$ 1723/MT
- Density: 1.36 g/cc
- Water Absorption: 1.05 % @Temperature 23.0 °C, Time 86400 sec
- Viscosity: 30 cP @Shear Rate 10000 1/s, Temperature 240 °C
- Viscosity: 30 cP @Shear Rate 10000 1/s, Temperature 250 °C
- Viscosity: 30 cP @Shear Rate 10000 1/s, Temperature 260 °C
$ 1984/MT
- Density: 1.32 g/cc
- Water Absorption: 0.90 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0085 cm/cm
- Tensile Strength at Break: 170 MPa
$ 1763/MT
- Density: 1.38 g/cc
- Tensile Strength at Break: 105 MPa
- Elongation at Break: 4.1 %
- Tensile Modulus: 6.50 GPa
- Flexural Strength: 155 MPa
$ 1564/MT
- Density: 1.36 g/cc
- Linear Mold Shrinkage, Flow: 0.0037 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0075 cm/cm
- Tensile Strength at Break: 140 MPa
- Elongation at Break: 2.0 %
$ 2082/MT
- Density: 1.57 g/cc
- Tensile Strength at Break: 95.0 MPa
- Elongation at Break: 3.5 %
- Tensile Modulus: 7.00 GPa
- Flexural Strength: 170 MPa
$ 1604/MT
- Density: 1.38 g/cc
- Water Absorption: 0.80 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Hardness, Rockwell R: 121
$ 1920/MT
- Density: 1.37 g/cc
- Water Absorption: 0.95 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage: 0.0070 cm/cm
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
$ 2003/MT
- Density: 1.37 g/cc
- Water Absorption: 0.75 % @Temperature 23.0 °C, Time 86400 sec
- Tensile Strength at Break: 80.0 MPa
- Tensile Strength, Yield: 80.0 MPa
- Elongation at Break: 9.0 %
$ 1479/MT
- Density: 1.27 g/cc
- Linear Mold Shrinkage: 0.0060 cm/cm
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0085 cm/cm
- Tensile Strength at Break: 170 MPa
$ 1474/MT
- Density: 1.35 g/cc
- Water Absorption: 0.95 %
- Tensile Strength, Ultimate: 110 MPa
- Elongation at Break: 4.5 %
- Tensile Modulus: 6.20 GPa
$ 1466/MT
- Density: 1.35 g/cc
- Water Absorption: 0.95 % @Temperature 23.0 °C, Time 86400 sec
- Tensile Strength at Break: 190 MPa
- Elongation at Break: 3.8 %
- Tensile Modulus: 9.60 GPa
$ 1598/MT
- Density: 1.32 g/cc
- Elongation at Break: 4.0 %
- Tensile Modulus: 6.30 GPa
- Flexural Strength: 155 MPa
- Flexural Modulus: 5.00 GPa
$ 1540/MT
- Density: 1.37 g/cc
- Water Absorption: 0.80 % @Temperature 23.0 °C, Time 86400 sec
- Viscosity: 120 cP @Shear Rate 1000 1/s, Temperature 275 °C
- Viscosity: 300 cP @Shear Rate 100 1/s, Temperature 275 °C
- Linear Mold Shrinkage: 0.0062 cm/cm
$ 1814/MT
- Density: 1.35 g/cc
- Water Absorption: 0.80 % @Temperature 23.0 °C, Time 86400 sec
- Viscosity: 120 cP @Shear Rate 100 1/s, Temperature 290 °C
- Viscosity: 150 cP @Shear Rate 100 1/s, Temperature 280 °C
- Viscosity: 200 cP @Shear Rate 100 1/s, Temperature 270 °C
$ 1602/MT
- Density: 1.37 g/cc
- Tensile Strength at Break: 60.0 MPa
- Elongation at Break: 12 %
- Tensile Modulus: 2.50 GPa
- Flexural Modulus: 1.90 GPa
$ 1895/MT
- Density: 1.34 g/cc
- Water Absorption: 0.95 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage: 0.0054 cm/cm
- Linear Mold Shrinkage, Flow: 0.0035 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0065 cm/cm
$ 1736/MT
- Density: 1.32 g/cc
- Tensile Strength at Break: 110 MPa
- Elongation at Break: 3.5 %
- Tensile Modulus: 6.20 GPa
- Flexural Strength: 155 MPa
$ 1820/MT
- Density: 1.35 g/cc
- Tensile Strength at Break: 130 MPa
- Elongation at Break: 4.0 %
- Tensile Modulus: 7.50 GPa
- Flexural Strength: 180 MPa
$ 2459/MT
- Density: 1.35 g/cc
- Water Absorption: 0.95 %
- Tensile Strength, Ultimate: 190 MPa
- Elongation at Break: 3.8 %
- Tensile Modulus: 9.60 GPa
$ 2012/MT
- Density: 1.35 g/cc
- Tensile Strength at Break: 110 MPa
