3 microns
- Coating Weight: 18.2 g/m²
- Coefficient of Friction: 0.25
- Film Tensile Strength at Break, MD: 138 MPa
$ 1512/MT
- Density: 0.900 g/cc
- Melt Flow: 17 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 22.2 MPa
- Elongation at Yield: 4.6 %
- Flexural Modulus, 1% Secant: 1230 MPa
$ 1777/MT
- Water Vapor Transmission: 0.807 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 100 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 101 cc/m²/day @Temperature 23.0 °C
- Thickness: 20.1 microns
- Coating Weight: 17.9 g/m²
$ 1510/MT
- Water Vapor Transmission: 1.10 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 4.97 g/m²/day @Temperature 38.0 °C
- Thickness: 24.9 microns
- Coating Weight: 21.8 g/m²
- Film Elongation at Break, MD: 175 %
$ 2054/MT
- Thickness: 76.2 microns
- Coating Weight: 51.5 g/m²
- Film Elongation at Break, MD: 190 %
- Film Elongation at Break, TD: 50 %
- Film Tensile Strength at Break, MD: 89.6 MPa
$ 1456/MT
- Water Vapor Transmission: 5.00 g/m²/day
- Thickness: 30.5 microns
- Coating Weight: 27.0 g/m²
- Coefficient of Friction: 0.23
- Film Tensile Strength at Break, MD: 117 MPa
$ 1574/MT
- Density: 0.900 g/cc
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 22.2 MPa
- Elongation at Yield: 6.2 %
- Flexural Modulus, 1% Secant: 1030 MPa
$ 2052/MT
- Density: 0.900 g/cc
- Melt Flow: 75 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 61
- Tensile Strength, Yield: 23.0 MPa
- Elongation at Yield: 5.0 %
$ 1671/MT
- Water Vapor Transmission: 1.40 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 6.98 g/m²/day @Temperature 38.0 °C
- Thickness: 21.1 microns
- Coating Weight: 18.7 g/m²
- Film Elongation at Break, MD: 140 %
$ 1468/MT
- Thickness: 38.1 microns
- Coating Weight: 23.2 g/m²
- Film Elongation at Break, MD: 140 %
- Film Elongation at Break, TD: 50 %
- Modulus of Elasticity: 1.30 GPa
$ 1645/MT
- Thickness: 50.8 microns
- Coating Weight: 45.4 g/m²
- Film Elongation at Break, MD: 175 %
- Film Elongation at Break, TD: 65 %
- Modulus of Elasticity: 2.00 GPa
$ 1922/MT
- Thickness: 50.8 microns
- Coating Weight: 46.4 g/m²
- Film Elongation at Break, MD: 175 %
- Film Elongation at Break, TD: 65 %
- Modulus of Elasticity: 2.00 GPa
$ 1822/MT
- Water Vapor Transmission: 5.70 g/m²/day
- Thickness: 25.4 microns
- Coating Weight: 22.2 g/m²
- Coefficient of Friction: 0.24
- Film Tensile Strength at Break, MD: 137 MPa
$ 1520/MT
- Thickness: 91.4 microns
- Coating Weight: >= 43.7 g/m²
- Film Elongation at Break, MD: 86 %
- Film Elongation at Break, TD: 25 %
- Film Tensile Strength at Break, MD: 42.13 MPa
$ 1631/MT
- Density: 0.900 g/cc
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1576/MT
- Water Vapor Transmission: 0.497 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 2.95 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 20.0 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 20.2 cc/m²/day @Temperature 23.0 °C
- Thickness: 43.2 microns
$ 2210/MT
- Water Vapor Transmission: 4.30 g/m²/day
- Thickness: 30.5 microns
- Coating Weight: 27.4 g/m²
- Coefficient of Friction: 0.20
- Film Tensile Strength at Break, MD: 124 MPa
$ 1837/MT
- Water Vapor Transmission: 1.10 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 4.97 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 850 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 854 cc/m²/day @Temperature 23.0 °C
- Thickness: 24.9 microns
$ 2403/MT
- Density: 0.900 g/cc
- Melt Flow: 35 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 34.4 MPa
- Elongation at Yield: 3.9 %
- Flexural Modulus, 1% Secant: 1830 MPa
$ 1645/MT
- Density: 0.900 g/cc
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 23.9 MPa
- Elongation at Yield: 8.0 %
- Flexural Modulus: 1.08 GPa
$ 2527/MT
- Water Vapor Transmission: 5.90 g/m²/day
- Thickness: 33.0 microns
- Coating Weight: 20.0 g/m²
- Film Tensile Strength at Break, MD: 74.463 MPa
- Film Tensile Strength at Break, TD: 179.26 MPa
$ 1860/MT
- Water Vapor Transmission: 1.10 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 5.28 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 801 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 807 cc/m²/day @Temperature 23.0 °C
- Thickness: 40.6 microns
$ 1477/MT
- Thickness: 55.9 microns
- Coating Weight: 50.9 g/m²
- Film Elongation at Break, MD: 175 %
- Film Elongation at Break, TD: 65 %
- Modulus of Elasticity: 2.00 GPa
$ 1826/MT
- Water Vapor Transmission: 7.10 g/m²/day
- Thickness: 17.8 microns
- Coating Weight: 15.7 g/m²
- Coefficient of Friction: 0.40
- Coefficient of Friction: 0.40
$ 2196/MT
- Thickness: 17.8 microns
- Coating Weight: 15.7 g/m²
- Film Elongation at Break, MD: 165 %
- Film Elongation at Break, TD: 47 %
- Coefficient of Friction: 0.40
$ 1759/MT
- Water Vapor Transmission: 1.55 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 7.76 g/m²/day @Temperature 38.0 °C
