$ 1885/MT
- Water Absorption: 1.1 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0075 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0112 cm/cm
- Tensile Strength at Break: 70.0 MPa
- Elongation at Break: 2.0 %
$ 1555/MT
- Density: 1.35 g/cc
- Water Absorption: 1.1 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0065 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0085 cm/cm
- Tensile Strength at Break: 85.0 MPa
$ 1723/MT
- Density: 1.36 g/cc
- Water Absorption: 1.05 % @Temperature 23.0 °C, Time 86400 sec
- Viscosity: 30 cP @Shear Rate 10000 1/s, Temperature 240 °C
- Viscosity: 30 cP @Shear Rate 10000 1/s, Temperature 250 °C
- Viscosity: 30 cP @Shear Rate 10000 1/s, Temperature 260 °C
$ 1586/MT
- Density: 1.16 g/cc
- Tensile Strength at Break: 40.0 MPa
- Tensile Strength, Yield: 50.0 MPa
- Elongation at Break: 38 %
- Elongation at Yield: 5.0 %
$ 1899/MT
- Density: 1.57 g/cc
- Water Absorption: 0.60 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0034 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0042 cm/cm
- Hardness, Rockwell R: 121
$ 1564/MT
- Density: 1.36 g/cc
- Linear Mold Shrinkage, Flow: 0.0037 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0075 cm/cm
- Tensile Strength at Break: 140 MPa
- Elongation at Break: 2.0 %
$ 2251/MT
- Density: 1.14 g/cc
- Volume Resistivity: 1.00e+10 ohm-cm
- Surface Resistance: 1.00e+10 ohm
- Dielectric Strength: 18.0 kV/mm
- Dissipation Factor: 0.10
- Moisture Content: <= 0.20 %
$ 1615/MT
- Density: 1.51 g/cc
- Tensile Strength at Break: 145 MPa
- Elongation at Break: 3.9 %
- Tensile Modulus: 8.30 GPa
- Charpy Impact Unnotched: 8.50 J/cm²
$ 1474/MT
- Density: 1.35 g/cc
- Water Absorption: 0.95 %
- Tensile Strength, Ultimate: 110 MPa
- Elongation at Break: 4.5 %
- Tensile Modulus: 6.20 GPa
$ 1466/MT
- Density: 1.35 g/cc
- Water Absorption: 0.95 % @Temperature 23.0 °C, Time 86400 sec
- Tensile Strength at Break: 190 MPa
- Elongation at Break: 3.8 %
- Tensile Modulus: 9.60 GPa
$ 1854/MT
- Density: 1.68 g/cc
- Tensile Strength at Break: 220 MPa
- Elongation at Break: 2.5 %
- Tensile Modulus: 18.7 GPa
- Izod Impact, Notched (ISO): 19.6 kJ/m²
$ 1895/MT
- Density: 1.34 g/cc
- Water Absorption: 0.95 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage: 0.0054 cm/cm
- Linear Mold Shrinkage, Flow: 0.0035 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0065 cm/cm
$ 1936/MT
- Density: 1.57 g/cc
- Water Absorption: 0.60 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0034 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0042 cm/cm
- Tensile Strength at Break: 255 MPa
$ 2459/MT
- Density: 1.35 g/cc
- Water Absorption: 0.95 %
- Tensile Strength, Ultimate: 190 MPa
- Elongation at Break: 3.8 %
- Tensile Modulus: 9.60 GPa
$ 2012/MT
- Density: 1.35 g/cc
- Tensile Strength at Break: 110 MPa
- Elongation at Break: 4.5 %
- Tensile Modulus: 6.20 GPa
- Flexural Modulus: 5.50 GPa
$ 2247/MT
- Density: 1.37 g/cc
- Tensile Strength at Break: 113 MPa
- Elongation at Break: 4.2 %
- Tensile Modulus: 6.62 GPa
- Flexural Modulus: 6.04 GPa
$ 1949/MT
- Density: 1.37 g/cc
