$ 1633/MT
- Density: 0.900 g/cc
- Linear Mold Shrinkage: 0.013 cm/cm
- Linear Mold Shrinkage: 0.014 cm/cm
- Melt Flow: 2.2 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ball Indentation Hardness: 65.0 MPa
$ 1565/MT
- Density: 0.900 - 0.910 g/cc
- Melt Flow: 1.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Film Elongation at Break, MD: 550 - 600 %
- Tensile Modulus: 0.730 GPa
- Flexural Modulus: 0.650 GPa
$ 2187/MT
- Density: 0.905 g/cc
- Linear Mold Shrinkage: 0.0015 cm/cm
- Linear Mold Shrinkage: 0.014 cm/cm
- Melt Flow: 11 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 55
$ 1495/MT
- Density: 0.940 g/cc
- Linear Mold Shrinkage: 0.0085 - 0.0095 cm/cm
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ball Indentation Hardness: 35.0 MPa
- Tensile Strength, Yield: 16.50 MPa
$ 1829/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 30 g/10 min @Load 5.00 kg, Temperature 230 °C
- Ball Indentation Hardness: 57.0 MPa
$ 1477/MT
- Density: 1.17 g/cc
- Linear Mold Shrinkage: 0.0010 cm/cm
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 10.0 MPa
- Elongation at Break: 450 %
$ 2501/MT
- Density: 1.01 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 30 g/10 min @Load 5.00 kg, Temperature 230 °C
- Ball Indentation Hardness: 50.0 MPa
$ 1499/MT
- Density: 1.01 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 30 g/10 min @Load 5.00 kg, Temperature 230 °C
- Ball Indentation Hardness: 50.0 MPa
$ 1861/MT
- Density: 1.01 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 30 g/10 min @Load 5.00 kg, Temperature 230 °C
- Ball Indentation Hardness: 50.0 MPa
$ 2190/MT
- Density: 1.01 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 30 g/10 min @Load 5.00 kg, Temperature 230 °C
- Ball Indentation Hardness: 50.0 MPa
$ 1837/MT
- Density: 1.01 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 30 g/10 min @Load 5.00 kg, Temperature 230 °C
- Ball Indentation Hardness: 50.0 MPa
$ 2319/MT
- Density: 1.01 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 30 g/10 min @Load 5.00 kg, Temperature 230 °C
- Ball Indentation Hardness: 50.0 MPa
$ 2036/MT
- Density: 1.01 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 30 g/10 min @Load 5.00 kg, Temperature 230 °C
- Ball Indentation Hardness: 50.0 MPa
$ 1453/MT
- Density: 0.902 g/cc
- Melt Flow: 1.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 24.0 MPa
- Tensile Modulus: 0.900 GPa
- Charpy Impact, Notched: 2.00 J/cm² @Temperature 23.0 °C
$ 1510/MT
- Density: 1.13 g/cc
- Linear Mold Shrinkage: 0.0090 cm/cm
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 11.2 g/10 min @Load 5.00 kg, Temperature 230 °C
- Ball Indentation Hardness: 71.0 MPa
$ 2486/MT
- Melt Flow: 3.7 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ash: 0.0010 - 0.0020 %
- Melting Point: 161 - 165 °C
- Dielectric Constant: 2.25
- Calcium, ppm: 5
$ 1899/MT
- Filler Content: 20 %
- Tensile Strength at Break: 100 MPa
- Elongation at Break: 2.5 %
- Tensile Modulus: 5.30 GPa
- Flexural Strength: 130 MPa
$ 1938/MT
- Density: 0.905 g/cc
- Linear Mold Shrinkage: 0.015 - 0.020 cm/cm
- Melt Flow: 2.8 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 39.50 MPa
- Elongation at Yield: 7.0 %
$ 1650/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage: 0.0020 cm/cm
- Linear Mold Shrinkage: 0.011 cm/cm
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ball Indentation Hardness: 112 MPa
$ 2429/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0010 cm/cm
- Linear Mold Shrinkage: 0.0065 cm/cm
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ball Indentation Hardness: 30.0 MPa
$ 1973/MT
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 89
- Tensile Strength, Yield: 27.0 MPa
- Elongation at Yield: 4.5 %
$ 2114/MT
- Density: 0.908 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 98
- Tensile Strength, Yield: 33.5 MPa
$ 1501/MT
- Density: 0.905 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 75
- Tensile Strength, Yield: 27.0 MPa
$ 1959/MT
- Filler Content: 40 %
- Tensile Strength at Break: 145 MPa
- Elongation at Break: 2.1 %
- Tensile Modulus: 10.0 GPa
- Flexural Strength: 195 MPa
$ 1730/MT
- Density: 0.950 g/cc
- Linear Mold Shrinkage: 0.0015 cm/cm
- Linear Mold Shrinkage: 0.0080 cm/cm
- Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ball Indentation Hardness: 23.0 MPa
$ 1699/MT
- Density: 0.900 - 0.910 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Film Elongation at Break, MD: 500 - 700 %
- Film Elongation at Break, TD: 500 - 700 %
- Tensile Modulus: 0.650 - 0.750 GPa
$ 1577/MT
- Density: 0.905 g/cc
- Melt Flow: 0.75 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 35.0 MPa
- Elongation at Yield: 10 %
- Tensile Modulus: 1.49 GPa
$ 1555/MT
- Density: 0.905 g/cc
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 90
- Tensile Strength, Yield: 28.0 MPa
- Elongation at Yield: 12 %
$ 2067/MT
- Density: 0.970 g/cc
- Linear Mold Shrinkage: 0.0015 cm/cm
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ball Indentation Hardness: 33.0 MPa
$ 1459/MT
- Density: 0.905 g/cc
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 0.50 g/10 min @Load 5.00 kg, Temperature 190 °C
- Tensile Strength, Yield: 30.000 MPa
- Elongation at Yield: 10 %
$ 2233/MT
- Density: 0.900 - 0.910 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Slip Level: 2000 ppm
- Film Elongation at Break, MD: 500 - 700 %
- Film Elongation at Break, TD: 500 - 700 %
$ 2041/MT
- Density: 0.905 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 82
- Tensile Strength, Yield: 25.0 MPa
$ 1593/MT
- Density: 0.900 - 0.910 g/cc
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Film Elongation at Break, MD: 600 - 800 %