- Thickness: 15.0 microns
- Coating Weight: 13.4 g/m²
- Film Elongation at Break, MD: 205 %
$ 1735/MT
- Water Vapor Transmission: 6.52 g/m²/day @Temperature 38.0 °C
- Thickness: 17.8 microns
- Coating Weight: 15.7 g/m²
- Coefficient of Friction: 0.20
- Film Tensile Strength at Break, MD: 138 MPa
$ 1549/MT
- Density: 0.900 g/cc
- Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 190 °C
- Melt Flow: 150 g/10 min @Load 2.16 kg, Temperature 190 °C
- Collected Volatile Condensable Material: <= 0.20 %
- Melting Point: 138 °C
$ 1604/MT
- Water Vapor Transmission: 4.00 g/m²/day
- Oxygen Transmission Rate: 14.0 cc/m²/day
- Thickness: 38.1 microns
- Coating Weight: 21.6 g/m²
- Coefficient of Friction: 0.53
$ 2367/MT
- Density: 0.900 g/cc
- Melt Flow: 24 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 17.2 MPa
- Tensile Strength, Yield: 32.8 MPa
- Elongation at Break: 51 %
$ 1458/MT
- Water Vapor Transmission: 0.497 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 2.95 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 20.0 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 20.2 cc/m²/day @Temperature 23.0 °C
- Thickness: 43.2 microns
$ 1488/MT
- Density: 0.900 g/cc
- Melt Flow: 30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 22.4 MPa
- Elongation at Yield: 5.0 %
- Flexural Modulus, 1% Secant: 1100 MPa
$ 2094/MT
- Thickness: 61.0 microns
- Coating Weight: 45.9 g/m²
- Film Elongation at Break, MD: 170 %
- Film Elongation at Break, TD: 55 %
- Modulus of Elasticity: 1.60 GPa
$ 1588/MT
- Density: 0.900 g/cc
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Modulus: 1.50 GPa
- Charpy Impact, Notched: 0.294 J/cm²
- Deflection Temperature at 1.8 MPa (264 psi): 53.9 °C
$ 1591/MT
- Thickness: 19.0 microns
- Coating Weight: 17.0 g/m²
- Film Elongation at Break, MD: 150 %
- Film Elongation at Break, TD: 50 %
- Coefficient of Friction: 0.20
$ 1576/MT
- Thickness: 30.5 microns
- Coating Weight: >= 27.2 g/m²
- Shrinkage, MD: 26 %
- Shrinkage, TD: 0.00 %
- Haze: 2.0 %
$ 1685/MT
- Water Vapor Transmission: 5.10 g/m²/day
- Oxygen Transmission Rate: 70.0 cc/m²/day
- Thickness: 27.9 microns
- Coating Weight: 25.9 g/m²
- Coefficient of Friction: 0.23
$ 1815/MT
- Thickness: 50.8 microns
- Coating Weight: 45.4 g/m²
- Film Elongation at Break, MD: 175 %
- Film Elongation at Break, TD: 50 %
- Modulus of Elasticity: 2.10 GPa
$ 1456/MT
- Water Vapor Transmission: 1.01 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 4.50 g/m²/day @Temperature 38.0 °C
- Thickness: 35.6 microns
- Coating Weight: 27.4 g/m²
- Film Elongation at Break, MD: 160 %
$ 2432/MT
- Water Vapor Transmission: 6.70 g/m²/day
- Thickness: 21.6 microns
- Coating Weight: 19.5 g/m²
- Coefficient of Friction: 0.24
- Film Tensile Strength at Break, MD: 138 MPa
$ 2278/MT
- Thickness: 40.6 microns
- Coating Weight: 28.5 g/m²
- Film Elongation at Break, MD: 170 %
- Film Elongation at Break, TD: 55 %
- Modulus of Elasticity: 1.70 GPa
$ 2538/MT
- Density: 0.900 g/cc
- Melt Flow: 32 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 31.7 MPa
- Elongation at Yield: 9.0 %
- Flexural Modulus: 1.24 GPa
$ 2553/MT
- Thickness: 27.9 microns
- Coating Weight: 17.3 g/m²
- Film Elongation at Break, MD: 97 %
- Film Elongation at Break, TD: 35 %
- Coefficient of Friction: 0.36
$ 1587/MT
- Density: 0.900 g/cc
- Melt Flow: 16 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 71
- Tensile Strength, Yield: 32.0 MPa
- Elongation at Yield: 7.0 %
$ 1504/MT
- Thickness: 66.0 microns
- Coating Weight: >= 47.7 g/m²
- Film Elongation at Break, MD: 200 %
- Film Elongation at Break, TD: 50 %
- Film Tensile Strength at Break, MD: 84.861 MPa
$ 1583/MT
- Thickness: 66.0 microns
- Coating Weight: 48.0 g/m²
- Film Elongation at Break, MD: 170 %
- Film Elongation at Break, TD: 55 %
- Film Tensile Strength at Break, MD: 105 MPa
$ 1510/MT
- Water Vapor Transmission: 1.10 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 4.97 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 850 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 854 cc/m²/day @Temperature 23.0 °C
- Thickness: 25.4 microns
$ 1864/MT
- Density: 0.900 g/cc
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 28.2 MPa
- Tensile Strength, Yield: 28.8 MPa
- Elongation at Yield: 5.0 %
$ 1448/MT
- Density: 0.900 g/cc
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 71
- Tensile Strength, Yield: 33.0 MPa
- Elongation at Yield: 8.0 %
$ 1781/MT
- Thickness: 17.8 microns
- Coating Weight: >= 15.7 g/m²
- Film Elongation at Break, MD: 200 %
- Film Elongation at Break, TD: 60 %
- Film Tensile Strength at Break, MD: 118.20 MPa
$ 2343/MT
- Water Vapor Transmission: 0.900 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 2.95 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 20.0 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 20.2 cc/m²/day @Temperature 23.0 °C
- Thickness: 25.4 microns