- Water Absorption: 1.0 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0080 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0075 cm/cm
- Tensile Strength at Break: 80.0 MPa
$ 1485/MT
- Density: 1.35 g/cc
- Water Absorption: 0.95 %
- Tensile Strength at Break: 193 MPa
- Elongation at Break: 3.8 %
- Tensile Modulus: 9.58 GPa
$ 1864/MT
- Density: 1.06 g/cc
- Water Absorption: 1.2 % @Temperature 23.0 °C, Time 86400 sec
- Hardness, Rockwell R: 110
- Tensile Strength, Yield: 50.0 MPa
- Elongation at Break: 200 %
$ 1582/MT
- Density: 1.65 g/cc
- Water Absorption: 0.55 % @Temperature 23.0 °C, Time 86400 sec
- Tensile Strength at Break: 240 MPa
- Elongation at Break: 2.5 %
- Tensile Modulus: 21.0 GPa
$ 2135/MT
- Density: 1.09 g/cc
- Water Absorption: 1.2 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0142 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0132 cm/cm
- Tensile Strength, Yield: 75.0 MPa
$ 1515/MT
- Density: 1.06 g/cc
- Volume Resistivity: 1.00e+10 ohm-cm
- Surface Resistance: 1.00e+10 ohm
- Dielectric Constant: 4.0
- Dielectric Strength: 18.0 kV/mm
$ 1775/MT
- Density: 1.41 g/cc
- Tensile Strength at Break: 115 MPa
- Elongation at Break: 4.5 %
- Tensile Modulus: 7.40 GPa
- Flexural Strength: 195 MPa
$ 1446/MT
- Density: 1.14 g/cc
- Water Absorption: 1.3 %
- Tensile Strength, Yield: 85.0 MPa
- Elongation at Break: 120 %
- Tensile Modulus: 2.85 GPa
$ 1604/MT
- Density: 1.09 g/cc
- Water Absorption: 1.27 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage: 0.0099 cm/cm
- Linear Mold Shrinkage, Flow: 0.0146 cm/cm
- Linear Mold Shrinkage, Flow: 0.0206 cm/cm
$ 1444/MT
- Density: 1.13 g/cc
- Water Absorption: 1.37 % @Temperature 23.0 °C, Time 86400 sec
- Tensile Strength, Yield: 80.0 MPa
- Elongation at Break: 160 %
- Elongation at Yield: 4.2 %
$ 1470/MT
- Density: 1.09 g/cc
- Water Absorption: 1.27 % @Temperature 23.0 °C, Time 86400 sec
- Viscosity: 220 cP @Shear Rate 1000 1/s, Temperature 270 °C
- Viscosity: 1050 cP @Shear Rate 100 1/s, Temperature 270 °C
- Viscosity: 2200 cP @Shear Rate 10.0 1/s, Temperature 270 °C
$ 1674/MT
- Density: 1.31 g/cc
- Water Absorption: 1.0 %
- Tensile Strength at Break: 162 MPa
- Elongation at Break: 3.9 %
- Tensile Modulus: 8.41 GPa
$ 1758/MT
- Density: 1.62 g/cc
- Tensile Strength at Break: 85.0 MPa
- Elongation at Break: 6.0 %
- Tensile Modulus: 8.05 GPa
- Charpy Impact Unnotched: 4.00 J/cm²
$ 1531/MT
- Density: 1.45 g/cc
- Tensile Strength at Break: 140 MPa
- Elongation at Break: 3.5 %
- Tensile Modulus: 7.30 GPa
- Izod Impact, Notched (ISO): 34.0 kJ/m²
$ 1766/MT
- Density: 1.14 g/cc
- Volume Resistivity: 1.00e+10 ohm-cm
- Surface Resistance: 1.00e+10 ohm
- Dielectric Strength: 3.90 kV/mm
- Dissipation Factor: 0.10
- Moisture Content: <= 0.20 %
$ 1705/MT
- Tensile Strength at Break: 120 MPa
- Elongation at Break: 4.5 %
- Tensile Modulus: 6.20 GPa
- Volume Resistivity: 1.00e+11 ohm-cm
- Dielectric Constant: 4.5
$ 1825/MT
- Density: 1.66 g/cc
- Tensile Strength at Break: 165 MPa
- Elongation at Break: 3.7 %
- Tensile Modulus: 15.5 GPa
- Flexural Modulus: 13.2 GPa
$ 1595/MT
- Density: 1.42 g/cc
- Tensile Strength at Break: 97.0 MPa