- Elongation at Break: 4.5 %
- Tensile Modulus: 6.20 GPa
- Flexural Modulus: 5.50 GPa
$ 1485/MT
- Density: 1.35 g/cc
- Water Absorption: 0.95 %
- Tensile Strength at Break: 193 MPa
- Elongation at Break: 3.8 %
- Tensile Modulus: 9.58 GPa
$ 1644/MT
- Density: 1.37 g/cc
- Water Absorption: 0.80 % @Temperature 23.0 °C, Time 86400 sec
- Viscosity: 20 cP @Shear Rate 1000 1/s, Temperature 280 °C
- Viscosity: 20 cP @Shear Rate 1000 1/s, Temperature 290 °C
- Viscosity: 20 cP @Shear Rate 1000 1/s, Temperature 300 °C
$ 1576/MT
- Density: 1.37 g/cc
- Tensile Strength at Break: 140 MPa
- Elongation at Break: 4.0 %
- Tensile Modulus: 7.50 GPa
- Flexural Modulus: 6.40 GPa
$ 1929/MT
- Density: 1.32 g/cc
- Water Absorption: 0.90 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage: 0.0071 cm/cm
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0085 cm/cm
$ 1676/MT
- Density: 1.32 g/cc
- Water Absorption: 0.90 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage: 0.0055 cm/cm
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
$ 1709/MT
- Density: 1.57 g/cc
- Water Absorption: 0.80 % @Temperature 23.0 °C, Time 86400 sec
- Viscosity: 70 cP @Shear Rate 100 1/s, Temperature 300 °C
- Viscosity: 105 cP @Shear Rate 100 1/s, Temperature 290 °C
- Viscosity: 120 cP @Shear Rate 100 1/s, Temperature 280 °C
$ 2413/MT
- Density: 1.46 g/cc
- Linear Mold Shrinkage, Flow: 0.0123 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0056 cm/cm
- Tensile Strength at Break: 150 MPa
- Elongation at Break: 2.5 %
$ 2086/MT
- Density: 1.29 g/cc
- Tensile Strength at Break: 85.0 MPa
- Elongation at Break: 9.0 %
- Tensile Modulus: 4.50 GPa
- Flexural Modulus: 3.50 GPa
$ 1674/MT
- Density: 1.31 g/cc
- Water Absorption: 1.0 %
- Tensile Strength at Break: 162 MPa
- Elongation at Break: 3.9 %
- Tensile Modulus: 8.41 GPa
$ 1758/MT
- Density: 1.62 g/cc
- Tensile Strength at Break: 85.0 MPa
- Elongation at Break: 6.0 %
- Tensile Modulus: 8.05 GPa
- Charpy Impact Unnotched: 4.00 J/cm²
$ 2069/MT
- Density: 1.37 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Tensile Strength at Break: 120 MPa
- Elongation at Break: 2.3 %
$ 1880/MT
- Density: 1.37 g/cc
- Tensile Strength at Break: 135 MPa
- Elongation at Break: 4.0 %
- Tensile Modulus: 7.50 GPa
- Izod Impact, Notched (ISO): 16.0 kJ/m²
$ 1705/MT
- Tensile Strength at Break: 120 MPa
- Elongation at Break: 4.5 %
- Tensile Modulus: 6.20 GPa
- Volume Resistivity: 1.00e+11 ohm-cm
- Dielectric Constant: 4.5
$ 1454/MT
- Density: 1.37 g/cc
- Tensile Strength at Break: 140 MPa
- Elongation at Break: 4.0 %
- Tensile Modulus: 7.50 GPa
- Flexural Strength: 185 MPa
$ 1774/MT
- Density: 1.27 g/cc
- Tensile Strength at Break: 110 MPa
- Elongation at Break: 5.5 %
- Tensile Modulus: 6.60 GPa
- Flexural Strength: 180 MPa
$ 1522/MT
- Density: 1.32 g/cc
- Water Absorption: 0.90 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage: 0.0075 cm/cm
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
$ 1595/MT
- Density: 1.42 g/cc
- Tensile Strength at Break: 97.0 MPa
- Elongation at Break: 5.1 %
- Tensile Modulus: 8.50 GPa
- Flexural Strength: 175 MPa
$ 2595/MT
- Density: 1.32 g/cc
- Water Absorption: 0.90 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage: 0.0047 cm/cm
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0085 cm/cm
$ 1508/MT
- Density: 1.32 g/cc
- Water Absorption: 0.90 % @Temperature 23.0 °C, Time 86400 sec
- Viscosity: 30 cP @Shear Rate 1000 1/s, Temperature 280 °C
- Viscosity: 30 cP @Shear Rate 1000 1/s, Temperature 290 °C
- Viscosity: 30 cP @Shear Rate 1000 1/s, Temperature 300 °C
$ 1446/MT