$ 2560/MT
- Density: 0.900 g/cc
- Melt Flow: 14 g/10 min
- Tensile Modulus: 1.10 GPa
- Charpy Impact, Notched: 0.294 J/cm² @Temperature -20.0 °C
- Charpy Impact, Notched: 0.399 J/cm² @Temperature 0.000 °C
$ 2435/MT
- Water Vapor Transmission: 0.807 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 4.04 g/m²/day @Temperature 38.0 °C
- Thickness: 40.6 microns
- Coating Weight: 31.4 g/m²
- Film Elongation at Break, MD: 160 %
$ 1988/MT
- Thickness: 12.7 microns
- Coating Weight: 11.4 g/m²
- Film Elongation at Break, MD: 160 %
- Film Elongation at Break, TD: 45 %
- Coefficient of Friction: 0.32
$ 1446/MT
- Water Vapor Transmission: 0.900 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 4.19 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 745 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 751 cc/m²/day @Temperature 23.0 °C
- Thickness: 33.0 microns
$ 1934/MT
- Density: 0.900 g/cc
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 70
- Tensile Strength, Yield: 33.0 MPa
- Elongation at Yield: 9.0 %
$ 1450/MT
- Density: 0.900 g/cc
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 35.3 MPa
- Flexural Modulus, 1% Secant: 1530 MPa
- Flexural Modulus, 1% Secant: 1740 MPa
$ 1693/MT
- Density: 0.900 g/cc
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 35.3 MPa
- Flexural Modulus, 1% Secant: 1530 MPa
- Flexural Modulus, 1% Secant: 1740 MPa
$ 1451/MT
- Density: 0.900 g/cc
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 35.3 MPa
- Flexural Modulus, 1% Secant: 1530 MPa
- Flexural Modulus, 1% Secant: 1740 MPa
$ 1820/MT
- Density: 0.910 g/cc
- Thickness: 50.8 microns
- Coating Weight: 44.8 g/m²
- Coefficient of Friction: 0.37
- Shrinkage, MD: 4.0 % @Temperature 80.0 °C
$ 2346/MT
- Water Vapor Transmission: 1.40 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 6.98 g/m²/day @Temperature 38.0 °C
- Thickness: 15.0 microns
- Coating Weight: 13.4 g/m²
- Film Elongation at Break, MD: 160 %
$ 1817/MT
- Thickness: 38.1 microns
- Coating Weight: 35.7 g/m²
- Haze: 2.5 %
- Yield: 19400 in/lb
$ 1482/MT
- Thickness: 38.1 microns
- Coating Weight: 20.2 g/m²
- Film Elongation at Break, MD: 110 %
- Film Elongation at Break, TD: 40 %
- Modulus of Elasticity: 1.20 GPa
$ 1960/MT
- Water Vapor Transmission: 0.101 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 0.101 g/m²/day @Temperature 25.0 °C
- Water Vapor Transmission: 0.202 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 26.1 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 26.4 cc/m²/day @Temperature 23.0 °C
$ 1912/MT
- Density: 0.900 g/cc
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 38.4 MPa
- Elongation at Yield: 6.5 %
- Flexural Modulus, 1% Secant: 1740 MPa
$ 1957/MT
- Water Vapor Transmission: 1.40 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 6.98 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 1000 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 1010 cc/m²/day @Temperature 23.0 °C
- Thickness: 30.5 microns
$ 1605/MT
- Water Vapor Transmission: 4.19 g/m²/day @Temperature 38.0 °C
- Thickness: 35.6 microns
- Coating Weight: 28.2 g/m²
- Coefficient of Friction: 0.39
- Film Tensile Strength at Break, MD: 98.6 MPa
$ 2190/MT
- Water Vapor Transmission: 5.43 g/m²/day @Temperature 38.0 °C
- Thickness: 30.5 microns
- Coating Weight: 20.0 g/m²
- Film Tensile Strength at Break, MD: 84.8 MPa
- Film Tensile Strength at Break, TD: 179 MPa
$ 1689/MT
- Water Vapor Transmission: 1.40 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 6.98 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 1000 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 1010 cc/m²/day @Temperature 23.0 °C
- Thickness: 20.1 microns
$ 1595/MT
- Density: 0.900 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 24.8 MPa
- Elongation at Yield: 6.4 %
- Flexural Modulus: 1.12 GPa
$ 2108/MT
- Water Vapor Transmission: 4.20 g/m²/day
- Thickness: 33.0 microns
- Coating Weight: 28.2 g/m²
- Coefficient of Friction: 0.34
- Coefficient of Friction: 0.39
$ 1534/MT
- Water Vapor Transmission: 4.04 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 0.698 cc/m²/day @Temperature 23.0 °C
- Thickness: 21.1 microns
- Coating Weight: 18.4 g/m²
- Film Elongation at Break, MD: 140 %
$ 1697/MT
- Density: 0.900 g/cc
- Melt Flow: 32 g/10 min @Load 2.16 kg, Temperature 230 °C
- Elongation at Break: 118 %
- Tenacity: 0.344 N/tex
- Molecular Weight Distribution, Mw/Mn: 1.9
$ 1664/MT
- Water Vapor Transmission: 5.70 g/m²/day
- Thickness: 25.4 microns
- Coating Weight: 22.2 g/m²
- Coefficient of Friction: 0.24
- Film Tensile Strength at Break, MD: 137 MPa
$ 1741/MT
- Thickness: 50.8 microns
- Coating Weight: 37.3 g/m²
- Film Elongation at Break, MD: 170 %
- Modulus of Elasticity: 1.70 GPa
- Film Tensile Strength at Break, MD: 105 MPa
$ 1800/MT
- Density: 0.900 g/cc
- Melt Flow: 16 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 71