- Film Elongation at Break, TD: 600 - 800 %
- Tensile Modulus: 0.450 - 0.550 GPa
$ 2191/MT
- Density: 0.900 g/cc
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 30.00 MPa
- Elongation at Yield: 10 %
- Tensile Modulus: 1.50 GPa
$ 1799/MT
- Density: 1.15 g/cc
- Linear Mold Shrinkage, Flow: <= 0.0020 cm/cm @Thickness 2.00 mm
- Linear Mold Shrinkage, Transverse: >= 0.010 cm/cm
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Spiral Flow: 95.0 cm @Thickness 2.00 mm, Temperature 250 °C
$ 1655/MT
- Density: 0.900 - 0.910 g/cc
- Thickness: 50.0 microns
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Film Elongation at Break, MD: 650 %
- Film Elongation at Break, TD: 850 %
$ 2355/MT
- Density: 0.910 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 45 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 85
- Tensile Strength, Yield: 26.0 MPa
$ 1653/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0060 cm/cm
- Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 15.00 MPa
- Elongation at Yield: 6.0 %
$ 2112/MT
- Density: 1.07 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 14 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 56 g/10 min @Load 5.00 kg, Temperature 230 °C
- Tensile Strength, Yield: 23.0 MPa
$ 2388/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.011 cm/cm
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 27.5 g/10 min @Load 5.00 kg, Temperature 230 °C
- Ball Indentation Hardness: 80.6 MPa
$ 1989/MT
- Melt Flow: 450 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melting Point: 161 - 165 °C
$ 1497/MT
- Density: 0.905 g/cc
- Melt Flow: 0.25 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 25.0 MPa
- Elongation at Yield: 13.5 %
- Tensile Modulus: 0.900 GPa
$ 1462/MT
- Density: 0.905 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 19 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 93
- Tensile Strength, Yield: 29.5 MPa
$ 1898/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.011 cm/cm
- Melt Flow: 23 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 88 g/10 min @Load 5.00 kg, Temperature 230 °C
- Ball Indentation Hardness: 78.0 MPa
$ 1965/MT
- Density: 0.900 - 0.910 g/cc
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Film Elongation at Break, MD: 400 - 500 %
- Tensile Modulus: 0.650 - 0.850 GPa
- Flexural Modulus: 0.700 GPa
$ 1517/MT
- Melt Flow: 1200 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melting Point: 156 - 160 °C
$ 1527/MT
- Melt Flow: 6.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Flexural Modulus: 0.750 GPa
- Heat Seal Strength Initiation Temperature: 108 °C
- Melting Point: 130 - 134 °C
- Vicat Softening Point: 117 °C
- Haze: 1.8 %
$ 1754/MT
- Bulk Density: 0.500 - 0.600 g/cc
- Density: 0.905 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 21 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 102
$ 1961/MT
- Density: 0.920 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 112
- Tensile Strength, Yield: 40.00 MPa
$ 1445/MT
- Bulk Density: 0.500 - 0.600 g/cc
- Density: 0.902 g/cc
- Melt Flow: 1.9 g/10 min @Load 1.90 kg, Temperature 230 °C
- Tensile Strength, Yield: 26.0 MPa
- Elongation at Yield: 12 %
$ 1578/MT
- Density: 1.24 g/cc
- Linear Mold Shrinkage: 0.0040 cm/cm
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Elongation at Break: 2.0 %
- Tensile Modulus: 9.00 GPa
$ 1737/MT
- Density: 0.905 g/cc
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 25.00 MPa
- Elongation at Yield: 10 %
- Modulus of Elasticity: 0.900 GPa
$ 1469/MT
- Melt Flow: 3.2 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 4.4 g/10 min @Load 5.00 kg, Temperature 190 °C
- Melt Flow: 14 g/10 min @Load 5.00 kg, Temperature 230 °C
- Ash: 0.0010 - 0.0020 %
- Melting Point: 161 - 165 °C
$ 1696/MT
- Density: 0.920 g/cc
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ball Indentation Hardness: 90.0 MPa
- Tensile Strength, Yield: 41.0 MPa
- Tensile Modulus: 2.10 GPa
$ 2425/MT
- Melt Flow: 22 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 14.0 MPa
- Elongation at Yield: 15 %
- Tensile Modulus: 0.450 GPa
- Flexural Modulus: 0.400 GPa
$ 1446/MT
- Density: 1.03 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 11 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 40 g/10 min @Load 5.00 kg, Temperature 230 °C
- Ball Indentation Hardness: 50.0 MPa
$ 1606/MT
- Density: 0.920 g/cc
- Melt Flow: 22 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 96 g/10 min @Load 5.00 kg, Temperature 230 °C
- Ball Indentation Hardness: 85.0 MPa
- Tensile Strength, Yield: 35.0 MPa
$ 1562/MT
- Density: 0.905 g/cc
- Melt Flow: 30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 90
- Tensile Strength, Yield: 27.50 MPa
- Elongation at Yield: 12 %
$ 2134/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.011 cm/cm
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 49 g/10 min @Load 5.00 kg, Temperature 230 °C
- Ball Indentation Hardness: 62.0 MPa
$ 2031/MT
- Density: 0.905 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 45 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 80
- Tensile Strength, Yield: 27.0 MPa
$ 1763/MT
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Flexural Modulus: 0.700 GPa
- Heat Seal Strength Initiation Temperature: 103 °C
- Melting Point: 128 - 132 °C
- Vicat Softening Point: 114 °C
$ 2162/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage: 0.0020 cm/cm
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ball Indentation Hardness: 124 MPa
$ 1453/MT
- Density: 1.07 g/cc
- Linear Mold Shrinkage: 0.0090 cm/cm
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 22.99 MPa
