$ 1949/MT
- Density: 1.40 g/cc
- Water Absorption: 5.9 %
- Moisture Absorption at Equilibrium: 1.8 %
- Tensile Strength at Break: 195 MPa
- Elongation at Break: 3.0 %
$ 1519/MT
- Density: 1.10 g/cc
- Water Absorption: 9.0 %
- Moisture Absorption at Equilibrium: 3.0 %
- Charpy Impact Unnotched: NB @Temperature -30.0 °C
- Charpy Impact Unnotched: NB @Temperature 23.0 °C
$ 1824/MT
- Density: 1.23 g/cc
- Water Absorption: 7.6 %
- Moisture Absorption at Equilibrium: 2.3 %
- Tensile Strength at Break: 130 MPa
- Elongation at Break: 3.5 %
$ 1872/MT
- Density: 1.36 g/cc
- Water Absorption: 6.8 %
- Moisture Absorption at Equilibrium: 2.0 %
- Tensile Strength at Break: 90.0 MPa
- Elongation at Break: 2.5 %
$ 1463/MT
- Density: 1.27 g/cc
- Water Absorption: 7.2 %
- Moisture Absorption at Equilibrium: 2.15 %
- Tensile Strength at Break: 87.0 MPa
- Elongation at Break: 5.5 %
$ 2525/MT
- Density: 1.07 g/cc
- Water Absorption: 8.5 %
- Moisture Absorption at Equilibrium: 2.3 %
- Charpy Impact Unnotched: NB @Temperature -30.0 °C
- Charpy Impact Unnotched: NB @Temperature 23.0 °C
$ 2533/MT
- Density: 1.13 g/cc
- Water Vapor Transmission: 35.0 g/m²/day @Temperature 23.0 °C
- Oxygen Transmission: 1.05 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Oxygen Transmission: 1.55 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Viscosity: 1.45e+6 cP @Temperature 260 °C
$ 1503/MT
- Density: 1.13 g/cc
- Water Vapor Transmission: 35.0 g/m²/day @Temperature 23.0 °C
- Oxygen Transmission: 1.30 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Oxygen Transmission: 1.90 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Viscosity: 1.60e+6 cP @Temperature 260 °C
$ 1601/MT
- Density: 1.23 g/cc
- Water Absorption: 7.6 %
- Moisture Absorption at Equilibrium: 2.3 %
- Tensile Strength at Break: 70.0 MPa
- Elongation at Break: 6.0 %
$ 1499/MT
- Density: 1.13 g/cc
- Water Absorption: 9.0 %
- Moisture Absorption at Equilibrium: 2.5 %
- Tensile Strength, Yield: 55.0 MPa
- Elongation at Break: >= 50 %
$ 1979/MT
- Density: 1.53 g/cc
- Water Absorption: 6.2 %
- Moisture Absorption at Equilibrium: 1.7 %
- Melt Flow: 33.66 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength at Break: 70.0 MPa
$ 1497/MT
- Density: 1.13 g/cc
- Viscosity: 150000 cP @Shear Rate 1000 1/s, Temperature 290 °C
- Viscosity: 175000 cP @Shear Rate 1000 1/s, Temperature 260 °C
- Viscosity: 175000 cP @Shear Rate 0.100 1/s, Temperature 290 °C
- Viscosity: 200000 cP @Shear Rate 1000 1/s, Temperature 230 °C
$ 1483/MT
- Density: 1.40 g/cc
- Water Absorption: 5.9 %
- Moisture Absorption at Equilibrium: 1.8 %
- Tensile Strength at Break: 195 MPa
- Elongation at Break: 3.0 %
$ 1824/MT
- Density: 1.35 g/cc
- Water Absorption: 6.3 %
- Moisture Absorption at Equilibrium: 1.9 %
- Tensile Strength at Break: 185 MPa
- Elongation at Break: 3.5 %
$ 1667/MT
- Density: 1.29 g/cc
- Moisture Absorption: 2.30 %
- Tensile Strength, Ultimate: 38.0 MPa
- Tensile Strength, Ultimate: 77.0 MPa
- Elongation at Break: 4.0 %
$ 1552/MT
- Density: 1.13 g/cc
- Water Vapor Transmission: 35.0 g/m²/day @Temperature 23.0 °C
- Oxygen Transmission: 1.15 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Oxygen Transmission: 1.65 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Viscosity: 2.25e+6 cP @Temperature 260 °C
$ 1556/MT
- Density: 1.13 g/cc
- Water Absorption: 9.5 %
- Moisture Absorption: 2.50 %
- Viscosity Test: 450 cm³/g
- Tensile Strength, Yield: 85.0 MPa
$ 2103/MT
- Density: 1.38 g/cc
- Water Absorption: 6.3 %
- Moisture Absorption at Equilibrium: 1.9 %
- Tensile Strength at Break: 110 MPa
- Elongation at Break: 5.0 %
$ 1825/MT
- Density: 1.54 g/cc
- Moisture Absorption: 1.90 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength, Ultimate: 135 MPa
$ 1921/MT
- Density: 1.23 g/cc
- Water Absorption: 7.6 %
- Moisture Absorption at Equilibrium: 2.3 %
