$ 1489/MT
- Density: 1.18 g/cc
- Moisture Absorption at Equilibrium: 3.7 %
- Tensile Strength, Yield: 100 MPa
- Elongation at Yield: 40 %
- Tensile Modulus: 3.30 GPa
$ 1978/MT
- Density: 1.25 g/cc
- Moisture Absorption at Equilibrium: 3.2 %
- Tensile Strength, Yield: 90.0 MPa
- Elongation at Yield: 25 %
- Tensile Modulus: 2.90 GPa
$ 1448/MT
- Density: 1.18 g/cc
- Moisture Absorption: 3.70 %
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Tensile Strength, Yield: 55.0 MPa
$ 1620/MT
- Density: 1.54 g/cc
- Water Absorption: 7.8 %
- Moisture Absorption at Equilibrium: 2.2 %
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Flow: 0.013 cm/cm
$ 1496/MT
- Density: 1.87 g/cc
- Moisture Absorption at Equilibrium: 1.1 %
- Tensile Strength at Break: 150 MPa
- Elongation at Break: 1.3 %
- Tensile Modulus: 16.0 GPa
$ 1785/MT
- Density: 1.87 g/cc
- Moisture Absorption at Equilibrium: 1.1 %
- Tensile Strength at Break: 200 MPa
- Elongation at Break: 1.5 %
- Tensile Modulus: 18.0 GPa
$ 2120/MT
- Density: 1.31 g/cc
- Moisture Absorption at Equilibrium: 2.1 %
- Tensile Strength at Break: 140 MPa
- Elongation at Break: 5.0 %
- Flexural Modulus: 6.30 GPa
$ 1480/MT
- Density: 1.76 g/cc
- Tensile Strength at Break: 170 MPa
- Elongation at Break: 3.0 %
- Tensile Modulus: 12.0 GPa
- Charpy Impact Unnotched: 10.0 J/cm²
$ 1450/MT
- Density: 1.65 g/cc
- Moisture Absorption at Equilibrium: 1.2 %
- Tensile Strength at Break: 145 MPa
- Elongation at Break: 3.0 %
- Tensile Modulus: 11.0 GPa
$ 1655/MT
- Density: 1.52 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
- Tensile Strength, Ultimate: 55.0 MPa
- Elongation at Break: 2.0 %
$ 2167/MT
- Density: 1.51 g/cc
- Moisture Absorption: 2.20 %
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength, Ultimate: 140 MPa
$ 1684/MT
- Density: 1.41 g/cc
- Water Absorption: 9.5 %
- Moisture Absorption at Equilibrium: 2.6 %
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Flow: 0.013 cm/cm
$ 2546/MT
- Density: 1.42 g/cc
- Water Absorption: 9.5 %
- Moisture Absorption at Equilibrium: 2.6 %
- Tensile Strength at Break: 70.0 MPa
- Elongation at Break: 6.0 %
$ 1565/MT
- Density: 1.68 g/cc
- Water Absorption: 5.9 %
- Moisture Absorption at Equilibrium: 1.6 %
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Flow: 0.011 cm/cm
$ 1702/MT
- Density: 1.41 g/cc
- Viscosity Test: 85 cm³/g
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Tensile Strength at Break: 210 MPa
$ 1595/MT
- Density: 1.26 g/cc
- Moisture Absorption: 3.00 %
- Linear Mold Shrinkage, Flow: 0.022 cm/cm
- Linear Mold Shrinkage, Transverse: 0.022 cm/cm
- Tensile Strength, Ultimate: 80.0 MPa
$ 1583/MT
- Density: 1.62 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0030 cm/cm
- Tensile Strength, Ultimate: 55.0 MPa
- Elongation at Break: 0.60 %
$ 1857/MT
- Density: 1.68 g/cc
- Water Absorption: 5.9 %
- Moisture Absorption at Equilibrium: 1.6 %
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Flow: 0.011 cm/cm
$ 2211/MT
- Density: 1.76 g/cc
- Tensile Strength at Break: 255 MPa
- Elongation at Break: 2.0 %
- Tensile Modulus: 20.0 GPa
- Charpy Impact Unnotched: 9.00 J/cm²