- Elongation at Yield: 5.1 %
$ 1517/MT
- Density: 0.990 g/cc
- Linear Mold Shrinkage: 0.0090 cm/cm
- Melt Flow: 16 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ball Indentation Hardness: 31.0 MPa
- Tensile Strength, Yield: 16.0 MPa
$ 1498/MT
- Density: 0.905 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 70
- Tensile Strength, Yield: 20.99 MPa
$ 1768/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0060 cm/cm
- Melt Flow: 14 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ball Indentation Hardness: 32.0 MPa
- Tensile Strength at Break: 12.0 MPa
$ 1799/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0060 cm/cm
- Melt Flow: 14 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ball Indentation Hardness: 32.0 MPa
- Tensile Strength at Break: 12.0 MPa
$ 2071/MT
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Flexural Modulus: 0.700 GPa
- Heat Seal Strength Initiation Temperature: 103 °C
- Melting Point: 128 - 132 °C
- Vicat Softening Point: 114 °C
- Haze: 1.0 %
$ 1785/MT
- Melt Flow: 3.2 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 4.5 g/10 min @Load 5.00 kg, Temperature 190 °C
- Melt Flow: 15 g/10 min @Load 5.00 kg, Temperature 230 °C
- Film Elongation at Break, MD: 150 - 200 %
- Film Elongation at Break, TD: 50 - 90 %
$ 1590/MT
- Melt Flow: 3.2 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 4.4 g/10 min @Load 5.00 kg, Temperature 190 °C
- Melt Flow: 14 g/10 min @Load 5.00 kg, Temperature 230 °C
- Ash: 0.0010 - 0.0020 %
- Melting Point: 161 - 165 °C
$ 2053/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage: 0.0020 cm/cm
- Linear Mold Shrinkage: 0.011 cm/cm
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ball Indentation Hardness: 112 MPa
$ 1481/MT
- Density: 0.980 g/cc
- Linear Mold Shrinkage: 0.0015 cm/cm
- Linear Mold Shrinkage: 0.0080 cm/cm
- Melt Flow: 40 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ball Indentation Hardness: 28.0 MPa
$ 1462/MT
- Density: 0.902 g/cc
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 86
- Tensile Strength, Yield: 25.0 MPa
- Elongation at Yield: 6.0 %
$ 1658/MT
- Melt Flow: 2.4 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 40.00 MPa
- Elongation at Yield: 6.0 %
- Tensile Modulus: 1.95 GPa
- Flexural Modulus: 1.85 GPa
$ 1544/MT
- Density: 0.910 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 101
- Tensile Strength, Yield: 35.0 MPa
$ 1645/MT
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Flexural Modulus: 0.700 GPa
- Heat Seal Strength Initiation Temperature: 103 °C
- Melting Point: 128 - 132 °C
- Vicat Softening Point: 114 °C
- Haze: 1.0 %
$ 2484/MT
- Density: 0.900 - 0.910 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Antiblock Level: 1800 ppm
- Slip Level: 2100 ppm
- Film Elongation at Break, MD: 550 - 750 %
$ 1658/MT
- Density: 0.905 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 125 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ball Indentation Hardness: 78.0 MPa
- Tensile Strength, Yield: 35.0 MPa
$ 1444/MT
- Density: 0.910 g/cc
- Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 230 °C
- Neck In: 5.80 cm
- Coating Weight: >= 10.0 g/m²
- Vicat Softening Point: 132 °C @Load 1.02 kg
$ 1657/MT
- Density: 0.900 - 0.910 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Film Elongation at Break, MD: 550 - 750 %
- Tensile Modulus: 0.350 - 0.450 GPa
- Flexural Modulus: 0.650 GPa
$ 2088/MT
- Density: 0.900 g/cc
- Melt Flow: 0.90 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 62
- Tensile Strength, Yield: 25.0 MPa
- Elongation at Break: >= 100 %
$ 1820/MT
- Density: 0.900 g/cc
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 29.0 MPa
- Elongation at Yield: 10 %
- Flexural Modulus: 1.50 GPa
$ 1762/MT
- Density: 0.980 g/cc
- Linear Mold Shrinkage: 0.00090 cm/cm
- Linear Mold Shrinkage: 0.0090 cm/cm
- Melt Flow: 11 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 23.0 MPa
$ 1522/MT
- Density: 0.905 g/cc
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Modulus: 0.500 GPa
- Flexural Modulus: 0.900 GPa
- Dart Drop, Total Energy: 20.0 J @Thickness 0.0500 mm
$ 1688/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage: 0.0020 cm/cm
- Linear Mold Shrinkage: 0.0090 cm/cm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ball Indentation Hardness: 121 MPa
$ 2065/MT
- Density: 0.905 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 67
- Tensile Strength, Yield: 23.0 MPa
$ 1534/MT
- Density: 0.905 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 18 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 89
- Tensile Strength, Yield: 26.0 MPa
$ 1699/MT
- Density: 0.905 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 70 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 88
- Tensile Strength, Yield: 30.0 MPa
$ 1863/MT
- Density: 0.900 - 0.910 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Film Elongation at Break, MD: 80 %
- Film Elongation at Break, TD: 120 %
- Flexural Modulus: 2.10 GPa
$ 2241/MT
- Density: 0.900 - 0.910 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Antiblock Level: 1800 ppm
- Slip Level: 2000 ppm
- Film Elongation at Break, MD: 500 - 700 %
$ 1601/MT
- Density: 0.900 g/cc
- Melt Flow: 16 g/10 min @Load 2.16 kg, Temperature 230 °C
- Neck In: 11.0 cm
- Coating Weight: 12.0 g/m²
- Tensile Modulus: 0.850 GPa
$ 1974/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.011 cm/cm
- Melt Flow: 16 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ball Indentation Hardness: 61.0 MPa
- Tensile Strength at Break: 10.0 MPa
$ 1509/MT
- Density: 0.910 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 35 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 102
