$ 1677/MT
- Density: 0.928 g/cc
- Thickness: 40.0 microns
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 300 %
- Film Elongation at Break, TD: 550 %
$ 1832/MT
- Density: 0.922 g/cc
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 1100 ppm
- Slip Level: 700 ppm
- Film Elongation at Break, MD: 400 %
$ 1559/MT
- Density: 0.936 g/cc
- Oxidative Induction Time (OIT): >= 40 min
- High Load Melt Index: 10 g/10 min @Load 21.6 kg, Temperature 190 °C
- Tensile Strength, Yield: 22.00 MPa
- Elongation at Yield: 10 %
$ 1545/MT
- Density: 0.964 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 63
- Tensile Strength, Yield: 27.0 MPa
$ 1552/MT
- Density: 0.919 g/cc
- Melt Flow: 1.25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 11.0 MPa
- Film Elongation at Break, MD: 550 %
- Film Elongation at Break, TD: 710 %
$ 1872/MT
- Density: 0.948 g/cc
- Environmental Stress Crack Resistance: >= 5.0 hour @Pressure 0.800 MPa, Temperature 80.0 °C
- Oxidative Induction Time (OIT): >= 20 min @Temperature 200 °C
- Melt Flow: 0.40 g/10 min @Load 5.00 kg, Temperature 190 °C
- Tensile Strength, Yield: 19.0 MPa
$ 1456/MT
- Density: 0.923 g/cc
- Water Vapor Transmission: 8.00 g/m²/day
- Oxygen Transmission Rate: 5000 cc/m²/day
- Thickness: 40.0 microns
- Melt Flow: 0.20 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 2341/MT
- Density: 0.954 g/cc
- Melt Flow: 0.30 g/10 min @Load 5.00 kg, Temperature 190 °C
$ 1501/MT
- Density: 0.931 g/cc
- Water Vapor Transmission: 6.00 g/m²/day
- Oxygen Transmission Rate: 3500 cc/m²/day
- Thickness: 40.0 microns
- Melt Flow: 0.20 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 2366/MT
- Density: 0.950 g/cc
- Density: 0.960 g/cc
- ESCR 10% Igepal®: >= 10000 hour
- Carbon Black Loading: 2.0 %
- Melt Flow: >= 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1569/MT
- Density: 0.943 g/cc
- Environmental Stress Crack Resistance: >= 2000 hour @Temperature 80.0 °C
- Melt Flow: 0.90 g/10 min @Load 5.00 kg, Temperature 190 °C
- Tensile Strength, Yield: 19.00 MPa
- Tensile Modulus: 0.800 GPa
$ 2136/MT
- Density: 0.948 g/cc
- Density: 0.959 g/cc
- Environmental Stress Crack Resistance: >= 5.0 hour @Pressure 0.920 MPa, Temperature 80.0 °C
- Oxidative Induction Time (OIT): >= 20 min @Temperature 210 °C
- Carbon Black Loading: 2.0 - 2.5 %
$ 1551/MT
- Density: 0.964 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 63
- Tensile Strength, Yield: 27.0 MPa
$ 1542/MT
- Density: 0.963 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 64
- Tensile Strength at Break: 33.0 MPa
- Elongation at Break: 600 %
$ 1498/MT
- Bulk Density: 0.500 - 0.600 g/cc
- Density: 0.943 g/cc
- Density: 0.945 g/cc
- Thermal Stress Crack Resistance: 1.50 hour @Temperature 105 °C
- Oxidative Induction Time (OIT): >= 50 min @Temperature 200 °C
$ 2060/MT
- Density: 0.919 g/cc
- Molecular Weight: 133000 g/mol
- Melt Flow: 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 12.0 MPa
- Film Elongation at Break, MD: 740 %
$ 2382/MT
- Density: 0.954 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 61
- Tensile Strength, Yield: 24.0 MPa
$ 1818/MT
- Density: 0.927 g/cc
- Thickness: 40.0 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 750 ppm
- Film Elongation at Break, MD: 230 %
$ 1984/MT
- Density: 0.923 g/cc
- Density: 1.05 g/cc
- Density: 2.00 g/cc
- Melt Flow: 0.90 g/10 min
- Tensile Strength, Yield: >= 14.58 MPa
$ 1702/MT
- Density: 1.10 g/cc
- Water Absorption: 0.030 %
- Tensile Strength at Break: <= 4.40 MPa
- Tensile Strength at Break: >= 22.0 MPa
- Elongation at Break: 380 %
$ 1907/MT
- Density: 0.956 g/cc
- Melt Flow: 0.30 g/10 min @Load 5.00 kg, Temperature 190 °C
- Melt Flow: 9.0 g/10 min @Load 21.6 kg, Temperature 190 °C
- Film Elongation at Break, MD: 250 %
- Film Elongation at Break, TD: 300 %
$ 1472/MT
- Density: 0.923 g/cc
- Melt Flow: 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 250 %
- Film Elongation at Break, TD: 550 %
- Tensile Modulus: 0.230 GPa
$ 2204/MT
- Density: 0.956 g/cc
- Density: 0.958 g/cc
- High Load Melt Index: 6.0 g/10 min @Load 21.6 kg, Temperature 190 °C
- Maximum Service Temperature, Air: 210 °C
$ 1655/MT
- Density: 0.927 g/cc
- Melt Flow: 0.30 g/10 min @Load 5.00 kg, Temperature 190 °C
- Hardness, Shore D: 52
- Tensile Strength, Yield: 12.0 MPa
- Elongation at Break: 700 %
$ 1627/MT
- Density: 0.923 g/cc
- Environmental Stress Crack Resistance: >= 96 hour @Temperature 50.0 °C
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 52
- Tensile Strength at Break: <= 11.25 MPa