- Density: 1.39 g/cc
- Tensile Strength at Break: 140 MPa
- Tensile Modulus: 7.60 GPa
- Flexural Modulus: 6.00 GPa
- Izod Impact, Notched (ISO): 20.0 kJ/m²
$ 1673/MT
- Density: 1.37 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength at Break: 140 MPa
- Elongation at Break: 2.8 %
$ 2000/MT
- Density: 1.39 g/cc
- Water Absorption: 0.75 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0108 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0036 cm/cm
- Tensile Strength at Break: 200 MPa
$ 1886/MT
- Tensile Strength at Break: 160 MPa
- Elongation at Break: 2.1 %
- Tensile Modulus: 10.4 GPa
- Charpy Impact Unnotched: 4.50 J/cm²
- Charpy Impact, Notched: 0.810 J/cm²
$ 1949/MT
- Density: 1.37 g/cc
- Tensile Strength at Break: 135 MPa
- Elongation at Break: 4.0 %
- Tensile Modulus: 7.50 GPa
- Flexural Strength: 185 MPa
$ 2489/MT
- Density: 1.32 g/cc
- Tensile Strength at Break: 90.0 MPa
- Elongation at Break: 7.0 %
- Tensile Modulus: 5.40 GPa
- Flexural Modulus: 5.20 GPa
$ 1636/MT
- Density: 1.37 g/cc
- Tensile Strength at Break: 135 MPa
- Elongation at Break: 4.0 %
- Tensile Modulus: 7.50 GPa
- Izod Impact, Notched (ISO): 16.0 kJ/m²
$ 1447/MT
- Density: 1.37 g/cc
- Water Absorption: 0.80 %
- Hardness, Rockwell R: 119
- Tensile Strength at Break: 175 MPa
- Elongation at Break: 4.0 %
$ 2247/MT
- Density: 1.37 g/cc
- Tensile Strength at Break: 135 MPa
- Tensile Stress: 25.0 MPa @Strain 1.00 %, Temperature 150 °C
- Tensile Stress: 30.0 MPa @Strain 1.00 %, Temperature 120 °C
- Tensile Stress: 40.0 MPa @Strain 1.00 %, Temperature 80.0 °C
$ 1843/MT
- Density: 1.32 g/cc
- Tensile Strength at Break: 90.0 MPa
- Elongation at Break: 10 %
- Tensile Modulus: 4.90 GPa
- Charpy Impact Unnotched: 10.2 J/cm² @Temperature -30.0 °C
$ 1551/MT
- Density: 1.34 g/cc
- Water Absorption: 0.95 % @Temperature 23.0 °C, Time 86400 sec
- Tensile Strength at Break: 180 MPa
- Elongation at Break: 3.3 %
- Tensile Modulus: 9.60 GPa
$ 1873/MT
- Density: 1.32 g/cc
- Tensile Strength at Break: 120 MPa
- Elongation at Break: 4.0 %
- Tensile Modulus: 6.30 GPa
- Flexural Modulus: 5.00 GPa
$ 1497/MT
- Moisture Content: <= 0.15 %
$ 1708/MT
- Density: 1.37 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength at Break: 100 MPa
- Tensile Modulus: 6.00 GPa
$ 1928/MT
- Density: 1.29 g/cc
- Water Absorption: 1.2 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage: 0.0075 cm/cm
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
$ 1490/MT
- Density: 1.46 g/cc
- Moisture Content: <= 0.20 %
$ 1494/MT
- Density: 1.37 g/cc
- Water Absorption: 0.95 % @Temperature 23.0 °C, Time 86400 sec
- Tensile Strength at Break: 185 MPa
- Tensile Strength, Yield: 185 MPa
- Elongation at Break: 3.0 %
$ 2493/MT
- Density: 1.32 g/cc
- Water Absorption: 0.88 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage: 0.0084 cm/cm
- Linear Mold Shrinkage, Flow: 0.0039 cm/cm
- Linear Mold Shrinkage, Flow: 0.0084 cm/cm
$ 1554/MT
- Density: 1.37 g/cc
- Water Absorption: 0.80 % @Temperature 23.0 °C, Time 86400 sec
- Viscosity: 20 cP @Shear Rate 1000 1/s, Temperature 280 °C
- Viscosity: 20 cP @Shear Rate 1000 1/s, Temperature 290 °C
- Viscosity: 20 cP @Shear Rate 1000 1/s, Temperature 300 °C
$ 2099/MT
- Density: 1.37 g/cc
- Water Absorption: 0.80 %
- Linear Mold Shrinkage: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Tensile Strength, Ultimate: 135 MPa
$ 1712/MT
- Tensile Strength at Break: 142 MPa
- Elongation at Break: 142 %
- Tensile Modulus: 8.90 GPa
- Flexural Strength: 221 MPa
- Flexural Modulus: 6.626 GPa
$ 2314/MT
- Tensile Strength at Break: 189.3 MPa
