CLAL-MSX CUPROROR® TL2 1/2 hard, Copper Alloy price 1867 per MT

Physical Properties
Density
8.90 g/cc

Mechanical Properties
Hardness, Vickers
115 - 140
Hardness, Vickers
112 @Temperature 500 °C, Time 1800 sec
Hardness, Vickers
114 @Temperature 500 °C, Time 600 sec
Hardness, Vickers
117 @Temperature 500 °C, Time 180 sec
Hardness, Vickers
120 @Temperature 350 °C, Time 180 sec
Hardness, Vickers
120 @Temperature 500 °C, Time 60.0 sec
Hardness, Vickers
120 @Temperature 350 °C, Time 600 sec
Hardness, Vickers
120.5 @Temperature 350 °C, Time 60.0 sec
Hardness, Vickers
121 @Temperature 350 °C, Time 30.0 sec
Hardness, Vickers
121 @Temperature 350 °C, Time 1800 sec
Hardness, Vickers
121 @Temperature 500 °C, Time 30.0 sec
Hardness, Vickers
122 @Temperature 500 °C, Time 10.0 sec
Hardness, Vickers
122 @Temperature 350 °C, Time 0.000 sec
Hardness, Vickers
122 @Temperature 350 °C, Time 10.0 sec
Hardness, Vickers
123 @Temperature 500 °C, Time 0.000 sec
Tensile Strength, Ultimate
350 - 440 MPa
Tensile Strength, Yield
>= 300 MPa @Strain 0.200 %
Elongation at Break
>= 10 %
Modulus of Elasticity
140 GPa

Thermal Properties
CTE, linear
16.3 µm/m-°C @Temperature 0.000 - 500 °C
CTE, linear
16.4 µm/m-°C @Temperature 0.000 - 250 °C
CTE, linear
16.7 µm/m-°C @Temperature 0.000 - 100 °C
Specific Heat Capacity
0.383 J/g-°C
Thermal Conductivity
338 W/m-K
Melting Point
1080 °C

Component Elements Properties
Cobalt, Co
0.080 %
Phosphorous, P
0.080 %

Electrical Properties
Electrical Resistivity
0.00000181 - 0.00000229 ohm-cm

Alternative products

IBC Advanced Alloys C17510 Beryllium Copper Alloy Rounds, Temper AT(TF00) accurate 66%

$ 1667/MT

Density: 8.83 g/cc
Hardness, Rockwell B: 92 - 100
Tensile Strength: 689 - 896 MPa
Tensile Strength, Yield: 552 - 689 MPa @Strain 0.200 %
Elongation at Break: >= 10 %

BASF Ultramid® 8260 HS BK-102 40% Mineral Filled PA6 (Dry) accurate 99%

$ 1923/MT

Density: 1.49 g/cc
Water Absorption: 1.1 %
Water Absorption: 5.7 %
Moisture Absorption at Equilibrium: 1.6 %
Linear Mold Shrinkage: 0.0090 cm/cm

HP Alloys Alloy 718, 50% Cold Worked accurate 66%

$ 2144/MT

Density: 8.20 g/cc
Tensile Strength, Ultimate: 1544 MPa
Tensile Strength, Yield: 1413 MPa
Elongation at Break: 10 %
Reduction of Area: 43 %

Haynes Hastelloy® C-22HSâ„¢ Nickel Alloy Sheet, Cold-rolled, Solution Annealed, Age-hardened accurate 66%

$ 1446/MT

Density: 8.60 g/cc
Density: 8.64 g/cc
Hardness, Rockwell C: 30
Hardness, Rockwell C: 35
Hardness, Rockwell C: 40

Kennametal Stellite Stellite® 31 PM cast accurate 66%

$ 1671/MT

Density: 8.45 g/cc
Density: 8.61 g/cc
Tensile Strength, Ultimate: 745 MPa
Tensile Strength, Ultimate: 436 MPa @Temperature 760 °C
Tensile Strength, Ultimate: 521 MPa @Temperature 649 °C

Carpenter MP35N* Ni-Co-Cr-Mo Alloy, Cold Drawn 53%, Aged 565°C/4hr/AC accurate 99%

$ 2358/MT

Density: 8.43 g/cc
Tensile Strength, Ultimate: 2027 MPa
Tensile Strength, Ultimate: 1655 MPa @Temperature 426 °C
Tensile Strength, Ultimate: 1689 MPa @Temperature 371 °C
Tensile Strength, Ultimate: 1724 MPa @Temperature 316 °C

Haynes 282® Nickel Alloy Sheet, Solution Annealed and Age-hardened accurate 66%

$ 2138/MT

Density: 8.27 g/cc
Density: 8.29 g/cc
Hardness, Rockwell C: 30
Tensile Strength, Ultimate: 115 MPa @Temperature 1000 °C
Tensile Strength, Ultimate: 447 MPa @Temperature 900 °C

SABIC Innovative Plastics Xenoy® X4870HH PC+PET (Asia Pacific) accurate 66%

$ 1842/MT

Specific Gravity: 1.34 g/cc
Density: 1.34 g/cc
Moisture Absorption: 0.140 %
Water Absorption at Saturation: 0.42 %
Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm

Haynes Hastelloy® C-22HSâ„¢ Nickel Alloy Plate, Annealed accurate 66%

$ 1446/MT

Density: 8.60 g/cc
Density: 8.64 g/cc
Hardness, Rockwell B: 92
Tensile Strength, Ultimate: 822 MPa
Tensile Strength, Ultimate: 814 MPa @Treatment Temp. 427 °C, Time 2.88e+7 sec

Special Metals INCOLOY® Alloy 907 accurate 99%

$ 2017/MT

Density: 8.33 g/cc
Tensile Strength, Ultimate: 1140 MPa @Temperature 550 °C
Tensile Strength, Ultimate: 1350 MPa @Temperature 23.0 °C
Tensile Strength, Yield: 1100 MPa @Strain 0.200 %
Tensile Strength, Yield: 970 MPa @Strain 0.200 %, Temperature 550 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, sale ships. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for CLAL-MSX CUPROROR® TL2 1/2 hard, Copper Alloy

Seller from Toronto – 2021-06-30:

Seller from Toronto work with company: Solvay, Dow Corning, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2003 per MT

Seller from Alexandria – 2021-07-09:

Seller from Alexandria work with company: Solvay, PolyOne Corporation, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1867 per MT