$ 2234/MT
- Density: 0.923 g/cc
- Density: 0.933 g/cc
- Melt Index of Compound: 0.90 g/10 min
- Tensile Strength, Yield: >= 13.28 MPa
- Tensile Strength, Yield: 14.8 MPa
$ 1479/MT
- Density: 0.956 g/cc
- Density: 0.959 g/cc
- High Load Melt Index: 6.0 g/10 min @Load 21.6 kg, Temperature 190 °C
- Maximum Service Temperature, Air: 210 °C
$ 1703/MT
- Density: 0.922 g/cc
- Melt Flow: 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 850 ppm
- Film Elongation at Break, MD: 300 %
- Film Elongation at Break, TD: 500 %
$ 1730/MT
- Density: 0.958 g/cc
- ESCR 10% Igepal®: >= 100 hour
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 1.3 g/10 min @Load 5.00 kg, Temperature 190 °C
- High Load Melt Index: 28 g/10 min @Load 21.6 kg, Temperature 190 °C
$ 1813/MT
- Density: 0.922 g/cc
- Melt Flow: 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 850 ppm
- Slip Level: 500 ppm
- Film Elongation at Break, MD: 350 %
$ 1588/MT
- Density: 0.944 g/cc
- Environmental Stress Crack Resistance: >= 5.0 hour @Temperature 50.0 °C
- Melt Flow: 1.7 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 58
- Hardness, Shore D: 61
$ 2409/MT
- Density: 0.959 g/cc
- Environmental Stress Crack Resistance: 1.0 hour @Pressure 0.920 MPa, Temperature 80.0 °C
- Oxidative Induction Time (OIT): >= 20 min @Temperature 200 °C
- Carbon Black Loading: 2.0 %
- Melt Flow: 0.55 g/10 min @Load 5.00 kg, Temperature 190 °C
$ 1465/MT
- Density: 0.951 g/cc
- Oxidative Induction Time (OIT): >= 50 min @Temperature 210 °C
- Melt Flow: 10 g/10 min @Load 21.6 kg, Temperature 190 °C
- Tensile Strength, Yield: 22.0 MPa
$ 1520/MT
- Density: 0.945 g/cc
- Environmental Stress Crack Resistance: >= 80 hour @Temperature 50.0 °C
- Oxidative Induction Time (OIT): >= 60 min @Temperature 200 °C
- Melt Flow: 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 58
$ 1516/MT
- Density: 0.945 g/cc
- Environmental Stress Crack Resistance: >= 48 hour @Temperature 50.0 °C
- Oxidative Induction Time (OIT): 50 min @Temperature 200 °C
- Melt Flow: 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 61
$ 1827/MT
- Density: 0.942 g/cc
- Density: 0.954 g/cc
- ESCR 10% Igepal®: >= 2000 hour @Temperature 50.0 °C
- Melt Flow: 1.7 g/10 min
- Hardness, Shore D: 61
$ 1491/MT
- Density: 0.947 g/cc
- Melt Flow: 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 131 °C
- Molecular Weight: medium distribution
$ 1516/MT
- Density: 0.923 g/cc
- Density: 0.936 g/cc
- Environmental Stress Crack Resistance: >= 5.0 hour @Temperature 50.0 °C
- Melt Flow: 0.85 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 53
$ 1988/MT
- Density: 0.923 g/cc
- Water Vapor Transmission: 8.00 g/m²/day
- Oxygen Transmission Rate: 5000 cc/m²/day
- Thickness: 40.0 microns
- Melt Flow: 0.40 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1915/MT
- Density: 0.922 g/cc
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 400 %
- Film Elongation at Break, TD: 600 %
- Tensile Modulus: 0.190 GPa
$ 1672/MT
- Density: 0.923 g/cc
- Density: 1.38 g/cc
- Melt Index of Compound: 0.90 g/10 min
- Tensile Strength, Yield: >= 13.28 MPa
- Tensile Strength, Yield: 14.8 MPa
$ 1536/MT
- Density: 0.958 g/cc
- Water Vapor Transmission: 4.10 g/m²/day @Temperature 38.0 °C
- Oxygen Transmission Rate: 2210 cc/m²/day @Temperature 23.0 °C
- Molecular Weight: 130000 g/mol
- Melt Flow: 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1677/MT
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 50
- Tensile Strength at Break: >= 13.5 MPa
- Tensile Strength at Break: 15.0 MPa
- Elongation at Break: 400 %
$ 1577/MT
- Density: 0.923 g/cc
- Density: 1.05 g/cc
- Melt Flow: 0.90 g/10 min
- Tensile Strength, Yield: >= 13.28 MPa
- Tensile Strength, Yield: 14.8 MPa
$ 1894/MT
- Density: 0.951 g/cc
- High Load Melt Index: 10 g/10 min @Load 21.6 kg, Temperature 190 °C
- Tensile Strength, Yield: 22.00 MPa
- Elongation at Break: >= 600 %
$ 2361/MT
- Density: 0.923 g/cc
- Density: 0.941 g/cc
- Melt Flow: 0.90 g/10 min
- Tensile Strength, Yield: >= 13.28 MPa
- Tensile Strength, Yield: 14.8 MPa
$ 1496/MT
- Density: 0.922 g/cc
- Water Absorption: 0.020 %
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: <= 3.40 MPa
- Tensile Strength at Break: >= 17.0 MPa
$ 2299/MT
- Density: 0.923 g/cc
- Degree of Crosslinking: 12 %
- Hardness, Shore D: 50
- Tensile Strength, Yield: >= 14.3 MPa
- Tensile Strength, Yield: 15.9 MPa
$ 1768/MT
- Bulk Density: 0.500 - 0.600 g/cc
- Density: 0.924 g/cc
- Water Absorption: 0.020 %