- Elongation at Break: 5.1 %
- Tensile Modulus: 8.50 GPa
- Flexural Strength: 175 MPa
$ 1730/MT
- Tensile Strength at Break: 55.0 MPa
- Elongation at Break: 4.0 %
- Tensile Modulus: 4.00 GPa
- Izod Impact, Notched (ISO): 3.50 kJ/m²
- Charpy Impact Unnotched: 5.00 J/cm²
$ 2490/MT
- Density: 1.65 g/cc
- Tensile Strength at Break: 165 MPa
- Elongation at Break: 3.7 %
- Tensile Modulus: 15.5 GPa
- Flexural Modulus: 13.2 GPa
$ 1689/MT
- Density: 1.37 g/cc
- Water Absorption: 1.0 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage: 0.010 cm/cm
- Linear Mold Shrinkage, Flow: 0.0080 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
$ 1886/MT
- Tensile Strength at Break: 160 MPa
- Elongation at Break: 2.1 %
- Tensile Modulus: 10.4 GPa
- Charpy Impact Unnotched: 4.50 J/cm²
- Charpy Impact, Notched: 0.810 J/cm²
$ 1506/MT
- Density: 1.14 g/cc
- Tensile Strength at Break: 45.0 MPa
- Elongation at Break: 270 %
- Tensile Modulus: 1.10 GPa
- Flexural Strength: 40.0 MPa
$ 2489/MT
- Density: 1.32 g/cc
- Tensile Strength at Break: 90.0 MPa
- Elongation at Break: 7.0 %
- Tensile Modulus: 5.40 GPa
- Flexural Modulus: 5.20 GPa
$ 1554/MT
- Density: 1.45 g/cc
- Tensile Strength at Break: 140 MPa
- Elongation at Break: 3.5 %
- Tensile Modulus: 7.30 GPa
- Flexural Modulus: 7.20 GPa
$ 1536/MT
- Density: 1.32 g/cc
- Water Absorption: 1.1 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
- Tensile Strength at Break: 92.0 MPa
$ 1974/MT
- Density: 1.39 g/cc
- Water Absorption: 0.80 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Hardness, Rockwell R: 121
$ 2272/MT
- Density: 1.38 g/cc
- Water Absorption: 0.90 % @Temperature 23.0 °C, Time 86400 sec
- Tensile Strength at Break: 195 MPa
- Elongation at Break: 2.6 %
- Tensile Modulus: 10.6 GPa
$ 2185/MT
- Density: 1.16 g/cc
- Tensile Strength: 80.0 MPa
- Tensile Modulus: 3.70 GPa
- Flexural Strength: 110 MPa
- Flexural Modulus: 3.50 GPa
$ 1447/MT
- Density: 1.37 g/cc
- Water Absorption: 0.80 %
- Hardness, Rockwell R: 119
- Tensile Strength at Break: 175 MPa
- Elongation at Break: 4.0 %
$ 1843/MT
- Density: 1.32 g/cc
- Tensile Strength at Break: 90.0 MPa
- Elongation at Break: 10 %
- Tensile Modulus: 4.90 GPa
- Charpy Impact Unnotched: 10.2 J/cm² @Temperature -30.0 °C
$ 1881/MT
- Density: 1.47 g/cc
- Tensile Strength at Break: 125 MPa
- Elongation at Break: 2.5 %
- Tensile Modulus: 9.72 GPa
- Izod Impact, Notched (ISO): 4.20 kJ/m²
$ 2030/MT
- Density: 1.56 g/cc
- Water Absorption: 0.75 % @Temperature 23.0 °C, Time 86400 sec
- Tensile Strength at Break: 225 MPa
- Elongation at Break: 2.0 %
- Tensile Modulus: 14.6 GPa
$ 1551/MT
- Density: 1.34 g/cc
- Water Absorption: 0.95 % @Temperature 23.0 °C, Time 86400 sec
- Tensile Strength at Break: 180 MPa
- Elongation at Break: 3.3 %
- Tensile Modulus: 9.60 GPa
$ 1815/MT
- Density: 1.37 g/cc
- Water Absorption: 0.92 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
- Tensile Strength at Break: 193 MPa
$ 1497/MT
- Moisture Content: <= 0.15 %
$ 1542/MT
- Density: 1.22 g/cc
- Water Absorption: 1.15 %
- Elongation at Break: 4.0 %
- Tensile Modulus: 6.09 GPa
- Izod Impact, Notched (ISO): 5.46 kJ/m²