- Tensile Strength, Yield: 36.0 MPa
$ 1520/MT
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 30.0 MPa
- Elongation at Yield: 6.0 %
- Tensile Modulus: 2.40 GPa
- Flexural Strength: 40.0 MPa
$ 1597/MT
- Density: 0.900 - 0.910 g/cc
- Melt Flow: 1.2 g/10 min @Load 2.16 kg, Temperature 230 °C
- Film Elongation at Break, MD: 550 - 750 %
- Film Elongation at Break, TD: 550 - 750 %
- Tensile Modulus: 0.500 - 0.600 GPa
$ 2511/MT
- Density: 0.900 g/cc
- Density: 0.920 g/cc
- Melt Flow: 0.90 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 62
- Tensile Strength, Yield: 25.0 MPa
$ 1674/MT
- Density: 0.905 g/cc
- Linear Mold Shrinkage: 0.015 - 0.020 cm/cm
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 89
- Tensile Strength, Yield: 27.00 MPa
$ 1451/MT
- Melt Flow: 37 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melting Point: 161 - 165 °C
- Molecular Weight: narrow distribution
$ 1641/MT
- Density: 1.03 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 11 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 40 g/10 min @Load 5.00 kg, Temperature 230 °C
- Ball Indentation Hardness: 50.0 MPa
$ 1948/MT
- Density: 0.905 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Modulus: 0.400 GPa
- Flexural Modulus: 0.700 GPa
- Dart Drop, Total Energy: 30.0 J @Thickness 0.0500 mm
$ 1489/MT
- Density: 1.02 g/cc
- Linear Mold Shrinkage: 0.0090 cm/cm
- Melt Flow: 26 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ball Indentation Hardness: 49.0 MPa
- Tensile Strength, Yield: 22.0 MPa
$ 1576/MT
- Density: 0.906 g/cc
- Melt Flow: 30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 27.0 MPa
- Elongation at Yield: 13 %
- Tensile Modulus: 1.05 GPa
$ 2133/MT
- Density: 0.950 g/cc
- Linear Mold Shrinkage: 0.0080 cm/cm
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 16.0 MPa
- Elongation at Break: 400 %
$ 1762/MT
- Density: 0.910 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 55 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 107
- Tensile Strength, Yield: 38.0 MPa
$ 2394/MT
- Density: 0.902 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 86
- Tensile Strength, Yield: 25.0 MPa
$ 1456/MT
- Density: 0.900 g/cc
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 53
- Tensile Strength, Yield: 18.0 MPa
- Elongation at Yield: 10 %
$ 2251/MT
- Density: 0.900 - 0.910 g/cc
- Melt Flow: 11 g/10 min @Load 2.16 kg, Temperature 230 °C
- Film Elongation at Break, MD: 550 - 750 %
- Tensile Modulus: 0.400 - 0.500 GPa
- Flexural Modulus: 0.800 GPa
$ 2430/MT
- Density: 0.900 - 0.910 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Antiblock Level: 1800 ppm
- Slip Level: 1000 ppm
- Film Elongation at Break, MD: 550 - 750 %
$ 1940/MT
- Density: 0.905 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 33.5 MPa
- Elongation at Yield: 10 %
- Tensile Modulus: 1.40 GPa
$ 2174/MT
- Density: 0.902 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 112
- Tensile Strength, Yield: 40.0 MPa
$ 1622/MT
- Melt Flow: 6.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Flexural Modulus: 0.700 GPa
- Heat Seal Strength Initiation Temperature: 103 °C
- Melting Point: 128 - 132 °C
- Vicat Softening Point: 114 °C
- Haze: 1.8 %
$ 2224/MT
- Density: 0.900 g/cc
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 59
- Tensile Strength, Yield: 18.0 MPa
- Elongation at Yield: 4.0 %
$ 1495/MT
- Bulk Density: 0.500 - 0.600 g/cc
- Density: 0.900 - 0.910 g/cc
- Melt Flow: 11 g/10 min @Load 2.16 kg, Temperature 230 °C
- Slip Level: 2000 ppm
- Film Elongation at Break, MD: 550 - 750 %
$ 1529/MT
- Density: 0.910 g/cc
- Linear Mold Shrinkage: 0.0095 cm/cm
- Melt Flow: 22 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 18.0 MPa
- Elongation at Break: 330 %
$ 1481/MT
- Density: 0.905 g/cc
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 25.0 MPa
- Elongation at Yield: 13.5 %
- Tensile Modulus: 0.900 GPa
$ 1882/MT
- Density: 0.905 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 29.0 MPa
- Elongation at Yield: 11 %
$ 2259/MT
- Density: 0.905 g/cc
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 90
- Tensile Strength, Yield: 28.0 MPa
- Elongation at Yield: 12 %
$ 1888/MT
- Density: 0.905 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 82
- Tensile Strength, Yield: 29.0 MPa
$ 1632/MT
- Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melting Point: 161 - 165 °C
- Molecular Weight: narrow distribution
$ 1663/MT
- Melt Flow: 19 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melting Point: 161 - 165 °C
- Molecular Weight: narrow distribution
$ 2051/MT
- Density: 1.145 g/cc
- Linear Mold Shrinkage: 0.0010 cm/cm
- Linear Mold Shrinkage: 0.0075 cm/cm
- Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ball Indentation Hardness: 63.0 MPa
$ 2065/MT
- Density: 0.910 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 45 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 34.0 MPa
$ 1528/MT
- Density: 0.990 g/cc
- Linear Mold Shrinkage: 0.0090 cm/cm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ball Indentation Hardness: 35.0 MPa
- Tensile Strength, Yield: 17.00 MPa
$ 1664/MT
- Density: 0.905 g/cc
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Modulus: 0.330 GPa
- Flexural Modulus: 0.550 GPa
- Dart Drop, Total Energy: 15.0 J
$ 1538/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.011 cm/cm
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 60 g/10 min @Load 5.00 kg, Temperature 230 °C
- Ball Indentation Hardness: 88.5 MPa
$ 1990/MT
- Density: 0.904 g/cc
- Melt Flow: 90 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 25.0 MPa
