$ 1822/MT
- Density: 0.946 g/cc
- ESCR 100% Igepal®: >= 1000 hour
- Melt Flow: <= 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 5.5 g/10 min @Load 21.6 kg, Temperature 190 °C
- Tensile Strength, Yield: 24.1 MPa
$ 1470/MT
- Density: 0.922 g/cc
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 3500 ppm
- Slip Level: 1000 ppm
- Film Tensile Strength at Yield, MD: 10.2 MPa
$ 2125/MT
- Density: 0.926 g/cc
- Environmental Stress Crack Resistance: 180 hour
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 12.4 MPa
- Elongation at Break: 750 %
$ 1817/MT
- Density: 0.925 g/cc
- Vinyl Acetate Content: 3.0 %
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 2500 ppm
- Slip Level: 800 ppm
$ 1664/MT
- Density: 0.932 g/cc
- ESCR 100% Igepal®: >= 1000 hour
- ESCR 10% Igepal®: 650 hour
- Melt Flow: 5.20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 15.2 MPa
$ 1509/MT
- Density: 0.927 g/cc
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 13.1 MPa
- Film Tensile Strength at Yield, TD: 15.2 MPa
- Film Elongation at Break, MD: 470 %
$ 1723/MT
- Density: 0.927 g/cc
- Melt Flow: 1.3 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 750 ppm
- Slip Level: 1250 ppm
- Film Elongation at Break, MD: 530 %
$ 1589/MT
- Density: 0.924 g/cc
- Thickness: 50.8 microns
- Melt Flow: 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 4000 ppm
- Film Tensile Strength at Yield, MD: 11.0 MPa
$ 1687/MT
- Density: 0.925 g/cc
- Melt Flow: 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 620 %
- Film Elongation at Break, TD: 910 %
- Elmendorf Tear Strength MD: 50 g
$ 1993/MT
- Density: 0.918 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 3500 ppm
- Slip Level: 1500 ppm
- Film Tensile Strength at Yield, MD: 8.27 MPa
$ 1847/MT
- Specific Gravity: 0.900 g/cc
- Volatiles: <= 0.15 %
- Melt Flow: 17 g/10 min @Load 5.00 kg, Temperature 230 °C
- Yellow Index: <= 20 %
- Maleic anhydride graft level: High
$ 2009/MT
- Density: 0.918 g/cc
- Melt Flow: 4.5 g/10 min
- Film Tensile Strength at Yield, MD: 8.34 MPa
- Film Tensile Strength at Yield, TD: 7.31 MPa
- Film Elongation at Break, MD: 500 %
$ 2130/MT
- Density: 0.926 g/cc
- ESCR 10% Igepal®: 180 hour
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 12.4 MPa
- Elongation at Break: 750 %
$ 2157/MT
- Density: 0.952 g/cc
- Melt Flow: 9.0 g/10 min @Load 21.6 kg, Temperature 190 °C
- Hardness, Shore D: 62 @Time 15.0 sec
- Tensile Strength at Break: 33.1 MPa
- Tensile Strength, Yield: 26.9 MPa
$ 1674/MT
- Density: 0.964 g/cc
- Thickness: 25.4 microns
- Melt Flow: 2.40 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 31.72 MPa
- Film Tensile Strength at Yield, TD: 27.58 MPa
$ 1477/MT
- Density: 0.924 g/cc
- ESCR 10% Igepal®: 40 hour @Temperature 50.0 °C
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 10.3 MPa
- Elongation at Break: 100 %
$ 1984/MT
- Density: 0.918 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 600 %
- Film Elongation at Break, TD: 730 %
- Elmendorf Tear Strength MD: 300 g
$ 1673/MT
- Density: 0.926 g/cc
- Melt Flow: 50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: <= 253 °C
- Volume Resistivity: 7.00e+15 ohm-cm
- Dielectric Constant: 2.2
$ 1789/MT
- Density: 0.926 g/cc
- Melt Flow: 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 1500 ppm
- Slip Level: 550 ppm
- Film Elongation at Break, MD: 420 %
$ 1507/MT
- Density: 0.870 g/cc
- Melt Flow: 9.0 g/10 min @Load 10.0 kg, Temperature 230 °C
- Collected Volatile Condensable Material: <= 0.15 %
- Glass Transition Temp, Tg: -42.0 °C
- Yellow Index: <= 15 %
- Maleic anhydride graft level: high
$ 1498/MT
- Density: 0.912 g/cc
- Melt Flow: 12 g/10 min
- Neck In: 6.30 cm
- Neck In: 6.50 cm
- Drawdown: 6.172 m/s
$ 1608/MT
- Density: 0.923 g/cc
- Thickness: 38.1 microns
- Melt Flow: 2.4 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 11.7 MPa
$ 1450/MT
- Density: 0.928 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 1750 ppm
- Film Elongation at Break, MD: 310 %
- Film Elongation at Break, TD: 520 %
$ 1736/MT
- Density: 0.937 g/cc
- ESCR 100% Igepal®: >= 1000 hour
- ESCR 10% Igepal®: 190 hour
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 17.9 MPa
$ 1724/MT
- Density: 0.949 g/cc
- Vinyl Acetate Content: 24 %
- Melt Flow: 1.8 g/10 min
- Melting Point: <= 171 °C
- Crystallization Temperature: <= 190 °C
$ 2214/MT
- Density: 0.918 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 5000 ppm
- Slip Level: 1000 ppm
- Film Tensile Strength at Yield, MD: 9.65 MPa
$ 1704/MT
- Density: 0.918 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 9.65 MPa
- Film Tensile Strength at Yield, TD: 9.65 MPa
- Film Elongation at Break, MD: 480 %
$ 1975/MT
- Density: 0.923 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 49 @Time 15.0 sec
- Tensile Strength at Break: 11.7 MPa
- Tensile Strength, Yield: 11.7 MPa
$ 1494/MT
- Density: 0.948 g/cc
- ESCR 10% Igepal®: 10 hour
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 0.896 MPa
- Tensile Strength, Yield: 22.8 MPa
$ 2150/MT
- Density: 0.918 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 7500 ppm
- Slip Level: 1350 ppm
- Film Tensile Strength at Yield, MD: 8.27 MPa
$ 1791/MT
- Density: 0.917 g/cc
- Thickness: 25.4 microns
- Melt Flow: 0.90 g/10 min
- Antiblock Level: 6500 ppm
- Slip Level: 1400 ppm
$ 1523/MT
- Density: 0.918 g/cc
- Melt Flow: 1.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 8.96 MPa
- Film Tensile Strength at Yield, TD: 9.65 MPa
- Film Elongation at Break, MD: 550 %
$ 1995/MT
- Density: 0.927 g/cc
- Melt Flow: 1.3 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 750 ppm
- Slip Level: 1300 ppm
- Film Tensile Strength at Yield, MD: 12.4 MPa
$ 1453/MT
- Density: 0.953 g/cc
- Melt Flow: 0.25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 30 g/10 min @Load 21.6 kg, Temperature 190 °C
- Tensile Strength, Yield: 28.3 MPa
- Flexural Modulus, 1% Secant: 965 MPa
- Notched Constant Ligament Stress (NCLS): ASTM F2136
$ 1772/MT
- Density: 0.936 g/cc
- ESCR 100% Igepal®: 300 hour
- ESCR 10% Igepal®: 60 hour
- Melt Flow: 6.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 17.2 MPa
$ 1951/MT
- Density: 0.936 g/cc
- Thickness: 50.8 microns
- Melt Flow: 0.20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 4.0 g/10 min @Load 10.0 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.6 MPa
$ 2222/MT
- Density: 0.919 g/cc
- Hardness, Shore A: 89
- Hardness, Shore D: 42
- Tensile Strength at Break: 7.58 MPa
- Tensile Strength, Yield: 11.0 MPa
$ 2271/MT
- Density: 0.923 g/cc
- Melt Flow: 2.4 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 11.7 MPa
- Film Elongation at Break, MD: 270 %
$ 1593/MT
- Density: 0.927 g/cc
- Melt Flow: 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 750 ppm
- Slip Level: 1250 ppm
- Film Elongation at Break, MD: 540 %
$ 2133/MT
- Density: 0.952 g/cc
- ESCR 10% Igepal®: 4.0 hour
- Melt Flow: 6.7 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 8.96 MPa
- Tensile Strength, Yield: 26.2 MPa
$ 1449/MT
- Density: 0.923 g/cc
- Thickness: 38.1 microns