- Melt Flow: 2.8 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: <= 3.40 MPa
$ 1766/MT
- Density: 1.22 g/cc
- Tensile Strength, Yield: >= 13.28 MPa
- Tensile Strength, Yield: 14.8 MPa
- Elongation at Break: 315 %
- Elongation at Break: 350 %
$ 1449/MT
- Density: 0.956 g/cc
- Density: 0.966 g/cc
- Carbon Black Loading: 2.2 %
- High Load Melt Index: 6.0 g/10 min @Load 21.6 kg, Temperature 190 °C
- Maximum Service Temperature, Air: 210 °C
$ 1958/MT
- Density: 0.954 g/cc
- Environmental Stress Crack Resistance: 500 hour
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 1.5 g/10 min @Load 5.00 kg, Temperature 190 °C
- Melt Flow: 32 g/10 min @Load 21.6 kg, Temperature 190 °C
$ 1597/MT
- Density: 0.923 g/cc
- Density: 1.38 g/cc
- Melt Index of Compound: 0.90 g/10 min
- Tensile Strength, Yield: >= 13.28 MPa
- Tensile Strength, Yield: 14.8 MPa
$ 1581/MT
- Density: 0.934 g/cc
- ESCR 10% Igepal®: >= 300 hour
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 17.9 MPa
- Flexural Modulus: 0.490 GPa
$ 1651/MT
- Density: 1.17 g/cc
- Volume Resistivity: 50 ohm-cm @Temperature 23.0 °C
- Volume Resistivity: 90 ohm-cm @Temperature 90.0 °C
- Shelf Life: 12.0 Month
$ 1589/MT
- Density: 1.14 g/cc
- Water Absorption: 0.050 %
- Melt Flow: 10 g/10 min @Load 21.6 kg, Temperature 190 °C
- Hardness, Shore D: 56
- Tensile Strength at Break: 12.0 MPa
$ 1618/MT
- Density: 0.922 g/cc
- Water Absorption: 0.020 %
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: <= 3.40 MPa
- Tensile Strength at Break: >= 17.0 MPa
$ 1734/MT
- Density: 0.930 g/cc
- Density: 0.933 g/cc
- Melt Index of Compound: 0.70 g/10 min
- Tensile Strength, Yield: >= 18.6 MPa
- Tensile Strength, Yield: 20.7 MPa
$ 1808/MT
- Density: 0.962 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 62
- Tensile Strength, Yield: 26.0 MPa
$ 2110/MT
- Density: 0.930 g/cc
- Density: 1.05 g/cc
- Melt Flow: 0.70 g/10 min
- Tensile Strength, Yield: >= 18.6 MPa
- Tensile Strength, Yield: 20.7 MPa
$ 2496/MT
- Bulk Density: 0.500 - 0.600 g/cc
- Density: 0.922 g/cc
- Water Absorption: 0.020 %
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: <= 3.40 MPa
$ 1929/MT
- Density: 0.922 g/cc
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 400 %
- Film Elongation at Break, TD: 650 %
- Tensile Modulus: 0.180 GPa
$ 1787/MT
- Density: 0.923 g/cc
- Melt Flow: 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C
- Slip Level: 550 ppm
- Film Elongation at Break, MD: 250 %
- Film Elongation at Break, TD: 550 %
$ 1538/MT
- Density: 0.962 g/cc
- Linear Mold Shrinkage: 0.020 cm/cm
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 62
- Tensile Strength, Yield: 26.0 MPa
$ 2195/MT
- Density: 1.15 g/cc
- Melt Flow: 5.2 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1687/MT
- Density: 0.956 g/cc
- High Load Melt Index: 6.0 g/10 min @Load 21.6 kg, Temperature 190 °C
- Tensile Strength, Yield: 22.00 MPa
- Elongation at Break: >= 600 %
$ 1807/MT
- Density: 0.934 g/cc
- ESCR 10% Igepal®: >= 300 hour
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 17.9 MPa
- Flexural Modulus: 0.490 GPa
$ 1500/MT
- Density: 0.944 g/cc
- Density: 0.946 g/cc
- High Load Melt Index: 8.5 g/10 min @Load 21.6 kg, Temperature 190 °C
- Tensile Strength, Yield: 18.00 MPa
- Elongation at Break: >= 600 %
$ 1619/MT
- Density: 0.915 g/cc
- Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 190 °C
- Neck In: 6.30 cm
- Coating Weight: >= 5.00 g/m²
- Coating Speed (m/min): < 650
$ 1808/MT
- Density: 0.927 g/cc
- Thickness: 40.0 microns
- Melt Flow: 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 300 %
- Film Elongation at Break, TD: 600 %
$ 1503/MT
- Density: 0.957 g/cc
- Environmental Stress Crack Resistance: 40 hour
- Melt Flow: 0.20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 1.0 g/10 min @Load 5.00 kg, Temperature 190 °C
- Melt Flow: 23 g/10 min @Load 21.6 kg, Temperature 190 °C
$ 1843/MT
- Density: 0.920 g/cc
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Degree of Crosslinking: 12 %
- Hardness, Shore D: 52
- Tensile Strength, Yield: 17.2 MPa
$ 1923/MT
- Density: 0.923 g/cc
- Melt Flow: 4.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Neck In: 6.80 cm
- Coating Weight: >= 7.00 g/m²
- Coating Speed (m/min): < 700
$ 1454/MT
- Density: 0.962 g/cc
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 190 °C
- Coating Weight: 9.00 g/m²
- Melting Point: 131 °C
- Coating Speed (m/min): > 400 m/min
$ 1768/MT
- Density: 0.934 g/cc
- Melt Flow: 4.0 - 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 47