- Elongation at Break: 10 %
- Tensile Modulus: 1.30 GPa
$ 1703/MT
- Density: 0.902 g/cc
- Melt Flow: 1.9 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 26.2 MPa
- Elongation at Yield: 13 %
- Tensile Modulus: 1.00 GPa
$ 2425/MT
- Density: 0.905 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 34.5 MPa
- Elongation at Yield: 9.0 %
- Tensile Modulus: 1.70 GPa
$ 1638/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0020 cm/cm
- Linear Mold Shrinkage: 0.011 cm/cm
- Melt Flow: 2.2 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ball Indentation Hardness: 101 MPa
$ 2035/MT
- Density: 0.910 g/cc
- Melt Flow: 96 g/10 min @Load 5.00 kg, Temperature 230 °C
- Ball Indentation Hardness: 66.0 MPa
- Tensile Strength, Yield: 26.0 MPa
- Elongation at Yield: 6.0 %
$ 2489/MT
- Density: 0.950 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 18.0 MPa
- Elongation at Break: 60 %
$ 2104/MT
- Density: 0.905 g/cc
- Melt Flow: 2.8 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 35.0 MPa
- Elongation at Yield: 9.0 %
- Tensile Modulus: 1.60 GPa
$ 2084/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 26 g/10 min @Load 5.00 kg, Temperature 230 °C
$ 1729/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage: 0.0060 cm/cm
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 16.0 MPa
- Elongation at Break: 123 %
$ 1666/MT
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melting Point: 161 - 165 °C
- Molecular Weight: medium distribution
$ 2420/MT
- Density: 0.900 - 0.910 g/cc
- Thickness: 50.0 microns
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Film Elongation at Break, MD: 650 %
- Film Elongation at Break, TD: 850 %
$ 2321/MT
- Density: 0.905 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 82
- Tensile Strength, Yield: 29.0 MPa
$ 1910/MT
- Density: 0.905 g/cc
- Melt Flow: 0.25 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 25.0 MPa
- Elongation at Yield: 13.5 %
- Tensile Modulus: 0.900 GPa
$ 1835/MT
- Melt Flow: 3.0 g/10 min
- Tensile Strength, Yield: 30.0 MPa
- Tensile Modulus: 1.00 GPa
- Charpy Impact, Notched: 0.400 J/cm² @Temperature 0.000 °C
- Charpy Impact, Notched: 1.50 J/cm² @Temperature 23.0 °C
$ 2382/MT
- Density: 1.18 g/cc
- Linear Mold Shrinkage: 0.0010 - 0.0020 cm/cm
- Linear Mold Shrinkage: 0.0080 - 0.012 cm/cm
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 118 MPa
$ 1591/MT
- Density: 1.06 g/cc
- Linear Mold Shrinkage: 0.0060 cm/cm
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 30 g/10 min @Load 5.00 kg, Temperature 230 °C
- Hardness, Shore D: 50
$ 1471/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0065 cm/cm
- Melt Flow: 22 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 17.0 MPa
- Elongation at Break: 300 %
$ 2052/MT
- Melt Flow: 3.7 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ash: 0.0010 - 0.0020 %
- Melting Point: 161 - 165 °C
- Dielectric Constant: 2.25
- Calcium, ppm: 2 max
$ 1993/MT
- Density: 0.700 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 11.0 MPa
- Elongation at Break: >= 50 %
- Tensile Modulus: 2.00 GPa
$ 2193/MT
- Density: 0.900 g/cc
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 60
- Tensile Strength, Yield: 28.0 MPa
- Elongation at Yield: 6.0 %
$ 1666/MT
- Density: 0.905 g/cc
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 25.0 MPa
- Elongation at Yield: 13.5 %
- Tensile Modulus: 0.900 GPa
$ 2286/MT
- Density: 1.14 g/cc
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 25 g/10 min @Load 5.00 kg, Temperature 230 °C
- Ball Indentation Hardness: 132 MPa
- Tensile Strength, Yield: 103 MPa
$ 1681/MT
- Density: 0.925 g/cc
- Linear Mold Shrinkage: 0.0015 cm/cm
- Linear Mold Shrinkage: 0.0080 cm/cm
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ball Indentation Hardness: 36.0 MPa
$ 1828/MT
- Density: 0.908 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 34.5 MPa
$ 1498/MT
- Density: 0.900 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 58
- Tensile Strength, Yield: 22.0 MPa
- Elongation at Yield: 6.0 %
$ 1886/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Elongation at Break: 2.1 %
- Tensile Modulus: 7.40 GPa
$ 1641/MT
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Flexural Modulus: 0.750 GPa
- Heat Seal Strength Initiation Temperature: 108 °C
- Melting Point: 130 - 134 °C
- Vicat Softening Point: 117 °C
- Haze: 1.0 %
$ 2032/MT
- Density: 0.905 g/cc
- Linear Mold Shrinkage: 0.016 cm/cm
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 20.0 MPa
- Tensile Modulus: 0.940 GPa
$ 1526/MT
- Density: 0.940 g/cc
- Linear Mold Shrinkage: 0.0080 cm/cm
- Melt Flow: 17 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 16.0 MPa
- Elongation at Break: 400 %
$ 1752/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0065 cm/cm
- Melt Flow: 22 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 17.0 MPa
- Elongation at Break: 300 %
$ 1984/MT
- Melt Flow: 2.1 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 40.00 MPa
- Elongation at Yield: 6.0 %
- Tensile Modulus: 2.00 GPa
- Flexural Modulus: 1.90 GPa
$ 1486/MT
- Density: 0.900 - 0.910 g/cc
- Thickness: 50.0 microns
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Film Elongation at Break, MD: 650 %
- Film Elongation at Break, TD: 850 %
$ 2367/MT
- Melt Flow: 1.9 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 2.5 g/10 min @Load 5.00 kg, Temperature 190 °C
- Melt Flow: 8.1 g/10 min @Load 5.00 kg, Temperature 230 °C
- Film Elongation at Break, MD: 80 - 100 %
- Tensile Modulus: 1.10 - 1.30 GPa
$ 2408/MT
- Density: 0.900 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 62
- Tensile Strength, Yield: 20.0 MPa