- Tensile Strength, Yield: 32.0 MPa
- Elongation at Yield: 7.0 %
$ 1561/MT
- Water Vapor Transmission: 1.01 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 4.50 g/m²/day @Temperature 38.0 °C
- Thickness: 30.5 microns
- Coating Weight: 26.9 g/m²
- Film Elongation at Break, MD: 205 %
$ 2411/MT
- Water Vapor Transmission: 0.807 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 4.04 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 745 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 751 cc/m²/day @Temperature 23.0 °C
- Thickness: 43.2 microns
$ 1984/MT
- Water Vapor Transmission: 2.02 g/m²/day @Temperature 38.0 °C
- Thickness: 38.1 microns
- Coating Weight: 23.2 g/m²
- Film Elongation at Break, MD: 140 %
- Film Elongation at Break, TD: 50 %
$ 1915/MT
- Density: 0.900 g/cc
- Melt Flow: 16 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 64
- Tensile Strength, Yield: 25.0 MPa
- Elongation at Yield: 4.0 %
$ 2049/MT
- Density: 0.900 g/cc
- Melt Flow: 35 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 22.8 MPa
- Elongation at Yield: 7.6 %
- Flexural Modulus: 1.01 GPa
$ 2453/MT
- Oxygen Transmission Rate: 650 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 652 cc/m²/day @Temperature 23.0 °C
- Thickness: 50.8 microns
- Coating Weight: 37.6 g/m²
- Film Elongation at Break, MD: 170 %
$ 1515/MT
- Water Vapor Transmission: 3.60 g/m²/day
- Oxygen Transmission Rate: 70.0 cc/m²/day
- Thickness: 38.1 microns
- Coating Weight: 35.5 g/m²
- Coefficient of Friction: 0.23
$ 1559/MT
- Water Vapor Transmission: 5.00 g/m²/day
- Thickness: 30.5 microns
- Coating Weight: 26.6 g/m²
- Coefficient of Friction: 0.25
- Coefficient of Friction: 0.52
$ 1501/MT
- Water Vapor Transmission: 5.70 g/m²/day
- Thickness: 25.4 microns
- Coating Weight: 22.6 g/m²
- Coefficient of Friction: 0.23
- Film Tensile Strength at Break, MD: 138 MPa
$ 1626/MT
- Density: 0.900 g/cc
- Melt Flow: 30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 21.0 MPa
- Elongation at Yield: 3.9 %
- Flexural Modulus, 1% Secant: 1190 MPa
$ 2247/MT
- Thickness: 61.0 microns
- Coating Weight: 48.5 g/m²
- Film Elongation at Break, MD: 170 %
- Film Elongation at Break, TD: 55 %
- Modulus of Elasticity: 1.60 GPa
$ 1591/MT
- Water Vapor Transmission: 6.70 g/m²/day
- Thickness: 19.0 microns
- Coating Weight: 17.0 g/m²
- Coefficient of Friction: 0.20
- Film Tensile Strength at Break, MD: 124 MPa
$ 1959/MT
- Density: 0.900 g/cc
- Melt Flow: 2.7 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 34.7 MPa
- Elongation at Yield: 10 %
- Flexural Modulus, 1% Secant: 1460 MPa
$ 1686/MT
- Thickness: 33.0 microns
- Coating Weight: 20.2 g/m²
- Film Elongation at Break, MD: 140 %
- Film Elongation at Break, TD: 50 %
- Modulus of Elasticity: 1.30 GPa
$ 2010/MT
- Water Vapor Transmission: 0.190 g/m²/day
- Oxygen Transmission Rate: 26.0 cc/m²/day
- Thickness: 17.8 microns
- Coating Weight: 15.7 g/m²
- Film Tensile Strength at Break, MD: 152 MPa
$ 2058/MT
- Density: 0.900 g/cc
- Melt Flow: 10 g/10 min
- Tensile Modulus: 1.50 GPa
- Charpy Impact, Notched: 0.199 J/cm²
- Deflection Temperature at 1.8 MPa (264 psi): 53.9 °C
$ 1493/MT
- Water Vapor Transmission: 0.295 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 49.7 cc/m²/day @Temperature 23.0 °C
- Thickness: 18.0 microns
- Coating Weight: 16.2 g/m²
- Film Elongation at Break, MD: 175 %
$ 1689/MT
- Thickness: 66.0 microns
- Coating Weight: 46.1 g/m²
- Film Elongation at Break, MD: 185 %
- Film Elongation at Break, TD: 50 %
- Film Tensile Strength at Break, MD: 90.3 MPa
$ 1481/MT
- Water Vapor Transmission: 0.404 g/m²/day @Temperature 38.0 °C
- Water Vapor Transmission: 0.807 g/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 698 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 702 cc/m²/day @Temperature 23.0 °C
- Thickness: 45.7 microns
$ 2099/MT
- Thickness: 50.8 microns
- Coating Weight: >= 44.6 g/m²
- Film Elongation at Break, MD: 185 %
- Film Elongation at Break, TD: 60 %
- Film Tensile Strength at Break, MD: 114 MPa
$ 1965/MT
- Thickness: 27.9 microns
- Coating Weight: 25.9 g/m²
- Film Elongation at Break, MD: 175 %
- Film Elongation at Break, TD: 60 %
- Modulus of Elasticity: 2.00 GPa
$ 1843/MT
- Water Vapor Transmission: 1.40 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 6.98 g/m²/day @Temperature 38.0 °C
- Thickness: 20.1 microns
- Coating Weight: 17.9 g/m²
- Film Elongation at Break, MD: 175 %
$ 1585/MT
- Water Vapor Transmission: 6.36 g/m²/day @Temperature 38.0 °C
- Thickness: 17.8 microns
- Coating Weight: 15.7 g/m²
- Coefficient of Friction: 0.24
- Film Tensile Strength at Break, MD: 124 MPa
$ 1583/MT
- Density: 0.900 g/cc
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 21.0 MPa
- Elongation at Yield: 5.1 %
- Flexural Modulus, 1% Secant: 1100 MPa
$ 1614/MT
- Water Vapor Transmission: 6.70 g/m²/day
- Thickness: 19.0 microns