- Melt Flow: 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 2000 ppm
- Slip Level: 400 ppm
$ 1943/MT
- Density: 0.942 g/cc
- ESCR 100% Igepal®: 550 hour
- ESCR 10% Igepal®: 50 hour
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 20.0 MPa
$ 1779/MT
- Density: 0.952 g/cc
- Environmental Stress Crack Resistance: 6.0 hour
- Melt Flow: 4.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 26.20 MPa
- Elongation at Break: 1200 %
$ 1622/MT
- Density: 0.952 g/cc
- Melt Flow: 16 g/10 min @Load 21.6 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 29.0 MPa
- Film Tensile Strength at Yield, TD: 29.0 MPa
- Film Elongation at Break, MD: 320 %
$ 1831/MT
- Water Vapor Transmission: 7.00 g/m²/day
- Thickness: 30.5 microns
- Coating Weight: >= 28.3 g/m²
- Coefficient of Friction: 0.30
- Film Tensile Strength at Break, MD: 33.1 MPa
$ 1799/MT
- Density: 0.937 g/cc
- ESCR 100% Igepal®: >= 1000 hour
- ESCR 10% Igepal®: 185 hour
- Melt Flow: 5.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 17.6 MPa
$ 1780/MT
- Density: 0.923 g/cc
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 2000 ppm
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 11.7 MPa
$ 1772/MT
- Density: 0.954 g/cc
- ESCR 100% Igepal®: 30 hour
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 28.3 MPa
- Elongation at Break: 560 %
$ 1769/MT
- Density: 0.925 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 200 %
- Film Elongation at Break, TD: 500 %
- Elmendorf Tear Strength MD: 200 g
$ 2511/MT
- Density: 0.936 g/cc
- ESCR 100% Igepal®: 300 hour
- ESCR 10% Igepal®: 60 hour
- Melt Flow: 6.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 17.2 MPa
$ 1727/MT
- Density: 0.932 g/cc
- ESCR 100% Igepal®: >= 1000 hour
- ESCR 10% Igepal®: 650 hour
- Melt Flow: 5.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 15.2 MPa
$ 1587/MT
- Density: 0.964 g/cc
- ESCR 10% Igepal®: 4.0 hour @Temperature 50.0 °C
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 26.2 MPa
- Elongation at Break: >= 100 %
$ 1483/MT
- Density: 0.918 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 5000 ppm
- Slip Level: 1700 ppm
- Film Tensile Strength at Yield, MD: 9.65 MPa
$ 1958/MT
- Density: 0.9180 g/cc
- Melt Flow: 3.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 6.89 MPa
- Film Tensile Strength at Yield, TD: 6.76 MPa
- Film Elongation at Break, MD: 560 %
$ 1488/MT
- Density: 0.925 g/cc
- Melt Flow: 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 750 ppm
- Slip Level: 1250 ppm
- Film Elongation at Break, MD: 620 %
$ 1803/MT
- Density: 0.922 g/cc
- Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 43
- Tensile Strength at Break: 8.27 MPa
- Elongation at Break: 140 %
$ 2380/MT
- Water Vapor Transmission: 7.00 g/m²/day
- Thickness: 30.0 microns
- Coating Weight: >= 27.5 g/m²
- Coefficient of Friction: 0.30
- Film Tensile Strength at Break, MD: 34.5 MPa
$ 2281/MT
- Density: 0.919 g/cc
- Thickness: 38.1 microns
- Melt Flow: 1.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 3000 ppm
- Film Tensile Strength at Yield, MD: 11.0 MPa
$ 1655/MT
- Density: 0.927 g/cc
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 13.1 MPa
- Film Tensile Strength at Yield, TD: 15.2 MPa
- Film Elongation at Break, MD: 480 %
$ 1557/MT
- Density: 0.954 g/cc
- ESCR 100% Igepal®: 50 hour
- ESCR 10% Igepal®: 20 hour
- Melt Flow: 0.35 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 29 g/10 min @Load 21.6 kg, Temperature 190 °C
$ 1805/MT
- Density: 0.925 g/cc
- Vinyl Acetate Content: 5.5 %
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 4000 ppm
- Film Elongation at Break, MD: 190 %
$ 1717/MT
- Density: 0.943 g/cc
- Viscosity: 3100 cP @Temperature 190 °C
- Vinyl Acetate Content: 14 %
- Melting Point: <= 201 °C
- Crystallization Temperature: <= 170 °C
$ 1720/MT
- Density: 0.929 g/cc
- Thickness: 38.1 microns
- Melt Flow: 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 1000 ppm
- Film Tensile Strength at Yield, MD: 14.5 MPa
$ 1744/MT
- Density: 0.926 g/cc
- Melt Flow: 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 420 %
- Film Elongation at Break, TD: 560 %
- Elmendorf Tear Strength MD: 280 g
$ 2084/MT
- Density: 0.942 g/cc
- Melt Flow: 4.3 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 16.5 MPa
- Film Tensile Strength at Yield, TD: 17.2 MPa
- Film Elongation at Break, MD: 590 %
$ 1652/MT
- Density: 0.952 g/cc
- Melt Flow: 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 10 g/10 min @Load 21.6 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 37.9 MPa
- Film Tensile Strength at Yield, TD: 33.1 MPa
$ 1740/MT
- Density: 0.923 g/cc
- Melt Flow: 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 12.4 MPa
- Film Elongation at Break, MD: 130 %
$ 2577/MT
- Density: 0.918 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 9.65 MPa
- Film Tensile Strength at Yield, TD: 9.65 MPa
- Film Elongation at Break, MD: 580 %
$ 1989/MT
- Density: 0.950 g/cc
- ESCR 100% Igepal®: 70 hour
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 26.9 MPa
- Elongation at Break: 600 %
$ 1609/MT
- Density: 0.917 g/cc
- Thickness: 25.4 microns
- Melt Flow: 0.90 g/10 min
- Antiblock Level: 8000 ppm
- Slip Level: 850 ppm
$ 1471/MT
- Density: 0.929 g/cc
- Melt Flow: 0.55 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 13.1 MPa
- Film Tensile Strength at Yield, TD: 13.1 MPa
- Film Elongation at Break, MD: 460 %
$ 1536/MT
- Density: 0.936 g/cc
- ESCR 100% Igepal®: >= 160 hour
- ESCR 10% Igepal®: 60 hour
- Melt Flow: 6.8 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 17.2 MPa
$ 1922/MT
- Density: 0.936 g/cc
- ESCR 10% Igepal®: 30 hour @Temperature 50.0 °C
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 13.8 MPa
- Elongation at Break: 100 %
$ 1743/MT
- Density: 0.926 g/cc
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 5000 ppm
- Film Tensile Strength at Yield, MD: 11.7 MPa
- Film Tensile Strength at Yield, TD: 13.8 MPa
$ 1862/MT
- Density: 0.960 g/cc
- ESCR 10% Igepal®: 6.0 hour @Temperature 50.0 °C
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 24.1 MPa
- Elongation at Break: >= 100 %
$ 1461/MT
- Density: 0.918 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 4500 ppm
- Film Tensile Strength at Yield, MD: 9.65 MPa
- Film Tensile Strength at Yield, TD: 9.65 MPa
$ 1857/MT
- Density: 0.925 g/cc
- Vinyl Acetate Content: 5.5 %
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 1000 ppm
- Slip Level: 500 ppm
$ 2489/MT
- Density: 0.922 g/cc
- Melt Flow: 0.33 g/10 min
- Film Tensile Strength at Yield, MD: 12.4 MPa
- Film Tensile Strength at Yield, TD: 11.7 MPa
- Film Elongation at Break, MD: 160 %
$ 1644/MT
- Density: 0.924 g/cc
- Melt Flow: 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 450 ppm
- Slip Level: 500 ppm
- Film Elongation at Break, MD: 340 %
$ 1827/MT
- Density: 0.935 g/cc
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: <= 257 °C
- Volume Resistivity: 7.00e+15 ohm-cm
- Dielectric Constant: 2.2 @Frequency 60.0 Hz
$ 1453/MT
- Density: 0.920 g/cc