- Tensile Strength at Break: 70.0 MPa
- Elongation at Break: 6.0 %
$ 2358/MT
- Density: 1.14 g/cc
- Moisture Absorption: 3.50 %
- Viscosity: 70000 cP @Shear Rate 10000 1/s, Temperature 240 °C
- Viscosity: 70000 cP @Shear Rate 10000 1/s, Temperature 260 °C
- Viscosity: 70000 cP @Shear Rate 10000 1/s, Temperature 280 °C
$ 1745/MT
- Density: 1.13 g/cc
- Water Absorption: 9.0 %
- Moisture Absorption at Equilibrium: 2.5 %
- Tensile Strength, Yield: 95.0 MPa
- Elongation at Break: 15 %
$ 2207/MT
- Density: 1.21 g/cc
- Water Absorption: 7.5 %
- Moisture Absorption: 2.00 %
- Linear Mold Shrinkage, Flow: 0.010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
$ 1950/MT
- Density: 1.17 g/cc
- Water Absorption: 9.0 %
- Moisture Absorption at Equilibrium: 2.5 %
- Tensile Strength, Yield: 40.0 MPa
- Elongation at Break: >= 50 %
$ 1591/MT
- Density: 1.35 g/cc
- Water Absorption: 6.3 %
- Moisture Absorption at Equilibrium: 1.9 %
- Tensile Strength at Break: 110 MPa
- Elongation at Break: 5.0 %
$ 1620/MT
- Density: 1.66 g/cc
- Water Absorption: 3.6 %
- Moisture Absorption at Equilibrium: 1.0 %
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
$ 1538/MT
- Density: 1.45 g/cc
- Water Absorption: 5.5 %
- Moisture Absorption: 1.70 %
- Linear Mold Shrinkage, Flow: 0.0034 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0083 cm/cm
$ 1822/MT
- Density: 1.13 g/cc
- Water Vapor Transmission: 35.0 g/m²/day @Temperature 23.0 °C
- Oxygen Transmission: 1.30 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Oxygen Transmission: 1.90 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Viscosity: 1.12e+6 cP @Temperature 260 °C
$ 2272/MT
- Density: 1.13 g/cc
- Water Vapor Transmission: 35.0 g/m²/day @Temperature 23.0 °C
- Oxygen Transmission: 1.30 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Oxygen Transmission: 1.90 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Viscosity: 1.12e+6 cP @Temperature 260 °C
$ 1552/MT
- Density: 1.13 g/cc
- Water Vapor Transmission: 35.0 g/m²/day @Temperature 23.0 °C
- Oxygen Transmission: 1.30 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Oxygen Transmission: 1.90 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Viscosity: 1.12e+6 cP @Temperature 260 °C
$ 1809/MT
- Density: 1.38 g/cc
- Water Absorption: 6.3 %
- Moisture Absorption at Equilibrium: 1.9 %
- Tensile Strength at Break: 180 MPa
- Elongation at Break: 3.5 %
$ 1879/MT
- Density: 1.07 g/cc
- Moisture Absorption: 2.80 %
- Linear Mold Shrinkage, Flow: 0.015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Tensile Strength, Yield: 30.0 MPa
$ 1527/MT
- Density: 1.66 g/cc
- Water Absorption: 3.6 %
- Moisture Absorption at Equilibrium: 1.0 %
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Flow: 0.0080 cm/cm
$ 1511/MT
- Density: 1.27 g/cc
- Water Absorption: 8.0 %
- Moisture Absorption at Equilibrium: 2.4 %
- Tensile Strength at Break: 135 MPa
- Elongation at Break: 4.0 %
$ 1973/MT
- Density: 1.13 g/cc
- Moisture Absorption: 3.20 %
- Linear Mold Shrinkage, Flow: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Tensile Strength, Yield: 45.0 MPa
$ 2089/MT
- Density: 1.13 g/cc
- Water Vapor Transmission: 35.0 g/m²/day @Temperature 23.0 °C
- Oxygen Transmission: 1.00 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Oxygen Transmission: 1.55 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Viscosity: 1.12e+6 cP @Temperature 260 °C
$ 2104/MT
- Density: 1.56 g/cc
- Water Absorption: 4.5 %
- Moisture Absorption at Equilibrium: 1.4 %
- Tensile Strength at Break: 230 MPa
- Elongation at Break: 3.0 %
$ 1785/MT
- Density: 1.33 g/cc
- Water Absorption: 6.0 %
- Moisture Absorption at Equilibrium: 1.8 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
$ 1768/MT
- Density: 1.57 g/cc
- Moisture Absorption: 1.70 %
- Tensile Strength, Ultimate: 230 MPa
- Elongation at Break: 4.1 %
- Tensile Modulus: 15.0 GPa