- Coating Weight: 17.0 g/m²
- Coefficient of Friction: 0.20
- Film Tensile Strength at Break, MD: 124 MPa
$ 2026/MT
- Density: 0.900 g/cc
- Melt Flow: 36 g/10 min @Load 2.16 kg, Temperature 230 °C
- Molecular Weight Distribution, Mw/Mn: 2.8
$ 1457/MT
- Water Vapor Transmission: 0.390 g/m²/day
- Thickness: 12.7 microns
- Coating Weight: 11.4 g/m²
- Film Tensile Strength at Break, MD: 131 MPa
- Film Tensile Strength at Break, TD: 262 MPa
$ 1807/MT
- Water Vapor Transmission: 1.10 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 5.28 g/m²/day @Temperature 38.0 °C
- Thickness: 38.1 microns
- Coating Weight: 23.2 g/m²
- Film Elongation at Break, MD: 140 %
$ 1708/MT
- Water Vapor Transmission: 0.295 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 0.0931 cc/m²/day
- Thickness: 35.6 microns
- Coating Weight: 24.8 g/m²
- Film Tensile Strength at Break, MD: 75.2 MPa
$ 1756/MT
- Thickness: 38.1 microns
- Coating Weight: 23.2 g/m²
- Film Elongation at Break, MD: 140 %
- Film Elongation at Break, TD: 50 %
- Modulus of Elasticity: 1.30 GPa
$ 2055/MT
- Thickness: 12.7 microns
- Coating Weight: >= 11.4 g/m²
- Film Elongation at Break, MD: 160 %
- Film Elongation at Break, TD: 45 %
- Coefficient of Friction: 0.32
$ 2232/MT
- Water Vapor Transmission: 4.20 g/m²/day
- Thickness: 43.2 microns
- Coating Weight: 28.2 g/m²
- Film Tensile Strength at Break, MD: 88.942 MPa
- Film Tensile Strength at Break, TD: 162.03 MPa
$ 2318/MT
- Thickness: 40.6 microns
- Coating Weight: 36.6 g/m²
- Film Elongation at Break, MD: 175 %
- Film Elongation at Break, TD: 65 %
- Modulus of Elasticity: 2.00 GPa
$ 2453/MT
- Water Vapor Transmission: 0.807 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 2.95 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 20.0 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 20.2 cc/m²/day @Temperature 23.0 °C
- Thickness: 33.0 microns
$ 1486/MT
- Water Vapor Transmission: 1.01 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 4.50 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 745 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 751 cc/m²/day @Temperature 23.0 °C
- Thickness: 30.5 microns
$ 1871/MT
- Thickness: 25.4 microns
- Coating Weight: 22.7 g/m²
- Film Elongation at Break, MD: 147 %
- Film Elongation at Break, TD: 45 %
- Coefficient of Friction: 0.19
$ 1949/MT
- Water Vapor Transmission: 7.92 g/m²/day @Temperature 38.0 °C
- Thickness: 17.8 microns
- Coating Weight: 15.7 g/m²
- Coefficient of Friction: 0.35
- Film Tensile Strength at Break, MD: 110 MPa
$ 1888/MT
- Water Vapor Transmission: 1.10 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 4.97 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 850 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 854 cc/m²/day @Temperature 23.0 °C
- Thickness: 24.9 microns
$ 1600/MT
- Water Vapor Transmission: 0.605 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 3.41 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 20.0 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 20.2 cc/m²/day @Temperature 23.0 °C
- Thickness: 50.8 microns
$ 1778/MT
- Water Vapor Transmission: 7.60 g/m²/day
- Thickness: 17.8 microns
- Coating Weight: 16.5 g/m²
- Coefficient of Friction: 0.22
- Film Tensile Strength at Break, MD: 138 MPa
$ 1529/MT
- Thickness: 15.2 microns
- Coating Weight: 13.6 g/m²
- Film Elongation at Break, MD: 153 %
- Film Elongation at Break, TD: 46 %
- Coefficient of Friction: 0.21
$ 1668/MT
- Melt Flow: 45 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2116/MT
- Thickness: 19.0 microns
- Coating Weight: 17.0 g/m²
- Film Elongation at Break, MD: 150 %
- Film Elongation at Break, TD: 50 %
- Coefficient of Friction: 0.20
$ 2373/MT
- Water Vapor Transmission: 1.01 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 4.50 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 751 cc/m²/day @Temperature 23.0 °C
- Thickness: 30.5 microns
- Coating Weight: 27.7 g/m²
$ 1580/MT
- Water Vapor Transmission: 0.497 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 2.95 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 650 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 652 cc/m²/day @Temperature 23.0 °C
- Thickness: 50.8 microns
$ 2142/MT
- Density: 0.900 g/cc
- Melt Flow: 7.3 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 25.6 MPa
- Elongation at Yield: 13 %
- Flexural Modulus, 1% Secant: 896 MPa
$ 2303/MT
- Density: 0.900 g/cc
- Melt Flow: 4.2 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2282/MT
- Density: 0.900 g/cc
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 35.1 MPa
- Elongation at Yield: 9.8 %
- Flexural Modulus, 1% Secant: 1480 MPa
$ 1945/MT
- Thickness: 66.0 microns
- Coating Weight: >= 46.1 g/m²
- Film Elongation at Break, MD: 200 %
- Film Elongation at Break, TD: 50 %
- Film Tensile Strength at Break, MD: 90.163 MPa
$ 1502/MT
- Density: 0.900 g/cc