$ 1538/MT
- Density: 1.36 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Linear Mold Shrinkage, Flow: 0.0054 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0108 cm/cm
- Tensile Strength at Break: 110 MPa
$ 2211/MT
- Density: 1.55 g/cc
- Tensile Strength at Break: 162 MPa
- Elongation at Break: 4.0 %
- Tensile Modulus: 11.6 GPa
- Flexural Modulus: 10.0 GPa
$ 1506/MT
- Density: 1.14 g/cc
- Tensile Strength at Break: 41.0 MPa
- Tensile Strength, Yield: 45.0 MPa
- Elongation at Break: 82 %
- Tensile Modulus: 1.30 GPa
$ 1454/MT
- Density: 1.51 g/cc
- Water Absorption: 0.80 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm
- Tensile Strength at Break: 190 MPa
$ 2493/MT
- Density: 1.32 g/cc
- Water Absorption: 0.88 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage: 0.0084 cm/cm
- Linear Mold Shrinkage, Flow: 0.0039 cm/cm
- Linear Mold Shrinkage, Flow: 0.0084 cm/cm
$ 2340/MT
- Density: 1.18 g/cc
- Tensile Strength at Break: 70.0 MPa
- Elongation at Break: 5.0 %
- Tensile Modulus: 3.80 GPa
- Izod Impact, Notched (ISO): 22.0 kJ/m²
$ 1712/MT
- Tensile Strength at Break: 142 MPa
- Elongation at Break: 142 %
- Tensile Modulus: 8.90 GPa
- Flexural Strength: 221 MPa
- Flexural Modulus: 6.626 GPa
$ 2314/MT
- Tensile Strength at Break: 189.3 MPa
- Elongation at Break: 3.3 %
- Tensile Modulus: 10.7 GPa
- Flexural Strength: 285 MPa
- Flexural Modulus: 9.088 GPa
$ 1471/MT
- Density: 1.65 g/cc
- Tensile Strength at Break: 165 MPa
- Elongation at Break: 4.0 %
- Tensile Modulus: 15.5 GPa
- Flexural Modulus: 13.2 GPa
$ 2472/MT
- Density: 1.55 g/cc
- Water Absorption: 0.72 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage: 0.0072 cm/cm
- Linear Mold Shrinkage, Flow: 0.0023 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0032 cm/cm
$ 2069/MT
- Density: 1.06 g/cc
- Tensile Strength, Yield: 40.0 MPa
- Elongation at Break: 50 %
- Tensile Modulus: 1.10 GPa
- Flexural Modulus: 9.50 GPa
$ 1648/MT
- Density: 1.17 g/cc
- Tensile Strength at Break: 90.0 MPa
- Elongation at Break: 7.0 %
- Flexural Strength: 135 MPa
- Flexural Modulus: 4.10 GPa
$ 1897/MT
- Density: 1.09 g/cc
- Tensile Strength at Break: 42.0 MPa
- Elongation at Break: 190 %
- Tensile Modulus: 0.910 GPa
- Flexural Modulus: 0.650 GPa
$ 1659/MT
- Density: 1.14 g/cc
- Water Absorption: 1.3 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.013 - 0.017 cm/cm
- Linear Mold Shrinkage, Transverse: 0.015 - 0.020 cm/cm
- Hardness, Rockwell R: 115
$ 1864/MT
- Density: 1.34 g/cc
- Water Absorption: 0.95 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0035 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0065 cm/cm
- Tensile Strength at Break: 110 MPa
$ 1499/MT
- Density: 1.13 g/cc
- Tensile Strength, Yield: 35.0 MPa
- Elongation at Break: 300 %
- Elongation at Yield: 2.5 %
- Tensile Modulus: 0.900 GPa
$ 1670/MT
- Density: 1.14 g/cc
- Water Absorption: 1.3 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.016 cm/cm
- Tensile Strength at Break: 80.0 MPa
$ 1535/MT
- Density: 1.56 g/cc
- Water Absorption: 0.75 %
- Tensile Strength at Break: 225 MPa
- Elongation at Break: 2.0 %