$ 1663/MT
- Density: 0.905 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 91
- Tensile Strength, Yield: 28.0 MPa
$ 1797/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 17.00 MPa
- Elongation at Break: 70 %
$ 1774/MT
- Density: 0.900 - 0.910 g/cc
- Thickness: 50.0 microns
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 230 °C
- Film Elongation at Break, MD: 600 %
- Film Elongation at Break, TD: 900 %
$ 1887/MT
- Density: 0.900 - 0.910 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Film Elongation at Break, MD: 550 - 750 %
- Film Elongation at Break, TD: 550 - 750 %
- Tensile Modulus: 0.500 - 0.600 GPa
$ 1805/MT
- Density: 0.905 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 110 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 30.0 MPa
- Elongation at Yield: 12 %
$ 1465/MT
- Density: 0.905 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 86
- Tensile Strength, Yield: 26.0 MPa
$ 1692/MT
- Density: 0.900 - 0.910 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Slip Level: 1800 ppm
- Film Elongation at Break, MD: 550 - 750 %
- Tensile Modulus: 0.400 - 0.500 GPa
$ 1476/MT
- Density: 0.999 g/cc
- Linear Mold Shrinkage: 0.0095 cm/cm
- Melt Flow: 26 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ball Indentation Hardness: 40.0 MPa
- Tensile Strength, Yield: 20.0 MPa
$ 1580/MT
- Density: 0.950 g/cc
- Linear Mold Shrinkage: 0.011 cm/cm
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 30 g/10 min @Load 5.00 kg, Temperature 230 °C
- Ball Indentation Hardness: 33.0 MPa
$ 1592/MT
- Density: 0.900 g/cc
- Melt Flow: 1.6 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 63
- Tensile Strength, Yield: 25.0 MPa
- Elongation at Break: <= 200 %
$ 1525/MT
- Density: 0.910 g/cc
- Melt Flow: 18 g/10 min @Load 2.16 kg, Temperature 230 °C
- Neck In: 8.00 cm
- Coating Weight: >= 12.0 g/m²
- Vicat Softening Point: 147 °C @Load 1.02 kg
$ 2019/MT
- Density: 0.905 g/cc
- Melt Flow: 2.8 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Modulus: 1.70 GPa
- Flexural Modulus: 1.65 GPa
- Charpy Impact, Notched: 0.500 J/cm² @Temperature 23.0 °C
$ 1937/MT
- Melt Flow: 27 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melting Point: 161 - 165 °C
- Molecular Weight: narrow distribution
$ 2358/MT
- Density: 0.905 g/cc
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 25.0 MPa
- Elongation at Yield: 13.5 %
- Tensile Modulus: 0.900 GPa
$ 1813/MT
- Density: 0.900 - 0.910 g/cc
- Melt Flow: 0.85 g/10 min @Load 2.16 kg, Temperature 230 °C
- Film Elongation at Break, MD: 550 - 750 %
- Film Elongation at Break, TD: 550 - 750 %
- Tensile Modulus: 0.500 - 0.600 GPa
$ 2262/MT
- Density: 0.904 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 80
- Tensile Strength, Yield: 22.5 MPa
$ 1470/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0010 cm/cm
- Linear Mold Shrinkage: 0.0070 cm/cm
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ball Indentation Hardness: 35.0 MPa
$ 2266/MT
- Density: 0.900 g/cc
- Melt Flow: 1.3 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 2.5 g/10 min @Load 5.00 kg, Temperature 190 °C
- Tensile Strength, Yield: 28.0 MPa
- Elongation at Yield: 8.0 %
$ 1822/MT
- Density: 0.904 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 45 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 89
- Tensile Strength, Yield: 26.0 MPa
$ 1585/MT
- Density: 0.900 - 0.910 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Antiblock Level: 1800 ppm
- Film Elongation at Break, MD: 500 - 700 %
- Film Elongation at Break, TD: 500 - 700 %
$ 1452/MT
- Density: 0.900 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 50
- Tensile Strength, Yield: 17.00 MPa
$ 1586/MT
- Melt Flow: 26 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melting Point: 161 - 165 °C
- Molecular Weight: medium distribution
$ 2542/MT
- Density: 0.905 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 90
- Tensile Strength, Yield: 31.0 MPa
$ 1879/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.011 cm/cm
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ball Indentation Hardness: 60.0 MPa
- Tensile Strength at Break: 10.0 MPa
$ 1560/MT
- Density: 0.905 g/cc
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Flexural Modulus: 1.45 GPa
- Charpy Impact, Notched: 0.200 J/cm² @Temperature -20.0 °C
- Charpy Impact, Notched: 2.50 J/cm² @Temperature 23.0 °C
$ 1678/MT
- Density: 0.905 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 27.0 - 29.0 MPa
- Elongation at Yield: 10 - 13 %
- Tensile Modulus: 1.30 GPa
$ 1639/MT
- Density: 0.902 g/cc
- Melt Flow: 37 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 97
- Tensile Strength, Yield: 34.0 MPa
- Elongation at Yield: 9.0 %
$ 1499/MT
- Density: 0.905 g/cc
- Melt Flow: 1.9 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Modulus: 0.400 GPa
- Flexural Modulus: 0.750 GPa
- Dart Drop, Total Energy: 40.0 J @Thickness 0.0500 mm
$ 2580/MT
- Density: 0.900 - 0.910 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Antiblock Level: 1800 ppm
- Slip Level: 2000 ppm
- Film Elongation at Break, MD: 550 - 750 %
$ 1555/MT
- Density: 0.902 g/cc
- Melt Flow: 1.9 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 26.0 MPa
- Elongation at Yield: 13 %
- Tensile Modulus: 1.15 GPa
$ 1761/MT
- Density: 0.905 g/cc
- Melt Flow: 22 g/10 min @Load 2.16 kg, Temperature 230 °C
- Neck In: 7.00 cm
- Coating Weight: 10.0 g/m²
- Tensile Modulus: 1.55 GPa
$ 1498/MT
- Density: 1.14 g/cc
- Linear Mold Shrinkage: 0.0010 cm/cm
- Linear Mold Shrinkage: 0.0050 cm/cm
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ball Indentation Hardness: 29.0 MPa
$ 1599/MT