- Melt Flow: 2.8 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 36.8 MPa
- Elongation at Yield: 9.0 %
- Flexural Modulus, 1% Secant: 1710 MPa
$ 1483/MT
- Thickness: 38.1 microns
- Coating Weight: 23.2 g/m²
- Film Elongation at Break, MD: 140 %
- Film Elongation at Break, TD: 50 %
- Modulus of Elasticity: 1.30 GPa
$ 1508/MT
- Thickness: 35.6 microns
- Coating Weight: 25.0 g/m²
- Film Elongation at Break, MD: 190 %
- Film Elongation at Break, TD: 55 %
- Modulus of Elasticity: 1.70 GPa
$ 1617/MT
- Water Vapor Transmission: 1.01 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 4.50 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 745 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 751 cc/m²/day @Temperature 23.0 °C
- Thickness: 30.5 microns
$ 1934/MT
- Density: 0.900 g/cc
- Melt Flow: 35 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 22.3 MPa
- Elongation at Yield: 5.8 %
- Flexural Modulus: 1.05 GPa
$ 1818/MT
- Thickness: 17.0 microns
- Coating Weight: 15.2 g/m²
- Film Elongation at Break, MD: 205 %
- Film Elongation at Break, TD: 55 %
- Modulus of Elasticity: 2.00 GPa
$ 1576/MT
- Water Vapor Transmission: 1.10 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 4.81 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 20.0 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 20.2 cc/m²/day @Temperature 23.0 °C
- Thickness: 35.6 microns
$ 1761/MT
- Density: 0.900 g/cc
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1625/MT
- Density: 1.05 g/cc
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 36.8 MPa
- Elongation at Yield: 5.8 %
- Flexural Modulus: 0.239 GPa
$ 1529/MT
- Water Vapor Transmission: 1.10 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 4.97 g/m²/day @Temperature 38.0 °C
- Thickness: 24.9 microns
- Coating Weight: 22.4 g/m²
- Film Elongation at Break, MD: 205 %
$ 1653/MT
- Water Vapor Transmission: 1.40 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 6.98 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 1000 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 1010 cc/m²/day @Temperature 23.0 °C
- Thickness: 20.1 microns
$ 1978/MT
- Water Vapor Transmission: 8.20 g/m²/day
- Thickness: 19.0 microns
- Coating Weight: 17.3 g/m²
- Coefficient of Friction: 0.23
- Film Tensile Strength at Break, MD: 124 MPa
$ 1548/MT
- Water Vapor Transmission: 0.807 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 3.88 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 20.0 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 20.2 cc/m²/day @Temperature 23.0 °C
- Thickness: 33.0 microns
$ 1920/MT
- Density: 0.900 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 4.0 g/10 min @Load 5.00 kg, Temperature 230 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 26.0 MPa
$ 2112/MT
- Thickness: 48.3 microns
- Coating Weight: 28.5 g/m²
- Film Elongation at Break, MD: 140 %
- Film Elongation at Break, TD: 50 %
- Modulus of Elasticity: 1.30 GPa
$ 2015/MT
- Thickness: 17.8 microns
- Coating Weight: 15.7 g/m²
- Film Elongation at Break, MD: 162 %
- Film Elongation at Break, TD: 47 %
- Coefficient of Friction: 0.20
$ 2016/MT
- Water Vapor Transmission: 4.19 g/m²/day @Temperature 38.0 °C
- Thickness: 35.6 microns
- Coating Weight: 28.2 g/m²
- Coefficient of Friction: 0.39
- Gloss: 70 %
$ 1553/MT
- Water Vapor Transmission: 0.190 g/m²/day
- Thickness: 17.8 microns
- Coating Weight: 15.7 g/m²
- Film Tensile Strength at Break, MD: 152 MPa
- Film Tensile Strength at Break, TD: 234 MPa
$ 2093/MT
- Water Vapor Transmission: 5.10 g/m²/day
- Thickness: 25.4 microns
- Coating Weight: 22.7 g/m²
- Coefficient of Friction: 0.20
- Film Tensile Strength at Break, MD: 124 MPa
$ 1847/MT
- Water Vapor Transmission: 0.807 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 0.900 g/m²/day @Temperature 25.0 °C
- Water Vapor Transmission: 4.04 g/m²/day @Temperature 38.0 °C
- Thickness: 48.3 microns
- Coating Weight: 28.5 g/m²
$ 1588/MT
- Density: 0.900 g/cc
- Melt Flow: 100 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 33.0 MPa
- Elongation at Yield: 4.4 %
- Flexural Modulus, 1% Secant: 1750 MPa
$ 1851/MT
- Water Vapor Transmission: 1.30 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 6.05 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 900 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 902 cc/m²/day @Temperature 23.0 °C
- Thickness: 35.6 microns
$ 1668/MT
- Thickness: 38.1 microns
- Coating Weight: 23.2 g/m²
- Film Elongation at Break, MD: 140 %
- Film Elongation at Break, TD: 50 %
- Modulus of Elasticity: 1.30 GPa
$ 1623/MT
- Density: 0.900 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 58
- Tensile Strength, Yield: 24.0 MPa
- Elongation at Yield: 5.0 %
$ 1588/MT
- Water Vapor Transmission: 0.101 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 0.101 cc/m²/day @Temperature 23.0 °C
- Thickness: 35.6 microns