$ 1969/MT
- Density: 1.35 g/cc
- Water Absorption: 6.3 %
- Moisture Absorption at Equilibrium: 1.9 %
- Tensile Strength at Break: 175 MPa
- Elongation at Break: 3.2 %
$ 1736/MT
- Density: 1.07 g/cc
- Water Absorption: 8.5 %
- Moisture Absorption at Equilibrium: 2.3 %
- Charpy Impact Unnotched: NB @Temperature -30.0 °C
- Charpy Impact Unnotched: NB @Temperature 23.0 °C
$ 1586/MT
- Density: 1.10 g/cc
- Water Absorption: 9.0 %
- Moisture Absorption at Equilibrium: 3.0 %
- Charpy Impact Unnotched: NB @Temperature -30.0 °C
- Charpy Impact Unnotched: NB @Temperature 23.0 °C
$ 1511/MT
- Density: 1.10 g/cc
- Water Absorption: 9.0 %
- Moisture Absorption at Equilibrium: 3.0 %
- High Load Melt Index: 44 g/10 min @Load 21.6 kg, Temperature 275 °C
- Tensile Strength, Yield: 60.0 MPa
$ 1566/MT
- Density: 1.36 g/cc
- Moisture Absorption: 2.40 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Tensile Strength, Ultimate: 67.0 MPa
$ 1687/MT
- Density: 1.32 g/cc
- Water Absorption: 5.7 %
- Moisture Absorption at Equilibrium: 1.7 %
- Tensile Strength at Break: 85.0 MPa
- Elongation at Break: 8.0 %
$ 2572/MT
- Density: 1.53 g/cc
- Water Absorption: 6.2 %
- Moisture Absorption at Equilibrium: 1.7 %
- Tensile Strength at Break: 40.0 MPa
- Elongation at Break: 4.0 %
$ 1905/MT
- Density: 1.48 g/cc
- Moisture Absorption: 2.00 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength, Ultimate: 122 MPa
$ 1908/MT
- Density: 1.13 g/cc
- Water Absorption: 9.5 %
- Moisture Absorption at Equilibrium: 2.5 %
- Viscosity Test: 165 cm³/g
- CTE, linear, Parallel to Flow: 90.0 µm/m-°C @Temperature 20.0 °C
$ 1450/MT
- Density: 1.23 g/cc
- Water Absorption: 7.6 %
- Moisture Absorption: 2.30 %
- Linear Mold Shrinkage, Flow: 0.0032 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0096 cm/cm
$ 1657/MT
- Density: 1.13 g/cc
- Water Absorption: 10 %
- Moisture Absorption at Equilibrium: 2.8 %
- Viscosity Test: 142 cm³/g
- Linear Mold Shrinkage, Flow: 0.0095 cm/cm
$ 1497/MT
- Density: 1.07 g/cc
- Water Absorption: 8.5 %
- Moisture Absorption at Equilibrium: 2.3 %
- Tensile Strength, Yield: 45.0 MPa
- Elongation at Break: >= 50 %
$ 2357/MT
- Density: 1.34 g/cc
- Tensile Strength at Break: 80.0 MPa
- Elongation at Break: 2.0 %
- Tensile Modulus: 6.00 GPa
- Charpy Impact Unnotched: 4.00 J/cm² @Temperature -30.0 °C
$ 1937/MT
- Density: 1.28 g/cc
- Moisture Absorption: 2.20 %
- Tensile Strength, Yield: 88.0 MPa
- Elongation at Break: 15 %
- Tensile Modulus: 6.70 GPa
$ 1512/MT
- Density: 1.35 g/cc
- Water Absorption: 6.3 %
- Moisture Absorption: 1.90 %
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
$ 1618/MT
- Density: 1.36 g/cc
- Moisture Absorption: 2.40 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength, Ultimate: 110 MPa
$ 1705/MT
- Density: 1.13 g/cc
- Water Vapor Transmission: 35.0 g/m²/day @Temperature 23.0 °C
- Oxygen Transmission: 1.15 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Oxygen Transmission: 1.65 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Viscosity: 2.25e+6 cP @Temperature 260 °C
$ 1488/MT
- Density: 1.20 g/cc
- Water Absorption: 6.8 %
- Moisture Absorption at Equilibrium: 2.0 %
- Tensile Strength at Break: 60.0 MPa
- Elongation at Break: 7.0 %
$ 2389/MT
- Density: 1.49 g/cc
- Moisture Absorption at Equilibrium: 1.7 %
- Tensile Strength at Break: 67.0 MPa
- Elongation at Break: 6.0 %
- Tensile Modulus: 4.80 GPa
$ 2309/MT
- Density: 1.45 g/cc
- Water Absorption: 5.5 %
- Moisture Absorption: 1.70 %
- Tensile Strength, Ultimate: 200 MPa
- Elongation at Break: 2.5 %
$ 1945/MT
- Density: 1.02 g/cc
- Moisture Absorption: 1.90 %
- Linear Mold Shrinkage, Flow: 0.018 cm/cm
- Linear Mold Shrinkage, Transverse: 0.022 cm/cm
- Tensile Strength, Yield: 20.0 MPa
$ 1535/MT
- Density: 1.07 g/cc
- Water Absorption: 7.0 %
- Moisture Absorption: 2.50 %
- Tensile Strength, Yield: 50.0 MPa
- Elongation at Break: >= 50 %