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.3 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
- Film Elongation at Break, MD: 480 %
$ 1564/MT
- Density: 0.948 g/cc
- ESCR 100% Igepal®: 10 hour
- ESCR 10% Igepal®: 8.0 hour
- Melt Flow: 5.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 23.4 MPa
$ 1944/MT
- Density: 0.912 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 5000 ppm
- Slip Level: 1000 ppm
- Film Tensile Strength at Yield, MD: 6.89 MPa
$ 1848/MT
- Density: 0.920 g/cc
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.3 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
- Film Elongation at Break, MD: 480 %
$ 1886/MT
- Density: 0.925 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 1800 ppm
- Slip Level: 330 ppm
- Film Elongation at Break, MD: 200 %
$ 1849/MT
- Density: 0.951 g/cc
- ESCR 100% Igepal®: >= 800 hour
- Melt Flow: 11 g/10 min
- Melt Flow: <= 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 25.5 MPa
$ 1452/MT
- Density: 0.924 g/cc
- Melt Flow: 22 g/10 min
- Hardness, Shore D: 44
- Tensile Strength at Break: 8.96 MPa
- Elongation at Break: 120 %
$ 1848/MT
- Density: 0.916 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Neck In: 3.81 cm @Temperature 315 °C
- Neck In: 4.06 cm @Temperature 315 °C
- Drawdown: 4.00 m/s @Temperature 315 °C
- Melting Point: <= 221 °C
$ 2003/MT
- Density: 0.922 g/cc
- Melt Flow: 40 g/10 min @Load 2.16 kg, Temperature 190 °C
- Slip Level: 550 ppm
- Hardness, Shore A: 88
- Hardness, Shore D: 43
$ 1881/MT
- Density: 0.954 g/cc
- ESCR 100% Igepal®: 30 hour
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 28.3 MPa
- Elongation at Break: 560 %
$ 2357/MT
- Density: 0.917 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 8.41 MPa
- Film Tensile Strength at Yield, TD: 7.72 MPa
- Film Elongation at Break, MD: 340 %
$ 1963/MT
- Density: 0.931 g/cc
- Melt Flow: 1.9 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 55
- Tensile Strength at Break: 11.7 MPa
- Tensile Strength, Yield: 15.2 MPa
$ 1836/MT
- Density: 0.919 g/cc
- Melt Flow: 26 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 86 @Time 15.0 sec
- Hardness, Shore D: 42 @Time 15.0 sec
- Tensile Strength at Break: 7.58 MPa
$ 1585/MT
- Density: 0.942 g/cc
- ESCR 100% Igepal®: 550 hour
- ESCR 10% Igepal®: 50 hour
- Melt Flow: 2.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 20.0 MPa
$ 1757/MT
- Density: 0.945 g/cc
- ESCR 100% Igepal®: >= 1000 hour
- Melt Flow: 0.35 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 24.1 MPa
- Elongation at Break: 900 %
$ 1447/MT
- Density: 0.912 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 6.89 MPa
- Film Tensile Strength at Yield, TD: 6.76 MPa
- Film Elongation at Break, MD: 450 %
$ 1826/MT
- ESCR 100% Igepal®: >= 1000 hour
- ESCR 10% Igepal®: >= 1000 hour
- Tensile Strength, Yield: 19.3 MPa
- Elongation at Break: 700 %
- Elongation at Yield: 20 %
$ 1500/MT
- Density: 0.926 g/cc
- Melt Flow: 50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: <= 253 °C
- Volume Resistivity: 7.00e+15 ohm-cm
- Dielectric Constant: 2.2
$ 1757/MT
- Density: 0.936 g/cc
- ESCR 100% Igepal®: >= 40 hour
- ESCR 10% Igepal®: 20 hour
- ESCR 10% Igepal®: 30 hour @Thickness 1.91 mm
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1463/MT
- Density: 0.920 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 2000 ppm
- Slip Level: 500 ppm
- Film Tensile Strength at Yield, MD: 9.65 MPa
$ 2510/MT
- Density: 0.954 g/cc
- ESCR 10% Igepal®: <= 1.0 hour @Temperature 50.0 °C
- Melt Flow: 30 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 22.1 MPa
- Elongation at Break: >= 100 %
$ 2018/MT
- Density: 0.942 g/cc
- ESCR 100% Igepal®: 550 hour
- ESCR 10% Igepal®: 50 hour
- Melt Flow: 2.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 20.0 MPa
$ 1646/MT
- Density: 0.935 g/cc
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: <= 257 °C
- Volume Resistivity: 7.00e+15 ohm-cm
- Dielectric Constant: 2.2 @Frequency 60.0 Hz
$ 1806/MT
- Density: 0.936 g/cc
- ESCR 100% Igepal®: >= 160 hour
- ESCR 10% Igepal®: 60 hour
- Melt Flow: 6.8 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 17.2 MPa
$ 1515/MT
- Density: 0.934 g/cc
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 1000 ppm
- Slip Level: 1050 ppm
- Film Tensile Strength at Yield, TD: 17.2 MPa
$ 1613/MT
- Density: 0.927 g/cc
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 13.1 MPa
- Film Elongation at Break, MD: 540 %
- Film Elongation at Break, TD: 760 %
$ 1702/MT
- Density: 0.924 g/cc
- Melt Flow: 1.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 1750 ppm
- Film Elongation at Break, MD: 200 %
- Film Elongation at Break, TD: 510 %
$ 2056/MT
- Density: 0.925 g/cc
- Vinyl Acetate Content: 5.5 %
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 3000 ppm
- Slip Level: 1100 ppm
$ 1761/MT
- Density: 0.952 g/cc
- Melt Flow: 19 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 25.5 MPa
- Elongation at Break: 270 %
- Flexural Modulus: 1.10 GPa
$ 1532/MT
- Density: 0.918 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 48 @Time 15.0 sec
- Tensile Strength at Break: 17.2 MPa
- Tensile Strength, Yield: 11.7 MPa
$ 2114/MT
- Density: 0.927 g/cc
- Melt Flow: 1.3 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 12.4 MPa
- Film Tensile Strength at Yield, TD: 13.8 MPa
- Film Elongation at Break, MD: 600 %
$ 1536/MT
- Density: 0.921 g/cc
- Melt Flow: 33 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 81 @Time 15.0 sec
- Hardness, Shore D: 49 @Time 15.0 sec
- Tensile Strength at Break: 8.27 MPa
$ 1863/MT
- Density: 0.918 g/cc
- Thickness: 20.3 microns
- Melt Flow: 3.5 g/10 min
- Film Tensile Strength at Yield, MD: 8.27 MPa
- Film Tensile Strength at Yield, TD: 7.58 MPa
$ 1722/MT
- Density: 0.963 g/cc
- ESCR 100% Igepal®: 10 hour
- Melt Flow: 0.73 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 32.4 MPa
- Elongation at Break: 350 %
$ 2235/MT
- Density: 0.918 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 9.65 MPa
- Film Tensile Strength at Yield, TD: 9.65 MPa
- Film Elongation at Break, MD: 580 %
$ 1597/MT
- Density: 0.965 g/cc
- ESCR 10% Igepal®: 3.0 hour
- Melt Flow: 8.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 3.03 MPa
- Tensile Strength, Yield: 30.3 MPa
$ 2214/MT
- Density: 0.918 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 5000 ppm
- Slip Level: 1000 ppm
- Film Tensile Strength at Yield, MD: 9.65 MPa
$ 1638/MT
- Density: 0.958 g/cc
- Melt Flow: 0.45 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 30 g/10 min @Load 21.6 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 34.5 MPa
- Film Tensile Strength at Yield, TD: 13.1 MPa
$ 1905/MT
- Density: 0.900 g/cc
- Thickness: 20.3 microns
- Melt Flow: 3.5 g/10 min
- Film Tensile Strength at Yield, MD: 6.27 MPa
- Film Tensile Strength at Yield, TD: 4.30 MPa
$ 1653/MT
- Density: 0.925 g/cc
- Melt Flow: 3.6 g/10 min @Load 2.16 kg, Temperature 190 °C
- Slip Level: 400 ppm
- Film Tensile Strength at Yield, MD: 10.3 MPa
- Film Tensile Strength at Yield, TD: 10.3 MPa
$ 1553/MT
- Density: 0.921 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 1500 ppm