- Coating Weight: 24.8 g/m²
- Film Elongation at Break, MD: 170 %
$ 1498/MT
- Density: 0.900 g/cc
- Melt Flow: 7.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 33.0 MPa
- Elongation at Yield: 8.0 %
$ 2052/MT
- Water Vapor Transmission: 1.10 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 4.97 g/m²/day @Temperature 38.0 °C
- Thickness: 30.5 microns
- Coating Weight: 23.5 g/m²
- Film Elongation at Break, MD: 160 %
$ 1595/MT
- Water Vapor Transmission: 0.404 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 2.48 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 543 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 551 cc/m²/day @Temperature 23.0 °C
- Thickness: 50.8 microns
$ 1690/MT
- Water Vapor Transmission: 1.10 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 5.28 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 20.0 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 20.2 cc/m²/day @Temperature 23.0 °C
- Thickness: 30.5 microns
$ 1457/MT
- Water Vapor Transmission: 4.20 g/m²/day
- Oxygen Transmission Rate: 15.0 cc/m²/day
- Thickness: 17.8 microns
- Coating Weight: 16.8 g/m²
- Film Tensile Strength at Break, MD: 121 MPa
$ 1935/MT
- Thickness: 35.6 microns
- Coating Weight: 31.4 g/m²
- Film Elongation at Break, MD: 205 %
- Film Elongation at Break, TD: 55 %
- Modulus of Elasticity: 2.00 GPa
$ 2183/MT
- Density: 1.07 g/cc
- Melt Flow: 18 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 84
- Tensile Strength, Yield: 24.0 MPa
- Flexural Modulus: 2.400 GPa
$ 1742/MT
- Density: 0.900 g/cc
- Melt Flow: 19 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 24.7 MPa
- Elongation at Yield: 5.6 %
- Flexural Modulus: 1.27 GPa
$ 2302/MT
- Density: 0.900 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 33.0 MPa
- Elongation at Yield: 8.0 %
$ 2507/MT
- Water Vapor Transmission: 1.01 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 4.50 g/m²/day @Temperature 38.0 °C
- Thickness: 27.9 microns
- Coating Weight: 25.9 g/m²
- Film Elongation at Break, MD: 175 %
$ 1818/MT
- Water Vapor Transmission: 4.00 g/m²/day
- Thickness: 30.5 microns
- Coating Weight: >= 27.2 g/m²
- Coefficient of Friction: 0.24
- Film Tensile Strength at Break, MD: 138 MPa
$ 1497/MT
- Water Vapor Transmission: 8.38 g/m²/day @Temperature 38.0 °C
- Thickness: 15.2 microns
- Coating Weight: 13.6 g/m²
- Coefficient of Friction: 0.20
- Film Tensile Strength at Break, MD: 124 MPa
$ 1741/MT
- Thickness: 76.2 microns
- Coating Weight: >= 51.5 g/m²
- Film Elongation at Break, MD: 165 %
- Film Elongation at Break, TD: 40 %
- Film Tensile Strength at Break, MD: 73.546 MPa
$ 1734/MT
- Water Vapor Transmission: 0.497 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 49.7 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 50.1 cc/m²/day @Temperature 23.0 °C
- Thickness: 18.0 microns
- Coating Weight: 16.2 g/m²
$ 1489/MT
- Thickness: 33.0 microns
- Coating Weight: 20.2 g/m²
- Film Elongation at Break, MD: 140 %
- Film Elongation at Break, TD: 50 %
- Modulus of Elasticity: 1.30 GPa
$ 1487/MT
- Water Vapor Transmission: 0.202 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 0.202 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 26.1 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 26.4 cc/m²/day @Temperature 23.0 °C
- Thickness: 18.0 microns
$ 1906/MT
- Density: 0.900 g/cc
- Melt Flow: 30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 25.1 MPa
- Tensile Strength, Yield: 26.6 MPa
- Elongation at Yield: 4.9 %
$ 1632/MT
- Thickness: 50.8 microns
- Coating Weight: 44.8 g/m²
- Coefficient of Friction: 0.35
- Shrinkage, MD: 19 % @Temperature 135 °C
- Shrinkage, TD: 2.0 % @Temperature 135 °C
$ 1452/MT
- Water Vapor Transmission: 1.30 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 6.05 g/m²/day @Temperature 38.0 °C
- Thickness: 33.0 microns
- Coating Weight: 20.2 g/m²
- Film Elongation at Break, MD: 140 %
$ 2364/MT
- Water Vapor Transmission: 2.50 g/m²/day
- Oxygen Transmission Rate: 4.70 cc/m²/day
- Thickness: 17.8 microns
- Coating Weight: 17.4 g/m²
- Film Tensile Strength at Break, MD: 114 MPa
$ 2085/MT
- Density: 0.890 g/cc
- Melt Flow: 22 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 58
- Tensile Strength, Yield: >= 15.00 MPa
- Flexural Modulus: >= 0.5000 GPa
$ 1589/MT
- Water Vapor Transmission: 0.900 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 4.19 g/m²/day @Temperature 38.0 °C
- Thickness: 40.6 microns
- Coating Weight: 28.5 g/m²
- Film Elongation at Break, MD: 170 %
$ 2277/MT
- Thickness: 30.5 microns
- Coating Weight: 27.4 g/m²
- Film Elongation at Break, MD: 183 %
- Film Elongation at Break, TD: 46 %
- Coefficient of Friction: 0.18
$ 1503/MT
- Water Vapor Transmission: 0.202 g/m²/day @Temperature 38.0 °C
- Thickness: 18.0 microns
- Coating Weight: 16.2 g/m²
- Film Elongation at Break, MD: 175 %
- Film Elongation at Break, TD: 60 %
$ 1697/MT