$ 1756/MT
- Density: 1.13 g/cc
- Water Vapor Transmission: 35.0 g/m²/day @Temperature 23.0 °C
- Oxygen Transmission: 1.00 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Oxygen Transmission: 1.55 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Viscosity: 810000 cP @Temperature 260 °C
$ 1712/MT
- Density: 1.20 g/cc
- Water Absorption: 6.8 %
- Moisture Absorption at Equilibrium: 2.0 %
- High Load Melt Index: 48 g/10 min @Load 21.6 kg, Temperature 275 °C
- Tensile Strength at Break: 105 MPa
$ 1662/MT
- Density: 1.13 g/cc
- Water Absorption: 10 %
- Moisture Absorption at Equilibrium: 2.8 %
- Linear Mold Shrinkage, Flow: 0.0095 cm/cm
- Linear Mold Shrinkage, Flow: 0.0095 cm/cm
$ 1981/MT
- Density: 1.36 g/cc
- Moisture Absorption: 2.40 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength, Ultimate: 110 MPa
$ 1498/MT
- Density: 1.13 g/cc
- Water Vapor Transmission: 35.0 g/m²/day @Temperature 23.0 °C
- Oxygen Transmission: 1.00 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Oxygen Transmission: 1.55 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Viscosity: 1.12e+6 cP @Temperature 260 °C
$ 2100/MT
- Density: 1.17 g/cc
- Water Absorption: 9.0 %
- Moisture Absorption at Equilibrium: 2.5 %
- Tensile Strength, Yield: 80.0 MPa
- Elongation at Break: 8.0 %
$ 2309/MT
- Density: 1.13 g/cc
- Water Vapor Transmission: 35.0 g/m²/day @Temperature 23.0 °C
- Oxygen Transmission: 1.00 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Oxygen Transmission: 1.55 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Viscosity: 810000 cP @Temperature 260 °C
$ 1498/MT
- Density: 1.56 g/cc
- Water Absorption: 4.5 %
- Moisture Absorption at Equilibrium: 1.4 %
- Tensile Strength at Break: 160 MPa
- Elongation at Break: 3.5 %
$ 1551/MT
- Density: 1.37 g/cc
- Water Absorption: 6.5 %
- Moisture Absorption at Equilibrium: 1.9 %
- Tensile Strength at Break: 120 MPa
- Elongation at Break: 3.0 %
$ 1783/MT
- Density: 1.34 g/cc
- Tensile Strength at Break: 80.0 MPa
- Elongation at Break: 2.0 %
- Tensile Modulus: 6.00 GPa
- Charpy Impact Unnotched: 4.00 J/cm² @Temperature -30.0 °C
$ 2076/MT
- Density: 1.35 g/cc
- Water Absorption: 6.3 %
- Moisture Absorption at Equilibrium: 1.9 %
- Tensile Strength at Break: 185 MPa
- Elongation at Break: 3.5 %
$ 1623/MT
- Density: 1.41 g/cc
- Water Absorption: 5.7 %
- Moisture Absorption at Equilibrium: 1.7 %
- Tensile Strength at Break: 110 MPa
- Elongation at Break: 8.5 %
$ 1824/MT
- Density: 1.49 g/cc
- Moisture Absorption at Equilibrium: 1.7 %
- Tensile Strength at Break: 120 MPa
- Elongation at Break: 3.0 %
- Tensile Modulus: 9.00 GPa
$ 1588/MT
- Density: 1.27 g/cc
- Water Absorption: 8.0 %
- Moisture Absorption at Equilibrium: 2.4 %
- Melting Point: 220 °C
- Blow Molding: Yes
$ 1705/MT
- Density: 1.38 g/cc
- Moisture Absorption: 2.30 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength, Ultimate: 120 MPa
$ 1875/MT
- Density: 1.43 g/cc
- Moisture Absorption: 1.50 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Tensile Strength, Ultimate: 100 MPa
$ 1482/MT
- Density: 1.35 g/cc
- Water Absorption: 6.3 %
- Moisture Absorption: 1.90 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
$ 1922/MT
- Density: 1.59 g/cc
- Water Absorption: 4.5 %
- Moisture Absorption: 1.30 %
- Linear Mold Shrinkage, Flow: 0.0021 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0077 cm/cm
$ 1859/MT
- Density: 1.13 g/cc
- Water Absorption: 10 %
- Moisture Absorption at Equilibrium: 3.0 %
- Viscosity Test: 214 cm³/g
- Tensile Strength, Yield: 85.0 MPa
$ 1708/MT
- Density: 1.50 g/cc
- Water Absorption: 5.5 %
- Moisture Absorption: 1.70 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
$ 1967/MT
- Density: 1.13 g/cc
- Water Absorption: 9.5 %
- Moisture Absorption: 2.50 %
- Viscosity Test: 135 cm³/g
- Tensile Strength, Yield: 75.2 MPa
$ 1569/MT
- Density: 1.49 g/cc