- Elongation at Break: 3.3 %
- Tensile Modulus: 10.7 GPa
- Flexural Strength: 285 MPa
- Flexural Modulus: 9.088 GPa
$ 2401/MT
- Density: 1.14 g/cc
- Tensile Strength at Break: 40.0 MPa
- Tensile Strength, Yield: 60.0 MPa
- Elongation at Break: 200 %
- Elongation at Yield: 10 %
$ 1556/MT
- Density: 1.37 g/cc
- Water Absorption: 0.80 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Tensile Strength at Break: 195 MPa
$ 1867/MT
- Density: 1.46 g/cc
- Water Absorption: 0.73 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage: 0.0030 cm/cm
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
$ 1605/MT
- Density: 1.35 g/cc
- Water Absorption: 0.80 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage: 0.0062 cm/cm
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
$ 1747/MT
- Density: 1.38 g/cc
- Volume Resistivity: 1.00e+10 ohm-cm
- Surface Resistance: 1.00e+11 ohm
- Dielectric Constant: 4.0
- Dielectric Strength: 30.0 kV/mm
$ 1704/MT
- Density: 1.14 g/cc
- Water Absorption: 1.3 % @Temperature 23.0 °C, Time 86400 sec
- Viscosity: 20 cP @Shear Rate 1000 1/s, Temperature 290 °C
- Viscosity: 20.5 cP @Shear Rate 1000 1/s, Temperature 280 °C
- Viscosity: 60 cP @Shear Rate 100 1/s, Temperature 300 °C
$ 1824/MT
- Density: 1.37 g/cc
- Tensile Strength at Break: 115 MPa
- Elongation at Break: 8.0 %
- Tensile Modulus: 6.50 GPa
- Flexural Modulus: 4.70 GPa
$ 1864/MT
- Density: 1.34 g/cc
- Water Absorption: 0.95 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0035 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0065 cm/cm
- Tensile Strength at Break: 110 MPa
$ 1547/MT
- Density: 1.37 g/cc
- Water Absorption: 0.80 %
- Linear Mold Shrinkage: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Tensile Strength, Ultimate: 135 MPa
$ 1509/MT
- Density: 1.37 g/cc
- Water Absorption: 0.80 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage: 0.0062 cm/cm
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
$ 1562/MT
- Density: 1.37 g/cc
- Water Absorption: 0.80 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage: 0.0062 cm/cm
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
$ 1695/MT
- Density: 1.54 g/cc
- Tensile Strength at Break: 78.0 MPa
- Elongation at Break: 3.0 %
- Tensile Modulus: 7.00 GPa
- Izod Impact, Notched (ISO): 11.0 kJ/m²
$ 1758/MT
- Density: 1.38 g/cc
- Tensile Strength at Break: 88.0 MPa
- Elongation at Break: 2.7 %
- Tensile Modulus: 8.00 GPa
- Charpy Impact Unnotched: 8.50 J/cm²
$ 1877/MT
- Density: 1.46 g/cc
- Tensile Strength at Break: 115 MPa
- Elongation at Break: 4.2 %
- Tensile Modulus: 8.41 GPa
- Charpy Impact Unnotched: 7.80 J/cm²
$ 1446/MT
- Density: 1.37 g/cc
- Water Absorption: 0.95 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage: 0.0071 cm/cm
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
$ 1453/MT
- Density: 1.42 g/cc
- Water Absorption: 0.90 % @Temperature 23.0 °C, Time 86400 sec
- Viscosity: 50 cP @Shear Rate 1000 1/s, Temperature 270 °C
- Viscosity: 120 cP @Shear Rate 1000 1/s, Temperature 250 °C
- Viscosity: 120 cP @Shear Rate 100 1/s, Temperature 270 °C
$ 1690/MT
- Density: 1.36 g/cc
- Tensile Strength at Break: 110 MPa
- Tensile Stress: 42.0 MPa @Strain 1.00 %
- Tensile Stress: 70.0 MPa @Strain 2.00 %
- Tensile Stress: 85.0 MPa @Strain 3.00 %
$ 1493/MT
- Density: 1.38 g/cc
- Water Absorption: 0.83 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage: 0.0050 cm/cm
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
$ 1506/MT
- Density: 1.34 g/cc
- Tensile Strength at Break: 110 MPa
- Elongation at Break: 4.5 %
- Tensile Modulus: 6.20 GPa