- Tensile Modulus: 14.6 GPa
$ 2025/MT
- Density: 1.14 g/cc
- Water Absorption: 1.3 %
- Tensile Strength, Yield: 85.01 MPa
- Elongation at Break: 120 %
- Tensile Modulus: 2.80 GPa
$ 1522/MT
- Density: 1.56 g/cc
- Linear Mold Shrinkage, Flow: 0.0025 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0033 cm/cm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 220 MPa
$ 1788/MT
- Density: 1.14 g/cc
- Tensile Strength, Yield: 35.0 MPa
- Tensile Modulus: 0.550 GPa
- Flexural Strength: 30.0 MPa
- Flexural Modulus: 5.30 GPa
$ 1673/MT
- Density: 1.45 g/cc
- Tensile Strength at Break: 55.0 MPa
- Elongation at Break: 25 %
- Tensile Modulus: 2.60 GPa
- Flexural Strength: 65.0 MPa
$ 1446/MT
- Density: 1.55 g/cc
- Water Absorption: 0.72 % @Temperature 23.0 °C, Time 86400 sec
- Viscosity: 100 cP @Shear Rate 1000 1/s, Temperature 270 °C
- Viscosity: 110 cP @Shear Rate 1000 1/s, Temperature 250 °C
- Viscosity: 140 cP @Shear Rate 1000 1/s, Temperature 230 °C
$ 1764/MT
- Density: 1.56 g/cc
- Tensile Strength at Break: 150 MPa
- Elongation at Break: 3.0 %
- Tensile Modulus: 8.60 GPa
- Izod Impact, Notched (ISO): 29.0 kJ/m²
$ 1583/MT
- Density: 1.55 g/cc
- Water Absorption: 0.72 % @Time 86400 sec
- Tensile Strength at Break: 230 MPa
- Elongation at Break: 2.6 %
- Tensile Modulus: 17.0 GPa
$ 1453/MT
- Density: 1.42 g/cc
- Water Absorption: 0.90 % @Temperature 23.0 °C, Time 86400 sec
- Viscosity: 50 cP @Shear Rate 1000 1/s, Temperature 270 °C
- Viscosity: 120 cP @Shear Rate 1000 1/s, Temperature 250 °C
- Viscosity: 120 cP @Shear Rate 100 1/s, Temperature 270 °C
$ 1782/MT
- Density: 1.14 g/cc
- Water Absorption: 1.3 %
- Tensile Strength, Yield: 45.0 MPa
- Elongation at Break: 270 %
- Tensile Modulus: 1.10 GPa
$ 1690/MT
- Density: 1.36 g/cc
- Tensile Strength at Break: 110 MPa
- Tensile Stress: 42.0 MPa @Strain 1.00 %
- Tensile Stress: 70.0 MPa @Strain 2.00 %
- Tensile Stress: 85.0 MPa @Strain 3.00 %
$ 1630/MT
- Density: 1.14 g/cc
- Tensile Strength, Yield: 45.0 MPa
- Tensile Modulus: 1.10 GPa
- Flexural Strength: 40.0 MPa
- Flexural Modulus: 1.00 GPa
$ 2332/MT
- Density: 1.14 g/cc
- Water Absorption: 1.3 % @Temperature 23.0 °C, Time 86400 sec
- Tensile Strength, Yield: 85.0 MPa
- Tensile Modulus: 2.85 GPa
- Flexural Strength: 115 MPa
$ 1617/MT
- Density: 1.69 g/cc
- Tensile Strength at Break: 195 MPa
- Tensile Stress: 50.0 MPa @Strain 1.00 %, Temperature 160 °C
- Tensile Stress: 55.0 MPa @Strain 1.00 %, Temperature 120 °C
- Tensile Stress: 70.0 MPa @Strain 2.00 %, Temperature 160 °C
$ 1968/MT
- Density: 1.09 g/cc
- Tensile Strength at Break: 42.0 MPa
- Elongation at Break: 190 %
- Tensile Modulus: 0.910 GPa
- Flexural Strength: 28.0 MPa
$ 2322/MT
- Density: 1.36 g/cc
- Water Absorption: 0.95 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.000035 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0065 cm/cm
- Hardness, Rockwell R: 121
$ 1649/MT
- Density: 1.41 g/cc
- Water Absorption: 0.90 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage: 0.0042 cm/cm
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0053 cm/cm
$ 1506/MT
- Density: 1.34 g/cc