- Moisture Absorption at Equilibrium: 1.7 %
- Tensile Strength at Break: 67.0 MPa
- Elongation at Break: 6.0 %
- Tensile Modulus: 4.80 GPa
$ 1712/MT
- Density: 1.49 g/cc
- Moisture Absorption at Equilibrium: 1.7 %
- Tensile Strength at Break: 120 MPa
- Elongation at Break: 3.0 %
- Tensile Modulus: 9.00 GPa
$ 1622/MT
- Density: 1.41 g/cc
- Moisture Absorption: 2.30 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength, Ultimate: 120 MPa
$ 1772/MT
- Density: 1.38 g/cc
- Water Absorption: 6.2 %
- Moisture Absorption: 1.80 %
- Linear Mold Shrinkage, Flow: 0.0091 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0082 cm/cm
$ 1834/MT
- Density: 1.40 g/cc
- Water Absorption: 5.9 %
- Moisture Absorption at Equilibrium: 1.8 %
- Tensile Strength at Break: 130 MPa
- Elongation at Break: 4.5 %
$ 1702/MT
- Density: 1.17 g/cc
- Water Absorption: 9.0 %
- Moisture Absorption at Equilibrium: 2.5 %
- Tensile Strength, Yield: 80.0 MPa
- Elongation at Break: 8.0 %
$ 1764/MT
- Density: 1.38 g/cc
- Moisture Absorption: 2.30 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength, Ultimate: 118 MPa
$ 1446/MT
- Density: 1.36 g/cc
- Water Absorption: 6.8 %
- Moisture Absorption at Equilibrium: 2.0 %
- Tensile Strength at Break: 45.0 MPa
- Elongation at Break: 25 %
$ 1671/MT
- Density: 1.66 g/cc
- Moisture Absorption: 1.70 %
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength, Ultimate: 120 MPa
$ 1506/MT
- Density: 1.35 g/cc
- Water Absorption: 6.3 %
- Moisture Absorption at Equilibrium: 1.9 %
- Tensile Strength at Break: 110 MPa
- Elongation at Break: 5.0 %
$ 1999/MT
- Density: 1.41 g/cc
- Water Absorption: 5.7 %
- Moisture Absorption: 1.70 %
- Linear Mold Shrinkage, Flow: 0.0036 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0089 cm/cm
$ 1845/MT
- Density: 1.34 g/cc
- Tensile Strength at Break: 45.0 MPa
- Elongation at Break: 15 %
- Tensile Modulus: 2.50 GPa
- Charpy Impact Unnotched: 4.00 J/cm² @Temperature -30.0 °C
$ 2288/MT
- Density: 1.23 g/cc
- Water Absorption: 7.6 %
- Moisture Absorption at Equilibrium: 2.3 %
- Tensile Strength at Break: 70.0 MPa
- Elongation at Break: 6.0 %
$ 1583/MT
- Density: 1.13 g/cc
- Water Vapor Transmission: 35.0 g/m²/day @Temperature 23.0 °C
- Oxygen Transmission: 1.30 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Oxygen Transmission: 1.90 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Viscosity: 810000 cP @Temperature 260 °C
$ 1731/MT
- Density: 1.13 g/cc
- Water Vapor Transmission: 35.0 g/m²/day @Temperature 23.0 °C
- Oxygen Transmission: 1.30 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Oxygen Transmission: 1.95 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Viscosity: 1.13e+6 cP @Temperature 260 °C
$ 2519/MT
- Density: 1.13 g/cc
- Water Vapor Transmission: 35.0 g/m²/day @Temperature 23.0 °C
- Oxygen Transmission: 1.35 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Oxygen Transmission: 1.95 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Viscosity: 2.25e+6 cP @Temperature 260 °C
$ 1809/MT
- Density: 1.56 g/cc
- Water Absorption: 4.5 %
- Moisture Absorption at Equilibrium: 1.4 %
- Tensile Strength at Break: 230 MPa
- Elongation at Break: 3.0 %
$ 1716/MT
- Density: 1.10 g/cc
- Water Absorption: 9.0 %
- Moisture Absorption at Equilibrium: 3.0 %
- Melt Flow: 44 g/10 min
- Tensile Strength, Yield: 60.0 MPa
$ 2464/MT
- Density: 1.23 g/cc
- Water Absorption: 7.6 %
- Moisture Absorption at Equilibrium: 2.3 %
- Tensile Strength at Break: 130 MPa
- Elongation at Break: 3.5 %
$ 2082/MT
- Density: 1.13 g/cc
- Water Absorption: 9.5 %
- Moisture Absorption at Equilibrium: 2.5 %
- Viscosity Test: 245 cm³/g
- Elongation at Break: 45 %
$ 1565/MT
- Density: 1.36 g/cc
- Moisture Absorption: 2.40 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength, Ultimate: 110 MPa
$ 1752/MT
- Density: 1.35 g/cc
- Water Absorption: 6.3 %