$ 1578/MT
- Density: 1.54 g/cc
- Moisture Absorption at Equilibrium: 2.2 %
- Tensile Strength at Break: 190 MPa
- Elongation at Break: 3.7 %
- Tensile Modulus: 8.90 GPa
$ 2224/MT
- Density: 1.54 g/cc
- Water Absorption: 7.8 %
- Moisture Absorption at Equilibrium: 2.2 %
- Viscosity Test: 145 cm³/g
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
$ 1569/MT
- Density: 1.87 g/cc
- Moisture Absorption at Equilibrium: 1.1 %
- Viscosity Test: 70 cm³/g
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
$ 1852/MT
- Density: 1.18 g/cc
- Water Absorption: 13 %
- Moisture Absorption at Equilibrium: 3.7 %
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
$ 1908/MT
- Density: 1.18 g/cc
- Water Absorption: 13 %
- Moisture Absorption at Equilibrium: 3.7 %
- Viscosity Test: 185 cm³/g
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
$ 1795/MT
- Density: 1.37 g/cc
- Moisture Absorption: 2.00 %
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Tensile Strength, Yield: 45.0 MPa
$ 2592/MT
- Density: 1.21 g/cc
- Tensile Modulus: 1.00 GPa
- Melting Point: 295 °C
- Injection molding: Yes
$ 2427/MT
- Density: 1.21 g/cc
- Viscosity Test: 180 cm³/g
- Tensile Modulus: 2.80 GPa
- CTE, linear, Parallel to Flow: 80.0 µm/m-°C @Temperature 20.0 °C
- CTE, linear, Transverse to Flow: 100 µm/m-°C @Temperature 20.0 °C
$ 2432/MT
- Density: 1.43 g/cc
- Moisture Absorption: 2.35 %
- Linear Mold Shrinkage, Flow: 0.015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.015 cm/cm
- Tensile Strength, Yield: 80.0 MPa
$ 2569/MT
- Density: 1.18 g/cc
- Tensile Strength, Yield: 55.0 MPa
- Elongation at Yield: >= 55 %
- Tensile Modulus: 1.00 GPa
- Charpy Impact Unnotched: NB
$ 1717/MT
- Density: 1.18 g/cc
- Water Absorption: 13.5 %
- Moisture Absorption at Equilibrium: 3.7 %
- Viscosity Test: 175 cm³/g
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
$ 2191/MT
- Density: 1.18 g/cc
- Tensile Strength, Yield: 55.0 MPa
- Elongation at Yield: >= 55 %
- Tensile Modulus: 1.00 GPa
- Charpy Impact Unnotched: NB
$ 1458/MT
- Density: 1.18 g/cc
- Moisture Absorption at Equilibrium: 3.7 %
- Tensile Strength, Yield: 100 MPa
- Elongation at Yield: 40 %
- Tensile Modulus: 3.30 GPa
$ 1774/MT
- Density: 1.18 g/cc
- Water Absorption: 13.5 %
- Moisture Absorption at Equilibrium: 3.7 %
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
$ 1575/MT
- Density: 1.10 g/cc
- Tensile Strength, Yield: 45.0 MPa
- Elongation at Yield: >= 50 %
- Tensile Modulus: 0.600 GPa
- Charpy Impact Unnotched: NB
$ 1518/MT
- Density: 1.10 g/cc
- Moisture Absorption at Equilibrium: 3.0 %
- Tensile Strength, Yield: 60.0 MPa
- Elongation at Yield: >= 50 %
- Tensile Modulus: 1.85 GPa
$ 2292/MT
- Density: 1.10 g/cc
- Water Absorption: 11 %
- Moisture Absorption at Equilibrium: 3.0 %
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
$ 2434/MT
- Density: 1.25 g/cc
- Water Absorption: 11.4 %
- Moisture Absorption at Equilibrium: 3.2 %
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
$ 1741/MT
- Density: 1.25 g/cc
- Water Absorption: 11.4 %
- Moisture Absorption at Equilibrium: 3.2 %
- Viscosity Test: 180 cm³/g