- Density: 0.900 g/cc
- Linear Mold Shrinkage: 0.014 - 0.016 cm/cm
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ball Indentation Hardness: 44.0 MPa
- Tensile Strength, Yield: 24.0 MPa
$ 1500/MT
- Density: 2.00 g/cc
- Filler Content: 70 %
- Melt Flow: 2.8 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 18.0 MPa
- Elongation at Break: 50 %
$ 1520/MT
- Density: 1.06 g/cc
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 34 g/10 min @Load 5.00 kg, Temperature 230 °C
- Ball Indentation Hardness: 124 MPa
- Tensile Strength, Yield: 86.0 MPa
$ 1753/MT
- Density: 0.900 - 0.910 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Antiblock Level: 1800 ppm
- Slip Level: 1800 ppm
- Film Elongation at Break, MD: 550 - 750 %
$ 2015/MT
- Density: 0.915 g/cc
- Melt Flow: 0.25 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 33.00 MPa
- Elongation at Yield: 8.0 %
- Flexural Modulus: 1.90 GPa
$ 2546/MT
- Density: 0.905 g/cc
- Melt Flow: 350 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ball Indentation Hardness: 72.0 MPa
- Tensile Strength, Yield: 33.0 MPa
- Elongation at Break: 6.0 %
$ 1647/MT
- Melt Flow: 3.2 g/10 min @Load 2.16 kg, Temperature 230 °C
- Flexural Modulus: 1.65 GPa
$ 2075/MT
- Density: 0.900 - 0.910 g/cc
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Antiblock Level: 1500 ppm
- Slip Level: 2000 ppm
- Film Elongation at Break, MD: 550 - 750 %
$ 1544/MT
- Density: 0.910 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 39.0 MPa
$ 1445/MT
- Density: 0.905 g/cc
- Melt Flow: 0.25 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 25.0 MPa
- Elongation at Yield: 13.5 %
- Tensile Modulus: 0.900 GPa
$ 1688/MT
- Density: 0.910 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 98
- Tensile Strength, Yield: 36.5 MPa
$ 1846/MT
- Density: 0.990 g/cc
- Linear Mold Shrinkage: 0.0085 - 0.0095 cm/cm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ball Indentation Hardness: 35.0 MPa
- Tensile Strength, Yield: 17.00 MPa
$ 1531/MT
- Density: 0.905 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 67
- Tensile Strength, Yield: 22.99 MPa
$ 1776/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0010 cm/cm
- Linear Mold Shrinkage: 0.0080 cm/cm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ball Indentation Hardness: 43.0 MPa
$ 1452/MT
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ash: 0.0010 - 0.0020 %
- Melting Point: 161 - 165 °C
- Dielectric Constant: 2.25
- Calcium, ppm: 5
$ 1501/MT
- Density: 0.905 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Flow: 11.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ball Indentation Hardness: 43.0 MPa
- Tensile Strength at Break: 15.0 MPa
$ 2121/MT
- Density: 0.905 g/cc
- Melt Flow: 14 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ball Indentation Hardness: 62.0 MPa
- Tensile Strength, Yield: 26.0 MPa
- Elongation at Yield: 5.0 %
$ 1934/MT
- Density: 0.900 - 0.910 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Film Elongation at Break, MD: 80 %
- Film Elongation at Break, TD: 120 %
- Flexural Modulus: 2.10 GPa
$ 1813/MT
- Density: 0.940 g/cc
- Linear Mold Shrinkage: 0.0105 cm/cm
- Melt Flow: 11 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 50 g/10 min @Load 5.00 kg, Temperature 230 °C
- Ball Indentation Hardness: 28.0 MPa
$ 1540/MT
- Melt Flow: 2.4 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 30.0 MPa
- Elongation at Yield: 13 %
- Tensile Modulus: 0.900 GPa
- Flexural Modulus: 0.850 GPa
$ 1749/MT
- Density: 0.905 g/cc
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 25.00 MPa
- Elongation at Yield: 10 %
- Modulus of Elasticity: 0.900 GPa
$ 2383/MT
- Density: 0.900 g/cc
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 31.00 MPa
- Elongation at Yield: 8.0 %
- Flexural Modulus: 1.70 GPa
$ 2272/MT
- Melt Flow: 3.9 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ash: 0.0010 - 0.0020 %
- Melting Point: 161 - 165 °C
- Dielectric Constant: 2.25
- Calcium, ppm: 5
$ 2524/MT
- Density: 0.900 - 0.910 g/cc
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Elongation at Break: 600 - 800 %
- Tensile Modulus: 0.450 - 0.550 GPa
- Flexural Modulus: 1.00 GPa
$ 1829/MT
- Density: 0.900 g/cc
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 28.0 MPa
- Elongation at Yield: 6.0 %
- Flexural Modulus: 1.30 GPa
$ 1918/MT
- Density: 0.910 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 88
- Tensile Strength, Yield: 27.0 MPa
$ 1637/MT
- Density: 0.905 g/cc
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Flexural Modulus: 1.40 GPa
- Charpy Impact, Notched: 0.230 J/cm² @Temperature -20.0 °C
- Charpy Impact, Notched: 4.00 J/cm² @Temperature 23.0 °C
$ 2403/MT
- Filler Content: 20 %
- Tensile Strength at Break: 93.0 MPa
- Elongation at Break: 2.5 %
- Tensile Modulus: 5.07 GPa
- Flexural Strength: 120 MPa
$ 2228/MT
- Density: 0.900 - 0.910 g/cc
- Thickness: 40.0 microns
- Melt Flow: 1.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Film Elongation at Break, MD: 700 %
- Film Elongation at Break, TD: 800 %
$ 1516/MT
- Filler Content: 40 %
- Tensile Strength at Break: 135 MPa
- Elongation at Break: 2.1 %
- Tensile Modulus: 9.60 GPa
- Flexural Strength: 185 MPa
$ 1493/MT
- Density: 1.02 g/cc
- Linear Mold Shrinkage: 0.0095 cm/cm
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 230 °C
- Ball Indentation Hardness: 44.0 MPa
- Tensile Strength, Yield: 22.0 MPa
$ 1676/MT
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Slip Level: 2000 ppm
- Tensile Modulus: 0.500 GPa
- Flexural Modulus: 0.900 GPa
- Dart Drop, Total Energy: 20.0 J
$ 1458/MT
- Density: 0.908 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 80