- Moisture Absorption at Equilibrium: 1.9 %
- Tensile Strength at Break: 185 MPa
- Elongation at Break: 3.5 %
$ 1718/MT
- Density: 1.38 g/cc
- Water Absorption: 6.6 %
- Moisture Absorption at Equilibrium: 1.9 %
- Tensile Strength at Break: 80.0 MPa
- Elongation at Break: 3.0 %
$ 1725/MT
- Density: 1.48 g/cc
- Moisture Absorption: 2.00 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength, Ultimate: 118 MPa
$ 1463/MT
- Density: 1.30 g/cc
- Water Absorption: 7.0 %
- Moisture Absorption at Equilibrium: 2.1 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
$ 1937/MT
- Density: 1.23 g/cc
- Water Absorption: 7.6 %
- Moisture Absorption at Equilibrium: 2.3 %
- Tensile Strength at Break: 70.0 MPa
- Elongation at Break: 6.0 %
$ 1572/MT
- Density: 1.50 g/cc
- Water Absorption: 5.0 %
- Moisture Absorption at Equilibrium: 1.5 %
- Tensile Strength at Break: 220 MPa
- Elongation at Break: 3.0 %
$ 1459/MT
- Density: 1.16 g/cc
- Moisture Absorption: 3.00 %
- Linear Mold Shrinkage, Flow: 0.010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength, Yield: 40.0 MPa
$ 1826/MT
- Density: 1.13 g/cc
- Water Absorption: 9.0 %
- Moisture Absorption at Equilibrium: 2.5 %
- Tensile Strength, Yield: 55.0 MPa
- Elongation at Break: >= 50 %
$ 1599/MT
- Density: 1.20 g/cc
- Water Absorption: 6.8 %
- Moisture Absorption at Equilibrium: 2.0 %
- Tensile Strength at Break: 105 MPa
- Elongation at Break: 4.0 %
$ 1849/MT
- Density: 1.40 g/cc
- Tensile Strength, Ultimate: 150 MPa
- Elongation at Break: 2.1 %
- Tensile Modulus: 11.3 GPa
- Charpy Impact Unnotched: 6.10 J/cm² @Temperature 23.0 °C
$ 1586/MT
- Density: 1.17 g/cc
- Water Absorption: 9.0 %
- Moisture Absorption at Equilibrium: 2.5 %
- Tensile Strength, Yield: 40.0 MPa
- Elongation at Break: >= 50 %
$ 1506/MT
- Density: 1.07 g/cc
- Moisture Absorption: 2.80 %
- Linear Mold Shrinkage, Flow: 0.015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Tensile Strength, Yield: 45.0 MPa
$ 1634/MT
- Density: 1.20 g/cc
- Water Absorption: 6.8 %
- Moisture Absorption at Equilibrium: 2.0 %
- Tensile Strength at Break: 60.0 MPa
- Elongation at Break: 7.0 %
$ 1578/MT
- Density: 1.34 g/cc
- Tensile Strength at Break: 45.0 MPa
- Elongation at Break: 15 %
- Tensile Modulus: 2.50 GPa
- Charpy Impact Unnotched: 4.00 J/cm² @Temperature -30.0 °C
$ 1445/MT
- Density: 1.41 g/cc
- Water Absorption: 5.7 %
- Moisture Absorption at Equilibrium: 1.7 %
- Tensile Strength at Break: 170 MPa
- Elongation at Break: 5.2 %
$ 1612/MT
- Density: 1.23 g/cc
- Moisture Absorption: 3.00 %
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Tensile Strength, Ultimate: 70.0 MPa
$ 1526/MT
- Density: 1.11 g/cc
- Water Absorption: 9.0 %
- Moisture Absorption at Equilibrium: 2.5 %
- Tensile Strength, Yield: 70.0 MPa
- Elongation at Break: >= 50 %
$ 1530/MT
- Density: 1.13 g/cc
- Water Absorption: 9.5 %
- Moisture Absorption: 2.50 %
- Viscosity Test: 152 cm³/g
- Tensile Strength, Yield: 45.0 MPa
$ 1489/MT
- Density: 1.13 g/cc
- Water Vapor Transmission: 35.0 g/m²/day @Temperature 23.0 °C
- Oxygen Transmission: 1.30 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Oxygen Transmission: 1.90 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Viscosity: 1.12e+6 cP @Temperature 260 °C
$ 2067/MT
- Density: 1.13 g/cc
- Water Absorption: 9.5 %
- Moisture Absorption: 2.50 %
- Viscosity Test: 370 cm³/g
- Tensile Strength, Yield: 85.0 MPa
$ 1719/MT
- Density: 1.13 g/cc
- Water Vapor Transmission: 35.0 g/m²/day @Temperature 23.0 °C
- Oxygen Transmission: 1.30 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Oxygen Transmission: 1.90 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Viscosity: 810000 cP @Temperature 260 °C
$ 1984/MT
- Density: 1.13 g/cc
- Water Vapor Transmission: 35.0 g/m²/day @Temperature 23.0 °C