- Tensile Strength, Yield: 18.00 MPa
- Elongation at Break: >= 700 %
$ 1912/MT
- Density: 0.965 g/cc
- Environmental Stress Crack Resistance: 15 hour
- Melt Flow: 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 60 g/10 min @Load 21.6 kg, Temperature 190 °C
- Tensile Strength, Yield: 32.0 MPa
$ 2515/MT
- Density: 0.943 g/cc
- Melt Flow: 0.85 g/10 min
$ 1755/MT
- Density: 0.924 g/cc
- Water Absorption: 0.020 %
- Melt Flow: 2.4 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: <= 3.40 MPa
- Tensile Strength at Break: >= 17.0 MPa
$ 1527/MT
- Density: 1.40 g/cc
- Hardness, Shore D: 50
- Tensile Strength at Break: 12.8 MPa
- Tensile Strength at Break: 16.0 MPa
- Elongation at Break: 220 %
$ 2392/MT
- Density: 0.930 g/cc
- Melt Flow: 0.30 g/10 min @Load 5.00 kg, Temperature 190 °C
- Hardness, Shore D: 53
- Tensile Strength, Yield: 14.0 MPa
- Tensile Modulus: 0.400 GPa
$ 1832/MT
- Density: 1.40 g/cc
- Hardness, Shore D: 48
- Tensile Strength at Break: 9.00 MPa
- Elongation at Break: 280 %
- Volume Resistivity: 1.00e+6 ohm-cm
$ 1954/MT
- Density: 0.955 g/cc
- High Load Melt Index: 3.0 g/10 min @Load 21.6 kg, Temperature 190 °C
- Tensile Strength, Yield: 22.00 MPa
- Elongation at Break: >= 600 %
$ 1873/MT
- Density: 0.918 g/cc
- Density: 0.931 g/cc
- Environmental Stress Crack Resistance: >= 1000 hour @Temperature 50.0 °C
- Melt Flow: 0.20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 50
$ 2143/MT
- Density: 0.934 g/cc
- ESCR 10% Igepal®: >= 300 hour
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 17.9 MPa
- Flexural Modulus: 0.490 GPa
$ 1475/MT
- Density: 0.960 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 31 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 62
- Tensile Strength, Yield: 25.0 MPa
$ 1603/MT
- Density: 0.922 g/cc
- Melt Flow: 0.30 g/10 min @Load 5.00 kg, Temperature 190 °C
- Hardness, Shore D: 49
- Tensile Strength, Yield: 10.0 MPa
- Elongation at Break: 700 %
$ 2118/MT
- Density: 1.04 g/cc
- Tensile Strength, Yield: >= 17.69 MPa
- Tensile Strength, Yield: 19.7 MPa
- Elongation at Break: 472.5 %
- Elongation at Break: 525 %
$ 1848/MT
- Density: 0.922 g/cc
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 400 %
- Film Elongation at Break, TD: 600 %
- Tensile Modulus: 0.190 GPa
$ 1986/MT
- Density: 0.918 g/cc
- Environmental Stress Crack Resistance: >= 96 hour @Temperature 50.0 °C
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 50
- Tensile Strength at Break: 15.0 MPa
$ 1988/MT
- Density: 0.921 g/cc
- Density: 0.933 g/cc
- Environmental Stress Crack Resistance: >= 2500 hour @Temperature 50.0 °C
- Melt Flow: 0.35 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 50
$ 2046/MT
- Density: 0.929 g/cc
- Thickness: 40.0 microns
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 550 ppm
- Film Elongation at Break, MD: 250 %
$ 1472/MT
- Density: 0.932 g/cc
- Thickness: 40.0 microns
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 550 ppm
- Slip Level: 750 ppm
$ 1608/MT
- Density: 0.942 g/cc
- ESCR 10% Igepal®: >= 5000 hour
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 2.0 g/10 min @Load 5.00 kg, Temperature 190 °C
- Hardness, Shore D: 60
$ 1663/MT
- Water Absorption: 0.040 %
- Environmental Stress Crack Resistance: >= 2.0 hour @Temperature 50.0 °C
- Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 45
- Tensile Strength at Break: 3.125 MPa
$ 2177/MT
- Density: 0.934 g/cc
- ESCR 10% Igepal®: >= 4.0 hour
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 55
- Tensile Strength, Yield: 18.0 MPa
$ 2542/MT
- Density: 1.22 g/cc
- Tensile Strength at Break: >= 11.8 MPa
- Tensile Strength at Break: 13.1 MPa
- Elongation at Break: 275 %
- Oxygen Index: 27 %
$ 1448/MT
- Density: 0.948 g/cc
- Environmental Stress Crack Resistance: 300 hour
- Melt Flow: 7.0 g/10 min @Load 21.6 kg, Temperature 190 °C
- Hardness, Shore D: 62
- Tensile Strength, Yield: 24.0 MPa
$ 1624/MT
- Density: 0.934 g/cc
- Melt Flow: 1.3 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 47
- Tensile Strength, Yield: 18.0 MPa
- Elongation at Break: >= 700 %
$ 1673/MT
- Density: 0.941 g/cc
- Melt Flow: 7.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Neck In: 9.50 cm
- Coating Weight: >= 8.00 g/m²
- Coating Speed (m/min): < 500
$ 1524/MT
- Density: 1.13 g/cc
- Water Absorption: 0.080 %
- Tensile Strength at Break: 15.0 MPa
- Elongation at Break: 400 %
- Volume Resistivity: <= 100 ohm-cm @Temperature 23.0 °C
$ 1851/MT
- Density: 0.920 g/cc