- Tensile Strength, Yield: 25.0 MPa
$ 1655/MT
- Melt Flow: 2.2 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 2.9 g/10 min @Load 5.00 kg, Temperature 190 °C
- Melt Flow: 9.5 g/10 min @Load 5.00 kg, Temperature 230 °C
- Ash: 0.0010 - 0.0020 %
- Melting Point: 161 - 165 °C
$ 2481/MT
- Filler Content: 30 %
- Tensile Strength at Break: 120 MPa
- Elongation at Break: 2.3 %
- Tensile Modulus: 7.40 GPa
- Flexural Strength: 160 MPa
$ 1556/MT
- Density: 0.900 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 18.0 MPa
- Elongation at Yield: 15 %
$ 1564/MT
- Density: 0.905 g/cc
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 25.0 MPa
- Elongation at Yield: 13.5 %
- Tensile Modulus: 0.900 GPa
$ 1563/MT
- Density: 0.906 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 80
- Tensile Strength, Yield: 27.0 MPa
$ 1800/MT
- Density: 0.900 g/cc
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 27.0 MPa
- Elongation at Yield: 10 %
- Flexural Modulus: 1.10 GPa
$ 2411/MT
- Density: 0.910 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 19.50 MPa
- Elongation at Break: 570 %
$ 1663/MT
- Density: 0.905 g/cc
- Melt Flow: 45 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 27.0 MPa
- Elongation at Yield: 13 %
- Tensile Modulus: 1.05 GPa
$ 1539/MT
- Density: 0.902 g/cc
- Melt Flow: 1.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 24.0 MPa
- Elongation at Yield: 13 %
- Tensile Modulus: 0.900 GPa
$ 1673/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.011 cm/cm
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 24 g/10 min @Load 5.00 kg, Temperature 230 °C
- Ball Indentation Hardness: 59.0 MPa
$ 1630/MT
- Density: 0.906 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 80 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 89
- Tensile Strength, Yield: 25.0 MPa
$ 1974/MT
- Density: 1.02 g/cc
- Linear Mold Shrinkage: 0.0060 cm/cm
- Melt Flow: 6.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 16.0 MPa
- Elongation at Break: 80 %
$ 1528/MT
- Density: 0.906 g/cc
- Melt Flow: 1.3 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 2.3 g/10 min @Load 5.00 kg, Temperature 190 °C
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 230 °C
- Hardness, Rockwell R: 90
$ 1676/MT
- Density: 0.970 g/cc
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 74.2 g/10 min @Load 5.00 kg, Temperature 230 °C
- Ball Indentation Hardness: 66.0 MPa
- Tensile Strength, Yield: 26.3 MPa
$ 1635/MT
- Melt Flow: 2.1 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 40.0 MPa
- Elongation at Yield: 6.0 %
- Tensile Modulus: 2.00 GPa
- Flexural Modulus: 1.90 GPa
$ 2457/MT
- Density: 1.22 g/cc
- Linear Mold Shrinkage: 0.0090 cm/cm
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 27 g/10 min @Load 5.00 kg, Temperature 230 °C
- Ball Indentation Hardness: 90.0 MPa
$ 1874/MT
- Density: 0.905 g/cc
- Linear Mold Shrinkage: 0.015 - 0.020 cm/cm
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 22.99 MPa
- Elongation at Yield: 5.3 %
$ 2041/MT
- Density: 0.907 g/cc
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 94
- Tensile Strength, Yield: 29.5 MPa
- Elongation at Yield: 13 %
$ 1948/MT
- Density: 0.900 - 0.910 g/cc
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Elongation at Yield: 38.5 %
- Tensile Modulus: 1.90 GPa
- Flexural Modulus: 1.35 GPa
$ 1513/MT
- Density: 0.905 g/cc
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 0.60 g/10 min @Load 5.00 kg, Temperature 190 °C
- Tensile Strength, Yield: 36.0 MPa
- Elongation at Yield: 10 %
$ 1471/MT
- Density: 0.920 g/cc
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 57 g/10 min @Load 5.00 kg, Temperature 230 °C
- Ball Indentation Hardness: 62.0 MPa
- Tensile Strength, Yield: 26.0 MPa
$ 2407/MT
- Density: 1.16 g/cc
- Linear Mold Shrinkage: 0.00060 cm/cm
- Linear Mold Shrinkage: 0.00080 cm/cm
- Melt Flow: 3.3 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 65.0 MPa
$ 1607/MT
- Density: 1.27 g/cc
- Linear Mold Shrinkage: 0.0090 cm/cm
- Linear Mold Shrinkage: 0.010 cm/cm
- Melt Flow: 16 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 23.0 MPa
$ 2010/MT
- Density: 0.906 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 60 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 90
- Tensile Strength, Yield: 25.0 MPa
$ 1870/MT
- Density: 0.905 g/cc
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 25.0 MPa
- Elongation at Yield: 13.5 %
- Tensile Modulus: 0.900 GPa
$ 1533/MT
- Density: 0.905 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Modulus: 0.550 GPa
- Flexural Modulus: 1.00 GPa
- Dart Drop, Total Energy: 17.0 J @Thickness 0.0500 mm
$ 1519/MT
- Density: 0.960 g/cc
- Linear Mold Shrinkage: 0.0011 cm/cm
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 45 g/10 min @Load 5.00 kg, Temperature 230 °C
- Ball Indentation Hardness: 42.0 MPa
$ 1460/MT
- Density: 0.928 g/cc
- Environmental Stress Crack Resistance: >= 250 hour @Temperature 50.0 °C
- Thermal Stress Crack Resistance: >= 1.00 hour @Temperature 105 °C
- Oxidative Induction Time (OIT): 50 min @Temperature 200 °C
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 2060/MT
- Density: 0.905 g/cc
- Linear Mold Shrinkage: 0.010 - 0.020 cm/cm
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 80
- Tensile Strength, Yield: 28.0 MPa
$ 1697/MT
- Density: 0.905 g/cc
- Melt Flow: 0.30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 25.0 MPa
- Elongation at Yield: 13.5 %
- Tensile Modulus: 0.900 GPa
Delivery Polypropylene (PP) Borealis
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
lng carrier for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.