- Flexural Strength: 140 MPa
$ 1902/MT
- Density: 1.37 g/cc
- Tensile Strength at Break: 115 MPa
- Tensile Strength, Yield: 115 MPa
- Elongation at Break: 8.0 %
- Tensile Modulus: 6.50 GPa
$ 1527/MT
- Density: 1.54 g/cc
- Tensile Strength at Break: 95.0 MPa
- Elongation at Break: 2.5 %
- Tensile Modulus: 8.80 GPa
- Izod Impact, Notched (ISO): 9.80 kJ/m²
$ 2290/MT
- Density: 1.37 g/cc
- Water Absorption: 0.80 %
- Linear Mold Shrinkage: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Tensile Strength, Ultimate: 190 MPa
$ 2110/MT
- Density: 1.37 g/cc
- Tensile Strength at Break: 115 MPa
- Elongation at Break: 8.0 %
- Tensile Modulus: 5.90 GPa
- Flexural Strength: 140 MPa
$ 1490/MT
- Density: 1.35 g/cc
- Tensile Strength at Break: 135 MPa
- Elongation at Break: 4.0 %
- Tensile Modulus: 7.50 GPa
- Flexural Modulus: 6.50 GPa
$ 2508/MT
- Density: 1.62 g/cc
- Water Absorption: 0.95 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage: 0.0075 cm/cm
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
$ 1482/MT
- Density: 1.34 g/cc
- Tensile Strength at Break: 110 MPa
- Elongation at Break: 5.5 %
- Tensile Modulus: 6.20 GPa
- Flexural Modulus: 5.20 GPa
$ 1481/MT
- Density: 1.32 g/cc
- Tensile Strength at Break: 125 MPa
- Elongation at Break: 2.5 %
- Tensile Modulus: 7.80 GPa
- Flexural Strength: 200 MPa
Delivery 30% Glass Fiber Filled Solvay
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):| Country | 20’ Container | 40’ Container | 5,000 MT |
|---|---|---|---|
| 🇦🇺 Australia | $3345 | $4181 | $401400 |
| 🇦🇹 Austria | $2825 | $3531 | $339000 |
| 🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
| 🇦🇱 Albania | $2500 | $3125 | $300000 |
| 🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
| 🇦🇴 Angola | $2762.5 | $3453 | $331500 |
| 🇦🇷 Argentina | $3230 | $4038 | $387600 |
| 🇦🇲 Armenia | $2625 | $3281 | $315000 |
| 🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
| 🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
| 🇧🇭 Bahrain | $3095 | $3869 | $371400 |
| 🇧🇾 Belarus | $2825 | $3531 | $339000 |
| 🇧🇿 Belize | $3155 | $3944 | $378600 |
| 🇧🇪 Belgium | $2575 | $3219 | $309000 |
| 🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
| 🇧🇴 Bolivia | $3230 | $4038 | $387600 |
| 🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
| 🇧🇷 Brazil | $3120 | $3900 | $374400 |
| 🇭🇺 Hungary | $2575 | $3219 | $309000 |
| 🇻🇪 Venezuela | $3230 | $4038 | $387600 |
| 🇻🇳 Vietnam | $2625 | $3281 | $315000 |
| 🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
| 🇬🇹 Guatemala | $3230 | $4038 | $387600 |
| 🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
| 🇩🇪 Germany | $2475 | $3094 | $297000 |
| 🇭🇳 Honduras | $3230 | $4038 | $387600 |
| 🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
| 🇬🇷 Greece | $2575 | $3219 | $309000 |
| 🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
| 🇩🇰 Denmark | $2400 | $3000 | $288000 |
| 🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
| 🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
| 🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
| 🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
| 🇮🇱 Israel | $2625 | $3281 | $315000 |
| 🇮🇳 India | $3712.5 | $4641 | $445500 |
| 🇮🇩 Indonesia | $3095 | $3869 | $371400 |
| 🇯🇴 Jordan | $2625 | $3281 | $315000 |
| 🇮🇶 Iraq | $2625 | $3281 | $315000 |
| 🇮🇷 Iran | $3095 | $3869 | $371400 |
| 🇮🇪 Ireland | $2500 | $3125 | $300000 |
| 🇮🇸 Iceland | $2575 | $3219 | $309000 |
| 🇪🇸 Spain | $2500 | $3125 | $300000 |
| 🇮🇹 Italy | $2400 | $3000 | $288000 |
| 🇾🇪 Yemen | $2625 | $3281 | $315000 |