- Melt Flow: 7.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Neck In: 6.80 cm
- Coating Weight: >= 7.50 g/m²
- Coating Speed (m/min): < 850
$ 1725/MT
- Density: 1.135 g/cc
- Water Absorption: 0.030 %
- Tensile Strength at Break: <= 4.40 MPa
- Tensile Strength at Break: 22.0 MPa
- Elongation at Break: 200 %
$ 1743/MT
- Density: 1.135 g/cc
- Water Absorption: 0.060 %
- Tensile Strength at Break: <= 2.20 MPa
- Tensile Strength at Break: 11.0 MPa
- Elongation at Break: 200 %
$ 1559/MT
- Density: 1.16 g/cc
- Melt Flow: 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 53
- Tensile Strength at Break: 2.25 MPa
- Tensile Strength at Break: 15.0 MPa
$ 1547/MT
- Density: 0.951 g/cc
- Environmental Stress Crack Resistance: >= 1000 hour @Temperature 80.0 °C
- Melt Flow: 0.30 g/10 min @Load 5.00 kg, Temperature 190 °C
- Tensile Strength, Yield: 24.99 MPa
- Elongation at Break: >= 600 %
$ 1457/MT
- Density: 0.958 g/cc
- Melt Flow: 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 131 °C
$ 1680/MT
- Density: 0.951 g/cc
- Melt Flow: 0.30 g/10 min @Load 5.00 kg, Temperature 190 °C
$ 2335/MT
- Density: 1.17 g/cc
- Water Absorption: 0.15 %
- Tensile Strength at Break: 15.0 MPa
- Elongation at Break: 300 %
- Volume Resistivity: 100 ohm-cm @Temperature 23.0 °C
$ 1458/MT
- Density: 0.923 g/cc
- Water Absorption: 0.020 %
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: <= 3.40 MPa
- Tensile Strength at Break: >= 17.0 MPa
$ 1589/MT
- Density: 0.964 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 63
- Tensile Strength, Yield: 27.0 MPa
$ 1989/MT
- Density: 0.944 g/cc
- High Load Melt Index: 10 g/10 min @Load 21.6 kg, Temperature 190 °C
- Elongation at Break: >= 600 %
$ 2222/MT
- Density: 0.947 g/cc
- Oxidative Induction Time (OIT): 30 min
- Melt Index of Compound: 3.3 g/10 min
- Dielectric Constant: 2.05 @Frequency 1.80e+10 Hz
- Dielectric Constant: 2.24 @Frequency 3.00e+9 Hz
$ 2256/MT
- Density: 0.948 g/cc
- ESCR 10% Igepal®: >= 2000 hour
- Melt Flow: 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 55
- Tensile Strength, Yield: >= 24.8 MPa
$ 1846/MT
- Density: 0.942 g/cc
- Melt Flow: 1.0 g/10 min @Load 5.00 kg, Temperature 190 °C
- Tensile Strength at Break: 18.0 MPa
- Tensile Strength, Yield: 27.00 MPa
- Elongation at Break: 195 %
$ 1500/MT
- Density: 0.942 g/cc
- Density: 0.952 g/cc
- ESCR 10% Igepal®: >= 5000 hour
- Carbon Black Loading: >= 2.0 %
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 2254/MT
- Density: 1.17 g/cc
- Tensile Strength at Break: 13.0 MPa
- Elongation at Break: >= 75 %
- Elongation at Break: 300 %
- Brittleness Temperature: <= -35.0 °C
$ 1537/MT
- Density: 0.923 g/cc
- Environmental Stress Crack Resistance: >= 96 hour @Temperature 50.0 °C
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 52
- Tensile Strength at Break: <= 11.25 MPa
$ 1572/MT
- Density: 0.923 g/cc
- Elongation at Break: >= 300 %
- Elongation at Break: >= 360 %
- Elongation at Break: 400 %
- Melting Point: 135 °C
$ 1483/MT
- Density: 0.922 g/cc
- Melt Flow: 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 350 %
- Film Elongation at Break, TD: 600 %
- Tensile Modulus: 0.200 GPa
$ 2565/MT
- Density: 0.936 g/cc
- ESCR 10% Igepal®: >= 2000 hour
- Melt Flow: 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 54
- Tensile Strength, Yield: >= 24.8 MPa
$ 1462/MT
- Density: 1.10 g/cc
- ESCR 10% Igepal®: >= 2000 hour
- Melt Flow: 0.40 g/10 min @Load 2.16 kg
- Melt Flow: 2.0 g/10 min @Load 5.00 kg
- Hardness, Shore D: 59
$ 1490/MT
- Density: 0.935 g/cc
- Melt Flow: 0.70 g/10 min @Load 5.00 kg, Temperature 190 °C
- Melt Flow: 15 g/10 min @Load 21.6 kg, Temperature 190 °C
- Film Elongation at Break, MD: 400 %
- Film Elongation at Break, TD: 650 %
$ 1499/MT
- Density: 1.16 g/cc
- Tensile Strength at Break: >= 11.1 MPa
- Tensile Strength at Break: 13.1 MPa
- Elongation at Break: 400 %
- Oxygen Index: 23 %
$ 1935/MT
- Density: 0.960 g/cc
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Coating Weight: 6.00 g/m²
- Melting Point: >= 130 °C
- Vicat Softening Point: 124 °C
- Maximum Coating Weight m/min: 450 min
$ 1531/MT
- Density: 0.946 g/cc
- Melt Flow: 0.20 g/10 min @Load 5.00 kg, Temperature 190 °C
- High Load Melt Index: 6.0 g/10 min @Load 21.6 kg, Temperature 190 °C
- Film Elongation at Break, MD: 300 %
- Film Elongation at Break, TD: 450 %
$ 1454/MT
- Density: 0.945 g/cc
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 1.2 g/10 min @Load 5.00 kg, Temperature 190 °C
- Melt Flow: 25 g/10 min @Load 21.6 kg, Temperature 190 °C
