CP-Polymer-Technik Wellamid® 6000/52 GV 15 HWUVCP 15% Glass Fiber Nylon 6, Low Temperature Impact Modified, UV Stabilized, Heat Stabilized, Dry price 1450 per MT

Physical Properties
Density
1.21 g/cc
Moisture Absorption at Equilibrium
2.0 - 2.5 %
Linear Mold Shrinkage
0.0030 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse
0.0080 cm/cm @Thickness 4.00 mm

Mechanical Properties
Tensile Strength at Break
105 MPa
Elongation at Break
4.0 %
Tensile Modulus
5.80 GPa
Flexural Modulus
5.20 GPa
Charpy Impact Unnotched
5.00 J/cm² @Temperature 23.0 °C
Charpy Impact, Notched
1.30 J/cm² @Temperature 23.0 °C

Thermal Properties
CTE, linear
30.0 µm/m-°C @Temperature 23.0 - 80.0 °C
Melting Point
215 °C
Deflection Temperature at 0.46 MPa (66 psi)
200 °C
Deflection Temperature at 1.8 MPa (264 psi)
170 °C
Vicat Softening Point
200 °C
Flammability, UL94
HB @Thickness 1.60 mm
Flammability, UL94
HB @Thickness 3.20 mm

Electrical Properties
Volume Resistivity
1.00e+15 ohm-cm
Surface Resistance
1.00e+12 ohm
Dielectric Constant
4.0 @Frequency 1e+6 Hz
Dielectric Strength
40.0 kV/mm
Dielectric Loss Index
0.025
Comparative Tracking Index
550 V

Processing Properties
Melt Temperature
250 - 280 °C
Mold Temperature
60.0 - 90.0 °C

Descriptive Properties
Back Pressure
Low
Holding Pressure
High
Injection Speed
Medium to High
Screw Speed
High

Alternative products

CP-Polymer-Technik Wellamid® 6000 GVS 10/20 HWUVCP 10% Glass Fiber and 20% Glass Sphere Nylon 6, UV Stabilized, Heat Stabilized, Dry accurate 64%

$ 1512/MT

Density: 1.38 g/cc
Moisture Absorption at Equilibrium: 1.8 - 2.3 %
Linear Mold Shrinkage: 0.0050 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse: 0.0070 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 110 MPa

CP-Polymer-Technik Wellamid® 6000/52 GV 15 HWCP 15% Glass Fiber Nylon 6, Low Temperature Impact Modified, Heat Stabilized, Dry accurate 99%

$ 2225/MT

Density: 1.21 g/cc
Moisture Absorption at Equilibrium: 2.0 - 2.5 %
Linear Mold Shrinkage: 0.0030 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse: 0.0080 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 105 MPa

BASF Ultramid® 8231G HS 14% Glass Filled PA6 (Dry) accurate 70%

$ 1919/MT

Density: 1.067 g/cc
Density: 1.23 g/cc
Water Absorption: 1.4 %
Water Absorption: 8.1 %
Moisture Absorption at Equilibrium: 2.3 %

CP-Polymer-Technik Wellamid® 6000/58 GV 15 HWUVCP 15% Glass Fiber Nylon 6, Impact Modified Until -40°C, UV Stabilized, Heat Stabilized, Dry accurate 87%

$ 1761/MT

Density: 1.16 g/cc
Moisture Absorption at Equilibrium: 2.0 - 2.5 %
Linear Mold Shrinkage: 0.0030 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse: 0.0080 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 100 MPa

CP-Polymer-Technik Wellamid® 6000 GV 15 HWCP 15% Glass Fiber Nylon 6, Heat Stabilized, Dry accurate 70%

$ 1642/MT

Density: 1.23 g/cc
Moisture Absorption at Equilibrium: 2.0 - 2.5 %
Linear Mold Shrinkage: 0.0040 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse: 0.0090 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 125 MPa

SABIC Innovative Plastics LNP Faradex EX06464 PEI (Asia Pacific) accurate 75%

$ 1957/MT

Specific Gravity: 1.50 g/cc
Density: 1.46 g/cc
Density: 1.46 g/cc
Linear Mold Shrinkage, Flow: 0.0055 cm/cm
Linear Mold Shrinkage, Flow: 0.0055 cm/cm @Time 86400 sec

CP-Polymer-Technik Wellamid® 6000 GV 20 HWCP 20% Glass Fiber Nylon 6, Heat Stabilized, Dry accurate 70%

$ 1740/MT

Density: 1.29 g/cc
Moisture Absorption at Equilibrium: 2.0 - 2.5 %
Linear Mold Shrinkage: 0.0030 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse: 0.0090 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 140 MPa

CP-Polymer-Technik Wellamid® 6000 MF 30 HWCP 30% Milled Glass Fiber Nylon 6, Heat Stabilized, Dry accurate 75%

$ 2177/MT

Density: 1.32 g/cc
Moisture Absorption at Equilibrium: 1.8 - 2.3 %
Linear Mold Shrinkage: 0.0050 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse: 0.0070 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 130 MPa

CP-Polymer-Technik Wellamid® 6000/42 GV 15 HWCP 15% Glass Fiber Nylon 6, Polymer Modified, Heat Stabilized, Dry accurate 93%

$ 1602/MT

Density: 1.20 g/cc
Moisture Absorption at Equilibrium: 2.0 - 2.5 %
Linear Mold Shrinkage: 0.0030 cm/cm @Thickness 4.00 mm
Linear Mold Shrinkage, Transverse: 0.0090 cm/cm @Thickness 4.00 mm
Tensile Strength at Break: 100 MPa

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, chemical carrier for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

4 prices for CP-Polymer-Technik Wellamid® 6000/52 GV 15 HWUVCP 15% Glass Fiber Nylon 6, Low Temperature Impact Modified, UV Stabilized, Heat Stabilized, Dry

Seller from Rio de Janeiro – 2021-04-30:

Seller from Rio de Janeiro work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2555 per MT

Seller from Bogotá – 2021-06-23:

Seller from Bogotá work with company: 3M, Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics)

Price: $1450 per MT

Seller from Shenzhen – 2021-05-26:

Seller from Shenzhen work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2286 per MT

Seller from Buenos Aires – 2021-07-27:

Seller from Buenos Aires work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1489 per MT

Would you like to sell CP-Polymer-Technik Wellamid® 6000/52 GV 15 HWUVCP 15% Glass Fiber Nylon 6, Low Temperature Impact Modified, UV Stabilized, Heat Stabilized, Dry?