| 🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
| 🇰🇭 Cambodia | $3095 | $3869 | $371400 |
| 🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
| 🇨🇦 Canada | $3230 | $4038 | $387600 |
| 🇶🇦 Qatar | $2625 | $3281 | $315000 |
| 🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
| 🇨🇾 Cyprus | $2625 | $3281 | $315000 |
| 🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
| 🇨🇳 China | $3712.5 | $4641 | $445500 |
| 🇨🇴 Colombia | $3230 | $4038 | $387600 |
| 🇰🇷 Korea South | $2625 | $3281 | $315000 |
| 🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
| 🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
| 🇨🇺 Cuba | $3230 | $4038 | $387600 |
| 🇰🇼 Kuwait | $2625 | $3281 | $315000 |
| 🇱🇻 Latvia | $2575 | $3219 | $309000 |
| 🇱🇧 Lebanon | $2625 | $3281 | $315000 |
| 🇱🇾 Libya | $2762.5 | $3453 | $331500 |
| 🇱🇹 Lithuania | $2500 | $3125 | $300000 |
| 🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
| 🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
| 🇲🇾 Malaysia | $2625 | $3281 | $315000 |
| 🇲🇹 Malta | $2500 | $3125 | $300000 |
| 🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
| 🇲🇽 Mexico | $3155 | $3944 | $378600 |
| 🇲🇩 Moldova | $2400 | $3000 | $288000 |
| 🇲🇨 Monaco | $2475 | $3094 | $297000 |
| 🇲🇳 Mongolia | $2625 | $3281 | $315000 |
| 🇲🇲 Myanmar | $2625 | $3281 | $315000 |
| 🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
| 🇳🇵 Nepal | $2625 | $3281 | $315000 |
| 🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
| 🇳🇱 Netherlands | $2575 | $3219 | $309000 |
| 🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
| 🇳🇿 New Zealand | $3345 | $4181 | $401400 |
| 🇳🇴 Norway | $2400 | $3000 | $288000 |
| 🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
| 🇴🇲 Oman | $2625 | $3281 | $315000 |
| 🇵🇰 Pakistan | $2625 | $3281 | $315000 |
| 🇵🇦 Panama | $3230 | $4038 | $387600 |
| 🇵🇾 Paraguay | $3155 | $3944 | $378600 |
| 🇵🇪 Peru | $3230 | $4038 | $387600 |
| 🇵🇱 Poland | $2575 | $3219 | $309000 |
| 🇵🇹 Portugal | $2500 | $3125 | $300000 |
| 🇷🇺 Russia | $2575 | $3219 | $309000 |
| 🇷🇴 Romania | $2475 | $3094 | $297000 |
| 🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
| 🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
| 🇷🇸 Serbia | $2575 | $3219 | $309000 |
| 🇸🇬 Singapore | $3095 | $3869 | $371400 |
| 🇸🇾 Syria | $3095 | $3869 | $371400 |
| 🇸🇰 Slovakia | $2500 | $3125 | $300000 |
| 🇸🇮 Slovenia | $2500 | $3125 | $300000 |
| 🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
| 🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
| 🇺🇸 United States | $2902.5 | $3628 | $348300 |
| 🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
| 🇹🇭 Thailand | $2625 | $3281 | $315000 |
| 🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
| 🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
| 🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
| 🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
| 🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
| 🇹🇷 Turkey | $2625 | $3281 | $315000 |
| 🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
| 🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
| 🇺🇦 Ukraine | $2500 | $3125 | $300000 |
| 🇺🇾 Uruguay | $2675 | $3344 | $321000 |
| 🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
| 🇵🇭 Philippines | $2625 | $3281 | $315000 |
| 🇫🇮 Finland | $2500 | $3125 | $300000 |
| 🇫🇷 France | $2575 | $3219 | $309000 |
| 🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
| 🇲🇪 Montenegro | $2575 | $3219 | $309000 |
| 🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
| 🇨🇱 Chile | $3355 | $4194 | $402600 |