- Oxygen Transmission: 1.30 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Oxygen Transmission: 1.90 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Viscosity: 810000 cP @Temperature 260 °C
$ 1705/MT
- Density: 1.13 g/cc
- Water Vapor Transmission: 35.0 g/m²/day @Temperature 23.0 °C
- Oxygen Transmission: 1.30 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Oxygen Transmission: 1.90 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Viscosity: 810000 cP @Temperature 260 °C
$ 1893/MT
- Density: 1.33 g/cc
- Water Absorption: 6.0 %
- Moisture Absorption at Equilibrium: 1.8 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Flow: 0.011 cm/cm
$ 1687/MT
- Density: 1.13 g/cc
- Water Absorption: 10 %
- Moisture Absorption at Equilibrium: 2.8 %
- Viscosity Test: 129 cm³/g
- Linear Mold Shrinkage, Flow: 0.011 cm/cm
$ 1548/MT
- Density: 1.49 g/cc
- Moisture Absorption: 1.90 %
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Tensile Strength, Ultimate: 150 MPa
$ 2232/MT
- Density: 1.38 g/cc
- Water Absorption: 6.2 %
- Moisture Absorption at Equilibrium: 1.8 %
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
$ 1818/MT
- Density: 1.13 g/cc
- Moisture Absorption: 3.30 %
- Viscosity Test: 118 cm³/g
- Linear Mold Shrinkage, Flow: 0.010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
$ 1505/MT
- Density: 1.17 g/cc
- Water Absorption: 9.0 %
- Moisture Absorption at Equilibrium: 2.5 %
- Tensile Strength, Yield: 80.0 MPa
- Elongation at Break: 8.0 %
$ 1714/MT
- Density: 1.38 g/cc
- Water Absorption: 6.3 %
- Moisture Absorption at Equilibrium: 1.9 %
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
$ 1899/MT
- Density: 1.23 g/cc
- Water Absorption: 7.6 %
- Moisture Absorption at Equilibrium: 2.3 %
- Tensile Strength at Break: 130 MPa
- Elongation at Break: 3.5 %
$ 2244/MT
- Density: 1.13 g/cc
- Water Vapor Transmission: 35.0 g/m²/day @Temperature 23.0 °C
- Oxygen Transmission: 1.30 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Oxygen Transmission: 1.90 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Viscosity: 560000 cP @Temperature 260 °C
$ 1513/MT
- Density: 1.13 g/cc
- Water Absorption: 9.0 %
- Moisture Absorption at Equilibrium: 2.5 %
- Tensile Strength, Yield: 95.0 MPa
- Elongation at Break: 15 %
$ 1573/MT
- Density: 1.33 g/cc
- Water Absorption: 6.0 %
- Moisture Absorption at Equilibrium: 1.8 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Flow: 0.011 cm/cm
$ 2094/MT
- Density: 1.56 g/cc
- Water Absorption: 4.5 %
- Moisture Absorption at Equilibrium: 1.4 %
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
$ 1655/MT
- Density: 1.33 g/cc
- Water Absorption: 6.0 %
- Moisture Absorption at Equilibrium: 1.8 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
$ 1706/MT
- Density: 1.23 g/cc
- Water Absorption: 7.6 %
- Moisture Absorption at Equilibrium: 2.3 %
- Tensile Strength at Break: 130 MPa
- Elongation at Break: 3.5 %
$ 1761/MT
- Density: 1.13 g/cc
- Water Vapor Transmission: 35.0 g/m²/day @Temperature 23.0 °C
- Oxygen Transmission: 1.35 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Oxygen Transmission: 1.95 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Viscosity: 2.25e+6 cP @Temperature 260 °C
$ 1788/MT
- Density: 1.11 g/cc
- Water Absorption: 9.0 %
- Moisture Absorption at Equilibrium: 2.5 %
- Charpy Impact Unnotched: NB @Temperature -30.0 °C
- Charpy Impact Unnotched: NB @Temperature 23.0 °C
$ 1793/MT
- Density: 1.38 g/cc
- Water Absorption: 6.6 %
- Moisture Absorption at Equilibrium: 1.9 %
- Tensile Strength at Break: 40.0 MPa
- Elongation at Break: 4.5 %
$ 1613/MT
- Density: 1.30 g/cc
- Water Absorption: 7.0 %
- Moisture Absorption at Equilibrium: 2.1 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
$ 1947/MT
- Density: 1.13 g/cc
- Water Vapor Transmission: 35.0 g/m²/day @Temperature 23.0 °C
- Oxygen Transmission: 1.30 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Oxygen Transmission: 1.90 cc-mm/m²-24hr-atm @Temperature 23.0 °C