- Slip Level: 750 ppm
- Film Tensile Strength at Yield, MD: 10.3 MPa
$ 1470/MT
- Density: 0.924 g/cc
- Melt Flow: 21 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 44
- Tensile Strength at Break: 8.96 MPa
- Elongation at Break: 140 %
$ 1991/MT
- Density: 0.938 g/cc
- ESCR 100% Igepal®: >= 1000 hour
- ESCR 10% Igepal®: 150 hour
- Melt Flow: 3.3 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 17.9 MPa
$ 1727/MT
- Density: 0.925 g/cc
- Vinyl Acetate Content: 4.6 %
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 4000 ppm
- Slip Level: 800 ppm
$ 1960/MT
- Density: 0.936 g/cc
- ESCR 10% Igepal®: 30 hour @Temperature 50.0 °C
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 13.8 MPa
- Elongation at Break: 100 %
$ 1662/MT
- Density: 0.918 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 8.96 MPa
- Film Tensile Strength at Yield, TD: 8.96 MPa
- Film Elongation at Break, MD: 590 %
$ 1545/MT
- Density: 0.917 g/cc
- Thickness: 25.4 microns
- Melt Flow: 0.90 g/10 min
- Antiblock Level: 6500 ppm
- Film Tensile Strength at Yield, MD: 10.3 MPa
$ 2268/MT
- Density: 0.921 g/cc
- Melt Flow: 6.8 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 3000 ppm
- Slip Level: 1200 ppm
- Film Tensile Strength at Yield, MD: 9.65 MPa
$ 1911/MT
- Density: 0.925 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 1000 ppm
- Slip Level: 750 ppm
- Film Elongation at Break, MD: 200 %
$ 2106/MT
- Density: 0.918 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 7.58 MPa
- Film Tensile Strength at Yield, TD: 6.48 MPa
- Film Elongation at Break, MD: 420 %
$ 1938/MT
- Density: 0.925 g/cc
- Melt Flow: 3.6 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 6000 ppm
- Slip Level: 1500 ppm
- Film Tensile Strength at Yield, MD: 10.3 MPa
$ 1843/MT
- Density: 0.925 g/cc
- Environmental Stress Crack Resistance: 330 hour
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 11.72 MPa
- Elongation at Break: 350 %
$ 1716/MT
- Density: 0.938 g/cc
- ESCR 100% Igepal®: >= 1000 hour
- ESCR 10% Igepal®: 150 hour
- Melt Flow: 3.3 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 17.9 MPa
$ 1750/MT
- Density: 0.926 g/cc
- Melt Flow: 0.50 g/10 min
- Film Elongation at Break, MD: 430 %
- Film Elongation at Break, TD: 550 %
- Elmendorf Tear Strength MD: 100 g
$ 1592/MT
- Density: 0.926 g/cc
- ESCR 10% Igepal®: 6.0 hour
- Melt Flow: 50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 10.3 MPa
- Elongation at Break: 100 %
$ 2059/MT
- Density: 0.926 g/cc
- Vinyl Acetate Content: 6.0 %
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 300 %
- Film Elongation at Break, TD: 620 %
$ 1446/MT
- Density: 0.918 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 7000 ppm
- Film Tensile Strength at Yield, MD: 9.65 MPa
- Film Tensile Strength at Yield, TD: 9.65 MPa
$ 1578/MT
- Density: 0.918 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 5000 ppm
- Slip Level: 1000 ppm
- Film Tensile Strength at Yield, MD: 9.65 MPa
$ 1940/MT
- Density: 0.917 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 9.65 MPa
- Film Tensile Strength at Yield, TD: 10.3 MPa
- Film Elongation at Break, MD: 500 %
$ 1468/MT
- Density: 0.963 g/cc
- ESCR 100% Igepal®: 10 hour
- Melt Flow: 0.47 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 31.7 MPa
- Elongation at Break: 400 %
$ 1687/MT
- Density: 0.919 g/cc
- Melt Flow: 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C
- Slip Level: 200 ppm
- Hardness, Shore A: 84 @Time 15.0 sec
- Hardness, Shore D: 45 @Time 15.0 sec
$ 1465/MT
- Density: 0.936 g/cc
- ESCR 100% Igepal®: 300 hour
- ESCR 10% Igepal®: 60 hour
- Melt Flow: 6.8 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 17.2 MPa
$ 1923/MT
- Density: 0.923 g/cc
- Thickness: 38.1 microns
- Melt Flow: 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 1500 ppm
- Slip Level: 750 ppm
$ 1463/MT
- Density: 0.941 g/cc
- Thickness: 50.8 microns
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 5.8 g/10 min @Load 10.0 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 14.0 MPa
$ 1955/MT
- Density: 0.921 g/cc
- Melt Flow: 33 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 81 @Time 15.0 sec
- Hardness, Shore D: 49
- Tensile Strength at Break: 8.27 MPa
$ 2245/MT
- Density: 0.929 g/cc
- Thickness: 38.1 microns
- Melt Flow: 1.6 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 1000 ppm
- Slip Level: 250 ppm
$ 1716/MT
- Density: 0.921 g/cc
- Melt Flow: 6.8 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 3000 ppm
- Slip Level: 1200 ppm
- Film Tensile Strength at Yield, MD: 9.65 MPa
$ 1722/MT
- Density: 0.963 g/cc
- ESCR 100% Igepal®: 20 hour
- Melt Flow: 0.25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 31.7 MPa
- Elongation at Break: 450 %
$ 1506/MT
- Density: 0.924 g/cc
- Melt Flow: 1.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 1800 ppm
- Slip Level: 650 ppm
- Film Elongation at Break, MD: 200 %
$ 1690/MT
- ESCR 100% Igepal®: >= 1000 hour
- ESCR 10% Igepal®: >= 1000 hour
- Tensile Strength, Yield: 19.3 MPa
- Elongation at Break: 700 %
- Elongation at Yield: 20 %
$ 1578/MT
- Density: 0.918 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 7000 ppm
- Film Tensile Strength at Yield, MD: 9.65 MPa
- Film Tensile Strength at Yield, TD: 9.65 MPa
$ 1458/MT
- Density: 0.923 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 450 ppm
- Slip Level: 500 ppm
- Film Tensile Strength at Yield, MD: 11.0 MPa
$ 1876/MT
- Density: 0.923 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 1000 ppm
- Slip Level: 750 ppm
- Film Tensile Strength at Yield, MD: 11.0 MPa
$ 1683/MT
- Density: 0.933 g/cc
- Melt Flow: 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, TD: 15.9 MPa
- Film Elongation at Break, MD: 400 %
- Film Elongation at Break, TD: 600 %
$ 1486/MT
- Density: 0.923 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 1000 ppm
- Slip Level: 572 ppm
- Film Tensile Strength at Yield, MD: 11.0 MPa
$ 1786/MT
- Density: 0.923 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 1800 ppm
- Slip Level: 330 ppm
- Film Tensile Strength at Yield, MD: 11.0 MPa
$ 1749/MT
- Density: 0.931 g/cc
- Melt Flow: 1.9 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, TD: 17.2 MPa
- Film Elongation at Break, MD: 380 %
- Film Elongation at Break, TD: 600 %
$ 1850/MT
- Density: 0.918 g/cc
- Melt Flow: 4.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 8.27 MPa
- Film Tensile Strength at Yield, TD: 7.58 MPa
- Film Elongation at Break, MD: 500 %
$ 1980/MT
- Thickness: 22.9 microns
- Coating Weight: >= 21.6 g/m²
- Coefficient of Friction: 0.25
- Coefficient of Friction: 0.25
- Film Tensile Strength at Break, MD: 141 MPa
$ 1819/MT
- Density: 0.952 g/cc
- Melt Flow: 19 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 1.86 MPa
- Tensile Strength, Yield: 25.5 MPa
- Flexural Modulus: 1.10 GPa
$ 1516/MT
- Density: 0.929 g/cc
- Melt Flow: 1.6 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 1000 ppm
- Slip Level: 250 ppm
- Film Tensile Strength at Yield, MD: 13.8 MPa
$ 1823/MT