| 🇨🇭 Switzerland | $2575 | $3219 | $309000 |
| 🇸🇪 Sweden | $2500 | $3125 | $300000 |
| 🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
| 🇪🇨 Ecuador | $3155 | $3944 | $378600 |
| 🇦🇸 American Samoa | $3345 | $4181 | $401400 |
| 🇸🇻 El Salvador | $3230 | $4038 | $387600 |
| 🇪🇪 Estonia | $2575 | $3219 | $309000 |
| 🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
| 🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
| 🇯🇵 Japan | $3095 | $3869 | $371400 |
| 🇦🇩 Andorra | $2500 | $3125 | $300000 |
| 🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
| 🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
| 🇧🇧 Barbados | $3230 | $4038 | $387600 |
| 🇧🇹 Bhutan | $3095 | $3869 | $371400 |
| 🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
| 🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
| 🇧🇳 Brunei | $2625 | $3281 | $315000 |
| 🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
| 🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
| 🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
| 🇹🇩 Chad | $2762.5 | $3453 | $331500 |
| 🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
| 🇧🇯 Benin | $2762.5 | $3453 | $331500 |
| 🇩🇲 Dominica | $3230 | $4038 | $387600 |
| 🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
| 🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
| 🇫🇯 Fiji | $3345 | $4181 | $401400 |
| 🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
| 🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
| 🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
| 🇰🇮 Kiribati | $3345 | $4181 | $401400 |
| 🇬🇩 Grenada | $3355 | $4194 | $402600 |
| 🇬🇺 Guam | $3345 | $4181 | $401400 |
| 🇬🇾 Guyana | $3230 | $4038 | $387600 |
| 🇭🇹 Haiti | $3120 | $3900 | $374400 |
| 🇯🇲 Jamaica | $3230 | $4038 | $387600 |
| 🇰🇵 Korea, North | $2625 | $3281 | $315000 |
| 🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
| 🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
| 🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
| 🇲🇻 Maldives | $2625 | $3281 | $315000 |
| 🇲🇱 Mali | $2762.5 | $3453 | $331500 |
| 🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
| 🇨🇼 Curaçao | $3230 | $4038 | $387600 |
| 🇦🇼 Aruba | $3120 | $3900 | $374400 |
| 🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
| 🇳🇪 Niger | $2762.5 | $3453 | $331500 |
| 🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
| 🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
| 🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
| 🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
| 🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
| 🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
| 🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
| 🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
| 🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
| 🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
| 🇸🇲 San Marino | $2500 | $3125 | $300000 |
| 🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
| 🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
| 🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
| 🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
| 🇸🇷 Suriname | $3230 | $4038 | $387600 |
| 🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
| 🇹🇬 Togo | $2762.5 | $3453 | $331500 |
| 🇹🇴 Tonga | $3345 | $4181 | $401400 |
| 🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
| 🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
| 🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, old cargo ship. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.