Celanese Zenite® 6140L BK010 LCP

Seller in Shenzhen price: $1967 per MT
Seller in Montréal price: $1488 per MT

Celanese Zenite® 6140L BK010 LCP in Polymer, Thermoplastic, 40% Glass Fiber Filled, Liquid Crystal Polymer (LCP)

  • Physical Properties
  • Specific Gravity
  • 1.71 g/cc
  • Density
  • 1.71 g/cc
  • Filler Content
  • 40 %
  • Linear Mold Shrinkage, Flow
  • 0.00050 cm/cm @Thickness 2.00 mm
  • Linear Mold Shrinkage, Transverse
  • 0.0050 cm/cm @Thickness 2.00 mm
  • Mechanical Properties
  • Tensile Strength at Break
  • 130 MPa
  • Tensile Strength, Ultimate
  • 135 MPa @Thickness 3.17 mm, Temperature 23.0 °C
  • Elongation at Break
  • 1.1 %
  • Elongation at Break
  • 1.3 % @Thickness 3.17 mm, Temperature 23.0 °C
  • Tensile Modulus
  • 17.0 GPa @Temperature 23.0 °C
  • Flexural Strength
  • 190 MPa @Temperature 23.0 °C
  • Flexural Strength
  • 183 MPa @Thickness 3.17 mm, Temperature 23.0 °C
  • Flexural Modulus
  • 16.5 GPa @Temperature 23.0 °C
  • Flexural Modulus
  • 15.6 GPa @Thickness 3.17 mm, Temperature 23.0 °C
  • Izod Impact, Notched
  • 1.12 J/cm @Thickness 3.17 mm, Temperature 23.0 °C
  • Izod Impact, Notched (ISO)
  • 12.0 kJ/m² @Temperature 23.0 °C
  • Izod Impact, Unnotched (ISO)
  • 20.0 kJ/m² @Temperature -30.0 °C
  • Izod Impact, Unnotched (ISO)
  • 20.0 kJ/m² @Temperature 23.0 °C
  • Charpy Impact Unnotched
  • 2.00 J/cm² @Temperature -30.0 °C
  • Charpy Impact Unnotched
  • 2.30 J/cm² @Temperature 23.0 °C
  • Charpy Impact, Notched
  • 1.50 J/cm² @Temperature -30.0 °C
  • Charpy Impact, Notched
  • 1.50 J/cm² @Temperature 23.0 °C
  • Thermal Properties
  • CTE, linear
  • 0.000 µm/m-°C @Thickness 2.00 mm, Temperature 160 - 260 °C
  • CTE, linear
  • 2.00 µm/m-°C @Thickness 4.00 mm, Temperature 160 - 260 °C
  • CTE, linear
  • 3.00 µm/m-°C @Thickness 4.00 mm, Temperature -40.0 - 23.0 °C
  • CTE, linear
  • 3.00 µm/m-°C @Thickness 2.00 mm, Temperature -40.0 - 23.0 °C
  • CTE, linear
  • 3.00 µm/m-°C @Thickness 2.00 mm, Temperature -40.0 - 260 °C
  • CTE, linear
  • 3.00 µm/m-°C @Thickness 4.00 mm, Temperature -40.0 - 260 °C
  • CTE, linear
  • 3.00 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C
  • CTE, linear
  • 3.00 µm/m-°C @Thickness 2.00 mm, Temperature 55.0 - 160 °C
  • CTE, linear
  • 4.00 µm/m-°C @Thickness 4.00 mm, Temperature 23.0 - 55.0 °C
  • CTE, linear
  • 5.00 µm/m-°C @Thickness 4.00 mm, Temperature 55.0 - 160 °C
  • CTE, linear, Transverse to Flow
  • 55.0 µm/m-°C @Temperature -40.0 - 23.0 °C
  • CTE, linear, Transverse to Flow
  • 56.0 µm/m-°C @Temperature -40.0 - 23.0 °C
  • CTE, linear, Transverse to Flow
  • 77.0 µm/m-°C @Temperature -40.0 - 260 °C
  • CTE, linear, Transverse to Flow
  • 79.0 µm/m-°C @Temperature -40.0 - 260 °C
  • CTE, linear, Transverse to Flow
  • 62.0 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C
  • CTE, linear, Transverse to Flow
  • 64.0 µm/m-°C @Thickness 4.00 mm, Temperature 23.0 - 55.0 °C
  • CTE, linear, Transverse to Flow
  • 80.0 µm/m-°C @Thickness 2.00 mm, Temperature 55.0 - 160 °C
  • CTE, linear, Transverse to Flow
  • 82.0 µm/m-°C @Thickness 4.00 mm, Temperature 55.0 - 160 °C
  • CTE, linear, Transverse to Flow
  • 90.0 µm/m-°C @Thickness 2.00 mm, Temperature 160 - 260 °C
  • CTE, linear, Transverse to Flow
  • 94.0 µm/m-°C @Thickness 4.00 mm, Temperature 160 - 260 °C
  • Melting Point
  • 335 °C
  • Melting Point
  • 335 °C
  • Deflection Temperature at 1.8 MPa (264 psi)
  • 271 °C
  • Deflection Temperature at 1.8 MPa (264 psi)
  • 280 °C
  • Glass Transition Temp, Tg
  • 120 °C
  • UL RTI, Electrical
  • 240 °C @Thickness 1.50 mm
  • UL RTI, Electrical
  • 240 °C @Thickness 0.750 mm
  • UL RTI, Electrical
  • 240 °C @Thickness 3.00 mm
  • UL RTI, Mechanical with Impact
  • 220 °C @Thickness 1.50 mm
  • UL RTI, Mechanical with Impact
  • 220 °C @Thickness 0.750 mm
  • UL RTI, Mechanical with Impact
  • 220 °C @Thickness 3.00 mm
  • UL RTI, Mechanical without Impact
  • 240 °C @Thickness 1.50 mm
  • UL RTI, Mechanical without Impact
  • 240 °C @Thickness 0.750 mm
  • UL RTI, Mechanical without Impact
  • 240 °C @Thickness 3.00 mm
  • Electrical Properties
  • Volume Resistivity
  • >= 1.00e+15 ohm-cm
  • Volume Resistivity
  • 1.00e+16 ohm-cm
  • Surface Resistance
  • >= 1.00e+15 ohm
  • Surface Resistance
  • 1.00e+16 ohm
  • Dielectric Strength
  • 27.0 kV/mm @Thickness 2.00 mm
  • Dielectric Strength
  • 45.0 kV/mm @Thickness 1.00 mm
  • Comparative Tracking Index
  • 175 V
  • Comparative Tracking Index
  • 175 - 249 V

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, ship for sale norway. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for Celanese Zenite® 6140L BK010 LCP

Seller from Shenzhen – 2021-03-18:

Seller from Shenzhen work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), Lehmann & Voss & Co.

Price: $1967 per MT

Seller from Montréal – 2021-06-13:

Seller from Montréal work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1488 per MT

Share on Pinterest
Share on LinkedIn
Share on Reddit

Would you like to sell Celanese Zenite® 6140L BK010 LCP?

Plastic warehouse

Find a direct plastic supplier if you're interested in a supplier or Wax supplier in Singapore open-nearme.com