Celanese Thermx® CG923 BK010 PCT price 2496 per MT

Physical Properties
Specific Gravity
1.58 g/cc
Density
1.58 g/cc
Filler Content
20 %

Mechanical Properties
Hardness, Rockwell M
84
Tensile Strength at Break
100 MPa
Tensile Strength, Ultimate
99.0 MPa @Temperature 23.0 °C
Elongation at Break
1.8 %
Elongation at Break
2.1 % @Temperature 23.0 °C
Tensile Modulus
8.00 GPa @Temperature 23.0 °C
Flexural Strength
140 MPa
Flexural Strength
145 MPa
Flexural Modulus
6.75 GPa
Flexural Modulus
7.40 GPa
Izod Impact, Notched
0.450 J/cm @Temperature 23.0 °C
Izod Impact, Unnotched
430 J/cm @Temperature 23.0 °C
Izod Impact, Notched (ISO)
5.00 kJ/m² @Temperature 23.0 °C
Charpy Impact Unnotched
3.00 J/cm² @Temperature 23.0 °C
Charpy Impact, Notched
0.500 J/cm² @Temperature 23.0 °C

Thermal Properties
Melting Point
283 °C
Deflection Temperature at 0.46 MPa (66 psi)
272 °C
Deflection Temperature at 1.8 MPa (264 psi)
225 °C
Deflection Temperature at 1.8 MPa (264 psi)
234 °C
UL RTI, Electrical
150 °C @Thickness 1.50 mm
UL RTI, Electrical
150 °C @Thickness 3.00 mm
UL RTI, Mechanical without Impact
130 °C @Thickness 1.50 mm
UL RTI, Mechanical without Impact
130 °C @Thickness 3.00 mm
Flammability, UL94
V-0 @Thickness 1.50 mm
Flammability, UL94
V-0 @Thickness 1.50 mm
Flammability, UL94
V-0 @Thickness 3.00 mm
Flammability, UL94
V-0 @Thickness 3.00 mm

Electrical Properties
Volume Resistivity
1.00e+15 ohm-cm
Surface Resistance
1.00e+16 ohm
Dielectric Constant
3.0 @Frequency 1000 Hz, Temperature 23.0 °C
Dielectric Constant
3.0 @Frequency 10000 Hz, Temperature 23.0 °C
Dielectric Constant
3.0 @Frequency 100000 Hz, Temperature 23.0 °C
Dielectric Constant
3.0 @Frequency 1.00e+6 Hz, Temperature 23.0 °C
Dielectric Strength
20.7 kV/mm @Thickness 3.20 mm, Temperature 23.0 °C
Dissipation Factor
0.0030 @Frequency 100000 Hz
Dissipation Factor
0.0080 @Frequency 1.00e+6 Hz
Dissipation Factor
0.013 @Frequency 1000 Hz
Dissipation Factor
0.021 @Frequency 10000 Hz

Processing Properties
Melt Temperature
300 °C
Melt Temperature
295 - 310 °C
Mold Temperature
100 °C
Mold Temperature
80.0 - 120 °C
Drying Temperature
95.0 °C
Dry Time
4 - 6 hour
Moisture Content
<= 0.030 %

Descriptive Properties
Color
Black
Drying Recommended
Yes
Features
Electrical Properties, Good
Features
Flame Retardant
Filler
Glass fiber reinforcement
Forms
Pellets
Generic
PCT
Part Marking Code
>PCT-GF20FR(17)<
Polymer Family
Polyester
Polymer Type
PCT
Processing Method
Injection Molding
Product Category
Electrical Resins
Product Category
Flame Retardant Resins
Product Category
Glass Reinforced Resins
Region Available
Americas
Region Available
Asia/Pacific
Region Available
Europe
Resin Identification
PCT-GF20FR(17)
Uses
Connectors
Uses
E/E Applications

Alternative products

Celanese Thermx® CG923 PCT, 20% Glass Reinforced (Unverified Data**) accurate 47%

$ 1730/MT

Density: 1.57 g/cc
Linear Mold Shrinkage, Flow: 0.0040 cm/cm
Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
Tensile Strength at Break: 100 MPa
Elongation at Break: 1.8 %

Celanese Thermx® CG033 NC010 PCT accurate 58%

$ 1765/MT

Specific Gravity: 1.46 g/cc
Density: 1.45 g/cc
Filler Content: 30 %
Linear Mold Shrinkage, Flow: 0.0025 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.0090 cm/cm @Thickness 2.00 mm

Celanese Thermx® TE3002 BK010 PCT accurate 47%

$ 1455/MT

Density: 1.65 g/cc
Filler Content: 30 %
Tensile Strength at Break: 100 MPa
Elongation at Break: 1.2 %
Tensile Modulus: 10.0 GPa @Temperature 23.0 °C

Lucas-Milhaupt BRAZE 999 Commercial Grade Fine Silver accurate 51%

$ 1640/MT

Density: 10.49 g/cc
Vapor Pressure: 0.00133 bar @Temperature 1360 °C
Tensile Strength at Break: 165 - 207 MPa
Tensile Strength at Break: 165 - 207 MPa
Tensile Strength at Break: 179 - 228 MPa

Celanese Thermx® CGT33 NC010 PCT accurate 47%

$ 1920/MT

Density: 1.44 g/cc
Filler Content: 30 %
Tensile Strength at Break: 120 MPa
Elongation at Break: 2.8 %
Tensile Modulus: 8.40 GPa @Temperature 23.0 °C

Celanese Thermx® CG933 NC010 PCT accurate 66%

$ 1958/MT

Specific Gravity: 1.63 g/cc
Density: 1.63 g/cc
Filler Content: 30 %
Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.0080 cm/cm @Thickness 2.00 mm

Celanese Thermx® CG023 NC010 PCT accurate 69%

$ 1711/MT

Specific Gravity: 1.39 g/cc
Density: 1.38 g/cc
Filler Content: 20 %
Hardness, Rockwell M: 72
Tensile Strength at Break: 100 MPa

Celanese Thermx® CG923 NC010 PCT accurate 58%

$ 2426/MT

Density: 1.57 g/cc
Filler Content: 20 %
Tensile Strength at Break: 100 MPa
Elongation at Break: 1.8 %
Tensile Modulus: 8.00 GPa @Temperature 23.0 °C

Celanese Thermx® CG033 BK010T PCT accurate 47%

$ 1588/MT

Density: 1.45 g/cc
Filler Content: 30 %
Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.0080 cm/cm @Thickness 2.00 mm
Tensile Strength at Break: 120 MPa

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, tanker ship for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for Celanese Thermx® CG923 BK010 PCT

Seller from Tehran – 2021-04-19:

Seller from Tehran work with company: RTP Company, SABIC Innovative Plastics (GE Plastics), Lehmann & Voss & Co., ALIMEX GmbH

Price: $2496 per MT