- Density: 0.965 g/cc
- ESCR 10% Igepal®: 3.0 hour
- Melt Flow: 8.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 3.03 MPa
- Tensile Strength, Yield: 30.3 MPa
$ 1522/MT
- Density: 0.942 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 17.2 MPa
- Film Tensile Strength at Yield, TD: 22.8 MPa
- Film Elongation at Break, MD: 770 %
$ 2053/MT
- Density: 0.919 g/cc
- Melt Flow: 1.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 10.3 MPa
- Film Elongation at Break, MD: 150 %
$ 1956/MT
- Density: 0.919 g/cc
- Melt Flow: 1.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 3000 ppm
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 10.3 MPa
$ 1647/MT
- Density: 0.942 g/cc
- ESCR 100% Igepal®: 550 hour
- ESCR 10% Igepal®: 50 hour
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 20.0 MPa
$ 1860/MT
- Density: 0.916 g/cc
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Neck In: 3.05 cm @Temperature 315 °C
- Neck In: 3.30 cm @Temperature 315 °C
- Drawdown: 2.33 m/s @Temperature 315 °C
- Melting Point: <= 221 °C
$ 1662/MT
- Density: 0.952 g/cc
- Melt Flow: 9.0 g/10 min @Load 21.6 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 40.7 MPa
- Film Tensile Strength at Yield, TD: 30.3 MPa
- Film Elongation at Break, MD: 220 %
$ 1916/MT
- Density: 0.928 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 310 %
- Film Elongation at Break, TD: 520 %
- Elmendorf Tear Strength MD: 90 g
$ 1764/MT
- Density: 0.925 g/cc
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 50
- Tensile Strength at Break: 7.45 MPa
- Tensile Strength, Yield: 14.5 MPa
$ 1834/MT
- Density: 0.927 g/cc
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 580 %
- Film Elongation at Break, TD: 780 %
- Elmendorf Tear Strength MD: 100 g
$ 2047/MT
- Density: 0.925 g/cc
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 50 @Time 15.0 sec
- Tensile Strength at Break: 7.58 MPa
- Tensile Strength, Yield: 14.5 MPa
$ 1583/MT
- Density: 0.924 g/cc
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: <= 253 °C
- Volume Resistivity: 7.00e+15 ohm-cm
- Dielectric Constant: 2.1 @Frequency 60.0 Hz
$ 1451/MT
- Density: 0.923 g/cc
- Melt Flow: 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 370 %
- Film Elongation at Break, TD: 570 %
- Elmendorf Tear Strength MD: 200 g
$ 1487/MT
- Density: 0.923 g/cc
- Melt Flow: 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 450 ppm
- Slip Level: 500 ppm
- Film Elongation at Break, MD: 370 %
$ 1931/MT
- Density: 0.915 g/cc
- Melt Flow: 12 g/10 min
- Neck In: 4.32 cm @Temperature 315 °C
- Neck In: 4.57 cm @Temperature 315 °C
- Drawdown: 9.17 m/s @Temperature 315 °C
- Melting Point: <= 219 °C
$ 1601/MT
- Density: 0.919 g/cc
- Melt Flow: 26 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 86
- Hardness, Shore D: 42
- Tensile Strength at Break: 7.58 MPa
$ 1700/MT
- Density: 0.957 g/cc
- ESCR 100% Igepal®: >= 1000 hour
- Melt Flow: 0.46 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 30.3 MPa
- Elongation at Break: 1100 %
$ 1626/MT
- Density: 0.918 g/cc
- Melt Flow: 2.0 g/10 min
- Antiblock Level: 7500 ppm
- Slip Level: 1350 ppm
- Film Tensile Strength at Yield, MD: 8.48 MPa
$ 1569/MT
- Density: 0.950 g/cc
- Melt Flow: 33 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 0.138 MPa
- Tensile Strength, Yield: 23.4 MPa
- Flexural Modulus: 0.965 GPa
$ 1829/MT
- Density: 0.958 g/cc
- Melt Flow: 0.45 g/10 min @Load 2.16 kg, Temperature 190 °C
- High Load Melt Index: 30 g/10 min @Load 21.6 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 34.5 MPa
- Film Tensile Strength at Yield, TD: 13.1 MPa
$ 1530/MT
- Density: 0.918 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 5000 ppm
- Slip Level: 1700 ppm
- Film Tensile Strength at Yield, MD: 9.65 MPa
$ 2438/MT
- Density: 0.924 g/cc
- ESCR 10% Igepal®: 40 hour @Temperature 50.0 °C
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 10.3 MPa
- Elongation at Break: 100 %
$ 1772/MT
- Density: 0.932 g/cc
- ESCR 100% Igepal®: >= 1000 hour
- ESCR 10% Igepal®: 650 hour
- Melt Flow: 5.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 15.2 MPa
$ 2073/MT
- Density: 0.928 g/cc
- Melt Flow: 0.35 g/10 min
- Film Tensile Strength at Yield, MD: 13.1 MPa
- Film Tensile Strength at Yield, TD: 13.1 MPa
- Film Elongation at Break, MD: 450 %
$ 1570/MT
- Density: 0.954 g/cc
- Melt Flow: 0.43 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1482/MT
- Density: 0.927 g/cc
- Melt Flow: 1.3 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 570 %
- Film Elongation at Break, TD: 710 %
- Elmendorf Tear Strength MD: 200 g
$ 1694/MT
- Density: 0.927 g/cc
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 13.1 MPa
- Film Tensile Strength at Yield, TD: 14.5 MPa
- Film Elongation at Break, MD: 520 %
$ 2353/MT
- Density: 0.919 g/cc
- Melt Flow: 0.25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 4000 ppm
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 10.3 MPa
$ 2380/MT
- Density: 0.917 g/cc
- Thickness: 25.4 microns
- Melt Flow: 0.90 g/10 min
- Antiblock Level: 8000 ppm
- Slip Level: 1400 ppm
$ 1470/MT
- Density: 0.918 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 39 @Time 15.0 sec
- Tensile Strength at Break: 13.1 MPa
- Tensile Strength, Yield: 11.7 MPa
$ 1490/MT
- Density: 0.918 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 4500 ppm
- Slip Level: 450 ppm
- Film Tensile Strength at Yield, MD: 9.65 MPa
$ 2533/MT
- Density: 0.937 g/cc
- ESCR 100% Igepal®: >= 1000 hour
- ESCR 10% Igepal®: 185 hour
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 17.9 MPa
$ 1539/MT
- Density: 0.936 g/cc
- ESCR 100% Igepal®: >= 160 hour
- ESCR 10% Igepal®: 60 hour
- Melt Flow: 6.8 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 17.2 MPa
$ 1631/MT
- Density: 0.926 g/cc
- ESCR 10% Igepal®: 180 hour
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 12.4 MPa
- Elongation at Break: 750 %
$ 2193/MT
- Density: 0.923 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 1000 ppm
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
$ 1533/MT
- Density: 0.929 g/cc
- Melt Flow: 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 2000 ppm
- Slip Level: 400 ppm
- Film Tensile Strength at Yield, MD: 14.5 MPa
$ 1795/MT
- Specific Gravity: 0.960 g/cc
- Volatiles: <= 0.15 %
- Melt Flow: 1.4 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 3.4 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melting Point: 134 °C
$ 1897/MT
- Density: 0.926 g/cc
- Thickness: 38.1 microns
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 5000 ppm
- Film Tensile Strength at Yield, MD: 11.7 MPa
$ 1575/MT
- Density: 0.918 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 4500 ppm
- Slip Level: 450 ppm
- Film Tensile Strength at Yield, MD: 9.65 MPa
$ 1790/MT
- Density: 0.923 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
- Film Elongation at Break, MD: 370 %
$ 1502/MT
- Density: 0.860 g/cc
- Melt Flow: 3.3 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 22 g/10 min @Load 10.0 kg, Temperature 230 °C
- Collected Volatile Condensable Material: <= 0.15 %