- Tensile Strength at Break: 110 MPa
- Elongation at Break: 4.5 %
- Tensile Modulus: 6.20 GPa
- Flexural Strength: 140 MPa
$ 1819/MT
- Density: 1.22 g/cc
- Tensile Strength at Break: 70.0 MPa
- Elongation at Break: 7.0 %
- Tensile Modulus: 2.90 GPa
- Izod Impact, Notched (ISO): 14.0 kJ/m²
$ 2138/MT
- Density: 1.13 g/cc
- Tensile Strength at Break: 50.0 MPa
- Tensile Strength, Yield: 78.0 MPa
- Elongation at Break: 30 %
- Elongation at Yield: 4.0 %
$ 1623/MT
- Density: 1.45 g/cc
- Water Absorption: 0.90 % @Temperature 23.0 °C, Time 86400 sec
- Tensile Strength at Break: 215 MPa
- Elongation at Break: 2.3 %
- Tensile Modulus: 1.31 GPa
$ 1578/MT
- Density: 1.41 g/cc
- Water Absorption: 0.90 % @Temperature 23.0 °C, Time 86400 sec
- Tensile Strength at Break: 195 MPa
- Elongation at Break: 3.0 %
- Tensile Modulus: 10.7 GPa
$ 1924/MT
- Density: 1.37 g/cc
- Tensile Strength at Break: 35.0 MPa
- Tensile Strength, Yield: 35.0 MPa
- Elongation at Break: 12.2 %
- Elongation at Yield: 18.2 %
$ 2086/MT
- Density: 1.18 g/cc
- Water Absorption: 1.42 % @Temperature 23.0 °C, Time 86400 sec
- Tensile Strength at Break: 85.0 MPa
- Elongation at Break: 3.0 %
- Tensile Modulus: 5.00 GPa
$ 1463/MT
- Density: 1.06 g/cc
- Tensile Strength, Yield: 45.0 MPa
- Elongation at Break: 50 %
- Tensile Modulus: 2.00 GPa
- Flexural Modulus: 1.90 GPa
$ 2127/MT
- Density: 1.14 g/cc
- Water Absorption: 1.9 % @Temperature 23.0 °C, Time 86400 sec
- Tensile Strength, Yield: 55.0 MPa
- Tensile Modulus: 1.20 GPa
- Flexural Strength: 50.0 MPa
$ 2062/MT
- Density: 1.32 g/cc
- Tensile Strength at Break: 65.0 MPa
- Elongation at Break: 4.8 %
- Tensile Modulus: 4.55 GPa
- Charpy Impact Unnotched: 7.90 J/cm²
$ 1572/MT
- Density: 1.35 g/cc
- Tensile Strength at Break: 51.0 MPa
- Elongation at Break: 4.2 %
- Tensile Modulus: 4.35 GPa
- Charpy Impact Unnotched: 8.40 J/cm²
$ 1655/MT
- Density: 1.55 g/cc
- Tensile Strength at Break: 162 MPa
- Elongation at Break: 4.0 %
- Tensile Modulus: 11.6 GPa
- Flexural Modulus: 10.0 GPa
$ 1980/MT
- Density: 1.42 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
- Tensile Strength at Break: 97.0 MPa
$ 2046/MT
- Density: 1.14 g/cc
- Water Absorption: 1.3 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.011 - 0.015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.012 - 0.015 cm/cm
- Hardness, Rockwell R: 115
$ 1625/MT
- Density: 1.65 g/cc
- Tensile Strength at Break: 240 MPa
- Elongation at Break: 2.5 %
- Tensile Modulus: 21.0 GPa
- Flexural Modulus: 19.0 GPa
$ 2508/MT
- Density: 1.62 g/cc
- Water Absorption: 0.95 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage: 0.0075 cm/cm
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
$ 1482/MT
- Density: 1.34 g/cc
- Tensile Strength at Break: 110 MPa
- Elongation at Break: 5.5 %
- Tensile Modulus: 6.20 GPa
- Flexural Modulus: 5.20 GPa
$ 1468/MT
- Density: 1.09 g/cc
- Tensile Strength, Yield: 39.0 MPa
- Tensile Modulus: 1.00 GPa
- Flexural Strength: 35.0 MPa
- Flexural Modulus: 0.800 GPa
Delivery Nylon 6 Solvay
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
cargo ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.