- Film Elongation at Break, MD: 100 %
$ 1511/MT
- Density: 0.925 g/cc
- Thickness: 70.0 microns
- Melt Flow: 0.40 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 2.0 g/10 min @Load 5.00 kg, Temperature 190 °C
- Film Elongation at Break, MD: 650 %
$ 1512/MT
- Density: 0.956 g/cc
- Oxidative Induction Time (OIT): >= 15 min @Temperature 210 °C
- Melt Flow: 0.30 g/10 min @Load 5.00 kg, Temperature 190 °C
- Hardness, Shore D: 60
- Charpy Impact, Notched: 1.40 J/cm² @Temperature 0.000 °C
$ 2037/MT
- Density: 0.956 g/cc
- Environmental Stress Crack Resistance: >= 2000 hour @Temperature 80.0 °C
- Carbon Black Loading: >= 2.0 %
- Melt Flow: 0.30 g/10 min @Load 5.00 kg, Temperature 190 °C
- Tensile Strength, Yield: 22.0 MPa
$ 1468/MT
- Density: 0.948 g/cc
- Melt Flow: 0.30 g/10 min @Load 5.00 kg, Temperature 190 °C
$ 1900/MT
- Density: 0.950 g/cc
- Melt Flow: 0.30 g/10 min @Load 5.00 kg, Temperature 190 °C
$ 1721/MT
- Density: 0.953 g/cc
- Melt Flow: 0.30 g/10 min @Load 5.00 kg, Temperature 190 °C
$ 1732/MT
- Density: 0.953 g/cc
- Melt Flow: 0.30 g/10 min @Load 5.00 kg, Temperature 190 °C
$ 1743/MT
- Density: 0.920 g/cc
- Environmental Stress Crack Resistance: >= 5.0 hour @Temperature 50.0 °C
- Melt Flow: 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 50
- Hardness, Shore D: 52
$ 1624/MT
- Density: 0.954 g/cc
- ESCR 10% Igepal®: >= 40 hour
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 61
- Tensile Strength, Yield: 22.0 MPa
$ 1483/MT
- Density: 0.940 g/cc
- Density: 0.951 g/cc
- ESCR 10% Igepal®: >= 5000 hour
- Carbon Black Loading: >= 2.0 %
- Melt Flow: 0.20 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1612/MT
- Density: 0.944 g/cc
- Environmental Stress Crack Resistance: >= 2000 hour @Temperature 80.0 °C
- Melt Flow: 0.80 g/10 min @Load 5.00 kg, Temperature 190 °C
- Tensile Strength, Yield: 19.00 MPa
- Elongation at Break: >= 600 %
$ 1538/MT
- Density: 0.949 g/cc
- Melt Flow: 0.80 g/10 min @Load 5.00 kg, Temperature 190 °C
$ 1697/MT
- Density: 0.958 g/cc
- ESCR 10% Igepal®: >= 100 hour
- Melt Flow: 0.40 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 1.8 g/10 min @Load 5.00 kg, Temperature 190 °C
- High Load Melt Index: 28 g/10 min @Load 21.6 kg, Temperature 190 °C
$ 1989/MT
- Density: 0.951 g/cc
- Environmental Stress Crack Resistance: >= 1000 hour @Temperature 80.0 °C
- Melt Flow: 0.30 g/10 min @Load 5.00 kg, Temperature 190 °C
- Tensile Strength, Yield: 24.99 MPa
- Elongation at Break: >= 600 %
$ 1551/MT
- Density: 0.954 g/cc
- ESCR 10% Igepal®: >= 40 hour
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 61
- Tensile Strength, Yield: 22.0 MPa
$ 1960/MT
- Density: 0.937 g/cc
- Melt Flow: 0.40 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 2.1 g/10 min @Load 5.00 kg, Temperature 190 °C
- Film Elongation at Break, MD: 530 %
- Film Elongation at Break, TD: 830 %
$ 1479/MT
- Density: 0.946 g/cc
- Density: 0.958 g/cc
- ESCR 10% Igepal®: >= 2000 hour @Temperature 50.0 °C
- Absorption Coefficient: >= 400
- Carbon Black Loading: 2.5 %
$ 1558/MT
- Density: 0.942 g/cc
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 61
- Tensile Strength, Yield: 13.8 MPa
- Elongation at Break: 700 %
$ 1873/MT
- Density: 0.934 g/cc
- ESCR 10% Igepal®: >= 300 hour
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 17.9 MPa
- Flexural Modulus: 0.490 GPa
$ 1758/MT
- Density: 0.934 g/cc
- ESCR 10% Igepal®: >= 200 hour
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 19.3 MPa
- Flexural Modulus: 0.558 GPa
$ 1516/MT
- Density: 0.923 g/cc
- Density: 0.941 g/cc
- Density: 2.00 g/cc
- Melt Flow: 0.90 g/10 min
- Tensile Strength, Yield: >= 14.58 MPa
$ 1523/MT
- Density: 1.40 g/cc
- Hardness, Shore D: 50
- Tensile Strength at Break: 12.8 MPa
- Tensile Strength at Break: 16.0 MPa
- Elongation at Break: 220 %
$ 1492/MT
- Density: 0.940 g/cc
- ESCR 10% Igepal®: >= 250 hour
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 22.1 MPa
- Flexural Modulus: 0.641 GPa
$ 1520/MT
- Tensile Strength at Break: 11.0 MPa
- Elongation at Break: <= 75 %
- Elongation at Break: 250 %
- Volume Resistivity: 100 ohm-cm @Temperature 23.0 °C
- Volume Resistivity: 100 ohm-cm @Temperature 90.0 °C
- Shelf Life: 12.0 Month
$ 2132/MT
- Density: 0.923 g/cc
- Density: 1.05 g/cc
- Density: 2.00 g/cc
- Melt Flow: 0.90 g/10 min
- Tensile Strength, Yield: >= 14.58 MPa
$ 1596/MT
- Density: 0.480 g/cc
- Density: 0.945 g/cc
- Oxidative Induction Time (OIT): 50 min
- Tensile Strength, Yield: 13.1 MPa
- Tensile Strength, Yield: 22.8 MPa