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
$ 1526/MT
- Density: 1.18 g/cc
- Tensile Strength, Yield: 55.0 MPa
- Elongation at Yield: >= 55 %
- Tensile Modulus: 1.00 GPa
- Charpy Impact Unnotched: NB
$ 1446/MT
- Density: 1.18 g/cc
- Moisture Absorption at Equilibrium: 3.7 %
- Tensile Strength, Yield: 100 MPa
- Elongation at Yield: 40 %
- Tensile Modulus: 3.30 GPa
$ 2073/MT
- Density: 1.18 g/cc
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Tensile Strength, Yield: 55.0 MPa
- Elongation at Break: >= 50 %
$ 1829/MT
- Density: 1.18 g/cc
- Viscosity Test: 220 cm³/g
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Tensile Strength, Yield: 100 MPa
$ 1469/MT
- Density: 1.18 g/cc
- Water Absorption: 13.5 %
- Moisture Absorption at Equilibrium: 3.7 %
- Viscosity Test: 185 cm³/g
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
$ 1925/MT
- Density: 1.10 g/cc
- Water Absorption: 11 %
- Moisture Absorption at Equilibrium: 3.0 %
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
$ 2356/MT
- Density: 1.51 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength at Break: 230 MPa
- Elongation at Break: 3.0 %
$ 1834/MT
- Density: 1.87 g/cc
- Moisture Absorption at Equilibrium: 1.1 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
- Melting Point: 295 °C
$ 1872/MT
- Density: 1.28 g/cc
- Moisture Absorption: 2.60 %
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength, Ultimate: 150 MPa
$ 2193/MT
- Density: 1.56 g/cc
- Moisture Absorption at Equilibrium: 1.3 %
- Tensile Strength at Break: 170 MPa
- Elongation at Break: 2.0 %
- Tensile Modulus: 12.0 GPa
$ 1982/MT
- Density: 1.63 g/cc
- Tensile Strength, Ultimate: 210 MPa
- Elongation at Break: 3.0 %
- Tensile Modulus: 13.0 GPa
- Flexural Modulus: 11.5 GPa
$ 1959/MT
- Density: 1.51 g/cc
- Moisture Absorption at Equilibrium: 2.2 %
- Tensile Strength at Break: 230 MPa
- Elongation at Break: 3.0 %
- Tensile Modulus: 13.0 GPa
$ 1994/MT
- Density: 1.56 g/cc
- Tensile Strength at Break: 150 MPa
- Elongation at Break: 2.0 %
- Tensile Modulus: 9.20 GPa
- Charpy Impact, Notched: 0.800 J/cm² @Temperature 23.0 °C
$ 1716/MT
- Density: 1.22 g/cc
- Moisture Absorption: 3.15 %
- Tensile Strength, Ultimate: 110 MPa
- Tensile Strength, Ultimate: 185 MPa
- Elongation at Break: 2.0 %
$ 2178/MT
- Density: 1.51 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength at Break: 140 MPa
- Elongation at Break: 6.0 %
$ 1648/MT
- Density: 1.69 g/cc
- Tensile Strength, Ultimate: 225 MPa
- Elongation at Break: 2.0 %
- Tensile Modulus: 16.0 GPa
- Izod Impact Resistance: 1.80 J/cm² @Temperature 23.0 °C
$ 1746/MT
- Density: 1.62 g/cc
- Moisture Absorption at Equilibrium: 1.8 %
- Tensile Strength at Break: 250 MPa
- Elongation at Break: 2.7 %
- Tensile Modulus: 16.0 GPa
$ 2443/MT
- Density: 1.41 g/cc
- Water Absorption: 9.5 %
- Moisture Absorption at Equilibrium: 2.6 %
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Flow: 0.013 cm/cm
$ 2550/MT
- Density: 1.18 g/cc
- Moisture Absorption: 3.70 %
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Tensile Strength, Yield: 55.0 MPa
$ 1631/MT