- Glass Transition Temp, Tg: -59.0 °C
$ 1824/MT
- Density: 0.936 g/cc
- ESCR 10% Igepal®: 240 hour
- Melt Flow: 6.8 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Break: 1100 %
$ 1484/MT
- Density: 0.918 g/cc
- Melt Flow: 3.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 6.89 MPa
- Film Tensile Strength at Yield, TD: 6.76 MPa
- Film Elongation at Break, MD: 560 %
$ 2001/MT
- Density: 0.965 g/cc
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 31.7 MPa
- Film Tensile Strength at Yield, TD: 27.6 MPa
- Film Elongation at Break, MD: 790 %
$ 1496/MT
- Density: 0.923 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 49 @Time 15.0 sec
- Tensile Strength at Break: 11.7 MPa
- Tensile Strength, Yield: 11.0 MPa
$ 1867/MT
- Density: 0.913 g/cc
- Melt Flow: 70 g/10 min
- Hardness, Shore D: 38
- Tensile Strength at Break: 6.89 MPa
- Elongation at Break: 150 %
$ 1711/MT
- Density: 0.926 g/cc
- Melt Flow: 52 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 51 @Time 15.0 sec
- Tensile Strength at Break: 7.58 MPa
- Tensile Strength, Yield: 15.2 MPa
$ 2098/MT
- Density: 0.932 g/cc
- ESCR 100% Igepal®: >= 1000 hour
- ESCR 10% Igepal®: 650 hour
- Melt Flow: 5.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 15.2 MPa
$ 2477/MT
- Density: 0.952 g/cc
- Melt Flow: 9.5 g/10 min @Load 21.6 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 40.7 MPa
- Film Tensile Strength at Yield, TD: 29.0 MPa
- Film Elongation at Break, MD: 210 %
$ 1559/MT
- Density: 0.919 g/cc
- Melt Flow: 9.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 89 @Time 15.0 sec
- Hardness, Shore D: 42 @Time 15.0 sec
- Tensile Strength at Break: 7.58 MPa
$ 1642/MT
- Density: 0.935 g/cc
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 17.2 MPa
- Film Tensile Strength at Yield, TD: 19.3 MPa
- Film Elongation at Break, MD: 550 %
$ 2100/MT
- Density: 0.949 g/cc
- ESCR 100% Igepal®: >= 800 hour
- Melt Flow: 10 g/10 min
- Melt Flow: <= 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 26.2 MPa
$ 1852/MT
- Density: 0.952 g/cc
- ESCR 10% Igepal®: 6.0 hour
- Melt Flow: 4.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 8.27 MPa
- Tensile Strength, Yield: 26.2 MPa
$ 1511/MT
- Density: 0.912 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 6.89 MPa
- Film Tensile Strength at Yield, TD: 6.76 MPa
- Film Elongation at Break, MD: 450 %
$ 2338/MT
- Density: 0.918 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 8.27 MPa
- Film Tensile Strength at Yield, TD: 7.58 MPa
- Film Elongation at Break, MD: 350 %
$ 2129/MT
- Density: 0.924 g/cc
- Vinyl Acetate Content: 3.5 %
- Melt Flow: 1.3 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 2500 ppm
- Slip Level: 500 ppm
$ 2165/MT
- Density: 0.920 g/cc
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.3 MPa
- Film Tensile Strength at Yield, TD: 10.3 MPa
- Film Elongation at Break, MD: 480 %
$ 1623/MT
- Density: 0.954 g/cc
- ESCR 100% Igepal®: >= 1000 hour
- Melt Flow: <= 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 5.5 g/10 min @Load 21.6 kg, Temperature 190 °C
- Tensile Strength, Yield: 28.3 MPa
$ 1848/MT
- Density: 0.942 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 15.2 MPa
- Film Tensile Strength at Yield, TD: 15.9 MPa
- Film Elongation at Break, MD: 520 %
$ 1951/MT
- Density: 0.952 g/cc
- Melt Flow: 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C
- High Load Melt Index: 10 g/10 min @Load 21.6 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 37.9 MPa
- Film Tensile Strength at Yield, TD: 33.1 MPa
$ 1471/MT
- Density: 0.918 g/cc
- Melt Flow: 4.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 8.27 MPa
- Film Tensile Strength at Yield, TD: 7.58 MPa
- Film Elongation at Break, MD: 500 %
$ 1645/MT
- Density: 0.915 g/cc
- Melt Flow: 7.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Neck In: 3.30 cm
- Neck In: 3.56 cm
- Drawdown: 1.83 m/s
$ 1787/MT
- Vinyl Acetate Content: 7.5 %
- Melt Flow: 0.50 g/10 min
$ 1905/MT
- Density: 0.924 g/cc
- Thickness: 50.8 microns
- Antiblock Level: 2000 ppm
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 11.8 MPa
$ 1999/MT
- Density: 0.918 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 8.27 MPa
- Film Tensile Strength at Yield, TD: 8.27 MPa
- Film Elongation at Break, MD: 660 %
$ 1890/MT
- Density: 0.918 g/cc
- Thickness: 20.3 microns
- Melt Flow: 3.5 g/10 min
- Film Tensile Strength at Yield, MD: 8.27 MPa
- Film Tensile Strength at Yield, TD: 7.58 MPa
$ 2143/MT
- Density: 0.915 g/cc
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 190 °C
- Neck In: 3.56 cm
- Neck In: 4.06 cm
- Drawdown: 4.00 m/s
$ 2153/MT
- Density: 0.912 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 4500 ppm
- Film Tensile Strength at Yield, MD: 6.89 MPa
- Film Tensile Strength at Yield, TD: 7.58 MPa
$ 1522/MT
- Density: 0.928 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 1500 ppm
- Slip Level: 550 ppm
- Film Elongation at Break, MD: 310 %
$ 1505/MT
- Density: 0.930 g/cc
- Vinyl Acetate Content: 8.7 %
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 330 %
- Film Elongation at Break, TD: 660 %
$ 1931/MT
- Density: 0.922 g/cc
- Melt Flow: 40 g/10 min @Load 2.16 kg, Temperature 190 °C
- Slip Level: 550 ppm
- Hardness, Shore A: 88 @Time 15.0 sec
- Hardness, Shore D: 43 @Time 15.0 sec
$ 1673/MT
- Density: 0.919 g/cc
- Melt Flow: 8.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Neck In: 4.32 cm @Temperature 315 °C
- Neck In: 4.83 cm @Temperature 315 °C
- Drawdown: 7.17 m/s @Temperature 295 °C
- Melting Point: <= 223 °C
$ 1710/MT
- Density: 0.945 g/cc
- ESCR 100% Igepal®: >= 1000 hour
- Melt Flow: <= 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 6.3 g/10 min @Load 21.6 kg, Temperature 190 °C
- Tensile Strength, Yield: 22.8 MPa
$ 2120/MT
- Density: 0.924 g/cc
- Melt Flow: 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 4000 ppm
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 11.7 MPa
$ 1538/MT
- Density: 0.931 g/cc
- Melt Flow: 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 54 @Time 15.0 sec
- Tensile Strength at Break: 15.9 MPa
- Tensile Strength, Yield: 13.8 MPa
$ 2120/MT
- Density: 0.923 g/cc
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 1200 ppm
- Slip Level: 900 ppm
- Film Tensile Strength at Yield, MD: 10.3 MPa
$ 2574/MT
- Density: 0.918 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 9.65 MPa
- Film Tensile Strength at Yield, TD: 9.65 MPa
- Film Elongation at Break, MD: 480 %
$ 1759/MT
- Density: 0.913 g/cc
- Melt Flow: 150 g/10 min
- Hardness, Shore D: 35
- Tensile Strength at Break: 6.00 MPa
- Elongation at Break: 170 %
$ 1629/MT
- Density: 0.952 g/cc
- Environmental Stress Crack Resistance: 4.0 hour
- Melt Flow: 6.7 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 26.2 MPa
- Elongation at Break: 1300 %
$ 1456/MT
- Density: 0.920 g/cc
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 2000 ppm
- Slip Level: 500 ppm
- Film Tensile Strength at Yield, MD: 10.3 MPa
$ 2593/MT
- Density: 0.880 g/cc
- Melt Flow: 8.0 g/10 min @Load 5.00 kg, Temperature 230 °C