$ 2223/MT
- Density: 0.945 g/cc
- Oxidative Induction Time (OIT): >= 200 min
- Tensile Strength, Yield: 13.1 MPa
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Break: 500 %
$ 1506/MT
- Density: 0.934 g/cc
- Density: 0.937 g/cc
- Thermal Stress Crack Resistance: 1.50 hour @Temperature 105 °C
- Oxidative Induction Time (OIT): 50 min @Temperature 200 °C
- Tensile Strength at Break: 11.0 MPa
$ 1731/MT
- Density: 0.955 g/cc
- Environmental Stress Crack Resistance: 180 hour
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 1.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 23.0 MPa
$ 1987/MT
- Density: 1.40 g/cc
- Hardness, Shore D: 50
- Tensile Strength at Break: 13.8 MPa
- Tensile Strength at Break: 17.25 MPa
- Elongation at Break: 200 %
$ 2206/MT
- Density: 0.947 g/cc
- Melt Flow: 0.20 g/10 min @Load 5.00 kg, Temperature 190 °C
- Melt Flow: 6.0 g/10 min @Load 21.6 kg, Temperature 190 °C
- Film Elongation at Break, MD: 250 %
- Film Elongation at Break, TD: 300 %
$ 1842/MT
- Density: 1.135 g/cc
- Water Absorption: 0.030 %
- Tensile Strength at Break: <= 4.40 MPa
- Tensile Strength at Break: >= 22.0 MPa
- Elongation at Break: 200 %
$ 2295/MT
- Density: 1.135 g/cc
- Water Absorption: 0.030 %
- Tensile Strength at Break: <= 4.40 MPa
- Tensile Strength at Break: >= 22.0 MPa
- Elongation at Break: 200 %
$ 2378/MT
- Density: 0.923 g/cc
- Density: 1.05 g/cc
- Melt Flow: 0.90 g/10 min
- Tensile Strength, Yield: >= 13.28 MPa
- Tensile Strength, Yield: 14.8 MPa
$ 1552/MT
- Density: 0.923 g/cc
- Density: 0.941 g/cc
- Density: 2.00 g/cc
- Melt Flow: 0.90 g/10 min
- Tensile Strength, Yield: >= 14.58 MPa
$ 1860/MT
- Density: 0.923 g/cc
- Density: 0.941 g/cc
- Melt Flow: 0.90 g/10 min
- Tensile Strength, Yield: >= 13.28 MPa
- Tensile Strength, Yield: 14.8 MPa
$ 2195/MT
- Density: 0.928 g/cc
- Density: 0.933 g/cc
- Melt Flow: 4.5 g/10 min
- Tensile Strength, Yield: >= 9.93 MPa
- Tensile Strength, Yield: 11.0 MPa
$ 1501/MT
- Specific Gravity: 0.935 g/cc
- Hardness, Shore D: 51
- Tensile Strength, Yield: >= 13.8 MPa
- Tensile Strength, Yield: 16.2 MPa
- Elongation at Break: 255 %
$ 1480/MT
- Density: 1.08 g/cc
- Water Absorption: 0.020 %
- Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 50
- Tensile Strength at Break: <= 2.60 MPa
$ 2164/MT
- Density: 0.940 g/cc
- ESCR 10% Igepal®: >= 120 hour
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 21.0 MPa
- Flexural Modulus: 0.621 GPa
$ 1506/MT
- Density: 0.922 g/cc
- Water Absorption: 0.020 %
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: <= 3.40 MPa
- Tensile Strength at Break: >= 17.0 MPa
$ 1540/MT
- Density: 1.16 g/cc
- Tensile Strength at Break: >= 14.4 MPa
- Tensile Strength at Break: 16.0 MPa
- Elongation at Break: 200 %
- Elongation at Break: 250 %
$ 1601/MT
- Density: 0.955 g/cc
- Environmental Stress Crack Resistance: 180 hour
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 1.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 23.0 MPa
$ 2430/MT
- Density: 0.922 g/cc
- Water Absorption: 0.020 %
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: <= 3.40 MPa
- Tensile Strength at Break: >= 17.0 MPa
$ 1900/MT
- Density: 0.922 g/cc
- Melt Flow: 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 850 ppm
- Slip Level: 450 ppm
- Film Elongation at Break, MD: 300 %
$ 1963/MT
- Density: 0.958 g/cc
- Environmental Stress Crack Resistance: 100 hour
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 1.3 g/10 min @Load 5.00 kg, Temperature 190 °C
- Melt Flow: 28 g/10 min @Load 21.6 kg, Temperature 190 °C
$ 2514/MT
- Density: 0.940 g/cc
- ESCR 10% Igepal®: >= 90 hour
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 22.1 MPa
- Flexural Modulus: 0.655 GPa
$ 2274/MT
- Density: 0.920 g/cc
- Melt Flow: 0.25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 400 %
- Film Elongation at Break, TD: 600 %
- Tensile Modulus: 0.160 GPa
$ 1969/MT
- Density: 0.923 g/cc
- Environmental Stress Crack Resistance: >= 96 hour @Temperature 50.0 °C
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 52
- Tensile Strength at Break: <= 10.5 MPa
$ 2060/MT
- Density: 0.935 g/cc
- Melt Flow: 1.0 g/10 min @Load 5.00 kg, Temperature 190 °C
- Tensile Strength at Break: 15.0 MPa
- Tensile Strength, Yield: 20.00 MPa
- Elongation at Break: 180 %
$ 1992/MT
- Density: 1.27 g/cc
- Water Absorption: 0.063 % @Temperature 70.0 °C, Time 1.21e+6 sec
- Environmental Stress Crack Resistance: >= 1.0 hour @Temperature 50.0 °C
