Celanese Thermx® CG023 NC010 PCT price 1711 per MT

Physical Properties
Specific Gravity
1.39 g/cc
Density
1.38 g/cc
Filler Content
20 %

Mechanical Properties
Hardness, Rockwell M
72
Tensile Strength at Break
100 MPa
Tensile Strength, Ultimate
100 MPa @Temperature 23.0 °C
Elongation at Break
2.3 %
Elongation at Break
2.7 % @Temperature 23.0 °C
Tensile Modulus
6.40 GPa @Temperature 23.0 °C
Flexural Strength
155 MPa
Flexural Strength
155 MPa
Flexural Modulus
5.80 GPa
Flexural Modulus
5.90 GPa
Izod Impact, Notched
0.600 J/cm @Temperature 23.0 °C
Izod Impact, Unnotched
5.20 J/cm @Temperature 23.0 °C
Izod Impact, Notched (ISO)
6.00 kJ/m² @Temperature 23.0 °C
Charpy Impact Unnotched
3.50 J/cm² @Temperature 23.0 °C
Charpy Impact, Notched
0.600 J/cm² @Temperature 23.0 °C

Thermal Properties
Melting Point
285 °C
Deflection Temperature at 1.8 MPa (264 psi)
250 °C
Deflection Temperature at 1.8 MPa (264 psi)
256 °C

Electrical Properties
Volume Resistivity
1.00e+15 ohm-cm
Surface Resistance
1.00e+17 ohm
Dielectric Constant
3.1 @Frequency 1000 Hz, Temperature 23.0 °C
Dielectric Constant
3.1 @Frequency 100000 Hz, Temperature 23.0 °C
Dielectric Constant
3.1 @Frequency 1.00e+6 Hz, Temperature 23.0 °C
Dielectric Strength
19.7 kV/mm @Thickness 3.20 mm, Temperature 23.0 °C
Dissipation Factor
0.0030 @Frequency 1000 Hz
Dissipation Factor
0.011 @Frequency 100000 Hz
Dissipation Factor
0.011 @Frequency 1.00e+6 Hz

Processing Properties
Melt Temperature
300 °C
Melt Temperature
295 - 310 °C
Mold Temperature
100 °C
Mold Temperature
80.0 - 120 °C
Drying Temperature
95.0 °C
Dry Time
4 - 6 hour
Moisture Content
<= 0.030 %

Descriptive Properties
Color
Natural
Drying Recommended
Yes
Features
Electrical Properties, Good
Filler
Glass fiber reinforcement
Forms
Pellets
Generic
PCT
Part Marking Code
>PCT-GF20<
Polymer Family
Polyester
Polymer Type
PCT
Processing Method
Injection Molding
Product Category
Electrical Resins
Product Category
Glass Reinforced Resins
Region Available
Americas
Region Available
Asia/Pacific
Region Available
Europe
Resin Identification
PCT-GF20
Uses
Connectors
Uses
E/E Applications

Alternative products

SABIC Innovative Plastics Valox® 855 PBT (Europe-Africa-Middle East) accurate 49%

$ 1444/MT

Specific Gravity: 1.50 g/cc
Density: 1.50 g/cc
Filler Content: 15 %
Moisture Absorption: 0.0600 %
Water Absorption at Saturation: 0.45 %

Celanese Thermx® CG023 PCT, 20% Glass Reinforced (Unverified Data**) accurate 49%

$ 1847/MT

Density: 1.38 g/cc
Density of Compound: 1.14 g/cc
Viscosity Test: 85 cm³/g
Linear Mold Shrinkage, Flow: 0.0030 cm/cm
Linear Mold Shrinkage, Transverse: 0.0080 cm/cm

Celanese Thermx® CG923 BK010 PCT accurate 65%

$ 2496/MT

Specific Gravity: 1.58 g/cc
Density: 1.58 g/cc
Filler Content: 20 %
Hardness, Rockwell M: 84
Tensile Strength at Break: 100 MPa

Celanese Thermx® CG933 NC010 PCT accurate 55%

$ 1958/MT

Specific Gravity: 1.63 g/cc
Density: 1.63 g/cc
Filler Content: 30 %
Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.0080 cm/cm @Thickness 2.00 mm

Celanese Celstran® PP-GF30-02 AD 3002 PP, 30% Glass Reinforced accurate 52%

$ 2015/MT

Specific Gravity: 1.12 g/cc
Density: 1.12 g/cc
Tensile Strength at Break: 92.0 MPa
Tensile Strength at Break: 108 MPa
Tensile Strength at Break: 66.9 MPa @Temperature 93.3 °C

SABIC Innovative Plastics Valox® DR48 PBT (Europe-Africa-Middle East) accurate 52%

$ 1710/MT

Specific Gravity: 1.51 g/cc
Density: 1.51 g/cc
Filler Content: 17 %
Moisture Absorption: 0.0700 %
Water Absorption at Saturation: 0.17 %

SABIC Innovative Plastics LNP Faradex EX06464 PEI (Asia Pacific) accurate 58%

$ 1957/MT

Specific Gravity: 1.50 g/cc
Density: 1.46 g/cc
Density: 1.46 g/cc
Linear Mold Shrinkage, Flow: 0.0055 cm/cm
Linear Mold Shrinkage, Flow: 0.0055 cm/cm @Time 86400 sec

SABIC Innovative Plastics LNP LUBRICOMP DCP32 PC (Asia Pacific) accurate 55%

$ 1599/MT

Density: 1.30 g/cc
Density: 1.30 g/cc
Moisture Absorption: 0.100 %
Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Time 86400 sec
Linear Mold Shrinkage, Flow: 0.0043 cm/cm @Time 86400 sec

Celanese Celstran® PP-GF30-02 AD 3019 PP, 30% Glass Reinforced accurate 49%

$ 1742/MT

Specific Gravity: 1.12 g/cc
Density: 1.12 g/cc
Tensile Strength at Break: 100 MPa
Tensile Strength at Break: 108 MPa
Tensile Strength at Break: 66.9 MPa @Temperature 93.3 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lpg tanker for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for Celanese Thermx® CG023 NC010 PCT

Seller from Karachi – 2021-08-05:

Seller from Karachi work with company: 3M, Solvay, PolyOne Corporation, SABIC Innovative Plastics (GE Plastics)

Price: $1711 per MT

Seller from Toronto – 2021-04-12:

Seller from Toronto work with company: RTP Company, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2587 per MT

Seller from Monterrey – 2021-07-03:

Seller from Monterrey work with company: ChevronTexaco Corp, SABIC Innovative Plastics (GE Plastics), BASF, ALIMEX GmbH

Price: $2003 per MT