- Collected Volatile Condensable Material: <= 0.15 %
- Yellow Index: <= 10 %
- Maleic anhydride graft level: medium
$ 1731/MT
- Density: 0.936 g/cc
- ESCR 100% Igepal®: >= 160 hour
- ESCR 10% Igepal®: 60 hour
- Melt Flow: 6.8 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 17.2 MPa
$ 2301/MT
- Density: 0.928 g/cc
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 360 %
- Film Elongation at Break, TD: 600 %
- Elmendorf Tear Strength MD: 120 g
$ 2066/MT
- Density: 0.936 g/cc
- Thickness: 50.8 microns
- Melt Flow: 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 2.6 g/10 min @Load 10.0 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.9 MPa
$ 1795/MT
- Density: 0.920 g/cc
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.3 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
- Film Elongation at Break, MD: 480 %
$ 1813/MT
- Density: 0.956 g/cc
- ESCR 10% Igepal®: 2.0 hour @Temperature 50.0 °C
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 22.8 MPa
- Elongation at Break: >= 100 %
$ 1823/MT
- Density: 0.921 g/cc
- Melt Flow: 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 90 @Time 15.0 sec
- Hardness, Shore D: 44 @Time 15.0 sec
- Tensile Strength at Break: 10.3 MPa
$ 1836/MT
- Density: 0.926 g/cc
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.7 MPa
- Film Tensile Strength at Yield, TD: 13.8 MPa
- Film Elongation at Break, MD: 510 %
$ 1801/MT
- Density: 0.957 g/cc
- Environmental Stress Crack Resistance: >= 1000 hour
- Melt Flow: 0.46 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 24.1 MPa
- Tensile Strength, Yield: 30.3 MPa
$ 1713/MT
- Density: 0.948 g/cc
- ESCR 10% Igepal®: 20 hour
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 6.89 MPa
- Tensile Strength, Yield: 23.4 MPa
$ 1794/MT
- Density: 0.920 g/cc
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 2000 ppm
- Slip Level: 500 ppm
- Film Tensile Strength at Yield, MD: 10.3 MPa
$ 1476/MT
- Density: 0.923 g/cc
- Melt Flow: 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 1500 ppm
- Slip Level: 750 ppm
- Film Tensile Strength at Yield, MD: 11.0 MPa
$ 1592/MT
- Density: 0.914 g/cc
- Melt Flow: 22 g/10 min
- Hardness, Shore D: 40
- Tensile Strength at Break: 8.27 MPa
- Elongation at Break: 120 %
$ 1809/MT
- Density: 0.926 g/cc
- Vinyl Acetate Content: 2.9 %
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, TD: 6.83 MPa
- Film Elongation at Break, MD: 360 %
$ 2064/MT
- ESCR 100% Igepal®: >= 1000 hour
- ESCR 10% Igepal®: >= 1000 hour
- Tensile Strength, Yield: 19.3 MPa
- Elongation at Break: 700 %
- Elongation at Yield: 20 %
$ 1598/MT
- Density: 0.912 g/cc
- Thickness: 20.3 microns
- Melt Flow: 3.5 g/10 min
- Film Tensile Strength at Yield, MD: 7.52 MPa
- Film Tensile Strength at Yield, TD: 5.72 MPa
$ 2066/MT
- Density: 0.924 g/cc
- Melt Flow: 6.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 46 @Time 15.0 sec
- Tensile Strength at Break: 10.3 MPa
- Elongation at Break: 120 %
$ 1490/MT
- Density: 0.926 g/cc
- Melt Flow: 0.50 g/10 min
- Antiblock Level: 1500 ppm
- Slip Level: 833 ppm
- Film Elongation at Break, MD: 430 %
$ 1478/MT
- Density: 0.964 g/cc
- ESCR 10% Igepal®: 4.0 hour @Temperature 50.0 °C
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 26.2 MPa
- Elongation at Break: >= 100 %
$ 1681/MT
- Density: 0.961 g/cc
- Melt Flow: 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 490 %
- Elmendorf Tear Strength MD: 10 g
- Elmendorf Tear Strength TD: 810 g
$ 1723/MT
- Density: 0.923 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 1000 ppm
- Slip Level: 750 ppm
- Film Tensile Strength at Yield, MD: 11.0 MPa
$ 1531/MT
- Density: 0.922 g/cc
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 3500 ppm
- Slip Level: 1700 ppm
- Film Tensile Strength at Yield, MD: 10.3 MPa
$ 1667/MT
- Density: 0.948 g/cc
- ESCR 100% Igepal®: 10 hour
- ESCR 10% Igepal®: 8.0 hour
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 23.4 MPa
$ 1468/MT
- Density: 0.950 g/cc
- ESCR 100% Igepal®: 70 hour
- Melt Flow: 0.33 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 26.9 MPa
- Elongation at Break: 600 %
$ 1715/MT
- Density: 0.924 g/cc
- Melt Flow: 3.6 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 51 @Time 15.0 sec
- Tensile Strength at Break: 10.3 MPa
- Tensile Strength, Yield: 13.8 MPa
$ 2202/MT
- Density: 0.926 g/cc
- Melt Flow: 52 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 51
- Tensile Strength at Break: 15.4 MPa
- Elongation at Break: 40 %
$ 1537/MT
- Density: 0.888 g/cc
- Thickness: 25.4 microns
- Melt Flow: 2.2 g/10 min
- Film Tensile Strength at Yield, MD: 3.52 MPa
- Film Tensile Strength at Yield, TD: 3.10 MPa
$ 2274/MT
- Density: 0.917 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 8.27 MPa
- Film Tensile Strength at Yield, TD: 7.58 MPa
- Film Elongation at Break, MD: 340 %
$ 1561/MT
- Density: 0.952 g/cc
- Melt Flow: 19 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 25.5 MPa
- Elongation at Break: 270 %
- Flexural Modulus: 1.10 GPa
$ 1455/MT
- Density: 0.918 g/cc
- Melt Flow: 2.8 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 500 %
- Film Elongation at Break, TD: 810 %
- Elmendorf Tear Strength MD: 40 g
$ 1834/MT
- Density: 0.921 g/cc
- Melt Flow: 4.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Neck In: 3.80 cm
- Neck In: 4.10 cm
- Drawdown: 3.30 m/s
$ 1543/MT
- Density: 0.918 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 9.65 MPa
- Film Tensile Strength at Yield, TD: 9.65 MPa
- Film Elongation at Break, MD: 570 %
$ 1511/MT
- Density: 0.945 g/cc
- Apparent Bulk Density: 0.480 g/cc
- Melt Flow: 1.7 g/10 min
- Melt Flow: <= 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 28.3 MPa
$ 1889/MT
- Density: 0.925 g/cc
- ESCR 10% Igepal®: 330 hour
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 11.7 MPa
- Elongation at Break: 350 %
$ 2362/MT
- Density: 0.927 g/cc
- Melt Flow: 3.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 1000 ppm
- Slip Level: 750 ppm
- Film Tensile Strength at Yield, MD: 13.1 MPa
$ 1464/MT
- Density: 0.952 g/cc
- ESCR 100% Igepal®: 600 hour
- ESCR 10% Igepal®: 490 hour
- Melt Flow: 9.0 g/10 min @Load 21.6 kg, Temperature 190 °C
- Hardness, Shore D: 63 @Time 15.0 sec
$ 1762/MT
- Density: 0.924 g/cc
- Vinyl Acetate Content: 3.5 %
- Melt Flow: 1.3 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 2500 ppm
- Slip Level: 500 ppm
$ 1725/MT
- Density: 0.926 g/cc
- ESCR 10% Igepal®: 6.0 hour
- Melt Flow: 50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 10.3 MPa
- Elongation at Break: 100 %
$ 1485/MT
- Density: 0.925 g/cc
- Thickness: 38.1 microns
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.7 MPa
- Film Tensile Strength at Yield, TD: 13.8 MPa
$ 2003/MT
- Density: 0.937 g/cc
- ESCR 100% Igepal®: >= 1000 hour
- ESCR 10% Igepal®: 190 hour
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 17.9 MPa
$ 2544/MT
- Density: 0.915 g/cc
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 190 °C
- Neck In: 3.60 cm
- Neck In: 4.10 cm
- Drawdown: 4.00 m/s
$ 2314/MT