- Melt Flow: 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 48
$ 1759/MT
- Density: 0.930 g/cc
- Density: 1.38 g/cc
- Melt Index of Compound: 0.70 g/10 min
- Tensile Strength, Yield: >= 18.6 MPa
- Tensile Strength, Yield: 20.7 MPa
$ 1805/MT
- Density: 1.135 g/cc
- Tensile Strength at Break: >= 9.30 MPa
- Tensile Strength at Break: 18.6 MPa
- Elongation at Break: 200 %
- Volume Resistivity: <= 100 ohm-cm @Temperature 90.0 °C
- Shelf Life: 18.0 Month
$ 1491/MT
- Density: 1.40 g/cc
- Tensile Strength at Break: 13.8 MPa
- Elongation at Break: 180 %
- Brittleness Temperature: <= -40.0 °C
- Volume Resistivity: 1.00e+6 ohm-cm
$ 2458/MT
- Density: 1.15 g/cc
- Water Absorption: 0.0087 % @Time 1.21e+6 sec
- Melt Flow: 0.90 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 40
- Tensile Strength at Break: <= 2.60 MPa
$ 2301/MT
- Density: 0.923 g/cc
- Melt Flow: 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 800 ppm
- Slip Level: 550 ppm
- Film Elongation at Break, MD: 250 %
$ 1637/MT
- Density: 0.940 g/cc
- ESCR 10% Igepal®: >= 250 hour
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 22.1 MPa
- Flexural Modulus: 0.641 GPa
$ 1491/MT
- Density: 0.924 g/cc
- Density: 0.934 g/cc
- Environmental Stress Crack Resistance: >= 1000 hour @Temperature 50.0 °C
- Melt Flow: 0.35 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 45
$ 1550/MT
- Density: 0.923 g/cc
- Density: 0.933 g/cc
- Melt Index of Compound: 0.90 g/10 min
- Tensile Strength, Yield: >= 13.28 MPa
- Tensile Strength, Yield: 14.8 MPa
$ 1650/MT
- Density: 0.924 g/cc
- Water Absorption: 0.020 %
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: <= 3.40 MPa
- Tensile Strength at Break: >= 17.0 MPa
$ 2248/MT
- Density: 0.929 g/cc
- Thickness: 40.0 microns
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 550 ppm
- Slip Level: 500 ppm
$ 1446/MT
- Density: 0.940 g/cc
- ESCR 10% Igepal®: >= 200 hour
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 22.1 MPa
- Flexural Modulus: 0.655 GPa
$ 1499/MT
- Density: 1.135 g/cc
- Water Absorption: 0.060 %
- Tensile Strength at Break: <= 2.20 MPa
- Tensile Strength at Break: 11.0 MPa
- Elongation at Break: 200 %
$ 2200/MT
- Density: 0.920 g/cc
- Melt Flow: 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 52
- Tensile Strength at Break: 13.0 MPa
- Elongation at Break: 600 %
$ 2019/MT
- Density: 0.920 g/cc
- ESCR 100% Igepal®: >= 1000 hour
- ESCR 10% Igepal®: >= 1000 hour
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Degree of Crosslinking: 12 %
$ 1930/MT
- Density: 0.922 g/cc
- Melt Flow: 0.90 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 625 ppm
- Slip Level: 480 ppm
- Tensile Strength, Yield: 12.0 MPa
$ 1568/MT
- Density: 0.934 g/cc
- ESCR 10% Igepal®: >= 200 hour
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 19.3 MPa
- Flexural Modulus: 0.558 GPa
$ 1871/MT
- Density: 0.935 g/cc
- Environmental Stress Crack Resistance: >= 96 hour @Temperature 50.0 °C
- Carbon Black Loading: 2.5 %
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: <= 10.5 MPa
$ 1491/MT
- Density: 0.962 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 62
- Tensile Strength, Yield: 26.0 MPa
$ 2384/MT
- Density: 0.923 g/cc
- Melt Flow: 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Elongation at Break: 400 %
- Volume Resistivity: 1.00e+6 ohm-cm
- Dielectric Constant: 2.3 @Frequency 50000 Hz
$ 1687/MT
- Density: 1.225 g/cc
- Water Absorption: 0.065 % @Time 1.21e+6 sec
- Melt Flow: 0.25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 53
- Tensile Strength at Break: >= 2.10 MPa
$ 1590/MT
- Density: 1.17 g/cc
- Volume Resistivity: 50 ohm-cm @Temperature 23.0 °C
- Volume Resistivity: 90 ohm-cm @Temperature 90.0 °C
- Shelf Life: 12.0 Month
$ 1896/MT
- Density: 0.922 g/cc
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 400 %
- Film Elongation at Break, TD: 650 %
- Tensile Modulus: 0.180 GPa
$ 1935/MT
- Density: 0.940 g/cc
- ESCR 10% Igepal®: >= 120 hour
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 21.0 MPa
- Flexural Modulus: 0.621 GPa
$ 2101/MT
- Density: 0.954 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 61
- Tensile Strength, Yield: 24.0 MPa
$ 2292/MT
- Density: 0.922 g/cc
- Melt Flow: 0.90 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 1250 ppm
- Tensile Strength, Yield: 12.0 MPa
- Film Elongation at Break, MD: 800 %
Delivery Polyethylene (PE) Borealis
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
lng tankers for sale in europe. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.