- Density: 0.900 g/cc
- Melt Flow: 17 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 62
- Tensile Strength, Yield: 23.0 MPa
- Elongation at Yield: 4.0 %
$ 2146/MT
- Density: 0.900 g/cc
- Melt Flow: 110 g/10 min @Load 1.20 kg, Temperature 190 °C
- Melt Flow: 430 g/10 min @Load 2.16 kg, Temperature 190 °C
- Collected Volatile Condensable Material: <= 0.30 %
- Melting Point: 162 °C
$ 1514/MT
- Water Vapor Transmission: 1.40 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 6.98 g/m²/day @Temperature 38.0 °C
- Thickness: 20.1 microns
- Coating Weight: 17.9 g/m²
- Film Elongation at Break, MD: 205 %
$ 2467/MT
- Water Vapor Transmission: 2.95 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 49.7 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 50.1 cc/m²/day @Temperature 23.0 °C
- Thickness: 15.0 microns
- Coating Weight: 13.4 g/m²
$ 1535/MT
- Density: 0.900 g/cc
- Melt Flow: 2.1 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 37.4 MPa
- Flexural Modulus, 1% Secant: 1770 MPa
- Izod Impact, Notched: 0.534 J/cm
- Deflection Temperature at 0.46 MPa (66 psi): 112 °C
$ 1619/MT
- Oxygen Transmission Rate: 0.636 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 2.48 cc/m²/day @Temperature 23.0 °C
- Thickness: 61.0 microns
- Coating Weight: 42.9 g/m²
- Film Elongation at Break, MD: 170 %
$ 1850/MT
- Thickness: 17.8 microns
- Coating Weight: 15.7 g/m²
- Film Elongation at Break, MD: 160 %
- Film Elongation at Break, TD: 50 %
- Coefficient of Friction: 0.55
$ 1484/MT
- Thickness: 12.7 microns
- Coating Weight: >= 11.4 g/m²
- Film Elongation at Break, MD: 160 %
- Film Elongation at Break, TD: 45 %
- Film Tensile Strength at Break, MD: 138 MPa
$ 1503/MT
- Density: 0.900 g/cc
- Melt Flow: 35 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 35.4 MPa
- Elongation at Yield: 23 %
- Flexural Modulus: 1.47 GPa
$ 2022/MT
- Density: 0.900 g/cc
- Melt Flow: 2.1 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 28.5 MPa
- Elongation at Yield: 13 %
- Flexural Modulus, 1% Secant: 972 MPa
$ 1746/MT
- Water Vapor Transmission: 0.310 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 0.0931 cc/m²/day @Temperature 23.0 °C
- Thickness: 27.9 microns
- Coating Weight: 20.3 g/m²
- Film Tensile Strength at Break, MD: 90.3 MPa
$ 1950/MT
- Water Vapor Transmission: 0.0931 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 0.101 cc/m²/day @Temperature 23.0 °C
- Thickness: 18.0 microns
- Coating Weight: 16.2 g/m²
- Film Tensile Strength at Break, MD: 124 MPa
$ 1630/MT
- Density: 0.900 g/cc
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 28.5 MPa
- Elongation at Yield: 13 %
- Flexural Modulus, 1% Secant: 122 MPa
$ 2030/MT
- Density: 0.900 g/cc
- Melt Flow: 36 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1562/MT
- Density: 0.980 g/cc
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 50
- Tensile Strength, Yield: 19.00 MPa
- Flexural Modulus: 1.300 GPa
$ 1770/MT
- Density: 0.900 g/cc
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 24.4 MPa
- Tensile Strength, Yield: 25.5 MPa
- Elongation at Yield: 3.4 %
$ 2240/MT
- Thickness: 50.8 microns
- Coating Weight: 35.7 g/m²
- Film Elongation at Break, MD: 170 %
- Film Elongation at Break, TD: 55 %
- Modulus of Elasticity: 1.70 GPa
$ 1765/MT
- Water Vapor Transmission: 0.605 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 3.57 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 601 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 605 cc/m²/day @Temperature 23.0 °C
- Thickness: 40.6 microns
$ 1476/MT
- Density: 0.900 g/cc
- Melt Flow: 11 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 70
- Tensile Strength, Yield: 33.0 MPa
- Elongation at Yield: 9.0 %
$ 1746/MT
- Density: 0.900 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 25.8 MPa
- Tensile Strength, Yield: 25.9 MPa
- Elongation at Yield: 4.0 %
$ 2083/MT
- Water Vapor Transmission: 1.40 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 6.98 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 1000 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 1010 cc/m²/day @Temperature 23.0 °C
- Thickness: 20.1 microns
$ 1759/MT
- Water Vapor Transmission: 1.40 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 6.98 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 1000 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 1010 cc/m²/day @Temperature 23.0 °C
- Thickness: 20.1 microns
$ 1764/MT
- Water Vapor Transmission: 0.0497 g/m²/day @Temperature 23.0 °C
- Water Vapor Transmission: 1.20 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 200 cc/m²/day @Temperature 23.0 °C
- Oxygen Transmission Rate: 202 cc/m²/day @Temperature 23.0 °C
- Thickness: 30.5 microns
Delivery Polypropylene (PP) Exxon Chemical
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
chemical tankers for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.