- Viscosity: 410000 cP @Temperature 260 °C
$ 2224/MT
- Density: 1.50 g/cc
- Water Absorption: 5.0 %
- Moisture Absorption at Equilibrium: 1.5 %
- Tensile Strength at Break: 150 MPa
- Elongation at Break: 4.0 %
$ 2023/MT
- Density: 1.35 g/cc
- Water Absorption: 6.3 %
- Moisture Absorption at Equilibrium: 1.9 %
- Tensile Strength at Break: 110 MPa
- Elongation at Break: 5.0 %
$ 1574/MT
- Density: 1.13 g/cc
- Water Absorption: 10 %
- Moisture Absorption at Equilibrium: 2.8 %
- Linear Mold Shrinkage, Flow: 0.011 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
$ 1719/MT
- Density: 1.47 g/cc
- Moisture Absorption: 1.70 %
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm
- Tensile Strength, Ultimate: 85.0 MPa
$ 1817/MT
- Density: 1.34 g/cc
- Water Absorption: 6.5 %
- Moisture Absorption: 2.00 %
- Linear Mold Shrinkage, Flow: 0.011 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
$ 1530/MT
- Density: 1.14 g/cc
- Moisture Absorption: 3.50 %
- Viscosity: 70000 cP @Shear Rate 10000 1/s, Temperature 240 °C
- Viscosity: 70000 cP @Shear Rate 10000 1/s, Temperature 260 °C
- Viscosity: 70000 cP @Shear Rate 10000 1/s, Temperature 280 °C
$ 1495/MT
- Density: 1.27 g/cc
- Water Absorption: 7.2 %
- Moisture Absorption at Equilibrium: 2.15 %
- Tensile Strength at Break: 140 MPa
- Elongation at Break: 3.5 %
$ 1841/MT
- Density: 1.17 g/cc
- Water Absorption: 9.0 %
- Moisture Absorption at Equilibrium: 2.5 %
- Tensile Strength, Yield: 40.0 MPa
- Elongation at Break: >= 50 %
$ 1460/MT
- Density: 1.40 g/cc
- Water Absorption: 5.9 %
- Moisture Absorption at Equilibrium: 1.8 %
- Tensile Strength at Break: 130 MPa
- Elongation at Break: 4.5 %
$ 1799/MT
- Density: 1.37 g/cc
- Water Absorption: 6.1 %
- Moisture Absorption: 1.60 %
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
$ 1478/MT
- Density: 1.13 g/cc
- Water Absorption: 9.5 %
- Moisture Absorption at Equilibrium: 2.5 %
- Viscosity Test: 244 cm³/g
- Melting Point: 220 °C
$ 1582/MT
- Density: 1.20 g/cc
- Water Absorption: 6.8 %
- Moisture Absorption at Equilibrium: 2.0 %
- Tensile Strength at Break: 105 MPa
- Elongation at Break: 4.0 %
$ 2509/MT
- Density: 1.13 g/cc
- Water Absorption: 9.5 %
- Moisture Absorption: 2.50 %
- Viscosity Test: 152 cm³/g
- Melting Point: 220 °C
$ 2425/MT
- Density: 1.56 g/cc
- Water Absorption: 4.5 %
- Moisture Absorption at Equilibrium: 1.4 %
- Tensile Strength at Break: 160 MPa
- Elongation at Break: 3.5 %
$ 1451/MT
- Density: 1.13 g/cc
- Viscosity: 300000 cP @Shear Rate 1000 1/s, Temperature 240 °C
- Viscosity: 300000 cP @Shear Rate 1000 1/s, Temperature 260 °C
- Viscosity: 300000 cP @Shear Rate 1000 1/s, Temperature 280 °C
- Viscosity: 1.00e+6 cP @Shear Rate 0.100 1/s, Temperature 280 °C
$ 1642/MT
- Density: 1.34 g/cc
- Water Absorption: 6.5 %
- Moisture Absorption: 2.00 %
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
$ 1939/MT
- Density: 1.35 g/cc
- Water Absorption: 6.3 %
- Moisture Absorption at Equilibrium: 1.9 %
- Tensile Strength at Break: 110 MPa
- Elongation at Break: 5.0 %
$ 1628/MT
- Density: 1.13 g/cc
- Water Absorption: 10 %
- Moisture Absorption at Equilibrium: 3.0 %
- Charpy Impact Unnotched: NB @Temperature -30.0 °C
- Charpy Impact Unnotched: NB @Temperature 23.0 °C
$ 2129/MT
- Density: 1.23 g/cc
- Moisture Absorption: 3.00 %
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Tensile Strength, Ultimate: 70.0 MPa
$ 1478/MT
- Density: 1.38 g/cc
- Water Absorption: 6.3 %
- Moisture Absorption at Equilibrium: 1.9 %
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
$ 1503/MT
- Density: 1.35 g/cc
- Water Absorption: 6.3 %
- Moisture Absorption: 1.90 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
Delivery Nylon 6 DSM Engineering Plastics
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
lng carrier for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.