- Density: 1.29 g/cc
- Tensile Strength at Break: 70.0 MPa
- Elongation at Break: 8.0 %
- Tensile Modulus: 2.80 GPa
- Melting Point: 295 °C
$ 1923/MT
- Density: 1.22 g/cc
- Moisture Absorption: 3.15 %
- Tensile Strength, Ultimate: 110 MPa
- Tensile Strength, Ultimate: 185 MPa
- Elongation at Break: 2.0 %
$ 1546/MT
- Density: 1.22 g/cc
- Moisture Absorption: 3.10 %
- Tensile Strength, Ultimate: 115 MPa
- Elongation at Break: 4.0 %
- Tensile Modulus: 4.50 GPa
$ 1536/MT
- Density: 1.40 g/cc
- Moisture Absorption: 2.40 %
- Tensile Strength, Ultimate: 180 MPa
- Elongation at Break: 2.0 %
- Tensile Modulus: 9.00 GPa
$ 1584/MT
- Density: 1.18 g/cc
- Moisture Absorption: 3.70 %
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Tensile Strength, Yield: 55.0 MPa
$ 1471/MT
- Density: 1.43 g/cc
- Moisture Absorption at Equilibrium: 2.6 %
- Tensile Strength at Break: 115 MPa
- Elongation at Break: 7.0 %
- Flexural Modulus: 6.00 GPa
$ 2390/MT
- Density: 1.62 g/cc
- Water Absorption: 7.0 %
- Moisture Absorption at Equilibrium: 1.8 %
- Viscosity Test: 140 cm³/g
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
$ 1658/MT
- Density: 1.41 g/cc
- Moisture Absorption: 2.60 %
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Tensile Strength, Ultimate: 115 MPa
$ 2054/MT
- Density: 1.56 g/cc
- Moisture Absorption at Equilibrium: 1.3 %
- Tensile Strength at Break: 140 MPa
- Elongation at Break: 3.0 %
- Tensile Modulus: 9.00 GPa
$ 1622/MT
- Density: 1.62 g/cc
- Tensile Strength at Break: 160 MPa
- Elongation at Break: 5.0 %
- Tensile Modulus: 10.0 GPa
- Charpy Impact Unnotched: 10.0 J/cm²
$ 1946/MT
- Density: 1.77 g/cc
- Water Absorption: 4.5 %
- Moisture Absorption at Equilibrium: 1.3 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm
$ 1542/MT
- Density: 1.27 g/cc
- Moisture Absorption: 2.90 %
- Linear Mold Shrinkage, Flow: 0.015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.015 cm/cm
- Tensile Strength, Ultimate: 90.0 MPa
$ 1792/MT
- Density: 1.43 g/cc
- Moisture Absorption at Equilibrium: 2.6 %
- Tensile Strength at Break: 205 MPa
- Elongation at Break: 3.5 %
- Flexural Modulus: 9.00 GPa
$ 2471/MT
- Density: 1.77 g/cc
- Water Absorption: 4.5 %
- Moisture Absorption at Equilibrium: 1.3 %
- Viscosity Test: 150 cm³/g
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
$ 1791/MT
- Density: 1.77 g/cc
- Water Absorption: 4.5 %
- Moisture Absorption at Equilibrium: 1.3 %
- Viscosity Test: 80 cm³/g
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
$ 1767/MT
- Density: 1.41 g/cc
- Tensile Strength at Break: 115 MPa
- Elongation at Break: 7.0 %
- Tensile Modulus: 6.00 GPa
- Charpy Impact Unnotched: 9.00 J/cm²
$ 1559/MT
- Density: 1.43 g/cc
- Tensile Strength at Break: 115 MPa
- Elongation at Break: 7.0 %
- Tensile Modulus: 6.00 GPa
- Flexural Modulus: 6.00 GPa
$ 2015/MT
- Density: 1.54 g/cc
- Tensile Strength at Break: 110 MPa
- Elongation at Break: 7.0 %
- Tensile Modulus: 4.10 GPa
- Charpy Impact, Notched: 1.50 J/cm²
$ 2036/MT
- Density: 1.68 g/cc
- Tensile Strength at Break: 180 MPa
- Elongation at Break: 2.5 %
- Tensile Modulus: 12.0 GPa