- Density: 0.9180 g/cc
- Melt Flow: 3.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 6.89 MPa
- Film Tensile Strength at Yield, TD: 6.76 MPa
- Film Elongation at Break, MD: 530 %
$ 1600/MT
- Density: 0.912 g/cc
- Melt Flow: 12 g/10 min
- Neck In: 4.30 cm
- Drawdown: 2.41 m/s
- Drawdown: 3.58 m/s
$ 1865/MT
- Density: 0.938 g/cc
- ESCR 100% Igepal®: >= 1000 hour
- ESCR 10% Igepal®: 150 hour
- Melt Flow: 3.3 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 17.93 MPa
$ 2301/MT
- Density: 0.920 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 2000 ppm
- Slip Level: 500 ppm
- Film Tensile Strength at Yield, MD: 9.65 MPa
$ 1770/MT
- Density: 0.920 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 9.65 MPa
- Film Tensile Strength at Yield, TD: 10.3 MPa
- Film Elongation at Break, MD: 540 %
$ 1635/MT
- Density: 0.926 g/cc
- Vinyl Acetate Content: 4.0 %
- Melt Flow: 0.28 g/10 min
- Film Elongation at Break, MD: 500 %
- Film Elongation at Break, TD: 650 %
$ 1530/MT
- Density: 0.895 g/cc
- Thickness: 20.3 microns
- Melt Flow: 3.5 g/10 min
- Film Tensile Strength at Yield, MD: 4.76 MPa
- Film Tensile Strength at Yield, TD: 4.21 MPa
$ 1728/MT
- Density: 0.946 g/cc
- ESCR 100% Igepal®: >= 1000 hour
- Melt Flow: 5.5 g/10 min
- Melt Flow: <= 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 24.1 MPa
$ 1673/MT
- Density: 0.918 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 2500 ppm
- Slip Level: 750 ppm
- Film Elongation at Break, MD: 480 %
$ 1543/MT
- Density: 0.888 g/cc
- Melt Flow: 2.2 g/10 min
- Film Tensile Strength at Yield, MD: 4.34 MPa
- Film Tensile Strength at Yield, TD: 3.24 MPa
- Film Elongation at Break, MD: 440 %
$ 2432/MT
- Density: 0.952 g/cc
- Environmental Stress Crack Resistance: 4.0 hour
- Melt Flow: 6.7 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 26.2 MPa
- Elongation at Break: 1300 %
$ 1507/MT
- Density: 0.922 g/cc
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 3500 ppm
- Slip Level: 1000 ppm
- Film Tensile Strength at Yield, MD: 10.3 MPa
$ 2402/MT
- Density: 0.922 g/cc
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 3500 ppm
- Slip Level: 1000 ppm
- Film Tensile Strength at Yield, MD: 10.3 MPa
$ 1678/MT
- Density: 0.922 g/cc
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 3500 ppm
- Slip Level: 1000 ppm
- Film Tensile Strength at Yield, MD: 10.3 MPa
$ 1556/MT
- Density: 0.923 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 4500 ppm
- Film Tensile Strength at Yield, MD: 10.3 MPa
- Film Tensile Strength at Yield, TD: 10.3 MPa
$ 2038/MT
- Density: 0.931 g/cc
- Melt Flow: 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, TD: 15.9 MPa
- Film Elongation at Break, MD: 450 %
- Film Elongation at Break, TD: 600 %
$ 1480/MT
- Density: 0.923 g/cc
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 11.7 MPa
- Film Elongation at Break, MD: 480 %
$ 2021/MT
- Density: 0.923 g/cc
- Thickness: 38.1 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 1000 ppm
- Slip Level: 750 ppm
$ 1474/MT
- Density: 0.923 g/cc
- Thickness: 38.1 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 1000 ppm
- Slip Level: 750 ppm
$ 1707/MT
- ESCR 100% Igepal®: 99 hour
- ESCR 10% Igepal®: >= 1000 hour
- Tensile Strength, Yield: 20.7 MPa
- Elongation at Break: 700 %
- Elongation at Yield: 20 %
$ 1452/MT
- Density: 0.923 g/cc
- Thickness: 38.1 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 1000 ppm
- Film Tensile Strength at Yield, MD: 11.0 MPa
$ 1856/MT
- Density: 0.923 g/cc
- Melt Flow: 3.8 g/10 min @Load 2.16 kg, Temperature 190 °C
- Neck In: 4.06 cm @Temperature 315 °C
- Neck In: 4.32 cm @Temperature 315 °C
- Drawdown: 4.50 m/s @Temperature 315 °C
- Melting Point: <= 228 °C
$ 2043/MT
- Density: 0.918 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 5000 ppm
- Slip Level: 850 ppm
- Film Tensile Strength at Yield, MD: 9.65 MPa
$ 1629/MT
- Thickness: 30.0 microns
- Coating Weight: >= 27.5 g/m²
- Coefficient of Friction: 0.30
- Film Tensile Strength at Break, MD: 34.5 MPa
- Film Tensile Strength at Break, TD: 150 MPa
$ 2284/MT
- Density: 0.917 g/cc
- Thickness: 25.4 microns
- Melt Flow: 0.90 g/10 min
- Film Tensile Strength at Yield, MD: 9.10 MPa
- Film Tensile Strength at Yield, TD: 9.38 MPa
$ 1703/MT
- Density: 0.928 g/cc
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 1000 ppm
- Slip Level: 750 ppm
- Film Elongation at Break, MD: 360 %
$ 1534/MT
- Density: 0.922 g/cc
- Melt Flow: 0.33 g/10 min
- Film Tensile Strength at Yield, MD: 11.7 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
- Film Elongation at Break, MD: 500 %
$ 1522/MT
- Density: 0.954 g/cc
- ESCR 100% Igepal®: >= 1000 hour
- Melt Flow: <= 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 5.0 g/10 min @Load 21.6 kg, Temperature 190 °C
- Tensile Strength, Yield: 28.3 MPa
$ 1553/MT
- Density: 0.925 g/cc
- Vinyl Acetate Content: 4.6 %
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 5000 ppm
- Slip Level: 1100 ppm
$ 1513/MT
- Density: 0.934 g/cc
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, TD: 17.2 MPa
- Film Elongation at Break, MD: 370 %
- Film Elongation at Break, TD: 610 %
$ 2223/MT
- Density: 0.953 g/cc
- Melt Flow: 0.25 g/10 min @Load 2.16 kg, Temperature 190 °C
- High Load Melt Index: 26 g/10 min @Load 21.6 kg, Temperature 190 °C
- Tensile Strength, Yield: 28.3 MPa
- 2% Secant Modulus: 1.24 GPa
$ 1756/MT
- Density: 0.935 g/cc
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 15.9 MPa
- Film Tensile Strength at Yield, TD: 17.9 MPa
- Film Elongation at Break, MD: 590 %
$ 1885/MT
- Density: 0.952 g/cc
- Melt Flow: 19 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 1.86 MPa
- Tensile Strength, Yield: 25.5 MPa
- Flexural Modulus: 1.10 GPa
$ 1832/MT
- Density: 0.918 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 2500 ppm
- Slip Level: 800 ppm
- Film Tensile Strength at Yield, MD: 9.65 MPa
$ 2261/MT
- Density: 0.927 g/cc
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 13.1 MPa
- Film Tensile Strength at Yield, TD: 15.2 MPa
- Film Elongation at Break, MD: 480 %
$ 2437/MT
- Density: 0.920 g/cc
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 9.65 MPa
- Film Tensile Strength at Yield, TD: 10.3 MPa
- Film Elongation at Break, MD: 470 %
$ 1649/MT
- Density: 0.935 g/cc
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 17.2 MPa
- Film Tensile Strength at Yield, TD: 19.3 MPa
- Film Elongation at Break, MD: 550 %
$ 1903/MT
- Density: 0.928 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 1000 ppm
- Slip Level: 750 ppm
- Film Elongation at Break, MD: 310 %
$ 1875/MT
- Density: 0.926 g/cc
- Melt Flow: 0.50 g/10 min
- Antiblock Level: 1800 ppm
- Slip Level: 330 ppm
- Film Elongation at Break, MD: 430 %
$ 1650/MT
- Density: 0.927 g/cc
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.3 MPa
- Film Tensile Strength at Yield, TD: 9.65 MPa
- Film Elongation at Break, MD: 530 %
Delivery Polyethylene (PE) Exxon Chemical
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
passenger boat for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.