- Charpy Impact, Notched: 0.900 J/cm² @Temperature -30.0 °C
$ 1524/MT
- Density: 1.32 g/cc
- Moisture Absorption: 2.40 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
- Tensile Strength, Ultimate: 170 MPa
$ 1498/MT
- Density: 1.29 g/cc
- Water Absorption: 9.5 %
- Moisture Absorption at Equilibrium: 3.1 %
- Tensile Strength at Break: 70.0 MPa
- Elongation at Break: 8.0 %
$ 1577/MT
- Density: 1.82 g/cc
- Water Absorption: 4.5 %
- Moisture Absorption at Equilibrium: 1.2 %
- Viscosity Test: 140 cm³/g
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
$ 1670/MT
- Density: 1.25 g/cc
- Tensile Strength, Yield: 50.0 MPa
- Elongation at Yield: >= 50 %
- Tensile Modulus: 1.00 GPa
- Charpy Impact, Notched: 3.00 J/cm²
$ 1632/MT
- Density: 1.62 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0030 cm/cm
- Tensile Strength, Ultimate: 55.0 MPa
- Elongation at Break: 0.60 %
$ 1468/MT
- Density: 1.77 g/cc
- Tensile Strength at Break: 130 MPa
- Elongation at Break: 2.5 %
- Tensile Modulus: 12.0 GPa
- Charpy Impact Unnotched: 7.00 J/cm²
$ 1867/MT
- Density: 1.77 g/cc
- Moisture Absorption at Equilibrium: 1.3 %
- Tensile Strength at Break: 190 MPa
- Elongation at Break: 1.7 %
- Tensile Modulus: 15.0 GPa
$ 1957/MT
- Density: 1.53 g/cc
- Moisture Absorption: 2.10 %
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength, Ultimate: 100 MPa
$ 1491/MT
- Density: 1.52 g/cc
- Moisture Absorption at Equilibrium: 2.1 %
- Tensile Strength at Break: 140 MPa
- Elongation at Break: 3.0 %
- Tensile Modulus: 8.00 GPa
$ 2014/MT
- Density: 1.68 g/cc
- Tensile Strength at Break: 125 MPa
- Elongation at Break: 3.5 %
- Tensile Modulus: 8.00 GPa
- Charpy Impact Unnotched: 6.00 J/cm²
$ 1713/MT
- Density: 1.68 g/cc
- Moisture Absorption at Equilibrium: 1.6 %
- Tensile Strength at Break: 180 MPa
- Elongation at Break: 2.5 %
- Tensile Modulus: 12.0 GPa
$ 2341/MT
- Density: 1.82 g/cc
- Tensile Strength at Break: 130 MPa
- Elongation at Break: 3.0 %
- Tensile Modulus: 12.0 GPa
- Charpy Impact Unnotched: 7.50 J/cm²
$ 1616/MT
- Density: 1.82 g/cc
- Moisture Absorption at Equilibrium: 1.2 %
- Tensile Strength at Break: 200 MPa
- Elongation at Break: 2.0 %
- Tensile Modulus: 17.0 GPa
$ 1975/MT
- Density: 1.77 g/cc
- Moisture Absorption: 1.25 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength, Ultimate: 140 MPa
$ 1567/MT
- Density: 1.66 g/cc
- Moisture Absorption: 1.60 %
- Linear Mold Shrinkage, Flow: 0.0080 cm/cm
- Linear Mold Shrinkage, Transverse: 0.017 cm/cm
- Tensile Strength, Ultimate: 120 MPa
$ 1648/MT
- Density: 1.29 g/cc
- Water Absorption: 9.5 %
- Moisture Absorption at Equilibrium: 3.1 %
- Viscosity Test: 150 cm³/g
- Tensile Strength at Break: 140 MPa
$ 1482/MT
- Density: 1.41 g/cc
- Moisture Absorption at Equilibrium: 2.6 %
- Tensile Strength at Break: 210 MPa
- Elongation at Break: 4.0 %
- Tensile Modulus: 10.0 GPa
$ 1647/MT
- Density: 1.82 g/cc
- Water Absorption: 4.5 %
- Moisture Absorption at Equilibrium: 1.2 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm
$ 2053/MT
- Density: 1.51 g/cc
- Water Absorption: 8.0 %
- Moisture Absorption at Equilibrium: 2.2 %
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Flow: 0.011 cm/cm
$ 1656/MT
- Density: 1.31 g/cc
- Tensile Strength at Break: 85.0 MPa
- Elongation at Break: 10 %
- Flexural Modulus: 3.20 GPa
- Melting Point: 295 °C
$ 1716/MT
- Density: 1.29 g/cc
- Tensile Strength at Break: 140 MPa
- Elongation at Break: 4.0 %
- Tensile Modulus: 6.10 GPa
- CTE, linear: 30.0 µm/m-°C @Temperature 20.0 °C
$ 1636/MT
- Density: 1.34 g/cc
- Moisture Absorption: 2.60 %
- Tensile Strength, Ultimate: 170 MPa
- Elongation at Break: 1.8 %
- Tensile Modulus: 8.00 GPa
$ 1702/MT
- Density: 1.35 g/cc
- Moisture Absorption: 2.25 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm
- Tensile Strength, Ultimate: 160 MPa
$ 1469/MT
- Density: 1.42 g/cc
- Moisture Absorption: 2.00 %
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.012 cm/cm
- Tensile Strength, Ultimate: 65.0 MPa
$ 1451/MT
- Density: 1.35 g/cc
- Moisture Absorption: 2.80 %
- Tensile Strength, Ultimate: 180 MPa
- Elongation at Break: 3.0 %
- Tensile Modulus: 9.00 GPa
$ 1506/MT
- Density: 1.52 g/cc
- Moisture Absorption at Equilibrium: 2.1 %
- Viscosity Test: 145 cm³/g
- Linear Mold Shrinkage, Flow: 0.010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.015 cm/cm
$ 1631/MT
- Density: 1.47 g/cc
- Moisture Absorption: 2.90 %
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength, Ultimate: 110 MPa
$ 1995/MT
- Density: 1.62 g/cc
- Moisture Absorption: 1.85 %
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength, Ultimate: 170 MPa
$ 1464/MT
- Density: 1.32 g/cc
- Moisture Absorption: 2.60 %
- Tensile Strength, Ultimate: 120 MPa
- Tensile Strength, Ultimate: 185 MPa
- Tensile Strength, Ultimate: 76.0 MPa @Temperature 200 °C
$ 1848/MT
- Density: 1.65 g/cc
- Moisture Absorption at Equilibrium: 1.2 %
- Tensile Strength at Break: 180 MPa
- Elongation at Break: 2.0 %
- Tensile Modulus: 14.0 GPa
$ 1612/MT
- Density: 1.62 g/cc
- Moisture Absorption: 1.85 %
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength, Ultimate: 160 MPa
$ 1580/MT
- Density: 1.51 g/cc
- Water Absorption: 8.0 %
- Moisture Absorption at Equilibrium: 2.2 %
- Viscosity Test: 145 cm³/g
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
$ 2314/MT
- Density: 1.62 g/cc
- Water Absorption: 7.0 %
- Moisture Absorption at Equilibrium: 1.8 %
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm
$ 1737/MT
- Density: 1.41 g/cc
- Moisture Absorption: 2.60 %
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Tensile Strength, Ultimate: 115 MPa
$ 1972/MT
- Density: 1.41 g/cc
- Tensile Strength at Break: 115 MPa
- Elongation at Break: 6.0 %
- Tensile Modulus: 6.00 GPa
- Charpy Impact Unnotched: 9.00 J/cm²
$ 2057/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Tensile Strength at Break: 115 MPa
- Elongation at Break: 7.0 %
$ 1450/MT
- Density: 1.87 g/cc
- Moisture Absorption at Equilibrium: 1.1 %
- Viscosity Test: 70 cm³/g
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
$ 2129/MT
- Density: 1.77 g/cc
- Water Absorption: 4.5 %
- Moisture Absorption at Equilibrium: 1.3 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm
$ 1515/MT
- Density: 1.47 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength, Ultimate: 50.0 MPa
- Elongation at Break: 0.60 %
$ 1463/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Tensile Strength at Break: 210 MPa
- Elongation at Break: 4.0 %
$ 1681/MT
- Density: 1.43 g/cc
- Moisture Absorption at Equilibrium: 2.6 %
- Tensile Strength at Break: 205 MPa
- Elongation at Break: 3.5 %
- Tensile Modulus: 10.5 GPa
$ 1446/MT
- Density: 1.56 g/cc
- Tensile Strength at Break: 100 MPa
- Elongation at Break: 4.0 %
- Tensile Modulus: 6.00 GPa
- Charpy Impact, Notched: 0.800 J/cm² @Temperature -30.0 °C
$ 1936/MT
- Density: 1.48 g/cc
- Tensile Strength, Ultimate: 105 MPa
- Tensile Strength, Ultimate: 190 MPa
- Elongation at Break: 3.2 %
- Elongation at Break: 6.0 %
$ 2092/MT
- Density: 1.41 g/cc
- Water Absorption: 9.5 %
- Moisture Absorption at Equilibrium: 2.6 %
- Viscosity Test: 145 cm³/g
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
$ 1772/MT
- Density: 1.76 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
- Tensile Strength at Break: 170 MPa
- Elongation at Break: 3.0 %
$ 1628/MT
- Density: 1.41 g/cc
- Water Absorption: 9.5 %
- Moisture Absorption at Equilibrium: 2.6 %
- Viscosity Test: 145 cm³/g
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
$ 2151/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Flow: 0.013 cm/cm
- Tensile Strength at Break: 115 MPa
- Elongation at Break: 6.0 %
$ 1622/MT
- Density: 1.68 g/cc
- Tensile Strength at Break: 125 MPa
- Elongation at Break: 3.5 %
- Tensile Modulus: 8.00 GPa
- Charpy Impact, Notched: 0.900 J/cm² @Temperature -30.0 °C
$ 1700/MT
- Density: 1.68 g/cc
- Water Absorption: 5.9 %
- Moisture Absorption at Equilibrium: 1.6 %
- Viscosity Test: 145 cm³/g
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
$ 1494/MT
- Density: 1.52 g/cc
- Moisture Absorption at Equilibrium: 2.1 %
- Linear Mold Shrinkage, Flow: 0.010 cm/cm
- Linear Mold Shrinkage, Flow: 0.015 cm/cm
- Melting Point: 295 °C
$ 1606/MT
- Density: 1.62 g/cc
- Moisture Absorption: 2.20 %
- Tensile Strength, Ultimate: 135 MPa
- Tensile Strength, Ultimate: 240 MPa
- Tensile Strength, Ultimate: 60.0 MPa @Temperature 200 °C
$ 1808/MT
- Density: 1.42 g/cc
- Water Absorption: 9.5 %
- Moisture Absorption at Equilibrium: 2.6 %
- Viscosity Test: 145 cm³/g
- Tensile Strength at Break: 140 MPa
$ 1945/MT
- Density: 1.22 g/cc
- Moisture Absorption: 3.15 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength, Ultimate: 110 MPa
$ 1877/MT
- Density: 1.63 g/cc
- Moisture Absorption: 1.80 %
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0125 cm/cm
- Tensile Strength, Ultimate: 160 MPa
$ 1943/MT
- Density: 1.41 g/cc
- Tensile Strength at Break: 210 MPa
- Elongation at Break: 3.0 %
- Tensile Modulus: 10.0 GPa
- Charpy Impact Unnotched: 6.00 J/cm²
$ 1624/MT
- Density: 1.18 g/cc
- Moisture Absorption: 3.70 %
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Tensile Strength, Yield: 55.0 MPa
Delivery Nylon 46 DSM Engineering Plastics
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
lng tankers for sale france. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.